KR20010016066A - Equipment casting of rotary - Google Patents
Equipment casting of rotary Download PDFInfo
- Publication number
- KR20010016066A KR20010016066A KR1020000062225A KR20000062225A KR20010016066A KR 20010016066 A KR20010016066 A KR 20010016066A KR 1020000062225 A KR1020000062225 A KR 1020000062225A KR 20000062225 A KR20000062225 A KR 20000062225A KR 20010016066 A KR20010016066 A KR 20010016066A
- Authority
- KR
- South Korea
- Prior art keywords
- mold
- rotating plate
- cooling water
- continuous casting
- product
- Prior art date
Abstract
Description
본 발명은 회전식 연속 주조장치에 관한 것으로서, 보다 상세하게는 용탕주입시 발생되는 스컴(Scum)을 억제하고, 질소나 아르곤가스를 주입하여 용탕표면을 미려하고 표면변화가 없도록 한 것이며, 발생된 열을 이용하여 응고시간을 조절하여 표면의 수평상태를 유지시키는 것이고, 구동장치가 외부에 구비되어 유지보수가 용이하며 더 나아가서는 고온물질의 취급에 따른 안전성을 확보하여 제품을 품질과 신뢰성을 대폭 향상시킬 수 있도록 한 것이다.The present invention relates to a rotary continuous casting device, and more particularly, to suppress scum generated during molten metal injection, and to inject a nitrogen or argon gas to make the surface of the molten metal beautiful and without surface change. It maintains the horizontal state of the surface by adjusting the solidification time by using, and the driving device is provided on the outside for easy maintenance and further improves the quality and reliability of the product by securing safety according to the handling of high temperature materials. It was made to be possible.
주지하다시피 비철금속물은 용해성(溶解性)이 있어 고온으로 가열하면 용해된다. 이 용해된 금속을 준비된 형틀에 주입하면 제품(ingot)을 만드는 것으로, 이 제품(ingot)을 만드는 작업을 주조(鑄造:casting)라 하고, 용해된 비철금속물을 주입하는 형을 주형(鑄型:mould)이라 한다.As is well known, nonferrous metals are soluble and dissolve when heated to high temperatures. When the molten metal is injected into the prepared mold, the ingot is made into a mold. The work of making the ingot is called casting, and a mold in which the molten nonferrous metal is injected is cast. mould).
상기와 같이 주물을 만드는 장치는 일반적으로 국내에서 널리 알려진 기술이며, 외국에서도 이미 독일의 「MANNESMANN(DEMAG)」이라는 회사가 회전식 연속 주조장치를 사용하고 있었다.As described above, the apparatus for making castings is a technology widely known in Korea, and a company called "MANNESMANN (DEMAG)" of Germany has already used a rotary continuous casting apparatus in foreign countries.
그러나 상기와 같은 종래의 기술은 중앙에 모든 하중을 받게 집중되어 있고, 사용되는 스러스트 볼 베어링이 충격하중을 견디지 못하고 편하중이 발생됨으로 회전부분의 마모나 고장률이 발생됨은 물론 외측에 하중이 집중되므로 휨이나 수평유지가 어려운 문제점이 발생되었다.However, the prior art as described above is concentrated to receive all loads in the center, and the thrust ball bearings used do not endure impact loads and uneven loads are generated, so that the load or the failure rate of the rotating part is generated as well as the loads are concentrated on the outside. There was a problem that the bending and leveling is difficult.
또한 구동장치가 회전판의 내부에 설치됨으로 인해 안전성 및 유지보수에 불편한 문제점이 발생되었다.In addition, the driving device is installed inside the rotating plate has caused a problem of safety and maintenance uncomfortable.
그리고 종래의 기술은 용탕주입시 대기중의 공기와의 접촉을 차단하는 장치가 없어 스컴(Scum)이 발생되는 문제점이 발생되었다.In the prior art, there is no device for blocking contact with air in the air during injection of a molten metal.
또한 종래의 기술은 냉각수파이프가 지하에 매설된 상태에서 상부로 연장되어 분배통과 연결됨으로 인해 회전판이 회전하는 과정에서 누수현상이 발생되는 문제점 또한 발생되었고, 이로 인하여 유지 보수하는데 상당한 불편한 점이 발생되었던 것이다.In addition, the prior art also has a problem that the leakage occurs during the rotation of the rotating plate due to the cooling water pipe is buried underground and connected to the distribution cylinder to the upper portion, which caused a significant inconvenience in maintenance .
더 나아가서 종래에는 작업자가 햄머로 때려서 몰드와 제품을 이완시켰던 것이나, 그 작업이 매우 어렵고 안전하지 못하다는 문제점이 있었다.Furthermore, in the related art, a worker hits with a hammer to relax a mold and a product, but there is a problem that the work is very difficult and unsafe.
또한 종래에는 몰드에 주입되는 비철금속물의 양을 정확한 계량을 할 수 없어 제품의 일정 중량의 유지가 어렵다는 문제점 등이 발생되었다.In addition, there is a problem in that it is difficult to maintain a certain weight of the product because it can not accurately measure the amount of non-ferrous metal injected into the mold.
본 발명은 상기와 같은 종래 기술의 제반 문제점을 해소하기 위하여 안출한 것으로, 용탕주입시 발생되는 스컴(Scum)을 억제함과 동시에 질소나 아르곤가스를 주입하여 용탕표면을 미려하고 표면변화가 없도록 함은 물론 발생된 열을 이용하여 응고시간을 조절하여 표면의 수평상태를 유지시킴을 제1목적으로 하는 것이고, 제2목적은 회전판의 하단에 구비된 로울러가 레일면의 수평도에 따라 일정하게 유지되므로 종래와 같이 휨에 의해 발생되는 진동을 방지할 수 있도록 한 것이며, 제3목적은 회전판을 구동하는 구동장치를 외부에 설치하여 유지보수가 용이하고 작업중에도 항상 기계상태를 점검할 수 있도록 한 것이고, 제4목적은 용탕주입시 공기접촉을 최소화하기 위해 상부커버를 구비하여 스컴(Scum)발생을 최소화 하는 것이고, 제5목적은 파이프와 분배통이 상호 이격되어도 누수현상이 없도록 함은 물론 분배통이 냉각통보다 높게 설치되어 있어 자연 낙차에 의하여 각각의 냉각통에 냉각수를 공급할 수 있도록 한 것이며, 제6목적은 햄머실린더와 바이브레이터의 진동과 충격을 이용하여 제품을 손쉽게 몰드에서 이탈시킬 수 있도록 한 것이고, 제7목적은 주입장치의 하단 적소에 로드셀(load cell)을 구비하여 탕도에서 용융된 비철금속물이 통과되는 량을 연산방법으로 산정하여 규정량에 도달하면 실린더가 상승과 동시에 비철금속물 투입이 정지되도록 한 것이며, 제8목적은 상기와 같은 기술적 작용에 의해 고온물질의 취급에 따른 안전성을 확보하여 제품을 품질과 신뢰성을 대폭 향상시킬 수 있도록 한 회전식 연속 주조장치를 제공한다.The present invention has been made in order to solve the problems of the prior art as described above, while suppressing the scum (Scum) generated during the injection of the molten metal by injecting nitrogen or argon gas to make the surface of the molten metal beautiful and there is no surface change Of course, the first purpose is to maintain the horizontal state of the surface by adjusting the solidification time by using the heat generated, the second purpose is to maintain a constant roller according to the horizontal level of the rail provided on the bottom of the rotating plate Therefore, it is possible to prevent the vibration caused by bending as in the prior art, and the third purpose is to install a drive device for driving the rotating plate to the outside to facilitate maintenance and to check the machine status at all times during work , The fourth purpose is to minimize the occurrence of scum by having an upper cover to minimize the air contact when injecting molten metal, the fifth purpose is to Even if the distribution cylinders are spaced apart from each other, there are no leaks, and the distribution cylinders are installed higher than the cooling cylinders so that the cooling water can be supplied to each cooling cylinder by a natural drop. The sixth object is the vibration of the hammer cylinder and the vibrator. The product can be easily removed from the mold by using the impact and the seventh purpose is to provide a load cell at the bottom of the injection device to calculate the amount of non-ferrous metals melted in the water flow through the calculation method When the calculated amount is reached, the cylinder rises and the non-ferrous metals are stopped at the same time.The eighth objective is to secure the safety of the handling of high temperature materials by the above technical action, and greatly improve the quality and reliability of the product. Provided is a rotary continuous casting device.
이러한 목적 달성을 위하여 본 발명은 회전식 연속 주조장치에 있어서, 바닥면의 센터축을 중심으로 회전하며, 외주면에 기어치가 형성된 회전판; 상기 기어치와 상호 맞물려 회전되게 평기어가 구비되며, 이 평기어를 구동시키는 모터; 상기 회전판의 하단 적소에 적어도 두개 이상의 레일상에 설치되는 2셋트의 로울러와, 이 로울러가 상단에 위치하여 이동되도록 바닥면의 적소에 형성되는 적어도 두개 이상의 레일; 상기 회전판의 상단 중앙에 설치되며, 상부의 냉각수공급파이프를 통해 이송된 물을 수납시키는 냉각수분배통; 상기 회전판의 상단 적소에 일정간격으로 다수개 설치되며, 냉각수분배통의 물이 자유낙하에 의해 일측으로 흘러 들어와 타측으로 배출시키는 냉각통; 상기 각각의 냉각통의 내부에 설치되며, 비철금속물이 주입되어 제품을 주조하는 몰드; 용해로의 비철금속물을 상·하부 탕도를 통해 몰드로 주입하며, 상기 하부 탕도를 실린더로 작동시키는 주입장치로 이루어짐을 특징으로 하는 회전식 연속 주조장치를 제공한다.In order to achieve the above object, the present invention provides a rotary continuous casting apparatus, comprising: a rotating plate rotating around a center axis of a bottom surface and having gear teeth formed on an outer circumferential surface thereof; A spur gear is provided to rotate in engagement with the gear tooth, the motor for driving the spur gear; Two sets of rollers installed on at least two rails at the lower end of the swivel plate, and at least two rails formed at the bottom of the roller so that the rollers are positioned at the top; A cooling water distribution container installed at the upper center of the rotating plate and configured to receive water transferred through the upper cooling water supply pipe; A plurality of cooling cylinders installed at predetermined intervals at an upper end of the rotating plate, and cooling water distribution cylinders flow into one side by free fall and discharge to the other side; A mold installed in each of the cooling cylinders and injecting non-ferrous metals to cast a product; It provides a rotary continuous casting device characterized in that the non-ferrous metal of the melting furnace is injected into the mold through the upper and lower runway, the injection device for operating the lower runway in a cylinder.
이하에서는 이러한 목적 달성을 위한 본 발명의 바람직한 실시예를 첨부된 도면에 따라 상세히 설명하면 다음과 같다.Hereinafter, described in detail with reference to the accompanying drawings a preferred embodiment of the present invention for achieving this purpose are as follows.
도 1 은 본 발명에 적용된 회전식 연속 주조장치를 나타낸 부분 정단면도.1 is a partial front cross-sectional view showing a rotary continuous casting apparatus applied to the present invention.
도 2 는 본 발명에 적용된 회전식 연속 주조장치를 나타낸 평면도.Figure 2 is a plan view showing a rotary continuous casting apparatus applied to the present invention.
도 3 은 본 발명에 적용된 회전판의 기어치를 다른 실시예로 구성한 부분 확대 평면도.Figure 3 is a partially enlarged plan view of the gear teeth of the rotating plate applied to the present invention in another embodiment.
도 4 는 본 발명의 회전식 연속 주조장치의 다른 실시예의 부분 정단면도.4 is a partial front sectional view of another embodiment of the rotary continuous casting device of the present invention.
도 5 는 본 발명 몰드부분의 구성을 다른 실시예로 구성한 부분 정단면도.5 is a partial front cross-sectional view of another embodiment of the configuration of the mold portion of the present invention.
도 6 은 본 발명에 적용된 몰드부분의 구성을 또 다른 실시예로 구성한 부분 정단면도.Figure 6 is a partial front cross-sectional view of the configuration of the mold portion applied to the present invention in another embodiment.
도 7 은 본 발명에 적용된 상부커버를 다른 실시예로 구성한 부분 정단면도.Figure 7 is a partial front cross-sectional view of the upper cover applied in another embodiment of the present invention.
도 8 은 본 발명의 회전식 연속 주조장치를 이용하여 제조된 제품을 이탈시키 위한 구성을 보인 부분 정단면도.Figure 8 is a partial front cross-sectional view showing a configuration for leaving the product produced using the rotary continuous casting apparatus of the present invention.
〈도면의 주요 부분에 대한 부호의 설명〉<Explanation of symbols for main parts of drawing>
20 : 회전판 30 : 냉각통20: rotating plate 30: cooling cylinder
40 : 상부커버 50 : 냉각수분배통40: upper cover 50: cooling water distribution container
60 : 주입장치 70 : 햄머실린더60: injection device 70: hammer cylinder
80 : 배출부 100 : 실린더80: discharge part 100: cylinder
본 발명에 적용된 회전식 연속 주조장치는 도 1 내지 도 8 에 도시된 바와 같이 구성되는 것으로, 여기서 부호 20은 바닥면(10)의 센터축(23)을 중심으로 회전하며, 외주면에는 기어치(21)가 형성된 회전판(20)이다.Rotary continuous casting apparatus applied to the present invention is configured as shown in Figures 1 to 8, wherein reference numeral 20 rotates around the center axis 23 of the bottom surface 10, the gear teeth 21 on the outer peripheral surface Is a rotating plate 20 formed.
이때 상기 기어치(21)의 일측에는 기어치(21)와 상호 맞물려 회전되게 평기어(26)가 구비되며, 이 평기어(26)는 감속기(27)와 연결된 모터(25)의 구동에 의해 회전하도록 구성된다.At this time, one side of the gear tooth 21 is provided with a spur gear 26 to rotate in engagement with the gear tooth 21, the spur gear 26 is driven by the motor 25 connected to the reducer 27 Configured to rotate.
본 발명에서는 도 3 에 도시된 바와 같이 상기 회전판(20)의 외주면에 기어치(21) 대신 래치기어(28)를 형성하고, 이 래치기어(28)를 래치실린더(29)가 선택적으로 작동하여 밀면 회전판(20)이 소정간격만큼 회전되도록 구성함은 물론이다.In the present invention, as shown in FIG. 3, the latch gear 28 is formed on the outer circumferential surface of the rotating plate 20 instead of the gear tooth 21, and the latch cylinder 29 is selectively operated to operate the latch gear 28. Of course, the push surface rotating plate 20 is configured to rotate by a predetermined interval.
또한 상기 회전판(20)의 하단 적소에는 각각 적어도 두개 이상 로울러(22)가 설치되고, 이 로울러(22)가 상단에 위치하여 이동되도록 바닥면(10)의 적소에는 적어도 두개 이상의 레일(11)이 형성되며, 상기 바닥면(10)의 적소에는 배출로(12)가 형성된다.In addition, at least two rollers 22 are installed at the lower end of the rotating plate 20, and at least two rails 11 are disposed at the bottom surface 10 so that the rollers 22 are positioned at the upper end thereof. Is formed, the discharge path 12 is formed in place of the bottom surface (10).
또한 상기 회전판(20)의 상단 중앙에는 상부의 냉각수공급파이프(51)를 통해 이송된 물을 수납시키는 냉각수분배통(50)이 설치되고, 상기 회전판(20)의 상단 적소에는 냉각수분배통(50)의 물이 자유낙하에 의해 일측으로 흘러 들어와 타측으로 배출시키는 냉각통(30)이 일정 간격으로 다수개 설치된다.In addition, a cooling water distribution tank 50 for receiving the water transferred through the upper cooling water supply pipe 51 is installed in the center of the upper end of the rotating plate 20, the cooling water distribution tank 50 in the upper position of the rotating plate 20. ) Is provided with a plurality of cooling cylinders (30) for flowing water to one side by free fall and discharge to the other side at regular intervals.
그리고 본 발명에서는 상기 각각의 냉각통(30)의 내부에 비철금속물이 주입되어 제품을 주조하는 몰드(31)가 구비되는 한편 용해로(1)의 비철금속물을 상·하부 탕도(61)(62)를 통해 몰드(31)로 주입하며, 상기 하부탕도(62)를 실린더(100)로 작동시키는 주입장치(60)로 이루어지는 것이다.In the present invention, a mold 31 for casting a product by injecting a non-ferrous metal material into the respective cooling cylinders 30 is provided, while the non-ferrous metal material of the melting furnace 1 is provided with upper and lower inlets 61 and 62. Injecting into the mold 31 through the), it is composed of the injection device 60 for operating the lower tap water 62 to the cylinder (100).
이때 도 5 에 도시된 바와 같이 상기 몰드(31)의 내부 적소에는 실린더(100)의 작동에 의해 상하로 동작되고, 버너(36)에서 발생된 열이 몰드(31)의 바닥면과 측면을 골고루 가열하여 몰드(31)내면을 일정온도로 유지시키는 동시에 예열시간을 단축시키는 가이드판(35)이 구비됨은 물론이다.In this case, as shown in FIG. 5, the inside of the mold 31 is vertically operated by the operation of the cylinder 100, and the heat generated from the burner 36 is evenly distributed on the bottom and side surfaces of the mold 31. Of course, the guide plate 35 for heating the mold 31 to maintain a constant temperature at the same time and shorten the preheating time is provided.
그리고 이때 도 6 에 도시된 바와 같이 주조후 한핏치 이동후 제품이 응고시 상기 몰드(31)의 상단에는 가열된 질소나 아르곤가스가 주입되는 상부커버(40)가 선택적으로 씌워지고, 이 몰드(31)와 상부커버(40)의 내부에는 가열파이프(42)가 구비되어 질소나 아르곤가스가 응고되기 시작하는 부분을 가열하여 용탕 응고시 전표면을 일정온도로 유지시켜 응고시 표면상태를 일정하게 유지시키도록 구성됨은 물론이다.In this case, as shown in FIG. 6, when the product is solidified after casting by one pitch, the upper cover 40 into which the heated nitrogen or argon gas is injected is selectively covered with the mold 31, and the mold 31 is covered. ) And the upper cover 40 is provided with a heating pipe 42 to heat the portion where nitrogen or argon gas starts to solidify, thereby maintaining the entire surface at a constant temperature during solidification, and thus maintaining a constant surface state during solidification. Of course, it is configured to.
또한 도 7 에 도시된 바와같이 주조시 질소나 아르곤가스가 주입되어 상기 몰드(31)의 상단에는 실린더(100)의 작동에 의해 열을 배출시키는 상부커버(40)가 선택적으로 씌워지고, 상부커버(40)의 내부에는 지그재그로 간격판(41)이 형성되어 내부에서 발생되는 가스의 온도를 최대한 상승시킬 수 있도록 구성됨은 물론이며, 이때 이곳에서 고온으로 가열된 가스가 도 6 의 배관으로 전달되도록 구성된다.In addition, as shown in FIG. 7, nitrogen or argon gas is injected during casting to selectively cover the upper end of the mold 31 to discharge heat by the operation of the cylinder 100. In the interior of the 40, a zigzag spacer plate 41 is formed to increase the temperature of the gas generated therein as much as possible, and of course, in this case, the gas heated at a high temperature is transferred to the pipe of FIG. 6. It is composed.
도 8 은 상기 몰드(31)의 상단 양측에 응고된 제품을 인출하기 위해 몰드(31)에 충격을 가해 제품과 몰드(31)가 상호 분리되도록 한 햄머실린더(70)가 구비되고, 상기 제품의 상단 적소에는 진동에 의해 몰드와 제품을 상호 떨어지게 하는 바이브레이터(71)가 구비되며, 상기 제품에는 고정된 볼트(72)에 와이어를 상호 연결한 후 이 와이어에 크레인(81)을 걸어 상부로 들어올려 일정장소로 이송시키는 배출부(80)가 구비된다.8 is provided with a hammer cylinder 70 which impacts the mold 31 so as to separate the product and the mold 31 from each other in order to take out the solidified product on both sides of the upper end of the mold 31. The upper part is provided with a vibrator 71 which separates the mold and the product from each other by vibration. The product has a wire 81 connected to the fixed bolt 72 and then hangs the crane 81 on the wire to lift it upward. Discharge part 80 for transferring to a certain place is provided.
또한 도 4 에 도시된 바와 같이 본 발명에서는 상기 상부탕도(61)의 내부 적소에 용해로(1)에서 출탕될때의 용융금속에 포함된 스컴(Scum)을 제거하는 제거판(64)이 구비되어 구성됨은 물론이고, 상기 주입장치(60)의 하단 적소에 로드셀(load cell)(63)을 구비하여 탕도(61)(62)에서 용융된 비철금속물이 통과되는 량을 연산방법으로 산정하여 규정량에 도달하면 실린더(100)가 상승과 동시에 비철금속물 투입이 정지되도록 구성함은 물론이다. 이때 다음 핏치에 몰드가 올 수 있게 모터(도면상 미 도시함)에 의해 회전하게 된다.In addition, as shown in Figure 4 in the present invention is provided with a removal plate 64 for removing the scum (Scum) contained in the molten metal when tapping in the melting furnace 1 in the inner place of the upper waterway (61) Of course, by providing a load cell (63) at the lower end of the injection device 60, the amount of non-ferrous metals melted in the waterway (61, 62) is calculated by calculating the calculation method When the amount is reached, the cylinder 100 rises and at the same time configured to stop the non-ferrous metals input. At this time it is rotated by a motor (not shown in the figure) so that the mold comes to the next pitch.
또한 상기 하부탕도(62)의 입구에는 질소나 아르곤가스를 투입시켜 용융금속이 공기와의 접촉을 피하도록 하고, 몰드(31)의 상단에는 공기와의 접촉을 최소화하기 위해 실린더의 작동에 의해 상부커버(40)가 개폐되도록 구성할 수 있다.In addition, by injecting nitrogen or argon gas into the inlet of the lower tap 62 to prevent the molten metal from contact with air, and by the operation of the cylinder to minimize the contact with air at the top of the mold 31 The upper cover 40 may be configured to open and close.
상기와 같이 구성된 본 발명 회전식 연속 주조장치의 작용은 다음과 같다.The action of the present invention, the rotary continuous casting device configured as described above is as follows.
우선, 도 1, 2 도 및 도 4 도에 도시된 바와 같이 용해로(1)의 비철금속물이 상·하부탕도(61)(62)를 통해 흘러 내려가 몰드(31)에 주입되는 것으로, 이때 주입장치(60)에 구비된 로드셀(63)은 비철금속물의 일정량을 산정하여 규정량에 도달하면 실린더(100)에 신호를 보내 상승 작동시켜 몰드(31)로의 비철금속물 투입을 정지시킨다.First, as shown in FIGS. 1, 2 and 4, non-ferrous metals of the melting furnace 1 flow down through the upper and lower wet and cold water 61 and 62 and are injected into the mold 31. The load cell 63 included in the device 60 calculates a certain amount of the nonferrous metal and reaches a predetermined amount to signal the cylinder 100 to ascend and stop the input of the nonferrous metal into the mold 31.
본 발명에서는 도 4 에 도시된 바와 같이 다른 실시예로 상기 상부탕도(61)의 입구에 제거판(64)을 구비하여 비철금속물이 하부탕도(62)로 흘러 내려가는 과정에서스컴(Scum)을 제거하는 동시에 상기 하부탕도(62)의 입구에는 질소나 아르곤가스를 투입시켜 비철금속물이 공기와의 접촉을 최소화하도록 하여 스컴(Scum) 발생을 억제시키게 된다.In another embodiment of the present invention, as shown in FIG. 4, a scum is provided in a process in which a non-ferrous metal is flowed down to the lower tap 62 by having a removal plate 64 at an inlet of the upper tap 61. At the same time, nitrogen or argon gas is injected into the inlet of the lower bath 62 to minimize the contact of non-ferrous metals with air, thereby suppressing the occurrence of scum.
상기와 같이 상태에서 본 발명에 구비된 회전판(20)은 센터축(23)을 중심으로 회전하게 되는데, 이때 상기 회전판(20)은 회전판(20)의 일측에 구비된 모터(25)와 감속기 그리고 회전판(20)의 외주면에 형성된 기어치(21)에 맞물린 평기어(26)의 구동에 의해 회전하게 된다.In the state as described above, the rotating plate 20 provided in the present invention is rotated about the center shaft 23, wherein the rotating plate 20 is provided with a motor 25 and a reducer provided on one side of the rotating plate 20 and It rotates by the drive of the spur gear 26 meshed with the gear tooth 21 formed in the outer peripheral surface of the rotating plate 20.
본 발명에서는 상기 회전판(20)의 구동을 도 3 에 도시된 바와 같이 다른 실시예로 구성하여 구동시킬 수 있도록 한 것으로, 회전판(20)의 외주면에 래치기어(28)를 형성하고, 이 래치기어(28)는 래치실린더(29)의 선택적인 전진 작동에 의해 회전판(20)을 일정각도로 회전시켜 작동시키는 것이다.In the present invention, the drive of the rotating plate 20 is configured to drive in another embodiment as shown in Figure 3, the latch gear 28 is formed on the outer peripheral surface of the rotating plate 20, the latch gear Reference numeral 28 is to rotate the rotary plate 20 by a predetermined angle by the selective forward operation of the latch cylinder 29 to operate.
상기와 같이 작동하는 과정에서 본 발명은 회전판(20)의 하단 적소에는 로울러(22)를 설치하고, 바닥면(10)의 적소에는 상기 로울러(22)가 이동될 수 있도록 두개의 레일(11)을 형성하므로, 상기 회전판(20)은 레일면의 수평도에 따라 일정하게 유지되므로 중량물인 몰드(31)의 수평과 휨에 의하여 생기는 진동도 방지할 수 있게 된다.In the process of operating as described above, the present invention is installed in the lower end of the rotating plate 20, the roller 22, the two rails 11 so that the roller 22 is moved in place of the bottom surface (10). Since the rotating plate 20 is kept constant according to the horizontal level of the rail surface it is also possible to prevent the vibration caused by the horizontal and warp of the heavy mold 31.
한편 도 5 에 도시된 바와 같이 상기 몰드(31)에 비철금속물을 투입하기 전에 예열장치를 이용하여 몰드(31) 전체를 예열하게 되는 것으로, 실린더(100)의 하강에 의해 가이드판(35)이 몰드(31)의 내부에 근접 위치하면 버너(36)에서 발생된 열에 의해 몰드(31)의 내부 전체를 골고루 예열시키게 된다.Meanwhile, as shown in FIG. 5, the entire mold 31 is preheated by using a preheating device before the non-ferrous metal is introduced into the mold 31. The guide plate 35 is lowered by the lowering of the cylinder 100. When located close to the inside of the mold 31, the entire heat of the mold 31 is evenly preheated by the heat generated from the burner 36.
도 4 는 상기와 같이 몰드(31)를 예열시키면 전술한 주입장치(60)에 의해 몰드(31) 내부로 비철금속물이 투입되는 것으로, 본 발명에서는 상기 몰드(31)의 상단에 상부커버(40)를 씌워 비철금속물이 공기와의 접촉을 피하도록 하여 스컴(Scum) 발생을 최소화 할 수 있도록 한 것이다.FIG. 4 illustrates that the non-ferrous metal is introduced into the mold 31 by the above-described injection device 60 when the mold 31 is preheated as described above. In the present invention, the upper cover 40 is disposed on the upper end of the mold 31. ), So that non-ferrous metals avoid contact with air, so that the occurrence of scum is minimized.
또한 본 발명은 도 7 에 도시된 바와 같이 비철금속물을 몰드(31)에 투입시 상부커버(40)는 실린더(100)의 동작에 의해 하강하여 몰드(31)의 상면에 밀착시키는 것이고, 이와 같은 상태에서 질소나 아르곤가스를 내부로 투입시키면 비철금속물을 주입하면서 공기를 차단하여 스컴(Scum) 발생을 방지하고 공급되는 가스는 주입된 열에 의하여 가열되고 열이 올라가면 간격판(41)을 가스가 지그재그로 통과하면서 가열하게 된다.In addition, in the present invention, when the non-ferrous metal is introduced into the mold 31 as shown in FIG. 7, the upper cover 40 is lowered by the operation of the cylinder 100 to closely adhere to the upper surface of the mold 31. When nitrogen or argon gas is introduced into the gas in a state, the air is blocked while injecting non-ferrous metals to prevent the occurrence of scum, and the supplied gas is heated by the injected heat, and when the heat rises, the gas is zigzag in the spacer plate 41. It is heated while passing through.
한편 본 발명에서는 도 6 에 도시된 바와 같이 가열된 가스는 다음 몰드(31)에서 제품 표면에 가열파이프(42)에 의해 먼저 냉각되는 외부를 가열되게 된다.Meanwhile, in the present invention, as shown in FIG. 6, the heated gas is heated outside of the first cooled by the heating pipe 42 on the surface of the product in the next mold 31.
본 발명에서는 가열된 몰드(31)를 냉각시키기 위해 몰드(31)의 외주연이 냉각통(30)으로 구성되는 것으로, 상부 냉각수공급파이프(51)를 통해 하부 냉각수분배통(50)으로 공급된 냉각수는 자연 낙차에 의해 상기 냉각통(30)의 일측으로 투입된 후 타측의 배출구를 통해 배출로(12)로 배출되는 것이다.In the present invention, the outer periphery of the mold 31 is configured as a cooling cylinder 30 to cool the heated mold 31, and is supplied to the lower cooling water distribution tank 50 through the upper cooling water supply pipe 51. The cooling water is discharged to the discharge path 12 through the discharge port on the other side after being injected into one side of the cooling barrel 30 by the natural drop.
도 8 은 상기와 같은 동작에 의해 배출부(80)에 도달하면 제품에 부착된 볼트(72)(비철금속물을 투입하기 전에 미리 몰드 내부에 수납시킴)에 와이어를 연결시킨 후 이 와이어에 크레인(81)을 걸고 이후 크레인(81)이 약간 상승시킨다.FIG. 8 shows that when the discharge portion 80 is reached by the above-described operation, the wire is connected to the bolt 72 attached to the product (preceived in the mold before the non-ferrous metal is added) and then the crane ( 81) and then the crane 81 is slightly raised.
이와 같이 크레인(81)에 의해 상승되는 제품은 햄머실린더(70)가 지그재그로 몰드(31)에 충격을 가하는 동시에 제품의 상단에 위치한 바이브레이터(71)가 진동을 발생시키면 몰드(31)와 제품이 상호 이탈되고, 이때 상기 크레인(81)은 계속 상승하여 몰드(31)에서 제품을 이탈시키 별도의 장소로 제품을 이동시키게 된다.As such, the product lifted by the crane 81 causes the mold cylinder 31 and the product to vibrate when the hammer cylinder 70 zigzags the mold 31 and the vibrator 71 located at the top of the product generates vibration. In this case, the crane 81 continues to ascend to move the product to a separate place by removing the product from the mold 31.
본 발명은 상기와 같은 동작은 계속적으로 반복됨으로 제품의 대량 생산이 가능하게 된다.The present invention allows the mass production of the product as the above operation is repeated continuously.
이상과 같이 본 발명은 용탕주입시 발생되는 스컴(Scum)을 억제함과 동시에 질소나 아르곤가스를 주입하여 용탕표면을 미려하고 표면변화가 없도록 함은 물론 발생된 열을 이용하여 응고시간을 조절하여 표면의 수평상태를 유지시킬 수 있도록 한 것이고, 회전판의 하단에 구비된 로울러가 두개의 레일면의 수평도에 따라 일정하게 유지되므로 종래와 같이 휨에 의해 발생되는 진동을 방지할 수 있도록 한 것이다. 그리고 회전판을 구동하는 구동장치를 외부에 설치하여 유지보수가 용이하고 작업중에도 항상 기계상태를 점검할 수 있도록 한 것이고, 용탕주입시 공기접촉을 최소화하기 위해 상부커버를 구비하여 스컴(Scum)발생을 최소화 하는 것이고, 파이프와 분배통이 상호 이격되어도 누수현상이 없도록 함은 물론 분배통이 냉각통보다 높게 설치되어 있어 자연 낙차에 의하여 각각의 냉각통에 냉각수를 공급할 수 있도록 한 것이다. 또한 햄머실린더와 바이브레이터의 진동과 충격을 이용하여 제품을 손쉽게 몰드에서 이탈시킬 수 있도록 한 것이고, 주입장치의 하단 적소에 로드셀(load cell)을 구비하여 탕도에서 용융된 비철금속물이 통과되는 량을 연산방법으로 산정하여 규정량에 도달하면 실린더가 상승과 동시에 비철금속물 투입이 정지되도록 한 것이며, 상기와 같은 기술적 작용에 의해 고온물질의 취급에 따른 안전성을 확보하여 제품을 품질과 신뢰성을 대폭 향상시킬 수 있도록 한 매우 유용한 발명인 것이다.As described above, the present invention suppresses the scum generated during the injection of the molten metal and simultaneously injects nitrogen or argon gas to beautifully melt the surface of the molten metal and prevent surface changes, and to adjust the solidification time by using the generated heat. It is to maintain the horizontal state of the surface, the roller provided at the bottom of the rotating plate is kept constant according to the horizontal level of the two rails to prevent vibration caused by bending as in the prior art. In addition, it is easy to maintain and always check the state of the machine even during work by installing the driving device to drive the rotating plate outside, and it is equipped with the top cover to minimize the air contact during the injection of molten metal. Minimization, and even if the pipe and the distribution tank is spaced apart from each other, there is no leakage phenomenon, as well as the distribution tank is installed higher than the cooling cylinder to supply the cooling water to each cooling cylinder by the natural drop. In addition, the vibration and impact of the hammer cylinder and the vibrator allows the product to be easily removed from the mold. A load cell is provided at the lower end of the injection device to allow the molten non-ferrous metal to pass through the water. When the calculated amount is reached and the specified amount is reached, the cylinder rises and the non-ferrous metal input is stopped.The above technical action ensures the safety of handling high temperature materials and greatly improves the quality and reliability of the product. It is a very useful invention.
Claims (9)