KR102653762B1 - 방수 수명 연장기능이 향상된 자외선 차단 기능을 갖춘 방수제 보강공법 - Google Patents
방수 수명 연장기능이 향상된 자외선 차단 기능을 갖춘 방수제 보강공법 Download PDFInfo
- Publication number
- KR102653762B1 KR102653762B1 KR1020230100564A KR20230100564A KR102653762B1 KR 102653762 B1 KR102653762 B1 KR 102653762B1 KR 1020230100564 A KR1020230100564 A KR 1020230100564A KR 20230100564 A KR20230100564 A KR 20230100564A KR 102653762 B1 KR102653762 B1 KR 102653762B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- exterior wall
- anchoring
- waterproofing
- Prior art date
Abstract
본 발명은 방수 수명 연장기능이 향상된 자외선 차단 기능을 갖춘 방수제 보강공법에 관한 것으로, 보다 상세하게는 방수포를 이용하여 콘크리트 건축물의 외벽 방수 기능을 증대시킬 뿐만 아니라, 자외선을 차단하여 자외선에 의한 외벽 열화를 억제하도록 개선된 방수 수명 연장기능이 향상된 자외선 차단 기능을 갖춘 방수제 보강공법에 관한 것이다.
Description
본 발명은 건축 기술 분야 중 방수 수명 연장기능이 향상된 자외선 차단 기능을 갖춘 방수제 보강공법에 관한 것으로, 보다 상세하게는 방수포를 이용하여 콘크리트 건축물의 외벽 방수 기능을 증대시킬 뿐만 아니라, 자외선을 차단하여 자외선에 의한 외벽 열화를 억제하도록 개선된 방수 수명 연장기능이 향상된 자외선 차단 기능을 갖춘 방수제 보강공법에 관한 것이다.
철근 콘크리트 구조물은 건설 후 염해나 중성화, 알칼리 골재 반응, 화학적 부식 외에 물의 침투에 의한 강재의 부식 팽창 등으로 구조물이 열화되면서 크고 작은 균열이 발생하고 장기적으로 내구성 및 사용성이 저하된다.
이러한 구조물의 열화 및 균열이 계속 진행되면 결국 구조물의 붕괴를 초래할 위험성이 있기 때문에 지속적으로 관리하고 보수할 필요가 있다.
콘크리트 열화의 주요 원인이라고 할 수 있는 중성화는 콘크리트 내측으로 물이 침투하거나 공기 중의 탄산가스가 침투하여 콘크리트 내측에서 콘크리트 중의 수산화칼슘을 서서히 배출시킴으로써 C-S-H(칼슘 실리케이트 수화물) 결정체를 약화시킴에 따라 알칼리성이 상실되고 중성화가 진행된다. 콘크리트의 중성화가 진행되면 균열부위가 손상되면서 틈새가 넓어지고 이후 틈새 사이로 철근이 노출되면서 부식으로 진행되며, 일단 철근의 부식이 진행되면 녹에 의해 체적 팽창이 진행되어 그로 인한 팽창압이 콘크리트의 응력을 넘어 새로운 균열을 유발시키게 되며, 새로운 균열은 중성화를 더욱 가속화시켜 콘크리트 구조물의 내구성을 급속히 약화시키게 된다.
따라서 콘크리트 구조물의 균열이 발생하거나 균열 발생 가능성이 있으면 초기에 중성화가 급속히 진행하는 것을 방지하기 위해 보수 공사를 진행할 필요가 있다.
뿐만 아니라, 태양광에서 방출되는 자외선은 콘크리트 건축물의 외벽 표면에 장기간 조사시 표면을 산화시켜 건축물의 수명을 단축시키는 주요 요인중 하나이기도 하다.
때문에, 방수처리와 함께 자외선 차단 기능 실현은 콘크리트 건축물의 외벽에 있어 매우 중요하다.
본 발명은 상술한 바와 같은 종래 기술상의 제반 문제점들을 감안하여 이를 해결하고자 창출된 것으로, 방수포를 이용하여 콘크리트 건축물의 외벽 방수 기능을 증대시킬 뿐만 아니라, 자외선을 차단하여 자외선에 의한 외벽 열화를 억제하도록 개선된 방수 수명 연장기능이 향상된 자외선 차단 기능을 갖춘 방수제 보강공법을 제공하는 것이다.
본 발명은 상기한 목적을 달성하기 위한 수단으로, 크랙부분은 메우고 외벽은 물로 세척하여 건조하는 외벽세척단계; 건조된 외벽을 검사하여 곰팡이 발생지점을 확인하는 외벽검사단계; 확인된 곰팡이 발생지역에 곰팡이억제제를 살포하고 건조하는 외벽세정마감단계; 마감면에 하도제를 도포하여 하도층을 형성하는 하도제도포단계; 하도층에 앵커링유도제를 도포하여 앵커링 기능을 강화시키는 앵커링유도제살포단계; 도포 건조된 하도층 위에 방수포를 포설하는 방수포포설단계; 방수포 상면에 상도제를 도포하여 상도층을 형성하고 마감하는 상도제도포단계; 상도층 위에 표면마감제를 도포하는 마감단계;를 포함하고,
상기 앵커링유도제살포단계는 앵커링유도제를 건조된 하도층에 살포하되, 상기 앵커링유도제는 아크릴수지 100중량부에 대해, 1-하이드록시-3-메틸벤젠(1-HYDROXY-3-METHYLBENZENE) 15중량부, 에틸렌테트라플루오로에틸렌 8.5중량부, 디아릴프탈레이트(diarylphthalae) 10중량부를 혼합하여 제조되며;
상기 방수포포설단계는 아크릴계 부직포시트를 사용하되, 상기 아크릴계 부직포시트의 표면에는 실리콘수지 100중량부에 대해, 무수말레인산(Maleic anhydride) 3.0중량부, 프로필렌 디카르복실산 10중량부, 세레신(Cerecin) 4.5중량부, 오르토인산이수소나트륨(NaH2PO4·2H2O) 8.5중량부, 에틸렌테트라플루오로에틸렌 3.5중량부를 혼합하여 조성된 도포액이 스프레이 코팅된 것을 특징으로 하는 방수 수명 연장기능이 향상된 자외선 차단 기능을 갖춘 방수제 보강공법을 제공한다.
본 발명에 따르면, 방수포를 이용하여 콘크리트 건축물의 외벽 방수 기능을 증대시킬 뿐만 아니라, 자외선을 차단하여 자외선에 의한 외벽 열화를 억제하도록 개선된 효과를 얻을 수 있다.
이하에서는, 본 발명에 따른 바람직한 실시예를 보다 상세하게 설명하기로 한다.
본 발명에 따른 방수 수명 연장기능이 향상된 자외선 차단 기능을 갖춘 방수제 보강공법은 크랙부분은 메우고 외벽은 물로 세척하여 건조하는 외벽세척단계; 건조된 외벽을 검사하여 곰팡이 발생지점을 확인하는 외벽검사단계; 확인된 곰팡이 발생지역에 곰팡이억제제를 살포하고 건조하는 외벽세정마감단계; 마감면에 하도제를 도포하여 하도층을 형성하는 하도제도포단계; 하도층에 앵커링유도제를 도포하여 앵커링 기능을 강화시키는 앵커링유도제살포단계; 도포 건조된 하도층 위에 방수포를 포설하는 방수포포설단계; 방수포 상면에 상도제를 도포하여 상도층을 형성하고 마감하는 상도제도포단계; 상도층 위에 표면마감제를 도포하는 마감단계;를 포함한다.
이때, 외벽세척단계는 콘크리트 건축물의 외벽을 물을 뿌려 세척하고, 세척 후 건조된 외벽에 존재하는 크랙, 갈라짐. 탈락 부위를 확인한 후 크랙, 갈라짐, 탈락부위를 메우는 단계이다.
여기에서, 크랙, 갈라짐, 탈락 부위의 메움재는 상기 아크릴수지 100중량부에 대해, HDFS(Heptadeca-fluoro-1,1,2,2-tetra-hydrodecyltrichloro-silane) 2.5중량부 3.5중량부, 카프릭산(Capric Acid) 2.5중량부, 액상 멜라민수지 10중량부, 를 혼합하여 사용할 수 있다.
이 경우, HDFS는 트리클로로실란 계열로서 실란 그룹이 포함된 알킬기 혹은 불소가 치환된 알킬기 물질에 의해 소수성을 강화시켜 방수특성을 증대시키기 위해 첨가된다.
그리고, 카프릭산(Capric Acid)은 기포발생을 억제하면서 흐름성을 증대시켜 균열 보수성을 강화시킨다.
또한, 액상 멜라민수지는 접착력을 극대화시켜 코팅층의 표면 박리를 강력하게 억제한다.
한편, 외벽세정마감단계에서 살포되는 곰팡이억제제는 수용성 폴리우레탄수지 100중량부에 대해, 물 40중량부, 요오드화부틸카르바메이트(Iodopropynyl butylcarbamate) 25중량부, 메타크레졸 5.5중량부, 오레가노 오일(oregano oil) 5.5중량부, 알콕시레이티드 알코올(alkoxylated alcohol) 8.5중량부를 혼합하여 만들어진다.
이때, 요오드화부틸카르바메이트(IPBC:Iodopropynyl butylcarbamate)는 방부성을 강화시킴으로써 곰팡이 발생을 억제하는데, CAS 넘버는 55406-53-6이다.
또한, 메타크레졸은 도료와 피착면에서의 앵커링 기능을 통해 계면 분리를 억제한다.
그리고, 오레가노 오일(oregano oil)은 곰팡이 등의 오염균에 대한 항균 기능을 강화시킨다.
아울러, 알콕시레이티드 알코올(alkoxylated alcohol)은 비이온성 계면활성제로서 표면에서 곰팡이 포자의 공기접촉을 차단하여 곰팡이 발생을 억제한다.
다른 한편, 하도제도포단계는 콘크리트 건축물의 외벽에 하도제를 도포하여 방수성, 방습성, 내수압특성을 강화시키는 단계이다.
이러한 용도의 하도제로는 폴리우레탄수지 100중량부를 기준으로, 중탄산나트륨 3.5중량부, 옥틸아크릴아미드(Octylacrylamide) 8.5중량부, 붕사 5.5중량부, 폴리이소시아네이트 4.5중량부, 호모살리에이트 5.5중량부를 혼합하여 조성된다.
이때, 중탄산나트륨은 기화된 나트륨 가스가 표면에 작용하여 유리상을 형성함으로써 광택도는 물론 방수성을 강화시키고, 자외선 차단력을 증가시킨다.
또한, 옥틸아크릴아미드(Octylacrylamide)는 탄산칼슘 생성을 억제하여 콘크리트의 중성화를 막고, 수밀화를 높여 방수성을 강화시키기 위해 첨가된다.
뿐만 아니라, 붕사는 외벽 표면의 유면을 매끄럽게 하면서 결합력을 강화시키기 위해 첨가된다.
아울러, 폴리이소시아네이트는 경화를 촉진하여 고정안정성을 증가시킨다.
그리고, 호모살리에이트는 외벽 표면으로 조사된 자외선을 흡수하여 분해함으로 인해 일광견뢰도를 증대시키고, 내수압특성을 강화시킨다.
또다른 한편, 앵커링유도제살포단계는 앵커링유도제를 건조된 하도층에 살포하여 후속하여 포설되는 방수포가 하도층에 완전히 밀착되면서 들뜨지 않도록 견실안정적으로 고정하는 역할을 하도록 하는 앵커링층을 형성하는 단계이다.
이러한 앵커링층 형성을 위한 앵커링유도제는 아크릴수지 100중량부에 대해, 1-하이드록시-3-메틸벤젠(1-HYDROXY-3-METHYLBENZENE) 15중량부, 에틸렌테트라플루오로에틸렌 8.5중량부, 디아릴프탈레이트(diarylphthalae) 10중량부를 혼합하여 제조된다.
이 경우, 1-하이드록시-3-메틸벤젠(1-HYDROXY-3-METHYLBENZENE)은 표면 거칠기를 증대시켜 방수포에 형성된 공극과의 쐐기형 결합을 유도하여 들뜸억제, 앵커링 강화 효과를 제공한다.
또한, 에틸렌테트라플루오로에틸렌(Ethylene Tetra Fluoro Ethylene) 수지는 불소가 결합된 수지로서, 수소결합이 형성되지 않아 상대적으로 물방울과 같은 물질에 대한 접촉을 낮추어 매우 낮은 표면 에너지를 가지게 되므로 방오성을 향상시킨다.
아울러, 디아릴프탈레이트(diarylphthalae)는 성분간 접착성과 인성을 개선하여 크랙발생 억제를 포함한 내열성, 치수안정성, 내약품성을 높이기 위해 첨가된다.
또다른 한편, 방수포포설단계는 아크릴계 부직포시트를 사용함이 바람직하다.
이때, 상기 아크릴계 부직포시트의 표면에는 방수기능과 신율 증대를 위해 실리콘수지 100중량부에 대해, 무수말레인산(Maleic anhydride) 3.0중량부, 프로필렌 디카르복실산 10중량부, 세레신(Cerecin) 4.5중량부, 오르토인산이수소나트륨(NaH2PO4·2H2O) 8.5중량부, 에틸렌테트라플루오로에틸렌 3.5중량부를 혼합하여 조성된다.
이때, 무수말레인산(Maleic anhydride)은 수축변형성을 억제하고 신율을 유지한다.
그리고, 사이클로메티콘(Cyclomethicone)은 자외선에 대한 차단특성을 더욱 더 강화시킨다.
또한, 프로필렌 디카르복실산(propylene dicarboxylic acid)은 산화를 억제하여 크랙발생과 계면탈락 및 계면 분리를 억제한다.
아울러, 세레신(Cerecin)은 유화안정감을 높이고 성분간 결합력을 증대시키면서 방수시트의 유연성을 유지하여 인장강도와 신율을 증대시키고 내크랙성을 강화시키기 위해 첨가된다.
뿐만 아니라, 오르토인산이수소나트륨(NaH2PO4·2H2O)은 방수시트의 내크랙성, 내침식성, 내부식성을 강화시킨다.
또한, 에틸렌테트라플루오로에틸렌(Ethylene Tetra Fluoro Ethylene) 수지는 불소가 결합된 수지로서, 수소결합이 형성되지 않아 상대적으로 물방울과 같은 물질에 대한 접촉을 낮추어 매우 낮은 표면 에너지를 가지게 되므로 방오성을 향상시킨다.
또다른 한편, 상기 상도제도포단계에서 도포 사용되는 상도제는 표면을 보호하고 표면을 마감하는 도장액이다.
이러한 상도제는 수용성 아크릴수지 100중량부에 대해, 물 20중량부, 액화무수암모니아 10중량부, 탄산바륨 12.5중량부, 디베헤닐푸마레이트 15중량부, 산화세륨 분말 10중량부를 혼합하여 조성된다.
이때, 액화무수암모니아(ammonia anhydrous liquefied)는 수지와 무기물의 결합성을 강화시키기 위해 첨가된다.
아울러, 탄산바륨은 응집을 촉진하여 경화성을 좋게 하고 자외선을 흡수하지 않아 산화방지 및 변색방지 기능을 갖는다.
또한, 디베헤닐푸마레이트(Dibehenyl Fumarate)는 베헤닐알코올과 푸마릭애씨드의 디에스터로서 균일분산성을 증대시키면서 평탄화 피막을 촉진하여 방수성, 방습성, 내침식성, 내부성, 내수압특성을 강화시킨다.
그리고, 산화세륨 분말은 금속산화물로서 차열 기능을 수행하며, 특히 마찰저항을 높여 계면간 층분리 억제력을 증진시킨다.
또다른 한편, 상기 마감단계는 상도층 위에 표면마감제를 도포하여 마감하는 단계로서, 상기 표면마감제는 폴리카보네이트수지 100중량부에 대해, 스테아린산 15중량부, Ca(OH)2 분말 10중량부, 실리카 10중량부, 파라핀왁스 5중량부가 혼합된 것이다.
이때, 스테아린산은 무기입자가 마찰을 줄여 배합성을 좋게 하고, 표면균일도를 증가시킨다.
또한, Ca(OH)2 분말은 실리카와 반응하여 규산염칼슘 수화물을 생성함으로써 표면 피막 및 강도를 향상시키고, 자외선 저항성을 강화시켜 표면 열화를 방지한다.
그리고, 파라핀왁스는 분산안정성을 높이 유기물의 오염을 방지하기 위해 첨가된다.
이와 같이, 본 발명은 방수포를 이용하여 콘크리트 건축물의 외벽 방수 기능을 증대시킬 뿐만 아니라, 자외선을 차단하여 자외선에 의한 외벽 열화를 억제하도록 기여할 수 있게 된다.
Claims (1)
- 크랙부분은 메우고 외벽은 물로 세척하여 건조하는 외벽세척단계; 건조된 외벽을 검사하여 곰팡이 발생지점을 확인하는 외벽검사단계; 확인된 곰팡이 발생지역에 곰팡이억제제를 살포하고 건조하는 외벽세정마감단계; 마감면에 하도제를 도포하여 하도층을 형성하는 하도제도포단계; 하도층에 앵커링유도제를 도포하여 앵커링 기능을 강화시키는 앵커링유도제살포단계; 도포 건조된 하도층 위에 방수포를 포설하는 방수포포설단계; 방수포 상면에 상도제를 도포하여 상도층을 형성하고 마감하는 상도제도포단계; 상도층 위에 표면마감제를 도포하는 마감단계;를 포함하고,
상기 앵커링유도제살포단계는 앵커링유도제를 건조된 하도층에 살포하되, 상기 앵커링유도제는 아크릴수지 100중량부에 대해, 1-하이드록시-3-메틸벤젠(1-HYDROXY-3-METHYLBENZENE) 15중량부, 에틸렌테트라플루오로에틸렌 8.5중량부, 디아릴프탈레이트(diarylphthalae) 10중량부를 혼합하여 제조되며;
상기 방수포포설단계는 아크릴계 부직포시트를 사용하되, 상기 아크릴계 부직포시트의 표면에는 실리콘수지 100중량부에 대해, 무수말레인산(Maleic anhydride) 3.0중량부, 프로필렌 디카르복실산 10중량부, 세레신(Cerecin) 4.5중량부, 오르토인산이수소나트륨(NaH2PO4·2H2O) 8.5중량부, 에틸렌테트라플루오로에틸렌 3.5중량부를 혼합하여 조성된 도포액이 스프레이 코팅된 것을 특징으로 하는 방수 수명 연장기능이 향상된 자외선 차단 기능을 갖춘 방수제 보강공법.