KR102527411B1 - 습윤 밴드용 조성물, 상기 습윤밴드 및 이의 제조방법 - Google Patents
습윤 밴드용 조성물, 상기 습윤밴드 및 이의 제조방법 Download PDFInfo
- Publication number
- KR102527411B1 KR102527411B1 KR1020220016458A KR20220016458A KR102527411B1 KR 102527411 B1 KR102527411 B1 KR 102527411B1 KR 1020220016458 A KR1020220016458 A KR 1020220016458A KR 20220016458 A KR20220016458 A KR 20220016458A KR 102527411 B1 KR102527411 B1 KR 102527411B1
- Authority
- KR
- South Korea
- Prior art keywords
- composition
- band
- wet
- weight
- wet band
- Prior art date
Abstract
본 발명은 습윤 밴드용 조성물, 상기 조성물을 포함하는 습윤밴드와 이의 제조방법에 관한 것으로서, 상기 조성물은 저메톡시펙틴 및 한천을 포함하고, 상기 저메톡시펙틴 및 한천은, 20 내지 40 : 1의 중량부로 혼합되는 것을 특징으로 한다.
Description
본 발명은 습윤 밴드용 조성물, 상기 습윤밴드 및 이의 제조방법에 관한 것이다.
기존의 액상밴드에서 제품의 신속한 건조를 위해 첨가된 휘발성 성분인 알코올과 상처가 만났을 때 피부의 자극과 따가움이 있다는 단점이 있다. 그로 인해 상처가 건조해져 흉터가 생기거나 홍반을 동반한 피부발진의 문제점을 일으키게 되었다. 또한 습윤 효과가 좋지 못하고 제품 도포 후 필름으로 형성되어 여러 번 덧발라야 하는 번거로움과 작은 상처에만 사용이 가능해 부착 면적에 제한이 있었다. 또한, 습윤 밴드의 경우 습윤 효과로 인한 상처 치료 효과는 우수하나 미미한 방수 효과로 세균 침범이 잦아 흉터 발생 가능성이 높으며 제품의 규격이 정해져 있어 사용할 수 있는 상처의 크기에 제한이 있었다.
따라서, 본 발명은 액상밴드와 습윤 밴드의 문제점을 상호 보완한 젤 형태의 밴드에 관한 것이다.
본 발명은 상기 종래 기술상의 한계점을 극복한, 습윤 밴드용 조성물을 제공하고자 한다.
상기와 같은 본 발명의 목적을 달성하기 위하여, 본 발명은 습윤 밴드용 조성물로서,
상기 조성물은 저메톡시펙틴 및 한천을 포함하고, 상기 저메톡시펙틴 및 한천은, 20 내지 40 : 1의 중량부로 혼합되는 것인, 습윤 밴드용 조성물을 제공한다.
본 발명의 일구현예로서, 상기 조성물은 D-판테놀 및 히알루론산을 더 포함하고, 상기 D-판테놀 및 히알루론산은, 6 내지 4 : 4 내지 6의 중량부로 혼합되는 것을 특징으로 한다.
본 발명의 다른 구현예로서, 상기 조성물은 트랜스글루타미나아제를 더 포함하고, 상기 트랜스글루타미나아제는, 저메톡시펙틴 100 중량부에 대하여, 15 내지 25 중량부로 포함되는 것을 특징으로 한다.
본 발명의 또다른 구현예로서, 상기 조성물은 라벤더오일 및 봉독을 더 포함하고, 상기 조성물은 라벤더오일 0.1 내지 1.5 중량% 및 봉독 3 내지 4 중량%를 포함하는 것을 특징으로 한다.
본 발명의 또다른 구현예로서, 상기 조성물은, 글리세릴스테아레이트, 화이트토마토추출물, EGF, FGF, 구연산수 및 유로나프리로 이루어지는 군으로부터 선택되는 1종 이상을 더 포함하는 것을 특징으로 한다.
또한, 본 발명은 상기 조성물을 포함하는 습윤 밴드를 제공한다.
아울러, 본 발명은 습윤 밴드의 제조방법으로서,
a) 50 내지 100℃온도를 갖는 증류수에 펙틴을 용해하는 단계;
b) 용해 후, 한천을 첨가하고, 60 내지 100℃로 가열하는 단계;
c) 상기 가열 후 트랜스글루타미나아제를 첨가하고, 유화제를 첨가하는 단계;
d) 상기 유화제의 첨가 후, 히알루론산 및 판테놀을 첨가하는 단계; 및
e) 상기 첨가 후 성형하여 밴드를 제조하는 단계를 포함하는, 습윤 밴드의 제조방법을 제공한다.
본 발명에 의한 습윤 밴드는 펙틴을 포함하여, 피부 자극 없이 인체에 자극이 없는 펙틴 사용으로 피부 자극을 줄일 수 있다. 또한, 보습 성분의 첨가로 피부 건조로 인한 흉터 및 피부 발진 유발의 단점을 보완할 수 있고, 방수 기능으로서 물과의 접촉을 최소화하고, 2차 감염을 막을 수 있으며, 다양한 면적에 사용할 수 있는 효과가 있다. 아울러, 라벤더오일을 포함하여 상처 치료와 함께 심리적 안정감을 가질 수 있다.
도 1은 본 발명의 젤 형태의 밴드의 제조 방법을 도식화하여 나타낸 것이다.
도 2는 본 발명에서 제조된 젤 형태의 밴드의 겔화 여부를 확인한 결과를 나타낸 것이다.
도 3은 본 발명에서 제조한 젤 형태의 밴드의 수분 함량을 확인한 결과를 나타낸 것이다.
도 4는 본 발명에서 제조한 젤 형태의 밴드의 방수력을 확인한 결과를 나타낸 것이다.
도 5는 본 발명에서 제조된 젤 형태의 밴드의 초기 중량과 보관 후 중량을 측정한 결과를 나타낸 것이다.
도 6은 본 발명에서 제조한 젤 형태의 밴드의 접착력을 확인한 결과를 나타낸 것이다.
도 7은 본 발명에서 제조한 젤 형태의 밴드의 항균력을 확인한 결과를 나타낸 것이다.
도 8은 본 발명에서 제조한 젤 형태의 밴드의 사용에 따른 스트레스 지수 변화를 확인한 결과를 나타낸 것이다.
도 2는 본 발명에서 제조된 젤 형태의 밴드의 겔화 여부를 확인한 결과를 나타낸 것이다.
도 3은 본 발명에서 제조한 젤 형태의 밴드의 수분 함량을 확인한 결과를 나타낸 것이다.
도 4는 본 발명에서 제조한 젤 형태의 밴드의 방수력을 확인한 결과를 나타낸 것이다.
도 5는 본 발명에서 제조된 젤 형태의 밴드의 초기 중량과 보관 후 중량을 측정한 결과를 나타낸 것이다.
도 6은 본 발명에서 제조한 젤 형태의 밴드의 접착력을 확인한 결과를 나타낸 것이다.
도 7은 본 발명에서 제조한 젤 형태의 밴드의 항균력을 확인한 결과를 나타낸 것이다.
도 8은 본 발명에서 제조한 젤 형태의 밴드의 사용에 따른 스트레스 지수 변화를 확인한 결과를 나타낸 것이다.
본 발명에서는 기존에 사용되는 밴드의 문제점을 상호 보완한 것이다. 액상밴드는 신속한 건조를 위한 휘발성 물질 알코올의 첨가로 인한 피부 자극 및 따가움 유발과, 건조함으로 인한 흉터와 홍반 등 피부발진, 낮은 습윤 효과, 여러 번 도포해야 하는 번거로움, 면적이 작은 상처 부위에 사용 가능한 단점이 있으며. 습윤 밴드는 미미한 방수효과로 세균 침범이 잦아 높아지는 흉터 발생 가능성과 부착 면적의 정형화의 단점이 있는데 이를 개선하기 위해 인체에 무해하고 식용이 가능한 펙틴을 주성분으로 제조하였다.
따라서, 본 발명은, 습윤 밴드용 조성물로서, 상기 조성물은 저메톡시펙틴 및 한천을 포함하고, 상기 저메톡시펙틴 및 한천은, 20 내지 40 : 1의 중량부로 혼합되는 것인, 습윤 밴드용 조성물을 제공한다. 바람직하게는, 상기 저메톡시펙틴 및 한천은, 30 내지 35 : 1의 중량부로 혼합될 수 있다. 펙틴은 계란상자 구조로 형성되어 있으며 세포나 생활성 물질을 혼합하여 상처 치료에 사용되고 있으며 천연 치료제로 사용할 수 있다.
본 발명의 일실시예로서, 상기 조성물은 트랜스글루타미나아제를 더 포함하여, 상기 펙틴과 한천의 결합을 보다 강력하게 할 수 있다. 상기 트랜스글루타미나아제는, 저메톡시펙틴 100 중량부에 대하여, 15 내지 25 중량부로 포함되는 것일 수 있다.
또한 본 발명에서는, 제조된 겔형태의 펙틴LM에 저분자 히알루론산과 D-판테놀 첨가로 보습력을 높이고, 한천 첨가로 겔화의 강도를 올려 방수에 적합한 형태로 제조하였으며, 물과의 결합력이 좋은 특성으로 습윤 효과에 탁월하여 습윤력에 의한 상처 치료의 효과를 높일 수 있는 효과가 있다.
본 발명의 일실시예로서, 상기 조성물은 D-판테놀 및 히알루론산을 더 포함하고, 상기 D-판테놀 및 히알루론산은, 6 내지 4 : 4 내지 6의 중량부로 혼합되는 것일 수 있다. 보다 바람직하게는, 8:2의 중량부로 혼합될 수 있다.
또한 본 발명의 조성물에 의해 제조된 습윤 밴드는 다양한 면적의 상처에 활용할 수 있도록 자유로운 드레싱이 가능하며, 라벤더 에센셜 오일과 봉독을 첨가하여 살균과 함께 심리적 안정감을 가질 수 있다. 상기 조성물에는 라벤더오일 0.1 내지 1.5 중량% 및 봉독 3 내지 4 중량%를 포함할 수 있다.
본 발명의 일 실시예로서, 상기 조성물은, 글리세릴스테아레이트, 화이트토마토추출물, EGF, FGF, 구연산수 및 유로나프리로 이루어지는 군으로부터 선택되는 1종 이상을 더 포함할 수 있다.
또한, 본 발명은 상기 조성물에 의한 습윤 밴드를 제공한다.
아울러, 본 발명은 습윤 밴드의 제조방법으로서,
a) 50 내지 100℃온도를 갖는 증류수에 펙틴을 용해하는 단계;
b) 용해 후, 한천을 첨가하고, 60 내지 100℃로 가열하는 단계;
c) 상기 가열 후 트랜스글루타미나아제를 첨가하고, 유화제를 첨가하는 단계;
d) 상기 유화제의 첨가 후, 히알루론산 및 판테놀을 첨가하는 단계; 및
e) 상기 첨가 후 성형하여 밴드를 제조하는 단계;를 포함하는, 습윤 밴드의 제조방법을 제공할 수 있다.
결과적으로 본 발명은 다음과 같은 장점을 가진다. 1) 인체에 자극이 없는 펙틴 사용으로 피부 자극을 줄일 수 있다. 2) 보습 성분의 첨가로 피부 건조로 인한 흉터 및 피부 발진 유발의 단점을 보완할 수 있다. 3) 방수 기능으로서 물과의 접촉을 최소화하고, 2차 감염을 막을 수 있다. 4) 다양한 면적에 사용할 수 있다. 5) 상처 치료와 함께 심리적 안정감을 가질 수 있다.
이하 다음의 실시예에서는 본 발명의 습윤밴드와 이의 제조방법에 대한 비한정적인 예시를 하고 있다.
실시예 1. 제조방법
1.1. 고체상 제조
증류수 중량 60g 을 기준으로 제조하였다. 펙틴LM과 한천의 용해 온도로서 80℃가 적합하며, 먼저 증류수를 가열하여 60℃의 온도에서 펙틴LM 20g 을 먼저 녹이고, 한천 0.6g 을 가한 후 80℃의 온도에서 충분히 용해하였다. 펙틴LM과 한천이 잘 용해되었는지 확인한 후 펙틴과 한천의 결합을 더욱 강화하기 위해 트랜스글루타미나아제를 4g 첨가하였다.
이후, 수상층과 유상층이 혼합될 수 있도록 유화제로 글리세릴스테아레이트 1g 을 첨가하고, 용액의 온도를 확인하여 70℃를 맞춘 후 자외선 차단 효과에 용이한 화이트토마토추출물 1g 을 첨가하였다.
1.2. 액상제조
수상층과 유상층의 혼합을 위해서 용액의 온도를 확인하여 70℃를 맞췄다. 70℃는 수상층과 유상층이 섞이는 최적의 온도로, 먼저 항염 및 항균력에 용이한 봉독 4g 을 첨가하였으며, 피부의 노화방지를 위해 무화과 추출물 4g과 파파야 추출물 2g을 첨가하였다. 이후, 보습력에 용이한 저분자 히알루론산 4g과 D-판테놀 16g을 첨가한 후 보존제로서 구연산수와 천연보존제 유로나프리를 첨가하였다. 다음으로 온도를 30℃로 낮춰 유지한 후 상피세포와 섬유아세포의 성장을 촉진하는 EGF, FGF를 각각 0.2g 씩 가한 후 잘 섞어주었다. 마지막으로 심신 안정에 도움이 되는 라벤더 에센셜 오일을 첨가하여 살균 및 심리적 안정에 도움이 되는 젤 형태의 밴드를 제조하였다.
실시예 2. 펙틴 및 한천의 배합비율에 따른 효과 확인
펙틴LM과 한천의 함량에 따른 젤 형태 밴드의 겔화 여부를 실험하고자 한천 0.3g에 펙틴LM의 함량을 각각 1g, 5g, 10g, 20g, 40g으로 배합하여 위 제조 방법에 따라 5가지의 젤 형태의 밴드를 제조하였다.
제조된 젤 형태의 밴드를 각각 몰드에 넣어 실온에서 2시간 굳힌 뒤 확인한 결과, 한천 0.3g과 펙틴LM 10g을 배합한 젤 형태의 밴드의 제형이 가장 이상적인 겔화 정도임을 도 2를 통해 나타내었다.
실시예 3. 보습제의 배합에 따른 보습력 차이 확인
젤 형태 밴드의 보습력의 효과를 실험하고자 D-판테놀과 히알루론산의 비율을 각각 10:0, 8:2, 6:4, 4:6, 2:8, 0:10 으로 혼합하여 총 6개의 시료를 사용하였으며 20대 성인 3명을 대상으로 팔 상박부 안쪽 부위에 보습력을 측정하였다. 겔밴드를 도포 후 밴드를 제거하였을 때 피부의 남아있는 보습 지속력을 측정하기 위해 Skin-O-Mat와 수분계 (Corneometer CM825)를 사용하였다. 기계는 피부 표면에 접착하는 전극 간격을 통해 전도되는 전류의 정전부하용량을 계측하는 원리로 피부의 수분함량과 정전부하용량은 서로 비례하여 피부의 보습도가 높을수록 수치가 높게 나타나게 된다.
피부 표면에 도포한 후 평균온도 22℃평균습도 56%에서 1, 2, 3, 4시간 단위 및 각 비율별로 피부 수분 함유량을 측정하였다. 분석 결과, D-판테놀:히알루론산, 8:2의 비율이 부착 시간이 길어질수록 수분 함량이 지속적으로 상승함을 도 3에서 확인 할 수 있다.
실시예 4. 방수력 확인
펙틴LM 10g 으로만 제조한 젤 형태의 밴드와 펙틴LM과 한천을 10g, 0.3g의 비율로 제조한 젤 형태의 밴드를 동일한 크기로 제조하였다. 각각의 페트리 접시에 중앙에 같은 크기의 사각형 종이를 놓고 그 위에 젤 형태의 밴드를 놓아두고, 일정시간동안 계속적으로 물을 부어 종이가 물에 젖는지 여부를 확인하였다. 이 실험은 5회 반복하였고 결과를 도 4에 나타내었다. 이로서 본 발명의 젤 형태의 밴드가 방수력이 있음을 확인할 수 있다.
실시예 5. 습윤력 확인
습윤력 효과를 실험하고자 도 1과 같이 젤 형태의 밴드를 제조한다. 실험용 비이커의 중량을 미리 재어놓는다. 100.1g의 물이 들어있는 비이커의 입구를 상기 과정을 통해 굳혀 놓은 젤 형태의 밴드로 밀봉한 후, 24시간 동안 상온에 보관하였다. 이후 초기 중량과 비교하여 증발정도를 계산하여 도 5에 나타내었다. 이를 통해 젤 형태의 밴드를 굳혀 물이 들어있는 비이커의 입구를 봉하면, 24시간 동안 비이커로부터 수분의 증발 및 손실을 10.04배 이상 방지할 수 있음을 확인할 수 있다.
실시예 6. 접착력 확인
젤 형태 밴드의 접착력 증진과 더불어 겔 강도를 높여주기 위하여 트랜스글루타미나아제를 1g, 2g, 4g, 8g 으로 각각의 젤 형태의 밴드를 만들어 접착력 테스트를 실시하였다.
20대 성인 3명을 대상으로 하박부 안쪽 부위에 젤 형태의 밴드를 도포하고 1분경과 후 흐르는 물에 도포한 부위를 갖다 대어 수압을 이용하여 접착력을 확인하는 원리다. 각각의 젤 형태의 밴드를 같은 위치에 같은 크기로 도포 후 동일한 물줄기를 유지한 채 위 실험과정을 3번 반복하였다. 실험 결과 트랜스글루타미나아제 1g을 첨가한 젤 형태 밴드는 흐르는 물줄기의 수압을 3분 이상 견디지 못하였고, 4g을 첨가한 것은 5분 이상의 접착력은 확인할 수 있었으나 젤 형태의 밴드의 응집력이 강해져 겔 강도가 너무 높았다. 또한 8g을 첨가한 젤 형태 밴드는 접착 효과를 확인하기 어려울 정도로 겔 강도가 높음을 확인할 수 있었다.
본 발명품의 트랜스글루타미나아제를 이용한 결합력의 증진과 접착 용이성의 최적화 배합량이 2g 임을 도 6에 나타내었다.
실시예 7. 항균력 확인
젤 형태 밴드의 항균력을 알아보기 위하여 황색포도상구균을 이용하여 실험을 수행하였다. 젤 형태의 밴드의 항균력을 주는 성분으로는 봉독과 라벤더 오일이 포함된다. 고체 배지에 황색포도상구균을 도포한 후 35℃에서 24시간 배양하여 항균 시험을 진행하였다. 젤 형태 도포 전은 24시간 경과 후 균이 배양되는 것을 확인 할 수 있고, 봉독 3.4%와 라벤더 오일 0.7%를 첨가한 젤 형태의 밴드 도포 후는 균이 배양되지 않았으므로 젤 형태의 밴드에 항균력이 있음을 도 7 에 나타내었다.
실시예 8. 스트레스 지수
라벤더 오일은 향기를 맡으면 스트레스 완화와 신경 안정 및 숙면을 돕는데 효과적이다.
스트레스 측정기(UBio Macpa)를 이용하여 라벤더 에센셜 오일을 함유하고 있는 젤 형태밴드의 심리적 안정 효과가 있는지 시험을 진행하였다. 먼저 성인 20대 4명의 실험자들의 누적 스트레스 지수를 측정하였다. 그리고 라벤더 에션셜 오일을 함유한 젤 형태 밴드의 향을 맡은 후 5분 경과, 20분 경과 후의 스트레스 지수를 측정하였다. 분석 결과 대조군의 누적 스트레스 지수는 35에서 23으로 감소하였으며, 실험자 1은 36에서 25, 실험자 2는 40에서 24, 실험자 3은 30에서 19로 감소하였다. 향기를 흡입한 실험자와 대조군의 차이가 큰 것을 도 8에서 확인할 수 있으며 이로서 본 발명은 심리적 안정 효과가 있음을 확인할 수 있었다.
이상에서 본 발명의 습윤밴드에 대한 기술사상을 첨부도면과 함께 서술하였지만, 이는 본 발명의 가장 양호한 실시예를 예시적으로 설명한 것이지 본 발명을 한정하는 것은 아니다.
따라서, 본 발명은 상술한 특정의 바람직한 실시예에 한정되지 아니하며, 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 누구든지 다양한 변형 실시가 가능한 것은 물론이고, 그와 같은 변경은 청구범위 기재의 범위내에 있게 된다.
Claims (13)
- 습윤 밴드용 조성물로서,
상기 조성물은 저메톡시펙틴 및 한천을 포함하고,
상기 저메톡시펙틴 및 한천은, 20 내지 40 : 1의 중량부로 혼합되고,
상기 조성물은, 글리세릴스테아레이트, 화이트토마토추출물, EGF, FGF, 구연산수 및 유로나프리를 더 포함하는 것인, 습윤 밴드용 조성물.
- 제1항에 있어서,
상기 조성물은 D-판테놀 및 히알루론산을 더 포함하고,
상기 D-판테놀 및 히알루론산은, 6 내지 4 : 4 내지 6의 중량부로 혼합되는 것인, 습윤 밴드용 조성물.
- 제1항에 있어서,
상기 조성물은 트랜스글루타미나아제를 더 포함하고,
상기 트랜스글루타미나아제는, 저메톡시펙틴 100 중량부에 대하여, 15 내지 25 중량부로 포함되는 것인, 습윤 밴드용 조성물.
- 제1항에 있어서,
상기 조성물은 라벤더오일 및 봉독을 더 포함하고,
상기 조성물은 라벤더오일 0.1 내지 1.5 중량% 및 봉독 3 내지 4 중량%를 포함하는 것인, 습윤 밴드용 조성물.
- 삭제
- 제1항의 조성물을 포함하는 습윤 밴드.
- 습윤 밴드의 제조방법으로서,
60℃의 증류수에 저메톡시펙틴 20g을 용해하는 제 1 단계;
상기 제 1 단계 이후에, 상기 저메톡시펙틴이 용해된 용액에 0.6g의 한천을 첨가하고, 80℃까지 가열하는 제 2 단계;
상기 제 2 단계 이후에, 상기 한천이 첨가된 용액에 4g의 트랜스글루타미나아제를 첨가하는 제 3 단계;
상기 제 3 단계 이후에, 상기 트랜스글루타미나아제가 첨가된 용액에 유화제로서 1g의 글리세릴스테아레이트를 첨가하는 제 4 단계;
상기 제 4 단계 이후에, 상기 글리세릴스테아레이트가 첨가된 용액의 온도를 70℃로 설정하고, 1g의 화이트토마토추출물을 첨가하는 제 5 단계;
상기 제 5 단계 이후에, 상기 화이트토마토추출물이 첨가된 용액에 히알루론산 4g 및 D-판테놀 16g을 첨가하는 제 6 단계; 및
상기 제 6 단계 이후에, 성형하여 밴드를 제조하는 제 7 단계;
를 포함하는, 습윤 밴드의 제조방법.
- 삭제
- 삭제
- 삭제
- 제7항에 있어서,
상기 제 5 단계와 상기 제 6 단계에서 봉독 3 내지 4 중량%를 더 첨가하는 단계; 및
상기 제 6 단계와 상기 제 7 단계의 사이에서 라벤더오일 0.1 내지 1.5 중량% 를 더 첨가하는 단계;
를 더 포함하는 것인, 습윤 밴드의 제조방법.
- 삭제
- 삭제