KR20010055980A - Wire saw with adhesive diamond electrodeposited on it and its manufacturing method - Google Patents

Wire saw with adhesive diamond electrodeposited on it and its manufacturing method Download PDF

Info

Publication number
KR20010055980A
KR20010055980A KR1019990057327A KR19990057327A KR20010055980A KR 20010055980 A KR20010055980 A KR 20010055980A KR 1019990057327 A KR1019990057327 A KR 1019990057327A KR 19990057327 A KR19990057327 A KR 19990057327A KR 20010055980 A KR20010055980 A KR 20010055980A
Authority
KR
South Korea
Prior art keywords
diamond
nickel
plating
layer
wire
Prior art date
Application number
KR1019990057327A
Other languages
Korean (ko)
Other versions
KR100338386B1 (en
Inventor
박평렬
송재업
Original Assignee
최의박
홍덕스틸코드주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 최의박, 홍덕스틸코드주식회사 filed Critical 최의박
Priority to KR1019990057327A priority Critical patent/KR100338386B1/en
Publication of KR20010055980A publication Critical patent/KR20010055980A/en
Application granted granted Critical
Publication of KR100338386B1 publication Critical patent/KR100338386B1/en

Abstract

PURPOSE: A wire saw and its manufacturing method improves the adhering force of diamond grits to minimize cutting marks due to the falling particles and abrasion performance of the grits to reduce slurry. CONSTITUTION: A copper coated layer with the thickness less than 1μm is formed on the surface of a high-rigidity steel wire(13) as a base coating. A nickel-diamond grits electrodeposition layer of 18¯25μm is formed on the base coating. The copper coated layer is made of pure copper or brass. The size of the diamond grit in the nickel-diamond grits electrodeposition layer is 5¯30μm. The packing rate of the grits is 5¯30%.

Description

밀착성이 우수한 다이어몬드 전착 와이어 쏘우 및 그 제조방법{Wire saw with adhesive diamond electrodeposited on it and its manufacturing method}Diamond electrodeposited wire saw with excellent adhesion and its manufacturing method {Wire saw with adhesive diamond electrodeposited on it and its manufacturing method}

본 발명은 반도체 웨이퍼로 사용되는 실리콘 단결정과 같은 각종 취성 재료의 절단에 사용되는 다이어몬드 전착 와이어 쏘우(wire saw)에 관한 것으로서, 더 자세하게는 피아노용 선재와 같은 고강도 선재의 표면에 하지도금으로 구리 또는 황동의 1차 도금을 하고, 그 위에 2차 니켈도금을 함에 있어 니켈 도금조에 일정한 크기의 다이어몬드 지립(砥粒)을 넣고 교반하면서 다이어몬드 지립의 충진율을 적절한 수준으로 균일하게 전착시킨 도금층을 형성시키므로써 다이어몬드 지립의 밀착성이 우수하여 경질 재료의 절단시 다이어몬드 지립의 탈락이 매우 적은, 밀착성이 우수한 다이어몬드 전착 와이어 쏘우와 그 제조 방법에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to diamond electrodeposited wire saws used for cutting various brittle materials such as silicon single crystals used as semiconductor wafers, and more particularly copper on base surface of high strength wires such as piano wires. Alternatively, in the first plating of brass and the second nickel plating on it, a diamond layer having a certain size is put in a nickel plating bath and stirred while uniformly electrodepositing the filling rate of the diamond abrasive grain to an appropriate level. The present invention relates to a diamond electrodeposited wire saw having excellent adhesion, and a method of producing the same, wherein the diamond abrasive grains are excellent in adhesion, and thus diamond particles are hardly dropped during cutting of hard materials.

일반적으로, 반도체 재료로 사용되는 실리콘, 갈륨-비소 잉고트(ingot) 또는 유리 등의 경질 취성재료의 절단에 사용되는 종래의 공구로는 다이어몬드 입자가 고착된 원판상의 블레이드(blade) 톱, 유리 분말등의 절단용 슬러리를 절단부에 공급하면서 다수 개의 와이어 쏘우를 절단면에 통과시키는 멀티 와이어 쏘우 및 피아노선등의 와이어 표면에 다이어몬드 입자를 전착시킨 다이어몬드 전착 와이어 쏘우 등이 알려져 있다.In general, conventional tools used for cutting hard brittle materials such as silicon, gallium-arsenic ingots, or glass, which are used as semiconductor materials, include disk-shaped blade saws and glass powders having diamond particles fixed thereto. BACKGROUND ART Multi-wire saws for passing a plurality of wire saws through a cut surface while supplying a cutting slurry such as a cutting part, and a diamond electrodeposition wire saw for electrodepositing diamond particles on a wire surface such as a piano wire are known.

반도체 산업의 비약적인 발전에 따라 상기의 경질 취성재료의 절단 가공량이 급증하고 있으며, 절단 정밀도의 확보와 절단면의 결함 발생을 감소시키는 문제가 매우 중요한 사항으로 대두되고 있다.With the rapid development of the semiconductor industry, the cutting processing amount of the above-mentioned hard brittle material is increasing rapidly, and the problem of securing the cutting precision and reducing the occurrence of the defect of a cutting surface is emerging as an important matter.

경질 취성재료를 절단함에 있어 절단면의 정밀성과 결함 발생 등 절단 성능측면에서의 상기 절단 공구를 살펴보면 각각 아래와 같은 특성이 있다.Looking at the cutting tools in terms of cutting performance, such as the precision and defects in the cutting surface in cutting the hard brittle material has the following characteristics.

종래의 취성재료 절단공구의 대표적인 블레이드 톱은 절단 성능면에서는 우수하나 다이어몬드 입자의 마모나 절단중 슬러리에 의한 절단부의 막힘 현상이 빈발하여 가공 능율이 떨어질 뿐아니라 절단면에 크랙의 흔적이 크다는 문제점이 있으며, 최근 실리콘 잉고트의 대형화 경향에 따라 블레이드 톱도 대형화(대직경화) 하고 있고 절단시 재료의 손실을 줄이기 위하여 블레이드 톱의 두께도 점차 박판화 되고 있으나 톱의 대형화에 따른 박판화에는 어쩔 수 없는 한계가 있다.Representative blade saws of conventional brittle cutting tools are excellent in cutting performance, but wear of diamond particles or clogging of the cutting part by slurry during cutting is not only low, but also the processing efficiency is lowered, and there are problems of cracks on the cutting surface. In addition, the blade saw has also been enlarged (larger diameter) in accordance with the recent trend of larger silicon ingots, and the thickness of the blade saw is gradually being reduced in order to reduce material loss during cutting, but there is an inevitable limitation in thinning due to the enlargement of the saw. .

그리고, 절삭용 슬러리를 사용하는 멀티 와이어 쏘우의 경우에는 대형의 공작물을 1회의 절단작업으로 수십 또는 수백장씩 절단할 수 있는 장점은 있으나, 슬러리 혼탁액에 경유를 혼합하여 사용하기 때문에 피절단재가 오염되기 쉽고 폐슬러리 혼탁액의 처리가 까다로우며 절단 속도가 늦을 뿐아니라 절단면이 거친 문제가있다. 또한, 절단 작업중 와이어 쏘우가 단선되면 실리콘 잉고트의 경우에는 전체가 불량으로 처리되어 경제적으로 손실이 크다.In addition, in the case of a multi-wire saw using a cutting slurry, a large workpiece can be cut tens or hundreds by one cutting operation, but the cutting material is contaminated because a mixture of light oil and a slurry turbidity is used. It is easy to handle waste slurry and difficult to process, and the cutting speed is slow and the cutting surface is rough. In addition, if the wire saw is disconnected during the cutting operation, the silicon ingot is treated as a whole in a bad way and economically high.

다이어몬드 전착 와이어는 상기 여타의 취성재료 절단공구에 비하여 피절단재의 절단면에 절단가공 크랙의 흔적을 적게 발생시키며, 절단면의 정밀도 역시 상대적으로 높다는 특성을 가지기 때문에 특히, 실리콘 잉고트등 반도체 재료의 절단용 공구로 널리 사용되고 있는 바, 이러한 종래 다이어몬드 전착 와이어 쏘우의 대표적인 몇 가지를 살펴보면 다음과 같다.The diamond electrodeposition wire generates less cutting cracks on the cutting surface of the cutting material than other brittle material cutting tools, and the cutting surface precision is also relatively high, and therefore, especially for cutting semiconductor materials such as silicon ingots. As widely used as a tool, a few representative examples of such a conventional diamond electrodeposition wire saw are as follows.

일본 특허공보 소62-260006호에는 피아노 선재의 표면을 열처리 하여 연질의페라이트(ferrite)조직으로 상변환시킨 후, 그 페라이트 기지에 다이어몬드 입자를 물리적으로 박아 넣은 다이어몬드 와이어 쏘우가 개시되어 있는 바, 이는 와이어 표면에 다이어몬드 압입에 따른 표면흠이 많아 절단 작업중 단선이 발생하기 쉬운 단점이 있다.Japanese Patent Laid-Open No. 62-260006 discloses a diamond wire saw in which a surface of a piano wire is heat-treated to phase-convert to a soft ferrite structure, and then the diamond particles are physically embedded in the ferrite matrix. This has a disadvantage in that a lot of surface defects due to diamond indentation on the wire surface tends to cause disconnection during cutting.

또 다른 종래 다이어몬드 전착 와이어 쏘우의 하나는 일본 공개특허 공보 평7-96455에는 피아노 선재에 니켈 도금층을 피복하고, 그 위에 불소수지등의 수지층을 다시 피복한 다음 수지층을 일정폭의 나선형태로 제거하여 노출된 니켈 도금층 위에 선택적인 2차 도금층과 함께 다이어몬드 입자를 전착시킨 나선형 다이어몬드 전착 와이어 쏘우가 개시되어 있으나, 이러한 형태의 와이어 쏘우는 수지층을 피복시키고 그것을 다시 나선형태로 연삭·제거하는 등의 작업이 포함됨에따라 와이어 쏘우의 생산 공정이 복잡하여 생산성이 낮고 제조원가가 높아진다는 문제점이 있다.In another conventional diamond electrodeposition wire saw, Japanese Laid-Open Patent Publication No. Hei 7-96455 has a nickel plated layer coated on a piano wire rod, and a resin layer such as a fluororesin is coated thereon, and then the resin layer is formed in a spiral shape. Although a spiral diamond electrodeposition wire saw has been disclosed in which diamond particles are electrodeposited together with an optional secondary plating layer on an exposed nickel plating layer by removal of the metal oxide layer, this type of wire saw covers the resin layer and is then ground in a spiral manner. As the operations include the removal of the wire saw, the production process of the wire saw is complicated, resulting in low productivity and high manufacturing cost.

다이어몬드 전착 와이어 쏘우의 가장 일반적인 형태로서, 피아노 선재의 표면에 1차 하지 도금을 한 후, 2차 니켈 도금시 다이어몬드의 입자를 함께 전착시킨 와이어 쏘우는 비교적 손쉽게 제작이 가능하고 직경이 큰 피절단물의 절단도 가능한 장점이 있으나, 절단중 와이어 쏘우에서 탈락된 다이어몬드 입자가 섞인 슬러리에 의한 절단부의 막힘 현상이 발생되어 8인치 이상의 잉고트 절단시에는 와이어 쏘우의 단선과 탈락한 다이어몬드 입자에 의한 절단 흔적이 크고 절단면이 거칠게 되는 문제가 있다.The most common form of diamond electrodeposition wire saw is that the wire saw, which is first plated on the surface of the piano wire and then electrodeposited with diamond particles during the second nickel plating, is relatively easy to manufacture and has a large diameter. Although cutting of the cuttings has the advantage of being possible, the blockage of the cutting part caused by the slurry mixed with the diamond particles dropped from the wire saw during cutting occurs, and when cutting the ingot of 8 inches or more, the wire saw is disconnected and the diamond particles are dropped. There is a problem that the cutting marks are large and the cutting surface is rough.

특히, 종래의 다이어몬드 전착 와이어는 크기가 40∼80㎛정도 되는 다이어몬드 지립을 사용하고 있으며 지립의 충진율은 40% 이상으로써 절단 작업시 지립의 탈락이 가장 큰 문제이나 지립의 크기와 충진율에 대한 연구는 없는 실정이다.In particular, the conventional diamond electrodeposition wire uses diamond abrasive grains having a size of about 40 to 80 μm, and the filling rate of the abrasive grains is 40% or more. There is no research.

따라서, 상기에서 살펴본 바와 같이 본 발명은 경질의 취성재료를 절단함에 있어서 절단면의 정밀도와 절단 흔적의 발생 및 슬러리에 의한 절단부의 막힘에 영향을 주는, 다이어몬드 전착 와이어 쏘우에서의 다이어몬드 입자 탈락을 감소시키기 위하여 전착에 사용되는 다이어몬드 입자의 크기와 전착 충진율에 대한 최적의 값을 갖는 다이어몬드 전착 와이어 쏘우 및 그 제조 방법을 제공하는 것에 목적을 두고 있다.Thus, as discussed above, the present invention provides for diamond particle dropout in a diamond electrodeposition wire saw, which affects the precision of the cut surface and the generation of cut traces and the blockage of the cut portion by the slurry in cutting the hard brittle material. It is an object of the present invention to provide a diamond electrodeposition wire saw having an optimal value for the size and the electrodeposition filling rate of the diamond particles used for electrodeposition to reduce.

도 1은 본 발명 방법에 따른 다이어몬드 전착 와이어의 공정도로서,1 is a process diagram of a diamond electrodeposition wire according to the present invention,

(가)는 황동도금선을 사용한 경우이고,(A) is the case of using brass plating wire,

(나)는 고강도 선재를 사용한 경우이다.(B) is the case of using high strength wire rod.

도 2는 본 발명의 실시예인 다이어몬드 전착 와이어 쏘우의 절단능을 시험 r결과를 보인 그래프.Figure 2 is a graph showing the test r results of the cutting ability of the diamond electrodeposition wire saw which is an embodiment of the present invention.

((도면의 주요 부분에 대한 부호의 설명))((Explanation of symbols for main part of drawing))

1. 탕조 2. 산세조1. Bath bath 2. Pickling bath

3,5,10. 수세조 4. 구리도금조3,5,10. Wash bath 4. Copper plating bath

6,7,8,9. 1번∼4번 니켈 도금조 11. 건조로6,7,8,9. Nickel Plating Baths 1 to 4 11. Drying Furnace

본 발명의 상기 목적은, 고강도 피아노 선재의 표면 위에 1차 하지도금으로서 구리 또는 황동도금을 실시하고, 그 도금층 표면 위에 2차 도금인 니켈도금을 함에 있어 일정한 크기로 분류된 다이어몬드 입자를 니켈 도금조에 넣고 교반하면서 적절한 두께의 니켈-다이어몬드 전착층을 형성시키므로써 달성된다.The above object of the present invention is to nickel-plated diamond particles classified to a certain size in the case of performing copper or brass plating as the primary base plating on the surface of the high strength piano wire, and nickel plating as the secondary plating on the surface of the plating layer. This is achieved by forming a nickel-diamond deposit electrode layer of appropriate thickness with stirring into the bath.

이때, 1차 도금층의 두께는 1㎛이하 이고, 2차 도금층의 두께는 18∼25㎛ 범위로 하며, 2차 도금층의 다이어몬드 입자 크기와 충진율은 5∼30㎛ 및 5∼30%로 함이 바람직하다.At this time, the thickness of the primary plating layer is less than 1㎛, the thickness of the secondary plating layer is in the range of 18 to 25㎛, diamond particle size and filling rate of the secondary plating layer is 5 to 30㎛ and 5 to 30% desirable.

상기 본 발명의 목적과 기술적 구성 및 그에 따른 작용 효과를 비롯한 다이어몬드 전착 와이어 쏘우의 제조 과정은 본 발명의 바람직한 실시예를 도시하고 있는 도면을 참조한 아래의 상세한 설명에 의하여 명확하게 이해될 것이다.The manufacturing process of the diamond electrodeposition wire saw, including the object and the technical configuration of the present invention and the resulting effects thereof will be clearly understood by the following detailed description with reference to the drawings showing a preferred embodiment of the present invention.

먼저, 도1의 (가)와 (나)는 본 발명 방법에 따른 제조 공정도로서, (가)는 황동 도금선을 사용한 경우이고, (나)는 강선을 사용하여 1차 구리도금을 실시한 경우이다.First, Figure 1 (a) and (b) is a manufacturing process chart according to the method of the present invention, (a) is a case of using a brass plated wire, (b) is a case of primary copper plating using a steel wire. .

황동도금선(12)을 사용하는 경우에는, 피아노 선재에 아연도금과 구리도금을 행한 후 열확산에 의하여 1층의 황동층을 형성시킨 황동도금 선재(12)를 다음의 니켈도금 공정에 투입하게 되며, 황동도금 선재(12)는 열탕 탈지를 행하는 탕조(1) →산세조(2) →수세조(3) →1번 니켈 도금조(6) →2번 니켈 도금조(7) →3번 니켈 도금조(8) →4번 니켈 도금조(9) →수세조(10) →건조로(11)를 거쳐 권취되므로써 다이어몬드 전착 와이어 쏘우로 제조된다.In the case of using the brass plating wire 12, after the galvanizing and copper plating on the piano wire, the brass plating wire 12 having one layer of brass layer formed by thermal diffusion is introduced into the following nickel plating process. The brass plating wire (12) is a bath (1) → pickling tank (2) → washing tank (3) → nickel plating bath (1) → nickel plating bath (6) → nickel plating bath (7) → nickel nickel (3) It is made of a diamond electrodeposited wire saw by winding through a plating bath 8 → a nickel plating bath no. 4 9, a washing tank 10 → a drying furnace 11.

그리고, 피아노 강선과 같은 고강도 선재(13)를 이용하여 그 표면에 구리도금을 하는 경우에는, 탕조(1) →산세조(2) →수세조(3) →구리 도금조(4) →수세조(5) →1번 니켈 도금조(6) →2번 니켈 도금조(7) →3번 니켈 도금조(8) →4번 니켈 도금조(9) →수세조(10) →건조로(11)를 거쳐 다이어몬드 전착 와이어 쏘우로 완성된다.In the case where copper is plated on the surface using a high strength wire 13 such as a piano steel wire, a bath tub 1 → a pickling tank 2 → a water washing tank 3 → a copper plating tank 4 and a water washing tank (5) → No. 1 nickel plating bath (6) → No. 2 nickel plating bath (7) → No. 3 nickel plating bath (8) → No. 4 nickel plating bath (9) → Washing tank (10) → Drying furnace (11 Finished with diamond electrode wire saw.

상기의 두 공정에서 구리 또는 황동 도금층의 두께는 양자 공히 1㎛ 이하로 하는 것이 바람직한데, 이는 도금시 제어하거나 도금후 신선 과정을 통하여 조절될 수도 있으다. 이러한 하지도금은 본 도금층으로서의 니켈 도금층의 강선에 대한 접착력을 높이기 위한 것으로서, 1㎛을 초과하게 되면 오히려 니켈 도금층의 접착력이 떨어지게 된다.In the above two processes, the thickness of the copper or brass plating layer is preferably less than 1 μm, which may be controlled during plating or adjusted through the post-plating drawing process. The base plating is to increase the adhesion to the steel wire of the nickel plated layer as the main plated layer, and when it exceeds 1 μm, the adhesion of the nickel plated layer is rather deteriorated.

2차 니켈도금의 도금조가 4개로 분리되어 있는 것은 도금조의 길이가 길게 되면 도금욕 속에 침적된 선재의 길이가 길어지게 되고, 그에 따른 선재의 전기 저항때문에 열 발생이 증가하여 선재의 단선을 초래하기 때문이다.If the plating bath of secondary nickel plating is separated into four, the length of the wire deposited in the plating bath becomes longer as the length of the plating bath becomes longer, and heat generation increases due to the electrical resistance of the wire, resulting in wire breakage. Because.

그러나, 니켈 도금조의 갯수를 반드시 4개로 구성하여야만 되는 것은 아니고 각 도금조의 길이, 사용 전류의 세기, 피도금 선재의 선경 및 조성에 따라 2개 내지 6개의 범위 내에서 변경이 가능하다.However, the number of nickel plating baths is not necessarily four, and can be changed within the range of 2 to 6 depending on the length of each plating bath, the strength of the current used, the wire diameter and the composition of the wire to be plated.

그리고, 다이어몬드 지립을 니켈 도금액에 넣고 교반시키면서 니켈도금을 행하므로써 다이어몬드 지립이 전착된 니켈 도금층이 형성되는 것이며, 이때 니켈 도금액에 넣어지는 다이어몬드 지립의 크기는 5∼30㎛으로 하고 충진율을 5∼30%로 제어하는 것은, 지립 크기가 5㎛미만이거나 충진율이 5% 미만이면 절단 성능이 떨어지고, 지립 크기가 30㎛을 초과하거나 충진율이 30%를 초과하면 지립의 탈락이 증가하여 절단면이 거칠어지고 절단 흔적이 많이 남게 되기 때문이다.In addition, nickel plating is carried out by adding diamond abrasive grains to the nickel plating solution while stirring, thereby forming a nickel plated electrode electrodeposited with diamond abrasive particles, and the size of the diamond abrasive grains put in the nickel plating solution is 5 to 30 µm and the filling rate is reduced. The control of 5 to 30% results in poor cutting performance when the abrasive grain size is less than 5 μm or the filling rate is less than 5%, and when the abrasive grain size exceeds 30 μm or the filling rate exceeds 30%, the dropping of the abrasive grains increases and the cutting surface is increased. This is because roughness and a lot of cutting marks remain.

상기의 다이어몬드 지립은 4개의 니켈 도금조 모두에 넣는 것이 아니라 1번, 2번, 3번 3개의 니켈 도금조(7)(8)(9)에 넣는 것이고 4번 니켈 도금조(10) 즉, 최종 도금조에는 순수 니켈 전기 도금액만이 들어있다.The diamond abrasive grains are not placed in all four nickel plating baths, but are placed in three nickel plating baths (7) (8) (9) in the first, second, and third times. The final plating bath contains only pure nickel electroplating solution.

이와같이 최종 니켈 도금조에서 니켈-다이어몬드 도금층으로 전착되는 니켈 이온은 다이어몬드와 니켈사이의 계면을 보강해주는 역할을 하므로써 다이어몬드 지립의 니켈 도금층에 대한 접착력을 향상시키게된다.As such, the nickel ions electrodeposited to the nickel-diamond plating layer in the final nickel plating bath enhance the interface between the diamond and the nickel, thereby improving the adhesion of the diamond abrasive grains to the nickel plating layer.

상기에서 다이어몬드의 충진율이라 함은 다음의 식으로 구할 수 있다.The filling rate of diamond in the above can be obtained by the following equation.

다이어몬드 지립 충진율(%) =Diamond abrasive filling rate (%) =

식1에서, DGS는 다이어몬드 지립의 평균 크기이며, n은 지립의 수이고, A는 도금층의 단면적이다.In Equation 1, DGS is the average size of diamond abrasive grains, n is the number of abrasive grains, and A is the cross-sectional area of the plating layer.

본 발명 방법에 의한 실시예로서, 선경이 0.14mm인 강선에 황동도금을 1차 하지도금으로 실시하고, 5∼10㎛ 및 10∼20㎛인 입도 분포를 갖는 두 종류의 다이어몬드 지립을 두 차례에 걸쳐 1,2,3번 3개의 니켈 도금조에 넣고 교반하면서 니켈-다이어몬드 전착도금을 행하면서 4번 니켈 도금조에서는 니켈도금만을 하는 방법으로 2종의 다이어몬드 전착 와이어 쏘우 샘플을 제조하였고, 다이어몬드 지립의 충진율은 5∼30%로 조절하였다.As an embodiment according to the method of the present invention, a steel wire having a wire diameter of 0.14 mm is subjected to brass plating as a primary base plating, and two types of diamond abrasive grains having a particle size distribution of 5 to 10 μm and 10 to 20 μm are twice. Two types of diamond electrodeposited wire saw samples were prepared by performing nickel-diamond electrodeposition plating while stirring into three nickel plating baths 1, 2, 3 over the course of the nickel plating bath, and performing nickel plating only in nickel plating bath 4, The filling rate of diamond abrasive grains was adjusted to 5-30%.

상기 두 종류의 절단능을 조사한 결과가 도2의 그래프이며, 피절단재의 재질로 알루미나를 선정하였고 쏘우의 접촉압력을 0.2N/mm로 하여 왕복 횟수에 따른 절단능을 시험하였다.As a result of examining the two types of cutting ability is a graph of Figure 2, the alumina was selected as the material of the cutting material, and the cutting ability according to the number of round trips was tested with the contact pressure of the saw to 0.2N / mm.

상기 시험에서 쏘우의 왕복 횟수 1200회에서도 다이어몬드 지립의 마모와 탈락이 발견되지 않았으며, 동일 충진율 하에서 지립의 크기가 커짐에 따라 절단능도 향상되는 것을 알 수 있었다.In the test, the wear and drop of diamond abrasive grains were not found even at 1200 round trips of the saw, and the cutting performance was also improved as the size of the abrasive grains was increased under the same filling rate.

본 발명의 다이어몬드 전착 와이어 쏘우는 다이어몬드 지립 크기와 도금 충진율의 적절한 제어와 최종 순수 니켈 도금단계에 의하여 다이어몬드 지립의 접착력을 현저히 향상시킬 수가 있으므로서, 절단 작업시 지립 탈락에 의해 발생하는 절단면의 절단흔적을 최소화할 수 있는 잇점이 있다.The diamond electrodeposited wire saw of the present invention can significantly improve the adhesive strength of diamond abrasive grains by appropriate control of diamond abrasive size and plating fill rate and the final pure nickel plating step, so that the cutting surface caused by the grain dropping during the cutting operation can be improved. This has the advantage of minimizing the cutting traces.

또한, 본 발명의 다이어몬드 전착 와이어 쏘우는 다이어몬드 지립의 탈락이 쉽지 않게 됨에따라 지립의 마모성 역시 향상되어 절단시 슬러리의 발생이 감소하고, 슬러리에 탈락된 지립의 수가 매우 적어 절단부의 막힘현상이 거의 없게 되어 와이어 쏘우의 단선이 없이 대형의 잉고트 절단도 가능한 장점도 가지고 있다.In addition, the diamond electrodeposited wire saw of the present invention is not easy to drop the diamond abrasive grains, the abrasive wear of the abrasive is also improved to reduce the occurrence of slurry during cutting, the number of abrasive grains dropped in the slurry is very small, clogging of the cut portion It also has the advantage of being able to cut large ingots without disconnecting the wire saw.

Claims (9)

다이어몬드 전착 와이어 쏘우에 있어서, 고강도 강선의 표면에 1㎛이하의 하지도금인 구리계 도금층이 형성되고, 이 하지 도금층 위에 18∼25㎛ 두께의 니켈-다이어몬드 지립 전착층이 형성되어 구성됨을 특징으로 하는 밀착성이 우수한 다이어몬드 전착 와이어 쏘우.In the diamond electrodeposition wire saw, a copper-based plating layer having a base plating of 1 μm or less is formed on the surface of the high strength steel wire, and a nickel-diamond abrasive electrode layer having a thickness of 18 to 25 μm is formed on the base plating layer. Diamond electrodeposition wire saw with excellent adhesion. 제 1항에 있어서, 상기 구리계 도금층은 황동으로 이루어짐을 특징으로 하는 밀착성이 우수한 다이어몬드 전착 와이어 쏘우.The diamond electrodeposition wire saw of claim 1, wherein the copper plating layer is made of brass. 제 1항에 있어서, 상기 구리계 도금층은 순수한 구리로 이루어짐을 특징으로 하는 밀착성이 우수한 다이어몬드 전착 와이어 쏘우.The diamond electrodeposition wire saw having excellent adhesion, according to claim 1, wherein the copper-based plating layer is made of pure copper. 제 1항에 있어서, 상기 니켈-다이어몬드 지립 전착층 중의 다이어몬드 지립은 그 크기가 5∼30㎛이고, 지립의 충진율은 5∼30%인 것을 특징으로 하는 밀착성이 우수한 다이어몬드 전착 와이어 쏘우.The diamond electrodeposited wire saw according to claim 1, wherein the diamond abrasive grains in the nickel-diamond abrasive electrodeposition layer have a size of 5 to 30 µm and a filling rate of the abrasive grains to 5 to 30%. 고강도 강선의 표면에 아연도금과 구리도금을 차례로 실시하는 단계와, 상호확산에 의하여 황동 도금층으로 변화되도록 하는 열확산 단계와, 상기 황동 도금층이 형성된 강선을 5∼30㎛ 크기의 다이어몬드 지립이 채워져 교반되는 다수 개의 니켈-다이어몬드 도금조를 통과시켜 황동 도금층의 표면에 니켈-다이어몬드 지립 전착층을 형성시키는 단계와, 니켈-다이어몬드 지립 전착층이 형성된 강선을 다이어몬드 지립이 없이 니켈 도금액만으로 이루어진 니켈 도금조로 통과시켜 다이어몬드 지립의 접착력을 강화시키는 단계로 이루어짐을 특징으로 하는 밀착성이 우수한 다이어몬드 전착 와이어 쏘우의 제조방법.Performing zinc plating and copper plating on the surface of the high strength steel wire in order; The thermal diffusion step to change to the brass plating layer by mutual diffusion, and the steel wire formed with the brass plating layer is passed through a plurality of nickel-diamond plating baths filled with diamond abrasive grains of 5 to 30㎛ size and stirred to the surface of the brass plating layer. Forming a nickel-diamond abrasive electrodeposition layer, and passing the steel wire on which the nickel-diamond abrasive electrodeposition layer is formed through a nickel plating bath consisting of nickel plating solution without diamond abrasives to strengthen the adhesion of the diamond abrasive grains. A method for producing a diamond electrodeposited wire saw having excellent adhesion. 제 5항에 있어서, 상기 황동 도금층은 1㎛이하의 두께인 것을 특징으로 하는 밀착성이 우수한 다이어몬드 전착 와이어 쏘우의 제조방법.6. The method of claim 5, wherein the brass plating layer has a thickness of 1 µm or less. 제 5항에 있어서, 상기 니켈-다이어몬드 지립 전착층의 다이어몬드 지립 충진율은 5∼30%인 것을 특징으로 하는 밀착성이 우수한 다이어몬드 전착 와이어 쏘우의 제조방법.6. The method for producing a diamond electrodeposited wire saw having excellent adhesion according to claim 5, wherein the diamond abrasive grain filling rate of the nickel-diamond abrasive grain layer is 5 to 30%. 제 5항에 있어서, 상기 고강도 강선은 피아노선인 것을 특징으로 하는 밀착성이 우수한 다이어몬드 전착 와이어 쏘우의 제조방법.6. The method for producing a diamond electrodeposited wire saw having excellent adhesion according to claim 5, wherein the high strength steel wire is a piano wire. 고강도 강선의 표면에 1㎛이하의 구리 도금층이 형성되도록 구리도금을 실시하는 단계와, 구리도금된 강선을 5∼30㎛ 크기의 다이어몬드 지립이 채워져 교반되는 다수의 니켈-다이어몬드 도금조를 순차적으로 통과시켜 구리 도금층의 표면에 다이어몬드 지립의 충진율이 5∼30%가 되도록 니켈-다이어몬드 지립 전착층을 형성시키는 단계와, 니켈-다이어몬드 지립 전착층이 형성된 강선을 다이어몬드 지립이 없이 니켈 도금액만으로 이루어진 니켈 도금조로 통과시켜 다이어몬드 지립의 접착력을 강화시키는 단계로 이루어짐을 특징으로 하는 밀착성이 우수한 다이어몬드 전착 와이어 쏘우의 제조방법.Copper plating is performed to form a copper plating layer of 1 μm or less on the surface of the high-strength wire, and a plurality of nickel-diamond plating baths in which copper-plated steel wires are filled with diamond abrasive grains having a size of 5 to 30 μm are stirred. Forming a nickel-diamond abrasive electrodeposition layer on the surface of the copper plated layer so that the diamond abrasiveness rate is 5 to 30%; and nickel-diamond abrasive electrodeposition layer having a nickel wire without diamond abrasive grains. Method of producing a diamond electrodeposited wire saw having excellent adhesion, characterized in that the step of passing through the nickel plating bath consisting of the plating solution to strengthen the adhesion of the diamond abrasive grains.
KR1019990057327A 1999-12-13 1999-12-13 Wire saw with adhesive diamond electrodeposited on it and its manufacturing method KR100338386B1 (en)