KR102671862B1 - 친환경 수성 주차장 바닥용 표면 마감구조 및 이를 이용한 바닥표면마감공법 - Google Patents
친환경 수성 주차장 바닥용 표면 마감구조 및 이를 이용한 바닥표면마감공법 Download PDFInfo
- Publication number
- KR102671862B1 KR102671862B1 KR1020230086029A KR20230086029A KR102671862B1 KR 102671862 B1 KR102671862 B1 KR 102671862B1 KR 1020230086029 A KR1020230086029 A KR 1020230086029A KR 20230086029 A KR20230086029 A KR 20230086029A KR 102671862 B1 KR102671862 B1 KR 102671862B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- water
- layer
- parts
- parking lot
- Prior art date
Abstract
본 발명은 친환경 수성 주차장 바닥용 표면 마감구조 및 이를 이용한 바닥표면마감공법에 관한 것으로, 보다 상세하게는 주차장 바닥면에 도장된 유성 타입의 마감재로 인한 유해성과 바닥면 크랙시 함께 발생되는 도장면 크랙으로 인한 유지보수기간 단축, 그에 따른 비용증가를 줄이고 인해 무해성의 친환경 도장면을 구현할 뿐만 아니라 도장면의 내구성을 향상시킬 수 있도록 개선된 친환경 수성 주차장 바닥용 표면 마감구조 및 이를 이용한 바닥표면마감공법에 관한 것이다.
Description
본 발명은 친환경 수성 주차장 바닥용 표면 마감구조 및 이를 이용한 바닥표면마감공법에 관한 것으로, 보다 상세하게는 주차장 바닥면에 도장된 유성 타입의 마감재로 인한 유해성과 바닥면 크랙시 함께 발생되는 도장면 크랙으로 인한 유지보수기간 단축, 그에 따른 비용증가를 줄이고 인해 무해성의 친환경 도장면을 구현할 뿐만 아니라 도장면의 내구성을 향상시킬 수 있도록 개선된 친환경 수성 주차장 바닥용 표면 마감구조 및 이를 이용한 바닥표면마감공법에 관한 것이다.
일반적으로 건축 현장에서 2액형 우레탄 도막 방수 공사나 1액형 우레탄 도막 방수 시공시 시멘트콘크리트 표면에 서로 부착이 잘되고, 외관이 평탄한 도막을 얻기 위하여 다량의 유기 용제 및 미반응된 톨루엔디이소시아네이트가 포함되어 있는 유성 우레탄 프라이머를 사용하고 있다.
유기계 프라이머는 벤젠, 톨루엔, 자일렌, 초산부틸, 메칠에틸케톤, 셀로솔브아세테이트등의 유독성 유기용제를 사용함으로써 작업시 심한 약품 냄새로 인하여 작업자의 두통이나 호흡곤란을 일으켜 안전사고를 유발할 뿐 아니라 작업자의 건강에 나쁜 영향을 끼친다.
특히, 도 1의 예시와 같이, 지하 주차장 바닥면을 도장할 때는 바닥면(10)에 에폭시 프라이머(20)를 칠한 후 에폭시 라이닝(30)으로 마감하게 된다.
하지만, 이 역시 유성 타입이기 때문에 지하 주차장 도장시에는 극심한 냄새 발생, 환경 유해물질(VOC) 발생 등의 문제가 생기고 있다.
뿐만 아니라, 유성 타입이기 때문에 습한 지하 주차장의 경우는 도장 불량이 발생되어 들뜸, 갈라짐, 벗겨짐 현상이 유발된다.
더구나, 바닥면에 크랙이 생기면 이와 함께 도장면에도 크랙이 함께 발생되는 단점이 있다.
이에, 친환경적인 수용성 도료의 개발이 활발하게 이루어지고 있다.
그럼에도 불구하고, 피도막면인 시멘트, 몰탈, 콘크리트 아스콘, 등의 바닥면에 대한 충분한 접착력을 갖지 못하거나, 내구성이나 강도 등의 물성이 떨어지거나 불량한 작업 특성을 갖는 등의 문제가 아직까지 남아 있다.
본 발명은 상술한 바와 같은 종래 기술상의 제반 문제점들을 감안하여 이를 해결하고자 창출된 것으로, 주차장 바닥면에 도장된 유성 타입의 마감재로 인한 유해성과 바닥면 크랙시 함께 발생되는 도장면 크랙으로 인한 유지보수기간 단축, 그에 따른 비용증가를 줄이고 인해 무해성의 친환경 도장면을 구현할 뿐만 아니라 도장면의 내구성을 향상시킬 수 있도록 개선된 친환경 수성 주차장 바닥용 표면 마감구조 및 이를 이용한 바닥표면마감공법를 제공함에 주된 목적이 있다.
본 발명은 상기한 목적을 달성하기 위한 수단으로, 주차장 바닥면의 상면에 수성 프라이머 조성물로 도포 형성되는 프라이머층과, 상기 프라이머층의 상면에 1차 수성 조성물로 도포 형성되는 1차 중도층과, 상기 1차 중도층 위에 메쉬로 부착되는 메쉬층과, 상기 메쉬층 위에 2차 수성 조성물로 도포 형성되는 2차 중도층을 포함하는 친환경 수성 주차장 바닥용 표면 마감구조를 제공한다.
본 발명에 따르면, 주차장 바닥면에 도장된 유성 타입의 마감재로 인한 유해성과 바닥면 크랙시 함께 발생되는 도장면 크랙으로 인한 유지보수기간 단축, 그에 따른 비용증가를 줄이고 인해 무해성의 친환경 도장면을 구현할 뿐만 아니라 도장면의 내구성을 향상시킬 수 있도록 개선된 효과를 얻을 수 있다.
도 1은 종래 기술에 따른 주차장 도장 구조를 보인 모식도이다.
도 2는 본 발명에 따른 주차장 도장 구조를 보인 모식적인 단면도이다.
도 2는 본 발명에 따른 주차장 도장 구조를 보인 모식적인 단면도이다.
이하에서는, 본 발명에 따른 바람직한 실시예를 보다 상세하게 설명하기로 한다.
본 발명에 따른 친환경 수성 주차장 바닥용 표면 마감구조는 도 2의 예시와 같이, 바닥면(100)의 상면에 도포된 수성 프라이머로 도포된 프라이머층(200)과, 상기 프라이머층(200)의 상면에 1차 수성 조성물로 도포 형성되는 1차 중도층(300)과, 상기 1차 중도층(300) 위에 메쉬로 부착되는 메쉬층(400)과, 상기 메쉬층(400) 위에 2차 수성 조성물로 도포 형성되는 2차 중도층(500)을 포함하고, 경우에 따라 상기 2차 중도층(500) 위에 표면보호층인 상도층(600)이 더 형성될 수 있다.
이때, 바닥면(100)은 주차장 바닥면일 수 있다. 특히, 지하 주차장 바닥면일 수 있다.
그리고, 상기 프라이머층(200)은 수성 프라이머 조성물로 도포되되, 수성 프라이머 조성물은 아크릴 에멀젼 10-40중량%, 첨가제 0.01-5.0중량% 및 나머지 물로 이루어진다.
여기에서, 첨가제는 소포제 및 레벨링제이며, 총 합이 상기 범위가 되게 첨가될 수 있다. 바람직하게는 소포제 0.005-2.5중량%, 레벨링제 0.005-2.5중량%가 될 수 있다. 이들 첨가제는 당해 분야해서 흔히 사용하는 공공연한 물질들로 소량 사용하는 것이기 때문에 이들을 특별히 한정할 필요는 없다.
다만, 부연설명하자면 소포제는 미네랄오일계, 실리콘계, 비실리콘계 폴리머 중에서 어느 하나를 사용할 수 있고, 바람직하게는 시중에 시판중인 상품명 Depol CFC-112W(주식회사 청우씨에프씨)를 구매하여 사용할 수도 있다.
또한, 레벨링제는 도료의 흐름성을 조절하여 도료 표면에 발생할수 있는 오렌지필, 크레이터 등 여러 도장 결함의 발생을 방지, 개선하기 위해 소량 첨가되는 첨가제로서 폴리아크릴산알킬(Polyalkyl acrylate), 폴리알킬비닐에테르(Polyalkyl vinylether), 셀룰로오즈 아세테이트 부틸레이트(Cellulose acetate butylate), 디메틸 폴리실록산(di-methyl polysiloxane), 메틸페닐 폴리실록산(Methyl phenyl polysiloxane), 유기 변성 폴리실록산(Organic modifide polysiloxane), 불소계 계면활성제 등이 있고, 바람직하게는 시중에 시판중인 상품명 Letch CFC-60LP(주식회사 청우씨에프씨)를 구매하여 사용할 수도 있다.
그리고, 아크릴 에멀젼은 수성으로서 생활방수가 가능하고, 가격이 저렴하며, 인열 및 부착강도가 높고, 유기용제를 사용하지 않기 때문에 VOC가 발생되지 않으며, 인체에 무해하여 친환경적이고, 화재위험성이 없다.
이 경우, 상기 프라이머층(200)은 상기 수성 프라이머 조성물 100중량부에 대해, 6-브로모헥산산(6-bromohexanoic acid) 15중량부, 세레신(Ceresin) 10중량부, 카사바(Cassava) 분말 5중량부, 헥사메틸렌테트라민(hexamethylenetetramine) 10중량부를 더 첨가 혼합하여 도포 형성될 수 있다.
이때, 6-브로모헥산산(6-bromohexanoic acid)은 산소의 흡습 침투를 막아 하도막의 크랙과 파단을 막아 열화를 방지하기 위해 첨가된다.
또한, 세레신(Ceresin)은 결합력을 증대시키고 유화안정화를 유도하여 크랙 발생을 억제하고, 이를 통해 찢어짐을 방지하기 위해 첨가된다.
그리고, 카사바(Cassava) 분말은 전분계로서 점도를 조절한다.
아울러, 헥사메틸렌테트라민(hexamethylenetetramine)은 방부성을 강화시키면서 산성에서 염을 만들면서 분해되어 포름알데히드를 방출시켜 유해성을 제거하고 친환경성을 강화하기 위해 첨가된다.
이것은 특히, 습한 지하 주차장 환경에서도 도장성을 좋게 하기 위한 것이다.
한편, 1차 중도층(300)은 1차 수성 조성물로 도포되되, 1차 수성 조성물은 아크릴 에멀젼 10-50중량%, 첨가제 0.03-6.0중량%, 안료 0.01-10중량%, 폴리비닐알콜(PVA) 1-30중량% 및 나머지 물로 이루어진다.
이때, 첨가제는 상술한 소포제 0.01-2.0중량%, 레벨링제 0.01-2.0중량% 외에 증점제 0.01-2.0중량%가 될 수 있다. 이 경우, 증점제는 점성을 증가시키기 위한 것으로 젤라틴, 카제인, 나트륨, 구아검, 펙틴, 카라기난 등이 될 수 있고, 바람직하게는 시중에 시판중인 상품명 CIMA-310P(주식회사 청우씨에프씨)를 구매하여 사용할 수도 있다.
또한, 안료는 유기안료, 무기안료 둘 중 어느 하나를 사용할 수 있으며, 공지된 것이므로 구체적인 설명은 생략한다.
뿐만 아니라, 폴리비닐알콜은 높은 결정성 때문에 내화학성이 있고, 산화 과정에서 가교되기 때문에 실질적으로 산, 알칼리, 산화제에 대한 저항성이 뛰어나 크랙 발생을 억제하는 장점이 있어 첨가된다.
이와 같이, 1차 중도층(300)은 아크릴 에멀젼에 의한 탄성과 부착력을 높여 콘크리트 크랙에 대한 저항성을 강화시키기 위한 기능을 수행한다.
이것은 습한 지하 주차장 환경에서도 도장성을 강화시키기 위한 것이다.
덧붙여, 본 발명에서는 상기 1차 중도층(300)이 더 높은 탄성력과 크랙 저항성을 갖도록 상기 1차 수성 조성물 100중량부에 대해, 부틸셀루솔브아세테이트(Butyl Cellosolve Acetate) 10중량부, 글리세롤모노스테아레이트(Glycerol Mono stearate) 15중량부, 담마검(gum dammar) 10중량부를 더 첨가할 수 있다.
이 경우, 부틸셀루솔브아세테이트(Butyl Cellosolve Acetate)는 1차 수성 조성물의 점도를 조절하기 위해 첨가되고; 또한 글리세롤모노스테아레이트(Glycerol Mono stearate)는 CAS No, 123-94-4에 해당하는 물질로서, 수지 연화에 따른 1차 중도층(300)의 연성과 탄성을 증대시키면서 계면활성 기능에 따른 정전방지 특성도 구현하게 된다.
그리고, 담마검(gum dammar)은 소나무에서 얻어지는 수지로서 파열 저항성을 높이면서 탄성과 신축성을 높여 1차 중도층(300)의 탄성변형력을 증대시키는 특성을 구현한다.
또한, 상기 2-5mm 메쉬층(400)을 구성하는 메쉬는 유리섬유, 나일론, 철 등을 엮어서 아래 그림과 같이 2-5mm의 격자 규격을 갖도록 구성할 수 있고, 1차 중도층(300) 위에 부착된다.
이 경우, 부착 방식은 메쉬에 접착성능이 있는 경우는 그냥 부착만하면 되고, 메쉬에 접착성능이 없는 경우는 1차중도층 위에 접착제를 도포하면서 메시를 부착하는 방식으로 시공할 수 있다.
물론, 후자보다 전자가 공정상 더 편리하고 공사일수를 더 단축시킬 수 있다.
이러한 메쉬층(400)은 1차 중도층(300)에서 생길 수 있는 크랙 발생에너지를 2차 중동층(500) 및 상도층(600)으로 전달되지 못하도록 흡수 차단하는 기능을 수행한다.
이것은 메쉬층(400) 자체의 유연성, 탄성변형성, 격자로 인한 에너지 분산성에 의해 달성된다.
다른 한편, 2차 중도층(500)은 2차 수성 조성물로 도포되되, 2차 수성 조성물은 아크릴 에멀젼 10-50중량%, 첨가제 0.03-6.0중량%, 폴리비닐알콜(PVA) 1-30중량% 및 나머지 물로 이루어진다.
이때, 첨가제는 앞서 설명하였던 1차 수성 조성물의 소포제, 레벨링제, 증점제와 같다.
특히, 2차 중도층(500)은 최종 마감재일 수도 있기 때문에 외부 충격에 강하고, 불연성을 갖도록 이에 더하여, 2차 수성 조성물 100중량부에 대해, 수산화알루미늄 5중량부, 디페닐포스포릴 아자이드(diphenylphosphoryl azide) 10중량부, 폴리옥시에틸렌라우릴에테르(Poly oxyethylene Lauryl ether) 5중량부, 팽창흑연(Exandable Graphite) 10중량부, 스테아르산아연(Zinc Stearate) 5중량부를 더 첨가할 수 있다.
이때, 수산화알루미늄은 폴리머의 소수화를 막고 친수화를 유도하여 결합력을 높이면서 불연성을 강화시키기 위해 첨가되며, 디페닐포스포릴 아자이드(diphenylphosphoryl azide)는 내수압특성을 강화시키기 위해 첨가된다.
또한, 폴리옥시에틸렌라우릴에테르(Poly oxyethylene Lauryl ether)는 Cas 넘버 9002-92-0에 해당하는 물질로서 우수한 계면활성 작용으로 인해 자정기능을 활성화시키기 위해 첨가되고, 팽창흑연(Exandable Graphite)은 그라파이트의 층상 구조를 갖기 때문에 그 층상 사이에 원자나 작은 분자를 집어 넣고 열을 가할 경우 아코디언처럼 분리가 되면서 입자가 수백배 팽창하게 되는 현상을 이용하여 방염성을 넘어 불연성을 강화시키기 위해 첨가된다.
그리고, 스테아르산아연(Zinc Stearate)은 열적 안정제로서 내화성을 강화시키기 위해 첨가된다.
아울러, 상도층(600)은 필요에 따라 형성할 수 있으며, 상도층(600)을 형성하지 않을 때는 2차 중도층(500)이 마감층이 된다.
이 경우, 상도층(600)은 상도층형성도료를 사용하여 도포할 수 있는데, 상도층형성도료로는 에폭시수지, 우레탄수지, 수성 또는 수용성 에폭시수지, 수성 또는 수용성 우레탄수지 등이 단독 사용될 수 있다.
더 바람직하기로는 상기 수지중에서 선택된 어느 하나의 수지 100중량부에 대해, 벤질살리실레이트(Benzyl-Salicylate) 5중량부, 인산지르코늄(Zirconium Phosphate) 5중량부, 폴리카프로락톤 5중량부, 포타슘코코에이트(Potassium Cocoate) 5중량부가 더 첨가될 수 있다.
이때, 벤질살리실레이트(Benzyl-Salicylate)는 달콤한 향을 발산하기도 하지만, 자외선을 흡수하여 변색을 방지하는 특성이 있다. 또한, 인산지르코늄(Zirconium Phosphate)은 무기계 항균제이다.
그리고, 폴리카프로락톤은 CAS No. 24980-41-4에 해당하는 물질로서, 무독성에 생체적합성, 생체 무해성이 뛰어나고 생분해성이 있으며, 투명성이 증대되면서 성형 자유도를 높이기 위해 첨가된다.
아울러, 포타슘코코에이트(Potassium Cocoate)는 본체의 유화성을 강화시켜 유연성을 증대시키면서 기름 성분을 용해 제거하는 특성으로 인해 방유성을 갖는다.
본 발명에서는 이와 같은 주차장 바닥용 표면 마감재 레이어를 구성하기 위한 바닥표면마감공법은 다음과 같다.
먼저, 주차장 바닥면을 형성하는 제1단계가 수행된다.
상기 제1단계는 보통 콘크리트가 타설되어 콘크리트구조물을 이루며, 표면이 수평하게 레벨링된 후 양생되는 단계이다.
상기 제1단계가 완료되면, 바닥면에 상술한 수성 프라이머 조성물을 도포하여 프라이머층을 형성하는 제2단계가 수행된다.
이어, 경화된 프라이머층에 1차 수성 조성물을 도포하여 1차 중도층을 형성하는 제3단계가 수행된다.
상기 1차 중도층은 탄성을 갖도록 하여 크랙 저항성을 높이기 위한 층으로, 상기 프라이머층은 전술한 바와 같이 수성 프라이머 조성물로 도포되되, 수성 프라이머 조성물은 아크릴 에멀젼 10-40중량%, 첨가제 0.01-5.0중량% 및 나머지 물로 이루어진다.
그런 다음, 상기 1차 중도층에 메쉬를 부착하고 가압 밀착하여 메쉬층을 형성하는 제4단계가 수행된다.
이렇게 메쉬가 고정되어 메쉬층이 형성되면, 상기 메쉬층 위에 2차 수성 조성물을 도포하여 2차 중도층을 형성하는 제5단계가 수행된다.
상기 2차 중도층은 마감층에 해당하는 층으로서 내구성과 불연성을 확보하고, 내유성도 갖도록 구성함이 바람직하다.
이후, 필요하다면 상도층을 더 형성하는 제6단계가 수행될 수 있으며, 상기 상도층은 전술한 바와 같이, 에폭시수지, 우레탄수지, 수성 또는 수용성 에폭시수지, 수성 또는 수용성 우레탄수지 중에서 선택된 어느 하나의 수지 100중량부에 대해, 벤질살리실레이트(Benzyl-Salicylate) 5중량부, 인산지르코늄(Zirconium Phosphate) 5중량부, 폴리카프로락톤 5중량부, 포타슘코코에이트(Potassium Cocoate) 5중량부가 더 첨가될 수 있다.
Claims (4)
- 주차장 바닥면의 상면에 수성 프라이머 조성물로 도포 형성되는 프라이머층과, 상기 프라이머층의 상면에 1차 수성 조성물로 도포 형성되는 1차 중도층과, 상기 1차 중도층 위에 메쉬로 부착되는 메쉬층과, 상기 메쉬층 위에 2차 수성 조성물로 도포 형성되는 2차 중도층을 포함하되,
상기 프라이머층은 수성 프라이머 조성물로 도포되되, 수성 프라이머 조성물은 아크릴 에멀젼 10-40중량%, 첨가제 0.01-5.0중량% 및 나머지 물로 이루어지고;
상기 2차 중도층 위에는 상도층이 더 형성되되, 상기 상도층은 에폭시수지, 우레탄수지, 수성 또는 수용성 에폭시수지, 수성 또는 수용성 우레탄수지 중에서 선택된 어느 하나의 수지 100중량부에 대해, 벤질살리실레이트(Benzyl-Salicylate) 5중량부, 인산지르코늄(Zirconium Phosphate) 5중량부, 폴리카프로락톤 5중량부, 포타슘코코에이트(Potassium Cocoate) 5중량부가 더 첨가된 것을 특징으로 하는 친환경 수성 주차장 바닥용 표면 마감구조. - 삭제
- 제1항에 있어서,
상기 1차 중도층은 1차 수성 조성물로 도포되되, 1차 수성 조성물은 아크릴 에멀젼 10-50중량%, 첨가제 0.03-6.0중량%, 안료 0.01-10중량%, 폴리비닐알콜(PVA) 1-30중량% 및 나머지 물로 이루어지고;
상기 2차 중도층은 2차 수성 조성물로 도포되되, 2차 수성 조성물은 아크릴 에멀젼 10-50중량%, 첨가제 0.03-6.0중량%, 폴리비닐알콜(PVA) 1-30중량% 및 나머지 물로 이루어진 것을 특징으로 하는 친환경 수성 주차장 바닥용 표면 마감구조. - 주차장 바닥면을 형성하는 제1단계; 제1단계가 완료되면, 바닥면에 수성 프라이머 조성물을 도포하여 프라이머층을 형성하는 제2단계; 경화된 프라이머층에 1차 수성 조성물을 도포하여 1차 중도층을 형성하는 제3단계; 상기 1차 중도층에 메쉬를 부착하고 가압 밀착하여 메쉬층을 형성하는 제4단계; 메쉬층이 형성되면, 상기 메쉬층 위에 2차 수성 조성물을 도포하여 2차 중도층을 형성하는 제5단계;가 수행되는 것을 특징으로 하되,
상기 프라이머층은 수성 프라이머 조성물로 도포되되, 수성 프라이머 조성물은 아크릴 에멀젼 10-40중량%, 첨가제 0.01-5.0중량% 및 나머지 물로 이루어지고;
상기 2차 중도층 위에 상도층을 형성하는 제6단계를 더 포함하며, 상기 상도층은 에폭시수지, 우레탄수지, 수성 또는 수용성 에폭시수지, 수성 또는 수용성 우레탄수지 중에서 선택된 어느 하나의 수지 100중량부에 대해, 벤질살리실레이트(Benzyl-Salicylate) 5중량부, 인산지르코늄(Zirconium Phosphate) 5중량부, 폴리카프로락톤 5중량부, 포타슘코코에이트(Potassium Cocoate) 5중량부가 더 첨가된 것을 특징으로 하는 친환경 수성 주차장 바닥용 표면 마감공법.