KR102186295B1 - 다층구조 매트 - Google Patents
다층구조 매트 Download PDFInfo
- Publication number
- KR102186295B1 KR102186295B1 KR1020200002268A KR20200002268A KR102186295B1 KR 102186295 B1 KR102186295 B1 KR 102186295B1 KR 1020200002268 A KR1020200002268 A KR 1020200002268A KR 20200002268 A KR20200002268 A KR 20200002268A KR 102186295 B1 KR102186295 B1 KR 102186295B1
- Authority
- KR
- South Korea
- Prior art keywords
- mat
- layer
- filler
- layered
- adhesive layer
- Prior art date
Abstract
본 발명은 다층구조 매트에 관한 것이다. 구체적으로 본 발명의 일 실시예에 따르면, 에틸렌초산비닐(ethylene vinyl acetate)을 포함하는 에바층; 다공성 물질을 포함하는 매트층; 및 적어도 폴리염화비닐수지(poly vinyl chloride)를 포함하는 폼층을 포함하는, 다층구조 매트가 제공될 수 있다.
Description
본 발명은 다층구조 매트에 대한 발명이다.
일반적으로 사람들의 주거형태는 아파트, 빌라 등의 공동주택 또는 단독주택으로 이루어진다. 그 중 공동주택은 여러 사람들이 하나의 건물에 사는 형태이며, 대한민국 인구의 약 77%의 사람들이 아파트, 빌라 등의 공동주택에 거주하고 있다.
이처럼, 대한민국 인구의 절반이상의 사람이 아파트, 빌라 등의 공동주택에 살다 보니, 생활하는 동안 소음이 발생할 수 있다. 이러한 공동주택의 소음의 원인으로는 사람의 보행, 문의 개폐, 기물의 이동이나 설비 기기의 가동 혹은 정지 등이 있을 수 있다. 또한, 공동주택 내의 층에서 충격이 발생되면, 충격에 의해 발생되는 고체 전달음이 사방으로 전달되게 되고, 이로 인하여 건물 구조체의 표면을 진동시킬 뿐만 아니라, 공기 전달음으로 전화되어 주변의 사람들 귀에 들리게 될 때, 소음으로 인식되게 된다.
이러한 공동주택에서 발생하는 소음을 방지하기 위해서 아파트와 같은 건물을 시공할 때, 소음 방지 매트가 사용될 수 있다. 그러나, 소음 방지 매트를 사용한다 하더라도 층간 소음 문제는 여전히 발생하고 있으며, 최근에는 이웃간에 층간 소음으로 인한 다툼이 빈번하게 발생하고, 정부에서도 층간 소음을 줄이기 위한 여러 방안들을 제시하고 있다. 따라서, 층간 소음을 효율적으로 방지할 수 있는 소음 방지 매트의 필요성이 있다.
본 발명의 실시예들은 상기와 같은 배경에 착안하여 발명된 것으로서, 층간 소음을 효율적으로 저감시킬 수 있는 다층구조 매트를 제공하고자 한다.
본 발명의 일 측면에 따르면, 에틸렌초산비닐(ethylene vinyl acetate)을 포함하는 에바층; 다공성 물질을 포함하는 매트층; 및 적어도 폴리염화비닐수지(poly vinyl chloride)를 포함하는 폼층을 포함하는, 다층구조 매트가 제공될 수 있다.
본 발명의 실시예들에 따르면, 층간 소음을 효율적으로 저감시킬 수 있는 효과가 있다.
도 1은 본 발명의 제1 실시예에 따른 다층구조 매트를 절개한 단면 사시도이다.
도 2는 도 1의 정면도이다.
도 3은 본 발명의 제3 실시예에 따른 다층구조 매트를 절개한 단면 사시도이다.
도 4는 도 3의 정면도이다.
도 5는 본 발명의 제1 실시예에 따른 다층구조 매트와 제1 비교예에 따른 매트에 충격이 가해졌을 때, 폼층의 밀도에 따라 측정된 충격음을 비교하여 나타낸 도면이다.
도 6은 본 발명의 제2 실시예에 따른 다층구조 매트와 제2 비교예에 따른 매트에 충격이 가해졌을 때, 폼층의 밀도에 따라 측정된 충격음을 비교하여 나타낸 도면이다.
도 7은 본 발명의 제3 실시예에 따른 다층구조 매트와 제3 비교예에 따른 매트에 충격이 가해졌을 때, 폼층의 밀도에 따라 측정된 충격음을 비교하여 나타낸 도면이다.
도 2는 도 1의 정면도이다.
도 3은 본 발명의 제3 실시예에 따른 다층구조 매트를 절개한 단면 사시도이다.
도 4는 도 3의 정면도이다.
도 5는 본 발명의 제1 실시예에 따른 다층구조 매트와 제1 비교예에 따른 매트에 충격이 가해졌을 때, 폼층의 밀도에 따라 측정된 충격음을 비교하여 나타낸 도면이다.
도 6은 본 발명의 제2 실시예에 따른 다층구조 매트와 제2 비교예에 따른 매트에 충격이 가해졌을 때, 폼층의 밀도에 따라 측정된 충격음을 비교하여 나타낸 도면이다.
도 7은 본 발명의 제3 실시예에 따른 다층구조 매트와 제3 비교예에 따른 매트에 충격이 가해졌을 때, 폼층의 밀도에 따라 측정된 충격음을 비교하여 나타낸 도면이다.
이하에서는 본 발명의 사상을 구현하기 위한 구체적인 실시예에 대하여 도면을 참조하여 상세히 설명하도록 한다.
아울러 본 발명을 설명함에 있어서 관련된 공지 구성 또는 기능에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략한다.
또한, 어떤 구성요소가 다른 구성요소에 '적층', '배치', '접촉'된다고 언급된 때에는 그 다른 구성요소에 직접적으로 적층, 배치, 접촉될 수도 있지만 중간에 다른 구성요소가 존재할 수도 있다고 이해되어야 할 것이다
본 명세서에서 사용된 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로 본 발명을 한정하려는 의도로 사용된 것은 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한 복수의 표현을 포함한다.
또한, 본 명세서에서 상측, 하측, 측면 등의 표현은 도면에 도시를 기준으로 설명한 것이며 해당 대상의 방향이 변경되면 다르게 표현될 수 있음을 미리 밝혀둔다. 마찬가지의 이유로 첨부 도면에 있어서 일부 구성요소는 과장되거나 생략되거나 또는 개략적으로 도시되었으며, 각 구성요소의 크기는 실제 크기를 전적으로 반영하는 것이 아니다.
또한, 제1, 제2 등과 같이 서수를 포함하는 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 해당 구성요소들은 이와 같은 용어들에 의해 한정되지는 않는다. 이 용어들은 하나의 구성요소들을 다른 구성요소로부터 구별하는 목적으로만 사용된다.
명세서에서 사용되는 "포함하는"의 의미는 특정 특성, 영역, 정수, 단계, 동작, 요소 및/또는 성분을 구체화하며, 다른 특정 특성, 영역, 정수, 단계, 동작, 요소, 성분 및/또는 군의 존재나 부가를 제외시키는 것은 아니다.
한편 본 명세서의, 상하 방향은 도 1의 z축 방향일 수 있다. 상 방향은 도 1의 +z축 방향일 수 있다.
이하, 도면을 참조하여 본 발명의 제1 실시예에 따른 다층구조 매트(1)의 구체적인 구성에 대하여 설명한다.
이하, 도 1 및 도 2를 참조하면, 본 발명의 제1 실시예에 따른 다층구조 매트(1)는 아파트와 같은 건물의 층간에 소음을 저감시키기 위하여 사용될 수 있다. 이러한 다층구조 매트(1)는 건물 시공 시 콘크리트 슬래브 상에 배치될 수 있다. 또한, 콘크리트 슬래브 상에 다층구조 매트(1)가 배치되면, 다층구조 매트(1) 상에 배관을 설치한 후, 몰탈을 하여 마감함으로써 건물을 시공할 수 있다. 예를 들어, 콘크리트 슬래브를 커버하는 다층구조 매트(1)는 소음을 저감시킬 수 있고, 열을 잘 전달할 수 있는 재료가 사용될 수 있다.
한편, 건물의 층간에서 발생하는 층간 소음은 경량충격음(Lightweight Impact Sound)와 중량충격음(Heavyweight Impact Sound)로 나뉠 수 있다. 예를 들어, 경량충격음은 식탁이나 의자를 끄는 소리 또는 작은 물건을 떨어트릴 때 발생하는 소리와 같이 충격이 작고 지속시간이 짧은 소음일 수 있다. 또한, 중량충격음은 사람이 뛰어다니면서 발생하는 소리, 망치질 소리 및 큰 물건을 떨어트릴 때 발생하는 소리 등과 같이 충격이 크고 소음의 지속시간이 긴 소음일 수 있다. 이러한 다층구조 매트(1)는 폼층(100), 매트층(200), 접착층(300) 및 에바층(400)을 포함할 수 있다. 또한, 다층구조 매트(1)는 폼층(100), 매트층(200), 접착층(300) 및 에바층(400)이 일 방향을 따라 순차적으로 적층되어 형성될 수 있다.
폼층(100)은 적어도 폴리염화비닐수지(poly vinyl chloride)를 포함할 수 있다. 이러한 폼층(100)은 다층구조 매트(1)의 최하측에 배치될 수 있다. 또한, 폼층(100)의 폴리염화비닐수지는 폐쇄형 셀 폼의 구조(closed cell foam structure)를 가질 수 있다. 이러한 폼층(100)은 폴리염화비닐수지가 폐쇄형 셀 폼의 구조를 가짐으로써, 충격 흡수에 강하며, 소음을 효과적으로 저감시킬 수 있다. 또한, 폼층(100)은 단열재의 역할을 함으로써 열이 방출되는 것을 최소화할 수 있다. 이러한 폐쇄형 셀 폼의 구조는 개방형 셀 폼 구조(open cell foam structure)보다 저주파 영역에서 더 높은 소음 감쇠 효과가 있다. 따라서, 폼층(100)은 중량충격음의 진동에너지를 효과적으로 감쇠시킬 수 있다. 이러한 폼층(100)의 밀도는 130kg/m3 이상 178kg/m3 이하일 수 있다.
매트층(200)은 단열재로서 열이 방출되는 것을 최소화할 수 있다. 이러한 매트층(200)은 매트릭스(210) 및 제1 필러(220)를 포함할 수 있다. 또한, 매트층(200)은 폼층(100) 상에 적층될 수 있다. 한편, 매트릭스(210)는 다공성 물질을 포함할 수 있으며, 이러한 다공성 물질은 발포 폴리스티렌(expanded polystyrene)을 포함할 수 있다. 또한, 제1 필러(220)는 매트릭스(210) 내에 제공될 수 있으며, 제1 필러(220)는 그래파이트 필러(graphite filler)를 포함할 수 있다. 예를 들어, 매트층(200) 내에서 발포 폴리스티렌과 그래파이트 필러는 19.5:0.5 내지 18.5:1.5의 중량 비율을 가질 수 있다. 또한, 매트층(200)의 밀도는 14kg/m3 이상 18kg/m3 이하일 수 있다.
접착층(300)은 폼층(100), 매트층(200) 및 에바층(400) 중 임의의 두 층 사이에 배치되며, 상기 임의의 두 층을 접착시킬 수 있다. 이러한 접착층(300)은 점성을 가진 물질을 포함할 수 있으며, 이러한 점성에 의해 접착층(300)으로 전해진 중량충격음의 진동을 감쇠시킴으로써, 소음을 저감시킬 수 있다. 이러한 접착층(300)은 부틸 고무(butyl rubber), 폴리이소부텐(polyisobutene), 나노클레이 필러(nanoclay filler), C5 레진(C5 resin) 및 폴리부텐(polybutene) 중 하나 이상을 포함할 수 있다. 특히, 접착층(300)의 부틸 고무는 높은 손실계수(loss coefficient)를 가짐으로써, 접착층(300)으로 전해진 중량충격음의 진동에너지를 감쇠시킬 수 있다. 예를 들어, 접착층(300) 내에서 부틸 고무, 폴리이소부텐나노클레이 필러, C5레진 및 폴리부텐은 4:3:6:2:5의 중량 비율을 가질 수 있다.
에바층(400)은 외부로부터 전해지는 중량충격음의 진동을 감쇠시킬 수 있다. 다시 말해, 에바층(400)은 중량충격음의 진동에너지를 감쇠시킴으로써, 소음을 저감시킬 수 있다. 또한, 에바층(400)은 기저부(410) 및 제2 필러(420)를 포함할 수 있다. 이러한 에바층(400)은 접착층(300) 상에 적층될 수 있다. 한편, 기저부(410)는 에틸렌초산비닐(ethylene vinyl acetate)을 포함할 수 있다. 또한, 제2 필러(420)는 기저부(410) 내에 제공될 수 있으며, 에바층(400)에 전해지는 중량충격음의 진동에너지를 감쇠시킬 수 있다. 다시 말해, 에바층(400)에 전해지는 중량충격음은 기저부(410)와 제2 필러(420) 사이의 경계를 지나면서 진동에너지가 감쇠될 수 있다. 이러한 필러(420)는 플레이트 형상을 가지는 카올린 필러(kaolin filler)를 포함할 수 있다. 예를 들어, 카올린 필러는 종횡비(aspect ratio)가 80이상 100이하가 되도록 형성될 수 있다.
한편, 상기 제1 실시예에서의 폼층(100)은 아크릴로니트릴 부타디엔 고무를 비포함할 수도 있지만, 본 발명의 제2 실시예 및 제3 실시예에 따르면, 폼층(100)은 아크릴로니트릴 부타디엔 고무와 같은 고무재료를 더 포함할 수 있다. 이 경우 폼층(100)은 고무를 포함하므로 고무층으로 명명될 수도 있다. 이하, 도 3 및 도 4를 더 참조하여, 본 발명의 제2 실시예 및 제3 실시예를 설명한다. 제2 실시예 및 제3 실시예를 설명함에 있어서, 상술한 실시예와 비교하였을 때의 차이점을 위주로 설명하며 동일한 설명 및 도면부호는 상술한 실시예를 원용한다.
폼층(100)은 고무재료를 더 포함할 수 있다. 이러한 폼층(100)의 고무재료는 아크릴로니트릴 부타디엔 고무(acrylonitrile butadiene rubber)를 포함할 수 있다. 또한, 폼층(100)의 아크릴로니트릴 부타디엔 고무와 폴리염화비닐수지는 2.5:7.5 내지 3.5:6.5의 중량 비율을 가질 수 있다. 이러한 아크릴로니트릴 부타디엔 고무를 포함하는 폼층(100)의 밀도는 150kg/m3 이상 230kg/m3 이하일 수 있다.
한편, 이러한 구성 이외에도, 본 발명의 제3 실시예에 따르면, 접착층(300)은 제1 첩착층(310) 및 제2 접착층(320)을 포함할 수 있다.
제1 첩착층(310)은 부틸 고무(butyl rubber), 폴리이소부텐(polyisobutene), 나노클레이 필러(nanoclay filler), C5 레진(C5 resin) 및 폴리부텐(polybutene) 중 하나 이상을 포함할 수 있다. 이러한 제1 첩착층(310)은 매트층(200)과 에바층(400) 사이에 배치될 수 있다.
제2 접착층(320)은 부틸 고무(butyl rubber), 폴리이소부텐(polyisobutene), 나노클레이 필러(nanoclay filler), C5 레진(C5 resin) 및 폴리부텐(polybutene) 중 하나 이상을 포함할 수 있다. 이러한 제2 접착층(320)은 폼층(100)과 매트층(200) 사이에 배치될 수 있다.
본 발명의 제3 실시예에 따른 다층구조 매트(1)는 폼층(100), 제2 접착층(320), 매트층(200), 제1 첩착층(310), 및 에바층(400)이 일 방향을 따라 순차적으로 적층되어 형성될 수 있다.
이하에서는 상술한 바와 같은 구성을 갖는 다층구조 매트(1)의 효과에 대하여 설명한다.
도 5의 표는 본 발명의 제1 실시예에 따른 다층구조 매트(1)가 바닥면에 설치되었을 때와, 제1 비교에에 따른 매트가 바닥면에 설치되었을 때, 바닥면에 가해지는 충격에 따라 측정되는 충격음을 비교하여 나타낸 것이다. 여기서 실험은 두 가지 충격음(중량충격음과 경량충격음)을 측정하였고, 폼층(100)의 밀도를 변경하면서 폼층(100)의 밀도에 따라 두 가지 충격음을 실험결과로 나타내었다(제1 실시예에 따라 두 번의 실험을 수행하였으며, 각 실험별 폼층(100)의 밀도는 130kg/m3, 170kg/m3이다.).
한편, 제1 비교예에 따른 다층구조 매트(1)와 제1 실시예에 따른 매트는 성분과 층은 동일하고, 폼층(100)의 밀도만 차이를 가진다(제1 비교예에 따라 두 번의 실험을 수행하였으며, 각 실험별 폼층(100)의 밀도는 120kg/m3, 180kg/m3이다). 이러한 두 가지 충격음 중 중량충격음은 뱅머신(bang machine)을 통하여 측정하였으며, 경량충격음은 탭머신(tap machine)을 통하여 측정하였다.
도 5를 참조하면, 본 발명의 제1 실시예에 따른 다층구조 매트(1)는 제1 비교예에 따른 매트 보다 중량충격음뿐만 아니라 경량충격음에서도 낮은 충격음(dB)이 측정되었다. 이처럼, 상대적으로 낮은 충격음이 측정된 것은 같은 충격이 가해질 때, 충격음이 더 낮게 측정된 것으로써, 소음을 보다 잘 차단할 수 있다는 것을 의미한다. 따라서, 제1 실시예에 따른 다층구조 매트(1)는 제1 비교예에 따른 매트보다 층간 소음을 효과적으로 저감시킬 수 있다.
도 6의 표는, 본 발명의 제2 실시예에 따른 다층구조 매트(1)가 바닥면에 설치되었을 때와, 제2 비교에에 따른 매트가 바닥면에 설치되었을 때, 바닥면에 가해지는 충격에 따라 측정되는 충격음을 비교하여 나타낸 것이다. 여기서 실험은 두 가지 충격음(중량충격음과 경량충격음)을 측정하였고, 폼층(100)의 밀도를 변경하면서 폼층(100)의 밀도에 따라 두 가지 충격음을 실험결과로 나타내었다(제2 실시예에 따라 세 번의 실험을 수행하였으며, 각 실험별 폼층(100)의 밀도는 150kg/m3, 190kg/m3, 230kg/m3이다).
한편, 제2 비교예에 따른 다층구조 매트(1)와 제2 실시예에 따른 매트는 성분과 층은 동일하고, 폼층(100)의 밀도만 차이를 가진다(제2 비교예에 따라 두 번의 실험을 수행하였으며, 각 실험별 폼층(100)의 밀도는 130kg/m3, 250kg/m3이다).
도 6을 참조하면, 본 발명의 제2 실시예에 따른 다층구조 매트(1)는 제2 비교예에 따른 매트 보다 중량충격음뿐만 아니라 경량충격음에서도 낮은 충격음(dB)이 측정되었다. 따라서, 제2 실시예에 따른 다층구조 매트(1)는 제2 비교예에 따른 매트보다 층간 소음을 효과적으로 저감시킬 수 있다.
도 7의 표는, 본 발명의 제3 실시예에 따른 다층구조 매트(1)가 바닥면에 설치되었을 때와, 제3 비교에에 따른 매트가 바닥면에 설치되었을 때, 바닥면에 가해지는 충격에 따라 측정되는 충격음을 비교하여 나타낸 것이다(제3 실시예에 따라 세 번의 실험을 수행하였으며, 각 실험별 폼층(100)의 밀도는 150kg/m3, 190kg/m3, 230kg/m3이다).
한편, 제3 비교예에 따른 다층구조 매트(1)와 제3 실시예에 따른 매트는 성분과 층은 동일하고, 폼층(100)의 밀도만 차이를 가진다(제3 비교예에 따라 두 번의 실험을 수행하였으며, 각 실험별 폼층(100)의 밀도는 130kg/m3, 250kg/m3이다).
도 7을 참조하면, 본 발명의 제3 실시예에 따른 다층구조 매트(1)는 제3 비교예에 따른 매트 보다 중량충격음뿐만 아니라 경량충격음에서도 낮은 충격음(dB)이 측정되었다. 따라서, 제3 실시예에 따른 다층구조 매트(1)는 제3 비교예에 따른 매트보다 층간 소음을 효과적으로 저감시킬 수 있다.
하기는 본 발명의 실시예들의 나열이다.
항목 1은 에틸렌초산비닐(ethylene vinyl acetate)을 포함하는 에바층; 다공성 물질을 포함하는 매트층; 및 적어도 폴리염화비닐수지(poly vinyl chloride)를 포함하는 폼층을 포함하는, 다층구조 매트이다.
항목 2는 상기 폼층, 상기 매트층, 및 상기 에바층 중 임의의 두 층 사이에 배치되고, 부틸 고무(butyl rubber)를 포함하는 접착층을 더 포함하는, 다층구조 매트이다.
항목 3은 상기 폼층, 상기 매트층, 상기 접착층 및 상기 에바층은 일 방향을 따라 순차적으로 적층되는, 다층구조 매트이다.
항목 4는 상기 폼층에 포함된 상기 폴리염화비닐수지는 폐쇄형 셀 폼의 구조(closed cell foam structure)를 가지는, 다층구조 매트이다.
항목 5는 상기 폼층은 아크릴로니트릴 부타디엔 고무(acrylonitrile butadiene rubber)인 고무재료를 더 포함하는 다층구조 매트이다.
항목 6은 상기 폼층은 150kg/m3 이상 230kg/m3 이하의 밀도를 가지는, 다층구조 매트이다.
항목 7은 상기 폼층 내에서 상기 아크릴로니트릴 부타디엔 고무와 상기 폴리염화비닐수지는 2.5:7.5 내지 3.5:6.5의 중량 비율을 가지는, 다층구조 매트이다.
항목 8은 부틸 고무(butyl rubber)를 포함하는 제1 접착층; 및 부틸 고무(butyl rubber)를 포함하는 제2 접착층을 더 포함하고, 상기 폼층, 상기 제2 접착층, 상기 매트층, 상기 제1 접착층 및 상기 에바층은 일 방향을 따라 순차적으로 적층되는, 다층구조 매트이다.
항목 9는 상기 매트층은, 상기 다공성 물질을 포함하는 매트릭스; 및
상기 매트릭스 내에 제공되는 제1 필러를 포함하고, 상기 다공성 물질은 폴리스티렌(expanded polystyrene)을 포함하는, 다층구조 매트이다.
항목 10은 상기 제1 필러는 그래파이트 필러(graphite filler)를 포함하는, 다층구조 매트이다.
항목 11은 상기 매트층 내에서 상기 발포 폴리스티렌과 상기 그래파이트 필러는 19.5:0.5 내지 18.5:1.5의 중량 비율을 가지는, 다층구조 매트이다.
항목 12는 상기 매트층의 밀도는 14kg/m3 이상 18kg/m3 이하인, 다층구조 매트이다.
항목 13은 상기 에바층은, 상기 에틸렌초산비닐을 포함하는 기저부; 및
상기 기저부 내에 제공되는 제2 필러를 포함하고, 상기 제2 필러는 플레이트 형상을 가지는 카올린 필러(kaolin filler)를 포함하는, 다층구조 매트이다.
항목 14는 상기 카올린 필러는 종횡비(aspect ratio)가 80이상 100이하가 되도록 형성된, 다층구조 매트이다.
항목 15는 제 2 항에 있어서, 상기 접착층은 폴리이소부텐(polyisobutene), 나노클레이 필러(nanoclay filler), C5 레진(C5 resin) 및 폴리부텐(polybutene) 중 하나 이상을 더 포함하는 다층구조 매트이다.
항목 16은 상기 접착층내에서 상기 부틸 고무, 상기 폴리이소부텐, 상기 나노클레이 필러, C5 레진 및 상기 폴리부텐은 4:3:6:2:5의 중량 비율을 가지는, 다층구조 매트이다.
항목 17은 상기 폼층은 아크릴로니트릴 부타디엔 고무를 비포함하고, 130kg/m3 이상 178kg/m3 이하의 밀도를 가지는, 다층구조 매트이다.
이상 본 발명의 실시예들을 구체적인 실시 형태로서 설명하였으나, 이는 예시에 불과한 것으로서, 본 발명은 이에 한정되지 않는 것이며, 본 명세서에 개시된 기초 사상에 따르는 최광의 범위를 갖는 것으로 해석되어야 한다. 당업자는 개시된 실시형태들을 조합/치환하여 적시되지 않은 형상의 패턴을 실시할 수 있으나, 이 역시 본 발명의 범위를 벗어나지 않는 것이다. 이외에도 당업자는 본 명세서에 기초하여 개시된 실시형태를 용이하게 변경 또는 변형할 수 있으며, 이러한 변경 또는 변형도 본 발명의 권리범위에 속함은 명백하다.
1: 다층구조 매트 100: 폼층
200: 매트층 210: 매트릭스
220: 제1 필러 300: 접착층
310: 제1 접착층 320: 제2 접착층
400: 에바층 410: 기저부
420: 제2 필러
200: 매트층 210: 매트릭스
220: 제1 필러 300: 접착층
310: 제1 접착층 320: 제2 접착층
400: 에바층 410: 기저부
420: 제2 필러
Claims (17)
- 에틸렌초산비닐(ethylene vinyl acetate)을 포함하는 에바층;
다공성 물질을 포함하는 매트층;
폐쇄형 셀 폼의 구조(closed cell foam structure)를 가지는 폴리염화비닐수지(poly vinyl chloride) 및 아크릴로니트릴 부타디엔 고무(acrylonitrile butadiene rubber)인 고무재료를 포함하는 폼층; 및
상기 매트층과 상기 에바층 사이에 배치되고, 부틸 고무(butyl rubber)를 포함하는 제1 접착층을 포함하는,
다층구조 매트. - 삭제
- 제 1 항에 있어서,
상기 폼층, 상기 매트층, 상기 제1 접착층 및 상기 에바층은 일 방향을 따라 순차적으로 적층되는,
다층구조 매트. - 삭제
- 삭제
- 제 1 항에 있어서,
상기 폼층은 150kg/m3 이상 230kg/m3 이하의 밀도를 가지는,
다층구조 매트. - 제 1 항에 있어서,
상기 폼층 내에서 상기 아크릴로니트릴 부타디엔 고무와 상기 폴리염화비닐수지는 2.5:7.5 내지 3.5:6.5의 중량 비율을 가지는,
다층구조 매트. - 제 1 항에 있어서,
부틸 고무(butyl rubber)를 포함하는 제2 접착층을 더 포함하고,
상기 폼층, 상기 제2 접착층, 상기 매트층, 상기 제1 접착층 및 상기 에바층은 일 방향을 따라 순차적으로 적층되는,
다층구조 매트. - 제 1 항에 있어서,
상기 매트층은,
상기 다공성 물질을 포함하는 매트릭스; 및
상기 매트릭스 내에 제공되는 제1 필러를 포함하고,
상기 다공성 물질은 발포 폴리스티렌(expanded polystyrene)을 포함하는,
다층구조 매트. - 제 9 항에 있어서,
상기 제1 필러는 그래파이트 필러(graphite filler)를 포함하는,
다층구조 매트. - 제 10 항에 있어서,
상기 매트층 내에서 상기 발포 폴리스티렌과 상기 그래파이트 필러는 19.5:0.5 내지 18.5:1.5의 중량 비율을 가지는,
다층구조 매트. - 제 1 항에 있어서,
상기 매트층의 밀도는 14kg/m3 이상 18kg/m3 이하인,
다층구조 매트. - 제 1 항에 있어서,
상기 에바층은,
상기 에틸렌초산비닐을 포함하는 기저부; 및
상기 기저부 내에 제공되는 제2 필러를 포함하고,
상기 제2 필러는 플레이트 형상을 가지는 카올린 필러(kaolin filler)를 포함하는,
다층구조 매트. - 제 13 항에 있어서,
상기 카올린 필러는 종횡비(aspect ratio)가 80이상 100이하가 되도록 형성된,
다층구조 매트. - 제 1 항에 있어서,
상기 제1 접착층은 폴리이소부텐(polyisobutene), 나노클레이 필러(nanoclay filler), C5 레진(C5 resin) 및 폴리부텐(polybutene) 중 하나 이상을 더 포함하는,
다층구조 매트. - 제 15 항에 있어서,
상기 제1 접착층내에서 상기 부틸 고무, 상기 폴리이소부텐, 상기 나노클레이 필러, C5 레진 및 상기 폴리부텐은 4:3:6:2:5의 중량 비율을 가지는,
다층구조 매트. - 삭제