KR102351477B1 - Self-healing agent and coating method of the same - Google Patents
Self-healing agent and coating method of the same Download PDFInfo
- Publication number
- KR102351477B1 KR102351477B1 KR1020200011888A KR20200011888A KR102351477B1 KR 102351477 B1 KR102351477 B1 KR 102351477B1 KR 1020200011888 A KR1020200011888 A KR 1020200011888A KR 20200011888 A KR20200011888 A KR 20200011888A KR 102351477 B1 KR102351477 B1 KR 102351477B1
- Authority
- KR
- South Korea
- Prior art keywords
- inorganic crystal
- weight
- self
- crystal accelerator
- parts
- Prior art date
Abstract
본 발명은 자기치유 조성물 및 그 코팅방법에 관한 것으로서, 보다 상세하게는 무기계 결정촉진제를 코팅함으로써 콘크리트의 수화 과정에서 무기계 결정촉진제의 반응을 억제하고 장기적으로 무기계 결정촉진제를 미반응 상태로 남겨 놓아 균열 발생시 빠르게 침투한 수분과 반응하여 자기치유 성능을 발현, 향상시킬 수 있는 자기치유 조성물 및 그 코팅방법에 관한 것이다.
본 발명에 의한 자기치유 조성물은 무기계 결정촉진제 100중량부에 대하여 유기계 코팅제 20~100중량부를 포함한다. The present invention relates to a self-healing composition and a coating method therefor, and more particularly, by coating an inorganic crystal accelerator to inhibit the reaction of the inorganic crystal accelerator in the hydration process of concrete, and to leave the inorganic crystal accelerator in an unreacted state for a long time to cause cracking It relates to a self-healing composition and a coating method therefor capable of expressing and improving self-healing performance by reacting with moisture that quickly penetrated upon occurrence.
The self-healing composition according to the present invention contains 20 to 100 parts by weight of an organic coating agent based on 100 parts by weight of the inorganic crystal accelerator.
Description
본 발명은 자기치유 조성물 및 그 코팅방법에 관한 것으로서, 보다 상세하게는 무기계 결정촉진제를 코팅함으로써 콘크리트의 수화 과정에서 무기계 결정촉진제의 반응을 억제하고 장기적으로 무기계 결정촉진제를 미반응 상태로 남겨 놓아 균열 발생시 빠르게 침투한 수분과 반응하여 자기치유 성능을 발현, 향상시킬 수 있는 자기치유 조성물 및 그 코팅방법에 관한 것이다. The present invention relates to a self-healing composition and a coating method therefor, and more particularly, by coating an inorganic crystal accelerator to inhibit the reaction of the inorganic crystal accelerator in the hydration process of concrete, and to leave the inorganic crystal accelerator in an unreacted state for a long time to cause cracking It relates to a self-healing composition capable of expressing and improving self-healing performance by reacting with moisture that quickly penetrated upon occurrence, and a coating method therefor.
최근 구조물의 노후화로 인해 내구성능 및 유지보수에 대한 관심이 높아지면서, 콘크리트 구조물에 발생한 균열을 스스로 치유하여 내구성능을 향상시키고 유지보수 비용을 절감시킬 수 있는 균열 자기치유 콘크리트에 대한 관심이 높아지고 있다. Recently, as interest in durability and maintenance increases due to deterioration of structures, interest in crack self-healing concrete that can heal cracks in concrete structures by itself to improve durability and reduce maintenance costs is increasing. .
이에, 콘크리트 구조물의 균열 발생에 따른 문제를 해결하기 위한 방안으로서 최근에는 콘크리트 구조물에 균열이 발생하였을 때, 외부의 인위적인 작용 없이 콘크리트 내부의 물질에 의하여 스스로 균열을 복구하여 원래의 기능을 유지하게 만드는 자기치유 콘크리트(Self Healing Concrete)의 개발이 큰 관심을 얻고 있다.Accordingly, as a method to solve the problem of cracks in concrete structures, when cracks occur in concrete structures, the cracks are repaired by themselves by the material inside the concrete without external artificial action to maintain the original function. The development of self-healing concrete is receiving great attention.
일반 콘크리트 구조물의 경우 시공과정에서 발생하는 수축 및 하중에 의한 인장력 등으로 인해 균열이 발생되는데, 상기 균열이 유해이온의 이동통로로 작용하여 콘크리트 구조물의 내구성을 급격하게 감소시킨다. 이에, 균열발생을 제어하는 것이 콘크리트 구조물의 내구성을 유지하고 유지보수비용을 감소시키는데 중요한 요소로 작용한다.In the case of a general concrete structure, cracks occur due to the tensile force caused by contraction and load occurring during the construction process, and the cracks act as a passage for harmful ions to rapidly decrease the durability of the concrete structure. Therefore, controlling crack occurrence is an important factor in maintaining the durability of concrete structures and reducing maintenance costs.
시멘트 페이스트에는 수화과정 중 수분에 접하지 못하였거나, 수분이 충분하지 못하기 때문에 완전히 수화 반응이 일어나지 않은 미수화 반응물이 존재한다. 시멘트 페이스트에 균열이 발생하는 경우, 미수화 반응물이 균열면에 노출되고 여기에 수분이 침투되면, 침투된 수분에 상기 미수화 반응물이 용해된다.In the cement paste, there are non-hydrated reactants that did not completely hydrate because they did not come into contact with moisture during the hydration process or because there was not enough moisture. When cracks occur in the cement paste, the non-hydrated reactant is exposed to the cracked surface and moisture penetrates thereto, and the non-hydrated reactant is dissolved in the permeated moisture.
시간이 흐름에 따라 미수화 반응물은 지속적으로 용해되고, 시멘트 페이스트의 이온이 확산으로 인해 균열면으로 지속적으로 용출되면 균열 내 용액의 농도가 증가하게 되고, 용액 농도가 포화 상태에 이르게 되면 침전물이 발생하게 된다. 이에, 시간흐름에 따라 균열 내 침전물이 지속적으로 쌓여 균열이 자기치유되는 것으로, 자기치유에 의한 균열 채움 효과를 나타낸다.As time goes by, the unhydrated reactants are continuously dissolved, and if the ions of the cement paste are continuously eluted to the crack surface due to diffusion, the concentration of the solution in the crack increases. will do Accordingly, the cracks are self-healing due to the continuous accumulation of sediment in the cracks over time, showing the crack filling effect by self-healing.
일반적으로 보통 포틀랜드 시멘트는 균열을 스스로 치유하는 자연 치유(autogenous healing) 특성을 가지고 있지만, 자연 치유에 의한 균열 치유 성능은 0.1mm 이하로 미비하기 때문에 시멘트 자체의 성능만으로는 콘크리트에 발생한 균열을 효과적으로 치유하지 못하는 것으로 알려져 있다.In general, Portland cement has the characteristic of autogenous healing, which heals cracks by itself, but since the crack healing performance by natural healing is insignificant at 0.1 mm or less, the performance of cement itself alone does not effectively heal cracks in concrete. is known not to.
이에, 자기치유 콘크리트 기술로 무기계 결정촉진제는 균열 발생 시 침투한 수분과 반응하여 탄산칼슘 및 silicate gel 등의 물질을 생성하여 균열을 치유하는 소재이다. 무기계 결정촉진제는 다른 자기치유 소재에 비해 상대적으로 가격이 저렴하고 강도 및 workability에 미치는 영향이 적기 때문에 일본 등을 중심으로 개발이 이루어지고 있다. Therefore, with the self-healing concrete technology, inorganic crystal accelerators react with the moisture that penetrates when cracks occur to produce materials such as calcium carbonate and silicate gel to heal cracks. Inorganic crystal accelerators are being developed mainly in Japan because they are relatively inexpensive compared to other self-healing materials and have little effect on strength and workability.
하지만 무기계 결정촉진제의 높은 반응성으로 인해 초기 수화과정에서 물과 반응하여 장기적으로 자기치유 성능을 확보하기 어렵다는 문제가 발생하고 있고, 이러한 무기계 결정촉진제의 한계를 극복하기 위한 방법으로 무기계 결정촉진제를 캡슐화하여 균열 발생 시 까지 반응하지 않도록 하는 방법을 연구하고 있다. However, due to the high reactivity of the inorganic crystal accelerator, it reacts with water during the initial hydration process, making it difficult to secure self-healing performance in the long term. Methods are being studied to prevent the reaction from occurring until cracks occur.
하지만 캡슐로 인해 콘크리트의 강도가 저하되는 문제와 균열 발생 시 캡슐이 파괴되지 않아 오히려 자기치유 성능이 감소하는 문제가 발생하고 있다. However, there is a problem that the strength of concrete is lowered due to the capsule, and the capsule is not destroyed when cracks occur, which leads to a decrease in self-healing performance.
본 발명은 상술한 문제점을 해결하기 위하여 안출된 것으로서, 본 발명의 목적은 콘크리트의 수화 과정에서 무기계 결정촉진제의 반응을 억제하고 장기적으로 무기계 결정촉진제를 미반응 상태로 남겨 놓을 수 있는 자기치유 조성물 및 그 코팅방법을 제공함에 있다. The present invention has been devised to solve the above problems, and an object of the present invention is to inhibit the reaction of the inorganic crystal accelerator in the hydration process of concrete and to leave the inorganic crystal accelerator in an unreacted state for a long time; a self-healing composition and To provide a coating method.
본 발명의 다른 목적은 수분과의 접촉 시간이 지남에 따라 성능이 저하되어 균열의 발생 여부와 관계없이 자연적으로 코팅제가 파괴되어 내부 물질인 무기계 결정촉진제가 콘크리트 내부에 반응 가능한 상태로 남아 있게 되어 균열 발생시 빠르게 반응이 가능한 자기치유 조성물 및 그 코팅방법을 제공함에 있다. Another object of the present invention is that the performance deteriorates over time in contact with moisture, and the coating is naturally destroyed regardless of whether cracks occur, so that the inorganic crystal accelerator, which is an internal material, remains in a state capable of reacting inside the concrete, resulting in cracks. An object of the present invention is to provide a self-healing composition capable of reacting quickly when it occurs and a coating method therefor.
위와 같은 기술적 과제를 해결하기 위하여 본 발명에 의한 자기치유 조성물은 무기계 결정촉진제 100중량부에 대하여 유기계 코팅제 20~100중량부를 포함하는 것을 특징으로 한다. In order to solve the above technical problem, the self-healing composition according to the present invention is characterized in that it contains 20 to 100 parts by weight of an organic coating agent with respect to 100 parts by weight of the inorganic crystal accelerator.
또한 상기 무기계 결정촉진제는 석고(CaSO4)분말 30 ~ 50 중량% 및 망초(Na2SO4)분말 50 ~ 70 중량%를 포함하는 것이 바람직하다. In addition, the inorganic crystal accelerator contains 30 to 50% by weight of gypsum (CaSO 4 ) powder and 50 to 70% by weight of mango (Na 2 SO 4 ) powder.
또한 상기 유기계 코팅제는 포화지방산인 것이 바람직하다. In addition, the organic coating agent is preferably a saturated fatty acid.
또한 상기 유기계 코팅제는 액상의 팔미트산(PALMITIC ACID)인 것이 바람직하다. In addition, the organic coating agent is preferably a liquid palmitic acid (PALMITIC ACID).
또한 상기 무기계 결정촉진제 100중량부에 대하여 유성용매 500 ~ 1,000 중량부가 더 포함되는 것이 바람직하다. In addition, it is preferable that 500 to 1,000 parts by weight of the oil-based solvent are further included with respect to 100 parts by weight of the inorganic crystal accelerator.
또한 상기 유성용매는 액상의 에탄올인 것이 바람직하다. In addition, the oily solvent is preferably liquid ethanol.
본 발명에 의한 자기치유물질 코팅방법은 분말 형태의 무기계 결정촉진제 100중량부에 대하여, 액상의 유기계 코팅제 20~100중량부와, 액상의 유성용매 500 ~ 1,000 중량부를 혼합하는 단계; 및 상기 혼합물을 건조하여 상기 유성용매를 증발시키는 단계;를 포함하는 것을 특징으로 한다. The self-healing material coating method according to the present invention comprises the steps of mixing 20 to 100 parts by weight of a liquid organic coating agent and 500 to 1,000 parts by weight of a liquid oily solvent with respect to 100 parts by weight of an inorganic crystal accelerator in powder form; and drying the mixture to evaporate the oily solvent.
또한 상기 유성용매를 증발시키는 단계는 상기 유기계 코팅제의 용융점 이하의 온도에서 건조되는 것이 바람직하다. In addition, the step of evaporating the oil solvent is preferably dried at a temperature below the melting point of the organic coating agent.
또한 상기 무기계 결정촉진제는 석고분말 30 ~ 50 중량% 및 망초분말 50 ~ 70 중량%를 포함하고, 상기 유기계 코팅제는 액상의 팔미트산(PALMITIC ACID)이며, 상기 유성용매는 액상의 에탄올인 것이 바람직하다. In addition, the inorganic crystal accelerator includes 30 to 50% by weight of gypsum powder and 50 to 70% by weight of mango grass powder, and the organic coating agent is liquid palmitic acid (PALMITIC ACID), and the oily solvent is preferably liquid ethanol. do.
본 발명에 따르면, 무기계 결정촉진제를 코팅함으로써 콘크리트의 수화 과정에서 무기계 결정촉진제의 반응을 억제하고 장기적으로 무기계 결정촉진제를 미반응 상태로 남겨 놓을 수 있는 효과가 있다. According to the present invention, by coating the inorganic crystal accelerator, there is an effect of suppressing the reaction of the inorganic crystal accelerator during the hydration process of concrete and leaving the inorganic crystal accelerator in an unreacted state for a long time.
따라서 균열 발생시 빠르게 침투한 수분과 반응하여 자기치유 성능을 발현, 향상시킬 수 있는 것이다. Therefore, it is possible to express and improve self-healing performance by reacting with moisture that quickly penetrates when cracks occur.
특히, 본 발명에 의한 코팅제는 수분과의 접촉 시간이 지남에 따라 자연적으로 성능이 저하되어 균열의 발생 여부와 관계없이 무기계 결정촉진제가 콘크리트 내부에 반응 가능한 상태로 남아 있게 되어 균열 발생시 빠르게 반응이 가능하다. In particular, the performance of the coating agent according to the present invention naturally deteriorates over time in contact with moisture, and the inorganic crystal accelerator remains in a state capable of reacting inside the concrete regardless of whether cracks occur. do.
도 1은 무기계 결정촉진제의 코팅유무에 따른 미반응물의 양을 나타낸 것이다.
도 2는 무기계 결정촉진제의 코팅유무에 따른 용해도를 나타낸 것이다.
도 3은 무기계 결정촉진제의 코팅유무에 따른 균열면에 존재하는 미반응 결정촉진제의 변화를 나타낸 것이다.
도 4는 무기계 결정촉진제의 코팅유무에 따른 자기치유 성능을 나타낸 것이다.
도 5는 무기계 결정촉진제의 코팅방법을 나타낸 것이다.
도 6은 수분에 의한 코팅두께의 감소를 나타낸 것이다.
도 7은 코팅두께에 따른 용해 개시시기를 나타낸 것이다.
도 8은 시간에 따른 이온의 농도를 나타낸 것이다.
도 9는 Water flow test 수행결과를 나타낸 것이다. 1 shows the amount of unreacted substances according to the presence or absence of coating of an inorganic crystal accelerator.
Figure 2 shows the solubility according to the presence or absence of coating of the inorganic crystal accelerator.
3 shows the change of the unreacted crystal accelerator present on the crack surface according to the presence or absence of coating of the inorganic crystal accelerator.
4 shows the self-healing performance according to the presence or absence of coating of the inorganic crystal accelerator.
5 shows a coating method of an inorganic crystal accelerator.
6 shows a decrease in the coating thickness due to moisture.
7 shows the dissolution initiation time according to the coating thickness.
8 shows the concentration of ions according to time.
9 shows the results of the water flow test.
이하, 본 발명의 구성 및 작용을 구체적으로 설명한다. Hereinafter, the configuration and operation of the present invention will be described in detail.
본 발명은 콘크리트의 초기 재령에서 반응을 억제하고 장기적으로 무기계 결정촉진제를 미반응 상태로 남아 있도록 하여 장기 자기치유 성능을 향상시킬 수 있는 무기계 결정촉진제 코팅 기술 및 이를 이용한 자기치유 콘크리트 제조에 관한 것이다. The present invention relates to an inorganic crystal accelerator coating technology capable of improving long-term self-healing performance by inhibiting the reaction at the initial age of concrete and allowing the inorganic crystal accelerator to remain unreacted for a long period of time, and to the manufacture of self-healing concrete using the same.
구체적으로 본 발명에 따른 자기치유 조성물은 무기계 결정촉진제 100중량부에 대하여 유기계 코팅제 20~100중량부와 유성용매 500 ~ 1,000중량부를 포함한다. Specifically, the self-healing composition according to the present invention contains 20 to 100 parts by weight of an organic coating agent and 500 to 1,000 parts by weight of an oil-based solvent based on 100 parts by weight of the inorganic crystal accelerator.
상기 무기계 결정촉진제는 망초(Na2SO4)와 석고(CaSO4)를 분말형태로 혼합하여 이루어진다. The inorganic crystal accelerator is made by mixing mango (Na 2 SO 4 ) and gypsum (CaSO 4 ) in powder form.
상기 망초는 Na+와 SO4 2-로 용해되어 SO4 2-는 침상형 수화물인 Ettringite와 판상형 수화물인 monosulfate를 형성하여 균열을 치유하고, Na+는 높은 확산 속도로 균열이 발생한 위치로 빠르게 이동하여 균열에서 Na-계 화합물을 형성하여 균열을 치유한다. The Glauber's salt is dissolved in Na + and SO 4 2- SO 4 2- is acicular hydrate healing cracks to form a plate-shaped Ettringite and hydrate of monosulfate, and Na + is quickly moved to the position of cracks occurring at a high rate of diffusion Thus, a Na-based compound is formed in the crack to heal the crack.
상기 망초는 Na+ 공급재료로서 자기치유에는 유리하지만, Na2+ 이온이 강도 발현에 나쁜 영향을 미치기 때문에 일부를 석고 분말로 대체하는 것이다. As a Na + feed material, Sesame Seed is advantageous for self-healing, but Na 2+ ions have a bad effect on strength development, so some of them are replaced with gypsum powder.
상기 석고는 Ca2+와 SO4 2-로 용해되어 SO4 2-는 침상형 수화물인 Ettringite와 판상형 수화물인 monosulfate를 형성하여 균열을 치유하고, Ca2+는 CO3 2-와 반응하여 탄산칼슘(CaCO3)를 형성하여 균열을 치유한다.The gypsum and Ca 2+ is dissolved as SO 4 2- SO 4 2- is acicular hydrate healing cracks to form Ettringite and a plate-shaped, and a hydrate of monosulfate, Ca 2+ is calcium carbonate by reaction with CO 3 2- (CaCO 3 ) is formed to heal cracks.
구체적으로 석고(CaSO4)분말 30 ~ 50중량% 및 망초(Na2SO4)분말 50 ~ 70중량%를 포함하는 것이 바람직하다. Specifically, 30 to 50% by weight of the gypsum (CaSO 4 ) powder and 50 to 70% by weight of the mango (Na 2 SO 4 ) powder is preferred.
또한 상기 유기계 코팅제는 액상의 포화지방산으로서, 팔미트산(PALMITIC ACID)인 것이 바람직하다. In addition, the organic coating agent is a liquid saturated fatty acid, preferably palmitic acid (PALMITIC ACID).
상기 팔미트산은 일정 시간 동안 수분을 차단하는 역할을 하지만, 수분과의 지속적인 접촉을 통해 그 성능이 상실되는 물질이다. The palmitic acid serves to block moisture for a certain period of time, but its performance is lost through continuous contact with moisture.
상기 팔미트산은 양 끝이 소수기와 친수기로 구성되어 있으며 친수기의 음전하가 결정촉진제의 양전하와 결합하여 결정촉진제 주변을 코팅하며 반대편이 소수기로 되어 있기 때문에 수분과의 접촉을 차단하게 된다. The palmitic acid is composed of a hydrophobic group and a hydrophilic group at both ends, and the negative charge of the hydrophilic group combines with the positive charge of the crystal promoter to coat the surrounding crystal promoter, and since the opposite side is a hydrophobic group, contact with moisture is blocked.
이러한 특성을 통해 팔미트산은 망초와 석고를 포함하는 상기 무기계 결정촉진제의 반응성을 일정 시간 지연시키는 작용을 하며, 시멘트의 수화 과정에서 물과의 지속적인 접촉에 의해 일정 시간이 지난 후 소실되어 결정촉진제가 반응이 가능한 상태로 만들 수 있다. Through these properties, palmitic acid acts to delay the reactivity of the inorganic crystal accelerator, including algae and gypsum, for a certain period of time, and is lost after a certain period of time by continuous contact with water during the hydration process of cement. It can make the reaction possible.
따라서 팔미트산을 이용한 코팅을 통해 장기적으로 무기계 결정촉진제를 콘크리트 내부에서 미반응 상태로 남아 있도록 할 수 있으며, 장기적으로 자기치유 성능을 향상시킬 수 있다.Therefore, through the coating using palmitic acid, the inorganic crystal accelerator can remain unreacted inside the concrete for a long time, and the self-healing performance can be improved in the long term.
특히, 상기 유기계 코팅제의 양에 따라 코팅의 두께가 달라지고 코팅의 두께가 두꺼워질수록 용해 속도가 달라지기 때문에 이를 고려하여 상기 유기계 코팅제는 무기계 결정촉진제 100중량부에 대하여 20~100중량부를 포함하는 것이 바람직하다. In particular, the thickness of the coating varies depending on the amount of the organic coating agent, and the dissolution rate varies as the thickness of the coating increases. it is preferable
다만, 유기계 코팅제가 많이 사용될 경우 강도 발현과 무관한 소재를 사용하는 것이기 때문에 콘크리트의 강도 저하 등의 문제가 발생할 수도 있다. However, when a lot of organic coatings are used, a problem such as a decrease in the strength of concrete may occur because a material irrelevant to the strength expression is used.
상기 유성용매는 액상의 에탄올인 것이 더욱 바람직하다. The oily solvent is more preferably liquid ethanol.
또한 상기 유성용매는 상기 무기계 결정촉진제 100중량부에 대하여 500~1,000중량부가 포함되는 것이 바람직하다. In addition, the oil-based solvent is preferably included in an amount of 500 to 1,000 parts by weight based on 100 parts by weight of the inorganic crystal accelerator.
도 1은 무기계 결정촉진제의 코팅유무에 따른 미반응물의 양을 나타낸 것이다. 도 1에서 원재료는 망초와 석고가 혼합된 무기계 결정촉진제를 일컫는다. 1 shows the amount of unreacted substances according to the presence or absence of coating of an inorganic crystal accelerator. In FIG. 1, the raw material refers to an inorganic crystal accelerator in which mango grass and gypsum are mixed.
이를 통해 알 수 있는 바와 같이, 코팅되지 않은 무기계 결정촉진제(일반소재)는 콘크리트 배합 직후 물에 용해되기 때문에 균열 발생 시기에는 소량만 남아 있게 된다. As can be seen from this, the uncoated inorganic crystal accelerator (general material) is dissolved in water immediately after mixing with concrete, so only a small amount remains at the time of cracking.
반면 본 발명에 따라 유기계 코팅제에 의해 코팅된 무기계 결정촉진제(코팅소재)는 유기계 코팅제가 무기계 결정촉지제가 수분과의 접촉을 차단하여 장기재령까지 미반응 상태로 남아 있게 된다. On the other hand, in the inorganic crystal accelerator (coating material) coated by the organic coating agent according to the present invention, the organic coating agent blocks the contact of the inorganic crystal promoter with moisture, and remains unreacted until long-term age.
그러나 균열 발생의 여부와 관계없이 코팅막의 성능 저하가 발생하면 무기계결정촉진제가 용해되는데, 이미 주변에 수화물에 생성되었기 때문에 초기 재령과 동일한 양이 반응하지는 않으며, 상대적으로 많은 양이 미반응 상태로 남아 있게 된다.However, regardless of the occurrence of cracks, if the performance of the coating film deteriorates, the inorganic crystal accelerator is dissolved, but since it is already formed in the surrounding hydrate, the same amount as the initial age does not react, and a relatively large amount remains unreacted. there will be
도 2는 무기계 결정촉진제의 코팅유무에 따른 용해도를 나타낸 것이다. 코팅되지 않은 무기계 결정촉진제(일반소재)는 물에 넣는 순간 용해되기 시작한 반면 코팅제가 코팅된 무기계 결정촉진제(코팅소재)는 코팅막이 제거된 이후 용해가 시작된다. 이러한 용해 개시 시기의 차이로 인해 장기적으로 자기치유 성능을 향상시킬 수 있다. Figure 2 shows the solubility according to the presence or absence of coating of the inorganic crystal accelerator. Uncoated inorganic crystal accelerator (general material) starts to dissolve as soon as it is put in water, whereas inorganic crystal accelerator (coating material) coated with coating begins to dissolve after the coating film is removed. Due to the difference in the dissolution initiation time, it is possible to improve the self-healing performance in the long term.
도 3과 도 4는 무기계 결정촉진제의 코팅에 따른 균열 주변부의 미반응 무기계 결정촉진제 변화와 그에 따른 자기치유 성능 변화를 나타낸다. 일반 소재는 코팅되지 않은 무기계 결정촉진제를 일컫는 것이고, 코팅 소재는 코팅제가 코팅된 무기계 결정촉진제를 일컫는 것이다. 3 and 4 show the change of the unreacted inorganic crystal promoter in the crack periphery according to the coating of the inorganic crystal promoter and the change in self-healing performance accordingly. A general material refers to an uncoated inorganic crystal accelerator, and a coating material refers to an inorganic crystal accelerator coated with a coating agent.
도 3을 보면 무기계 결정촉진제의 코팅 여부에 따라 균열 발생 시기에 존재하는 무기계 결정촉진제의 양이 달리지는 것을 확인할 수 있으며, 도 4와 같이 무기계 결정촉진제의 양의 차이로 인해 치유 성능이 향상되는 것을 알 수 있다. Referring to FIG. 3, it can be seen that the amount of the inorganic crystal accelerator present at the cracking time varies depending on whether the inorganic crystal accelerator is coated, and as shown in FIG. 4, the healing performance is improved due to the difference in the amount of the inorganic crystal accelerator Able to know.
도 5는 무기계 결정촉진제의 코팅 방법을 나타낸다. 5 shows a coating method of an inorganic crystal accelerator.
이와 같은 자기치유물질 코팅방법을 설명한다. A method of coating such a self-healing material will be described.
먼저, 분말 형태의 무기계 결정촉진제 100중량부에 대하여, 액상의 유기계 코팅제 20~100중량부와, 액상의 유성용매 500 ~ 1,000중량부를 혼합한다.First, with respect to 100 parts by weight of the inorganic crystal accelerator in powder form, 20 to 100 parts by weight of a liquid organic coating agent and 500 to 1,000 parts by weight of a liquid oily solvent are mixed.
다음으로, 상기 혼합물이 충분히 섞이도록 교반한다. Next, the mixture is stirred to sufficiently mix.
다음으로, 상기 혼합물을 건조하여 상기 유성용매를 증발시킨다. Next, the mixture is dried to evaporate the oily solvent.
무기계 결정촉진제 100중량부에 대하여 상기 유기계 코팅제인 포화지방산은 20~100중량부를 혼합한다. 상기 포화지방산이 20중량부 미만일 경우에는 지나치게 빠르게 용해되고, 100중량부를 초과하는 경우에는 반대로 너무 느리게 용해가 된다. 20-100 parts by weight of the organic coating agent, saturated fatty acid, is mixed with respect to 100 parts by weight of the inorganic crystal accelerator. When the amount of the saturated fatty acid is less than 20 parts by weight, it dissolves too quickly, and when it exceeds 100 parts by weight, it dissolves too slowly on the contrary.
무기계 결정촉진제 100중량부에 대하여 에탄올 500 ~ 1,000중량부를 혼합하는데, 에탄올이 500중량부 미만일 경우에는 유기계 코팅제가 무기계 결정촉진제 표면을 적절하게 둘러싸서 코팅하지 못하는 문제가 있고, 에탄올이 1,000중량부를 초과하는 경우에는 유기계 코팅제가 따로 뭉치는 현상이 발생하고 유성용매의 증발 시간이 오래 걸려 생산성의 문제가 있다. 500 to 1,000 parts by weight of ethanol are mixed with respect to 100 parts by weight of the inorganic crystal accelerator, but when the amount of ethanol is less than 500 parts by weight, there is a problem that the organic coating agent cannot properly surround the surface of the inorganic crystal accelerator to coat it, and the ethanol exceeds 1,000 parts by weight In this case, there is a problem in productivity because the organic coating agent agglomerates separately and it takes a long time to evaporate the oil solvent.
상기 포화지방산의 용융점 이하의 온도(약 40℃)에서 약 6~12시간 건조하여 에탄올을 휘발시킨다. The ethanol is volatilized by drying for about 6 to 12 hours at a temperature (about 40° C.) below the melting point of the saturated fatty acid.
상기 포화지방산의 코팅 조건은 다음과 같다. The coating conditions of the saturated fatty acid are as follows.
첫째, 코팅 물질의 반응성을 일정 시간 지연시키는 작용을 한다. First, it acts to delay the reactivity of the coating material for a certain time.
둘째, 시멘트의 수화시 소실되어야 한다.Second, it must be lost during hydration of cement.
셋째, 코팅된 분말의 분산작용에 용이한 물성을 나타내야 한다.Third, it should exhibit easy physical properties for the dispersing action of the coated powder.
넷째, 코팅 후 착염의 생성으로 분말의 표면에 안정적인 코팅 상태를 유지할 수 있어야 한다. Fourth, it should be possible to maintain a stable coating state on the surface of the powder by generating a complex salt after coating.
이러한 조건에 부합하는 물질로서 포화지방산은 팔미트산(Palmitic Acid)이 바람직하다. As a material satisfying these conditions, the saturated fatty acid is preferably palmitic acid.
도 6은 유기계 코팅제가 코팅되지 않은 무기계 결정촉진제(일반 소재)와 유기계 코팅제가 코팅된 무기계 결정촉진제(코팅 소재)를 나타낸 것이다. 코팅막은 지속적인 수분과의 접촉에 의해 사라지며, 코팅이 사라지면 용해가 가능한 상태가 된다. 6 shows an inorganic crystal accelerator (general material) that is not coated with an organic coating agent and an inorganic crystal accelerator (coating material) coated with an organic coating agent. The coating film disappears by continuous contact with moisture, and when the coating disappears, it becomes a state capable of dissolution.
도 7은 코팅 두께에 따른 용해 개시시기를 나타낸다. 코팅막이 두꺼울수록 용해 개시 시기가 길어지나, 코팅 재료비가 증가하고, 콘크리트 전체 부피에서 유기계 코팅 소재가 차지하는 비용이 증가한다. 따라서 목표로 하는 치유 시기에 맞춰 적절한 코팅 두께를 찾는 것이 필요하다. 7 shows the dissolution initiation time according to the coating thickness. The thicker the coating film, the longer the dissolution start time, but the cost of the coating material increases, and the cost of the organic coating material in the total volume of concrete increases. Therefore, it is necessary to find an appropriate coating thickness according to the target healing time.
이하, 실시예를 통하여 본 발명을 보다 상세히 설명하고자 한다. Hereinafter, the present invention will be described in more detail through examples.
본 실시예는 본 발명을 보다 구체적으로 설명하기 위한 것이며, 본 발명의 권리범위가 이들 실시예에 한정되는 것은 아니다. These examples are for explaining the present invention in more detail, and the scope of the present invention is not limited to these examples.
실시예 및 비교예Examples and Comparative Examples
본 발명에서 제시하고 있는 방법을 통해 제작한 코팅된 무기계 결정촉진제의 시간에 따른 용해도를 평가하기 위한 실험을 수행하였다. 비교예와 실시예를 증류수에 용해시킨 후 시간에 따라 용해되는 이온의 농도를 Ion chromatography를 통해 측정하였다. An experiment was performed to evaluate the solubility over time of the coated inorganic crystal accelerator prepared by the method presented in the present invention. After dissolving Comparative Examples and Examples in distilled water, the concentration of dissolved ions over time was measured through ion chromatography.
도 8은 증류수에 용해된 시간에 따른 이온의 농도를 나타낸 것이다. 이로부터 코팅제는 이온이 용해되기 시작하는데 약 72시간이 소요되는 것을 확인할 수 있다. 따라서 실시예가 장기 재령에도 무기계 결정촉진제가 미반응 상태로 남아있으며, 자기치유 성능을 확보할 수 있을 것으로 판단된다. 8 shows the concentration of ions according to time dissolved in distilled water. From this, it can be seen that it takes about 72 hours for the ions to start to dissolve in the coating agent. Therefore, in the embodiment, the inorganic crystal accelerator remains unreacted even with a long-term age, and it is determined that the self-healing performance can be secured.
본 발명에 의한 코팅제를 활용한 자기치유 콘크리트의 자기치유 성능을 평가하기 위한 실험을 수행하였다. 실험을 위해 표 1은 모르타르 배합비로서 표 1의 배합비를 이용하여 직경 100mm, 높이 50mm의 디스크를 만들었다. 비교예 1과 비교예 2는 실시예와의 성능 비교를 위해 사용되었다. An experiment was performed to evaluate the self-healing performance of self-healing concrete using the coating agent according to the present invention. For the experiment, Table 1 is a mortar mixing ratio, and using the mixing ratio of Table 1, a disk having a diameter of 100 mm and a height of 50 mm was made. Comparative Example 1 and Comparative Example 2 were used for performance comparison with Examples.
실험방법 및 평가Experimental method and evaluation
1) 균열 유도1) crack induction
시편 배합 이후 1일 간 23±1°C, RH 100% 챔버에서 양생하였으며, 이후 23±1°C 수조에서 재령 28일까지 수중 양생하였다.After mixing the specimen, it was cured in a chamber at 23±1°C,
재령 28일의 시편을 수조에서 꺼내 UTM을 이용하여 관통 균열을 낸 후 실리콘 시트를 시편 양 끝에 넣어 을 넣어 균열 폭이 250 ± 10㎛이 되도록 고정시킨다.After taking the 28-day-old specimen from the water tank and making a penetration crack using UTM, insert a silicone sheet into both ends of the specimen and fix it so that the crack width is 250 ± 10㎛.
2) 균열 자기치유 성능평가2) Crack self-healing performance evaluation
water flow test 세팅을 한 후 시간에 따른 투수량 변화를 측정한다. After setting the water flow test, measure the change in permeability over time.
실험은 총 28일간 수행하였으며, 투수량 감소율이 클수록 자기치유 성능이 뛰어난 것으로 볼 수 있다. The experiment was carried out for a total of 28 days, and it can be seen that the greater the permeability reduction rate, the better the self-healing performance.
3) 측정결과3) Measurement result
도 9에 나타난 바와 같이, 28일간 투수량(water flow) 변화를 측정한 결과 비교예 1은 약 40% 투수량이 감소하였으며, 비교예 2는 약 65% 감소하였다. As shown in FIG. 9 , as a result of measuring the change in water flow for 28 days, Comparative Example 1 decreased by about 40%, and Comparative Example 2 decreased by about 65%.
반면, 실시예는 투수량이 100% 감소되었는데, 이를 통해 무기계 결정촉진제의 코팅을 통해 자기치유 성능이 향상된다는 것을 확인할 수 있다. On the other hand, in the embodiment, the water permeability was reduced by 100%, and it can be confirmed that the self-healing performance is improved through the coating of the inorganic crystal accelerator.
Claims (9)
상기 무기계 결정촉진제에 유기계 코팅제가 1∼5㎛ 두께로 코팅되도록 상기 유기계 코팅제로서 액상의 팔미트산(PALMITIC ACID) 20∼100중량부가 포함되고,
상기 무기계 결정촉진제는 망초(Na2SO4)분말 50∼70 중량% 및 석고(CaSO4)분말 30∼50 중량%를 포함하는 것을 특징으로 하는 자기치유 조성물.
With respect to 100 parts by weight of the inorganic crystal accelerator,
20-100 parts by weight of liquid palmitic acid (PALMITIC ACID) is included as the organic coating agent so that the organic coating agent is coated to a thickness of 1-5 μm on the inorganic crystal accelerator,
The inorganic crystal accelerator is a self-healing composition, characterized in that it comprises 50 to 70% by weight of the powdery mildew (Na 2 SO 4 ) and 30 to 50% by weight of the gypsum (CaSO 4 ) powder.
상기 무기계 결정촉진제 100중량부에 대하여 유성용매로서 액상의 에탄올 500∼1,000 중량부가 더 포함되는 것을 특징으로 하는 자기치유 조성물.
The method of claim 1,
The self-healing composition, characterized in that it further comprises 500 to 1,000 parts by weight of liquid ethanol as an oily solvent based on 100 parts by weight of the inorganic crystal accelerator.
상기 혼합물을 건조하여 상기 유성용매를 증발시키는 단계;로 수행하여 상기 무기계 결정촉진제에 유기계 코팅제가 1∼5㎛ 두께로 코팅되고,
상기 무기계 결정촉진제는 석고분말 30∼50 중량% 및 망초분말 50∼70 중량%를 포함하고,
상기 유성용매는 액상의 에탄올인 것을 특징으로 하는 자기치유물질 코팅방법. Preparing a mixture by mixing 20 to 100 parts by weight of palmitic acid (PALMITIC ACID) liquid as an organic coating agent and 500 to 1,000 parts by weight of an oily solvent based on 100 parts by weight of the inorganic crystal accelerator in powder form; and
Drying the mixture and evaporating the oily solvent; and coating the inorganic crystal accelerator with an organic coating agent to a thickness of 1 to 5 μm,
The inorganic crystal accelerator comprises 30 to 50% by weight of gypsum powder and 50 to 70% by weight of Mangoshu powder,
The oil-based solvent is a self-healing material coating method, characterized in that the liquid ethanol.