KR102314948B1 - Adhesive sheet for window deco film and window deco film comprising the same - Google Patents

Adhesive sheet for window deco film and window deco film comprising the same Download PDF

Info

Publication number
KR102314948B1
KR102314948B1 KR1020180146495A KR20180146495A KR102314948B1 KR 102314948 B1 KR102314948 B1 KR 102314948B1 KR 1020180146495 A KR1020180146495 A KR 1020180146495A KR 20180146495 A KR20180146495 A KR 20180146495A KR 102314948 B1 KR102314948 B1 KR 102314948B1
Authority
KR
South Korea
Prior art keywords
meth
monomer
acrylate
weight
parts
Prior art date
Application number
KR1020180146495A
Other languages
Korean (ko)
Other versions
KR20200061113A (en
Inventor
이슬
김상환
홍재성
김우연
윤후영
송호경
Original Assignee
주식회사 엘지화학
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 엘지화학 filed Critical 주식회사 엘지화학
Priority to KR1020180146495A priority Critical patent/KR102314948B1/en
Publication of KR20200061113A publication Critical patent/KR20200061113A/en
Application granted granted Critical
Publication of KR102314948B1 publication Critical patent/KR102314948B1/en

Abstract

본 발명은 유연층과 점착층을 포함하는 윈도우 데코 필름용 점착 시트 및 이를 포함하는 윈도우 데코 필름으로서, 곡면 기재에 대한 점착 성능이 우수한 윈도우 데코 필름용 점착 시트 및 윈도우 데코 필름에 관한 것이다.The present invention relates to an adhesive sheet for a window decoration film including a flexible layer and an adhesive layer, and a window decoration film including the same, and to an adhesive sheet for a window decoration film and a window decoration film having excellent adhesion performance to a curved substrate.

Description

윈도우 데코 필름용 점착 시트 및 이를 포함하는 윈도우 데코 필름{ADHESIVE SHEET FOR WINDOW DECO FILM AND WINDOW DECO FILM COMPRISING THE SAME}Adhesive sheet for window decoration film and window decoration film including same

본 발명은 점착 시트 및 이를 포함하는 윈도우 데코 필름에 관한 것으로, 구체적으로는 점착 성능이 우수한 윈도우 데코 필름용 점착 시트 및 이를 포함하는 윈도우 데코 필름에 관한 것이다.The present invention relates to an adhesive sheet and a window decoration film including the same, and more particularly, to an adhesive sheet for a window decoration film having excellent adhesive performance, and a window decoration film including the same.

최근, 플렉서블 디스플레이(Flexible Display)가 발전됨에 따라서, 커브 구조를 가지는 스마트폰, TV, 노트북이나 컴퓨터의 모니터 등이 개발되고 있다. 이에 따라, 스마트폰, TV, 노트북이나 컴퓨터의 모니터 등의 외장재로 사용되는 유리도 커브 형태로 개발이 진행되고 있으며, 상기 커브 형태인 유리의 상부에 부착될 수 있는 윈도우 데코 필름의 개발도 진행되고 있다.Recently, with the development of flexible displays, smartphones, TVs, laptops, and computer monitors having a curved structure have been developed. Accordingly, glass used as an exterior material for smartphones, TVs, laptops or computer monitors, etc., is also being developed in a curved form, and a window decoration film that can be attached to the upper portion of the curved glass is also being developed. have.

한편, 기존의 윈도우 데코 필름(Window Deco Film)은 이형 필름, 점착 시트, 프라이머층, 인쇄층 및 보호 필름이 순차적으로 적층되어 있는 구조이다. 다만, 상기 외장재로 사용되는 유리의 커브 곡률이 높으면, 피착제인 커브 형태의 유리에 부착되는 윈도우 데코 필름의 점착 성능이 현저히 저하되는 문제가 있다. 즉, 유리에 대한 윈도우 데코 필름(Window Deco Film)에 포함되는 점착 시트의 점착 성능이 현저히 저하되는 문제가 있다.On the other hand, the existing window deco film (Window Deco Film) has a structure in which a release film, an adhesive sheet, a primer layer, a printing layer, and a protective film are sequentially stacked. However, when the curved curvature of the glass used as the exterior material is high, there is a problem in that the adhesive performance of the window decoration film attached to the curved glass, which is the adherend, is significantly reduced. That is, there is a problem in that the adhesive performance of the pressure-sensitive adhesive sheet included in the window deco film (Window Deco Film) to glass is significantly reduced.

따라서, 곡면 기재에 대하여 점착 성능이 우수한 윈도우 데코 필름용 점착 시트가 필요한 실정이다.Therefore, there is a need for an adhesive sheet for a window decoration film having excellent adhesive performance on a curved substrate.

한국 공개공보: 10-2017-0116969 AKorean Publication: 10-2017-0116969 A

본 발명이 이루고자 하는 기술적 과제는 곡면 기재에 대한 점착 성능이 우수한 윈도우 데코 필름용 점착 시트 및 이를 포함하는 윈도우 데코 필름을 제공하는 것이다.An object of the present invention is to provide an adhesive sheet for a window decoration film having excellent adhesive performance on a curved substrate, and a window decoration film including the same.

다만, 본 발명이 해결하고자 하는 과제는 상기 언급한 과제로 제한되지 않으며, 언급되지 않은 또 다른 과제들은 하기의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.However, the problems to be solved by the present invention are not limited to the above-mentioned problems, and other problems not mentioned will be clearly understood by those skilled in the art from the following description.

본 발명의 일 실시상태는 점착층; 및 상기 점착층 상부에 배치되는 유연층을 포함하고, 상기 점착층은 유리전이온도가 - 50 ℃ 이상 - 30 ℃ 이하인 아크릴레이트계 수지를 포함하는 점착층 조성물의 경화물이며, 상기 아크릴레이트계 수지는 알킬기 함유 (메트)아크릴레이트계 모노머, 헤테로사이클로알킬기 함유 (메트)아크릴레이트계 모노머 및 (메트)아크릴산계 모노머를 포함하는 수지 조성물의 중합체이고, 상기 점착층 두께와 상기 유연층 두께의 비는 2:3 내지 1:2인 윈도우 데코 필름용 점착 시트를 제공한다.One embodiment of the present invention is an adhesive layer; and a flexible layer disposed on the pressure-sensitive adhesive layer, wherein the pressure-sensitive adhesive layer is a cured product of an adhesive layer composition comprising an acrylate-based resin having a glass transition temperature of -50 ℃ or higher and 30 ℃ or lower, the acrylate-based resin is a polymer of a resin composition comprising an alkyl group-containing (meth)acrylate-based monomer, a heterocycloalkyl group-containing (meth)acrylate-based monomer and a (meth)acrylic acid-based monomer, and the thickness of the adhesive layer and the thickness of the flexible layer is A pressure-sensitive adhesive sheet for a window decoration film of 2:3 to 1:2 is provided.

본 발명의 다른 실시상태는, 이형 필름; 본 발명의 일 실시상태에 따른 윈도우 데코 필름용 점착 시트; 인쇄층; 및 보호 필름이 순차적으로 적층된 것을 포함하는 윈도우 데코 필름을 제공한다.Another embodiment of the present invention is a release film; Adhesive sheet for window decoration film according to an embodiment of the present invention; printed layer; And it provides a window decoration film comprising a sequentially laminated protective film.

본 발명의 일 실시상태에 따른 윈도우 데코 필름용 점착 시트는 점착 성능이 우수하다. 구체적으로, 곡면 기재에 대한 접착력 및 인쇄층에 대한 부착성이 우수하다.The adhesive sheet for a window decoration film according to an exemplary embodiment of the present invention has excellent adhesive performance. Specifically, it has excellent adhesion to a curved substrate and adhesion to a printed layer.

본 발명의 일 실시상태에 따른 윈도우 데코 필름은 점착 성능이 우수하다. 구체적으로, 곡면 기재에 대한 접착력 및 인쇄층에 대한 부착성이 우수하다.The window decoration film according to an exemplary embodiment of the present invention has excellent adhesive performance. Specifically, it has excellent adhesion to a curved substrate and adhesion to a printed layer.

본 명세서에 있어서, 어떤 부분이 어떤 구성요소를 "포함" 한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것을 의미한다.In the present specification, when a part "includes" a certain component, this means that other components may be further included rather than excluding other components unless otherwise stated.

본 명세서에 있어서, "(메트)아크릴레이트"는 아크릴레이트 또는 메타크릴레이트를 의미한다.In the present specification, "(meth)acrylate" means acrylate or methacrylate.

본 명세서에 있어서, 단위 "중량부"는 각 성분간의 중량의 비율을 의미할 수 있다.In the present specification, the unit “parts by weight” may mean a ratio of weight between each component.

본 명세서에 있어서, "단량체(monomer)"는 폴리머 형성 반응 조건에서 추가적으로 일련의 같거나 다른 분자로 공유결합을 형성할 수 있는 물질을 의미할 수 있다. 즉, "단량체(monomer)"는 폴리머 형성을 위한 중합 반응시 하나의 물질이 폴리머 배열(sequence)의 반복단위, 즉 단량체 단위(monomer unit)로 전환될 수 있다.As used herein, the term “monomer” may refer to a substance capable of forming a covalent bond with a series of additionally identical or different molecules under the polymer-forming reaction conditions. That is, a "monomer" may be converted into a repeating unit of a polymer sequence, ie, a monomer unit, in a polymerization reaction to form a polymer.

본 명세서에 있어서, 어떤 부재가 다른 부재 "상에" 위치하고 있다고 할 때, 이는 어떤 부재가 다른 부재에 접해 있는 경우뿐만 아니라 두 부재 사이에 또 다른 부재가 존재하고 있는 경우도 포함한다.In the present specification, when a member is said to be located "on" another member, this includes not only a case in which a member is in contact with another member but also a case in which another member exists between the two members.

이하, 본 발명에 대하여 더욱 상세하게 설명한다.Hereinafter, the present invention will be described in more detail.

본 발명의 일 실시상태는, 점착층; 및 상기 점착층 상부에 배치되는 유연층을 포함하고, 상기 점착층은 아크릴레이트계 수지를 포함하는 점착층 조성물의 경화물이며, 상기 아크릴레이트계 수지는 알킬기 함유 (메트)아크릴레이트계 모노머, 헤테로사이클로알킬기 함유 (메트)아크릴레이트계 모노머 및 (메트)아크릴산계 모노머를 포함하는 수지 조성물의 중합체인 윈도우 데코 필름용 점착 시트를 제공한다.An exemplary embodiment of the present invention, an adhesive layer; and a flexible layer disposed on the adhesive layer, wherein the adhesive layer is a cured product of an adhesive layer composition including an acrylate-based resin, and the acrylate-based resin is an alkyl group-containing (meth)acrylate-based monomer, hetero Provided is an adhesive sheet for a window decoration film, which is a polymer of a resin composition including a cycloalkyl group-containing (meth)acrylate-based monomer and a (meth)acrylic acid-based monomer.

상기 아크릴레이트계 수지는 유리전이온도가 - 50 ℃ 이상 - 30 ℃ 이하이다. 구체적으로, - 50 ℃ 이상 - 35 ℃ 이하, - 50 ℃ 이상 - 40 ℃ 이하일 수 있고, 더욱 구체적으로, - 50 ℃ 이상 - 45 ℃ 이하일 수 있다. 한편, 상기 점착층의 유리전이온도가 -50 ℃ 미만인 경우, 점착층이 소프트하여 점착층 자체의 응집력이 없을 수 있다. 상기 점착층의 유리전이온도가 - 30 ℃ 초과인 경우, 점착층이 하드하여 상기 점착층을 포함하는 윈도우 데코 필름용 점착 시트의 점착 성능이 좋지 않을 수 있다. 즉, 상기 점착층의 유리전이온도가 상기 범위 내인 경우, 윈도우 데코 필름용 점착 시트는 우수한 접착력을 구현할 수 있다. 특히, 곡면 기재에 대한 접착력이 우수할 수 있다.The acrylate-based resin has a glass transition temperature of -50 °C or higher - 30 °C or lower. Specifically, it may be -50 ℃ or more - 35 ℃ or less, -50 ℃ or more - 40 ℃ or less, and more specifically, -50 ℃ or more - 45 ℃ or less. On the other hand, when the glass transition temperature of the adhesive layer is less than -50 ℃, the adhesive layer is soft, there may be no cohesive force of the adhesive layer itself. If the glass transition temperature of the adhesive layer is greater than -30 ℃, the adhesive layer may be hard, so that the adhesive performance of the adhesive sheet for a window decoration film including the adhesive layer may not be good. That is, when the glass transition temperature of the adhesive layer is within the above range, the adhesive sheet for a window decoration film can implement excellent adhesion. In particular, the adhesive force to the curved substrate may be excellent.

상기 점착층 두께와 상기 유연층 두께의 비는 2:3 내지 1:2이다. 구체적으로, 상기 점착층 두께와 상기 유연층 두께의 비는 3:5 내지 1:2 또는 4:7 내지 1:2일 수 있다. 상기 점착층 두께와 상기 유연층 두께의 비가 상기 범위 내인 경우, 상기 점착층을 포함하는 윈도우 데코 필름용 점착 시트가 우수한 접착력 및 우수한 부착성을 구현할 수 있다. 특히, 곡면 기재에 대한 접착력 및 인쇄층에 대한 부착성이 우수할 수 있다.The ratio of the thickness of the adhesive layer to the thickness of the flexible layer is 2:3 to 1:2. Specifically, the ratio of the thickness of the adhesive layer to the thickness of the flexible layer may be 3:5 to 1:2 or 4:7 to 1:2. When the ratio of the thickness of the adhesive layer to the thickness of the flexible layer is within the above range, the adhesive sheet for a window decoration film including the adhesive layer may implement excellent adhesion and excellent adhesion. In particular, adhesion to a curved substrate and adhesion to a printed layer may be excellent.

본 발명의 일 실시상태에 따르면, 상기 헤테로사이클로알킬기 함유 (메트)아크릴레이트계 모노머는 상기 알킬기 함유 (메트)아크릴레이트계 모노머 100 중량부에 대하여 3 중량부 이상 15 중량부 이하일 수 있다. 구체적으로, 5 중량부 이상 15 중량부 이하, 5 중량부 이상 12 중량부 이하, 10 중량부 이상 15 중량부 이하 또는 12 중량부 이상 15 중량부 이하일 수 있다. 상기 헤테로사이클로알킬기 함유 (메트)아크릴레이트계 모노머의 함량이 상기 범위 내인 경우, 아크릴레이트계 수지가 일정 범위의 유리전이온도를 가질 수 있도록 하여, 윈도우 데코 필름용 점착 시트가 우수한 점착 성능을 구현할 수 있다.According to an exemplary embodiment of the present invention, the amount of the heterocycloalkyl group-containing (meth)acrylate-based monomer may be 3 parts by weight or more and 15 parts by weight or less based on 100 parts by weight of the alkyl group-containing (meth)acrylate-based monomer. Specifically, it may be 5 parts by weight or more and 15 parts by weight or less, 5 parts by weight or more and 12 parts by weight or less, 10 parts by weight or more and 15 parts by weight or less, or 12 parts by weight or more and 15 parts by weight or less. When the content of the heterocycloalkyl group-containing (meth)acrylate-based monomer is within the above range, the acrylate-based resin can have a glass transition temperature in a certain range, so that the adhesive sheet for a window decoration film can implement excellent adhesive performance. have.

또한, 상기 헤테로사이클로알킬기 함유 (메트)아크릴레이트계 모노머는 수분과 결합할 수 있어, 이를 상기 범위 내의 함량으로 포함하는 점착층은 고온 및 고습 조건에서 내구성이 뛰어나고 백탁 현상이 일어나지 않을 수 있다.In addition, the heterocycloalkyl group-containing (meth) acrylate-based monomer can bind to moisture, and the adhesive layer including it in an amount within the above range has excellent durability under high temperature and high humidity conditions, and cloudiness may not occur.

본 발명의 일 실시상태에 따르면, 상기 (메트)아크릴산계 모노머는 상기 수지 조성물 100 중량부에 대하여 1 중량부 이상 12 중량부 이하일 수 있다. 구체적으로, 1 중량부 이상 8 중량부 이하, 더욱 구체적으로, 3 중량부 이상 6 중량부 이하 일 수 있다. 상기 (메트)아크릴산계 모노머의 함량이 상기 범위 내인 경우, 점착층의 경도를 향상시킬 수 있고, 응집력을 향상시킬 수 있다. 또한, 점착층의 접착력 향상을 도모할 수 있다.According to an exemplary embodiment of the present invention, the (meth)acrylic acid-based monomer may be 1 part by weight or more and 12 parts by weight or less based on 100 parts by weight of the resin composition. Specifically, it may be 1 part by weight or more and 8 parts by weight or less, more specifically, 3 parts by weight or more and 6 parts by weight or less. When the content of the (meth)acrylic acid-based monomer is within the above range, the hardness of the adhesive layer may be improved, and cohesive force may be improved. In addition, it is possible to improve the adhesive force of the adhesive layer.

상기 알킬기 함유 (메트)아크릴레이트계 모노머는 메틸(메트)아크릴레이트 모노머, 에틸(메트)아크릴레이트 모노머, n-프로필(메트)아크릴레이트 모노머, 이소프로필(메트)아크릴레이트 모노머, n-부틸(메트)아크릴레이트 모노머, t-부틸(메트)아크릴레이트 모노머, sec-부틸(메트)아크릴레이트 모노머, 펜틸(메트)아크릴레이트 모노머, 2-에틸헥실(메트)아크릴레이트 모노머, 2-에틸부틸(메트)아크릴레이트 모노머, n-옥틸(메트)아크릴레이트 모노머, 및 이소옥틸(메트)아크릴레이트 모노머 중에서 선택된 1종 이상일 수 있다.The alkyl group-containing (meth) acrylate-based monomer is a methyl (meth) acrylate monomer, an ethyl (meth) acrylate monomer, an n-propyl (meth) acrylate monomer, an isopropyl (meth) acrylate monomer, n-butyl ( Meth) acrylate monomer, t-butyl (meth) acrylate monomer, sec-butyl (meth) acrylate monomer, pentyl (meth) acrylate monomer, 2-ethylhexyl (meth) acrylate monomer, 2-ethylbutyl ( It may be at least one selected from a meth) acrylate monomer, an n-octyl (meth) acrylate monomer, and an isooctyl (meth) acrylate monomer.

본 발명의 일 실시상태에 따르면, 상기 헤테로사이클로알킬기 함유 (메트)아크릴레이트계 모노머는 헤테로사이클로알킬기 내에 불포화 결합이 존재하지 않고 탄소 외의 이종 원소가 포함된 고리 구조를 포함할 수 있으며, 탄소수 2 이상 20 이하의 단일 고리(monocyclic ring) 또는 다중 고리(polycyclic ring)를 포함할 수 있다.According to an exemplary embodiment of the present invention, the heterocycloalkyl group-containing (meth)acrylate-based monomer may include a ring structure in which an unsaturated bond does not exist in the heterocycloalkyl group and includes a heterogeneous element other than carbon, and has 2 or more carbon atoms. It may contain up to 20 monocyclic rings or polycyclic rings.

본 발명의 일 실시상태에 따르면, 상기 헤테로사이클로알킬기 함유 (메트)아크릴레이트계 모노머는 테트라하이드로퍼퓨릴(메트)아크릴레이트 모노머, 테트라하이드로피라닐(메트)아크릴레이트 모노머, 아크릴로일모르폴린 모노머 및 사이클릭트리메틸올프로판포말아크릴레이트 모노머 중에서 선택된 1종 이상일 수 있다.According to an exemplary embodiment of the present invention, the heterocycloalkyl group-containing (meth)acrylate-based monomer is a tetrahydrofurfuryl (meth)acrylate monomer, a tetrahydropyranyl (meth)acrylate monomer, and an acryloylmorpholine monomer. And it may be at least one selected from cyclic trimethylol propane formal acrylate monomers.

본 발명의 일 실시상태에 따르면, 상기 (메트)아크릴산계 모노머는 아크릴산 모노머, 메타크릴산 모노머, 2-카르복시에틸아크릴산 모노머, 3-카르복시프로필아크릴산 모노머, 2-(메트)아크릴로일옥시아세트산 모노머, 3-(메트)아크릴로일옥시프로필산 모노머 및 4-(메트)아크릴로일옥시부틸산 모노머 중에서 선택된 1종 이상일 수 있다.According to an exemplary embodiment of the present invention, the (meth)acrylic acid-based monomer is an acrylic acid monomer, a methacrylic acid monomer, a 2-carboxyethylacrylic acid monomer, a 3-carboxypropylacrylic acid monomer, and a 2-(meth)acryloyloxyacetic acid monomer , 3-(meth)acryloyloxypropyl acid monomer and 4-(meth)acryloyloxybutyric acid monomer may be at least one selected from the group consisting of.

상기 아크릴레이트계 수지는 알킬기 함유 (메트)아크릴레이트계 모노머, 헤테로사이클로알킬기 함유 (메트)아크릴레이트계 모노머 및 (메트)아크릴산계 모노머를 포함하는 수지 조성물이 광중합 또는 열중합하여 제조된 것일 수 있다. 상기 수지 조성물은 추가적으로 용제, 광개시제 또는 열개시제, 산화방지제, UV 흡수제, 계면활성제 등을 더 포함할 수 있으나, 이에 한정되는 것은 아니다.The acrylate-based resin may be prepared by photopolymerizing or thermally polymerizing a resin composition including an alkyl group-containing (meth)acrylate-based monomer, a heterocycloalkyl group-containing (meth)acrylate-based monomer and a (meth)acrylic acid-based monomer. The resin composition may further include a solvent, a photoinitiator or thermal initiator, an antioxidant, a UV absorber, a surfactant, and the like, but is not limited thereto.

본 발명의 일 실시상태에 따르면, 상기 점착층의 두께는 5 ㎛ 이상 100 ㎛ 이하이고, 상기 유연층의 두께는 5 ㎛ 이상 200 ㎛ 이하일 수 있다. 상기 점착층의 두께와 상기 유연층의 두께가 상기 범위 내인 경우, 윈도우 데코 필름용 점착 시트가 우수한 부착성을 구현함과 동시에 우수한 접착력을 구현할 수 있다.According to an exemplary embodiment of the present invention, the thickness of the adhesive layer may be 5 μm or more and 100 μm or less, and the thickness of the flexible layer may be 5 μm or more and 200 μm or less. When the thickness of the adhesive layer and the thickness of the flexible layer are within the above ranges, the adhesive sheet for a window decoration film can implement excellent adhesion and at the same time realize excellent adhesion.

상기 점착층 상부에 배치되는 유연층은 중량평균분자량이 2,000 g/mol 이상 7,000 g/mol 이하인 폴리카보네이트계 우레탄 올리고머 및 사이클로알킬기 함유 (메트)아크릴레이트계 모노머를 포함하는 유연층 조성물의 경화물일 수 있으며, 상기 사이클로알킬기 함유 (메트)아크릴레이트계 모노머의 함량은 상기 유연층 조성물 100 중량부에 대하여 60 중량부 이상 80 중량부 이하일 수 있다. 본 발명의 일 실시상태에 따른 점착 시트는 상기 유연층을 포함함으로써, 우수한 부착성을 구현할 수 있다. 구체적으로, 윈도우 데코 필름의 인쇄층에 대하여 우수한 부착성을 구현할 수 있다.The flexible layer disposed on the adhesive layer is a cured product of a flexible layer composition comprising a polycarbonate-based urethane oligomer having a weight average molecular weight of 2,000 g/mol or more and 7,000 g/mol or less and a cycloalkyl group-containing (meth)acrylate-based monomer The content of the cycloalkyl group-containing (meth)acrylate-based monomer may be 60 parts by weight or more and 80 parts by weight or less based on 100 parts by weight of the flexible layer composition. The pressure-sensitive adhesive sheet according to an embodiment of the present invention can implement excellent adhesion by including the flexible layer. Specifically, excellent adhesion to the printed layer of the window decoration film can be implemented.

본 발명의 일 실시상태에 따르면, 상기 유연층 조성물에 포함되는 폴리카보네이트계 우레탄 올리고머의 중량평균분자량은 2,000 g/mol 이상 7,000 g/mol 이하이다. 상기 폴리카보네이트계 우레탄 올리고머의 중량평균분자량은 구체적으로, 3000 g/mol 이상 6000 g/mol 이하, 4000 g/mol 이상 5000 g/mol 또는 4500 g/mol 이상 5500 g/mol 이하일 수 있다. 한편, 상기 폴리카보네이트계 우레탄 올리고머의 중량평균분자량이 2,000 g/mol 미만인 경우, 유연층이 소프트하여 끈적이는 성분이 묻어날 수 있다. 그리고, 상기 폴리카보네이트계 우레탄 올리고머의 중량평균분자량이 7,000 g/mol 초과인 경우에는 유연층이 하드하여 유연성이 떨어지므로 부착성이 저하될 수 있다. 즉, 상기 폴리카보네이트계 우레탄 올리고머의 중량평균분자량이 상기 범위를 만족하는 경우, 윈도우 데코 필름용 점착 시트는 우수한 부착성을 구현할 수 있다. 구체적으로, 인쇄층에 대하여 우수한 부착성을 구현할 수 있다.According to an exemplary embodiment of the present invention, the weight average molecular weight of the polycarbonate-based urethane oligomer included in the flexible layer composition is 2,000 g/mol or more and 7,000 g/mol or less. Specifically, the weight average molecular weight of the polycarbonate-based urethane oligomer may be 3000 g/mol or more and 6000 g/mol or less, 4000 g/mol or more and 5000 g/mol or 4500 g/mol or more and 5500 g/mol or less. On the other hand, when the weight average molecular weight of the polycarbonate-based urethane oligomer is less than 2,000 g/mol, the flexible layer is soft and sticky components may be smeared. In addition, when the weight average molecular weight of the polycarbonate-based urethane oligomer is more than 7,000 g/mol, the flexible layer is hard and the flexibility is lowered, so adhesion may be reduced. That is, when the weight average molecular weight of the polycarbonate-based urethane oligomer satisfies the above range, the adhesive sheet for a window decoration film can implement excellent adhesion. Specifically, excellent adhesion to the printed layer can be realized.

본 발명의 일 실시상태에 따르면, 상기 사이클로알킬기 함유 (메트)아크릴레이트계 모노머의 함량은 상기 유연층 조성물 100 중량부 대비 60 중량부 이상 80 중량부 이하이다. 상기 사이클로알킬기 함유 (메트)아크릴레이트계 모노머의 함량은 구체적으로, 상기 유연층 조성물 100 중량부 대비 60 중량부 이상 70 중량부 이하, 70 중량부 이상 80 중량부 이하 또는 65 중량부 이상 75 중량부 이하일 수 있다. 한편, 상기 사이클로알킬기 함유 (메트)아크릴레이트계 모노머의 함량이 60 중량부 미만인 경우에는 유연층이 하드하여 유연성이 떨어지므로 곡면 기재에 대한 부착성이 저하될 수 있다. 또한, 상기 사이클로알킬기 함유 (메트)아크릴레이트계 모노머의 함량이 80 중량부 초과인 경우에는 중량평균분자량이 작은 모노머가 과량 포함됨으로써 유연층이 너무 소프트하여 끈적이는 성분이 묻어날 수 있다. 즉, 상기 사이클로알킬기 함유 (메트)아크릴레이트계 모노머의 함량이 상기 범위 내인 경우, 상기 유연층 조성물에 상기 폴리카보네이트계 우레탄 올리고머에 비하여 중량평균분자량이 작은 모노머가 다량 포함됨으로써 유연층이 소프트해져 윈도우 데코 필름용 점착 시트가 우수한 부착성을 구현할 수 있다. 구체적으로, 곡면 기재에 대해서도 우수한 부착성을 구현할 수 있다.According to an exemplary embodiment of the present invention, the content of the cycloalkyl group-containing (meth)acrylate-based monomer is 60 parts by weight or more and 80 parts by weight or less based on 100 parts by weight of the flexible layer composition. Specifically, the content of the cycloalkyl group-containing (meth)acrylate-based monomer is 60 parts by weight or more and 70 parts by weight or less, 70 parts by weight or more and 80 parts by weight or more, or 65 parts by weight or more and 75 parts by weight based on 100 parts by weight of the flexible layer composition. may be below. On the other hand, when the content of the cycloalkyl group-containing (meth)acrylate-based monomer is less than 60 parts by weight, the flexible layer is hard and the flexibility is lowered, so that adhesion to the curved substrate may be reduced. In addition, when the content of the cycloalkyl group-containing (meth)acrylate-based monomer is more than 80 parts by weight, an excessive amount of a monomer having a small weight average molecular weight is included, so that the flexible layer is too soft and a sticky component may be smeared. That is, when the content of the cycloalkyl group-containing (meth)acrylate-based monomer is within the above range, the flexible layer composition contains a large amount of a monomer having a small weight average molecular weight compared to the polycarbonate-based urethane oligomer in the flexible layer composition, so that the flexible layer becomes soft. An adhesive sheet for a decorative film can implement excellent adhesion. Specifically, excellent adhesion to a curved substrate may be implemented.

본 발명의 일 실시상태에 따르면, 상기 사이클로알킬기 함유 (메트)아크릴레이트계 모노머는 사이클로헥실(메트)아크릴레이트, 이소보르닐(메트)아크릴레이트, 3,3,5-트리메틸시클로헥실아크릴레이트 및 아크릴로일모르폴린 중에서 선택된 1종 이상일 수 있다. 또한, 상기 사이클로알킬기 함유 (메트)아크릴레이트계 모노머를 대신하여, 유리전이온도가 높은 모노머인 N-(2-히드록시프로필) 메타크릴레이트 또는 메틸메타크릴레이트가 이용될 수 있다.According to an exemplary embodiment of the present invention, the cycloalkyl group-containing (meth) acrylate-based monomer is cyclohexyl (meth) acrylate, isobornyl (meth) acrylate, 3,3,5-trimethylcyclohexyl acrylate and It may be at least one selected from acryloylmorpholine. In addition, instead of the cycloalkyl group-containing (meth)acrylate-based monomer, N-(2-hydroxypropyl) methacrylate or methyl methacrylate, which is a monomer having a high glass transition temperature, may be used.

본 발명의 일 실시상태에 따르면, 상기 사이클로알킬기 함유 (메트)아크릴레이트계 모노머의 유리전이온도는 60 ℃ 이상 100 ℃ 이하일 수 있다. 구체적으로, 60 ℃ 이상 90 ℃ 이하 또는 60 ℃ 이상 80 ℃ 이하일 수 있다. 상기 사이클로알킬기 함유 (메트)아크릴레이트계 모노머의 유리전이온도가 상기 범위 내인 경우, 윈도우 데코 필름용 점착 시트의 몰딩층 평가가 좋을 뿐만 아니라 우수한 부착성을 구현할 수 있다.According to an exemplary embodiment of the present invention, the glass transition temperature of the cycloalkyl group-containing (meth)acrylate-based monomer may be 60 ℃ or more and 100 ℃ or less. Specifically, it may be 60 °C or more and 90 °C or less, or 60 °C or more and 80 °C or less. When the glass transition temperature of the cycloalkyl group-containing (meth)acrylate-based monomer is within the above range, not only good evaluation of the molding layer of the adhesive sheet for window decoration film but also excellent adhesion can be realized.

본 발명의 일 실시상태에 따르면, 상기 폴리카보네이트계 우레탄 올리고머의 함량은 상기 유연층 조성물 100 중량부 대비 20 중량부 이상 40 중량부 이하일 수 있다. 상기 폴리카보네이트계 우레탄 올리고머의 함량은 구체적으로, 유연층 조성물 100 중량부 대비 30 중량부 이상 40 중량부 이하, 20 중량부 이상 30 중량부 이하 또는 25 중량부 이상 35 중량부 이하일 수 있다. 상기 폴리카보네이트계 우레탄 올리고머의 함량이 상기 범위 내인 경우, 유연층이 소프트하여 윈도우 데코 필름용 점착 시트의 몰딩층 코팅 평가가 좋을 뿐만 아니라 우수한 부착성을 구현할 수 있다.According to an exemplary embodiment of the present invention, the content of the polycarbonate-based urethane oligomer may be 20 parts by weight or more and 40 parts by weight or less based on 100 parts by weight of the flexible layer composition. Specifically, the content of the polycarbonate-based urethane oligomer may be 30 parts by weight or more and 40 parts by weight or less, 20 parts by weight or more and 30 parts by weight or less, or 25 parts by weight or more and 35 parts by weight or less, based on 100 parts by weight of the flexible layer composition. When the content of the polycarbonate-based urethane oligomer is within the above range, the flexible layer is soft, so that the molding layer coating evaluation of the adhesive sheet for a window decoration film is good and excellent adhesion can be implemented.

본 발명의 일 실시상태에 따르면, 상기 폴리카보네이트계 우레탄 올리고머는 폴리카보네이트 디올 및 디이소시아네이트계 화합물을 포함하는 조성물의 중합물일 수 있다. 구체적으로, 상기 폴리카보네이트계 우레탄 올리고머는 상기 구성성분들이 우레탄 결합에 의하여 공중합된 화합물일 수 있다.According to an exemplary embodiment of the present invention, the polycarbonate-based urethane oligomer may be a polymer of a composition including a polycarbonate diol and a diisocyanate-based compound. Specifically, the polycarbonate-based urethane oligomer may be a compound in which the components are copolymerized by a urethane bond.

본 발명의 일 실시상태에서 사용되는 폴리카보네이트계 우레탄 올리고머는 우수한 내습열성을 가져 유연층의 강도를 일정하게 유지시킬 수 있으므로, 본 발명의 일 실시상태에 따른 점착 시트는 우수한 부착성을 구현할 수 있다.Since the polycarbonate-based urethane oligomer used in an exemplary embodiment of the present invention has excellent heat-and-moisture resistance and can maintain the strength of the flexible layer constant, the pressure-sensitive adhesive sheet according to an exemplary embodiment of the present invention can implement excellent adhesion .

본 발명의 일 실시상태에 따르면, 상기 폴리카보네이트 디올은 디올과 카보네이트류를 반응시켜 얻어질 수 있다. 상기 디올류는 예를 들면, 에틸렌글리콜, 프로필렌글리콜, 1,3-프로판디올, 1,4-부탄디올, 1,5-펜탄디올, 3-메틸-1,5-펜탄디올, 1,6-헥산디올, 1,9-노난디올, 1,8-노난디올, 네오펜틸글리콜, 디에틸렌글리콜, 디프로필렌글리콜, 1,4-시클로헥산디올, 1,4-시클로헥산디메탄올, 비스페놀-A 등일 수 있다. 또한, 상기 카보네이트류는 예를 들면, 디메틸카보네이트, 디페닐카보네이트, 에틸렌카보네이트, 포스겐 등일 수 있다.According to an exemplary embodiment of the present invention, the polycarbonate diol may be obtained by reacting a diol with carbonates. The diol is, for example, ethylene glycol, propylene glycol, 1,3-propanediol, 1,4-butanediol, 1,5-pentanediol, 3-methyl-1,5-pentanediol, 1,6-hexane diol, 1,9-nonanediol, 1,8-nonanediol, neopentyl glycol, diethylene glycol, dipropylene glycol, 1,4-cyclohexanediol, 1,4-cyclohexanedimethanol, bisphenol-A, etc. have. In addition, the carbonates may be, for example, dimethyl carbonate, diphenyl carbonate, ethylene carbonate, phosgene, and the like.

본 발명의 일 실시상태에 따르면, 상기 디이소시아네이트계 화합물은 예를 들면, 4,4-디페닐메탄디이소시아네이트, 크실릴렌디이소시아네이트, 이소포론디이소시아네이트(IPDI), 4,4-디시클로헥실메탄디이소시아네이트, 1,3-시클로헥산비스메틸이소시아네이트, 헥사메틸렌디이소시아네이트, 2,2,4-트리메틸헥사메틸렌디이소시아네이트 등일 수 있다.According to an exemplary embodiment of the present invention, the diisocyanate-based compound is, for example, 4,4-diphenylmethane diisocyanate, xylylene diisocyanate, isophorone diisocyanate (IPDI), 4,4-dicyclohexylmethane diisocyanate, 1,3-cyclohexanebismethyl isocyanate, hexamethylene diisocyanate, 2,2,4-trimethylhexamethylene diisocyanate, and the like.

본 발명의 다른 실시상태는, 이형 필름; 본 발명의 일 실시상태에 따른 윈도우 데코 필름용 점착 시트; 인쇄층 및 보호 필름이 순차적으로 적층된 것을 포함하는 윈도우 데코 필름을 제공할 수 있다. 상기 윈도우 데코 필름은 상기 윈도우 데코 필름용 점착 시트의 우수한 점착 성능으로 인하여, 커브 곡률이 높은 유리에 부착하여도 박리되지 않을 수 있다.Another embodiment of the present invention is a release film; Adhesive sheet for window decoration film according to an embodiment of the present invention; It is possible to provide a window decoration film comprising a printed layer and a protective film sequentially laminated. Due to the excellent adhesive performance of the adhesive sheet for the window decoration film, the window decoration film may not be peeled off even when attached to a glass having a high curved curvature.

상기 점착 시트는 이형 필름 상에 상기 점착층 조성물 및 유연층 조성물을 순차적으로 도포하고 한번에 경화하여 제조할 수 있다.The pressure-sensitive adhesive sheet may be prepared by sequentially applying the pressure-sensitive adhesive layer composition and the flexible layer composition on a release film and curing the composition at once.

상기 윈도우 데코 필름은 상기 윈도우 데코필름용 점착 시트를 이형 필름에 해당하는 PET 시트 상부에 합지하고, 데코필름용 점착 시트 상부에 인쇄층에 해당하는 다른 PET 시트를 추가로 합지한 후, 조사에너지가 1000 mJ/cm2인 광으로 3 분 내지 7 분 동안 광경화하여 형성될 수 있다.In the window decoration film, the adhesive sheet for the window decoration film is laminated on the PET sheet corresponding to the release film, and another PET sheet corresponding to the printing layer is additionally laminated on the top of the adhesive sheet for decoration film. 1000 mJ/cm 2 It may be formed by photocuring with light of 3 to 7 minutes.

상기 윈도우 데코 필름은 커브 구조의 유리 기판 및 플렉서블 디스플레이의 폴리이미드 기판 상에 부착하여 사용할 수 있다.The window decoration film may be used by attaching it to a curved glass substrate and a polyimide substrate of a flexible display.

이하, 본 발명을 구체적으로 설명하기 위해 실시예를 들어 상세하게 설명하기로 한다. 그러나, 본 발명에 따른 실시예들은 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 아래에서 기술하는 실시예들에 한정되는 것으로 해석되지 않는다. 본 명세서의 실시예들은 당업계에서 평균적인 지식을 가진 자에게 본 발명을 보다 완전하게 설명하기 위해 제공되는 것이다.Hereinafter, examples will be given to describe the present invention in detail. However, the embodiments according to the present invention may be modified in various other forms, and the scope of the present invention is not to be construed as being limited to the embodiments described below. The embodiments of the present specification are provided to more completely explain the present invention to those of ordinary skill in the art.

실시예Example 1 One

2-에틸헥실아크릴레이트(2-EHA) 모노머 100 중량부, 테트라하이드로퍼퓨릴메타크릴레이트(THFMA) 모노머 14.3 중량부, 아크릴산(AA) 모노머 4.8 중량부 및 광개시제 0.1 중량부를 포함하는 조성물을 조사에너지가 1000mJ/cm2인 광으로 5 분 동안 광중합시켜 아크릴레이트계 수지를 제조하였다. 상기 아크릴레이트계 수지의 유리전이온도는 - 50 ℃ 이었다A composition comprising 100 parts by weight of a 2-ethylhexyl acrylate (2-EHA) monomer, 14.3 parts by weight of a tetrahydrofurfuryl methacrylate (THFMA) monomer, 4.8 parts by weight of an acrylic acid (AA) monomer, and 0.1 parts by weight of a photoinitiator was irradiated with energy An acrylate-based resin was prepared by photopolymerization with light of 1000mJ/cm 2 for 5 minutes. The glass transition temperature of the acrylate-based resin was -50 °C.

상기 아크릴레이트계 수지 30 중량부, 희석 모노머로서 2-EHA, THFMA 및 AA를 각각 58.8 중량부, 8.4, 및 2.8 중량부, 경화제로서 HDDA 0.2 중량부, 광개시제로서 이르가큐어 651 0.1 중량부를 포함하는 점착층 조성물을 제조하였다.30 parts by weight of the acrylate-based resin, 58.8 parts by weight, 8.4, and 2.8 parts by weight of 2-EHA, THFMA and AA as a diluting monomer, 0.2 parts by weight of HDDA as a curing agent, and 0.1 parts by weight of Irgacure 651 as a photoinitiator An adhesive layer composition was prepared.

중량평균분자량이 약 1150 g/mol인 폴리카보네이트 디올 1 당량에 대하여 이소포론 디이소시아네이트(IPDI)를 2 당량 첨가한 후 70 ℃에서 8 시간 동안 열중합하여, 중량평균분자량이 5,000 g/mol인 폴리카보네이트계 우레탄 올리고머를 제조하였다.After adding 2 equivalents of isophorone diisocyanate (IPDI) to 1 equivalent of polycarbonate diol having a weight average molecular weight of about 1150 g/mol, thermal polymerization was performed at 70° C. for 8 hours. Polycarbonate having a weight average molecular weight of 5,000 g/mol A urethane-based oligomer was prepared.

상기 폴리카보네이트계 우레탄 올리고머 20 중량부, 사이클로헥실메타크릴레이트(CHMA) 모노머 80 중량부, 경화제로서 1,6-헥산디올디아크릴레이트(HDDA) 0.2 중량부, 및 광개시제로서 이르가큐어 651 0.1 중량부를 포함하는 유연층 조성물을 제조하였다.20 parts by weight of the polycarbonate-based urethane oligomer, 80 parts by weight of a cyclohexyl methacrylate (CHMA) monomer, 0.2 parts by weight of 1,6-hexanediol diacrylate (HDDA) as a curing agent, and 0.1 parts by weight of Irgacure 651 as a photoinitiator A flexible layer composition comprising parts was prepared.

이형 PET 상에 상기 유연층 조성물 및 점착층 조성물을 순차적으로 도포하고 점착층 조성물 상에 이형 PET를 올린 후 한번에 조사에너지가 1000mJ/cm2인 광으로 5 분 동안 광경화하여, 윈도우 데코 필름용 점착 시트를 포함하는 이형 PET/유연층/점착층/이형 PET를 제조하였다.The flexible layer composition and the adhesive layer composition are sequentially applied on the release PET, and the release PET is placed on the adhesive layer composition, and then photocured for 5 minutes with light having an irradiation energy of 1000 mJ/cm 2 at a time. A release PET/flexible layer/adhesive layer/release PET including a sheet was prepared.

상기 점착층은 두께가 28 ㎛이었고, 상기 유연층은 두께가 52 ㎛이었다.The adhesive layer had a thickness of 28 μm, and the flexible layer had a thickness of 52 μm.

실시예Example 2 2

실시예 1에서 상기 점착층의 두께와 유연층의 두께를 각각 25 ㎛ 및 50 ㎛로 조절한 것을 제외하고, 실시예 1과 동일한 방법으로 윈도우 데코 필름용 점착 시트를 제조하였다.An adhesive sheet for a window decoration film was prepared in the same manner as in Example 1, except that in Example 1, the thickness of the adhesive layer and the thickness of the flexible layer were adjusted to 25 μm and 50 μm, respectively.

비교예comparative example 1 One

실시예 1에서 상기 점착층의 두께와 유연층의 37.5 ㎛ 및 37.5 ㎛로 조절한 것을 제외하고, 실시예 1과 동일한 방법으로 윈도우 데코 필름용 점착 시트를 제조하였다.An adhesive sheet for a window decoration film was prepared in the same manner as in Example 1, except that the thickness of the adhesive layer and 37.5 μm and 37.5 μm of the flexible layer were adjusted in Example 1.

비교예comparative example 2 2

실시예 1에서 2-에틸헥실아크릴레이트(2-EHA) 모노머 100 중량부, 테트라하이드로퍼퓨릴메타크릴레이트(THFMA) 모노머 13.3 중량부, 아크릴산(AA) 모노머 20 중량부 및 광개시제를 포함하는 조성물을 광중합시켜 유리전이온도가 - 20 ℃인 아크릴레이트계 수지를 제조한 것을 제외하고, 실시예 1과 동일한 방법으로 윈도우 데코 필름용 점착 시트를 제조하였다.In Example 1, a composition comprising 100 parts by weight of a 2-ethylhexyl acrylate (2-EHA) monomer, 13.3 parts by weight of a tetrahydrofurfuryl methacrylate (THFMA) monomer, 20 parts by weight of an acrylic acid (AA) monomer and a photoinitiator was prepared. An adhesive sheet for a window decoration film was prepared in the same manner as in Example 1, except that an acrylate-based resin having a glass transition temperature of −20° C. was prepared by photopolymerization.

부착성adherence 평가 evaluation

실시예 1, 2 및 비교예 1, 2의 점착 시트(크기: 가로 * 세로 = 20 cm * 20 cm)의 유연층 상에 몰딩액(KDP1002D, KCC社)을 도포하고, 광경화하여 20 ㎛ 두께의 몰딩층을 형성하였다. 그 후, 몰딩층을 ASTM D3359에 맞추어 크로스컷터(Crosscutter)를 커팅가이드로 이용하여, 몰딩층에 100칸의 격자를 칼질한 다음 Nichiban Tape로 격자를 제거하는 크로스 컷 방법을 통해 몰딩층이 유연층에서 떨어지는지 여부를 확인하여, 부착성을 평가하였다.A molding solution (KDP1002D, KCC) was applied on the flexible layer of the adhesive sheets (size: width * length = 20 cm * 20 cm) of Examples 1 and 2 and Comparative Examples 1 and 2, and photocured to a thickness of 20 μm of the molding layer was formed. After that, the molding layer is aligned with ASTM D3359 and using a cross cutter as a cutting guide, 100 grids are cut on the molding layer and then the grid is removed with Nichiban Tape. It was checked whether it fell off, and the adhesion was evaluated.

○: 몰딩층이 떨어지지 않음○: Molding layer does not fall off

Ⅹ: 몰딩층이 유연층에서 전부 떨어짐X: The molding layer is completely removed from the flexible layer

박리력peel force 평가 evaluation

실시예 1, 2 및 비교예 1, 2에서 제조한 점착 시트의 점착층이 1.1 T 두께의 유리 기재에 부착되도록, 2 kg 롤러를 이용하여 부착하고, 오토클레이브(60 ℃, 7 bar)에 30 분간 방치 후에, 25 ℃, 25 RH%의 항온항습 조건에서 박리 각도를 180 °로 하여 ASTM D903에 의하여 박리력을 측정하였다. Examples 1 and 2 and Comparative Examples 1 and 2 were attached using a 2 kg roller so that the pressure-sensitive adhesive layer of the pressure-sensitive adhesive sheet prepared in Examples 1 and 2 was attached to a glass substrate having a thickness of 1.1 T, and placed in an autoclave (60 ° C., 7 bar) for 30 minutes. After standing for a minute, the peeling force was measured according to ASTM D903 at a peel angle of 180° under constant temperature and humidity conditions of 25° C. and 25 RH%.

박리력이 2,000 gf/in 이상인 경우 ○, 2,000 gf/in 이하인 경우 Ⅹ로 나타내어 박리력을 평가하였다.When the peeling force is 2,000 gf/in or more, it is indicated by ○, and when it is 2,000 gf/in or less, it is indicated by X to evaluate the peeling force.

백탁cloudiness 방지 성능 평가 Prevention performance evaluation

실시예 1, 2 및 비교예 1, 2에서 제조한 점착 시트의 점착층이 1.1 T 두께의 유리 기재에 부착되도록, 2 kg 롤러를 이용하여 부착하고, 오토클레이브(40 ℃, 4 bar)에 20 분간 방치 후에, 80 ℃, 85 RH%의 항온항습기에 투입한 후, 3 일 후 꺼냈을 시 백탁이 생기지 않는 경우 ○, 생기는 경우 Ⅹ로 백탁 방지 성능을 평가하였다.Examples 1 and 2 and Comparative Examples 1 and 2 were attached using a 2 kg roller so that the adhesive layer of the pressure-sensitive adhesive sheet was attached to a glass substrate having a thickness of 1.1 T, and placed in an autoclave (40 ° C., 4 bar) for 20 After leaving for a minute, it was put into a thermo-hygrostat at 80 ° C. and 85 RH%, and when taken out after 3 days, the anti-clouding performance was evaluated as ○ if cloudiness did not occur and X if it occurred.

상기 실시예 1, 2 및 비교예 1, 2에 따른 점착 시트의 물성을 평가하여, 하기 표 1에 나타내었다.The physical properties of the adhesive sheets according to Examples 1 and 2 and Comparative Examples 1 and 2 were evaluated, and are shown in Table 1 below.

점착층과 유연층의 두께 비Thickness ratio of adhesive layer and flexible layer 아크릴레이트계 수지의 유리전이온도
(℃)Glass transition temperature of acrylate-based resins
(℃) 부착성adherence 박리력peel force 백탁 방지 성능Anti-whitening performance 실시예 1Example 1 2:32:3 - 50- 50 ○○ ○○ ○○ 실시예 2Example 2 1:21:2 - 50- 50 ○○ ○○ ○○ 비교예 1Comparative Example 1 1:11:1 - 50- 50 ⅩⅩ ○○ ○○ 비교예 2Comparative Example 2 2:32:3 - 20- 20 ○○ ⅩⅩ ○○

상기 표 1에 나타난 바와 같이, 상기 실시예 1, 2의 점착 시트는 백탁 방지 성능을 유지하면서 부착성 및 박리력도 우수한 것을 확인할 수 있었다.As shown in Table 1, it was confirmed that the adhesive sheets of Examples 1 and 2 were excellent in adhesion and peel strength while maintaining anti-fogging performance.

이에 비하여, 비교예 1의 경우에는 점착층과 유연층의 두께 비가 2:3 내지 1:2의 범위를 벗어나므로 즉, 유연층의 두께가 점착층에 비하여 얇으므로 부착성이 우수하지 않은 것을 확인할 수 있었다. 또한, 아크릴레이트계 수지의 유리전이온도가 - 30 ℃를 초과하는 비교예 2의 경우에는 점착층이 하드하여 표면의 점성이 사라져 박리력 즉, 접착력이 우수하지 않은 것을 확인할 수 있었다.On the other hand, in the case of Comparative Example 1, since the thickness ratio of the adhesive layer and the flexible layer is out of the range of 2:3 to 1:2, that is, since the thickness of the flexible layer is thinner than that of the adhesive layer, it is confirmed that the adhesion is not excellent. could In addition, in the case of Comparative Example 2, in which the glass transition temperature of the acrylate-based resin exceeds -30 ° C., it was confirmed that the adhesive layer was hard and the surface viscosity was lost and the peeling force, ie, the adhesive force, was not excellent.

따라서, 본 발명에 따른 윈도우 데코 필름용 점착 시트는 점착 성능이 우수한 것을 알 수 있다. 구체적으로, 곡면 기재에 대한 접착력 및 인쇄층에 대한 부착성이 우수한 것을 알 수 있다.Therefore, it can be seen that the adhesive sheet for a window decoration film according to the present invention has excellent adhesive performance. Specifically, it can be seen that the adhesion to the curved substrate and the adhesion to the printed layer are excellent.

Claims (8)

점착층; 및 상기 점착층 상부에 배치되는 유연층을 포함하고,
상기 점착층은 유리전이온도가 - 50 ℃ 이상 - 30 ℃ 이하인 아크릴레이트계 수지를 포함하는 점착층 조성물의 경화물이며,
상기 아크릴레이트계 수지는 알킬기 함유 (메트)아크릴레이트계 모노머, 헤테로사이클로알킬기 함유 (메트)아크릴레이트계 모노머 및 (메트)아크릴산계 모노머를 포함하는 수지 조성물의 중합체이고,
상기 (메트)아크릴산계 모노머는 상기 알킬기 함유 (메트)아크릴레이트계 모노머 100 중량부에 대하여 1 중량부 이상 12 중량부 이하이며,
상기 점착층 두께와 상기 유연층 두께의 비는 2:3 내지 1:2인 윈도우 데코 필름용 점착 시트.
adhesive layer; and a flexible layer disposed on the adhesive layer,
The adhesive layer is a cured product of an adhesive layer composition comprising an acrylate-based resin having a glass transition temperature of -50 ℃ or more - 30 ℃ or less,
The acrylate-based resin is a polymer of a resin composition comprising an alkyl group-containing (meth)acrylate-based monomer, a heterocycloalkyl group-containing (meth)acrylate-based monomer, and a (meth)acrylic acid-based monomer,
The (meth)acrylic acid-based monomer is 1 part by weight or more and 12 parts by weight or less based on 100 parts by weight of the alkyl group-containing (meth)acrylate-based monomer,
The ratio of the thickness of the adhesive layer to the thickness of the flexible layer is 2:3 to 1:2. An adhesive sheet for a window decoration film.
 제1항에 있어서,
상기 헤테로사이클로알킬기 함유 (메트)아크릴레이트계 모노머는 상기 알킬기 함유 (메트)아크릴레이트계 모노머 100 중량부에 대하여 3 중량부 이상 15 중량부 이하인 윈도우 데코 필름용 점착 시트.
According to claim 1,
The heterocycloalkyl group-containing (meth)acrylate-based monomer is 3 parts by weight or more and 15 parts by weight or less based on 100 parts by weight of the alkyl group-containing (meth)acrylate-based monomer.
 삭제delete 제1항에 있어서,
상기 알킬기 함유 (메트)아크릴레이트계 모노머는 메틸(메트)아크릴레이트 모노머, 에틸(메트)아크릴레이트 모노머, n-프로필(메트)아크릴레이트 모노머, 이소프로필(메트)아크릴레이트 모노머, n-부틸(메트)아크릴레이트 모노머, t-부틸(메트)아크릴레이트 모노머, sec-부틸(메트)아크릴레이트 모노머, 펜틸(메트)아크릴레이트 모노머, 2-에틸헥실(메트)아크릴레이트 모노머, 2-에틸부틸(메트)아크릴레이트 모노머, n-옥틸(메트)아크릴레이트 모노머, 및 이소옥틸(메트)아크릴레이트 모노머 중에서 선택된 1종 이상인 윈도우 데코 필름용 점착 시트.
According to claim 1,
The alkyl group-containing (meth) acrylate-based monomer is a methyl (meth) acrylate monomer, an ethyl (meth) acrylate monomer, an n-propyl (meth) acrylate monomer, an isopropyl (meth) acrylate monomer, n-butyl ( Meth) acrylate monomer, t-butyl (meth) acrylate monomer, sec-butyl (meth) acrylate monomer, pentyl (meth) acrylate monomer, 2-ethylhexyl (meth) acrylate monomer, 2-ethyl butyl ( Meth) acrylate monomer, n-octyl (meth) acrylate monomer, and isooctyl (meth) acrylate monomer selected from at least one type of adhesive sheet for a window decoration film.
 제1항에 있어서,
상기 헤테로사이클로알킬기 함유 (메트)아크릴레이트계 모노머는 테트라하이드로퍼퓨릴(메트)아크릴레이트 모노머, 테트라하이드로피라닐(메트)아크릴레이트 모노머, 아크릴로일모르폴린 모노머 및 사이클릭트리메틸올프로판포말아크릴레이트 모노머 중에서 선택된 1종 이상인 윈도우 데코 필름용 점착 시트.
According to claim 1,
The heterocycloalkyl group-containing (meth)acrylate-based monomer is a tetrahydrofurfuryl (meth)acrylate monomer, a tetrahydropyranyl (meth)acrylate monomer, an acryloylmorpholine monomer, and a cyclic trimethylolpropaneformal acrylate. Adhesive sheet for window decoration film of one or more selected from monomers.
 제1항에 있어서,
상기 (메트)아크릴산계 모노머는 아크릴산 모노머, 메타크릴산 모노머, 2-카르복시에틸아크릴산 모노머, 3-카르복시프로필아크릴산 모노머, 2-(메트)아크릴로일옥시아세트산 모노머, 3-(메트)아크릴로일옥시프로필산 모노머 및 4-(메트)아크릴로일옥시부틸산 모노머 중에서 선택된 1종 이상인 윈도우 데코 필름용 점착 시트.
According to claim 1,
The (meth)acrylic acid-based monomer is acrylic acid monomer, methacrylic acid monomer, 2-carboxyethylacrylic acid monomer, 3-carboxypropylacrylic acid monomer, 2-(meth)acryloyloxyacetic acid monomer, 3-(meth)acryloyl An adhesive sheet for a window decoration film of at least one selected from oxypropyl acid monomer and 4-(meth)acryloyloxybutyric acid monomer.
 제1항에 있어서,
상기 점착층의 두께는 5 ㎛ 이상 100 ㎛ 이하이고, 상기 유연층의 두께는 5 ㎛ 이상 200 ㎛ 이하인 윈도우 데코 필름용 점착 시트.
According to claim 1,
The thickness of the adhesive layer is 5 μm or more and 100 μm or less, and the thickness of the flexible layer is 5 μm or more and 200 μm or less.
 이형 필름; 제1항, 제2항, 제4항 내지 제7항 중 어느 한 항에 따른 윈도우 데코 필름용 점착 시트; 인쇄층; 및 보호 필름이 순차적으로 적층된 것을 포함하는 윈도우 데코 필름.
release film; The adhesive sheet for a window decoration film according to any one of claims 1, 2, and 4 to 7; printed layer; And a window decoration film comprising a sequentially laminated protective film.
KR1020180146495A 2018-11-23 2018-11-23 Adhesive sheet for window deco film and window deco film comprising the same KR102314948B1 (en)