KR200391443Y1 - Silver heat resistance ceramic kaolin a plate - Google Patents

Silver heat resistance ceramic kaolin a plate Download PDF

Info

Publication number
KR200391443Y1
KR200391443Y1 KR20-2005-0012357U KR20050012357U KR200391443Y1 KR 200391443 Y1 KR200391443 Y1 KR 200391443Y1 KR 20050012357 U KR20050012357 U KR 20050012357U KR 200391443 Y1 KR200391443 Y1 KR 200391443Y1
Authority
KR
South Korea
Prior art keywords
silver
heat
plate
silver powder
nano
Prior art date
Application number
KR20-2005-0012357U
Other languages
Korean (ko)
Inventor
박창림
Original Assignee
박창림
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 박창림 filed Critical 박창림
Priority to KR20-2005-0012357U priority Critical patent/KR200391443Y1/en
Application granted granted Critical
Publication of KR200391443Y1 publication Critical patent/KR200391443Y1/en

Abstract

본 고안은 인덕션렌지 조리용으로 사용되는 플레이트 부분을 내열 소지 및 유약성분에 나노 크기의 은분을 소정량 투입하여 초벌구이 및 본 소성의 재벌구이를 통하여 은분이 코팅된 내열용 플레이트로 성형하는데 그 목적이 있으며, 상기의 목적을 달성하기 위하여 고순도의 은을 전기분해장치에 의해 초미립자로 녹여 나오 크기의 은용출액 은분으로 형성시키되, 상기 나노 크기의 은용출액 은분을 플레이트의 재료로 사용되는 소지 및 유약에 투입하여 초벌구이 및 본 소성에 의해 실생활에 사용되는 인덕션렌지 조리용 내열 플레이트로 형성시킬 수 있는 특징이 있다.The present invention is to mold the plate portion used for induction stove cooking into a heat-resistant plate coated with silver powder through the first roasting and the chaebol roasting of the firing by putting a predetermined amount of nano-size silver powder in the heat-resistant base and glaze components. In order to achieve the above object, high-purity silver is melted into ultra-fine particles by an electrolysis device to form silver eluent silver powder, and the nano-size silver eluent silver powder is added to the base and glaze used as a material of the plate. By the first baking and the main firing is characterized in that it can be formed into a heat-resistant plate for induction stove cooking used in real life.

Description

나노 은분을 함유한 유약 및 소지로 형성된 조리용 내열 플레이트 {Silver heat resistance ceramic kaolin a plate}Cooking heat-resistant plate formed of glaze and base containing nano silver powder {Silver heat resistance ceramic kaolin a plate}

본 고안은 나노 은분을 함유한 유악 및 소지로 형성된 조리용 내열 플레이트에 관한 것으로서, 보다 상세하게는 조리용 플레이트 상판을 내열에 견딜 수 있는 형태의 소지로 형성시키되, 상기 소지에는 나노 크기의 은분을 소정량 투입하여 성형시킴과 아울러 상기 성형된 플레이트 상판의 표면에 도포되는 유약 성분에도 상기 나노 크기의 은분을 투입하여 초벌구이 및 본 소성을 통하여 형성되는 조리용 내열 플레이트에 관한 것이다.The present invention relates to a cooking heat-resistant plate formed of yuga and body containing nano silver powder, and more specifically, to form a substrate of the shape that can withstand the heat resistant cooking plate top plate, the substrate is nano-sized silver powder The present invention relates to a heat-resistant cooking plate which is formed through baking and main firing by injecting the nano-sized silver powder into the glaze component applied to the surface of the formed plate top plate by molding a predetermined amount.

주지된 바와 같이 인덕션렌지는 자장발생의 코일이 내장되어 있어 상기 코일에 고전압이 인가되면 자장이 유도되고, 이자장이 미치는 영역에 있는 자성체(감응판)가 가열되는 원리를 이용한 것으로, 불꽃이나 유해가스등이 발생되지 않기 때문에 화재의 위험성은 물론 가스를 열원으로 할 때 필연적으로 발생하는 일산화탄소의 발생이 없고 실내 산소의 소모가 없어 쾌적한 실내를 유지할 수 있는 특징이 있으며, 용기를 가열하는 도중에 상판에 손이 닿아도 화상의 우려가 없고 불꽃이 없기 때문에 화재 및 폭발의 위험성이 없으며, 전원이 공급된 상태에서 신체부위가 접촉되어도 손상이 없는 장점을 가지는 등의 효과가 있다.As is well known, an induction stove uses a magnetic field generating coil. When a high voltage is applied to the coil, a magnetic field is induced, and a magnetic material (sensing plate) in the region affected by the magnetic field is heated. Because it does not occur, there is no danger of fire as well as the fact that there is no carbon monoxide inevitably generated when gas is used as a heat source, and there is no consumption of indoor oxygen, and it is possible to maintain a comfortable room. There is no risk of burns or flames because there is no spark, and there is no risk of fire and explosion, and there is an effect that the body parts are not damaged even when the power is supplied.

그리고, 이와같은 장점을 갖는 인덕션렌지는 자성체를 보호할 목적으로 플레이트를 적층하여 고정시킨 후 일반적인 싱크대 및 식탁중앙에 형성할 수 있다.In addition, the induction stove having such an advantage can be formed in the general sink and the table center after laminating and fixing the plate for the purpose of protecting the magnetic material.

따라서, 음식조리시 발생되는 기름이나 양념등의 부산물은 상기 플레이트 표면에 흘러내리면서 냄새를 발생시키는 원인으로 작용하게 된다.Therefore, by-products such as oil or seasonings generated during food cooking flow to the surface of the plate and act as a cause of generating an odor.

또한, 상기 플레이트는 가격이 비싼 고압유리로 형성되어 있으므로 인하여 인덕션렌지의 가격대를 전체적으로 상승시키는 원인으로 작동하게 되는 단점이 있다.In addition, since the plate is formed of high-pressure glass, which is expensive, there is a disadvantage in that it operates as a cause of raising the price range of the induction stove as a whole.

본 고안은 상기와 같은 문제점을 해결하고자 하는 것으로서, 내열 플레이트를 내열성 자기로 형성시키되, 상기 내열 플레이트를 이루는 소지 및 유약 성분에 나노 크기의 은분을 소정량 투입하여 초벌구이 및 본 소성을 통하여 완제품의 플레이트로 형성되는 나노 은분을 함유한 유약 및 소지로 형성된 조리용 내열 플레이트를 제공하는데 그 목적이 있다.The present invention is to solve the above problems, the heat-resistant plate is formed of a heat-resistant porcelain, a predetermined amount of the nano-size silver powder is added to the base and glaze components forming the heat-resistant plate through the first baking and the main plate of the finished product It is an object of the present invention to provide a cooking heat-resistant plate formed of a glaze and a base containing nano silver powder.

상기의 목적을 달성하기 위하여 본 고안은 고순도의 은을 전기분해 장치에서 무광물증류수에 초미립자로 녹인 나노 크기의 은용출액 은분으로 형성시키되, 상기 나노 크기의 은용출액 은분을 플레이트의 재료로 사용되는 소지 및 유약에 투입하여 초벌구이 및 본 소성에 의해 실생활에 사용되는 인덕션렌지 조리용 플레이트를 제공하고자 한다.In order to achieve the above object, the present invention is to form a nano-sized silver eluent silver powder dissolved in high-purity silver in the mineral distilled water in an electrolysis device, but the nano-sized silver eluent silver powder is used as the material of the plate And it is to provide an induction stove cooking plate used in real life by the first baking and the main baking by glazing.

일반적으로 은은 금과 함께 인체에 해가 없는 무해한 물질로 알려진 귀한 광물이다.In general, silver, along with gold, is a rare mineral known to be harmless to humans.

한편, 은을 사용하여 은침이나 은수저등을 만들어 일상생활에 사용 하였을 뿐만 아니라, 한방책자인 동의보감에서는 은이 냉, 경기, 간질 등을 다스린다고 기록되어 있고, 본초강목도 은을 지니면 오장이 편하고 심신이 안정되며 사기를 쪼고 몸을 가볍게하여 수명을 길게한다고 기록하고 있어 은은 사람의 인체에 매우 유익한 광물임을 입증하고 있다.On the other hand, silver was used to make silver needles and silver spoons and used them in everyday life.In addition, in the booklet, Dongbobom, silver is said to control cold, game, and epilepsy. It is stable and has been documented to lengthen life by pecking and lightening the body, and silver has proved to be a very beneficial mineral for the human body.

그러나, 상기와 같은 은은 현재까지 식수를 정제하거나 해독하기 위하여서만 주로 사용되어지고 있었을 뿐으로 은을 초미립자로 분해한 상태에서 이를 섭취하거나 인체에 직접적으로 사용하는 방법이 개발되어지지 못하고 있는 실정이다.However, such silver has been used mainly only to purify or detox drinking water until now, and the situation in which it is ingested in the state in which silver is decomposed into ultrafine particles or used directly in the human body has not been developed.

또한, 지금까지 은에 대하여 알고 있는 것은 막연하게 은이 우리인체에 좋다는 정도이나 은이 어떻게 인체의 건강에 도움을 주는 가에 대하여는 확실한 과학적 근거없이 막연하게 알려지고 있는 것이나, 실제로 은은 650여가지의 세균을 인체에 전혀 독성을 주는일 없이 수분이내에 박멸시켜 병을 치료하게 하는 것으로 그 것은 금속의 은이 직접세균에 작용하는 신진대사에 작용하는 효소에 작용하여 이를 무력화시켜 세균을 막멸시킬 수 있는 것이다.In addition, what is known about silver so far is vaguely known without any clear scientific basis on the extent to which silver is good for our bodies and how it helps health of the human body. It treats the disease by eradicating it within a few minutes without toxic to the human body. It means that silver of the metal acts on the enzyme that acts on the metabolism that acts directly on the bacteria and can neutralize the bacteria.

이러한 작용을 하는 원리에 따라 은이온을 효과적으로 이용하는 방법에 있어서, 아직 인덱션렌지 조리용 플레이트에 적용하지 못하는 문제가 있다.In the method of effectively using the silver ions according to the principle of this action, there is a problem that can not be applied to the cooking plate for the index range yet.

한편, 일반적으로 사용되는 인덕션렌지 조리용 플레이트는 내열성이 높고, 가열과 냉각을 반복 수축성이 적어야만 직화등에 의한 조리시 균열이 가지 않기 때문에 내열성 소지를 사용하고자 한다.On the other hand, generally used induction stove cooking plate has a high heat resistance, and the heating and cooling should be less than the shrinkage of the repeated shrinkage when cooking due to direct fire, etc. to use the heat-resistant base material.

상기와 같은 인덕션렌지 조리용 플레이트의 소지 원료는 고령토나 점토, 산청토, 페타라이트의 무기물질을 혼합 반죽한 소지를 가마에서 고열로 소성하여 성형 제조하게 된다.The raw material of the induction stove cooking plate as described above is molded and manufactured by firing at a high temperature in a kiln a mixture of the kaolin, clay, acid blue soil, and the inorganic material of the petrilite.

그리고, 상기와 같이 초벌구이된 내열 플레이트는 유약을 도포한 후, 재벌구이 하는 방식이며, 상기에 이용되는 유약성분은 통상적으로 엽장석, 활석, 칼리장석, 석회석, 알루미나, 규석 등을 혼합하여 사용하게 된다.And, as described above, the first heat-resistant plate is a method of roasting chaebol after applying glaze, the glaze components used above are commonly used to mix the foliate, talc, kalifeldspar, limestone, alumina, quartzite, etc. do.

이하, 본 고안의 바람직한 실시예를 첨부된 도면에 의하여 상세하게 설명하면 다음과 같다.Hereinafter, described in detail by the accompanying drawings a preferred embodiment of the present invention as follows.

도 1은 본 고안의 요부가 형성된 상태의 사시도이며, 도 2는 본 고안의 요부를 발췌하여 확대한 상태의 단면도이다.1 is a perspective view of a state in which the main part of the present invention is formed, and FIG. 2 is a cross-sectional view of an enlarged state extracting the main part of the present invention.

먼저, 은분은 전기분해장치를 사용하여 얻을 수 있으며, 상기 전기분해장치에는 일정량의 무광물증류수를 담고 두개의 고순도 순은 막대를 삽입설치하고 순은 막대에 직류전기를 인가하여 주면 전류에 의하여 순은이 전기분해되어 무광물증류수에 초미립자로 녹아서 용해된 순은용출액 은분을 얻을 수 있다.First, silver powder can be obtained by using an electrolysis device. The electrolysis device contains a certain amount of mineral distilled water, and is installed by inserting two high purity pure silver bars and applying direct current electric current to the pure silver bars. Pure silver eluate silver powder dissolved and dissolved as ultra fine particles in mineral distilled water can be obtained.

그리고, 전기분해장치에는 막대로 된 순은을 무광물증류수가 담겨진 용기내에 서로 마주보도록 두개를 넣어 설치하고 전류를 공급하는 입력단자와 막대로 된 순은을 연결하여 놓으므로 무광물증류수에 고순도의 순은이 전기분해되면서 초미립자의 은용출액이 녹아 들 수 있게 구성하였다.In the electrolysis device, two rods of pure silver are placed to face each other in a container containing mineral distilled water, and an input terminal for supplying current and a rod of pure silver are connected to each other so that high purity pure silver is added to the mineral distilled water. As the electrolysis, the silver eluate of the ultrafine particles was dissolved.

상기와 같이 만들어진 은용출액은 나노 크기의 은분으로 형성될 수 있으며, 이를 인덕션렌지 조리용 내열 플레이트를 성형시키고자 하는 소지에 투입하여 혼합시킬 수 있는 구성이다.The silver eluate made as described above may be formed of silver powder having a nano size, and may be mixed by adding the same to a base to be molded into a heat resistant plate for induction stove cooking.

또한, 상기 은용출액 은분은 유액성분에 투입하므로 인하여 유약성분에도 나노크기의 은분을 혼합할 수 있다.In addition, since the silver eluate silver powder is added to the emulsion component, it is possible to mix nano-sized silver powder to the glaze component.

한편, 은분과 일체로 혼합되는 내열 플레이트의 소지 조성물은 엽장석, 활석, 회색점토로 구성된다.On the other hand, the holding composition of the heat-resistant plate mixed with the silver powder is composed of feldspar, talc, gray clay.

그리고, 유약 조성물은 엽장석, 활석, 흑색점토, 석회석에 나노 크기의 은분을 일체로 혼합하게 된다.In addition, the glaze composition is a mixture of nano-sized silver powder integrally with feldspar, talc, black clay, limestone.

또한, 이와 같은 구성으로 인덕션렌지 조리용 내열 플레이트를 성형시킨 후, 초벌구이 한 후, 다시 재벌구이하는 방식이다.In addition, after forming the heat-resistant plate for induction stove cooking in such a configuration, after the first roasting, the method is roasted again.

그리고, 초벌구이된 내열 플레이트 표면에 유약을 도포한 후, 재벌구이 하므로 인하여 플레이트의 내부와 표면에는 나노 크기의 은분이 다량 함유될 수 있는 구성이다.Then, after applying the glaze on the surface of the first-heated grill plate, because the chaebol is formed, the inside and the surface of the plate may contain a large amount of silver powder.

상기와 같은 구성으로 이루어진 본 고안의 작용과 효과를 상세히 설명하면 다음과 같다.Referring to the operation and effects of the present invention made in the above configuration in detail as follows.

먼저, 본 고안은 전기분해장치에 의하여 분해되어 무광물증류수에 녹아 있는 고순도 초미립자의 나노 크기 은용출액 은분은 본 고안을 이루는 인덕션렌지 조리용 내열 플레이트의 소지 내부에 투입하여 일체로 혼합하게 된다.First, the present invention is decomposed by an electrolysis device, the nano-sized silver eluate silver powder of high purity ultra-fine particles dissolved in the mineral distilled water is put into the body of the heat-resistant plate for cooking induction stove constituting the present invention is mixed integrally.

한편, 상기 내열 플레이트를 일반적인 식탁위에 적층되는 유리판의 대용으로 형성시킬 수 있으며, 또한 상기 식탁위에 고정되는 플레이트는 인덕션렌지에 형성된 코일에 고전압이 인가되어 자성체를 가열하는데 이무런 영향을 미치지 않게 된다.On the other hand, the heat-resistant plate can be formed as a substitute for the glass plate laminated on a general table, and the plate fixed on the table is a high voltage is applied to the coil formed on the induction stove does not have any effect on heating the magnetic material.

그리고, 상기 인덕션렌지 조리용 내열 플레이트는 은분이 함유된 소지로 성형시킨 후, 이를 초벌구이하고 다음으로 유약으로 코팅하게 된다.In addition, the induction stove cooking heat-resistant plate is molded into a base containing silver powder, and then first roasted and coated with glaze.

이때, 유악성분에도 초미립자의 나노 크기 은분을 투입하므로 인하여 유약이 코팅되는 내열 플레이트 표면 전체에 은분이 코팅될 수 있다.At this time, the silver powder may be coated on the entire surface of the heat-resistant plate on which the glaze is coated because the nano-size silver powder of the ultrafine particles is added to the toxic component.

이와 같이 코팅된 인덕션렌지 조리용 플레이트는 다시 재벌구이 하므로 인하여 내열 플레이트 표면과 그 내부에는 나노 크기의 은분이 다량함유될 수 있는 것이다.Since the induction stove cooking plate coated as described above is chaebol again, the heat-resistant plate surface and the inside may contain a large amount of nano-sized silver powder.

따라서, 본 고안의 인덕션렌지 조리용 내열 플레이트 표면과 그 내부에는 은분이 코팅성형됨으로써, 은분이 갖고 있는 자체 특성으로 인하여 향균 방취의 효과를 얻을 수 있다.Therefore, the silver powder is coated on the surface of the induction stove cooking heat plate and the inside of the present invention, and thus, the effect of antibacterial deodorization can be obtained due to its own characteristics.

그리고, 본 고안은 나노 은분을 함유한 유약이 도포된 내열 플레이트는 그 형성 및 모양의 변형이 가능하며 특히, 본 고안은 상술한 실시예에 한정되지 아니하며, 청구범위에서 청구한 본 고안의 요지를 벗어남이 없이 본 고안이 속하는 기술분야에서 통상의 지식을 가진 자라면 다양한 변형 실시가 가능한 것임은 물론이고, 그와 같은 변경은 본 고안의 청구범위 내에 있게 되는 것은 당연하다.In addition, the present invention is a heat-resistant plate coated with a glaze containing nano silver powder can be modified in its formation and shape, in particular, the present invention is not limited to the above-described embodiment, the subject matter of the present invention claimed in the claims Those skilled in the art to which the present invention pertains without departing from the various modifications can be made, of course, such changes are naturally within the scope of the claims of the present invention.

이상에서 설명한 바와 같이 은을 함유한 유약을 인덕션렌지 조리용 플레이트 표면에 도포하므로 항균력과 살균력은 발생하게 되면서 내열 플레이트 표면에 기생하는 각종 세균을 효과적으로 살균함은 물론, 내열 플레이트 표면의 각종 오염물질을 제거하며, 또한 음식조리 후 보관시 각종 세균물로 부터 오염을 예방하는 구조로 사용의 편리성과 별도의 유지보수에 소요되는 비용 없이 사용할 수 있는 특징이 있다.As described above, the silver-containing glaze is applied to the surface of the induction stove cooking plate, so that antibacterial and bactericidal properties are generated, as well as effectively sterilizing various parasitic bacteria on the surface of the heat-resistant plate. Also, it is a structure that prevents contamination from various germs when food is stored after cooking, and is characterized by convenience of use and no cost for separate maintenance.

도 1은 본 고안의 요부가 형성된 상태의 사시도1 is a perspective view of the main portion formed state of the present invention

도 2는 본 고안의 요부를 발췌하여 확대한 상태의 단면도Figure 2 is an enlarged cross-sectional view of the main portion of the subject innovation

* 도면의 주요 부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings

10. 인덕션렌지 11. 내열 플레이트10. Induction stove 11. Heat resistant plate

12. 은븐 13. 유약 코팅부12. ENVEN 13. Glaze Coating

Claims (2)

고순도의 은을 전기분해장치에 의해 초미립자로 녹여 나노 크기의 은용출액 은분으로 형성시키되, 상기 나노 크기의 은용출액 은분을 인덕션렌지 조리용 내열 플레이트의 재료로 사용되는 소지 및 유약에 투입한 후, 초벌구이 및 본 소성의 재벌구이에 의해 생활에 사용되는 내열 플레이트로 형성시킬 수 있도록 구성함을 특징으로 하는 나노 은분을 함유한 유약 및 소지로 형성된 인덕션렌지 조리용 내열 플레이트High-purity silver is melted into ultra-fine particles by an electrolysis device to form nano-sized silver eluate silver powder, and the nano-sized silver eluate silver powder is added to the base and glaze used as a material of a heat-resistant plate for induction stove cooking. And heat-resistant plates for cooking induction stoves formed of glazes and substrates containing nano silver powder, which are configured to be formed into heat-resistant plates used for living by chaebol roasting 제 1항에 있어서,The method of claim 1, 상기 내열 플레이트 표면 전체에 나노 은분이 함유된 유약으로 코팅시킴과 아울러 식탁위에 올려지는 상판으로 형성시킬 수 있도록 구성함을 특징으로 하는 나노 은분을 함유한 유약 및 소지로 형성된 인덕션렌지 조리용 내열 플레이트Induction stove cooking heat-resistant plate formed of glaze and the base containing nano silver powder, characterized in that the coating on the entire surface of the heat-resistant plate containing nano silver powder and formed as a top plate placed on the table
KR20-2005-0012357U 2005-04-30 2005-04-30 Silver heat resistance ceramic kaolin a plate KR200391443Y1 (en)