KR102477277B1 - 원적외선 방사 및 항균 기능을 나타내는 건축 자재 - Google Patents
원적외선 방사 및 항균 기능을 나타내는 건축 자재 Download PDFInfo
- Publication number
- KR102477277B1 KR102477277B1 KR1020220103750A KR20220103750A KR102477277B1 KR 102477277 B1 KR102477277 B1 KR 102477277B1 KR 1020220103750 A KR1020220103750 A KR 1020220103750A KR 20220103750 A KR20220103750 A KR 20220103750A KR 102477277 B1 KR102477277 B1 KR 102477277B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- extract
- powder
- acrylate
- Prior art date
Abstract
본 발명은 원적외선 방사기능 및 항균기능을 가지는 건축 자재용 조성물을 제공한다. 본 발명에 따른 건축 자재용 조성물은 원적외선 방사기능 및 항균기능을 나타내며, 원적외선 방사기능 및 항균기능의 지속력이 우수하다.
Description
본 발명은 원적외선 방사 및 항균 기능을 나타내는 건축 자재에 관한 것이다.
최근 원적외선이 주환경 개선이나 사람의 건강 증진에 기여하는 것이 넓게 알려지게 되어, 그 큰 작용 하나에 산화의 진행을 저지하는 항산화 작용이 있고, 이 항산화 작용은 유해 가스의 무해화, 곰팡이 발생 억제, 선도 유지, 체질개선의 효과를 발생시킴으로써 있다.
전자파의 일종인 원적외선은 인체에 가장 유익한 파장인 8-16 um를 갖고 있으며, 인체에 흡수 될 때 일반열보다 80배나 깊은 피부심층(4-5 cm)까지 침투하여 병원균이나 암세포 등을 죽일뿐만 아니라 인체 내 세포를 구성하는 수분과 단백질 분자에 방사되어 1분에 약 2,000번씩 미세한 진동으로 공진시켜 세포의 활동을 왕성하게 하여 열에너지를 발생시키면서 체온을 높이는 작용을 하는데, 체온이 높아지면 미세혈관이 확장되고 혈액 순환이 활성화되면서 신진대사가 강화되며, 조직재생력이 증가하면서 혈관 내 혈전을 분해하고 혈액순환을 촉진한다. 혈액이 맑아지므로 pH를 향상시켜 체질을 산성에서 약알칼리성으로 개선시키는 능력을 강화시키고 또한 정신건강에 도움이 되는 이완작용으로 성인병의 원인인 스트레스 해소에도 효과가 있다. 이러한 효과 때문에 원적외선을 생명광선 또는 생육광선이라고도 한다.
이와 같이 인체에 유익한 음이온 및 원적외선을 방사하는 물질 중에 최근 토르말린(tourmaline)이 각광받고 있는데, 토르말린은 철, 마그네슘, 알칼리금속 등과 알루미늄의 복잡한 붕규산염으로서, 마찰에 의해서 전기가 생기며, 가열하면 양끝이 양, 음으로 대전되기 때문에 '전기석'이라고도 한다.
토르말린은 물에 접촉할 때 효과가 극대화되는데, 물을 음이온화하는 동시에 약알칼리성으로 바꾸기 때문이다. 즉, 토르말린의 마이너스 전극에 축적된 전자는 물에 접촉되는 순간 방전되고 물은 수소이온과 수산화이온으로 전기 분해되는 것으로, 수소 이온은 토르말린이 방출한 마이너스 전자와 결합하여 수소가 되어 방출되며, 수산화이온은 물분자와 결합하여 음이온인 하이드록시 이온이 되는데, 이것이 바로 토르말린의 음이온 방출 효과를 말하는 것이다.
그러나 이러한 물질들을 건축 자재로 적용하는 경우 원적외선이 유효하게 방사되지 않거나, 안정적으로 오랜기간 동안 공급하는 것이 어려운 실정이다.
본 발명은 상기와 같은 문제점을 해결하기 위해 안출된 것으로서, 본 발명의 목적은 원적외선 방사에 효과적이고 항균 기능을 부여한 건축 자재 조성물을 제공하는 것이다.
본 발명의 과제는 이상에서 언급한 과제들로 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.
상기 목적을 달성하기 위하여 본 발명은
미네랄원료를 포함하는 건축 자재용 조성물을 제공한다.
또한, 상기 건축 자재용 조성물은 토르말린 분말 13-17 중량부, 일라이트 분말 13-17 중량부, 각섬석 분말 13-17 중량부, 흑운모 분말 13-17 중량부, 아크릴레이트계 고분자 바인더 28-32 중량부, 탄소섬유 분산액 2-6 중량부, 항균제 0.5-3 중량부, 기능성 추출물 0.5-3 중량부 및 미네랄원료 1-5 중량부를 포함하고,
상기 아크릴레이트계 고분자 바인더는 메틸메타크릴레이트 단량체 단위 23-27 중량%, 에틸헥실아크릴레이트 단량체 단위 23-27 중량%, 아크릴산 단량체 단위 23-27 중량% 및 글리시딜메타크릴레이트 단량체 단위 23-27 중량%인 제1 아크릴레이트계 공중합체 및 에틸메타크릴레이트 단량체 단위 23-27 중량%, n-부틸메타크릴레이트 단량체 단위 23-27 중량%, 글리시딜메타크릴레이트 단량체 단위 23-27 중량% 및 하이드록시에틸 메타크릴레이트 단량체 단위 23-27 중량%인 제2 아크릴레이트계 공중합체의 78-82:18-22의 중량비율로 혼합된 혼합물로 이루어지고,
상기 탄소섬유 분산액은 탄소섬유 33-37 중량부 및 토르말린 추출물, 일라이트 추출물, 각섬석 추출물 및 흑운모 추출물을 포함하는 증류수 63-67 중량부를 포함하고,
상기 항균제는 박하 추출물, 어성초 추출물, 고삼 추출물, 치자 추출물 및 애엽 추출물을 1:1:1:1:1의 중량비율로 혼합한 혼합물이고,
상기 기능성 추출물은 동충하초, 솔풍령, 해송, 삼나무, 삼백초, 백리향, 넓적떡다리버섯, 삼감황, 적운초, 육두구 및 돌배나무를 포함하는 혼합물을 추출한 것이고,
상기 미네랄원료는 칼슘 31-35 중량부, 마그네슘 18-22 중량부, 칼륨 14-18 중량부, 규소 14-18 중량부, 티타늄 8-12 중량부, 탄소 0.5-2 중량부, 붕소 0.1-1 중량부, 셀레늄 0.05-0.5 중량부, 인 0.05-0.5 중량부 및 황 0.05-0.5 중량부를 포함하는 것을 특징으로 한다.
또한, 본 발명은
메틸메타크릴레이트 단량체, 에틸헥실아크릴레이트 단량체, 아크릴산 단량체 및 글리시딜메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제1 아크릴레이트계 공중합체를 제조하는 단계; 에틸메타크릴레이트 단량체, n-부틸메타크릴레이트 단량체, 글리시딜메타크릴레이트 단량체 및 하이드록시에틸 메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제2 아크릴레이트계 공중합체를 제조하는 단계; 및 상기 제1 아크릴레이트계 공중합체와 상기 제2 아크릴레이트계 공중합체를 78-82:18-22의 중량비율로 혼합하는 단계;를 포함하는 아크릴레이트계 고분자 바인더를 제조하는 단계;
토르말린 분말, 일라이트 분말, 각섬석 분말 및 흑운모 분말을 1:1:1:1의 중량비율로 혼합한 혼합분말을 준비하는 단계; 상기 혼합분말 18-22 중량부 및 증류수 78-82 중량부를 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 84-88℃의 온도로 가열하여 추출하는 단계; 추출 후, 혼합물을 여과하여 추출액을 제조하는 단계; 및 탄소섬유 33-37 중량부 및 상기 추출액 63-67 중량부를 혼합하고 초음파조사하는 단계;를 포함하는 탄소섬유 분산액을 제조하는 단계;
박하, 어성초, 고삼, 치자 및 애엽을 세척한 후, 분쇄하여 준비하는 단계; 준비된 박하, 어성초, 고삼, 치자 및 애엽을 1:1:1:1:1의 중량비율로 혼합하여 혼합물을 제조하는 단계; 상기 혼합물 90-110 중량부 및 에탄올과 아세톤이 1:1의 부피비율로 혼합된 혼합용매 900-1100 중량부를 혼합한 후, 초음파공정으로 38-42℃의 온도에서 22-26시간 동안 추출액을 제조하는 단계; 및 상기 추출액을 감압농축 및 동결건조하는 단계;를 포함하는 항균제를 제조하는 단계;
동충하초, 솔풍령, 해송, 삼나무, 삼백초, 백리향, , 삼감황, 적운초 및 돌배나무를 세척한 후, 분쇄하여 준비하는 단계; 준비된 동충하초, 솔풍령, 해송, 삼나무, 삼백초, 백리향, 넓적떡다리버섯, 삼감황, 적운초 및 돌배나무를 1:1:1:1:1:1:1:1:1:1의 중량비율로 혼합하여 혼합물을 제조하는 단계; 및 상기 혼합물 90-110 중량부 및 증류수 900-1100 중량부를 혼합한 후 증기증류법으로 추출하는 단계;를 포함하는 기능성 추출물을 제조하는 단계; 및
토르말린 분말 13-17 중량부, 일라이트 분말 13-17 중량부, 각섬석 분말 13-17 중량부, 흑운모 분말 13-17 중량부, 상기 아크릴레이트계 고분자 바인더 28-32 중량부, 상기 탄소섬유 분산액 2-6 중량부, 상기 항균제 0.5-3 중량부, 상기 기능성 추출물 0.5-3 중량부 및 칼슘 31-35 중량부, 마그네슘 18-22 중량부, 칼륨 14-18 중량부, 규소 14-18 중량부, 티타늄 8-12 중량부, 탄소 0.5-2 중량부, 붕소 0.1-1 중량부, 셀레늄 0.05-0.5 중량부, 인 0.05-0.5 중량부 및 황 0.05-0.5 중량부를 포함하는 미네랄원료 1-5 중량부를 혼합하는 단계;를 포함하는 건축 자재용 조성물의 제조방법을 제공한다.
본 발명에 따른 건축 자재용 조성물은 원적외선 방사기능 및 항균기능을 나타내며, 원적외선 방사기능 및 항균기능의 지속력이 우수하다.
도 1은 본 발명에 따른 건축 자재용 조성물의 제조방법을 순서도로 나타낸 것이다.
이하에서는 첨부된 도면을 참조하여 다양한 실시예를 보다 상세하게 설명한다. 본 명세서에 기재된 실시예는 다양하게 변형될 수 있다. 특정한 실시예가 도면에서 묘사되고 상세한 설명에서 자세하게 설명될 수 있다. 그러나 첨부된 도면에 개시된 특정한 실시 예는 다양한 실시예를 쉽게 이해하도록 하기 위한 것일 뿐이다. 따라서 첨부된 도면에 개시된 특정 실시예에 의해 기술적 사상이 제한되는 것은 아니며, 발명의 사상 및 기술 범위에 포함되는 모든 균등물 또는 대체물을 포함하는 것으로 이해되어야 한다.
1차, 2차, 제1, 제2 등과 같이 서수를 포함하는 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 이러한 구성요소들은 상술한 용어에 의해 한정되지는 않는다. 상술한 용어는 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다.
본 명세서에서, '포함한다' 또는 '가지다' 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다. 어떤 구성요소가 다른 구성요소에 '연결되어' 있다거나 '접속되어' 있다고 언급된 때에는, 그 다른 구성요소에 직접적으로 연결되어 있거나 또는 접속되어 있을 수도 있지만, 중간에 다른 구성요소가 존재할 수도 있다고 이해되어야 할 것이다. 반면에, 어떤 구성요소가 다른 구성요소에 '직접 연결되어' 있다거나 '직접 접속되어' 있다고 언급된 때에는, 중간에 다른 구성요소가 존재하지 않는 것으로 이해되어야 할 것이다.
그 밖에도, 본 발명을 설명함에 있어서, 관련된 공지 기능 혹은 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우, 그에 대한 상세한 설명은 축약하거나 생략한다.
본 발명은 미네랄원료를 포함하는 건축 자재용 조성물을 제공한다.
이하, 본 발명에 따른 건축 자재용 조성물에 대하여 상세히 설명한다.
상기 건축 자재용 조성물은 토르말린 분말 13-17 중량부, 일라이트 분말 13-17 중량부, 각섬석 분말 13-17 중량부, 흑운모 분말 13-17 중량부, 아크릴레이트계 고분자 바인더 28-32 중량부, 탄소섬유 분산액 2-6 중량부, 항균제 1-5 중량부 및 기능성 추출물 1-5 중량부를 포함하는 것이 바람직하고, 토르말린 분말 14-16 중량부, 일라이트 분말 14-16 중량부, 각섬석 분말 14-16 중량부, 흑운모 분말 14-16 중량부, 아크릴레이트계 고분자 바인더 29-31 중량부, 탄소섬유 분산액 3-5 중량부, 항균제 0.5-3 중량부, 기능성 추출물 0.5-3 중량부 및 미네랄원료 1-5 중량부를 포함하는 것이 더욱 바람직하다.
토르말린(tourmaline)은 광물 중에서 유일하게 영구적인 전기특성을 가진 극성결정체로서 전기석이라고도 불리운다. 토르말린은 마그네슘, 철, 붕소, 규소 및 칼슘을 주성분으로 하고 있으며, 이 광석에서는 인체에 유익한 음이온, 미세전류, 및 원적외선을 발생하는 것으로 밝혀졌다.
일라이트(illite)는 대표적인 천연점토 광물질로서 다공성 운모 미네랄이며, 얇은 판상의 구조로 요곡성과 탄성을 가지고 있어 탄성과 흡착성이 뛰어나다. 또한, 40℃에서 방사율 93%, 3.71 x 102의 원적외선을 방사한다. 그밖에 항균작용 및 중금속 흡착 성능을 갖고 있다.
각섬석(amphibloe)은 칼슘, 마그네슘 및 철을 주성분으로 하고 알루미늄을 약간 함유하는 검은색의 광물질로 곱돌이라고도 한다. 이러한 각섬석은 열이 가해질 경우 원적외선 및 무기산 등을 다량 방출하는 것으로 밝혀졌다. 특히 인체에 유익한 9∼10 마이크론의 원적외선(방사율 92%)을 방출한다.
흑운모(biotite)는 40도의 온도에서 원적외선 방사율이 93%이다. 이러한 광물질 등은 각각 살균작용, 액체분자 미세화, 원적외선 방사, 산소보충기능, 인체흡수능력 향상, 산성중화기능, 흡착기능 등 다양한 기능을 지니고 있는 것으 로 알려져 있다. 특히 상기한 광물질에서 방사된 원적외선에서 방출하는 파장은 수분과 단백질 분자에 닿을 경우에 세포를 1분에 2,000번씩 미세하게 공명, 공진시켜 세포노화를 방지하는 기능을 가지고 있다.
본 발명에서는 상기 토르말린, 일라이트, 각섬석 및 흑운모를 1:1:1:1의 중량비율로 혼합된 조성물을 제시한다. 또한, 단순히 원적외선 효능을 나타내는 광석물질만을 사용한 것이 아닌, 고분자 바인더, 탄소섬유 분산액, 항균제 및 기능성 추출물을 더 포함함으로써 우수한 성능의 원적외선 방사기능과 동시에 항균기능을 나타내며 이러한 기능에 대한 지속력이 우수하다.
상기 아크릴레이트계 고분자 바인더는 메틸메타크릴레이트 단량체 단위 23-27 중량%, 에틸헥실아크릴레이트 단량체 단위 23-27 중량%, 아크릴산 단량체 단위 23-27 중량% 및 글리시딜메타크릴레이트 단량체 단위 23-27 중량%인 제1 아크릴레이트계 공중합체 및 에틸메타크릴레이트 단량체 단위 23-27 중량%, n-부틸메타크릴레이트 단량체 단위 23-27 중량%, 글리시딜메타크릴레이트 단량체 단위 23-27 중량% 및 하이드록시에틸 메타크릴레이트 단량체 단위 23-27 중량%인 제2 아크릴레이트계 공중합체의 78-82:18-22의 중량비율로 혼합된 혼합물로 이루어진 것을 사용하는 것이 바람직하다. 상기 아크릴레이트계 고분자 바인더로 상기 물질을 적용함으로써 건축 자재용 조성물에 포함된 성분들 간의 부착력을 높이고 제조되는 건축 자재의 내구성, 내수성 및 고탄성을 확보할 수 있다.
상기 탄소섬유 분산액은 탄소섬유 33-37 중량부 및 토르말린 추출물, 일라이트 추출물, 각섬석 추출물 및 흑운모 추출물을 포함하는 증류수 63-67 중량부를 포함하는 것이 바람직하고, 탄소섬유 34-36 중량부 및 토르말린 추출물, 일라이트 추출물, 각섬석 추출물 및 흑운모 추출물을 포함하는 증류수 64-66 중량부를 포함하는 것이 더욱 바람직하다.
상기 탄소섬유는 소취, 흡습, 단열을 수행할 수 있다. 더욱이, 상기 건축 자재용 조성물에 포함되어 토르말린 분말, 일라이트 분말, 각섬석 분말 및 흑운모 분말 또는 항균제를 바인더를 통해 더욱 강하게 결합시킬 수 있고, 이에 따라 원적외선 방사기능 및 항균기능의 지속력이 우수하다.
더욱이, 탄소섬유 분산액을 적용하기 위해 사용된 분산용매는 토르말린 분말, 일라이트 분말, 각섬석 분말 및 흑운모 분말을 증류수와 혼합한 후 가열하여 추출하고, 여과하여 얻은 것으로서, 원적외선 방사기능이 부여된 증류수이다. 이를 이용하여 탄소섬유 분산액을 제조하여 최종 건축 자재용 조성물의 용제로 적용하여 더욱 우수한 원적외선 방사기능 및 향균기능과 더불어 이의 지속력을 높일 수 있다.
상기 항균제는 박하 추출물, 어성초 추출물, 고삼 추출물, 치자 추출물 및 애엽 추출물을 1:1:1:1:1의 중량비율로 혼합한 혼합물을 포함한다.
박하는 온대지방이 고향인 여러해살이풀로, 잎 표면에 있는 기름샘에 정유의 대부분을 저장하여 잎과 줄기에서 진한 향이 난다. 박하유의 주성분은 멘톨이며, 이 멘톨은 도포제(塗布劑), 진통제, 흥분제, 건위제, 구충제 등 에 약용하거나 치약, 잼, 사탕, 화장품, 담배 등에 청량제 또는 향료로 사용된다.
어성초(Houttuynia cordata)는 약모밀이라고도 하며, 잎에서 비린내가 난다고 해서 어성초라고 이름 붙여졌다. 잡초와 같은 왕성한 번식력을 자랑하는 어성초는 나쁜 피, 즉 어혈을 풀어주고, 살균효과가 뛰어나 아토피에 좋다고 알려지면서 관심을 받기 시작하였다. 잎에는 쿠에르시트린이, 꽃과 열매 이삭에는 아이소쿠에르시트린이 들어 있어, 항균작용, 면역증강작용, 항염증작용, 이뇨작용, 진해작용 등이 있는 것으로 알려져 있다.
고삼(Sophora flavescens AIT)은 콩과에 속하는 다년생 초본으로, 주로 뿌리를 한약재로 사용한다. 약효성분으로는 마트린이 함유되어 있으며, 동물실험에서는 해열작용과 이뇨효과가 인정되었다. 또한, 건위작용이 있어, 위장염, 장염, 세균성 이질에 목향(木香)·감초와 같이 달여서 복용하면 치유되는 것으로 알려져 있다.
치자는 치자나무(Gardenia jasminoides J.Ellis)의 열매로, 뜨거운 물에 우려내면 식용으로 사용 가능한 노란색 색소를 추출할 수 있으나, 일정량 이상을 섭취할 경우 부작용이 발생한다. 한방에서는 해열, 지혈에 효능이 있는 것으로 알려져 있다.
애엽은 한방에서 국화과의 황해쑥(Artemisia argyi Lev. et Vant.), 쑥(A. princeps Pamp. var. orientlis Hara) 또는 산쑥(A. montana Pamp.)의 잎 및 어린줄기를 말린 약재를 의미하며, 특이한 방향이 있고 맛은 맵고 쓰며 성질은 따뜻하고 약간 독이 있는 것으로 알려져 있다. 따라서 애엽은 지혈작용, 억균작용, 기관지 평활근 이완작용, 진해거담작용, 수면작용, 자궁흥분유도작용, 과민성 쇼크 보호작용 등이 있다.
상기 물질들을 원료로하여 추출된 추출물을 항균제로 적용하여 친환경적일 뿐만 아니라, 우수한 항균기능을 부여할 수 있다.
상기 기능성 추출물은 동충하초, 솔풍령, 해송, 삼나무, 삼백초, 백리향, 넓적떡다리버섯, 삼감황, 적운초, 육두구 및 돌배나무를 포함하는 혼합물을 추출한 것을 특징으로 한다.
동충하초는 겨울철에 린시목에 속하는 곤충인 유충이 침입하여 그속에서 자라 균핵이 생기며 여름철에 머리 부분에서 곤봉모양의 자실체가 돋아난다. 겨울에는 벌레 밖에 보이지 않던 것이 여름에는 풀모양의 자실체로 변한다고 하여 동충하초라고 부른다.
솔풍령은 벌목후 3년 이상이지만 소나무 뿌리에 혹처럼 자란 균핵으로서 다당균인 파기만이 약 94% 존재하며, 이밖에 당, 무기물, 철, 칼슘, 마그네슘, 나트리움, 베르고테롤이 존재하며 신장에 좋고 불면증 치료제로 사용된다.
해송은 사철푸른 키나무로서 소나무와 비슷하지만 잎이 질기고 곧으며 껍질은 검은색을 띠고 우리나라 중부,남부 바닷가에서 자라며 성분은 잎에는 아스크로빈산, 카르티노이드, 피토스테린, 세틸알콜, 유니페르산을 주성분으로한 에스톨리드형랍, 헥사데칸2디올, 두어 데칸12디올, 트리아콘탄올정유가 있으며 정유는 -피넨,β-피넨, 캄펜, 디펜텐, 보르네올, 보르닐아세테이트, 세스쿠이테르펜, 세스쿠이테르펜알콜, 티데르펜동이 있고, 뿌리에는 -피넨을 주성분으로 하고 디펜텐, 캄펜등으로 이루어진 정유가 있다.
삼나무는 사철나무로서 잎은 짧은 모양이고 남부의 산에서 자라고 있으며,성분은 잎에 정유 0.7%, 목부 1%가 들어 있고 정유의 주성분은 피넨, 디펜텐, 카디넨, 크립토메디올, 마키롤동이 함유되어 있고 외상, 조갈, 각기병에 효과가 있다.
삼백초는 높이 15-30 cm 으로 다년생풀로서 우리나라 중부와 남부지방 습한곳에서 자라고 생선비린내가 나는 것이 특징이며, 성분으로서 유기성분은 메틸노닐케톤, 머르젠, 라우린 알데히드, 카프린알데히드, 카프린 산이고 무기성분으로서 주성분은 칼리움염이 있고 미량의 게르마늄도 포함되어 있다고 한다.
백리향은 높이 15 cm 홍색의 꽃이피고 뿌리로 번식하며 성분은 페놀성물질이고 정유에는 티몰, 카르바크롤찌몰이 함유되어 있으며, 기관지염, 살균제, 눈염증, 입안궤양, 입안냄새제거, 월경조절, 위경련에 유효하다.
넓적떡다리버섯은 갓의 크기가 직경 5-30 cm의 말발굽 모양으로 노란색이나 붉은 밤색이고, 성분으로서는 에르고르테롤, 우비키논(조효소) 5.6-디히드로 에르코르테롤이 함유되어 있고, 약효로는 피멎이약으로 혈봉, 혈림, 탈홍, 대하, 월경불순 치료제로 사용된다.
삼강황은 타원형의 노란 꽃이 피며 히말리아 고산 지방에서 자라며 성분으로서 뿌리줄기에는 노란색 소물질이 0.4-0.6%, 정유가 6-10% 함유되어 있다. 노란 색소물질은 쿠르쿠민과 그의 유사물질로 되어 있고, 정유에는 세스쿠이테르펜, 세스쿠이테르펜알콜, d-캄파, d-캄펜, 투루메론, P-토릴메틸카르비놀로 구성된다.
적운초는 잎이 공팥같은 모양이고 연한 가지색의 꽃이 핀다. 적운초의 특성은 오줌을 잘나가게 하고 콩팥 결석, 방광결석, 황달에도 유효하다.
육두구는 높이 8~16m나 되는 육두구과의 상록교목으로 암수 딴 그루이며 둥글고 굳은 열매가 감색으로 여문다. 인도네시아 몰루카 원산이며 동남아 열대지방에서 재배한다. 4-6월, 11-12월에 열매를 따서 씨만을 꺼내어 말린다. 검은색의 단단한 씨껍질을 까버리고 석회즙에 하룻밤 담갔다가 상온에서 말린 것을 육두구라하며, 육질의 겉껍질을 벗겨서 말린것을 육두구화라고 한다.
돌배나무는 장미과로서, 봄에 높지 않은 산지에서 가지마다 흰색의 꽃이 많이 피는 돌배나무는 중부 이남에 자라는 낙엽수이다. 잎은 어긋나고 염통 모양이며 가장자리에 바늘 모양의 톱니가 있다. 4-5 월에 피는 꽃은 희며 어긋난 우산살 꽃차례를 이루고, 꽃잎은 5개이다. 10월에 익는 열매는 둥글며 다갈색으로 먹기도 한다.
상기 동충하초, 솔풍령, 해송, 삼나무, 삼백초, 백리향, 넓적떡다리버섯, 삼감황, 적운초 및 돌배나무를 포함하는 혼합물을 추출한 추출물은 원적외선 방사기능 및 항균기능을 동시에 가져, 본 발명에 따른 건축 자재용 조성물에 적용하는 경우 우수한 원적외선 방사기능 및 항균기능을 제공한다.
상기 미네랄원료는 칼슘 31-35 중량부, 마그네슘 18-22 중량부, 칼륨 14-18 중량부, 규소 14-18 중량부, 티타늄 8-12 중량부, 탄소 0.5-2 중량부, 붕소 0.1-1 중량부, 셀레늄 0.05-0.5 중량부, 인 0.05-0.5 중량부 및 황 0.05-0.5 중량부를 포함한다. 본 발명에 따른 건축 자재용 조성물은 상기 미네랄원료를 포함하여 더욱 우수한 원적외선 방사기능 및 향균기능과 더불어 이의 지속력을 높일 수 있다.
또한, 본 발명은
메틸메타크릴레이트 단량체, 에틸헥실아크릴레이트 단량체, 아크릴산 단량체 및 글리시딜메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제1 아크릴레이트계 공중합체를 제조하는 단계; 에틸메타크릴레이트 단량체, n-부틸메타크릴레이트 단량체, 글리시딜메타크릴레이트 단량체 및 하이드록시에틸 메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제2 아크릴레이트계 공중합체를 제조하는 단계; 및 상기 제1 아크릴레이트계 공중합체와 상기 제2 아크릴레이트계 공중합체를 78-82:18-22의 중량비율로 혼합하는 단계;를 포함하는 아크릴레이트계 고분자 바인더를 제조하는 단계;
토르말린 분말, 일라이트 분말, 각섬석 분말 및 흑운모 분말을 1:1:1:1의 중량비율로 혼합한 혼합분말을 준비하는 단계; 상기 혼합분말 18-22 중량부 및 증류수 78-82 중량부를 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 84-88℃의 온도로 가열하여 추출하는 단계; 추출 후, 혼합물을 여과하여 추출액을 제조하는 단계; 및 탄소섬유 33-37 중량부 및 상기 추출액 63-67 중량부를 혼합하고 초음파조사하는 단계;를 포함하는 탄소섬유 분산액을 제조하는 단계;
박하, 어성초, 고삼, 치자 및 애엽을 세척한 후, 분쇄하여 준비하는 단계; 준비된 박하, 어성초, 고삼, 치자 및 애엽을 1:1:1:1:1의 중량비율로 혼합하여 혼합물을 제조하는 단계; 상기 혼합물 90-110 중량부 및 에탄올과 아세톤이 1:1의 부피비율로 혼합된 혼합용매 900-1100 중량부를 혼합한 후, 초음파공정으로 38-42℃의 온도에서 22-26시간 동안 추출액을 제조하는 단계; 및 상기 추출액을 감압농축 및 동결건조하는 단계;를 포함하는 항균제를 제조하는 단계;
동충하초, 솔풍령, 해송, 삼나무, 삼백초, 백리향, 넓적떡다리버섯, 삼감황, 적운초 및 돌배나무를 세척한 후, 분쇄하여 준비하는 단계; 준비된 동충하초, 솔풍령, 해송, 삼나무, 삼백초, 백리향, 넓적떡다리버섯, 삼감황, 적운초 및 돌배나무를 1:1:1:1:1:1:1:1:1:1의 중량비율로 혼합하여 혼합물을 제조하는 단계; 및 상기 혼합물 90-110 중량부 및 증류수 900-1100 중량부를 혼합한 후 증기증류법으로 추출하는 단계;를 포함하는 기능성 추출물을 제조하는 단계; 및
토르말린 분말 13-17 중량부, 일라이트 분말 13-17 중량부, 각섬석 분말 13-17 중량부, 흑운모 분말 13-17 중량부, 상기 아크릴레이트계 고분자 바인더 28-32 중량부, 상기 탄소섬유 분산액 2-6 중량부, 상기 항균제 0.5-3 중량부, 상기 기능성 추출물 0.5-3 중량부 및 칼슘 31-35 중량부, 마그네슘 18-22 중량부, 칼륨 14-18 중량부, 규소 14-18 중량부, 티타늄 8-12 중량부, 탄소 0.5-2 중량부, 붕소 0.1-1 중량부, 셀레늄 0.05-0.5 중량부, 인 0.05-0.5 중량부 및 황 0.05-0.5 중량부를 포함하는 미네랄원료 1-5 중량부를 혼합하는 단계;를 포함하는 건축 자재용 조성물의 제조방법을 제공한다.
이때, 도 1에 본 발명에 따른 건축 자재용 조성물의 제조방법을 순서도로 나타내었으며, 이하, 도 1을 참조하여 본 발명에 따른 건축 자재용 조성물의 제조방법을 각 단계별로 상세히 설명한다.
먼저, 본 발명에 따른 건축 자재용 조성물의 제조방법은 고분자 바인더를 제조하는 단계를 포함한다. 상기 고분자 바인더를 제조하는 단계는, 메틸메타크릴레이트 단량체, 에틸헥실아크릴레이트 단량체, 아크릴산 단량체 및 글리시딜메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제1 아크릴레이트계 공중합체를 제조하는 단계; 에틸메타크릴레이트 단량체, n-부틸메타크릴레이트 단량체, 글리시딜메타크릴레이트 단량체 및 하이드록시에틸 메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제2 아크릴레이트계 공중합체를 제조하는 단계; 및 상기 제1 아크릴레이트계 공중합체와 상기 제2 아크릴레이트계 공중합체를 78-82:18-22의 중량비율로 혼합하는 단계;를 포함한다.
먼저, 메틸메타크릴레이트 단량체, 에틸헥실아크릴레이트 단량체, 아크릴산 단량체 및 글리시딜메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제1 아크릴레이트계 공중합체를 제조한다. 상기 온도는 87-89℃인 것이 더욱 바람직하다.
다음, 에틸메타크릴레이트 단량체, n-부틸메타크릴레이트 단량체, 글리시딜메타크릴레이트 단량체 및 하이드록시에틸 메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제2 아크릴레이트계 공중합체를 제조한다. 상기 온도는 87-89℃인 것이 더욱 바람직하다.
다음, 상기 제1 아크릴레이트계 공중합체와 상기 제2 아크릴레이트계 공중합체를 78-82:18-22의 중량비율로 혼합한다. 상기 혼합은 79-81:19-21의 중량비율로 수행하는 것이 더욱 바람직하다.
다음으로, 본 발명에 따른 건축 자재용 조성물의 제조방법은 탄소섬유 분산액을 제조하는 단계를 포함한다. 상기 탄소섬유 분산액을 제조하는 단계는, 토르말린 분말, 일라이트 분말, 각섬석 분말 및 흑운모 분말을 1:1:1:1의 중량비율로 혼합한 혼합분말을 준비하는 단계; 상기 혼합분말 18-22 중량부 및 증류수 78-82 중량부를 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 84-88℃의 온도로 가열하여 추출하는 단계; 추출 후, 혼합물을 여과하여 추출액을 제조하는 단계; 및 탄소섬유 33-37 중량부 및 상기 추출액 63-67 중량부를 혼합하고 초음파조사하는 단계;를 포함한다.
먼저, 토르말린 분말, 일라이트 분말, 각섬석 분말 및 흑운모 분말을 1:1:1:1의 중량비율로 혼합한 혼합분말을 준비한다.
다음, 상기 혼합분말 18-22 중량부 및 증류수 78-82 중량부를 혼합하여 혼합물을 제조한다. 상기 혼합은 상기 혼합분말 19-21 중량부 및 증류수 79-81 중량부를 사용하여 수행하는 것이 더욱 바람직하다.
다음, 상기 혼합물을 84-88℃의 온도로 가열하여 추출한다. 상기 가열은 85-87℃의 온도로 수행하는 것이 더욱 바람직하다.
다음, 추출 후, 혼합물을 여과하여 추출액을 제조한다. 상기 혼합물을 여과함으로써 광석분말을 제거하고 추출액만을 사용한다. 상기 여과하여 제거되는 광석분말은 후단에서 건축 자재용 조성물 제조시 사용하는 것이 바람직하다.
다음, 탄소섬유 33-37 중량부 및 상기 추출액 63-67 중량부를 혼합하고 초음파조사하여 탄소섬유 분산액을 제조한다. 상기 혼합은 탄소섬유 34-36 중량부 및 상기 추출액 64-66 중량부를 사용하여 수행하는 것이 더욱 바람직하다.
다음으로, 본 발명에 따른 건축 자재용 조성물의 제조방법은 항균제를 제조하는 단계를 포함한다. 상기 항균제를 제조하는 단계는, 박하, 어성초, 고삼, 치자 및 애엽을 세척한 후, 분쇄하여 준비하는 단계; 준비된 박하, 어성초, 고삼, 치자 및 애엽을 1:1:1:1:1의 중량비율로 혼합하여 혼합물을 제조하는 단계; 상기 혼합물 90-110 중량부 및 에탄올과 아세톤이 1:1의 부피비율로 혼합된 혼합용매 900-1100 중량부를 혼합한 후, 초음파공정으로 38-42℃의 온도에서 22-26시간 동안 추출액을 제조하는 단계; 및 상기 추출액을 감압농축 및 동결건조하는 단계;를 포함한다.
먼저, 박하, 어성초, 고삼, 치자 및 애엽을 세척한 후, 분쇄하여 준비한다.
다음, 준비된 박하, 어성초, 고삼, 치자 및 애엽을 1:1:1:1:1의 중량비율로 혼합하여 혼합물을 제조한다.
다음, 상기 혼합물 90-110 중량부 및 에탄올과 아세톤이 1:1의 부피비율로 혼합된 혼합용매 900-1100 중량부를 혼합한 후, 초음파공정으로 38-42℃의 온도에서 22-26시간 동안 추출액을 제조한다. 상기 혼합은 상기 혼합물 95-105 중량부 및 에탄올과 아세톤이 1:1의 부피비율로 혼합된 혼합용매 950-1050 중량부를 사용하여 수행하는 것이 더욱 바람직하고, 상기 초음파공정은 39-41℃의 온도에서 23-25시간 동안 수행하는 것이 더욱 바람직하다.
다음, 상기 추출액을 감압농축 및 동결건조하여 추출분말을 제조하며, 이를 항균제로 사용한다.
다음으로, 본 발명에 따른 건축 자재용 조성물의 제조방법은 기능성 추출물을 제조하는 단계를 포함한다. 상기 기능성 추출물을 제조하는 단계는, 동충하초, 솔풍령, 해송, 삼나무, 삼백초, 백리향, 넓적떡다리버섯, 삼감황, 적운초 및 돌배나무를 세척한 후, 분쇄하여 준비하는 단계; 준비된 동충하초, 솔풍령, 해송, 삼나무, 삼백초, 백리향, 넙적다리버섯, 삼감황, 적운초 및 돌배나무를 1:1:1:1:1:1:1:1:1:1의 중량비율로 혼합하여 혼합물을 제조하는 단계; 및 상기 혼합물 90-110 중량부 및 증류수 900-1100 중량부를 혼합한 후 증기증류법으로 추출하는 단계;를 포함한다.
먼저, 동충하초, 솔풍령, 해송, 삼나무, 삼백초, 백리향, 넓적떡다리버섯, 삼감황, 적운초 및 돌배나무를 세척한 후, 분쇄하여 준비한다.
다음, 준비된 동충하초, 솔풍령, 해송, 삼나무, 삼백초, 백리향, 넙적다리버섯, 삼감황, 적운초 및 돌배나무를 1:1:1:1:1:1:1:1:1:1의 중량비율로 혼합하여 혼합물을 제조한다.
다음, 상기 혼합물 90-110 중량부 및 증류수 900-1100 중량부를 혼합한 후 증기증류법으로 추출한다. 상기 증기증류법은 일반적으로 추출액을 제조하기 위해 사용하는 방법을 사용할 수 있다.
다음으로, 본 발명에 따른 건축 자재용 조성물의 제조방법은 토르말린 분말 13-17 중량부, 일라이트 분말 13-17 중량부, 각섬석 분말 13-17 중량부, 흑운모 분말 13-17 중량부, 상기 아크릴레이트계 고분자 바인더 28-32 중량부, 상기 탄소섬유 분산액 2-6 중량부, 상기 항균제 0.5-3 중량부, 상기 기능성 추출물 0.5-3 중량부 및 칼슘 31-35 중량부, 마그네슘 18-22 중량부, 칼륨 14-18 중량부, 규소 14-18 중량부, 티타늄 8-12 중량부, 탄소 0.5-2 중량부, 붕소 0.1-1 중량부, 셀레늄 0.05-0.5 중량부, 인 0.05-0.5 중량부 및 황 0.05-0.5 중량부를 포함하는 미네랄원료 1-5 중량부를 혼합하는 단계를 포함한다.
상기 혼합은 토르말린 분말 14-16 중량부, 일라이트 분말 14-16 중량부, 각섬석 분말 14-16 중량부, 흑운모 분말 14-16 중량부, 아크릴레이트계 고분자 바인더 29-31 중량부, 탄소섬유 분산액 3-5 중량부, 항균제 1-2 중량부, 기능성 추출물 1-2 중량부 및 칼슘 32-34 중량부, 마그네슘 19-21 중량부, 칼륨 15-17 중량부, 규소 15-17 중량부, 티타늄 9-11 중량부, 탄소 1.2-1.8 중량부, 붕소 0.4-0.8 중량부, 셀레늄 0.2-0.4 중량부, 인 0.2-0.4 중량부 및 황 0.2-0.4 중량부를 포함하는 미네랄원료 2-4 중량부를 사용하여 수행하는 것이 더욱 바람직하다.
상기 토르말린 분말, 일라이트 분말, 각섬석 분말 및 흑운모 분말은 탄소섬유 분산액을 제조할 때 사용된 원료를 사용할 수 있다.
이하, 본 발명을 하기의 실시예에 의해 보다 상세하게 설명한다.
단, 하기 실시예는 본 발명의 내용을 예시하는 것일 뿐 발명의 범위가 실시예 및 실험예에 의해 한정되는 것은 아니다.
<제조예 1> 아크릴레이트계 고분자 바인더의 제조
4구 플라스크에 메틸메타크릴레이트 및 에틸헥실아크릴레이트를 투입하고 교반하면서 아크릴산과 글리시딜메타크릴레이트를 순차적으로 투입하고, 촉매로 아조비스이소부티로니트릴(AIBN) 2 g을 적하 투입하여 88℃까지 승온시켰다. 온도가 일정하게 되었을 때 90분 동안 유지시켰다. 반응이 종결된 후 투명한 액체 상태의 제1 아크릴레이트계 공중합체를 수득하였다.
다른 4구 플라스크에 에틸메타크릴레이트 및 n-부틸메타크릴레이트를 투입하고 교반하면서 글리시딜메타크릴레이트과 하이드록시에틸 메타크릴레이트를 순차적으로 투입하고, 촉매로 아조비스이소부티로니트릴(AIBN) 2 g을 적하 투입하여 88℃까지 승온시켰다. 온도가 일정하게 되었을 때 90분 동안 유지시켰다. 반응이 종결된 후 투명한 액체 상태의 제2 아크릴레이트계 공중합체를 수득하였다.
상기 제1 아크릴레이트계 공중합체와 상기 제2 아크릴레이트계 공중합체를 80:20의 중량비율로 혼합하여 아크릴레이트계 고분자 바인더를 제조하였다.
<제조예 2> 탄소섬유 분산액 의 제조
토르말린 분말, 일라이트 분말, 각섬석 분말 및 흑운모 분말을 1:1:1:1의 중량비율로 혼합한 혼합분말을 준비하였다. 상기 혼합분말 20 중량부 및 증류수 80 중량부를 혼합하고, 혼합물을 86℃의 온도로 가열하여 12시간 동안 추출하였다. 추출 후, 혼합물을 여과하여 각 광석분말을 제거함으로써 추출액을 제조하였다.
상기 추출액 65 중량부 및 탄소섬유 35 중량부를 혼합하고 초음파조사하여 탄소섬유 분산액을 제조하였다.
<제조예 3> 항균제의 제조
박하, 어성초, 고삼, 치자 및 애엽을 세척한 후, 분쇄하여 분말 상태로 준비한 후, 준비된 박하, 어성초, 고삼, 치자 및 애엽을 1:1:1:1:1의 중량비율로 혼합하여 혼합물을 제조하였다. 에탄올과 아세톤을 1:1의 부피비율로 혼합한 혼합용매 1000 중량부에 제조된 혼합물 100 중량부를 혼합하고, 초음파공정(ultra sonic)을 수행하여 40℃의 온도에서 24시간 동안 추출한 후, 여과지(Watman No. 2)로 여과한 뒤 농축기(EYELA N-3000, Japan)로 55℃에서 감압농축 및 동결건조하여 항균제를 제조하였다.
<제조예 4> 기능성 추출물의 제조
동충하초, 솔풍령, 해송, 삼나무, 삼백초, 백리향, 넓적떡다리버섯, 삼감황, 적운초 및 돌배나무를 준비하여 세척한 후, 분쇄하고, 동충하초, 솔풍령, 해송, 삼나무, 삼백초, 백리향, 넙적다리버섯, 삼감황, 적운초 및 돌배나무를 1:1:1:1:1:1:1:1:1:1의 중량비율로 혼합한 혼합물을 준비하였다. 준비된 혼합물 100 중량부에 증류수 1000 중량부를 혼합하여 증기증류법으로 정유를 추출하였다. 온도를 승온시켜 100℃의 온도에서 24시간 동안 휘발 성분들을 포집하였다. 발생한 휘발 성분들은 응축액 형태로 포집되도록 한 후, 응축액은 에틸아세테이트를 100 ml씩 첨가하여 3회 추출하고 회전식 증발기를 통해 농축시켜 기능성 추출물을 제조하였다.
<실시예 1> 건축 자재용 조성물의 제조
토르말린 분말 15 중량부, 일라이트 분말 15 중량부, 각섬석 분말 15 중량부, 흑운모 분말 15 중량부, 상기 제조예 1에서 제조된 아크릴레이트계 고분자 바인더 30 중량부, 상기 제조예 2에서 제조된 탄소섬유 분산액 4 중량부, 상기 제조예 3에서 제조된 항균제 1.5 중량부, 상기 제조예 4에서 제조된 기능성 추출물 1.5 중량부 및 미네랄원료 3 중량부를 혼합하여 건축 자재용 조성물을 제조하였다.
상기 미네랄원료는 성분이 칼슘 33.33 중량부, 마그네슘 20 중량부, 칼륨 16.67 중량부, 규소 16.67 중량부, 티타늄 10 중량부, 탄소 1.67 중량부, 붕소 0.67 중량부, 셀렌 0.33 중량부, 인 0.33 중량부 및 황 0.33 중량부를 포함한다.
<실험예 1>
1. 원적외선 방사기능 분석
상기 실시예 1에서 제조된 건축 자재용 조성물의 원적외선 방사기능을 확인하기 위하여 한국건자재시험연구원에 의뢰하여 시험하였다. 시험성적은 하기 표 1에 나타내었다. 구체적으로, 한국건자재시험연구원의 원적외선응용평가센터에서 수행한 것이고, 본 시험은 40℃의 온도에서 시험하였으며, FT-IR Spectrometer를 이용한 흑체(Black Body)대비 측정한 결과이다.
| 방사율 (5-20 ㎛) | 방사에너지 (W/m2) | |
| 실시예 1 | 0.957 | 5.72×102 |
또한, 원적외선 방사기능의 지속력을 확인하기 위하여, 상기 실시예 1에서 제조된 건축 자재용 조성물을 0-7일 동안 분석하였으며, 그 결과를 하기 표 2에 나타내었다.
| 시간경과 | 방사율 (5-20 ㎛) | 방사에너지 (W/m2) |
| 0일 | 0.957 | 5.72×102 |
| 1일 | 0.955 | 5.70×102 |
| 2일 | 0.948 | 5.70×102 |
| 3일 | 0.950 | 5.68×102 |
| 4일 | 0.949 | 5.66×102 |
| 5일 | 0.950 | 5.66×102 |
| 6일 | 0.948 | 5.65×102 |
| 7일 | 0.948 | 5.65×102 |
상기 표 1에 나타낸 바와 같이, 우수한 원적외선 방사기능을 나타냄을 확인하였다. 또한, 상기 표 2에 나타낸 바와 같이 그 지속력이 우수함을 확인하였다.
2. 항균기능 분석
상기 실시예 1에서 제조된 건축 자재용 조성물의 항균기능을 확인하기 위하여 한국건자재시험연구원에 의뢰하여 시험하였다. 시험성적은 하기 표 3에 나타내었다. 구체적으로, 한국건자재시험연구원의 원적외선응용평가센터에서 수행한 것이고, 본 시험에서 블랭크(Blank)는 시료를 넣지 않은 상태에서 측정한 것이고, CFU는 콜로니형성단위(colony forming unit)를 의미하며, 40p는 0.04ml를 말하며, 사용한 균주는 Escherichia coli ATCC 25922이다. 또한, 항균능의 지속력을 확인하기 위하여, 상기 실시예 1에서 제조된 건축 자재용 조성물을 0-5일 동안 방치한 후 동일한 분석을 수행하였다.
| 시험항목 | 시간경과 | 시료구분 | 초기농도 (CFU/40p) |
24시간후 농도 (CFU/40p) |
세균감소율 (%) |
| 대장균에 의한 항균시험 | 0일 | 블랭크 | 385 | 385 | - |
| 0일 | 실시예 1 | 385 | 4 | 98.9 | |
| 1일 | 실시예 1 | 385 | 4 | 98.9 | |
| 2일 | 실시예 1 | 385 | 5 | 98.7 | |
| 3일 | 실시예 1 | 385 | 4 | 98.9 | |
| 4일 | 실시예 1 | 385 | 5 | 98.7 | |
| 5일 | 실시예 1 | 385 | 5 | 98.7 |
상기 표 3에 나타낸 바와 같이, 우수한 항균기능을 나타내며 그 유지력이 뛰어난 것을 확인하였다.
Claims (3)
- 미네랄원료를 포함하는 건축 자재용 조성물로,
상기 건축 자재용 조성물은 토르말린 분말 13-17 중량부, 일라이트 분말 13-17 중량부, 각섬석 분말 13-17 중량부, 흑운모 분말 13-17 중량부, 아크릴레이트계 고분자 바인더 28-32 중량부, 탄소섬유 분산액 2-6 중량부, 항균제 0.5-3 중량부, 기능성 추출물 0.5-3 중량부 및 미네랄원료 1-5 중량부를 포함하고,
상기 아크릴레이트계 고분자 바인더는 메틸메타크릴레이트 단량체 단위 23-27 중량%, 에틸헥실아크릴레이트 단량체 단위 23-27 중량%, 아크릴산 단량체 단위 23-27 중량% 및 글리시딜메타크릴레이트 단량체 단위 23-27 중량%인 제1 아크릴레이트계 공중합체 및 에틸메타크릴레이트 단량체 단위 23-27 중량%, n-부틸메타크릴레이트 단량체 단위 23-27 중량%, 글리시딜메타크릴레이트 단량체 단위 23-27 중량% 및 하이드록시에틸 메타크릴레이트 단량체 단위 23-27 중량%인 제2 아크릴레이트계 공중합체의 78-82:18-22의 중량비율로 혼합된 혼합물로 이루어지고,
상기 탄소섬유 분산액은 탄소섬유 33-37 중량부 및 토르말린 추출물, 일라이트 추출물, 각섬석 추출물 및 흑운모 추출물을 포함하는 증류수 63-67 중량부를 포함하고,
상기 항균제는 박하 추출물, 어성초 추출물, 고삼 추출물, 치자 추출물 및 애엽 추출물을 1:1:1:1:1의 중량비율로 혼합한 혼합물이고,
상기 기능성 추출물은 동충하초, 솔풍령, 해송, 삼나무, 삼백초, 백리향, 넓적떡다리버섯, 삼감황, 적운초, 육두구 및 돌배나무를 포함하는 혼합물을 추출한 것이고,
상기 미네랄원료는 칼슘 31-35 중량부, 마그네슘 18-22 중량부, 칼륨 14-18 중량부, 규소 14-18 중량부, 티타늄 8-12 중량부, 탄소 0.5-2 중량부, 붕소 0.1-1 중량부, 셀레늄 0.05-0.5 중량부, 인 0.05-0.5 중량부 및 황 0.05-0.5 중량부를 포함하는 것을 특징으로 하는 건축 자재용 조성물. - 삭제
- 메틸메타크릴레이트 단량체, 에틸헥실아크릴레이트 단량체, 아크릴산 단량체 및 글리시딜메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제1 아크릴레이트계 공중합체를 제조하는 단계; 에틸메타크릴레이트 단량체, n-부틸메타크릴레이트 단량체, 글리시딜메타크릴레이트 단량체 및 하이드록시에틸 메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제2 아크릴레이트계 공중합체를 제조하는 단계; 및 상기 제1 아크릴레이트계 공중합체와 상기 제2 아크릴레이트계 공중합체를 78-82:18-22의 중량비율로 혼합하는 단계;를 포함하는 아크릴레이트계 고분자 바인더를 제조하는 단계;
토르말린 분말, 일라이트 분말, 각섬석 분말 및 흑운모 분말을 1:1:1:1의 중량비율로 혼합한 혼합분말을 준비하는 단계; 상기 혼합분말 18-22 중량부 및 증류수 78-82 중량부를 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 84-88℃의 온도로 가열하여 추출하는 단계; 추출 후, 혼합물을 여과하여 추출액을 제조하는 단계; 및 탄소섬유 33-37 중량부 및 상기 추출액 63-67 중량부를 혼합하고 초음파조사하는 단계;를 포함하는 탄소섬유 분산액을 제조하는 단계;
박하, 어성초, 고삼, 치자 및 애엽을 세척한 후, 분쇄하여 준비하는 단계; 준비된 박하, 어성초, 고삼, 치자 및 애엽을 1:1:1:1:1의 중량비율로 혼합하여 혼합물을 제조하는 단계; 상기 혼합물 90-110 중량부 및 에탄올과 아세톤이 1:1의 부피비율로 혼합된 혼합용매 900-1100 중량부를 혼합한 후, 초음파공정으로 38-42℃의 온도에서 22-26시간 동안 추출액을 제조하는 단계; 및 상기 추출액을 감압농축 및 동결건조하는 단계;를 포함하는 항균제를 제조하는 단계;
동충하초, 솔풍령, 해송, 삼나무, 삼백초, 백리향, 넓적떡다리버섯, 삼감황, 적운초 및 돌배나무를 세척한 후, 분쇄하여 준비하는 단계; 준비된 동충하초, 솔풍령, 해송, 삼나무, 삼백초, 백리향, 넙적다리버섯, 삼감황, 적운초 및 돌배나무를 1:1:1:1:1:1:1:1:1:1의 중량비율로 혼합하여 혼합물을 제조하는 단계; 및 상기 혼합물 90-110 중량부 및 증류수 900-1100 중량부를 혼합한 후 증기증류법으로 추출하는 단계;를 포함하는 기능성 추출물을 제조하는 단계; 및
토르말린 분말 13-17 중량부, 일라이트 분말 13-17 중량부, 각섬석 분말 13-17 중량부, 흑운모 분말 13-17 중량부, 상기 아크릴레이트계 고분자 바인더 28-32 중량부, 상기 탄소섬유 분산액 2-6 중량부, 상기 항균제 0.5-3 중량부, 상기 기능성 추출물 0.5-3 중량부 및 칼슘 31-35 중량부, 마그네슘 18-22 중량부, 칼륨 14-18 중량부, 규소 14-18 중량부, 티타늄 8-12 중량부, 탄소 0.5-2 중량부, 붕소 0.1-1 중량부, 셀레늄 0.05-0.5 중량부, 인 0.05-0.5 중량부 및 황 0.05-0.5 중량부를 포함하는 미네랄원료 1-5 중량부를 혼합하는 단계;를 포함하는 건축 자재용 조성물의 제조방법.