KR102513829B1 - 무방부제 화장료 조성물 및 이의 제조 방법 - Google Patents
무방부제 화장료 조성물 및 이의 제조 방법 Download PDFInfo
- Publication number
- KR102513829B1 KR102513829B1 KR1020220088275A KR20220088275A KR102513829B1 KR 102513829 B1 KR102513829 B1 KR 102513829B1 KR 1020220088275 A KR1020220088275 A KR 1020220088275A KR 20220088275 A KR20220088275 A KR 20220088275A KR 102513829 B1 KR102513829 B1 KR 102513829B1
- Authority
- KR
- South Korea
- Prior art keywords
- zinc
- cosmetic composition
- preservative
- free cosmetic
- mixtures
- Prior art date
Abstract
본 발명은 무방부제 화장료 조성물 및 이의 제조 방법에 관한 것으로, 이러한 조성물 및 이의 제조 방법에 따르면, 아연 화합물을 포함함으로써 통상의 방부제를 포함하지 않아도 방부 효과를 나타내어 제형 안정성을 확보할 수 있으며, 아연 화합물 그 자체에 의한 항염 및 항균 효과도 나타낼 수 있다.
Description
본 발명은 아연 화합물을 포함하는 무방부제 화장료 조성물 및 이의 제조 방법에 관한 것으로, 별도의 방부제 없이도 제형 안정성을 확보하고, 항염 및 항균 효과를 부여하는 무방부제 화장료 조성물 및 이의 제조 방법에 관한 것이다.
화장품이란 인체를 청결하게 하고 미화하여 용모를 밝게 변화시키거나 매력을 더하고, 피부와 모발의 건강을 유지 및 증진하기 위해 인체에 사용되는 물품을 말한다.
메이크업 화장품은 용모를 아름답게 변화시켜 피부를 아름답게 보이는 목적으로 사용되는 것으로, 피부에 도포 시 색채감을 부여하여 다채롭고 아름다운 피부색을 나타내도록 할 수 있고, 기초화장품으로 커버할 수 없는 피부의 결점을 보완하고 피부가 건강하고 매력적인 상태로 보일 수 있도록 한다.
또한 화장행위에 의하여 심리적인 만족감과 자신감을 생기게 하는 심리적 효과를 부여해주며, 피부를 아름답게 표현하는 미적 효과, 자외선으로 피부를 보호하는 보호적 효과를 부여한다.
과거의 메이크업 제품은 피부의 결점 보완 및 아름다운 피부색 표현과 같은 본연의 기능에만 충실했다면 최근에는 보습, 미백, 주름개선은 물론 항산화, 항염과 같은 실제 피부에 대해 케어 기능을 가지는 고효능 메이크업 제품이 늘어나고 있다.
이는 스킨케어와 메이크업의 경계가 허물어지고 단계가 간소화됨에 따른 현상으로, 색조 메이크업에서도 실제 인체에 좋은 영향을 줄 수 있는 제품 개발이 중요해지고 있다.
실제로 이런 유효한 기능을 가지는 제품에 가장 필수적인 요소는 제형의 안전성, 안정성, 유효성, 및 사용성이다. 안전성은 피부에 대한 자극, 알레르기, 독성이 없을 것, 안정성은 보관에 따른 산화, 변질, 변이, 미생물의 오염이 없을 것, 유효성은 피부 보습, 노화억제, 자외선차단, 미백, 세정, 색채효과 등 부여할 것, 사용성은 피부에 도포했을 때 사용감이 우수하고 매끄럽게 잘 스며들 것이다.
그러나, 일반적인 유화형태의 화장료 조성물은 시간이 지남에 따라 제형이 분리되는 현상이 발생하였고, 특히 방부제로 인하여 제형 안정성이 떨어져 오일분리 현상이 흔하게 발견되었으며, 이러한 오일분리 현상을 가지는 제품을 장기 보관시 오일층이 산패 및 변질되어 제품 사용시 피부에 안좋은 영향을 미칠 수 있다.
또한, 근래에 방부제가 피부에 미치는 자극성이 대두되면서, 방부제가 뾰루지, 가려움 등의 피부 트러블을 유발시킬 수 있는 원인이 되기도 한다는 문제가 제기되었다.
하지만 방부제가 사용되지 않는다면, 화장품은 식품 및 소비자가 직접 손으로 만지는 다른 제품들과 마찬가지로 미생물에 오염될 수 있으며, 이로 인해 변질, 변색, 변취 및 미생물 증식 등의 성능이 손실되고 이는 면역기능이 떨어져 있는 소비자에게 자극, 감염 등 건강에 해로운 반응을 야기할 수 있다.
따라서, 제형의 안정성이 곧 피부의 안전성과 연결되는 부분이며, 제품개발에 있어서 제형의 안정성을 확보하는 것은 매우 중요한 부분이다.
이에 본 발명자들은 항균 및 항염 효과를 가지는 아연 화합물을 화장료 조성물 내에 적용함으로써 제형 내 보존 효과를 개선함과 동시에 피부에 항균 및 항염 효과를 부여하는 무방부제 화장료 조성물에 관한 발명을 완성하였다.
본 발명의 목적은 아연 화합물을 포함함으로써 제형 내 항균 및 보존제의 역할을 하는 방부제 성분을 배합하지 않고도, 방부 효과를 나타내어, 제형의 안전성을 확보할 수 있는 화장료 조성물을 제공하는 것이다.
그리고 본 발명의 다른 목적은 실제 피부에 항균 및 항염 효과를 부여할 수 있는 화장료 조성물을 제공하는 것이다.
이하에서는, 본 발명을 더욱 상세히 설명한다.
한편, 본원에서 개시되는 각각의 설명 및 실시형태는 각각의 다른 설명 및 실시 형태에도 적용될 수 있다. 즉, 본원에서 개시된 다양한 요소들의 모든 조합이 본 발명의 범주에 속한다. 또한, 하기 기술되는 구체적인 서술에 의하여 본 발명의 범주가 제한된다고 할 수 없다.
어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 구비할 수 있다는 것을 의미한다.
본 발명은 아연 화합물을 포함하는 무방부제 화장료 조성물을 제공한다.
본 명세서에서, “아연 화합물”은 아연(Zn)을 포함하는 화합물이라면 특별히 제한되지 않으며, 아연은 염형태로 포함되거나, 다른 금속원자들과 배위결합된 형태를 나타낼 수 있다.
아연 화합물의 예시로는 할로겐화아연, 산화아연, 수산화아연, 질산아연, 인산아연, 징크설페이트, 징크카보네이트, 염화아연암모늄 등과 같은 무기 아연 화합물; 또는 포름산아연, 초산아연, 프로피온산아연, 스테아린산아연, 라우릴산아연, 라우린산아연, 올레인산아연, 아디프산아연, 글루콘산아연, 시트르산아연, 히드록시초산아연, 안식향산아연, 인산에스테르아연염 등의 유기산 아연염, 또는 방향족 아연염 화합물 등과 같은 유기 아연 화합물;을 들 수 있으나, 이에 제한되지 않는다.
일 구체예에서, 아연 화합물은, 징크, 산화아연, 마그네슘/알루미늄/징크/하이드록사이드/카보네이트(Magnesium/Aluminum/Zinc/Hydroxide/Carbonate), 징크피리치온(Zinc Pyrithione), 징크스테아레이트(Zinc Stearate), 징크글루코네이트(Zinc Gluconate), 징크설페이트(Zinc sulfate), 징크피씨에이(Zinc PCA, 피롤리돈카복실릭애씨드(PCA)의 아연염), 징크클로라이드(Zinc Chloride), 징크리시놀리에이트(Zinc ricinoleate), 징크미리스테이트(Zinc Myristate) 및 이들의 혼합물로 이루어진 군에서 선택된 적어도 어느 하나 이상일 수 있다. 보다 바람직하게는 산화아연일 수 있다.
일 구체예에서, 아연 화합물은 화장료 조성물 총 중량 대비 0.1wt% 내지 10wt%로 포함될 수 있다.
구체적으로, 아연 화합물은 화장료 조성물 총 중량 대비 0.1 wt% 이상, 0.5 wt% 이상, 0.7wt% 이상, 1.0wt% 이상, 1.5wt % 이상, 2wt% 이상, 또는 2.5wt% 이상일 수 있으며, 10 wt% 이하, 9.5 wt% 이하, 9 wt% 이하, 8.5 wt% 이하, 8 wt% 이하, 7.5 wt% 이하, 7 wt% 이하, 또는 6.5 wt% 이하로 포함될 수 있다. 바람직하게는 0.5 내지 8wt%, 1 내지 8wt%로 포함될 수 있고, 보다 바람직하게는 2 내지 7wt% 로 포함될 수 있다.
아연 화합물의 함량이 0.1wt% 미만일 경우, 본 발명의 조성물이 제형 내에서 항염 역할을 할 수 없으며, 10wt% 초과일 경우 제형의 사용감이 두꺼워지고 백탁이 생기는 등 부정적인 영향을 미칠 수 있다.
본 발명에 따른 무방부제 화장료 조성물은 유상 성분을 더 포함할 수 있으며, 상기 유상 성분은 지방, 왁스, 하이드로카본, 천연 오일, 에스테르 오일, 실리콘, 유화제 및 이들의 혼합물로 이루어진 군에서 선택된 하나 이상을 포함할 수 있다.
상기 유상 성분은 화장료 조성물 총 중량에 대하여 10 wt% 내지 75 wt% 로 포함될 수 있다. 구체적으로, 상기 유상 성분의 함량은 조성물 전체 중량 대비 10wt% 이상, 30wt% 이상, 35wt% 이상, 40wt% 이상, 45wt% 이상일 수 있으며, 75 wt% 이하, 70 wt% 이하, 68 wt% 이하, 65 wt% 이하일 수 있다.
일 구체예에서, 보다 구체적인 유상 성분은, 카프릴릭/카프릭트라이글리세라이드, 프로필렌카보네이트, 스테아랄코늄헥토라이트, 카프릴릭/카프릭트라이글리세라이드, 다이아이소스테아로일폴리글리세릴-3다이머다이리놀리에이트, 폴리글리세릴-4다이아이소스테아레이트/폴리하이드록시스테아레이트/세바케이트, 폴리글리세릴-3올리에이트, 합성비즈왁스 및 이들의 혼합물로 이루어진 군에서 선택된 적어도 어느 하나 이상을 포함할 수 있다.
본 발명에 따른 무방부제 화장료 조성물은 수상 성분을 더 포함할 수 있으며, 상기 수상 성분은 염, 금속이온봉쇄제, 폴리올 및 고분자 보습성분, 기능성성분, 및 이들의 혼합물로 이루어진 군에서 선택된 하나 이상을 포함할 수 있다.
상기 수상 성분은 화장료 조성물 총 중량에 대하여 10 wt% 내지 45 wt% 로 포함될 수 있다. 구체적으로, 상기 수상 성분의 함량은 조성물 전체 중량 대비 15wt% 이상, 20wt% 이상, 또는 25wt% 이상일 있으며, 45 wt% 이하, 40 wt% 이하, 38 wt% 이하, 또는 35 wt% 이하일 수 있다.
일 구체예에서, 보다 구체적인 수상 성분은 다이소듐이디티에이, 마그네슘설페이트, 부틸렌글라이콜, 정제수 및 이들의 혼합물로 이루어진 군에서 선택된 적어도 어느 하나 이상을 포함할 수 있다.
본 발명에 따른 무방부제 화장료 조성물은 살균제, 방부제 또는 보존제로 지정된 성분을 실질적으로 포함하지 않을 수 있다.
여기서, “포함하지 않을 수 있음”은 0.1중량% 미만, 0.01중량% 미만, 0.001중량% 미만, 또는 0.0001중량% 미만으로 해당 성분을 포함하거나, 전혀 포함하지 않음을 의미할 수 있다.
일반적으로, 화장료 조성물 내에 살균제, 방부제 또는 보존제로 지정된 성분들을 배합하지 않으면 화장료 내 미생물 오염이 쉽게 일어날 수 있다. 하지만, 본 발명에 따른 무방부제 화장료 조성물은 살균제, 방부제, 또는 보존제를 사용하지 않아도 우수한 방부 효과를 가질 수 있다.
상기 살균제, 방부제, 또는 보존제의 예시로, 파라벤류; 페녹시에탄올, 벤질알코올, 디클로로벤질알코올, 클로페네신과 같은 알코올류; 안식향산 및 이의 나트륨염, 소르빈산 및 이의 칼륨염, 디하이드로초산 및 이의 나트륨염과 같은 유기산 및 이의 염들; 메틸클로로이소티아졸, 메틸이소티아졸리논과 같은 이소티아졸 화합물; 이미다졸리디닐 우레아, 디아졸리디닐 우레아와 같은 우레아류; 디메칠옥사졸리딘, DMDM 하이단토인, 메텐아민, 트리클로산, 2-브로모-2-니트로프로판-1,3-디올 보레이트류, 브로모클로로펜, 살리실릭산 등이 있다.
한편, 본 발명에 따른 무방부제 화장료 조성물은 유중수형(W/O), 수중유형(O/W) 일 수 있으나, 그 제형에 있어 제한이 없다.
또한, 본 발명에 따른 무방부제 화장료 조성물은 메이크업 제품 또는 기초 화장 제품 등 제품의 종류에 제한되지 않으며, 구체적으로, 리퀴드 파운데이션, 비비크림, 메이크업베이스, 컨실러, 쿠션파운데이션, 유화 립틴트, 립스틱, 마스카라, 아이라이너 등 폭넓게 적용할 수 있다.
본 발명은 또한, 하기 단계를 포함하는 무방부제 화장료 조성물의 제조 방법을 제공한다:
1) 유상 성분 및 아연 화합물을 혼합하는 단계;
2) 상기 1) 단계의 혼합물을 교반하면서 수상 성분을 투입하여 에멀젼을 제조하는 단계; 및
3) 상기 2) 단계의 에멀젼을 냉각하는 단계.
상기 아연 화합물은 징크, 산화아연, 마그네슘/알루미늄/징크/하이드록사이드/카보네이트(Magnesium/Aluminum/Zinc/Hydroxide/Carbonate), 징크피리치온(Zinc Pyrithione), 징크스테아레이트(Zinc Stearate), 징크글루코네이트(Zinc Gluconate), 징크설페이트(Zinc sulfate), 징크피씨에이(Zinc PCA, 피롤리돈카복실릭애씨드(PCA)의 아연염), 징크클로라이드(Zinc Chloride), 징크리시놀리에이트(Zinc ricinoleate), 징크미리스테이트(Zinc Myristate) 및 이들의 혼합물로 이루어진 군에서 선택된 적어도 어느 하나 이상일 수 있다.
상기 유상 성분은 화장료 조성물 총 중량에 대하여 10 wt% 내지 75 wt%로 함유될 수 있다. 또한, 상기 유상 성분은 지방, 왁스, 하이드로카본, 천연오일, 에스테르, 실리콘, 유화제 및 이들의 혼합물로 이루어진 군에서 선택된 적어도 어느 하나 이상을 포함할 수 있다.
일 구체예에서, 상기 1) 단계는 화장료 조성물 총 중량에 대하여 10 wt% 내지 75 wt% 의 유상 성분과 0.1 wt% 내지 10 wt%의 아연 화합물을 혼합하는 단계를 포함할 수 있다.
상기 혼합은 실온에서 수행될 수 있고, 여기서, 실온은 20 내지 35℃, 보다 구체적으로 25 내지 30℃의 온도일 수 있다.
상기 1) 단계의 혼합 시 교반 속도는 500 내지 2000rpm, 보다 구체적으로 1000rpm 내지 1500rpm일 수 있다. 또한, 상기 1) 단계의 혼합 시간은 1분 내지 30분, 또는 2 내지 10분일 수 있으며, 혼합 방법은 패들 믹서를 이용할 수 있다.
일 구체예에서, 2) 에멀젼을 제조하는 단계는 상기 1) 단계의 혼합물을 고온에서 교반하면서 수상 성분을 투입하여 에멀젼을 제조하는 단계일 수 있다. 여기서, 상기 고온은 50℃ 이상, 60℃ 이상의 온도일 수 있고, 보다 구체적으로는 65 내지 85℃, 또는 70 내지 80℃ 의 온도일 수 있다.
상기 수상 성분은 화장료 조성물 총 중량에 대하여 10 wt% 내지 45 wt%로 함유될 수 있다. 또한, 상기 수상 성분은 염, 금속이온봉쇄제, 폴리올 및 고분자 보습성분, 기능성성분 및 이들의 혼합물로 이루어진 군에서 선택된 적어도 어느 하나 이상을 포함할 수 있다.
상기 2) 단계에서 교반 속도는 1000rpm 내지 2000rpm, 보다 구체적으로, 1500rpm 내지 1800rpm일 수 있다. 상기 2) 단계에서 수상 성분을 투입하고 5 내지 30분 동안 교반하여 에멀젼을 제조할 수 있다.
일 구체예에서, 3) 단계는 상기 제조된 2) 단계의 에멀젼을 냉각하는 단계로, 냉각 온도는 40℃ 이하, 35℃ 이하, 30℃ 이하, 구체적으로 30℃까지 냉각시킬 수 있다.
여기서, 유상 성분, 수상 성분, 아연 화합물의 구체 내용은 상기 무방부제 화장료 조성물에 기재된 내용을 그대로 적용할 수 있다.
본 발명에 따르면, 아연 화합물을 포함함으로써, 별도의 방부제 없이 방부 효과를 나타낼 수 있고, 이에 따라 제형의 안정성을 유지하며, 기존 방부제로 인한 피부 자극, 알레르기 및 독성 등으로부터 안전성을 확보할 수 있다.
또한, 아연 화합물 그 자체가 항균 및 항염 효과를 가져, 실제 피부에서 항균 및 항염 효과를 나타낼 수 있다.
도 1은 실험예 1에 따라 Mold (Aspergillus brasiliensis)균에서의 사멸률을 확인한 결과를 나타낸 그래프이다.
도 2는 실험예 2에 따라 실시예 2의 조성물의 세포독성 평가를 나타낸 그래프이다.
도 3은 실험예 2에 따라 실시예 2의 조성물의 NO 생성 억제능 평가를 나타낸 그래프이다.
도 2는 실험예 2에 따라 실시예 2의 조성물의 세포독성 평가를 나타낸 그래프이다.
도 3은 실험예 2에 따라 실시예 2의 조성물의 NO 생성 억제능 평가를 나타낸 그래프이다.
이하, 본 발명의 내용을 실시예 및 비교예를 통하여 보다 구체적으로 설명한다. 이들 실시예 및 비교예는 본 발명의 내용을 이해하기 위해 제시되는 것일 뿐 본 발명의 권리범위가 이들 실시예 및 비교예로 한정되는 것은 아니다.
<화장료 제조>
본 발명에 따른 무방부제 화장료 조성물은 다음과 같은 방법으로 제조하였다.
1) 표 1에 따라 유상 성분과 산화아연을 약 25℃내지 30℃의 실온에서 패들 믹서를 이용하여 1000rpm 내지 1500rpm으로 약 5분 동안 혼합하였다.
2) 상기 1)의 혼합물을 호모믹서를 이용하여 약 75℃내지 80℃의 고온에서 1500rpm 내지 1800rpm으로 약 10분 동안 혼합하면서 정제수 및 수용성 기능성 성분을 포함하는 수상 성분을 투입하여 에멀젼을 만들었다.
3) 상기 2)의 에멀젼을 30℃까지 냉각하였다.
| 구분 | 성분 | 비교예 1 | 실시예 1 | 실시예 2 | 실시예 3 | |
| 유상성분 | 사이클로펜타실록세인 | Cyclopentasiloxane | 10 | 10 | 10 | 10 |
| 다이스테아다이모늄헥토라이트 | Disteardimonium Hectorite | |||||
| 트라이에틸시트레이트 | Triethyl Citrate | |||||
| 폴리글리세릴-4다이아이소스테아레이트/폴리하이드록시스테아레이트/세바케이트 | Polyglyceryl-4 Diisostearate/Polyhydroxystearate/Sebacate | 2 | 2 | 2 | 2 | |
| 세틸피이지/피피지-10/1다이메티콘 | Cetyl PEG/PPG-10/1 Dimethicone | 5 | 5 | 5 | 5 | |
| 헥실라우레이트 | Hexyl Laurate | |||||
| 폴리글리세릴-4아이소스테아레이트 | Polyglyceryl-4 Isostearate | |||||
| 세틸피이지/피피지-10/1다이메티콘 | Cetyl PEG/PPG-10/1 Dimethicone | 4 | 4 | 4 | 4 | |
| 다이메티콘 | Dimethicone | 18 | 18 | 18 | 18 | |
| 페닐트라이메티콘 | Phenyl Trimethicone | 10 | 10 | 10 | 10 | |
| 부틸옥틸살리실레이트 | Butyloctyl Salicylate | 4 | 4 | 4 | 4 | |
| 다이에틸헥실카보네이트 | Diethylhexyl Carbonate | 10 | 10 | 10 | 10 | |
| 합성비즈왁스 | Synthetic Beeswax | 0.6 | 0.6 | 0.6 | 0.6 | |
| 폴리C10-30알킬아크릴레이트 | Poly C10-30 Alkyl Acrylate | 1 | 1 | 1 | 1 | |
| 트라이베헤닌 | Tribehenin | 1 | 1 | 1 | 1 | |
| 컬러런트 | 산화아연 | Zinc Oxide | 0 | 1 | 3 | 5 |
| 수상성분 | 트라이소듐에틸렌다이아민다이석시네이트 | Trisodium Ethylenediamine Disuccinate | 0.148 | 0.148 | 0.148 | 0.148 |
| 정제수 | Water | 32.452 | 31.452 | 29.452 | 27.452 | |
| 소듐클로라이드 | Sodium Chloride | 1.8 | 1.8 | 1.8 | 1.8 | |
실험예 1. 제형의 방부력 평가
상기 제조예에 따라 제조된 화장료 조성물에 대해, 제형의 방부력에 미치는 영향을 확인하는 실험을 진행하였다. 테스트 조건은 하기 표 2에 기재된 바와 같다.
| 조건 | 테스트 대상 | 비고 |
| 대상 | Bacteria / Yeast / Mold | 각 균주별 항균력 확인 Bacteria : 99.9%이상 사멸률일때 적합 Yeast : 90.0%이상 사멸률일때 적합 Mold : 90.0%이상 사멸률일때 적합 |
또한 다른 성분들이 동일한 함량으로 대응되도록 적용하고 그 결과를 하기 표 3에 나타내었다.
| 구분 | 균주 | 비교예 1 | 실시예 1 | 실시예 2 | 실시예 3 | |||||||||
| 7d | 14d | 28d | 7d | 14d | 28d | 7d | 14d | 28d | 7d | 14d | 28d | |||
| 사멸률 (%) |
Bacteria | Staphylococcus aureus | 87.28 | - | - | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 |
| Escherichia coli | 99.45 | - | - | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | ||
| Pseudomonas aeruginosa | 99.99 | - | - | 100 | 100 | 100 | 99.99 | 100 | 100 | 99.99 | 100 | 100 | ||
| Yeast | Candida albicans | 81.58 | - | - | 99.94 | 99.99 | 99.99 | 99.44 | 99.99 | 99.99 | 99.94 | 99.99 | 99.99 | |
| Mold | Aspergillus brasiliensis | 79.26 | - | - | 81.2 | 76 | 88 | 84.81 | 86.57 | 98.59 | 83.75 | 91.52 | 99.65 | |
상기 표 3에 따라 산화 아연이 첨가된 화장료 조성물에서 산화아연을 포함하는 제형이 포함하지 않는 제형보다 방부력에 우수한 효과가 있음을 확인하였다.
실험예 2. 세포 독성 평가 및 NO 생성 억제능 평가
상기 표 2의 방부효과가 있다고 판단되는 산화아연을 3wt%로 적용(실시예 2)하여 세포독성 평가와 NO 생성 억제능 평가를 통해 항염 효능을 확인하였다. 이의 테스트 조건은 표 4에 기재된 바와 같으며, 실험 결과는 표 5 및 6에 나타내었다.
구체적으로, 세포독성 평가의 실험 방법은, 먼저 96well plate에 RAW 264.7을 1 × 105cells/well씩 분주한 후, 세포 배양조건에서 배양하였다. 24시간 후, 배양액을 버리고 PBS로 세척한 다음 FBS를 함유하지 않은 DMEM 배지를 사용하여 세포를 기아 상태로 만들어주었다. 다음 날, 일정 농도의 시험물질을 처리하여 24시간 배양하였다. 배지에 10배 희석시킨 WST-1 시약을 각 well에 100 ul씩 넣고 2시간 배양 후, 450nm에서 흡광도를 측정하였다.
한편, NO 생성 억제능 평가 실험 방법은, 먼저 96well plate에 RAW 264.7을 1 × 105cells/well씩 분주한 후, 세포 배양조건에서 배양하였다. 24시간 후, 배양액을 버리고 PBS로 세척한 다음 FBS를 함유하지 않은 DMEM 배지를 사용하여 세포를 기아상태로 만들어주었다. 다음 날, 5 ug/ml의 LPS(lipopolysaccharide)와 함께 일정 농도의 시험물질을 처리하여 배양하였다. 24시간 후, 세포 배양액과 griess reagent를 동량 넣어 혼합 후, 15분간 상온에서 반응시켰다. 560nm에서 흡광도를 측정하였으며, NO의 양은 아질산나트륨(sodium nitrite)으로부터 얻은 표준곡선을 이용하여 결정하였다. 최종 NO의 양은 일정 단백질 당 NO의 양으로 환산하여 음성대조군과 비교하였다.
| 항목 | 테스트조건 | 비고 |
| 세포독성 평가 | RAW264.7의 세포독성 시험을 위해 시험물질을 농도별로 적용하여 시험 진행 | 세포 독성 확인 |
| No 생성 억제능 평가 | 효력시험을 위한 시험물질의 농도별로 적용하여 시험 진행 |
항염 효능 확인 |
| 시험물질 | 농도 | 세포 생존률(%) |
| Control | 100.0±3.8 | |
| 실시예 2 | 1000 | 31.8±5.1 |
| 500 | 67.5±2.1 | |
| 200 | 101.0±9.5 | |
| 100 | 103.0±3.2 | |
| 10 | 104.8±4.2 | |
| 시험물질 | 농도 | No 생성량(%) | |
| Control | 100.0±1.1 | ||
| LPS | 191.6±1.0 | ||
| Indomethacin (ug/ml) |
10 | 128.9±7.9 | |
| 실시예 2 | 200 | 165.4±7.8 | |
| 100 | 195.7±3.5 | ||
| 10 | 249.2±7.0 | ||
상기 표 5에 나타낸 바와 같이, 세포 독성 평가 결과, 산화아연을 포함하는 실시예 2의 조성물은 200 ug/ml 이하의 농도에서 RAW264.7 세포에 대한 세포 독성이 없는 것으로 나타났다.
NO 생성 억제능 평가에서의 농도는 세포독성이 없는 공통의 농도를 선정하여 효력의 농도 의존성을 확인하였다.
상기 표 6에 나타낸 바와 같이, NO 생성 억제능 평가 결과, LPS에 의해 91.6% 증가한 NO 생성량이 최고 26.2 % 억제되었으며, 농도 의존적으로 감소하였다.
지금까지 설명한 본 발명의 실시예들에 의한 아연 화합물을 포함하는 조성물에 따르면, 아연 화합물을 포함하는 조성물의 제형이 우수한 방부의 효과를 주기 위해서는 아연 화합물이 3wt% 이상 적용이 될 때 효과가 우수함을 확인하였으며, 그 결과에 따라서 제형의 안정도가 개선되면서 실제 피부에 항염의 기능까지도 제공할 수 있다.
상기에서는 본 발명의 일 실시예를 참조하여 설명하였지만, 해당 기술분야의 당업자는 이하에서 서술하는 특허 청구범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경 실시할 수 있을 것이다. 그러므로 변형된 실시가 기본적으로 본 발명의 특허청구범위의 구성 요소를 포함한다면 모두 본 발명의 기술적 범주에 포함된다고 보아야 한다.
Claims (14)
- 유상 성분, 10 wt% 내지 45 wt%의 수상 성분 및 0.1wt% 내지 10wt%의 아연 화합물을 포함하고,
방부 효과를 나타내는 성분으로 아연 화합물만을 포함하며,
아연 화합물 및 유상 성분을 혼합한 다음 수상 성분을 투입하여 제조되는 무방부제 화장료 조성물. - 제1항에 있어서,
상기 아연 화합물은 징크, 산화아연, 마그네슘/알루미늄/징크/하이드록사이드/카보네이트(Magnesium/Aluminum/Zinc/Hydroxide/Carbonate), 징크피리치온(Zinc Pyrithione), 징크스테아레이트(Zinc Stearate), 징크글루코네이트(Zinc Gluconate), 징크설페이트(Zinc sulfate), 징크피씨에이(Zinc PCA, 피롤리돈카복실릭애씨드(PCA)의 아연염), 징크클로라이드(Zinc Chloride), 징크리시놀리에이트(Zinc ricinoleate), 징크미리스테이트(Zinc Myristate) 및 이들의 혼합물로 이루어진 군에서 선택된 적어도 어느 하나 이상인 것을 특징으로 하는 무방부제 화장료 조성물. - 삭제
- 제1항에 있어서,
상기 아연 화합물의 함량은 화장료 조성물 총 중량 대비 2wt% 내지 7wt%인 무방부제 화장료 조성물. - 제1항에 있어서,
상기 유상 성분의 함량은 무방부제 화장료 조성물 총 중량에 대하여 10 wt% 내지 75 wt%인 무방부제 화장료 조성물. - 제1항에 있어서,
상기 유상 성분은 지방, 왁스, 하이드로카본, 천연오일, 에스테르, 실리콘, 유화제 및 이들의 혼합물로 이루어진 군에서 선택된 적어도 어느 하나 이상을 포함하는 것을 특징으로 하는 무방부제 화장료 조성물. - 삭제
- 제1항에 있어서,
상기 수상 성분은 염, 금속이온봉쇄제, 폴리올 및 고분자 보습 성분, 기능성 성분 및 이들의 혼합물로 이루어진 군에서 선택된 적어도 어느 하나 이상을 포함하는 것을 특징으로 하는 무방부제 화장료 조성물. - 1) 유상 성분 및 아연 화합물을 혼합하는 단계;
2) 상기 1) 단계의 혼합물을 교반하면서 수상 성분을 투입하여 에멀젼을 제조하는 단계; 및
3) 상기 2) 단계의 에멀젼을 냉각하는 단계;를 포함하는 제1항에 따른 무방부제 화장료 조성물의 제조 방법. - 제9항에 있어서,
상기 아연 화합물은 징크, 산화아연, 마그네슘/알루미늄/징크/하이드록사이드/카보네이트(Magnesium/Aluminum/Zinc/Hydroxide/Carbonate), 징크피리치온(Zinc Pyrithione), 징크스테아레이트(Zinc Stearate), 징크글루코네이트(Zinc Gluconate), 징크설페이트(Zinc sulfate), 징크피씨에이(Zinc PCA, 피롤리돈카복실릭애씨드(PCA)의 아연염), 징크클로라이드(Zinc Chloride), 징크리시놀리에이트(Zinc ricinoleate), 징크미리스테이트(Zinc Myristate) 및 이들의 혼합물로 이루어진 군에서 선택된 적어도 어느 하나 이상인 것을 특징으로 하는 무방부제 화장료 조성물의 제조 방법. - 제9항에 있어서,
상기 유상 성분은 화장료 조성물 총 중량에 대하여 10 wt% 내지 75 wt%로 함유되는 것을 특징으로 하는 무방부제 화장료 조성물의 제조 방법. - 제9항에 있어서,
상기 유상 성분은 지방, 왁스, 하이드로카본, 천연오일, 에스테르, 실리콘, 유화제 및 이들의 혼합물로 이루어진 군에서 선택된 적어도 어느 하나 이상을 포함하는 무방부제 화장료 조성물의 제조 방법. - 삭제
- 제9항에 있어서,
상기 수상 성분은 염, 금속이온봉쇄제, 폴리올 및 고분자 보습성분, 기능성성분, 및 이들의 혼합물로 이루어진 군에서 선택된 적어도 어느 하나 이상을 포함하는 것을 특징으로 하는 무방부제 화장료 조성물의 제조 방법.