KR200303092Y1 - Glass for decoration incorporated with synthetic resin film on which hologram pattern or aluminum layer is partially formed - Google Patents
Glass for decoration incorporated with synthetic resin film on which hologram pattern or aluminum layer is partially formed Download PDFInfo
- Publication number
- KR200303092Y1 KR200303092Y1 KR20-2002-0032184U KR20020032184U KR200303092Y1 KR 200303092 Y1 KR200303092 Y1 KR 200303092Y1 KR 20020032184 U KR20020032184 U KR 20020032184U KR 200303092 Y1 KR200303092 Y1 KR 200303092Y1
- Authority
- KR
- South Korea
- Prior art keywords
- film
- synthetic resin
- decorative
- pattern
- glass
- Prior art date
Abstract
홀로그램 증착면이 부분적으로 박리된 합성수지 필름을 삽입하여 심미감을 향상시킨 장식용 접합유리가 개시된다. 상기 장식용 접합 유리는 상호 대향하는 상부 및 하부 유리판재 사이에, 하부 접착용 필름, 소정의 무늬가 형성된 장식용 필름 및 상부 접착용 필름이 순차적으로 접합된 구조를 가지며, 상기 장식용 필름은 합성수지 기재층; 상기 합성수지 기재층의 일면에 형성되어 있으며, 소정 형상의 무늬를 가지는 알루미늄막; 및 상기 알루미늄막의 상부에 형성되어 있는 인쇄층을 포함한다.Disclosed is a decorative laminated glass in which a synthetic resin film having a holographic deposition surface partially peeled off is inserted to improve aesthetics. The decorative laminated glass has a structure in which a lower adhesive film, a decorative film having a predetermined pattern is formed, and an upper adhesive film are sequentially bonded between the upper and lower glass plates facing each other, and the decorative film includes a synthetic resin base layer; An aluminum film formed on one surface of the synthetic resin substrate layer and having a predetermined pattern; And a printing layer formed on the aluminum film.
Description
본 고안은 장식용 접합유리에 관한 것으로서, 더욱 상세하게는 홀로그램 금속막 또는 알루미늄 금속막이 부분 증착된 합성수지 필름을 삽입하여 심미감을 향상시킨 장식용 접합유리에 관한 것이다.The present invention relates to a decorative laminated glass, and more particularly to a decorative laminated glass to improve the aesthetics by inserting a holographic metal film or a synthetic resin film is partially deposited aluminum metal film.
판유리는 평활성(平滑性)이 우수하고, 투시상 및 반사상을 얻을 수 있기 때문에 일반 건축물을 비롯하여, 점포, 주택, 고층 건축물 등의 내·외장재로 널리 사용되고 있으나, 그 자체로는 심미적, 장식적 기능이 부족하다. 따라서 장식적 기능이 요구되는 경우에는 판유리 표면을 식각하여 특정 형상이나 무늬를 형성하거나, 장식적 무늬가 형성된 합성수지 필름을 판유리의 표면에 부착하는 방법이 사용되어 왔다. 그러나 유리 표면을 식각하는 방법은 생산성이 낮고, 고비용이 요구될 뿐만 아니라, 다양한 무늬를 형성하기 어려운 단점이 있고, 판유리의 표면에 장식적 무늬가 형성된 합성수지 필름을 부착하는 방법은 외부로 노출된 합성수지 필름이 변질 또는 변형될 우려가 있고, 고급스러운 느낌을 부여하지 못하는 단점이 있다.Plate glass is widely used for interior and exterior materials of general buildings, stores, houses, high-rise buildings, etc. because it has excellent flatness and obtains a perspective image and a reflection image, but it is an aesthetic and decorative function in itself. This is lacking. Therefore, when a decorative function is required, a method of etching a sheet glass surface to form a specific shape or pattern, or attaching a synthetic resin film having a decorative pattern to the surface of the plate glass has been used. However, the method of etching the glass surface is not only low productivity, high cost, but also difficult to form a variety of patterns, and the method of attaching a decorative patterned synthetic resin film on the surface of the plate glass is a synthetic resin exposed to the outside There is a fear that the film is deteriorated or deformed, there is a disadvantage that does not give a luxurious feeling.
이와 같은 단점을 개선하기 위한 장식용 접합유리가 대한민국 특허공개 1999-60551호에 개시되어 있다. 도 1은 상기 문헌에 개시된 장식용 접합유리의 분해 사시도로서, 도 1에 도시된 바와 같이, 종래의 장식용 접합유리(7)는 상호 대향하는 상부 및 하부 유리판재(1, 2) 사이에, 하부 접착용 필름(3), 소정의 무늬가 프린팅된 장식용 필름(4) 및 상부 접착용 필름(5)을 순차적으로 개재시키고, 이들을 가열 압착함으로서 제조된다. 여기서 상기 장식용 필름(4)는 폴리에틸렌계 합성수지 필름에 산수화 등 소정의 모양으로 인쇄 잉크를 프린트한 것이다. 이와 같이 제조된 장식용 접합유리(7)는 장식용 필름(4)의 양면이 상부 및 하부 유리판재(1, 2)에 의하여 보호되므로, 장식용 필름(4)이 변형 또는 변색될 우려가 없으나, 상기 장식용 필름(4)에 형성된 무늬는 잉크를 인쇄하여 이루어지는 것이므로, 인쇄가 불가능한 무늬 또는 재질, 예를 들면 알루미늄막 등의 금속막을 미세하게 가공하여 이루어진 무늬 또는 홀로그램 패턴이 형성된 무늬를 가지는 장식용 필름(4)를 제조하는 것은 곤란하다.Decorative laminated glass for improving such a disadvantage is disclosed in Korean Patent Laid-Open No. 1999-60551. 1 is an exploded perspective view of the decorative laminated glass disclosed in the above document, as shown in FIG. 1, a conventional decorative laminated glass 7 has a bottom adhesive between upper and lower glass plates 1 and 2 facing each other. The film 3 for printing, the decorative film 4 on which the predetermined | prescribed pattern was printed, and the upper adhesion film 5 are interposed sequentially, and these are manufactured by heat-pressing. Here, the decorative film 4 is a printing ink printed on a polyethylene synthetic resin film in a predetermined shape such as acidification. Since the decorative laminated glass 7 manufactured as described above is protected by both the upper and lower glass plate materials 1 and 2 of the decorative film 4, the decorative film 4 may not be deformed or discolored. Since the pattern formed on the film 4 is formed by printing ink, the decorative film 4 having a pattern formed by printing a pattern or material which cannot be printed, for example, a metal film such as an aluminum film, or a pattern formed by a hologram pattern is finely formed. It is difficult to manufacture.
따라서, 본 고안의 목적은 단순한 인쇄 공정으로는 형성할 수 없는 알루미늄막 무늬 또는 홀로그램 패턴을 가지는 소정 형상의 무늬를 나타내는 장식용 접합유리를 제공하는 것이다.Accordingly, an object of the present invention is to provide a decorative laminated glass exhibiting a pattern of a predetermined shape having an aluminum film pattern or a hologram pattern that cannot be formed by a simple printing process.
본 고안의 다른 목적은 알루미늄막 또는 홀로그램막에 장식 무늬를 형성하여, 심미감을 향상시킨 장식용 접합유리를 제공하는 것이다.Another object of the present invention is to provide a decorative laminated glass by forming a decorative pattern on the aluminum film or hologram film, thereby improving the aesthetics.
도 1은 통상적인 장식용 접합유리의 분해 사시도.1 is an exploded perspective view of a conventional decorative laminated glass.
도 2a 내지 도 2c는 본 고안에 따른 장식용 접합유리에 사용되는 장식용 필름의 제조 공정도.2a to 2c is a manufacturing process of the decorative film used in the decorative laminated glass according to the present invention.
도 3은 본 고안의 일 실시예에 따른 장식용 접합유리의 분해사시도.Figure 3 is an exploded perspective view of a decorative laminated glass according to an embodiment of the present invention.
상기 목적을 달성하기 위하여, 본 고안은 상호 대향하는 상부 및 하부 유리판재 사이에, 하부 접착용 필름, 소정의 무늬가 형성된 장식용 필름 및 상부 접착용 필름이 순차적으로 접합된 구조를 가지는 장식용 접합유리에 있어서, 상기 장식용 필름은 합성수지 기재층; 상기 합성수지 기재층의 일면에 형성되어 있으며, 소정 형상의 무늬를 가지는 알루미늄막; 및 상기 알루미늄막의 상부에 형성되어 있는 인쇄층을 포함하는 장식용 접합 유리를 제공한다. 여기서, 상기 알루미늄막에는 홀로그램 패턴이 형성되어 있는 것이 바람직하며, 상기 합성수지 기재층은 폴리에스테르 필름, 폴리비닐클로라이드 필름, 폴리에틸렌 필름, 또는 폴리프로필렌 필름으로 이루어질 수 있다.In order to achieve the above object, the present invention is a decorative laminated glass having a structure in which a lower adhesive film, a decorative film having a predetermined pattern is formed, and a top adhesive film are sequentially bonded between the upper and lower glass plates facing each other. In the above, the decorative film is a synthetic resin substrate layer; An aluminum film formed on one surface of the synthetic resin substrate layer and having a predetermined pattern; And it provides a decorative laminated glass comprising a printing layer formed on top of the aluminum film. Here, the aluminum film is preferably a hologram pattern is formed, the synthetic resin substrate layer may be made of a polyester film, polyvinyl chloride film, polyethylene film, or polypropylene film.
이하, 첨부된 도면을 참조하여 본 고안을 상세히 설명한다. 본 고안의 설명에 있어서, 패턴은 알루미늄막의 표면에 형성된 모양을 의미하는 것이며, 무늬는 알루미늄막의 외관이 이루는 모양을 의미한다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings. In the description of the present invention, the pattern means a shape formed on the surface of the aluminum film, and the pattern means a shape formed by the appearance of the aluminum film.
도 2a 내지 도 2c는 본 고안의 장식용 접합유리에 사용되는 장식용 필름의 제조 공정도이다. 본 고안의 장식용 접합유리에 사용되는 장식용 필름을 제조하기 위해서는, 먼저 도 2a에 도시된 바와 같이, 투명한 합성수지 기재층(10)의 상부에 알루미늄막(12)을 형성하여 원단(14)을 제조한다. 상기 합성수지 기재층(10)은 상부에 형성되는 알루미늄막(12)의 패턴 및 무늬가 기재층(10)을 통하여 투시될 수 있도록, 투명하고 강도가 우수한 합성수지 필름으로 이루어지며, 필요에 따라서는 유색의 반투명한 필름으로 이루어질 수도 있다. 이와 같은 투명한 합성수지 기재층(10)은, 예를 들면 투명한 폴리에스테르(Polyethyleneterephthalate: PET) 필름, 폴리비닐클로라이드(Polyvinylchloride: PVC) 필름, 폴리에틸렌(Polyethylene: PE) 필름, 폴리프로필렌(Polypropylene: PP) 필름 등으로 이루어질 수 있으며, 바람직하게는 폴리에스테르(PET) 필름으로 이루어진다. 상기 합성수지 기재층(10)의 상부에 형성된 알루미늄막(12)에는 홀로그램 패턴 등 소정의 패턴이 형성되어 있을 수 있다. 상기 알루미늄막(12)은 증착, 코팅, 접착 등 통상의 방법으로 상기 합성수지 기재층(10)의 상부에 부착되며, 홀로그램 문양 등 패턴이 형성된알루미늄막(12)의 경우에는, 먼저 합성수지 기재층(10)의 상부에 알루미늄막(12)을 형성하고, 홀로그램 패턴을 가지도록 알루미늄막(12)을 가공할 수도 있으며, 홀로그램 패턴이 형성된 알루미늄막(12)을 상기 합성수지 기재층(10)에 부착할 수도 있다. 이때, 사용되는 합성수지 기재층(10) 및 알루미늄막(12)의 두께 및 크기는 합성수지 필름의 재질, 형성하고자 하는 무늬 등에 따라 적절히 선정할 수 있다.2a to 2c is a manufacturing process diagram of the decorative film used in the decorative laminated glass of the present invention. In order to manufacture the decorative film used in the decorative laminated glass of the present invention, as shown in Figure 2a, to prepare a fabric 14 by forming an aluminum film 12 on top of the transparent synthetic resin substrate layer (10). . The synthetic resin base layer 10 is made of a transparent and excellent strength of the synthetic resin film, so that the pattern and pattern of the aluminum film 12 formed thereon can be seen through the base layer 10, if necessary, colored It may also be made of a translucent film. The transparent synthetic resin base layer 10 may be, for example, a transparent polyester (PET) film, a polyvinyl chloride (PVC) film, a polyethylene (PE) film, a polypropylene (PP) film Or the like, and preferably, a polyester (PET) film. A predetermined pattern, such as a hologram pattern, may be formed on the aluminum film 12 formed on the synthetic resin substrate layer 10. The aluminum film 12 is attached to the upper portion of the synthetic resin substrate layer 10 by a conventional method such as deposition, coating, adhesion, in the case of the aluminum film 12 having a pattern such as a hologram pattern, first, the synthetic resin substrate layer ( The aluminum film 12 may be formed on the upper part 10, and the aluminum film 12 may be processed to have a hologram pattern. The aluminum film 12 having the hologram pattern may be attached to the synthetic resin substrate layer 10. It may be. At this time, the thickness and size of the synthetic resin substrate layer 10 and the aluminum film 12 to be used may be appropriately selected according to the material of the synthetic resin film, the pattern to be formed.
다음으로, 도 2b에 도시된 바와 같이, 상기 투명한 합성수지 기재층(10)에 부착된 알루미늄막(12)의 상부에 소정 형상의 무늬를 가지는 인쇄층(16)을 형성한다. 상기 인쇄층(16)은 추후의 알루미늄막(12) 박리공정에서, 인쇄층(16) 하부의 알루미늄막(12)이 박리되지 않도록 보호할 뿐만 아니라, 인쇄층(16) 하부의 알루미늄막(12)이 대기와 반응하여 산화되는 것을 방지하는 기능을 한다. 상기 인쇄층(16)은 통상의 인쇄 매체를 이용하여 형성할 수 있으며, 바람직하게는 실크스크린 인쇄법, 그라비아 인쇄법 등으로 형성할 수 있다. 실크스크린 인쇄법은 공판화(孔版畵) 기법이라고도 알려져 있으며, 실크, 나일론 등으로 스크린을 만든 다음, 인쇄하고자 하는 무늬 이외의 부분에 풀을 칠하거나, 얇은 필름을 붙이고, 스크린 상부에 잉크를 올린 다음, 스퀴즈를 이용하여 압착하면, 풀 또는 필름이 붙어 있지 않은 부분으로 잉크가 새어나와, 하부의 기재층이 인쇄되도록 하는 것으로서, 특수한 문양의 합성수지 필름을 소량, 주문 제작하는 경우에 바람직하지만, 연속공정으로 합성수지 필름을 제조할 수 없는 단점이 있다. 그라비아 인쇄법은 원통형 인쇄동판에 소정 형상의 무늬를 음각으로 형성하고 상기 음각된 무늬에 인쇄용 잉크를 공급하면서, 상기 인쇄동판의 하부로 인쇄기재를 통과시켜, 기재상에 원하는 모양을 인쇄하는 것으로서, 반복되는 무늬를 기재층에 인쇄하는 경우, 대량, 연속 공정으로 인쇄를 수행할 수 있는 장점이 있다. 이와 같은 실크스크린 인쇄법 또는 그라비아 인쇄법을 사용함으로서 원하는 무늬를 정밀하게 형성할 수 있으며(대략, 40선의 망점을 가지는 무늬의 형성이 가능하다), 대량 생산이 가능하게 된다. 상기 인쇄층(16)은 알루미늄막(12) 박리액에 대하여 박리되지 않는 성질을 가지는 고형 인쇄잉크 성분을 시클로헥사논 등의 용제에 용해시켜 사용할 수 있으며, 또한 안료 등을 혼합하여 특정의 색상을 가질 수도 있고, 필요에 따라 무색의 투명한 인쇄잉크를 사용하여 상기 인쇄층(16)을 형성할 수도 있다.Next, as shown in FIG. 2B, a printing layer 16 having a pattern of a predetermined shape is formed on the aluminum film 12 attached to the transparent synthetic resin substrate layer 10. The print layer 16 not only protects the aluminum film 12 under the print layer 16 from being peeled off in a subsequent aluminum film 12 peeling step, but also protects the aluminum film 12 under the print layer 16. ) Reacts with the atmosphere to prevent oxidation. The printing layer 16 may be formed using a conventional printing medium, and preferably, may be formed by a silkscreen printing method, a gravure printing method, or the like. Silkscreen printing is also known as the stencil technique, and the screen is made of silk, nylon, etc., and then glued, thin film, or ink on top of the screen other than the pattern to be printed. Next, using a squeeze to squeeze, the ink is leaked to the portion where the glue or film is not attached, and the lower base layer is printed, which is preferable when a small amount of a special patterned synthetic resin film is made to order. There is a disadvantage in that a synthetic resin film cannot be manufactured by the process. The gravure printing method is to form a pattern of a predetermined shape on a cylindrical copper plate by engraving and supplying printing ink to the engraved pattern, while passing a printing material through the lower portion of the copper plate to print a desired shape on the substrate, When printing a repeating pattern on the base layer, there is an advantage that can be performed in a large amount, continuous process. By using such a silkscreen printing method or gravure printing method, a desired pattern can be precisely formed (approximately, a pattern having a dot dot of 40 lines can be formed), and mass production is possible. The printing layer 16 may be used by dissolving a solid printing ink component having a property of not being peeled off with respect to the aluminum film 12 peeling liquid in a solvent such as cyclohexanone. The printing layer 16 may be formed using a colorless and transparent printing ink as necessary.
이와 같이, 소정 형상의 무늬를 가지는 인쇄층(16)을 형성한 후, 도 2c에 도시된 바와 같이, 인쇄층(16)이 형성되지 않은 개방된 영역의 알루미늄막(12)을 박리한다. 이와 같은 박리공정은 인쇄층(16)이 형성된 필름을 박리액에 침지시켜 이루어지는 것이 바람직하다. 이때 사용하는 박리액은 인쇄층(16)은 박리시키지 않으며, 알루미늄막(12)을 박리시키는 성질을 가지는 글리세린, 가성소다 등을 사용할 수 있다. 인쇄층(16)이 형성되지 않은 부분의 알루미늄막(12)이 박리되면, 필요에 따라 박리액을 세정하고, 건조하여 장식용 필름을 완성한다. 이와 같이 제조된 장식용 필름에 형성된 알루미늄막 무늬 또는 홀로그램 패턴을 가지는 소정 형상의 무늬는 통상의 인쇄법 만으로는 형성할 수 없는 것으로서, 추후 설명되는 바와 같이 접합 유리사이에 개재되어 심미감이 우수한 장식용 접합유리를 구성한다.As described above, after the printing layer 16 having a predetermined pattern is formed, the aluminum film 12 in the open area in which the printing layer 16 is not formed is peeled off, as shown in FIG. 2C. It is preferable that such peeling process is made by immersing the film in which the printing layer 16 was formed in peeling liquid. The peeling liquid used at this time does not peel the printing layer 16, and can use glycerin, caustic soda, etc. which have the property which peels the aluminum film 12. When the aluminum film 12 of the part in which the printing layer 16 is not formed is peeled off, a peeling liquid is wash | cleaned and needed as needed, and a decorative film is completed. The pattern of a predetermined shape having an aluminum film pattern or a hologram pattern formed on the decorative film manufactured as described above cannot be formed only by a conventional printing method, and as described later, decorative laminated glass having excellent aesthetics as interposed between laminated glass. Configure
도 3은 이와 같이 제조한 장식용 필름을 포함하는 장식용 접합유리의 분해사시도이다. 도 3에 도시한 바와 같이, 본 고안에 따른 일 실시예에 따른 장식용 접합 유리(20)는 상호 대향하는 상부 및 하부 유리판재(22, 24) 사이에, 하부 접착용 필름(28), 소정의 무늬(34)가 형성된 장식용 필름(30) 및 상부 접착용 필름(26)이 순차적으로 접합된 구조를 가지며, 상기 장식용 필름(30)은 합성수지 기재층(10); 상기 합성수지 기재층(10)의 일면에 형성되어 있으며, 소정 형상의 무늬(34)를 가지는 알루미늄막(12); 및 상기 알루미늄막(12)의 상부에 형성되어 있는 인쇄층(16)을 포함한다. 또한 상술한 바와 같이, 상기 알루미늄막(12)에는 홀로그램 패턴(32)가 형성되어 있는 것이 바람직하다. 상기 상부 및 하부 유리판재(22, 24)로는 통상의 유리판재를 사용하고, 필요에 따라 곡면 가공을 하여 사용할 수도 있으며, 상기 하부 및 상부 접착용 필름(28, 26)은 상부 및 하부 유리판재(22, 24) 사이에 장식용 필름(30)을 개재시켜 접착할 수 있는 것으로서, 대표적으로는 에틸렌 비닐아세테이트 공중합체(ethylene vinyl acetate co-polymer)를 사용할 수 있다. 본 고안에 따른 장식용 접합 유리(20)는 하부 유리판재(24), 하부 접착용 필름(28), 장식용 필름(30), 상부 접착용 필름(26) 및 상부 유리판재(22)를 순차적으로 접합한 후, 가열 압착, 예를 들면 90℃, 12Kg/cm2의 압력에서 30 내지 40분간 가열한 뒤 냉각하여 제조할 수 있다.Figure 3 is an exploded perspective view of a decorative laminated glass comprising a decorative film prepared in this way. As shown in Figure 3, the decorative laminated glass 20 according to an embodiment of the present invention, the lower adhesive film 28, the predetermined between the upper and lower glass plate members 22, 24 facing each other The decorative film 30 on which the pattern 34 is formed and the upper adhesive film 26 are sequentially bonded, and the decorative film 30 includes a synthetic resin substrate layer 10; An aluminum film 12 formed on one surface of the synthetic resin substrate layer 10 and having a pattern 34 of a predetermined shape; And a printing layer 16 formed on the aluminum film 12. As described above, it is preferable that the hologram pattern 32 is formed on the aluminum film 12. As the upper and lower glass plate materials 22 and 24, a conventional glass plate material may be used, and if necessary, curved glass may be used, and the lower and upper adhesive films 28 and 26 may be formed of upper and lower glass plate materials ( 22, 24, which can be adhered to each other via the decorative film 30, typically ethylene vinyl acetate copolymer (ethylene vinyl acetate co-polymer) can be used. The decorative laminated glass 20 according to the present invention is sequentially bonded to the lower glass plate 24, the lower adhesive film 28, the decorative film 30, the upper adhesive film 26 and the upper glass plate 22 After that, it may be prepared by heating and pressing, for example, heating for 30 to 40 minutes at a temperature of 90 ° C. and 12 Kg / cm 2 , followed by cooling.
이와 같은 본 고안에 따른 장식용 접합 유리(20)은 알루미늄막(12)의 무늬(34) 및/또는 알루미늄막(12)에 형성된 홀로그램 패턴(32)에 의하여 종래의 장식 유리와는 차별화되는 심미감을 나타내게 되는데, 예를 들면 장식용 필름(30)의 알루미늄막(12)에 홀로그램(32) 패턴을 형성하고, 중앙부분의 알루미늄막(12)이 제거되는 형태로 무늬(34)를 형성하는 경우, 접합 유리(20) 밖의 경치가 가장자리에 형성된 홀로그램(32) 패턴에 의하여 둘러싸여 보이는 등의 환상적인 분위기를 연출하는 것이 가능하다. 또한 알루미늄막(12)에서 반사된 빛은 산란되므로 무지개빛 심미감을 줄수도 있다.The decorative laminated glass 20 according to the present invention has a esthetic sense that is different from the conventional decorative glass by the pattern 34 of the aluminum film 12 and / or the hologram pattern 32 formed on the aluminum film 12. For example, when the hologram 32 pattern is formed on the aluminum film 12 of the decorative film 30 and the pattern 34 is formed in such a manner that the aluminum film 12 in the center portion is removed, the bonding is performed. It is possible to produce a fantastic atmosphere such as the view outside the glass 20 is surrounded by the hologram 32 pattern formed at the edge. In addition, since the light reflected from the aluminum film 12 is scattered, it may give an iridescent aesthetic.
이상 상술한 바와 같이, 본 고안에 따른 장식용 접합유리는 단순한 인쇄 공정으로는 형성할 수 없는 알루미늄막 무늬 또는 홀로그램 패턴을 가지는 소정 형상의 무늬를 나타내어 심미감을 향상시키고, 환상적인 분위기를 연출할 수 있다. 본 고안에 따른 장식용 접합유리는 일반 건축물을 비롯하여, 점포, 주택, 고층 건축물 등의 내·외장재로 널리 활용할 수 있다.As described above, the decorative laminated glass according to the present invention exhibits a pattern of a predetermined shape having an aluminum film pattern or a hologram pattern that cannot be formed by a simple printing process, thereby improving aesthetics and creating a fantastic atmosphere. Decorative laminated glass according to the present invention can be widely used as interior and exterior materials, such as stores, houses, high-rise buildings, including general buildings.
Claims (3)