KR20020034502A - 모르타르 조성물 및 이것으로 구성된 벽돌 - Google Patents
모르타르 조성물 및 이것으로 구성된 벽돌 Download PDFInfo
- Publication number
- KR20020034502A KR20020034502A KR1020000064882A KR20000064882A KR20020034502A KR 20020034502 A KR20020034502 A KR 20020034502A KR 1020000064882 A KR1020000064882 A KR 1020000064882A KR 20000064882 A KR20000064882 A KR 20000064882A KR 20020034502 A KR20020034502 A KR 20020034502A
- Authority
- KR
- South Korea
- Prior art keywords
- parts
- weight
- mortar composition
- brick
- mortar
- Prior art date
Abstract
본 발명은 모르타르 조성물 및 이것으로 제조된 벽돌에 관한 것으로서 특히, 광산의 광물 선광 과정에서 배출되는 광물의 분말들을 배합하여 조성함으로서 광물들로부터 발생되는 원적외선의 방사에 따른 인체의 신진 대사 촉진과 방음 및 항균 효과를 얻을 수 있는 모르타르 조성물과 이에 의해 이루어진 벽돌에 관한 것이다.
이러한 본 발명은 광물의 선광 과정으로부터 배출된 견운모 90~110중량부에 알루미나시멘트15~25중량부, 황토200~300중량부 및 숯가루 0.1~0.2중량부를 혼합한 후, 혼합된 분말에 8~12중량부의 물을 서서히 첨가하며 교반하여 모르타르 조성물을 조성하고 이와 같이 조성된 모르타르 조성물로 저면에는 소정 형상의 횡홈(12)을 형성하고 종으로 관통하여서는 종혈(11)이 형성되어 벽돌이 쌓여졌을 때 서로 다른 벽돌들 사이에 연결되는 공기 이동로가 형성되게 구성된 벽돌에 관한 것이다.
Description
본 발명은 모르타르 조성물 및 이에 의해 제조된 벽돌에 대한 것으로서, 보다 상세하게는 광산에서 광석의 선광 과정에서 발생되는 광석의 가루 특히, 견운모에 숯가루, 황토 및 시멘트를 혼합한 분말에 소정량의 물을 혼합하여 조성된 모르타르 조성물과 이 조성물로 성형된 벽돌에 관한 것이다.
일반적으로 건물을 신축 또는 보수하는데 가장 많이 사용되는 건축재의 하나로 모르타르 등이 있다.
이와 같은 모르타르는 통상적으로 소정량의 자갈과 모래 및 시멘트를 혼합하고 여기에 물을 섞어 조성되며, 이와 같이 자갈이 혼합된 것은 건물의 뼈대나 보를 형성하는데 사용되고 자갈이 혼합되지 않은 것은 외장용 등 마감에 주로 사용되고있다.
이러한 모르타르는 사용 용도에 따라 강도나 연성을 가감시키거나 소성 속도를 증감하기 위해 시멘트를 더 넣거나 다른 첨가제를 넣어 사용하고 있다.
건축 기술이 발전하고 생활 수준이 향상됨에 따라 보다 인체에 이로운 영향을 줄 수 있는 건축재가 개발 사용되고 있으며, 모르타르 또한 원적외선을 방사하거나 보온성이 우수한 기능성을 갖는 것들이 개발되어 사용되고 있다.
또한 광산에서 채굴되는 광석을 선별하는 과정에서는 광석으로 사용할 수 없는 작은 조각 및 가루가 생산되며, 이러한 부산물은 통상적으로 폐기 처리되나 사후 처리가 충분히 이루어지지 않아 산야를 덮게 되어 농작물은 물론 임야의 동식물에 영향을 주는 문제가 있었다.
본 발명은 상기와 같은 문제점을 해소하고 보다 인체에 유익한 건축 자재를 제공하기 위한 것으로 광산에서 부산물로 생성되는 광석의 가루나 작은 조각 특히, 견운모에 황토와 숯가루 등을 혼합하여 모르타르 조성물을 조성하고 이렇게 조성된 모르타르 조성물로 벽돌을 제작함으로서 원적외선의 방사는 물론 탈취, 향균 기능을 갖는 기능성 모르타르조성물과 이에 의해 성형된 벽돌을 제공하는 데 그 목적이 있다.
이러한 목적을 갖는 본 발명은 광물을 이용한 모르타르 조성물에 있어서, 광물의 선광 과정으로부터 배출된 견운모 90~110중량부에 알루미나시멘트15~20중량부, 황토300중량부 및 숯가루 0.1~0.2중량부를 혼합한 후, 혼합된 분말에 8~12중량부의 물을 서서히 첨가하며 교반하여 조성됨을 특징으로 하는 모르타르 조성물에 의해 이루어진다.
또한 본 발명의 목적은 광물의 선광 과정으로부터 배출된 견운모 90~110중량부에 알루미나시멘트15~20중량부, 황토300중량부 및 숯가루 0.1~0.2중량부를 혼합하고 혼합된 분말에 8~12중량부의 물을 서서히 첨가하며 교반하여 조성된 모르타르를 소정 형상으로 성형하여 이루어짐을 특징으로 하는 벽돌에 의해 이루어진다.
더욱이 본 발명의 목적은 견운모와 황토분의 입도를 3mm이하로 형성하고, 숯가루의 입도를 325mesh 이하로 함에 의해 이루어지며, 벽돌의 저면에는 벽돌이 쌓여졌을 때 서로 다른 벽돌에 형성된 것과 연통되는 소정 형상의 횡홈을 형성하고, 벽돌을 관통하여 상하로 소정 형상의 종혈(11)을 형성하여 싸여진 벽돌의 내부에 공기 유로를 형성함에 의해 이루어진다.
도 1 은 본 발명에 따른 모르타르 조성물에 의해 제조된 구조물로부터 방사되는 적외선 열화상사진이고,
도 2 은 종래의 모르타르 조성물에 의해 제조된 구조물로부터 방사되는 적외선 열화상사진이고,
도 3은 본 발명에 따른 모르타르 조성물에 의해 제조된 구조물로부터 방사되는 방사에너지를 나타낸 도표이고,
도 4는 본 발명에 따른 모르타르 조성물에 의해 제조된 구조물로부터 방사되는 원적외선 방사율을 나타낸 도표이고,
도 5는 본 발명에 따른 모르타르 조성물에 의해 제조된 구조물의 가스 흡입성을 나타낸 도표이고,
도 6은 본 발명의 일실시예에 따른 모르타르 조성물에 의해 제조된 벽돌의 사시도이고,
도 7은 본 발명의 일실시예에 따른 모르타르 조성물에 의해 제조된 벽돌의 다른 일예의 사시도이고,
도 8은 본 발명의 일실시예에 따른 모르타르 조성물에 의해 제조된 벽돌이적조된 상태를 도시한 사시도이고,
도 9은 본 발명의 일실시예에 따른 모르타르 조성물에 의해 제조된 벽돌이 적조된 상태의 종단면도이며,
도 10는 본 발명의 일실시예에 따른 모르타르 조성물에 의해 제조된 벽돌이 적조된 상태의 측단면도이다.
*도면의 주요 부분에 대한 부호 설명*
10 : 벽돌 11 : 종혈
12 : 횡홈
상기와 같은 본 발명에 따른 모르타르 조성물 및 이에 의해 제조된 벽돌의 바람직한 실시예를 첨부된 도면에 의거 상세하게 설명하면 다음과 같다.
도 1 은 본 발명에 따른 모르타르 조성물에 의해 제조된 구조물로부터 방사되는 적외선 열화상사진이고, 도 3은 본 발명에 따른 모르타르 조성물에 의해 제조된 구조물로부터 방사되는 방사에너지를 나타낸 도표이고, 도 4는 본 발명에 따른 모르타르 조성물에 의해 제조된 구조물로부터 방사되는 원적외선 방사율을 나타낸 도표이고, 도 5는 본 발명에 따른 모르타르 조성물에 의해 제조된 구조물의 가스 흡입성을 나타낸 도표이고, 도 6은 본 발명의 일실시예에 따른 모르타르 조성물에의해 제조된 벽돌의 사시도이고, 도 7은 본 발명의 일실시예에 따른 모르타르 조성물에 의해 제조된 벽돌의 다른 일예의 사시도이고, 도 8은 본 발명의 일실시예에 따른 모르타르 조성물에 의해 제조된 벽돌이 적조된 상태를 도시한 사시도이고, 도 9는 본 발명의 일실시예에 따른 모르타르 조성물에 의해 제조된 벽돌이 적조된 상태의 종단면도이며, 도 10은 본 발명의 일실시예에 따른 모르타르 조성물에 의해 제조된 벽돌이 적조된 상태의 측단면도이다.
본 발명에 따른 모르타르 조성물은 광물의 선광 과정으로부터 배출된 견운모 90~110중량부에 알루미나시멘트15~20중량부, 황토300중량부 및 숯가루 0.1~0.2중량부를 혼합한 후, 혼합된 분말에 8~12중량부의 물을 서서히 첨가하며 교반하여 조성된다.
또한 본 발명에 따른 벽돌은 견운모 90~110중량부에 알루미나시멘트15~20중량부, 황토300중량부 및 숯가루 0.1~0.2중량부를 혼합하고 혼합된 분말에 8~12중량부의 물을 서서히 첨가하며 교반하여 조성된 모르타르를 소정 형상으로 성형하여 이루어진다.
상기 벽돌(10)은 도 6에 도시된 바와 같이, 바닥면에는 장축 방향으로 소정 형상의 횡홈(12)이 형성되어 있고, 단축 방향으로 그 중앙을 관통하여 상기 횡홈(12)과 연결되는 종혈(11)이 형성되어 있다.
상기 횡홈(12)과 종혈(11)은 도 8 및 도 9에 도시된 바와 같이, 쌓여졌을 때 서로 다른 벽돌과 연통되어 공기 유동로를 이루며, 이 공기 유동로를 따라 공기가 이동됨에 따라 외부의 찬 공기나 더운 공기가 내부로 침투하는 것을 방지함으로서보온 및 보냉 효과가 우수하다.
상기 견운모는 운모중의 하나로 특히, 거정화강암(페그마타이트)에서 산출되는 암석으로서 이를 음용시 오장을 편하게 하고 정자를 보하며 분을 밝게 하는 효과가 있어 풍증, 설사, 여자의 백대하, 난산과 급창의 치료, 소화기관의 출혈 등에 약재로 사용되고 있다. 이러한 견운모는 원적외선을 방사하고, 열전도 효과가 우수하며, 항균 탈취, 방음 및 흡음 효과가 있다.
상기 황토는 표면이 넓은 벌집구조로 수많은 공간이 복층 구조를 이루고 있으므로 이 스폰지 같은 구멍 안에는 원적외선이 다량 흡수, 저장되어 있어 열을 받으면 발산하여 다른 물체의 분자활동을 자극한다. 즉 황토는 오랜 세월동안 태양에너지를 흡수하고 규소성 광물로서 보온 및 축열 효과가 우수하다.
숯은 나무를 태워 수분을 증발시킨 가벼운 탄소결정체로서 1gm 당 약 300m2의 기공이 형성되어 있어 이 넓은 기공에서 많은 종류의 유해한 세균을 흡착하여 항균 효과가 있고, 습도 조절 기능, 탈취 기능, 정화 및 정수 기능, 전자파 차폐 기능, 가스 흡착 및 선도 유지 기능, 제련 제독기능 등이 있으며, 다공성으로는 공기청정, 여과, 배기 처리용으로 사용되고 있다. 또한 숯은 원적외선을 다량 발산하여 체액속의 물을 알카리성으로 만들어 체질의 산성화를 막아줌과 동시에, 혈액중의 탄산가스 발산을 활성화시켜 혈중의 알카리도를 높이므로 알카리 체질로의 체질을 변화시켜 인체의 신진대사를 원활하게 하는 작용을 한다.
이와 같은 기능성 광물 즉, 견운모, 황토 및 숯을 혼합하여 조성된 모르타르로 제작 또는 축조된 건축물은 전술한 바와 같은 각 구성 성분의 기능에 따라 보온효과가 우수하며, 방습은 물론 방충 기능을 갖으며, 전자파 등의 유해파를 차단하여 인체의 신진 대사를 활성화시킨다.
상기 견운모와 황토분은 5mm이하의 입도의 것을 사용하고, 상기 숯가루는 3mm 이하의 입도의 것을 사용함으로서 각 구성 성분이 보다 고르게 혼합되고 이에 따라 그 분포를 고르게 하여 구조물 전체에서 상술한 기능이 발휘되게 할 수 있으나 각 구성 성분의 입도는 본 발명의 모르타르의 사용 방법이나 사용 장소에 따라 달라 질 수 있다.
이와 같이 조성된 모르타르는 물의 함량을 조절하여 벽돌을 쌓을 때 벽돌들 사이에서 벽돌들을 연결시키는 접착 수단으로 사용되거나 또는 외벽이나 내벽의 마감재로 사용될 수 있을 뿐만 아니라, 벽돌이나 기와 등을 성형하는 성형용으로 사용될 수도 있다.
원적외선협회 부설 원적외선응용평가연구소의 시험 결과를 도 1내지 도 5에 도시하였고 도시된 도면 내지는 도표를 참고로 본 발명에 따른 모르타르로 제작된 구조물의 특성을 설명한다.
본 발명에 따른 모르타르 조성물로 구성된 구조물은 상온에서 발열성이 종래의 구조물에 비해 우수하다. 상온에서의 발열 상태 사진을 도 1에 도시하였으며, 이와 대비되는 통상의 구조물에서의 발열 상태를 도 2에 도시하였다.
또한 본 발명에 따른 모르타르 조성물로 제작된 구조물은 도 2 및 도 3에 도시된 바와 같이 인체에 유익한 원적외선(5~20Micron)을 방사한다. 특히, 인체에 최적의 파장으로 알려진 9~10Micron대의 에너지량이 최대로서 인체의 신진대사를 촉진시키는데 많은 효과가 있다.
더욱이 본 발명에 따른 모르타르 조성물로 구성된 구조물은 탈취 작용을 갖는다. 이러한 탈취 기능은 견운모와 황토 등에 의한 작용으로서 도 4에 도시되고 표 1에 나타난 바와 같이 본 발명의 모르타르 시료가 넣어지지 않은 상태에서 실험할 때에 비해 상당한 탈취 효과가 있음을 알 수 있다.
상기와 같은 본 발명은 광산의 광석 채굴 과정에서 생성되는 광석으로 사용할 수 없는 부산물을 건축재로 재활용함으로서 건축재의 원가를 절감하는 효과가 있다.
또한 본 발명은 각 구성 성분들로부터 발생되는 원적외선을 방사함으로서 체질의 산성화를 막아줌과 동시에, 혈액중의 탄산가스 발산을 활성화시켜 혈중의 알카리도를 높이므로 알카리 체질로의 체질을 변화시켜 인체의 신진대사를 원활하게 하는 효과가 있고, 견운모와 숯의 방습, 향균 및 탈취 기능에 의해 항상 쾌적한 상태를 유지할 수 있게 하는 효과가 있으며, 황토의 항온 기능에 의해 보온 및 보냉 효과를 얻을 수 있다.
더욱이 본 발명의 벽돌로 축조된 건축물은 벽돌들 중앙에 상호 연통되게 형성되 공기 이동로를 따라 공기가 유동되어 건물의 내부와 외부를 차단시켜 보온 및 보냉 효과가 우수하여 냉난방 비용을 절감할 수 있는 효과가 있다.
Claims (5)
- 광물을 이용한 모르타르 조성물에 있어서,광물의 선광 과정으로부터 배출된 견운모 90~110중량부에 알루미나시멘트 15~25중량부, 황토 200~300중량부 및 숯가루 0.1~0.2중량부를 혼합한 후, 혼합된 분말에 8~12중량부의 물을 서서히 첨가하며 교반하여 조성됨을 특징으로 하는 모르타르 조성물.
- 광물의 선광 과정으로부터 배출된 견운모 90~110중량부에 알루미나시멘트 15~25중량부, 황토200~300중량부 및 숯가루 0.1~0.2중량부를 혼합하고 혼합된 분말에 8~12중량부의 물을 서서히 첨가하며 교반하여 조성된 모르타르를 소정 형상으로 성형하고 이를 건조하여 이루어짐을 특징으로 하는 벽돌.
- 제 1 또는 제 2 항에 있어서, 상기 견운모와 황토분의 입도가 5mm이하이고, 상기 숯가루의 입도가 3mm 이하임을 특징으로 하는 모르타르 조성물 및 이로 구성된 벽돌.
- 제 1 또는 제 2 항에 있어서, 상기 알루미나시멘트는 보크사이트를 주원료로 함을 특징으로 하는 모르타르 조성물 및 이로 구성된 벽돌.
- 제 2 항에 있어서, 상기 벽돌의 저면에는 장축 방향으로 소정형상의 횡홈(12)이 형성되고, 상기 횡홈(12)과 연통되게 상하로 관통하여 종혈(11)이 더 형성되어 벽돌이 쌓여졌을 때 서로 다른 벽돌에 형성된 횡홈(12) 및 종혈(11)이 서로 연결되어 공기 이동로가 형성됨을 특징으로 하는 벽돌.