KR102310125B1 - UV absorbent comprising microalgae extract and paint composition with excellent UV blocking capacity comprising the same - Google Patents
UV absorbent comprising microalgae extract and paint composition with excellent UV blocking capacity comprising the same Download PDFInfo
- Publication number
- KR102310125B1 KR102310125B1 KR1020190165685A KR20190165685A KR102310125B1 KR 102310125 B1 KR102310125 B1 KR 102310125B1 KR 1020190165685 A KR1020190165685 A KR 1020190165685A KR 20190165685 A KR20190165685 A KR 20190165685A KR 102310125 B1 KR102310125 B1 KR 102310125B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- microalgae
- water
- coating composition
- parts
- Prior art date
Abstract
본 발명은 미세조류 추출물을 포함하는 자외선 흡수제 및 이를 포함하는 자외선 차단 또는 흡수용 도료 조성물에 관한 것으로 일반적으로 투명색의 도막은 장시간 동안 자외선에 노출되면 황변이 발생하는데 본 발명에서는 이를 해결하기 위하여 미세조류 추출물을 포함하여 자외선에 대한 저항성을 높임으로써 투명색의 도막이 장시간 동안 자외선에 노출되더라도 황변 발생을 방지한다. The present invention relates to a UV absorber containing a microalgae extract and a coating composition for blocking or absorbing UV rays comprising the same. In general, when a transparent coating film is exposed to UV light for a long time, yellowing occurs. In order to solve this problem, in the present invention, microalgae By increasing the resistance to UV rays by including the extract, it prevents yellowing even when the transparent coating film is exposed to UV rays for a long time.
Description
본 발명은 장시간 동안 자외선에 노출되더라도 황변 발생을 방지할 수 있는 미세조류 추출물을 포함하는 자외선 흡수제 및 이를 포함하는 자외선 차단 또는 흡수용 도료 조성물에 관한 것이다.The present invention relates to a UV absorbent containing a microalgae extract capable of preventing yellowing even when exposed to UV light for a long time, and a UV blocking or absorbing coating composition comprising the same.
자외선(ultraviolet, UV)은 파장에 따라 장파장(320-400 nm)의 UV-A, 중파장(280-320 nm)의 UV-B, 단파장(200-280 nm)의 UV-C로 분류된다. 상기 UV-A는 파장 이 긴 광선으로 에너지는 약하지만 피부의 진피까지 도달하여 피부의 탄력을 감소시켜 주름을 생성시키는 만성 광노화의 원인이 된다. 또한, 상기 UV-B는 자외선 중에서 에너지가 가장 큰 광선으로 피부의 표피와 진피의 유두층까지 도달하여 피부를 태우는 등 즉각적인 반응을 일으키며 UV-B에 대한 직접적인 피부노출은 광노화, 홍반, 색소과다침착, 피부암을 유발한다. 또한, UV-C는 파장이 가장 짧은 광선으로 오존층에 의해 흡수되어 지표면에 도달하지 못하므로 피부에 큰 영향을 미치지 않는다. 따라서 UV-A와 UV-B가 사람에게 유해한 자외선으로 알려져 있다 Ultraviolet (UV) is classified into long-wavelength (320-400 nm) UV-A, medium-wavelength (280-320 nm) UV-B, and short-wavelength (200-280 nm) UV-C according to the wavelength. The UV-A is a light with a long wavelength, and although the energy is weak, it reaches the dermis of the skin and reduces the elasticity of the skin, causing chronic photoaging to generate wrinkles. In addition, the UV-B is the light with the greatest energy among ultraviolet rays, and it reaches the epidermis and papillary layer of the dermis and causes an immediate reaction such as burning the skin. Direct skin exposure to UV-B is photoaging, erythema, hyperpigmentation, cause skin cancer In addition, UV-C has the shortest wavelength and is absorbed by the ozone layer and does not reach the earth's surface, so it does not have a significant effect on the skin. Therefore, UV-A and UV-B are known as harmful UV rays to humans.
이러한 자외선은 사람에 피부를 노화시키기도 하지만 투명한 도막이 자외선에 장시간 노출되면 황변되어 도막의 성능이 저하되고 미관상 좋지 못하다.Although such ultraviolet rays can age the skin of humans, when the transparent coating film is exposed to ultraviolet rays for a long time, it turns yellow, and the performance of the coating film is deteriorated and the appearance is not good.
특히, 가정이나 자동차 유리를 통해 자외선이 유입되는 경우에는 가정집 실내 또는 자동차 실내에서 생활하는 사람의 피부 및 유리에 문제를 일으킬 수 있다.In particular, when ultraviolet rays are introduced through the glass of a home or automobile, it may cause a problem on the skin and glass of a person living in the interior of a home or automobile.
해양식물 중 해조류는 다양한 단백질과 다당류를 포함하고 풍부한 무기질과 비타민이 함유되어 있어 생리활성물질 생산을 위한 소재로 많은 관심을 받고 있다. Manou 등에 따르면 해조류는 육상 식물보다 우수한 항산화, 약리활성, 항종양, 항염증 및 면역조절을 포함한 다양한 생리활성물질 등을 포함하고 있다고 한다.Among marine plants, seaweeds are receiving a lot of attention as a material for the production of physiologically active substances, as they contain various proteins and polysaccharides and contain abundant minerals and vitamins. According to Manou et al., seaweed contains various physiologically active substances, including antioxidant, pharmacological activity, anti-tumor, anti-inflammatory and immunomodulatory properties, superior to land plants.
이러한 해조류의 생리활성 기능은 다당류와 단백질의 저분자 형태인 펩타이드에서 기인한다고 보고되고 있다. It is reported that these physiologically active functions of seaweed originate from polysaccharides and peptides, which are low molecular weight forms of proteins.
한편, 신재생 에너지의 필요성이 높아지면서 해조류의 한 종류인 미세조류는 지질 추출을 통해 바이오디젤을 생산하는 제3세대 바이오매스로 그 활용도가 높아지고 있다. Meanwhile, as the need for new and renewable energy increases, microalgae, a type of seaweed, is increasingly being used as a third-generation biomass that produces biodiesel through lipid extraction.
본 발명의 목적은 장시간 동안 자외선에 노출되더라도 황변 발생을 방지할 수 있는 미세조류 추출물을 포함하는 자외선 흡수제를 제공하는데 있다.It is an object of the present invention to provide a UV absorbent containing a microalgae extract capable of preventing yellowing even when exposed to UV light for a long time.
또한 본 발명의 다른 목적은 상기 자외선 흡수제를 포함하는 자외선 차단 또는 흡수용 도료 조성물을 제공하는데 있다.Another object of the present invention is to provide a coating composition for blocking or absorbing ultraviolet rays comprising the ultraviolet absorber.
상기한 목적을 달성하기 위한 본 발명의 도료 조성물용 자외선 흡수제는 미세조류(microalgae) 추출물을 포함할 수 있다.The ultraviolet absorbent for a coating composition of the present invention for achieving the above object may include a microalgae extract.
상기 미세조류는 세네데스무스(scenedesmus), 테트라셀미스, 스피루리나, 클로렐라 또는 식물성 플라크톤일 수 있다.The microalgae may be scenedesmus, tetraselmis, spirulina, chlorella or phytoplankton.
상기 미세조류 추출물은 미세조류와 추출용매를 1 : 10 내지 30의 중량비로 혼합하여 50 내지 80 ℃에서 20 내지 50분 동안 추출한 것일 수 있다.The microalgae extract may be obtained by mixing microalgae and an extraction solvent in a weight ratio of 1: 10 to 30 and extracting the microalgae at 50 to 80 ° C. for 20 to 50 minutes.
상기 추출용매는 탄소수 1 내지 4의 저급알코올, 아세톤, 에틸렌글리콜 또는 에틸에테르일 수 있으며, 바람직하게는 아세톤, 무수 에탄올 또는 무수 메탄올일 수 있다.The extraction solvent may be lower alcohol, acetone, ethylene glycol or ethyl ether having 1 to 4 carbon atoms, preferably acetone, absolute ethanol or anhydrous methanol.
또한, 상기한 다른 목적을 달성하기 위한 본 발명의 자외선 차단용 도료 조성물은 상기 자외선 흡수제를 포함할 수 있다.In addition, the coating composition for blocking ultraviolet rays of the present invention for achieving the above other object may include the ultraviolet absorber.
상기 도료 조성물은 수계형 폴리아크릴레이트 디스퍼젼 수지 및 미세조류 추출물을 포함하는 주제부와 폴리이소시아네이트를 포함하는 경화제부로 이루어진 것일 수 있다.The coating composition may be composed of a main part including a water-based polyacrylate dispersion resin and microalgae extract, and a curing agent part including polyisocyanate.
상기 미세조류 추출물은 수계형 폴리아크릴레이트 디스퍼젼 수지 100 중량부에 대하여 0.01 내지 5의 중량부로 함유될 수 있다.The microalgal extract may be contained in an amount of 0.01 to 5 parts by weight based on 100 parts by weight of the water-based polyacrylate dispersion resin.
일반적으로 투명색의 도막은 장시간 동안 자외선에 노출되면 황변이 발생하는데 본 발명에서는 이를 해결하기 위하여 미세조류 추출물을 포함하는 자외선 흡수제를 이용하여 자외선에 대한 저항성을 높임으로써 도료 조성물로 이용 시 투명색의 도막이 장시간 동안 자외선에 노출되더라도 황변이 발생되는 것을 방지한다. In general, when a transparent coating film is exposed to ultraviolet rays for a long time, yellowing occurs. In order to solve this problem, in the present invention, a ultraviolet absorbent containing a microalgae extract is used to increase the resistance to ultraviolet rays, so that when used as a paint composition, the transparent color film is maintained for a long time. It prevents yellowing from occurring even when exposed to UV light for a while.
또한, 본 발명의 미세조류 추출물을 포함하는 자외선 차단 또는 흡수용 도료 조성물은 투명한 도막을 형성하고, 부착성, 연필경도, 내스크래치성, 내습성, 내수성, 내열성 및 내약품성에 대하여 우수하므로 품질이 우수한 투명 도막을 형성할 수 있다.In addition, the coating composition for blocking or absorbing ultraviolet rays containing the microalgal extract of the present invention forms a transparent coating film, and is excellent in adhesion, pencil hardness, scratch resistance, moisture resistance, water resistance, heat resistance and chemical resistance. An excellent transparent coating film can be formed.
본 발명은 장시간 동안 자외선에 노출되더라도 황변 발생을 방지할 수 있는 미세조류 추출물을 포함하는 자외선 흡수제 및 이를 포함하는 자외선 차단 또는 흡수용 도료 조성물에 관한 것이다.The present invention relates to a UV absorbent containing a microalgae extract capable of preventing yellowing even when exposed to UV light for a long time, and a UV blocking or absorbing coating composition comprising the same.
이하, 본 발명을 상세하게 설명한다. Hereinafter, the present invention will be described in detail.
본 발명의 자외선 흡수제는 미세조류 추출물을 포함하여 자외선을 흡수하여 자외선에 대한 저항성을 높임으로써 도료 조성물에 이용 시 투명한 도막이 황변되는 현상을 방지할 뿐만 아니라 부착성 및 경도를 향상시킨다.The ultraviolet absorbent of the present invention, including the microalgae extract, absorbs ultraviolet rays to increase resistance to ultraviolet rays, thereby preventing yellowing of the transparent coating film when used in a paint composition, as well as improving adhesion and hardness.
미세조류(microalgae)는 바다에 서식하는 식물성 플랑크톤으로, 흔히 적조를 일으키는 코클로디니움 같은 플랑크톤 역시 미세조류에 속한다. 해양 바이오에너지 연구가 주목하는 미세조류는 특히 지질, 즉 기름성분이 풍부한 미세조류 종(種)이다. 크기는 10 μm(미크론, 1 m의 100만분의 1)정도로 머리카락 굵기의 10분의 1 안팎이다.Microalgae are phytoplankton that inhabit the sea. Microalgae that marine bioenergy research pays attention to are microalgae species rich in lipids, that is, oil components. Its size is about 10 μm (microns, one millionth of 1 m), about one-tenth the thickness of a human hair.
본 발명의 미세조류(microalgae)는 50 내지 70 ℃의 오븐에서 7 내지 10시간 동안 건조시켜 잔류수분을 제거하여 이용한다. 수분이 잔존하는 경우에는 미세조류 추출물에 수분이 남아있어 자외선 흡수율이 저하되고 부착성이 낮아질 수 있다.The microalgae of the present invention are dried in an oven at 50 to 70° C. for 7 to 10 hours to remove residual moisture. If moisture remains, moisture may remain in the microalgae extract, thereby lowering the UV absorption rate and lowering adhesion.
상기 미세조류 추출물은 미세조류와 추출용매를 1 : 10 내지 30의 중량비, 바람직하게는 1 : 15 내지 20의 중량비로 혼합하여 50 내지 80 ℃, 바람직하게는 60 내지 70 ℃에서 20 내지 50분, 바람직하게는 30 내지 40분 동안 추출한 것이다.The microalgal extract is obtained by mixing microalgae and an extraction solvent in a weight ratio of 1: 10 to 30, preferably 1: 15 to 20 by weight at 50 to 80 ° C., preferably at 60 to 70 ° C. for 20 to 50 minutes, It is preferably extracted for 30 to 40 minutes.
상기 미세조류와 추출용매의 중량비가 상기 범위를 벗어나는 경우에는 추출물에 유효성분이 적은 양으로 추출되어 자외선 흡수율이 저하될 수 있다. 또한 추출 시 온도 및 시간이 상기 하한치 미만인 경우에는 유효성분이 적은 양으로 추출되어 자외선 흡수율이 저하될 수 있으며, 상기 상한치 초과인 경우에는 목적물질 이외의 다른 물질이 다량으로 추출되어 자외선을 흡수하지 못할 수 있다. When the weight ratio of the microalgae and the extraction solvent is out of the above range, the active ingredient is extracted in a small amount in the extract, so that the ultraviolet absorption rate may be reduced. In addition, when the temperature and time during extraction are less than the lower limit, the active ingredient is extracted in a small amount and the UV absorption rate may be lowered. have.
상기 추출물을 추출하는 추출용매는 탄소수 1 내지 4의 저급알코올, 아세톤, 에틸렌글리콜 또는 에틸에테르를 들 수 있지만, 높은 차외선 흡수율을 위해서는 아세톤, 무수 에탄올 또는 무수 메탄올을 들 수 있다.The extraction solvent for extracting the extract may include lower alcohol, acetone, ethylene glycol or ethyl ether having 1 to 4 carbon atoms, but acetone, anhydrous ethanol or anhydrous methanol may be used for high UV absorption.
본 명세서에서 미세조류을 언급하면서 사용되는 용어 '추출물'은 추출용매를 처리하여 얻은 조추출물뿐만 아니라 미세조류의 가공물도 포함한다. 예를 들어, 미세조류는 감압 증류 및 동결 건조 또는 분무 건조 등과 같은 추가적인 과정에 의해 분말 상태로 제조될 수 있다.The term 'extract' used while referring to microalgae in the present specification includes not only the crude extract obtained by treating the extraction solvent, but also the processed product of the microalgae. For example, microalgae may be prepared in a powder state by additional processes such as vacuum distillation and freeze drying or spray drying.
또한, 본 발명은 상기 미세조류 추출물을 포함하는 자외선 흡수제를 포함하는 자외선 차단용 도료 조성물을 제공할 수 있다.In addition, the present invention may provide a coating composition for blocking ultraviolet rays comprising an ultraviolet absorbent containing the extract of microalgae.
상기 도료 조성물은 주제부와 경화제부로 이루어진 이액형의 우레탄계 도료 조성물이라면 특별히 한정되지 않는다.The coating composition is not particularly limited as long as it is a two-component urethane-based coating composition comprising a main part and a curing agent part.
일예로, 상기 주제부는 수계형 폴리아크릴레이트 디스퍼젼 수지, 미세조류 추출물, 표면장력 조절제, 레벨링제, 조용제, 증점제를 포함할 수 있다. 상기 미세조류 추출물은 수계형 폴리아크릴레이트 디스퍼젼 수지와 결합되어 자외선 흡수율 및 강도가 우수한 도막을 형성할 수 있다.For example, the main part may include a water-based polyacrylate dispersion resin, a microalgae extract, a surface tension control agent, a leveling agent, a co-solvent, and a thickener. The microalgal extract may be combined with a water-based polyacrylate dispersion resin to form a coating film having excellent UV absorption and strength.
이때 상기 미세조류 추출물은 수계형 폴리아크릴레이트 디스퍼젼 수지 100 중량부에 대하여 0.01 내지 5의 중량부, 바람직하게는 0.02 내지 3의 중량부로 포함된다. 미세조류 추출물의 함량이 상기 하한치 미만인 경우에는 자외선 흡수율, 부착성 및 경도가 저하될 수 있으며, 상기 상한치 초과인 경우에는 오히려 자외선 흡수율이 저하될 수 있다.At this time, the microalgal extract is included in an amount of 0.01 to 5 parts by weight, preferably 0.02 to 3 parts by weight, based on 100 parts by weight of the water-based polyacrylate dispersion resin. When the content of the microalgal extract is less than the lower limit, the UV absorption rate, adhesion and hardness may be lowered, and if it exceeds the upper limit, the UV absorption rate may be rather reduced.
상기 수계형 폴리아크릴레이트 디스퍼젼 수지는 수평균 분자량이 50,000 내지 100,000이고, 고형분 함량이 45~60 중량%이며, pH가 5~9 범위이고, 점도가 1,000~4,000 mPa.s(23 ℃)이며, 히드록실기 함량이 고형분 기준으로 3 내지 5중량%인 것이다. 상기 수계형 폴리아크릴레이트 디스퍼젼 수지의 수평균 분자량이 상기 하한치 미만인 경우에는 내수성 및 부착성이 저하되고, 상기 상한치 초과인 경우에는 높은 점도로 인해 도료의 레올로지 제어가 어려운 문제가 초래된다. The water-based polyacrylate dispersion resin has a number average molecular weight of 50,000 to 100,000, a solid content of 45 to 60% by weight, a pH of 5 to 9, and a viscosity of 1,000 to 4,000 mPa.s (23 ° C.) , the hydroxyl group content is 3 to 5% by weight based on the solid content. When the number average molecular weight of the water-based polyacrylate dispersion resin is less than the lower limit, water resistance and adhesion are reduced, and when it exceeds the upper limit, it is difficult to control the rheology of the paint due to high viscosity.
또한, 상기 수계형 폴리아크릴레이트 디스퍼젼 수지의 고형분 함량이 상기 하한치 미만인 경우에는 도막의 내화학성이 나빠질 문제가 있고, 상기 상한치 초과인 경우에는 도료 가격 상승과 은폐 저하의 문제가 초래된다. In addition, when the solid content of the water-based polyacrylate dispersion resin is less than the lower limit, there is a problem in that the chemical resistance of the coating film is deteriorated.
뿐만 아니라, 상기 수계형 폴리아크릴레이트 디스퍼젼 수지의 pH가 5~9 범위를 벗어날 경우 안정성이 떨어지는 문제가 있고; 수계형 폴리아크릴레이트 디스퍼젼 수지의 점도가 상기 하한치 미만인 경우에는 역시 수직면에서 흘러내릴 문제가 있고, 상기 상한치 초과인 경우에는 오렌지필이 발생할 문제가 있다. In addition, when the pH of the water-based polyacrylate dispersion resin is out of the range of 5 to 9, there is a problem of poor stability; When the viscosity of the water-based polyacrylate dispersion resin is less than the lower limit, there is also a problem of flowing down on the vertical plane, and when the viscosity is greater than the upper limit, there is a problem that orange peel occurs.
또한, 상기 수계형 폴리아크릴레이트 디스퍼젼 수지의 히드록실기 함량이 고형분 기준으로 상기 하한치 미만인 경우에는 가교밀도 저하에 따른 부착 불량과 내굴곡성이 저하될 수 있고, 상기 상한치 초과인 경우에는 도료 가격이 상승하고 건조가 지연되는 문제점이 있다.In addition, when the hydroxyl group content of the water-based polyacrylate dispersion resin is less than the lower limit on the basis of the solid content, adhesion failure and bending resistance may be reduced due to a decrease in crosslinking density. There is a problem that rises and the drying is delayed.
상기 표면장력 조절제는 소재 웨팅성을 위하여 사용되는 것으로서, 종래에 사용되는 표면장력 조절제라면 특별히 한정되지 않는다. 상기 표면장력 조절제의 함량은 수계형 폴리아크릴레이트 디스퍼젼 수지 100 중량부에 대하여 0.2 내지 2 중량부로서, 표면장력 조절제의 함량이 상기 하한치 미만인 경우에는 첨가제 본연의 기능이 나타나기 어렵고, 상기 상한치 초과인 경우에는 크레이터 등의 현상이 발생된다.The surface tension control agent is used for material wetting, and is not particularly limited as long as it is a conventionally used surface tension control agent. The content of the surface tension regulator is 0.2 to 2 parts by weight based on 100 parts by weight of the water-based polyacrylate dispersion resin, and when the content of the surface tension regulator is less than the lower limit, it is difficult to show the original function of the additive, and the upper limit In this case, a phenomenon such as a crater occurs.
상기 레벨링제는 소재의 레벨링성을 위하여 사용되는 것으로서, 종래에 사용되는 레벨링제라면 특별히 한정되지 않는다. 상기 레벨링제의 함량은 수계형 폴리아크릴레이트 디스퍼젼 수지 100 중량부에 대하여 0.2 내지 2 중량부로서, 레벨링제의 함량이 상기 하한치 미만인 경우에는 첨가제 본연의 기능이 나타나기 어렵고, 상기 상한치 초과인 경우에는 크레이터 등의 현상이 발생된다. The leveling agent is used for the leveling property of the material, and is not particularly limited as long as it is a conventionally used leveling agent. The content of the leveling agent is 0.2 to 2 parts by weight based on 100 parts by weight of the water-based polyacrylate dispersion resin. A phenomenon such as craters occurs.
상기 증점제는 레올로지 특성을 부여하기 위하여 사용되는 것으로서, 종래에 사용되는 우레탄계 증점제라면 특별히 한정되지 않는다. 상기 증점제의 함량은 수계형 폴리아크릴레이트 디스퍼젼 수지 100 중량부에 대하여 0.1 내지 1 중량부로서, 증점제의 함량이 상기 하한치 미만인 경우에는 첨가제 본연의 기능이 나타나기 어렵고, 상기 상한치 초과인 경우에는 크랙이 발생될 수 있다. The thickener is used to impart rheological properties, and is not particularly limited as long as it is a conventionally used urethane-based thickener. The content of the thickener is 0.1 to 1 part by weight based on 100 parts by weight of the water-based polyacrylate dispersion resin, and when the content of the thickener is less than the lower limit, the original function of the additive is difficult to appear, and if it exceeds the upper limit, cracks can occur.
상기 조용제는 도막두께가 두껍거나 도장조건이 가혹한 경우 발생하는 핀홀, 팝핑 등의 이현상을 제거하기 위해 사용되는 것으로서, 구체적으로 프로필렌 글리콜 디아세테이트, 디프로필렌 글리콜 n-부틸에테르, 디에틸렌 글리콜 모노부틸에테르, 디에틸렌 글리콜 n-부틸 에테르 아세테이트로 이루어진 군에서 선택된 1종 이상을 들 수 있다. 상기 조용제의 함량은 수계형 폴리아크릴레이트 디스퍼젼 수지 100 중량부에 대하여 3 내지 5 중량부로서, 조용제의 함량이 상기 하한치 미만인 경우에는 그 효과가 미미하고, 상기 상한치 초과인 경우에는 도료의 VOC 수치가 높아질 수 있다.The co-solvent is used to remove abnormal phenomena such as pinholes and popping that occur when the coating film thickness is thick or the coating conditions are severe. Specifically, propylene glycol diacetate, dipropylene glycol n-butyl ether, diethylene glycol monobutyl ether , and at least one selected from the group consisting of diethylene glycol n-butyl ether acetate. The content of the co-solvent is 3 to 5 parts by weight based on 100 parts by weight of the water-based polyacrylate dispersion resin, and when the content of the co-solvent is less than the lower limit, the effect is insignificant. may increase
또한, 상기 주제부에는 수계형 폴리아크릴레이트 디스퍼젼 수지 100 중량부에 대하여 10 내지 20 중량부의 탈이온수가 첨가되어 모든 첨가제의 혼합을 용이하게 한다.In addition, 10 to 20 parts by weight of deionized water is added to the main part based on 100 parts by weight of the water-based polyacrylate dispersion resin to facilitate mixing of all additives.
상기 경화제부는 폴리이소시아네이트를 포함할 수 있다.The curing agent may include polyisocyanate.
상기 폴리이소시아네이트는 수계형 폴리이소시아네이트와 용제형 폴리이소시아네이트를 포함하는 것이 바람직하다. 상기 경화제부에 적용되는 폴리이소시아네이트는 그 구조 특성상 물과 친하지 않은 소수성 성질을 띠고 있어 수계형 도료에는 수용성(water soluble)으로 개질된 수계형 폴리이소시아네이트를 사용하는 것이 일반적이나, 수계형 폴리이소시아네이트를 단독으로 사용할 경우 내수성 및 내습성이 취약한 문제가 있어 외장 마감용 탑코트로는 부적한 문제점이 초래된다.The polyisocyanate preferably includes a water-based polyisocyanate and a solvent-type polyisocyanate. The polyisocyanate applied to the curing agent part has a hydrophobic property that is not friendly with water due to its structural characteristics, so it is common to use a water-based polyisocyanate modified to be water-soluble for a water-based paint, but water-based polyisocyanate alone When used as a top coat for exterior finishing, there is a problem with weak water resistance and moisture resistance.
반면에 용제형 폴리이소시아네이트를 단독으로 사용할 경우 내수성과 내습성이 양호하지만 물과 잘 섞이지 않는 성질로 인해 핸드믹싱이 거의 불가능하고 기계로 교반을 해야 하기 때문에 현장 작업 사용조건에 맞지 않는 단점이 있다.On the other hand, when solvent-type polyisocyanate is used alone, water resistance and moisture resistance are good, but hand mixing is almost impossible due to the property that it does not mix well with water.
따라서, 도장 작업시 핸드믹싱이 가능하면서 내수성과 내습성의 도막물성을 만족하는 수성 2액형 폴리우레탄 코팅도료를 제조하기 위해서는 경화제부는 수계형 폴리이소시아네이트와 용제형 폴리이소시아네이트를 적절한 비율로 혼합사용해야 한다. 바람하게는 수계형 폴리이소시아네이트 100 중량부에 대하여 용제형 폴리이소시아네이트를 90 내지 110 중량부 범위 내에서 혼합 사용한다. Therefore, in order to manufacture a water-based two-component polyurethane coating paint that can be hand-mixed during painting and that satisfies the water-resistance and moisture-resistance coating properties, the curing agent part must mix and use water-based polyisocyanate and solvent-type polyisocyanate in an appropriate ratio. Preferably, the solvent-type polyisocyanate is mixed and used within the range of 90 to 110 parts by weight based on 100 parts by weight of the water-based polyisocyanate.
상기 경화제부는 물이 아닌 용제로만 희석이 가능한데 이는 폴리이소시아네이트가 물과 반응하기 때문에 제조 후 2 내지 3일 내로 굳어지기 때문이다. 이때 용제선택은 주제부에서 언급한 조용제들을 단독 또는 2종 이상을 혼합하여 사용할 수 있으며 그 함량은 수계형 폴리이소시아네이트 100 중량부에 대하여 10 내지 35중량부로 제한된다. 조용제의 함량이 상기 하한치 미만인 경우에는 경화제부의 점도가 너무 높아 믹싱이 어렵고, 상기 상한치 초과인 경우에는 도료의 VOC 수치가 높아질 수 있다.The curing agent part can be diluted only with a solvent, not water, because the polyisocyanate reacts with water and hardens within 2 to 3 days after manufacture. In this case, the solvent selection can be used alone or in a mixture of two or more of the co-solvents mentioned in the main part, and the content is limited to 10 to 35 parts by weight based on 100 parts by weight of the water-based polyisocyanate. When the content of the co-solvent is less than the lower limit, mixing is difficult because the viscosity of the curing agent is too high, and when the content of the co-solvent is greater than the upper limit, the VOC value of the paint may be increased.
상기 주제부 및 경화제부는 2 : 1의 중량비로 혼합되는 것으로서, 주제부를 기준으로 경화제부의 함량이 상기 범위를 벗어나는 경우에는 도막이 형성되지 않고 크랙이 발생할 수 있다. The main part and the hardener part are mixed in a weight ratio of 2: 1, and when the content of the hardener part based on the main part is out of the above range, a coating film may not be formed and cracks may occur.
이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예를 제시하나, 하기 실시예는 본 발명을 예시하는 것일 뿐 본 발명의 범주 및 기술사상 범위 내에서 다양한 변경 및 수정이 가능함은 당업자에게 있어서 명백한 것이며, 이러한 변형 및 수정이 첨부된 특허청구범위에 속하는 것도 당연한 것이다.Hereinafter, preferred examples are presented to aid the understanding of the present invention, but the following examples are merely illustrative of the present invention and it will be apparent to those skilled in the art that various changes and modifications are possible within the scope and spirit of the present invention, It goes without saying that such variations and modifications fall within the scope of the appended claims.
대조군 1. 미세조류 추출물 생략Control 1. Microalgae extract omitted
수계형 폴리아크릴레이트 디스퍼젼 수지(Covestro사) 100 중량부에 대하여 표면장력 조절제(수계형 실리콘 첨가제 Surfynol104E, Air product사) 0.5 중량부, 레벨링제(수계형 레벨링 첨가제 Borchi gol LA-200, Borchers 사) 0.5 중량부, 조용제(프로필렌 글리콜 디아세테이트) 4 중량부, 증점제 0.5 중량부, 탈이온수 15 중량부를 혼합하여 주제부를 수득하였다.Based on 100 parts by weight of water-based polyacrylate dispersion resin (Covestro), 0.5 parts by weight of surface tension regulator (water-based silicone additive Surfynol104E, Air product), leveling agent (water-based leveling additive Borchi gol LA-200, Borchers) ) 0.5 parts by weight, 4 parts by weight of a co-solvent (propylene glycol diacetate), 0.5 parts by weight of a thickener, and 15 parts by weight of deionized water to obtain a main part.
수계형 폴리이소시아네이트(Covestro 사) 100 중량부, 용제형 폴리이소시아네이트(Covestro 사) 100 중량부, 조용제(디프로필렌 글리콜 n-부틸 에테르) 20 중량부를 혼합하여 경화제부를 수득하였다.A curing agent part was obtained by mixing 100 parts by weight of a water-based polyisocyanate (Covestro), 100 parts by weight of a solvent-type polyisocyanate (Covestro), and 20 parts by weight of a co-solvent (dipropylene glycol n-butyl ether).
상기 주제부와 경화제부를 2 : 1의 중량비로 혼합하여 도료 조성물을 제조하였다. A coating composition was prepared by mixing the main part and the curing agent part in a weight ratio of 2: 1.
실시예 1. 아세톤 추출_세네데스무스Example 1. Acetone Extraction_Senedesmus
미세조류 추출물Microalgae Extract
미세조류로는 세네데스무스를 사용하였으며, 시료는 60 ℃ 오븐에서 8시간 동안 건조시킨 후 상기 건조된 세네데스무스와 아세톤을 1 : 20의 중량비로 혼합하여 60 ℃에서 30분 동안 추출한 후 15000 rpm에서 15분 동안 원심분리한 후 상등액을 동결건조하여 세네데스무스 추출 분말을 수득하였다. Senedesmus was used as the microalgae, and the sample was dried in an oven at 60° C. for 8 hours, and then the dried Senedesmus and acetone were mixed in a weight ratio of 1:20, extracted at 60° C. for 30 minutes, and then 15000 rpm. After centrifugation for 15 minutes, the supernatant was freeze-dried to obtain a Senedesmus extract powder.
도료 조성물paint composition
수계형 폴리아크릴레이트 디스퍼젼 수지(Covestro사) 100 중량부에 대하여 세네데스무스 추출 분말 0.025 중량부, 표면장력 조절제(수계형 실리콘 첨가제 Surfynol104E, Air product사) 0.5 중량부, 레벨링제(수계형 레벨링 첨가제 Borchi gol LA-200, Borchers 사) 0.5 중량부, 조용제(프로필렌 글리콜 디아세테이트) 4 중량부, 증점제 0.5 중량부, 탈이온수 15 중량부를 혼합하여 주제부를 수득하였다.Based on 100 parts by weight of water-based polyacrylate dispersion resin (Covestro), 0.025 parts by weight of senedesmus extract powder, 0.5 parts by weight of a surface tension regulator (water-based silicone additive Surfynol104E, Air product) 0.5 parts by weight of a leveling agent (water-based leveling agent) Additive Borchi gol LA-200, Borchers) 0.5 parts by weight, co-solvent (propylene glycol diacetate) 4 parts by weight, thickener 0.5 parts by weight, and deionized water 15 parts by weight were mixed to obtain a main part.
수계형 폴리이소시아네이트(Covestro 사) 100 중량부, 용제형 폴리이소시아네이트(Covestro 사) 100 중량부, 조용제(디프로필렌 글리콜 n-부틸 에테르) 20 중량부를 혼합하여 경화제부를 수득하였다.A curing agent part was obtained by mixing 100 parts by weight of a water-based polyisocyanate (Covestro), 100 parts by weight of a solvent-type polyisocyanate (Covestro), and 20 parts by weight of a co-solvent (dipropylene glycol n-butyl ether).
상기 주제부와 경화제부를 2 : 1의 중량비로 혼합하여 도료 조성물을 제조하였다. A coating composition was prepared by mixing the main part and the curing agent part in a weight ratio of 2: 1.
실시예 2. 메탄올 추출_세네데스무스Example 2. Methanol extraction_Senedesmus
상기 실시예 1과 동일하게 실시하되, 세네데스무스 추출 시 용매로 아세톤 대신 무수 메탄올을 사용하여 도료 조성물을 제조하였다. A coating composition was prepared in the same manner as in Example 1, except that anhydrous methanol was used instead of acetone as a solvent during senedesmus extraction.
실시예 3. 에탄올 추출_세네데스무스Example 3. Ethanol Extraction_Senedesmus
상기 실시예 1과 동일하게 실시하되, 세네데스무스 추출 시 용매로 아세톤 대신 무수 에탄올을 사용하여 도료 조성물을 제조하였다. A coating composition was prepared in the same manner as in Example 1, except that anhydrous ethanol was used instead of acetone as a solvent during senedesmus extraction.
실시예 4. 아세톤 추출_클로렐라Example 4. Acetone Extraction_Chlorella
상기 실시예 1과 동일하게 실시하되, 세네데스무스 대신 클로렐라를 사용하여 도료 조성물을 제조하였다. A coating composition was prepared in the same manner as in Example 1, except that Chlorella was used instead of Senedesmus.
실시예 5. 메탄올 추출_클로렐라Example 5. Methanol Extraction_Chlorella
상기 실시예 4와 동일하게 실시하되, 클로렐라 추출 시 용매로 아세톤 대신 무수 메탄올을 사용하여 도료 조성물을 제조하였다. A coating composition was prepared in the same manner as in Example 4, except that anhydrous methanol was used instead of acetone as a solvent during chlorella extraction.
실시예 6. 에탄올 추출_클로렐라Example 6. Ethanol Extraction_Chlorella
상기 실시예 4와 동일하게 실시하되, 클로렐라 추출 시 용매로 아세톤 대신 무수 에탄올을 사용하여 도료 조성물을 제조하였다. A coating composition was prepared in the same manner as in Example 4, except that anhydrous ethanol was used instead of acetone as a solvent during chlorella extraction.
비교예 1. 증류수 추출Comparative Example 1. Distilled water extraction
상기 실시예 1과 동일하게 실시하되, 세네데스무스 추출 시 용매로 아세톤 대신 증류수를 사용하여 도료 조성물을 제조하였다. A coating composition was prepared in the same manner as in Example 1, except that distilled water was used instead of acetone as a solvent during extraction of Senedesmus.
비교예 2. 세네데스무스 추출 분말 함량_0.001 중량부Comparative Example 2. Senedesmus extract powder content_0.001 parts by weight
상기 실시예 1과 동일하게 실시하되, 세네데스무스 추출 분말을 0.001 중량부로 사용하여 도료 조성물을 제조하였다. A coating composition was prepared in the same manner as in Example 1, except that cenedesmus extract powder was used in an amount of 0.001 parts by weight.
비교예 3. 세네데스무스 추출 분말 함량_10 중량부Comparative Example 3. Senedesmus extract powder content_10 parts by weight
상기 실시예 1과 동일하게 실시하되, 세네데스무스 추출 분말을 10 중량부로 사용하여 도료 조성물을 제조하였다. A coating composition was prepared in the same manner as in Example 1, except that 10 parts by weight of Senedesmus extract powder was used.
비교예 4. 세네데스무스Comparative Example 4. Senedesmus
상기 실시예 1과 동일하게 실시하되, 세네데스무스를 추출하지 않고 그대로 사용하여 도료 조성물을 제조하였다. A coating composition was prepared in the same manner as in Example 1, except that Senedesmus was not extracted and used as it is.
<시험예><Test Example>
시험예 1. 자외선 흡수 특성Test Example 1. Ultraviolet absorption characteristics
실시예 및 비교예에 따라 제조된 추출물의 자외선 흡수능을 측정하기 위하여 UV/Vis spectrophotometer를 이용하여 UV-A, UV-B, UV-C 파장을 모두 포함하는 180 내지 420 nm에서 흡광도를 측정하였다. In order to measure the ultraviolet absorption capacity of the extracts prepared according to Examples and Comparative Examples, absorbance was measured at 180 to 420 nm including all UV-A, UV-B, and UV-C wavelengths using a UV/Vis spectrophotometer.
위 표 1에 나타낸 바와 같이, 실시예 1 내지 3에 따라 제조된 미세조류 추출물은 자외선 흡수능이 비교예 1의 미세조류 추출물에 비하여 높은 것을 확인하였다.As shown in Table 1 above, it was confirmed that the microalgal extracts prepared according to Examples 1 to 3 had higher UV absorption capacity than the microalgae extracts of Comparative Example 1.
특히, 실시예 1의 추출물이 실시예 2 및 3의 추출물에 비해서도 자외선 흡수능이 우수한 것을 확인하였으며, UVA 보다는 UVB의 흡수능이 우수한 것을 확인하였다.In particular, it was confirmed that the extract of Example 1 was superior to the extracts of Examples 2 and 3 in absorbing ultraviolet rays, and it was confirmed that the absorbing ability of UVB was superior to that of UVA.
시험예 2. 자외선, 적외선 및 가시광선 흡수율 측정Test Example 2. Measurement of UV, Infrared and Visible Light Absorption
실시예 및 비교예에 따라 제조된 우레탄계 도료 조성물을 아크릴판에 30 ㎛의 두께로 도포한 후 상온에서 1시간 동안 건조시켜 투명한 우레탄 도막을 형성하였다. 상기 형성된 우레탄 도막의 자외선, 적외선 및 가시광선 흡수율을 측정하기 위하여 Linshang사의 LS160 transmission meter를 이용하여 측정하였다.A transparent urethane coating film was formed by applying the urethane-based coating composition prepared according to Examples and Comparative Examples to a thickness of 30 μm on an acrylic plate and drying it at room temperature for 1 hour. In order to measure the ultraviolet, infrared and visible light absorptivity of the formed urethane coating film, it was measured using a Linshang LS160 transmission meter.
위 표 2에 나타낸 바와 같이, 본 발명의 실시예 1 내지 6에 따라 제조된 도료 조성물은 대조군 및 비교예 1 내지 4의 도료 조성물에 비하여 자외선을 우수하게 차단 또는 흡수한다는 것을 알 수 있으나 가시광선 흡수율에서는 큰 차이를 보이지 않아 자외선 차단 또는 흡수효과가 우수하고 시인성이 확보된 도료 생산이 가능하다.As shown in Table 2 above, it can be seen that the coating compositions prepared according to Examples 1 to 6 of the present invention block or absorb UV rays better than the coating compositions of Control and Comparative Examples 1 to 4, but the visible light absorption rate It does not show a big difference, so it is possible to produce paints with excellent UV blocking or absorption effects and with secure visibility.
특히, 비교예 3의 도료 조성물은 미세조류 추출 분말이 다량으로 첨가되어 투명한 도막이 형성되지 못하였다.In particular, in the coating composition of Comparative Example 3, a large amount of microalgae extract powder was added, so that a transparent coating film was not formed.
시험예 3. 도막 평가Test Example 3. Coating film evaluation
상시 시험예 2에서 형성된 도막을 이용하여 평가를 수행하였다.Evaluation was performed using the coating film formed in Test Example 2 at all times.
3-1. 부착성 시험: ASTM D3359에 의거 크로스 컷 테이프 테스트(cross cut tape test)를 시행하여 평가하였다.3-1. Adhesion test: It was evaluated by performing a cross cut tape test according to ASTM D3359.
3-2. 연필경도 시험: ISO 15184 및 JIS K 5600-5-4에 의거하여 HB 이상시 경도가 우수한 것으로 평가한다. 경도는 9H, 8H, 7H, 6H, 5H, 4H, 3H, 2H, H, F, HB, B, 2B, 3B, 4B, 5B, 6B, 7B, 8B, 9B로 나타내는 것으로서, 9H에서 9B로 갈수록 결도가 낮아지는 것이다.3-2. Pencil hardness test: In accordance with ISO 15184 and JIS K 5600-5-4, the hardness is evaluated as excellent when HB or more. Hardness is expressed as 9H, 8H, 7H, 6H, 5H, 4H, 3H, 2H, H, F, HB, B, 2B, 3B, 4B, 5B, 6B, 7B, 8B, 9B, and increases from 9H to 9B. the intensity will be lowered.
3-3. 내스크래치성 시험: Steelwool #0000 grade를 이용하여 500 g의 힘을 주어 10회 rubbing후 도막 손상을 확인하였다. 3-3. Scratch resistance test: Using Steelwool #0000 grade, 500 g of force was applied and after rubbing 10 times, damage to the coating film was confirmed.
3-4. 내습성 시험: 시험온도 및 상대습도가 50±2 ℃, 98±2%인 조건에서 240시간 방치 후, 꺼내어 1시간 동안 방치하여 관찰시 도막에 현저한 변색, 퇴색, 팽윤, 갈라짐, 광택저하 등이 없는지, 부착성에 이상이 없는지 평가하였다. 3-4. Moisture resistance test: After standing for 240 hours under the conditions of test temperature and relative humidity of 50±2 ℃ and 98±2%, take it out and leave it for 1 hour. It was evaluated whether or not there was any abnormality in adhesiveness.
3-5. 내수성 시험: 시편을 수돗물(TAP WATER, 시험온도 40 ℃) 중에 240시간 침적시킨 후 꺼내어 AIR BLOW에 의해 표면의 수분을 제거한 다음, 상온에서 1시간 방치 후 관찰시 도막의 현저한 변색, 퇴색, 팽윤, 갈라짐, 광택저하 등이 없는지, 부착성에 이상이 없는지 평가하였다.3-5. Water resistance test: After immersing the specimen in tap water (TAP WATER, test temperature 40 ℃) for 240 hours, take it out, remove moisture from the surface by air blow, and leave it at room temperature for 1 hour. It was evaluated whether there was cracking, deterioration of gloss, etc., and whether there was any abnormality in adhesion.
3-6. 내열성 시험: 시험온도(80±2 ℃) 조건 하에서 300시간 방치한 다음 꺼내어 실온에서 1시간 방치 후 관찰시 도막의 현저한 변색, 퇴색, 팽윤, 갈라짐, 광택저하 등이 없는지, 부착성에 이상이 없는지 평가하였다. 3-6. Heat resistance test: After standing for 300 hours under the test temperature (80±2 ℃) condition, take it out and leave it at room temperature for 1 hour. When observed, evaluate whether there is any significant discoloration, discoloration, swelling, cracking, deterioration of gloss, etc. of the coating film and there is no abnormality in adhesion did.
3-7. 내약품성 시험: 유리세정제, 엔진오일을 개별 사용하여 3 N의 힘으로 20회 왕복한 다음 도막의 표면을 문질러 외관을 육안 조사 후, 실온에서 24시간 방치 하여 관찰시 도막의 현저한 변색, 퇴색, 팽윤, 갈라짐, 광택저하 등이 없는지, 부착성에 이상이 없는지 평가하였다.3-7. Chemical resistance test: Using glass cleaner and engine oil separately, reciprocate 20 times with a force of 3 N, rub the surface of the coating film to visually inspect the appearance, and leave it at room temperature for 24 hours to observe significant discoloration, discoloration, and swelling , cracking, deterioration of gloss, etc., and no abnormality in adhesion were evaluated.
평가는 우수:○, 보통:△, 불량X로 표시하였다.Evaluation was expressed as excellent:○, average:Δ, and poor X.
위 표 3에 나타낸 바와 같이, 본 발명의 실시예 1 내지 6에 따라 제조된 도료 조성물은 비교예 1 내지 4의 도료 조성물에 비하여 부착성, 연필경도, 내스크래치성, 내습성, 내수성, 내열성 및 내약품성 모두 우수한 것을 확인하였다.As shown in Table 3 above, the coating compositions prepared according to Examples 1 to 6 of the present invention had better adhesion, pencil hardness, scratch resistance, moisture resistance, water resistance, heat resistance, and better properties than the coating compositions of Comparative Examples 1 to 4 It was confirmed that all of the chemical resistance were excellent.
특히, 비교예 1 내지 4의 도료 조성물은 모든 시험에서 우수하지 못하였다.In particular, the coating compositions of Comparative Examples 1 to 4 were not excellent in all tests.
Claims (7)
상기 미세조류는 세네데스무스(scenedesmus) 또는 클로렐라이고,
수계형 폴리아크릴레이트 디스퍼젼 수지 100 중량부에 대하여 상기 미세조류 추출물이 0.01 내지 5 중량부로 포함되는 것을 특징으로 하는 도료 조성물.Contains a UV absorbent containing microalgae extract,
The microalgae are Senedesmus (scenedesmus) or Chlorella,
A coating composition, characterized in that the microalgae extract is contained in an amount of 0.01 to 5 parts by weight based on 100 parts by weight of the water-based polyacrylate dispersion resin.
The coating composition according to claim 1, wherein the coating composition comprises a main part comprising a water-based polyacrylate dispersion resin and a microalgae extract, and a curing agent part comprising polyisocyanate.