KR200164613Y1

KR200164613Y1 - Coating chain

Info

Publication number: KR200164613Y1
Application number: KR2019990015751U
Authority: KR
Inventors: 김원철
Original assignee: 화성계전주식회사
Priority date: 1999-07-28
Filing date: 1999-07-28
Publication date: 2000-02-15

Abstract

본 고안은 쇠로 제작된 체인의 표면을 형광안료 또는 일반 색상안료로 조성된 코팅액으로 도포함으로써 장기간 물에 노출되어도 부식되지 않으며, 또한 야간에 식별이 가능할 뿐만 아니라 안전 사고를 예방할 수 있는 체인을 제공하기 위한 것이다.The present invention is applied to the surface of the chain made of metal with a coating solution composed of a fluorescent pigment or a general color pigment, so that it does not corrode even if exposed to water for a long time, it can be identified at night and also to provide a chain that can prevent safety accidents. It is for.

Description

Coated chain. {COATING CHAIN}

본 고안은 다수개의 링으로 구성된 체인에 관한 것으로서, 특히 체인의 표면에 형광안료 또는 일반 색상안료를 코팅 처리한 체인에 관한 것이다.The present invention relates to a chain consisting of a plurality of rings, and more particularly to a chain coated with a fluorescent pigment or a general color pigment on the surface of the chain.

통상적으로, 체인은 장공 타입의 링이 서로 연결되어 구성된 것이며, 이러한 체인은 현재 국/내외에서 다양한 용도로 활용되고 있는 실정이다. 한편 이러한 체인의 구성 및 용도는 이미 널리 공지된 기술이기 때문에 상세한 설명은 생략하기로 한다.In general, the chain is composed of a ring-type ring is connected to each other, the chain is currently being used for a variety of purposes in and outside the country. On the other hand, since the configuration and use of such a chain is already well known technology, a detailed description thereof will be omitted.

그러나, 이러한 체인은 그 자체가 물을 접하게 되면 쉽게 부식될 뿐만 아니라 촉감 자체가 차가우며 또한 외관상 투박하여 사용자로 하여금 불쾌감을 야기시켰다. 또한 상기 체인은 각 사용처에서 완벽한 효과를 구현하지 못하고, 특히 가이드 레일, 등산로, 선박, 주차장 E/L 등에 사용된 체인은 안전성에 많은 문제점을 가지고 있다.However, these chains themselves are not only easily corroded when they come in contact with water, but they are also cold and tactile in appearance, causing user discomfort. In addition, the chain does not implement a perfect effect in each use, especially the chain used for guide rails, hiking trails, ships, parking lot E / L has a lot of safety problems.

한편, 대한민국 공개실용신안공보 공개번호 제 98-59714 호에는 목걸이, 팔지를 구성하는 구슬의 일부분에 야광 또는 형광층을 형성시킨 장신구용 체인이 공개된 바가 있다.On the other hand, the Republic of Korea Utility Model Publication No. 98-59714 discloses a chain for ornaments formed by forming a luminous or fluorescent layer on a portion of the beads constituting the necklace, arm.

이러한 선출원 공개고안은 체인을 구성하고 있는 구슬에 홈을 형성한 후 여기에 야광액을 충전하여 구성된 것이며, 이는 통상의 체인, 상세하게는 장공 타입의 링으로 구성된 체인에는 적용할 수 없는 기술이다. 즉, 통상의 체인 링에는 홈을 형성할 수 없을 뿐만 아니라 설사 홈을 형성한다 해도 전술한 문제점을 해소할 수 없는 애로점이 예상된다.Such a prior application disclosure is formed by forming a groove in a bead constituting the chain and filling it with a luminous liquid, which is not applicable to a general chain, in particular, a chain composed of a ring-type ring. That is, not only a groove can be formed in a normal chain ring, but even if a groove is formed, it is expected that the above-mentioned problem cannot be solved.

따라서, 상기한 바와 같은 문제점을 해결하기 위한 본 고안의 목적은 형광안료 또는 일반 색상안료로 조성된 코팅액을 도포한 체인을 제공함에 있다.Accordingly, an object of the present invention for solving the above problems is to provide a chain coated with a coating liquid composed of a fluorescent pigment or a general color pigment.

본 고안의 다른 목적은 다수개의 링으로 구성된 체인의 촉감을 향상시킨 체인을 제공함에 있다.Another object of the present invention is to provide a chain that improves the feel of the chain consisting of a plurality of rings.

본 고안의 또 다른 목적은 야간에 식별 가능한 체인을 제공함에 있다.Another object of the present invention is to provide a chain that can be identified at night.

상기한 목적을 달성하기 위한 제1 견제에 따른 본 고안은, 폴리염화비닐 100중량부와 0.5∼2.0 중량부의 가소제, 0.05∼0.1 중량부의 충진제 및 0.01∼1.0 중량부의 안정제, 그리고 0.05∼3.0 중량부의 안료로 조성된 코팅액을 도포 처리한 체인을 구현하였다.The present invention according to the first check for achieving the above object is 100 parts by weight of polyvinyl chloride and 0.5 to 2.0 parts by weight of plasticizer, 0.05 to 0.1 parts by weight of filler and 0.01 to 1.0 parts by weight of stabilizer, and 0.05 to 3.0 parts by weight of A chain coated with a coating solution composed of pigments was implemented.

도 1은 본 고안의 바람직한 일 실시 예에 따라 형광안료 또는 일반 색상안료 및 기타 조성물들로 혼합된 코팅액이 도포처리된 체인의 구성을 도시한 부분 사시도1 is a partial perspective view showing the configuration of a chain coated with a coating liquid mixed with a fluorescent pigment or a general color pigment and other compositions according to an embodiment of the present invention

도 2는 도 1에서 도시하고 있는 코팅 처리된 체인의 단면도.FIG. 2 is a cross-sectional view of the coated chain shown in FIG. 1. FIG.

＜도면의 주요부분에 대한 부호의 설명＞<Description of the code | symbol about the principal part of drawing>

100: 체인 200: 코팅층100: chain 200: coating layer

이하 본 고안에 따른 바람직한 실시예를 첨부한 도면을 참조하여 상세히 설명한다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1은 본 고안의 일실시 예에 따라 코팅 처리된 체인의 형상을 도시한 사시도이다.1 is a perspective view showing the shape of a chain treated with a coating according to an embodiment of the present invention.

도 1에 도시한 바와 같이, 본 고안은 쇠로 제작된 통상의 체인(100), 즉 장공 타입으로 형성된 다수개의 링들이 서로 연결되어 구성된 체인의 표면을 코팅 처리하는 것이다. 상세하게는 전술한 체인을 예열기에 투입한 후 약 150∼350℃에서 1∼2분 동안 예열시킨 다음, 이를 본 고안의 주요 구성요소인 코팅액으로 디핑처리한다.As shown in Figure 1, the present invention is to coat the surface of the chain consisting of a conventional chain 100 made of steel, that is, a plurality of rings formed in the long hole type is connected to each other. Specifically, the chain is introduced into the preheater and then preheated at about 150 to 350 ° C. for 1 to 2 minutes, and then dipped into the coating liquid, which is the main component of the present invention.

한편, 상기의 코팅액은 수지를 주성분으로 하고 여기에 가소제, 충진제, 안정제 및 형광안료 또는 일반 색상안료로 조성된 것이다. 즉, 상기 코팅액은 폴리염화비닐 100 중량부와 가소제 0.5∼2 중량부, 충진제 0.05∼0.1 중량부, 안정제 0.01∼1.0 중량부 및 형광안료 또는 일반 색상안료 0.05∼3.0 중량부를 서로 혼합하여 제조된 것이다.On the other hand, the coating solution is a resin as a main component and is composed of a plasticizer, a filler, a stabilizer and a fluorescent pigment or a general color pigment. That is, the coating solution is prepared by mixing 100 parts by weight of polyvinyl chloride, 0.5 to 2 parts by weight of plasticizer, 0.05 to 0.1 parts by weight of filler, 0.01 to 1.0 parts by weight of stabilizer, and 0.05 to 3.0 parts by weight of fluorescent pigment or general color pigment. .

여기서 상기 가소제로는 3가지 물질 중에서 어느 하나를 선택하여 사용되며, 이는 D-2 헥실 프탈레이트(D-2 HEXYL PHTHALATE: 이하 'DOP'라 함), D-부틸 프탈레이트(D-BUTYL PHTHALATE: 이하 'DBP'라 함) 및 D-이소 프탈레이트(D-ISO PHTHALATE: 이하 'DOA'라 함)이다.Wherein the plasticizer is used to select any one of the three materials, which is D-2 hexyl phthalate (D-2 HEXYL PHTHALATE: hereinafter referred to as' DOP '), D-butyl phthalate (D-BUTYL PHTHALATE: hereinafter' DBP ') and D-iso phthalate (D-ISO PHTHALATE: hereinafter referred to as' DOA').

한편 상기 충진제로는 탄산칼슘 등이 사용되며, 상기 안정제는 주로 분말형태의 바륨 스트레이트 또는 카륨 아연에 BC 103을 섞어 사용된다.Meanwhile, calcium carbonate is used as the filler, and the stabilizer is mainly used by mixing BC 103 with barium straight or carium zinc in powder form.

그리고 상기 안료로는 형광안료 또는 일반 색상안료가 사용된다. 이때 상기 형광안료는 노란색 또는 오렌지색 혹은 밝은 녹색을 띄게 되며, 또한 AV Partile size: 5N, Light Fastness: 3, Heat stability: 110∼230F, Oil Absorption: 30~35% 및 Moisture content: 3.5%의 물리적 특성을 가진다. 또한 전술한 일반 색상안료는 통상의 색상을 띄게 된다.As the pigment, a fluorescent pigment or a general color pigment is used. In this case, the fluorescent pigment is yellow, orange or light green, and also has AV Partile size: 5N, Light Fastness: 3, Heat stability: 110 to 230F, Oil Absorption: 30 to 35%, and Moisture content: 3.5% Has In addition, the above-mentioned general color pigments will have a normal color.

이하, 전술한 방법으로 만들어진 코팅액을 통상의 체인의 표면에 코팅하는 방법을 도 1 내지 도 2를 참조하여 상세히 설명하면 하기와 같다.Hereinafter, a method of coating the coating liquid made by the above-described method on the surface of a conventional chain will be described in detail with reference to FIGS. 1 to 2.

우선, 쇠로 제작된 체인(100)을 150∼350℃에서 약 1∼2분 동안 예열시킨 후, 이를 전술한 코팅액으로 디핑처리한 다음, 약 150∼350℃의 온도에서 1∼2분 동안 열처리한 후, 곧바로 송풍로 안으로 투입시켜 대기 온도까지 냉각시킨다. 그러면 도 2에 도시한 바와 같이 체인(100)의 표면에는 코팅층(200)이 형성된다.First, the chain 100 made of iron is preheated at 150 to 350 ° C. for about 1 to 2 minutes, and then dipped with the coating solution described above, and then heat treated at a temperature of about 150 to 350 ° C. for 1 to 2 minutes. Immediately afterwards, the mixture is thrown into a blower and cooled to an ambient temperature. Then, as shown in FIG. 2, a coating layer 200 is formed on the surface of the chain 100.

이상으로 살펴본 바와 같이, 본 고안은 체인의 표면에 코팅 처리함으로써 장기간 물에 노출시켜도 부식되지 않을 뿐만 아니라 미적 감각이 뛰어나며, 또한 체인 촉감이 부드러운 장점을 가지고 있다. 그리고 상기 체인은 꼬임 현상 및 소음이 없을 뿐만 아니라 전기 누전을 방지할 수 있고, 또한 미끄럼을 방지할 수 있는 이점이 있다.As described above, the present invention has a merit that the coating surface of the chain is not corroded even if exposed to water for a long time, has excellent aesthetics, and has a soft touch to the chain. In addition, the chain is free from twisting and noise, and also has an advantage of preventing electric leakage and preventing slipping.

특히, 가이드 레일, 등산로, 선박, 주차장 E/L 등에 사용시 종래의 체인보다 안정된 상태에서 사용할 수 있는 이점이 있다. 그리고, 체인의 표면을 야광 코팅처리 함으로써 야간에 식별이 가능하여 사고의 위험으로부터 예방할 수 있으며, 또한 실내장식 및 각종 인테리어 등으로 사용할 수 있는 상승된 효과가 있다.In particular, when used in guide rails, hiking trails, ships, parking lot E / L, there is an advantage that can be used in a stable state than the conventional chain. And, by luminous coating the surface of the chain can be identified at night to prevent from the risk of accidents, there is also an increased effect that can be used for interior decoration and various interiors.

Claims

In chains connected by multiple rings,

The chain has a polyvinyl chloride as a main component, and the chain is coated with a coating liquid formed by mixing a plasticizer, a filler and a stabilizer, and a pigment.

The coating solution according to claim 1, wherein the chain is formed by mixing 100 parts by weight of polyvinyl chloride, 0.5 to 2.0 parts by weight of a plasticizer, 0.05 to 0.1 parts by weight of a filler, 0.01 to 1.0 parts by weight of a stabilizer, and 0.05 to 3.0 parts by weight of a pigment. The chain characterized in that the coating.

The chain according to claim 2, wherein the plasticizer is any one selected from D-2 hexyl phthalate, D-butyl phthalate, and D-isophthalate.

3. The chain of claim 2 wherein said filler is calcium carbonate.

The chain according to claim 2, wherein the stabilizer is prepared by mixing liquid BC 103 with barium straight or carium zinc.

The chain of claim 2, wherein the pigment is a fluorescent pigment or a general color pigment.