KR102247697B1 - Precious metal alloy composition and its manufacturing method - Google Patents
Precious metal alloy composition and its manufacturing method Download PDFInfo
- Publication number
- KR102247697B1 KR102247697B1 KR1020200002657A KR20200002657A KR102247697B1 KR 102247697 B1 KR102247697 B1 KR 102247697B1 KR 1020200002657 A KR1020200002657 A KR 1020200002657A KR 20200002657 A KR20200002657 A KR 20200002657A KR 102247697 B1 KR102247697 B1 KR 102247697B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- metal alloy
- gold
- noble metal
- alloy composition
- Prior art date
Abstract
Description
본 발명은 귀금속 합금 조성물 및 그 제조방법에 관한 것으로, 더욱 상세하게는 백금(WHITE GOLD)과 핑크골드(PINK GOLD)를 혼합 조성하여 자연스러운 핑크골드 색상을 백금에 부여한 귀금속 합금 조성물 및 그 제조방법에 관한 것이다. The present invention relates to a noble metal alloy composition and a method for producing the same, and more particularly, to a noble metal alloy composition in which a natural pink gold color is imparted to platinum by a mixture of platinum (WHITE GOLD) and pink gold (PINK GOLD), and a method for producing the same. About.
일반적으로 금반지와 같이 귀금속을 주재료로 한 주얼리는 액세사리로서 많은 사람들이 착용을 원하고 있으며, 사용되는 금 합금은 주로 색상구현, 내구성의 향상 목적을 위해 귀금속인 금(Au) 외에 은(Ag)이나 구리(Cu) 등이 합금되고 있다.In general, jewelry made with precious metals as the main material, such as gold rings, is an accessory that many people want to wear, and the gold alloy used is silver (Ag) or silver (Ag) other than gold (Au), a precious metal, mainly for color realization and durability Copper (Cu) and the like are being alloyed.
특히, 금의 본연의 색인 옐로우 외에, 소비자의 다양한 요구에 따라 추가적인 색상의 제품이 개발될 필요가 있으나, 현재까지는 귀금속 재료의 가공 기술 중 색상을 도입하는 기술은 아직까지 크게 발전하지 못하고 있는 실정이다.In particular, besides yellow, the natural color of gold, it is necessary to develop additional color products according to various demands of consumers, but the technology of introducing color among the processing technologies of precious metal materials has not yet developed significantly. .
본 발명은 상기한 종래 기술의 문제점을 해결하기 위하여 안출된 것으로서, 본 발명의 목적은 백금과 핑크골드를 혼합 조성하여 귀금속 합금 조성물을 제조함에 의해 백금에 핑크 색상을 부여하되, 핑크 색상의 명도를 크게 향상시키고, 경도를 높이며, 탁월한 광택도를 부여할 수 있는 귀금속 합금 조성물 및 그 제조방법을 제공하는데 있다. The present invention was conceived to solve the problems of the prior art, and an object of the present invention is to give a pink color to platinum by preparing a noble metal alloy composition by mixing platinum and pink gold, but to increase the brightness of the pink color. It is to provide a noble metal alloy composition that can greatly improve, increase hardness, and impart excellent glossiness, and a method of manufacturing the same.
상기 목적을 달성하기 위한 본 발명의 귀금속 합금 조성물은, 30 중량% 내지 70 중량%의 백금(Pt)과, 70 중량% 내지 30 중량%의 핑크골드를 포함하여 혼합 조성되되, 상기 핑크골드는: 75 중량%의 금(Au)과, 3 중량%의 은(Ag)과, 17.5 중량%의 동(Cu), 및 4.5 중량%의 팔라디윰(Pd)을 혼합 조성하여 이루어지는 것이 바람직하다. The noble metal alloy composition of the present invention for achieving the above object is a mixed composition comprising 30% to 70% by weight of platinum (Pt) and 70% to 30% by weight of pink gold, wherein the pink gold is: It is preferable to form a mixture of 75% by weight of gold (Au), 3% by weight of silver (Ag), 17.5% by weight of copper (Cu), and 4.5% by weight of palladium (Pd).
상기 귀금속 합금은, Lab 색지수에서 L 값은 90 이상인 것이 바람직하다. It is preferable that the noble metal alloy has an L value of 90 or more in the Lab color index.
또한, 본 발명은 귀금속 합금 조성물은, 22.5 중량% 내지 52.5 중량%의 금(Au); 0.9 중량% 내지 2.1 중량%의 은(Ag); 5.25 중량% 내지 12.25 중량%의 동(Cu); 1.35 중량% 내지 3.15 중량%의 팔라디움(Pd); 및 잔분인 백금(Pt);을 포함하되, 상기 백금은 전체에서 30 중량% 내지 70 중량%인 것이 바람직하다. In addition, the present invention is a noble metal alloy composition, 22.5% by weight to 52.5% by weight of gold (Au); 0.9% to 2.1% by weight of silver (Ag); 5.25% to 12.25% by weight of copper (Cu); 1.35% to 3.15% by weight of palladium (Pd); And platinum (Pt), which is the residue, wherein the platinum is preferably 30% by weight to 70% by weight in total.
한편, 상기 목적을 달성하기 위한 본 발명의 귀금속 합금 조성물의 제조방법은, 원하는 디자인 모양으로 왁스제 모형을 제작하고, 그 제작된 왁스모형에 석고를 입혀 굳힌 후 왁스를 녹여내고 거기에 귀금속 혼합물을 부어 성형하는 성형단계; 및 상기 성형단계를 통해 성형된 성형물을 소결하는 소결단계;를 포함하되, 상기 귀금속 혼합물은: 백금(Pt)분말 30 중량% 내지 70 중량%, 및 핑크골드분말 70 중량% 내지 30 중량%를 혼합 조성하여 이루어지되, 전체 중량에 대하여 5 중량% 내지 10 중량%의 금속바인더가 혼합되고, 상기 핑크골드분말은 100 중량%에 대하여 금(Au)분말 75 중량%, 은(Ag)분말 3 중량%, 동(Cu)분말 17.5 중량%, 및 팔라디윰(Pd)분말 4.5 중량%을 혼합 조성하여 제조하는 것이 바람직하다. On the other hand, in the manufacturing method of the noble metal alloy composition of the present invention for achieving the above object, a wax model is produced in a desired design shape, plaster is applied to the produced wax model, hardened, and then the wax is melted and the noble metal mixture is added thereto. A molding step of pouring and molding; And a sintering step of sintering the molded product formed through the molding step; wherein the noble metal mixture includes: platinum (Pt) powder 30 wt% to 70 wt%, and pink gold powder 70 wt% to 30 wt% The composition is made, but 5% to 10% by weight of a metal binder is mixed with respect to the total weight, and the pink gold powder is 75% by weight of gold (Au) powder and 3% by weight of silver (Ag) powder based on 100% by weight. , Copper (Cu) powder, 17.5% by weight, and palladium (Pd) powder is preferably prepared by mixing 4.5% by weight.
상기 금속바인더는 니켈 또는 코발트로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것이 바람직하다. It is preferable that the metal binder is made of at least one selected from the group consisting of nickel or cobalt.
상기 금속바인더는 니켈 및 코발트가 1:3의 중량비율로 혼합되어 이루어지는 것이 바람직하다. The metal binder is preferably made by mixing nickel and cobalt in a weight ratio of 1:3.
본 발명에 따른 귀금속 합금 조성물 및 그 제조방법에 의하면, 백금과 핑크콜드를 혼합 조성하여 백금에 핑크 색상을 부여하고 명도를 크게 향상시키며, 경도를 높이고, 탁월한 광택도를 부여할 수 있는 효과가 있다. According to the noble metal alloy composition and its manufacturing method according to the present invention, platinum and pink cold are mixed to give a pink color to platinum, greatly improve brightness, increase hardness, and provide excellent glossiness. .
도 1 및 도 2는 일반적인 핑크골드 반지의 예를 도시한 사진이다.
도 3은 본 발명의 일 실시 형태에 따라 제조된 반지의 예를 도시한 사진이다. 1 and 2 are photographs showing an example of a general pink gold ring.
3 is a photograph showing an example of a ring manufactured according to an embodiment of the present invention.
이하에서는, 첨부된 도면을 참고하여 본 발명에 따른 바람직한 실시예를 보다 상세하게 설명하기로 한다.Hereinafter, preferred embodiments of the present invention will be described in more detail with reference to the accompanying drawings.
본 발명의 설명에 앞서, 이하의 특정한 구조 내지 기능적 설명들은 단지 본 발명의 개념에 따른 실시예를 설명하기 위한 목적으로 예시된 것으로, 본 발명의 개념에 따른 실시예들은 다양한 형태로 실시될 수 있으며, 본 명세서에 설명된 실시예들에 한정되는 것으로 해석되어서는 아니된다.Prior to the description of the present invention, the following specific structure or functional descriptions are exemplified only for the purpose of describing embodiments according to the concept of the present invention, and embodiments according to the concept of the present invention may be implemented in various forms. , It should not be construed as being limited to the embodiments described herein.
또한, 본 발명의 개념에 따른 실시예는 다양한 변경을 가할 수 있고 여러 가지 형태를 가질 수 있으므로, 특정 실시예들을 도면에 예시하고 본 명세서에 상세하게 설명하고자 한다. 그러나, 이는 본 발명의 개념에 따른 실시예들을 특정한 개시 형태에 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경물, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다. In addition, since the embodiments according to the concept of the present invention can apply various changes and have various forms, specific embodiments will be illustrated in the drawings and described in detail in the present specification. However, this is not intended to limit the embodiments according to the concept of the present invention to a specific form of disclosure, and it should be understood that all modifications, equivalents, and substitutes included in the spirit and scope of the present invention are included.
본 발명에 따른 귀금속 합금 조성물은, 30 중량% 내지 70 중량%의 백금(Pt)과, 70 중량% 내지 30 중량%의 핑크골드를 포함하도록 혼합 조성되는 것이 바람직하다. The noble metal alloy composition according to the present invention is preferably a mixed composition comprising 30% by weight to 70% by weight of platinum (Pt) and 70% by weight to 30% by weight of pink gold.
상기 핑크골드의 함량을 한정한 이유는 백금과 혼합되었을 경우 핑크골드의 색상 및 명도를 향상시키며, 탁월한 광택도를 부여하기 위함이다. The reason for limiting the content of pink gold is to improve the color and brightness of pink gold when mixed with platinum, and to impart excellent glossiness.
상기 핑크골드의 함량이 30 중량% 미만일 경우 상기 백금과의 함량에 대해서 전체적으로 균일한 핑크골드 색상을 발휘하기 어렵고, 70 중량% 초과일 경우 핑크골드 색상에 의해 백금 효과가 저하될 수 있다. When the content of the pink gold is less than 30% by weight, it is difficult to exhibit an overall uniform pink gold color with respect to the content of the platinum, and when the content of the pink gold is more than 70% by weight, the platinum effect may be degraded by the pink gold color.
또한, 상기 핑크골드의 조성비는, 75 중량%의 금(Au)과, 3 중량%의 은(Ag)과, 17.5 중량%의 동(Cu), 및 4.5 중량%의 팔라디윰(Pd)으로 이루어지는 것이 바람직하다. In addition, the composition ratio of the pink gold is composed of 75% by weight of gold (Au), 3% by weight of silver (Ag), 17.5% by weight of copper (Cu), and 4.5% by weight of palladium (Pd). It is desirable.
한편, 본 발명의 귀금속 합금 조성물은 22.5 중량% 내지 52.5 중량%의 금(Au)과, 0.9 중량% 내지 2.1 중량%의 은(Ag)과, 5.25 중량% 내지 12.25 중량%의 동(Cu)과, 1.35 중량% 내지 3.15 중량%의 팔라디움(Pd), 및 잔분인 30 중량% 내지 70 중량%의 백금(Pt)을 포함하도록 혼합 조성될 수 있다. On the other hand, the noble metal alloy composition of the present invention comprises 22.5% by weight to 52.5% by weight of gold (Au), 0.9% by weight to 2.1% by weight of silver (Ag), and 5.25% by weight to 12.25% by weight of copper (Cu) , 1.35% by weight to 3.15% by weight of palladium (Pd), and the balance 30% by weight to 70% by weight of platinum (Pt) may be mixed to include.
도 3은 본 발명의 일 실시 형태에 따라 제조된 반지의 예를 도시한 사진이다. 3 is a photograph showing an example of a ring manufactured according to an embodiment of the present invention.
도 3에 도시된 바와 같이, 본 발명의 일 실시 형태에 따라 제조된 반드의 색상 차이를 확인할 수 있다. 즉, 백금과 핑크골드의 함량 차이로 인해 나타나는 색상 차이를 확인할 수 있다. As shown in FIG. 3, a difference in color of bands manufactured according to an embodiment of the present invention can be confirmed. That is, it is possible to check the color difference that appears due to the difference in the content of platinum and pink gold.
한편, 본 발명의 일 실시 형태에 따라 제조된 귀금속 합금은, Lab 컬러 색지수에서 L 값은 90 이상인 것이 바람직하다. 여기서, Lab 컬러 지수의 L은 0~100의 범위 내에서 명도를 나타낸다. On the other hand, in the noble metal alloy manufactured according to an embodiment of the present invention, it is preferable that the L value in the Lab color index is 90 or more. Here, L of the Lab color index represents the brightness within the range of 0 to 100.
본 발명에 따른 귀금속 합금 조성물의 제조방법은, 원하는 디자인 모양으로 왁스제 모형을 제작하고, 그 제작된 왁스모형에 석고를 입혀 굳힌 후 왁스를 녹여내고 거기에 귀금속 혼합물을 부어 성형하는 성형단계 및 상기 성형단계를 통해 성형된 성형물을 소결하는 소결단계를 포함하여 제조될 수 있다. The method for producing a noble metal alloy composition according to the present invention comprises a molding step of producing a wax model in a desired design shape, coating the produced wax model with gypsum to harden, melting the wax, pouring a noble metal mixture thereto, and molding it. It can be produced including a sintering step of sintering the molded product formed through the molding step.
이때, 상기 귀금속 혼합물은 백금(Pt)분말 30 중량% 내지 70 중량% 및 핑크골드분말 70 중량% 내지 30 중량%를 혼합 조성하여 이루어지는 것이 바람직하며, 여기에 전체 중량에 대하여 5 중량% 내지 10 중량%의 금속바인더가 혼합되는 것이 바람직하고, 상기 핑크골드분말은 100 중량%에 대하여 금(Au)분말 75 중량%, 은(Ag)분말 3 중량%, 동(Cu)분말 17.5 중량%, 및 팔라디윰(Pd)분말 4.5 중량%을 혼합 조성하여 이루어지는 것이 바람직하다. At this time, the noble metal mixture is preferably made by mixing 30% to 70% by weight of platinum (Pt) powder and 70% to 30% by weight of pink gold powder, and 5% to 10% by weight based on the total weight. % Of the metal binder is preferably mixed, and the pink gold powder is 75% by weight of gold (Au) powder, 3% by weight of silver (Ag) powder, 17.5% by weight of copper (Cu) powder, and pala based on 100% by weight of the pink gold powder. It is preferably made by mixing 4.5% by weight of Diium (Pd) powder.
이때, 상기 금속바인더는 백금분말과 핑크골드분말을 결속시키는 바인더의 역할과 본 발명에 따른 귀금속 합금 조성물의 강도를 향상시키는 역할을 하는데, 니켈 또는 코발트로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것이 바람직하며, 니켈 및 코발트가 1:3의 중량비율로 혼합되어 이루어지는 것이 바람직하다. At this time, the metal binder serves as a binder to bind the platinum powder and the pink gold powder, and serves to improve the strength of the noble metal alloy composition according to the present invention, and is preferably made of at least one selected from the group consisting of nickel or cobalt. , Nickel and cobalt are preferably mixed in a weight ratio of 1:3.
이와 같이 니켈 및 코발트가 1:3의 중량비율로 혼합되어 이루어진 금속바인더는 인체에 유해할 뿐만 아니라 피부트러블을 유발하는 니켈의 함량이 낮으면서도 우수한 결속력을 나타낸다. As such, a metal binder formed by mixing nickel and cobalt in a weight ratio of 1:3 is not only harmful to the human body, but also exhibits excellent binding strength while having a low content of nickel that causes skin trouble.
또한, 니켈의 함량이 낮은 상태에서 소결과정을 진행하게 되면, 비교적 낮은 온도에서도 기공이 없고 입성장이 거의 없는 미세한 조직의 완전한 귀금속 합금 조성물을 얻을 수 있다.In addition, if the sintering process is performed in a state where the nickel content is low, it is possible to obtain a complete noble metal alloy composition having a fine structure with almost no pores and little grain growth even at a relatively low temperature.
상기 금속바인더의 함량이 5 중량% 미만으로 함유되면 백금분말과 핑크골드분말을 결속시키는데 어려움이 있고, 상기 금속바인더의 함량이 10 중량%를 초과하게 되면 인체에 유해한 중금속인 피부 트러블을 유발할 수 있다. If the content of the metal binder is less than 5% by weight, it is difficult to bind the platinum powder and the pink gold powder, and if the content of the metal binder exceeds 10% by weight, it may cause skin trouble, which is a heavy metal harmful to the human body. .
한편, 본 발명에 귀금속 합금 조성물의 제조방법은, 위에서 설명한 중량비로 백금분말과 핑크골드분말 및 금속바인더를 혼합한다. 이와 같이 혼합한 혼합물 100 중량%를 볼밀링장치에 투입하고, 볼과 혼합물의 장입비를 4:1로 한 상태에서 혼합속도 40rpm으로 60시간 동안 혼합하고, 혼합이 완료된 혼합물을 건조기에 투입하여 90℃의 온도에서 90분 동안 건조하고, 건조된 혼합물을 1250 메시의 채로 채거름하고, 채거름된 혼합물을 금형 내에 투입하여 50ton/in2의 압력으로 성형하고, 성형된 성형물을 소결로에 투입하고, 500 마이크론(micron) 이내의 진동도를 유지하면서 1250℃의 온도에서 45분 동안 소결하여 귀금속 합금 조성물을 제조하게 된다. On the other hand, in the method for preparing the noble metal alloy composition according to the present invention, platinum powder, pink gold powder, and metal binder are mixed in the weight ratio described above. 100% by weight of the mixture thus mixed was added to the ball milling device, and the mixture was mixed for 60 hours at a mixing speed of 40 rpm while the charging ratio of the ball and the mixture was 4:1, and the mixed mixture was put into a dryer for 90 hours. After drying for 90 minutes at a temperature of °C, the dried mixture was squeezed with 1250 mesh, and the squeezed mixture was put into a mold and molded at a pressure of 50 ton/in2, and the molded product was put into a sintering furnace. The noble metal alloy composition is prepared by sintering for 45 minutes at a temperature of 1250° C. while maintaining a vibration degree within 500 microns.
이와 같이 제조된 본 발명의 귀금속 합금 조성물은 백금에 부여되는 핑크 색상의 명도가 크게 향상되고, 경도가 높으며, 탁월한 광택도를 갖게 된다. The noble metal alloy composition of the present invention thus prepared greatly improves the brightness of the pink color imparted to platinum, has high hardness, and has excellent gloss.
특히, 본 발명은 도금 기술에 의해 핑크골드 색상을 표현하는 것이 아니라 핑크골드를 백금에 혼합하여 제조함으로서 핑크골드의 색상 표현을 자연스럽게 할 수 있는 장덤을 갖는다.In particular, the present invention does not express the color of pink gold by plating technology, but has the advantage of natural expression of the color of pink gold by mixing pink gold with platinum.
이상에서와 같은 기술적 구성에 의해 본 발명의 기술적 과제가 달성되는 것이며, 비록 한정된 실시예와 도면에 의해 설명되었으나 여기에 한정되지 않고 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 본 발명의 기술사상과 아래에 기재될 특허청구범위의 균등범위 내에서 다양한 수정 및 변형이 가능한 것임은 물론이다.The technical task of the present invention is achieved by the technical configuration as described above, and although it has been described by the limited embodiments and drawings, the present invention is not limited thereto, and the present invention by those of ordinary skill in the art to which the present invention pertains. It goes without saying that various modifications and variations are possible within the scope of the technical idea and the scope of the claims to be described below.
Claims (6)
30 중량% 내지 70 중량%의 백금(Pt)과, 70 중량% 내지 30 중량%의 핑크골드를 포함하여 혼합 조성되되,
상기 핑크골드는:
75 중량%의 금(Au)과, 3 중량%의 은(Ag)과, 17.5 중량%의 동(Cu), 및 4.5 중량%의 팔라디윰(Pd)을 혼합 조성하여 이루어지는 것을 특징으로 하는 귀금속 합금 조성물.
In the noble metal alloy composition,
A mixed composition including 30% to 70% by weight of platinum (Pt) and 70% to 30% by weight of pink gold,
The pink gold is:
Noble metal alloy, characterized in that a mixture of 75% by weight of gold (Au), 3% by weight of silver (Ag), 17.5% by weight of copper (Cu), and 4.5% by weight of palladium (Pd) Composition.
상기 귀금속 합금은, Lab 색지수에서 L 값은 90 이상인 것을 특징으로 하는 귀금속 합금 조성물.
The method of claim 1,
The noble metal alloy is a noble metal alloy composition, characterized in that the L value in the Lab color index is 90 or more.
22.5 중량% 내지 52.5 중량%의 금(Au);
0.9 중량% 내지 2.1 중량%의 은(Ag);
5.25 중량% 내지 12.25 중량%의 동(Cu);
1.35 중량% 내지 3.15 중량%의 팔라디움(Pd); 및
잔분인 백금(Pt);을 포함하되,
상기 백금은 전체에서 30 중량% 내지 70 중량%인 것을 특징으로 하는 귀금속 합금 조성물.
In the noble metal alloy composition,
22.5% to 52.5% by weight of gold (Au);
0.9% to 2.1% by weight of silver (Ag);
5.25% to 12.25% by weight of copper (Cu);
1.35% to 3.15% by weight of palladium (Pd); And
Including the balance of platinum (Pt);
The noble metal alloy composition, characterized in that the platinum is 30% by weight to 70% by weight in the total.
원하는 디자인 모양으로 왁스제 모형을 제작하고, 그 제작된 왁스모형에 석고를 입혀 굳힌 후 왁스를 녹여내고 거기에 귀금속 혼합물을 부어 성형하는 성형단계; 및
상기 성형단계를 통해 성형된 성형물을 소결하는 소결단계;를 포함하되,
상기 귀금속 혼합물은:
백금(Pt)분말 30 중량% 내지 70 중량%, 및 핑크골드분말 70 중량% 내지 30 중량%를 혼합 조성하여 이루어지되,
전체 중량에 대하여 5 중량% 내지 10 중량%의 금속바인더가 혼합되고,
상기 핑크골드분말은 100 중량%에 대하여 금(Au)분말 75 중량%, 은(Ag)분말 3 중량%, 동(Cu)분말 17.5 중량%, 및 팔라디윰(Pd)분말 4.5 중량%을 혼합 조성하여 제조하는 것을 특징으로 하는 귀금속 합금 조성물의 제조방법.
In the manufacturing method of the noble metal alloy composition,
A molding step of producing a wax model in a desired design shape, applying plaster on the produced wax model, hardening, melting the wax, pouring a precious metal mixture thereto, and molding; And
Including; a sintering step of sintering the molded product formed through the molding step,
The noble metal mixture is:
Platinum (Pt) powder 30% by weight to 70% by weight, and pink gold powder 70% by weight to 30% by weight of a mixed composition,
5% to 10% by weight of a metal binder is mixed with respect to the total weight,
The pink gold powder is a mixture composition of 75% by weight of gold (Au) powder, 3% by weight of silver (Ag) powder, 17.5% by weight of copper (Cu) powder, and 4.5% by weight of palladium (Pd) powder based on 100% by weight of the pink gold powder. Method for producing a noble metal alloy composition, characterized in that produced by.
상기 금속바인더는 니켈 또는 코발트로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것을 특징으로 하는 귀금속 합금 조성물의 제조방법.
The method of claim 4,
The method for producing a noble metal alloy composition, wherein the metal binder is made of at least one selected from the group consisting of nickel or cobalt.
상기 금속바인더는 니켈 및 코발트가 1:3의 중량비율로 혼합되어 이루어지는 것을 특징으로 하는 귀금속 합금 조성물의 제조방법.The method of claim 4,
The metal binder is a method of producing a noble metal alloy composition, characterized in that the nickel and cobalt are mixed in a weight ratio of 1:3.