KR102446360B1 - Semiconductor resist composition, and method of forming patterns using the composition - Google Patents

Abstract

(화학식 1에 대한 구체적인 내용은 명세서 상에서 정의된 것과 같다.)It relates to a composition for a semiconductor photoresist comprising an organometallic compound represented by the following Chemical Formula 1 and a solvent, and a pattern forming method using the same.
[Formula 1]

(Specific details of Formula 1 are the same as defined in the specification.)

Description

A composition for a semiconductor photoresist and a pattern forming method using the same

The present disclosure relates to a composition for a semiconductor photoresist and a pattern forming method using the same.

EUV (extreme ultraviolet light) lithography is attracting attention as one of the elemental technologies for manufacturing next-generation semiconductor devices. EUV lithography is a pattern forming technique using EUV light having a wavelength of 13.5 nm as an exposure light source. According to EUV lithography, it is demonstrated that an extremely fine pattern (for example, 20 nm or less) can be formed in the exposure process of a semiconductor device manufacturing process.

Implementation of extreme ultraviolet (EUV) lithography requires the development of compatible photoresists that can perform at sub- 16 nm spatial resolutions. Currently, traditional chemically amplified (CA) photoresists provide resolution, photospeed, and feature roughness (also called line edge roughness or LER) for next-generation devices. efforts are being made to meet the specifications for

The intrinsic image blur due to acid catalyzed reactions taking place in these polymeric photoresists limits resolution at small feature sizes, which e-beam This is a fact that has long been known in lithography. Chemically amplified (CA) photoresists are designed for high sensitivity, but because their typical elemental makeup lowers the absorbance of photoresists at a wavelength of 13.5 nm, which in turn reduces their sensitivity, may suffer more under EUV exposure.

CA photoresists may also suffer from roughness issues at small feature sizes, and due in part to the nature of acid catalyzed processes, line edge roughness (LER) as photospeed decreases. has been shown to increase experimentally. Due to the drawbacks and problems of CA photoresists, there is a need in the semiconductor industry for new types of high performance photoresists.

In order to overcome the disadvantages of the above-described chemically amplified (CA) photosensitive composition, an inorganic photosensitive composition has been studied. In the case of an inorganic photosensitive composition, it is mainly used for negative tone patterning that is resistant to removal by a developer composition due to chemical modification by a non-chemical amplification mechanism. In the case of an inorganic composition, it contains inorganic elements with higher EUV absorption than hydrocarbons, so sensitivity can be secured even with a non-chemical amplification mechanism, and it is less sensitive to the stochastic effect, so it is known that the roughness of the line edge and the number of defects are small. .

Recently, a cationic hafnium metal oxide sulfate (HfSOx) material was used with a peroxo complexing agent to image 15 nm half-pitch (HP) by projection EUV exposure. , showed impressive performance in this case. However, in the case of a metal oxide-based inorganic resist having a peroxo complexing agent, it is difficult to handle using a corrosive strong acid, storage stability is not good, and it is difficult to change the structure to improve performance.

One embodiment provides a composition for a semiconductor photoresist excellent in storage stability and pattern formation.

Another embodiment provides a pattern forming method using the composition for a semiconductor photoresist.

The composition for a semiconductor photoresist according to an embodiment includes an organometallic compound represented by the following Chemical Formula 1 and a solvent.

[Formula 1]

In Formula 1,

R ¹ is a substituted or unsubstituted C1 to C20 alkyl group, a substituted or unsubstituted C3 to C20 cycloalkyl group, or a substituted or unsubstituted C6 to C20 aryl group, or a combination thereof;

X ¹ To X ³ are each independently a single bond, a substituted or unsubstituted divalent C1 to C20 saturated aliphatic hydrocarbon group, a substituted or unsubstituted divalent C3 to C20 saturated alicyclic hydrocarbon group, one or more double bonds or triple bonds A substituted or unsubstituted divalent C2 to C20 unsaturated aliphatic hydrocarbon group comprising a, a divalent substituted or unsubstituted C6 to C20 aromatic hydrocarbon group, or a combination thereof,

Y ¹ is C(-R ^a ) or nitrogen (N),

R ^a is hydrogen, a hydroxy group (-OH), or -OR ^b ;

R ^b is a substituted or unsubstituted monovalent C1 to C20 saturated aliphatic hydrocarbon group, a substituted or unsubstituted monovalent C3 to C20 saturated alicyclic hydrocarbon group, a substituted or unsubstituted 1 containing one or more double or triple bonds a valent C2 to C20 unsaturated aliphatic hydrocarbon group, a monovalent substituted or unsubstituted C6 to C30 aromatic hydrocarbon group, or a combination thereof.

R ¹ may be a substituted or unsubstituted C1 to C10 alkyl group, a substituted or unsubstituted C3 to C10 cycloalkyl group, or a substituted or unsubstituted C6 to C10 aryl group, or a combination thereof,

wherein X ¹ to X ³ are each independently a single bond, a substituted or unsubstituted divalent C1 to C8 saturated aliphatic hydrocarbon group, a substituted or unsubstituted divalent C3 to C6 saturated alicyclic hydrocarbon group, 1 or 2 double bonds Or it may be a substituted or unsubstituted divalent C2 to C8 unsaturated aliphatic hydrocarbon group containing a triple bond, a divalent substituted or unsubstituted C6 to C10 arylene group, or a combination thereof,

Wherein R ^b is a substituted or unsubstituted monovalent C1 to C10 saturated aliphatic hydrocarbon group, a substituted or unsubstituted monovalent C3 to C10 saturated alicyclic hydrocarbon group, a substituted or unsubstituted group containing 1 or 2 double or triple bonds It may be a cyclic monovalent C2 to C10 unsaturated aliphatic hydrocarbon group, a monovalent substituted or unsubstituted C6 to C10 aromatic hydrocarbon group, or a combination thereof.

Wherein R ¹ is a methyl group, an ethyl group, a propyl group, a butyl group, an isopropyl group, a tert-butyl group, a 2,2-dimethylpropyl group, a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, a phenyl group, a tall It may be a ryl group, a xylene group, a benzyl group, or a combination thereof,

wherein X ¹ to X ³ are each independently a single bond, a methylene group, an ethylene group, a propylene group, a butylene group, a cyclobutylene group, a cyclopentylene group, a cyclohexylene group, an ethenylene group, a propenylene group, an ethynylene group, It may be a propynylene group, a phenylene group, or a combination thereof,

R ^b is a methyl group, an ethyl group, a propyl group, a butyl group, an isopropyl group, a tert-butyl group, a 2,2-dimethylpropyl group, a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, an ethenyl group, It may be a propenyl group, a butenyl group, an ethynyl group, a propynyl group, a butynyl group, a phenyl group, a tolyl group, a xylene group, a benzyl group, or a combination thereof.

R ¹ may be any one of a methyl group, an ethyl group, a propyl group, an isopropyl group, a tert-butyl group, a phenyl group, and a benzyl group,

The X ¹ to X ³ may each independently be any one of a single bond, a methylene group, an ethylene group, a propylene group, and a butylene group,

The Y ¹ may be C(-R ^a ),

The R ^a may be hydrogen.

Wherein X ¹ is a methylene group,

Wherein X ² is a single bond,

X ³ may be any one of a single bond, a methylene group, an ethylene group, a propylene group, and a butylene group.

All of X ¹ to X ³ may be the same.

The composition for a semiconductor photoresist may include 1 to 20% by weight of the organometallic compound represented by Chemical Formula 1, based on the total weight of the composition.

The composition for a semiconductor photoresist may further include an additive of a surfactant, a crosslinking agent, a leveling agent, or a combination thereof.

A pattern forming method according to another embodiment includes forming an etch target layer on a substrate;

forming a photoresist layer by applying the composition for a semiconductor photoresist according to any one of claims 1 to 11 on the etch target layer;

forming a photoresist pattern by patterning the photoresist layer; and

and etching the etch target layer using the photoresist pattern as an etch mask.

In the forming of the photoresist pattern, light having a wavelength of 5 nm to 150 nm may be used.

The method may further include providing a resist underlayer film formed between the substrate and the photoresist film.

The photoresist pattern may have a width of 5 nm to 100 nm.

The composition for a semiconductor photoresist according to an exemplary embodiment has excellent storage stability and pattern formation characteristics, and using it, it is possible to provide a photoresist pattern in which the pattern does not collapse even though it has a high aspect ratio.

1 to 5 are cross-sectional views for explaining a pattern forming method using a composition for a semiconductor photoresist according to an exemplary embodiment.

Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. However, in describing the present description, descriptions of already known functions or configurations will be omitted in order to clarify the gist of the present description.

In order to clearly explain the present description, parts irrelevant to the description are omitted, and the same reference numerals are given to the same or similar elements throughout the specification. In addition, since the size and thickness of each component shown in the drawings are arbitrarily indicated for convenience of description, the present description is not necessarily limited to the illustrated bar.

In order to clearly express various layers and regions in the drawings, the thicknesses are enlarged. In addition, in the drawings, the thickness of some layers and regions is exaggerated for convenience of description. When a part, such as a layer, film, region, plate, etc., is "on" or "on" another part, it includes not only cases where it is "directly on" another part, but also cases where there is another part in between.

In the present description, "substitution" means that a hydrogen atom is deuterium, a halogen group, a hydroxyl group, a cyano group, a nitro group, -NRR' (wherein R and R' are each independently hydrogen, a substituted or unsubstituted C1 to C30 saturated or an unsaturated aliphatic hydrocarbon group, a substituted or unsubstituted C3 to C30 saturated or unsaturated alicyclic hydrocarbon group, or a substituted or unsubstituted C6 to C30 aromatic hydrocarbon group), -SiRR'R" (where R, R', and R" are each independently hydrogen, a substituted or unsubstituted C1 to C30 saturated or unsaturated aliphatic hydrocarbon group, a substituted or unsubstituted C3 to C30 saturated or unsaturated alicyclic hydrocarbon group, or a substituted or unsubstituted C6 to C30 aromatic hydrocarbon group), C1 to C30 alkyl group, C1 to C10 haloalkyl group, C1 to C10 alkylsilyl group, C3 to C30 cycloalkyl group, C6 to C30 aryl group, C1 to C20 alkoxy group, or a combination thereof means that "Unsubstituted" means that a hydrogen atom remains as a hydrogen atom without being substituted with another substituent.

As used herein, "hetero" means that, unless otherwise defined, one functional group contains 1 to 3 heteroatoms selected from the group consisting of N, O, S and P, and the remainder is carbon. .

As used herein, the term “alkyl group” refers to a straight-chain or branched-chain aliphatic hydrocarbon group, unless otherwise defined. The alkyl group may be a “saturated alkyl group” that does not contain any double or triple bonds.

The alkyl group may be a C1 to C20 alkyl group. For example, the alkyl group may be a C1 to C10 alkyl group, a C1 to C8 alkyl group, a C1 to C6 alkyl group, or a C1 to C4 alkyl group. For example, a C1 to C4 alkyl group may be a methyl, ethyl, propyl, isopropyl, n-butyl, isobutyl, sec-butyl, or tert-butyl group.

As used herein, the term "saturated aliphatic hydrocarbon group" refers to a hydrocarbon group in which the bond between carbon and carbon atoms in a molecule is a single bond, unless otherwise defined.

The saturated aliphatic hydrocarbon group may be a C1 to C20 saturated aliphatic hydrocarbon group. For example, the saturated aliphatic hydrocarbon group may be a C1 to C10 saturated aliphatic hydrocarbon group, a C1 to C8 saturated aliphatic hydrocarbon group, a C1 to C6 saturated aliphatic hydrocarbon group, a C1 to C4 saturated aliphatic hydrocarbon group, or a C1 to C2 saturated aliphatic hydrocarbon group. For example, the C1 to C6 saturated aliphatic hydrocarbon group may be a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a sec-butyl group, a 2,2-dimethylpropyl group, or a tert-butyl group. .

As used herein, the term "saturated alicyclic hydrocarbon group" refers to a hydrocarbon group including a ring in which the bond between carbon and carbon atoms in a molecule consists of a single bond.

The saturated alicyclic hydrocarbon group may be a C3 to C10 saturated alicyclic hydrocarbon group. For example, the saturated alicyclic hydrocarbon group may be a C3 to C8 saturated alicyclic hydrocarbon group, a C3 to C6 saturated alicyclic hydrocarbon group, a C3 to C5 saturated alicyclic hydrocarbon group, or a C3 or C4 saturated alicyclic hydrocarbon group. For example, the C3 to C6 saturated alicyclic hydrocarbon group may be a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, or a cyclohexyl group.

As used herein, the term "unsaturated aliphatic hydrocarbon group" refers to a hydrocarbon group including a bond in which the bond between carbon and a carbon atom in a molecule is a double bond, a triple bond, or a combination thereof.

The unsaturated aliphatic hydrocarbon group may be a C2 to C20 unsaturated aliphatic hydrocarbon group. For example, the unsaturated aliphatic hydrocarbon group may be a C2 to C10 unsaturated aliphatic hydrocarbon group, a C2 to C8 unsaturated aliphatic hydrocarbon group, a C2 to C6 unsaturated aliphatic hydrocarbon group, or a C2 to C4 unsaturated aliphatic hydrocarbon group. For example, the C2 to C4 unsaturated aliphatic hydrocarbon group is a vinyl group, an ethynyl group, an allyl group, a 1-propenyl group, a 2-propenyl group, a 1-propynyl group, a 2-propynyl group, a 1-butenyl group, and a 2-bute group. It may be a nyl group, a 3-butenyl group, a 1-butynyl group, a 2-butynyl group, or a 3-butynyl group.

As used herein, the term "unsaturated alicyclic hydrocarbon group" refers to a hydrocarbon group including a ring including a bond between carbon atoms that is a double bond or a triple bond.

The unsaturated alicyclic hydrocarbon group may be a C3 to C10 unsaturated alicyclic hydrocarbon group. For example, the unsaturated alicyclic hydrocarbon group may be a C3 to C8 unsaturated alicyclic hydrocarbon group, a C3 to C6 unsaturated alicyclic hydrocarbon group, a C3 to C5 unsaturated alicyclic hydrocarbon group, or a C3 or C4 unsaturated alicyclic hydrocarbon group. For example, the C3 to C6 unsaturated alicyclic hydrocarbon group is 1-cyclopropenyl group, 2-cyclopropenyl group, 1-cyclobutenyl group, 2-cyclobutenyl group, 1-cyclopentenyl group, 2-cyclopentenyl group, 3- It may be a cyclopentenyl group, a 1-cyclohexenyl group, a 2-cyclohexenyl group, or a 3-cyclohexenyl group.

As used herein, the term "aromatic hydrocarbon group" refers to a hydrocarbon group including an aromatic ring group in a molecule.

The aromatic hydrocarbon group may be a C6 to C10 aromatic hydrocarbon group. For example, the aromatic hydrocarbon group may be a phenyl group or a naphthalene group.

As used herein, the term "alkenyl group", unless otherwise defined, is a straight or branched aliphatic hydrocarbon group, and refers to an aliphatic unsaturated alkenyl group containing one or more double bonds. do.

As used herein, the term “cycloalkyl group” refers to a monovalent cyclic aliphatic saturated hydrocarbon group unless otherwise defined.

In the present description, "aryl group" means a substituent in which all elements of a cyclic substituent have p-orbitals, and these p-orbitals form a conjugate, monocyclic or fusion ring polycyclic (ie, rings that share adjacent pairs of carbon atoms) functional groups.

The composition for a semiconductor photoresist according to an embodiment of the present invention includes an organometallic compound and a solvent. The organometallic compound may be represented by the following formula (1).

[Formula 1]

In Formula 1,

R ¹ is a substituted or unsubstituted C1 to C20 alkyl group, a substituted or unsubstituted C3 to C20 cycloalkyl group, or a substituted or unsubstituted C6 to C20 aryl group, or a combination thereof;

X ¹ To X ³ are each independently a single bond, a substituted or unsubstituted divalent C1 to C20 saturated aliphatic hydrocarbon group, a substituted or unsubstituted divalent C3 to C20 saturated alicyclic hydrocarbon group, one or more double bonds or triple bonds A substituted or unsubstituted divalent C2 to C20 unsaturated aliphatic hydrocarbon group comprising a, a divalent substituted or unsubstituted C6 to C20 aromatic hydrocarbon group, or a combination thereof,

Y ¹ is C(-R ^a ) or nitrogen (N),

R ^a is hydrogen, a hydroxy group (-OH), or -OR ^b ;

R ^b is a substituted or unsubstituted monovalent C1 to C20 saturated aliphatic hydrocarbon group, a substituted or unsubstituted monovalent C3 to C20 saturated alicyclic hydrocarbon group, a substituted or unsubstituted 1 containing one or more double or triple bonds a valent C2 to C20 unsaturated aliphatic hydrocarbon group, a monovalent substituted or unsubstituted C6 to C30 aromatic hydrocarbon group, or a combination thereof.

The organometallic compound may include one homogeneous organometallic compound represented by Formula 1, or may include a mixture of two or more different organometallic compounds represented by Formula 1 above. Tin (Sn) included in the organometallic compound represented by Formula 1 may strongly absorb extreme ultraviolet light at 13.5 nm, and thus may have excellent sensitivity to light having high energy.

In the organometallic compound represented by Formula 1, three alkoxy groups and/or aryloxy groups are bonded to a tin (Sn) atom, and all of these alkoxy groups and/or aryloxy groups are connected to one Y ¹ to form a compound as a whole. It is characterized in that it forms a ring structure. That is, the compound is an organometallic compound into which a trivalent alkoxy and/or aryloxy ligand is introduced, and the trivalent alkoxy and/or aryloxy ligand is bonded to a tin metal, so that it may have excellent solubility in organic solvents.

In addition, as all three alkoxy groups and/or aryloxy groups are connected to Y ¹ to form a ring structure, the alkoxy group and/or aryloxy group can prevent moisture from penetrating into the ring, and as a result, the ring structure is Since tin (Sn) serves to prevent contact with moisture, the composition for semiconductor photoresists including the compound may have excellent moisture stability, that is, storage stability.

R ¹ may be a substituted or unsubstituted C1 to C10 alkyl group, a substituted or unsubstituted C3 to C10 cycloalkyl group, or a substituted or unsubstituted C6 to C10 aryl group, or a combination thereof, specifically, a methyl group , ethyl group, propyl group, butyl group, isopropyl group, tert-butyl group, 2,2-dimethylpropyl group, cyclopropyl group, cyclobutyl group, cyclopentyl group, cyclohexyl group, phenyl group, tolyl group, xylene group, It may be a benzyl group, or a combination thereof, and more specifically, may be any one of a methyl group, an ethyl group, a propyl group, an isopropyl group, a tert-butyl group, a phenyl group, and a benzyl group.

The R ¹ is combined with a tin (Sn) element to give the organometallic compound solubility in an organic solvent. In addition, the organotin polymer formed by polymerization of the organometallic compound represented by Formula 1 generates radicals as the R ¹ functional group is dissociated from the Sn-R ¹ bond when exposed to extreme ultraviolet light, The radicals thus generated form a -Sn-O-Sn- bond through an additional radical reaction to initiate a polycondensation reaction between organotin polymers, thereby forming a semiconductor photoresist from the composition according to an embodiment. Therefore, the composition for a semiconductor photoresist including the organotin compound including the R ¹ functional group may have better sensitivity to light than the composition for a semiconductor photoresist including the organotin compound not including the R ¹ functional group. have.

wherein X ¹ to X ³ are each independently a single bond, a substituted or unsubstituted divalent C1 to C8 saturated aliphatic hydrocarbon group, a substituted or unsubstituted divalent C3 to C6 saturated alicyclic hydrocarbon group, 1 or 2 double bonds or a substituted or unsubstituted divalent C2 to C8 unsaturated aliphatic hydrocarbon group including a triple bond, a divalent substituted or unsubstituted C6 to C10 arylene group, or a combination thereof, and specifically, each independently a single bond , methylene group, ethylene group, propylene group, butylene group, cyclobutylene group, cyclopentylene group, cyclohexylene group, ethenylene group, propenylene group, etynylene group, propynylene group, phenylene group, or a combination thereof may be, and more specifically, each independently may be any one of a single bond, a methylene group, an ethylene group, a propylene group, and a butylene group.

Wherein X ¹ to X ³ is a linking group that allows three alkoxy groups in a molecule to be connected to one Y ¹ , and according to the number of carbon atoms included in X ¹ to X ³ , the organometallic compound represented by Formula 1 The chain length in the ring structure can be determined. Therefore, as the number of carbons included in X ¹ to X ³ increases, the size of the molecule of the organometallic compound represented by Formula 1 becomes larger. In this case, when the number of carbons included in X ¹ to X ³ increases too much , for example, when it has more than 20 carbon atoms, the moisture blocking effect of the alkoxy group and carbon chain in the molecule of the organometallic compound represented by Formula 1 may decrease, and as a result, The moisture stability of the composition for semiconductor photoresists including the organometallic compound, that is, storage stability characteristics may be deteriorated. In addition, when the number of carbons included in X ¹ to X ³ increases and the volume of the organometallic compound represented by Chemical Formula 1 becomes excessively large, there is a risk that the characteristics of the line roughness (LER) in pattern formation may also be deteriorated.

In one embodiment, in the organometallic compound represented by Formula 1, X ¹ is a methylene group, X ² is a single bond, and X ³ is a single bond, a methylene group, an ethylene group, a propylene group, and a butylene group may be any one, and X ¹ to X ³ may be all the same.

In one embodiment, in the organometallic compound represented by Formula 1, X ¹ to X ³ may not all be single bonds. That is, in the organometallic compound represented by Formula 1, one or two of X ¹ to X ³ may be a single bond, and the rest may be one of the groups listed above rather than a single bond.

R ^b is a substituted or unsubstituted monovalent C1 to C10 saturated aliphatic hydrocarbon group, a substituted or unsubstituted monovalent C3 to C10 saturated alicyclic hydrocarbon group, a substituted or unsubstituted containing 1 or 2 double or triple bonds may be a monovalent C2 to C10 unsaturated aliphatic hydrocarbon group, a monovalent substituted or unsubstituted C6 to C10 aromatic hydrocarbon group, or a combination thereof, and specifically, a methyl group, an ethyl group, a propyl group, a butyl group, an isopropyl group, tert-butyl group, 2,2-dimethylpropyl group, cyclopropyl group, cyclobutyl group, cyclopentyl group, cyclohexyl group, ethenyl group, propenyl group, butenyl group, etynyl group, propynyl group, butynyl group, phenyl group, It may be a tolyl group, a xylene group, a benzyl group, or a combination thereof.

On the other hand, the organometallic compound may be represented by the following formula (2).

[Formula 2]

In Formula 2,

R ¹ is any one of a methyl group, an ethyl group, a propyl group, an isopropyl group, a tert-butyl group, a phenyl group, and a benzyl group,

X ³ is any one of a single bond, a methylene group, an ethylene group, a propylene group, and a butylene group.

Specifically, the organometallic compound according to an embodiment may be represented by any one of the following Chemical Formulas 3 to 8.

[Formula 3]

[Formula 4]

[Formula 5]

[Formula 6]

[Formula 7]

[Formula 8]

The composition for a semiconductor photoresist contains 1 to 20% by weight of the organometallic compound represented by Formula 1, for example, 1 to 19% by weight, for example, 1 to 18% by weight, based on the total weight of the composition. %, such as 1 to 17% by weight, such as 1 to 16% by weight, such as 1 to 15% by weight, such as 1 to 14% by weight, such as 1 to 13% by weight %, such as 1 to 12% by weight, such as 1 to 11% by weight, such as 1 to 10% by weight, such as 1 to 8% by weight, such as 1 to 6% by weight %, for example from 1 to 5% by weight, for example from 1 to 3% by weight. When the composition for a semiconductor photoresist contains the organometallic compound represented by Chemical Formula 1 in the above weight % range, moisture stability, that is, storage stability, of the composition for a semiconductor photoresist may be further improved.

The solvent included in the composition for a semiconductor photoresist according to an embodiment may be an organic solvent, for example, aromatic compounds (eg, xylene, toluene), alcohols (eg, 4-methyl-2- Pentanol, 4-methyl-2-propanol, 1-butanol, methanol, isopropyl alcohol, 1-propanol), ethers (eg, anisole, tetrahydrofuran), esters (n-butyl acetate, propylene) glycol monomethyl ether acetate, ethyl acetate, ethyl lactate), ketones (eg, methyl ethyl ketone, 2-heptanone), mixtures thereof, and the like.

In one embodiment, the semiconductor resist composition may further include a resin in addition to the organometallic compound and the solvent.

The resin may be a phenolic resin including at least one aromatic moiety listed in Group 1 below.

[Group 1]

The resin may have a weight average molecular weight of 500 to 20,000.

The resin may be included in an amount of 0.1 wt% to 50 wt% based on the total content of the composition for semiconductor resist.

When the resin is contained in the above content range, it may have excellent etch resistance and heat resistance.

On the other hand, the composition for a semiconductor resist according to an embodiment is preferably made of the aforementioned organometallic compound, a solvent, and a resin. However, the composition for a semiconductor resist according to the above-described embodiment may further include an additive in some cases. Examples of the additive include a surfactant, a crosslinking agent, a leveling agent, or a combination thereof.

The surfactant may be, for example, an alkylbenzenesulfonic acid salt, an alkylpyridinium salt, polyethylene glycol, a quaternary ammonium salt, or a combination thereof, but is not limited thereto.

The cross-linking agent may include, for example, a melamine-based cross-linking agent, a substituted urea-based cross-linking agent, or a polymer-based cross-linking agent, but is not limited thereto. Crosslinking agents having at least two crosslinking substituents, for example, methoxymethylated glycouryl, butoxymethylated glycouryl, methoxymethylated melamine, butoxymethylated melamine, methoxymethylated benzoguanamine, butoxymethylated benzoguanamine , methoxymethylated urea, butoxymethylated urea, or methoxymethylated thiourea may be used.

The leveling agent is for improving the coating flatness during printing, and a known leveling agent available in a commercial manner may be used.

The amount of these additives used may be easily adjusted according to desired physical properties or may be omitted.

In addition, the composition for semiconductor resist may further use a silane coupling agent as an additive to improve adhesion to the substrate (eg, to improve adhesion of the composition for semiconductor resist to the substrate), and as an adhesion promoter. The silane coupling agent is, for example, vinyltrimethoxysilane, vinyltriethoxysilane, vinyl trichlorosilane, vinyltris(β-methoxyethoxy)silane; or 3-methacryloxypropyltrimethoxysilane, 3-acryloxypropyltrimethoxysilane, p-styryl trimethoxysilane, 3-methacryloxypropylmethyldimethoxysilane, 3-methacryloxypropylmethyldi ethoxysilane; A silane compound containing a carbon-carbon unsaturated bond such as trimethoxy[3-(phenylamino)propyl]silane may be used, but the present invention is not limited thereto.

The composition for semiconductor resist does not cause pattern collapse even when a pattern having a high aspect ratio is formed, or the risk of pattern collapse can be greatly reduced. Thus, for example, a fine pattern having a width of 5 nm to 100 nm, for example a fine pattern having a width of 5 nm to 80 nm, for example, a fine pattern having a width of 5 nm to 70 nm, For example, a micropattern having a width of 5 nm to 50 nm, for example a micropattern having a width of 5 nm to 40 nm, for example, a micropattern having a width of 5 nm to 30 nm, for example For example, in order to form a fine pattern having a width of 5 nm to 20 nm, a photoresist process using light having a wavelength of 5 nm to 150 nm, for example, a photoresist using light having a wavelength of 5 nm to 100 nm process, eg a photoresist process using light with a wavelength of 5 nm to 80 nm, eg a photoresist process using light with a wavelength of 5 nm to 50 nm, eg, a wavelength between 5 nm and 30 nm It can be used in a photoresist process using light of, for example, a photoresist process using light having a wavelength of 5 nm to 20 nm. Therefore, using the composition for semiconductor resists according to the exemplary embodiment, extreme ultraviolet lithography using an EUV light source having a wavelength of about 13.5 nm may be implemented.

Meanwhile, according to another exemplary embodiment, a method of forming a pattern using the above-described composition for a semiconductor resist may be provided. For example, the manufactured pattern may be a photoresist pattern.

According to another exemplary embodiment, a method for forming a pattern includes forming an etch target film on a substrate, applying the above-described composition for semiconductor resist on the etch target film to form a photoresist film, patterning the photoresist film to form a photoresist pattern and etching the etch target layer using the photoresist pattern as an etch mask.

Hereinafter, a method of forming a pattern using the above-described composition for a semiconductor resist will be described with reference to FIGS. 1 to 5 . 1 to 5 are cross-sectional views for explaining a pattern forming method using a composition for a semiconductor resist according to the present invention.

Referring to FIG. 1 , an object to be etched is first prepared. An example of the object to be etched may be the thin film 102 formed on the semiconductor substrate 100 . Hereinafter, only the case where the object to be etched is the thin film 102 will be described. The surface of the thin film 102 is cleaned to remove contaminants and the like remaining on the thin film 102 . The thin film 102 may be, for example, a silicon nitride film, a polysilicon film, or a silicon oxide film.

Then, a composition for forming a resist underlayer film for forming the resist underlayer film 104 on the surface of the cleaned thin film 102 is coated by applying a spin coating method. However, one embodiment is not necessarily limited thereto, and various known coating methods, for example, spray coating, dip coating, knife edge coating, printing methods, such as inkjet printing and screen printing, may be used.

The resist underlayer coating process may be omitted. Hereinafter, a case of coating the resist underlayer film will be described.

Thereafter, drying and baking processes are performed to form the resist underlayer 104 on the thin film 102 . The baking treatment may be performed at about 100 °C to about 500 °C, for example, at about 100 °C to about 300 °C.

The resist underlayer film 104 is formed between the substrate 100 and the photoresist film 106, so that radiation reflected from the interface between the substrate 100 and the photoresist film 106 or from an interlayer hardmask is not intended. When the photoresist is scattered to the non-uniform photoresist region, it is possible to prevent the non-uniformity of the photoresist linewidth and prevent the pattern formation from being disturbed.

Referring to FIG. 2 , a photoresist film 106 is formed by coating the above-described composition for semiconductor resist on the resist underlayer 104 . The photoresist film 106 may be in a form in which the above-described semiconductor resist composition is coated on the thin film 102 formed on the substrate 100 and then cured through a heat treatment process.

More specifically, the step of forming the pattern using the composition for semiconductor resist is a process of applying the above-described composition for semiconductor resist on the substrate 100 on which the thin film 102 is formed by spin coating, slit coating, inkjet printing, etc. and drying the applied composition for semiconductor resist to form the photoresist film 106 .

Since the composition for a semiconductor resist has already been described in detail, a redundant description thereof will be omitted.

Next, a first baking process of heating the substrate 100 on which the photoresist film 106 is formed is performed. The first baking process may be performed at a temperature of about 80 °C to about 120 °C.

Referring to FIG. 3 , the photoresist layer 106 is selectively exposed.

For example, examples of the light that can be used in the exposure process include not only light having a short wavelength such as i-line (wavelength 365 nm), KrF excimer laser (wavelength 248 nm), ArF excimer laser (wavelength 193 nm), but also EUV ( Light having a high energy wavelength such as Extreme UltraViolet (wavelength 13.5 nm) and E-Beam (electron beam) may be mentioned.

More specifically, the light for exposure according to an embodiment may be short-wavelength light having a wavelength range of 5 nm to 150 nm, and light having a high energy wavelength such as EUV (Extreme Ultraviolet; wavelength 13.5 nm), E-Beam (electron beam), etc. can

The exposed region 106b of the photoresist film 106 has a solubility different from that of the unexposed region 106a of the photoresist film 106 as a polymer is formed by a crosslinking reaction such as condensation between organometallic compounds. .

Next, a second baking process is performed on the substrate 100 . The second baking process may be performed at a temperature of about 90 °C to about 200 °C. By performing the second baking process, the exposed region 106b of the photoresist layer 106 becomes difficult to dissolve in a developer.

4 shows a photoresist pattern 108 formed by dissolving and removing the photoresist film 106a corresponding to the unexposed region using a developer. Specifically, the photoresist pattern corresponding to the negative tone image ( 108) is completed.

As described above, the developer used in the pattern forming method according to the exemplary embodiment may be an organic solvent. As an example of the organic solvent used in the pattern forming method according to the embodiment, ketones such as methyl ethyl ketone, acetone, cyclohexanone, 2-haptanone, 4-methyl-2-propanol, 1-butanol, isopropanol, Alcohols such as 1-propanol and methanol, esters such as propylene glycol monomethyl ester acetate, ethyl acetate, ethyl lactate, n-butyl acetate and butyrolactone, aromatic compounds such as benzene, xylene and toluene, or these can be a combination of

However, the photoresist pattern according to the exemplary embodiment is not necessarily limited to being formed as a negative tone image, and may be formed to have a positive tone image. In this case, as a developer that can be used for forming a positive tone image, a quaternary ammonium hydroxide composition such as tetraethylammonium hydroxide, tetrapropylammonium hydroxide, tetrabutylammonium hydroxide, or a combination thereof, etc. can be heard

As described above, not only light having a wavelength such as i-line (wavelength 365 nm), KrF excimer laser (wavelength 248 nm), ArF excimer laser (wavelength 193 nm), but also EUV (Extreme UltraViolet; wavelength 13.5 nm), The photoresist pattern 108 formed by exposure to light having high energy, such as an E-beam (electron beam), may have a width of 5 nm to 100 nm. For example, the photoresist pattern 108 may be 5 nm to 90 nm, 5 nm to 80 nm, 5 nm to 70 nm, 5 nm to 60 nm, 10 nm to 50 nm, 10 nm to 40 nm, 10 nm to 30 nm, and may be formed to a width of 10 nm to 20 nm thick.

On the other hand, the photoresist pattern 108 has a half-pitch of about 50 nm or less, for example 40 nm or less, for example 30 nm or less, for example 25 nm or less, and about 10 nm or less, It may have a pitch having a line width roughness of about 5 nm or less.

Next, the resist underlayer 104 is etched using the photoresist pattern 108 as an etching mask. The organic layer pattern 112 is formed through the etching process as described above. The formed organic layer pattern 112 may also have a width corresponding to the photoresist pattern 108 .

Referring to FIG. 5 , the exposed thin film 102 is etched by applying the photoresist pattern 108 as an etching mask. As a result, the thin film is formed as a thin film pattern 114 .

The thin film 102 may be etched, for example, by dry etching using an etching gas, and the etching gas may be, for example, CHF ₃ , CF ₄ , Cl ₂ , BCl ₃ , or a mixture thereof.

In the exposure process performed above, the thin film pattern 114 formed using the photoresist pattern 108 formed by the exposure process performed using the EUV light source may have a width corresponding to the photoresist pattern 108 . . For example, the photoresist pattern 108 may have a width of 5 nm to 100 nm. For example, the thin film pattern 114 formed by the exposure process performed using the EUV light source may be 5 nm to 90 nm, 5 nm to 80 nm, 5 nm to 70 nm, 5 like the photoresist pattern 108 . It may have a width of nm to 60 nm, 10 nm to 50 nm, 10 nm to 40 nm, 10 nm to 30 nm, 10 nm to 20 nm, and more specifically, may be formed to a width of 20 nm or less.

Hereinafter, the present invention will be described in more detail through Examples relating to the preparation of the above-described composition for a semiconductor photoresist. However, the technical features of the present invention are not limited by the following examples.

Manufacture of organometallic compounds

Synthesis Example 1: Synthesis of a compound represented by Formula 3

In a 100 ml round bottom flask, nBuSnCl ₃ (8.5 g, 30 mmol) and 30 ml of toluene were added and dissolved, and triethylamine (9.4 g, 93 mmol), glycerol at 0 ° C. (2.8g, 30mmol) is slowly added sequentially, respectively. After stirring at room temperature for 12 hours, the filtrate from which the resulting salt is removed with a filter is concentrated and the solvent is completely removed by vacuum distillation to obtain a compound represented by the following Chemical Formula 3 in a yield of 72%.

[Formula 3]

Synthesis Example 2: Synthesis of the compound represented by Formula 4

In Synthesis Example 1, iPrSnCl ₃ instead of nBuSnCl ₃ was synthesized in the same manner as in Synthesis Example 1, except that the compound represented by the following Chemical Formula 4 was obtained in 68% yield.

[Formula 4]

Synthesis Example 3: Synthesis of the compound represented by Formula 5

In a 100 ml round-bottom flask, tBuSn(NEt ₂ ) ₃ (11.8 g, 30 mmol) and 40 ml of toluene were added and dissolved, and glycerol (2.8 g, 30 mmol) was slowly added at 0 ° C. do. After stirring at room temperature for 12 hours, the solvent is completely removed by vacuum distillation to obtain a compound represented by the following Chemical Formula 5 in 83% yield.

[Formula 5]

Synthesis Example 4: Synthesis of the compound represented by Formula 6

In Synthesis Example 1, except that BnSnCl ₃ was used instead of nBuSnCl ₃ , it was synthesized in the same manner as in Synthesis Example 1 to obtain a compound represented by the following Chemical Formula 6 in 87% yield.

[Formula 6]

Synthesis Example 5: Synthesis of the compound represented by Formula 7

In Synthesis Example 1, BnSnCl ₃ instead of nBuSnCl ₃ and 1,2,4-butantriol instead of glycerol were synthesized in the same manner as in Synthesis Example 1 to obtain a compound represented by the following Chemical Formula 7 in 80% yield.

[Formula 7]

Synthesis Example 6: Synthesis of the compound represented by Formula 8

In Synthesis Example 1, BnSnCl ₃ instead of nBuSnCl ₃ and 1,2,6-hexanetriol instead of glycerol were synthesized in the same manner as in Synthesis Example 1 to obtain a compound represented by the following Chemical Formula 8 in 78% yield.

[Formula 8]

Comparative Synthesis Example 1: Synthesis of a compound represented by Formula 9

Dissolve nBuSnCl ₃ (8.5 g, 30 mmol) in anhydrous pentane and lower the temperature to 0°C. Thereafter, triethylamine (10.0 g, 99 mmol) was slowly added dropwise, ethanol (4.2 g, 90 mmol) was added, and the mixture was stirred at room temperature for 5 hours. After completion of the reaction, the reaction is filtered, concentrated, and dried under vacuum to obtain a compound represented by the following Chemical Formula 9 in a yield of 40%.

[Formula 9]

Comparative Synthesis Example 2: Synthesis of a compound represented by Formula 10

In Comparative Synthesis Example 1, except that iPrSnCl ₃ was used instead of nBuSnCl ₃ , it was synthesized in the same manner as in Comparative Synthesis Example 1 to obtain a compound represented by the following Chemical Formula 10 in 63% yield.

[Formula 10]

Comparative Synthesis Example 3: Synthesis of the compound represented by Formula 11

tBuSn(NEt ₂ ) ₃ (8.5 g, 30 mmol) was dissolved in anhydrous pentane and the temperature was lowered to 0 °C. Then, ethanol (4.2 g, 90 mmol) is slowly added dropwise and stirred at room temperature for 10 hours. After completion of the reaction, the mixture is concentrated and vacuum dried to obtain a compound represented by the following Chemical Formula 11 in a yield of 60%.

[Formula 11]

Comparative Synthesis Example 4: Synthesis of the compound represented by Formula 12

In Comparative Synthesis Example 1, except that BnSnCl ₃ was used instead of nBuSnCl ₃ , it was synthesized in the same manner as in Comparative Synthesis Example 1 to obtain a compound represented by the following Chemical Formula 12 in 61% yield.

[Formula 12]

Examples 1 to 6: Preparation of a composition for a photoresist and formation of a photoresist film

The compounds of Formulas 3 to 8 obtained in Synthesis Examples 1 to 6 were dissolved in xylene at a concentration of 3 wt%, respectively, and filtered with a 0.1 μm PTFE syringe filter to obtain the photoresist composition according to Examples 1 to 6 manufacture

A circular silicon wafer with a diameter of 4 inches having a native-oxide surface was used as a substrate for thin film deposition, and the substrate was pretreated for 10 minutes under a UV ozone cleaning system. Thereafter, the prepared compositions for semiconductor photoresists according to Examples 1 to 6 were spin-coated at 1,500 rpm for 30 seconds on the pre-treated substrate, and fired on a hot plate at 100° C. for 120 seconds (fired after application, post-apply bake (PAB) to form a thin film.

After coating and baking, the thickness of the film was measured by ellipsometry, and the measured thickness was about 24 nm.

Comparative Examples 1 to 4: Preparation of a composition for a photoresist and formation of a photoresist film

The compounds of Chemical Formulas 9 to 12 synthesized in Comparative Synthesis Examples 1 to 4 were dissolved in xylene at a concentration of 3 wt%, and filtered through a 0.1 μm PTFE syringe filter, Comparative Examples 1 to 4 A composition for semiconductor resist according to the method is prepared.

Thereafter, a thin film is formed on the substrate through the same process as in the above-described embodiment with respect to the prepared compositions for semiconductor resists according to Comparative Examples 1 to 4, respectively.

After coating and baking, the thickness of the film was measured by ellipsometry, and the measured thickness was about 23 nm.

(evaluation)

Evaluation 1: Storage stability evaluation

For the semiconductor photoresist compositions prepared in Examples 1 to 6 and Comparative Examples 1 to 4, storage stability was evaluated according to the following criteria, and is shown in Table 1 below.

[Storage Stability]

When the compositions for semiconductor photoresists according to Examples 1 to 6 and Comparative Examples 1 to 4 were left standing for a specific period at room temperature (0 ° C. to 30 ° C. conditions), the degree of precipitation was observed with the naked eye, and the following It was evaluated in two stages according to the standard of storability.

- ○: Can be stored for more than 1 month

= X: Can be stored for less than 2 weeks

Evaluation 2: Pattern Formability Evaluation

A wafer was prepared by the same process as in the above example with the composition for semiconductor photoresists according to Examples 1 to 6 and Comparative Examples 1 to 4, and the wafer was prepared by extreme ultraviolet rays in an interval pattern of 18 nm lines and 36 nm pitches. (Exposure to extreme ultraviolet radiation). The equipment used at this time was a Lawrence Berkeley National Laboratory Micro Exposure Tool, MET 3, and 13.5 nm wavelength radiation, dipole illumination, and a numerical aperture of 0.3 were used. Thereafter, the resist and the substrate are exposed on a hotplate at 160° C. for 120 seconds, followed by post-exposure bake (PEB). The fired film was immersed in a developer (2-heptanone) for 30 seconds each, and then washed with the same developer for an additional 10 seconds to form a negative tone image, that is, to remove the unexposed coating portion. Finally, the process is terminated by performing hotplate firing at 150° C. for 120 seconds. As a result of SEM measurement of the developed resist film, an 18 nm line image on a 36 nm pitch is confirmed.

[Limited resolution]

- A: 18 nm or less

- B: greater than 18 nm

[Line Roughness]

- A: 2.5 nm or less

- B: >2.5 nm

storage stability limit resolution line roughness Example 1 ○ A A Example 2 ○ A A Example 3 ○ A A Example 4 ○ A A Example 5 ○ A A Example 6 ○ A A Comparative Example 1 X B B Comparative Example 2 X A B Comparative Example 3 X A B Comparative Example 4 X B B

Referring to Table 1, it can be seen that the compositions for semiconductor photoresists according to Examples 1 to 6 have better storage stability than the compositions for semiconductor photoresists according to Comparative Examples 1 to 4.

Referring to Table 1, the compositions for semiconductor photoresists according to Examples 1 to 6 showed excellent pattern formability by showing all of the limit resolution values of 18 nm or less, whereas the semiconductors according to Comparative Examples 1 and 4 It can be seen that the composition for photoresist exhibits a result value of greater than 18 nm in limit resolution, indicating that the pattern formability is not excellent.

In addition, the compositions for semiconductor photoresists according to Examples 1 to 6 showed excellent pattern formability by showing a result value of 2.5 nm or less for all of the line fill values, whereas the compositions for semiconductor photoresists according to Comparative Examples 1 to 4 It can be seen that the silver line roughness all showed a result value of more than 2.5 nm, indicating that the pattern formability was not excellent.

In the foregoing, specific embodiments of the present invention have been described and illustrated, but the present invention is not limited to the described embodiments, and it is common in the art that various modifications and variations can be made without departing from the spirit and scope of the present invention. This is obvious to those with knowledge. Accordingly, such modifications or variations should not be individually understood from the technical spirit or point of view of the present invention, and modified embodiments should be said to belong to the claims of the present invention.

100: substrate 102: thin film
104: photoresist underlayer film 106: photoresist film
106b: exposed area 106a: unexposed area
108: photoresist pattern 112: organic film pattern
114: thin film pattern
108: photoresist pattern 112: organic film pattern
114: thin film pattern

Claims (12)

A composition for a semiconductor photoresist comprising an organometallic compound represented by the following formula (1) and a solvent:
[Formula 1]

In Formula 1,
R ¹ is a substituted or unsubstituted C1 to C20 alkyl group, a substituted or unsubstituted C3 to C20 cycloalkyl group, or a substituted or unsubstituted C6 to C20 aryl group, or a combination thereof;
X ¹ To X ³ are each independently a single bond, a substituted or unsubstituted divalent C1 to C20 saturated aliphatic hydrocarbon group, a substituted or unsubstituted divalent C3 to C20 saturated alicyclic hydrocarbon group, one or more double bonds or triple bonds A substituted or unsubstituted divalent C2 to C20 unsaturated aliphatic hydrocarbon group comprising a, a divalent substituted or unsubstituted C6 to C20 aromatic hydrocarbon group, or a combination thereof,
Y ¹ is C(-R ^a ) or nitrogen (N),
R ^a is hydrogen, a hydroxy group (-OH), or -OR ^b ;
R ^b is a substituted or unsubstituted monovalent C1 to C20 saturated aliphatic hydrocarbon group, a substituted or unsubstituted monovalent C3 to C20 saturated alicyclic hydrocarbon group, a substituted or unsubstituted 1 containing one or more double or triple bonds a valent C2 to C20 unsaturated aliphatic hydrocarbon group, a monovalent substituted or unsubstituted C6 to C30 aromatic hydrocarbon group, or a combination thereof.
In claim 1,
R ¹ is a substituted or unsubstituted C1 to C10 alkyl group, a substituted or unsubstituted C3 to C10 cycloalkyl group, or a substituted or unsubstituted C6 to C10 aryl group, or a combination thereof,
X ¹ to X ³ are each independently a single bond, a substituted or unsubstituted divalent C1 to C8 saturated aliphatic hydrocarbon group, a substituted or unsubstituted divalent C3 to C6 saturated alicyclic hydrocarbon group, 1 or 2 double bonds, or a substituted or unsubstituted divalent C2 to C8 unsaturated aliphatic hydrocarbon group containing a triple bond, a divalent substituted or unsubstituted C6 to C10 arylene group, or a combination thereof;
R ^b is a substituted or unsubstituted monovalent C1 to C10 saturated aliphatic hydrocarbon group, a substituted or unsubstituted monovalent C3 to C10 saturated alicyclic hydrocarbon group, a substituted or unsubstituted containing 1 or 2 double or triple bonds A composition for a semiconductor photoresist comprising a monovalent C2 to C10 unsaturated aliphatic hydrocarbon group, a monovalent substituted or unsubstituted C6 to C10 aromatic hydrocarbon group, or a combination thereof.
In claim 1,
R ¹ is a methyl group, an ethyl group, a propyl group, a butyl group, an isopropyl group, a tert-butyl group, a 2,2-dimethylpropyl group, a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, a phenyl group, a tolyl group , a xylene group, a benzyl group, or a combination thereof,
X ¹ to X ³ are each independently a single bond, a methylene group, an ethylene group, a propylene group, a butylene group, a cyclobutylene group, a cyclopentylene group, a cyclohexylene group, an ethenylene group, a propenylene group, an ethynylene group, a pro a phenylene group, a phenylene group, or a combination thereof,
R ^b is a methyl group, an ethyl group, a propyl group, a butyl group, an isopropyl group, a tert-butyl group, a 2,2-dimethylpropyl group, a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, an ethenyl group, a pro A composition for a semiconductor photoresist comprising a phenyl group, a butenyl group, an ethynyl group, a propynyl group, a butynyl group, a phenyl group, a tolyl group, a xylene group, a benzyl group, or a combination thereof.
In claim 1,
R ¹ is any one of a methyl group, an ethyl group, a propyl group, an isopropyl group, a tert-butyl group, a phenyl group, and a benzyl group,
X ¹ to X ³ are each independently any one of a single bond, a methylene group, an ethylene group, a propylene group, and a butylene group,
Y ¹ is C(-R ^a ),
R ^a is hydrogen; a composition for a semiconductor photoresist;
In claim 1,
X ¹ is a methylene group,
X ² is a single bond,
X ³ is any one of a single bond, a methylene group, an ethylene group, a propylene group, and a butylene group, the composition for a semiconductor photoresist.
In claim 1,
The X ¹ to X ³ are all the same composition for a semiconductor photoresist.
The composition for a semiconductor photoresist according to claim 1, comprising 1 to 20% by weight of the organometallic compound represented by Formula 1, based on the total weight of the composition for a semiconductor photoresist.
The composition for a semiconductor photoresist of claim 1, wherein the composition for a semiconductor photoresist further comprises an additive of a surfactant, a crosslinking agent, a leveling agent, or a combination thereof.
forming an etch target layer on the substrate;
forming a photoresist layer by applying the composition for a semiconductor photoresist according to any one of claims 1 to 8 on the etching target layer;
forming a photoresist pattern by patterning the photoresist layer; and
and etching the etch target layer using the photoresist pattern as an etch mask.
The method of claim 9 , wherein the forming of the photoresist pattern uses light having a wavelength of 5 nm to 150 nm.
In claim 9,
The method further comprising the step of providing a resist underlayer film formed between the substrate and the photoresist film.
In claim 9,
The photoresist pattern is a pattern forming method having a width of 5 nm to 100 nm.