KR102179178B1 - Low temperature curable ceramic marker composition - Google Patents
Low temperature curable ceramic marker composition Download PDFInfo
- Publication number
- KR102179178B1 KR102179178B1 KR1020180145606A KR20180145606A KR102179178B1 KR 102179178 B1 KR102179178 B1 KR 102179178B1 KR 1020180145606 A KR1020180145606 A KR 1020180145606A KR 20180145606 A KR20180145606 A KR 20180145606A KR 102179178 B1 KR102179178 B1 KR 102179178B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- resin
- glycol
- low
- Prior art date
Abstract
본 발명은 저온경화형 세라믹 마카 조성물에 관한 것으로, 보다 상세하게는 열경화성 수지, 극성용매, 물, 표면장력조절제, 방부제, 보습제, 분산제 및 안료를 포함하여 마이크로웨이브를 이용한 저온경화가 가능하고, 경화시간을 단축할 수 있으며, 사용접근성 및 소비자 불편을 해소할 수 있는 저온경화형 세라믹 마카 조성물에 관한 것이다.The present invention relates to a low-temperature curing type ceramic marker composition, and more specifically, a thermosetting resin, a polar solvent, water, a surface tension control agent, a preservative, a moisturizing agent, a dispersant, and a pigment, and low-temperature curing using microwaves is possible, and curing time The present invention relates to a low-temperature curing type ceramic marker composition that can shorten the value and relieve user accessibility and consumer inconvenience.
Description
본 발명은 저온경화형 세라믹 마카 조성물에 관한 것으로, 보다 상세하게는 열경화성 수지, 극성용매, 물, 표면장력조절제, 방부제, 보습제, 분산제 및 안료를 포함하여 마이크로웨이브를 이용한 경화가 가능한 저온경화형 세라믹 마카 조성물에 관한 것이다.The present invention relates to a low temperature curing type ceramic marker composition, and more particularly, a low temperature curing type ceramic marker composition capable of curing using microwaves, including a thermosetting resin, a polar solvent, water, a surface tension control agent, a preservative, a moisturizing agent, a dispersant, and a pigment. It is about.
일반적으로 도자기는 일상생활에서 사용되는 그릇이나 다양한 가재도구 및 술병 등으로 많이 사용되고 있다. 이러한 도자기는 보편적으로 그 용도에 부합되는 형상으로 성형하여 건조시킨 다음, 그 표면에 이미지나 색깔을 넣고 가마에서 약한 온도로 초벌구이를 한 후, 유약처리를 하며, 다시 가마에서 높은 온도로 재벌구이를 하여 완성하게 된다. In general, ceramics are widely used as bowls used in everyday life, various household items, and wine bottles. These ceramics are generally molded into a shape suitable for their purpose, dried, and then unglazed at a low temperature in a kiln, followed by an image or color on the surface, then glazed, and then roasted at a high temperature in a kiln. To complete it.
이와 같은 제조과정을 통해 완성된 도자기의 표면에는 마커를 이용하여 이미지를 인쇄하게 되는데, 기존에는 인쇄된 마커를 경화시키기 위하여 오븐을 이용해야만 하였다. 또한 오븐을 이용한 경화 시에는 오븐의 예열한 후 도자기를 가열하고, 가열된 도자기를 식히는 등 높은 온도를 유지해야하는 오븐을 반드시 이용해야했고, 제작이 번거롭고 하나의 제품을 만드는데 많은 시간이 소요되기 때문에 예술품을 제작하는 데에는 적합할지 몰라도 일상생활에서 사용되는 도자기제품을 대량생산하기에는 부적합한 문제점이 있었다. Images are printed using markers on the surface of ceramics completed through such a manufacturing process, but conventionally, an oven had to be used to cure the printed markers. In addition, when curing using an oven, it is necessary to use an oven that has to maintain a high temperature, such as preheating the oven, heating the ceramics, and cooling the heated ceramics. Because the production is cumbersome and it takes a lot of time to make a single product, art works Although it may be suitable for manufacturing, there is a problem that is not suitable for mass production of ceramic products used in everyday life.
이에, 도자기 표면에 전사지 인쇄 방법을 통해 이미지를 부착하여 제작하는 방법이 개발되었으나, 전사지 인쇄 방법에 따라 전사지를 제조하는 공정에서 인쇄된 인쇄물 등이 종이 위에 직접적으로 오프셋 인쇄되어 인쇄물이 종이에 흡수 고착되는 문제점이 있으며, 전사공정 때에 인쇄물이 종이로부터 쉽게 분리되지 않거나 인쇄층의 선명도가 현저하게 떨어지는 문제점이 있었다.Accordingly, a method of attaching an image to the porcelain surface through the transfer paper printing method has been developed, but the printed material printed in the process of manufacturing the transfer paper according to the transfer paper printing method is directly offset printed on the paper so that the printed material is absorbed and fixed to the paper. There is a problem that the printing is not easily separated from the paper during the transfer process or there is a problem that the sharpness of the print layer is remarkably deteriorated.
상기와 같은 종래기술의 문제점을 해결하고자, 본 발명은 마이크로웨이브를 이용한 경화가 가능한 저온경화형 세라믹 마카 조성물을 제공하는 것을 목적으로 한다.In order to solve the problems of the prior art as described above, an object of the present invention is to provide a low-temperature curing type ceramic marker composition capable of curing using microwaves.
또한 본 발명은 저온경화가 가능하고, 경화시간을 단축할 수 있어 사용접근성 및 소비자 불편을 해소할 수 있는 저온경화형 세라믹 마카 조성물 및 이를 이용한 도자기 표면의 인쇄방법을 제공하는 것을 목적으로 한다.In addition, an object of the present invention is to provide a low-temperature curing type ceramic marker composition capable of low-temperature curing and shortening the curing time, thereby reducing accessibility and consumer inconvenience, and a printing method of a ceramic surface using the same.
상기 목적을 달성하기 위하여, 본 발명은 열경화성 수지, 극성용매, 물, 표면장력조절제, 방부제, 보습제, 분산제 및 안료를 포함하는 저온경화형 세라믹 마카 조성물을 제공한다.In order to achieve the above object, the present invention provides a low temperature curing type ceramic marker composition comprising a thermosetting resin, a polar solvent, water, a surface tension regulator, a preservative, a moisturizing agent, a dispersant and a pigment.
또한 본 발명은 상기의 저온경화형 세라믹 마카 조성물을 이용하여 도자기 표면에 이미지를 인쇄하는 단계 및 상기 이미지가 인쇄된 도자기를 마이크로웨이브에서 경화시키는 단계를 포함하는 도자기 표면의 인쇄방법을 제공한다.In addition, the present invention provides a method for printing a surface of porcelain including printing an image on the surface of porcelain using the low-temperature curing type ceramic marker composition and curing the porcelain on which the image is printed in a microwave.
본 발명의 저온경화형 세라믹 마카 조성물은 마이크로웨이브를 이용한 경화가 가능하고, 경화시간을 단축할 수 있어 사용접근성 및 소비자 불편을 해소할 수 있다.The low-temperature curing ceramic marker composition of the present invention can be cured using microwaves and can shorten the curing time, thereby reducing accessibility and consumer inconvenience.
이하 본 발명을 상세히 설명한다. Hereinafter, the present invention will be described in detail.
본 발명은 마이크로웨이브를 이용한 경화가 가능한 저온경화형 세라믹 마카 조성물에 관한 것으로, 본 발명의 저온경화형 세라믹 마카 조성물을 이용하여 표면에 이미지가 인쇄된 도자기는 고온의 오븐을 이용하지 않고도 마이크로웨이브를 이용한 저온경화가 가능하고, 경화시간 또한 2~30분 정도로 단축시킬 수 있어 도자기 제작이 용이하며, 사용접근성 및 소비자의 불편을 해소할 수 있다.The present invention relates to a low-temperature curing type ceramic marker composition capable of curing using microwaves, and ceramics with an image printed on the surface using the low-temperature curing type ceramic marker composition of the present invention use a microwave without using a high-temperature oven. It is possible to cure, and the curing time can be shortened to about 2 to 30 minutes, making it easy to manufacture ceramics, and it is possible to reduce the user's accessibility and inconvenience to consumers.
이러한 본 발명의 저온경화형 세라믹 마카 조성물은 열경화성 수지, 극성용매, 물, 표면장력조절제, 방부제, 보습제, 분산제 및 안료를 포함한다.The low-temperature curing ceramic marker composition of the present invention includes a thermosetting resin, a polar solvent, water, a surface tension regulator, a preservative, a moisturizing agent, a dispersant, and a pigment.
상기 열경화성 수지는 페놀계 수지, 폴리에스테르계 수지, 베이클라이트 수지, 아미노계 수지, 테플론계 수지, 멜라민계 수지, 폴리우레탄계 수지, 에폭시계 수지, 아크릴계 수지 등을 사용할 수 있다. 그 함량은 조성물 총 100중량부에 대하여 5~80중량부로 포함될 수 있으며, 그 함량이 상기 범위 내일 경우에는 접착력이 우수하며, 정밀하고 선명한 이미지를 유지할 수 있다. The thermosetting resin may be a phenol resin, a polyester resin, a bakelite resin, an amino resin, a Teflon resin, a melamine resin, a polyurethane resin, an epoxy resin, an acrylic resin, or the like. The content may be included in an amount of 5 to 80 parts by weight based on a total of 100 parts by weight of the composition, and when the content is within the above range, adhesion is excellent and a precise and clear image can be maintained.
상기 극성용매는 에틸렌글리콜, 프로필렌글리콜, 다이에틸렌글리콜, 트라이에틸렌글리콜, 다이프로필렌글리콜, 글리세린, 폴리에틸렌글라이콜(200~6,000), 부틸렌글리콜, 폴리프로필렌글리콜(400~2,000) 등의 글리콜류, 에탄올, 프로판올, 이소프로필알코올 등의 알코올류 등을 사용할 수 있다. 그 함량은 조성물 총 100중량부에 대하여 1~40중량부로 포함될 수 있으며, 그 함량이 상기 범위 내인 경우에는 마이크로웨이브에서 최적의 경화능을 나타낼 수 있다. The polar solvent is glycols such as ethylene glycol, propylene glycol, diethylene glycol, triethylene glycol, dipropylene glycol, glycerin, polyethylene glycol (200-6,000), butylene glycol, and polypropylene glycol (400-2,000) , Alcohols such as ethanol, propanol, and isopropyl alcohol can be used. The content may be included in an amount of 1 to 40 parts by weight based on a total of 100 parts by weight of the composition, and when the content is within the above range, the optimum curing ability may be exhibited in microwave.
상기 물은 총 100중량부에 대하여 2~60중량부로 포함될 수 있다. The water may be included in an amount of 2 to 60 parts by weight based on a total of 100 parts by weight.
상기 표면장력조절제로는 양이온계 계면화성제, 음이온계 계면활성제, 양쪽성계 계면활성제, 비이온계 계면활성제, 실리카 및 실리케이트류, 실리콘류 등이 사용될 수 있으며, 그 함량은 조성물 총 100중량부에 대하여 0.01~10중량부로 포함될 수 있다. As the surface tension control agent, cationic surfactants, anionic surfactants, amphoteric surfactants, nonionic surfactants, silica and silicates, silicones, etc. may be used, and the content is 100 parts by weight of the composition. It may be included in an amount of 0.01 to 10 parts by weight.
상기 방부제는 안식향산, 안식향산염류, 살리실산, 살리실산염류, 페놀, 솔빈산과 그 염류, 디하이드로초산 및 그 염류, 파라옥시안식향산에스테르(파라벤)류, 클로로크레졸, 헥사클로로펜, 레조르신, 이소프로필메틸 페놀, 오르소페닐 페놀, 염화벤잘코늄, 염산클로로헥시딘, 글루콘산클로로헥시딘, 브롬화 알킬이소퀴솔리니움, 트리클로로카르바닐리드, 할로카르반, 감광소 201호, 페녹시 에탄올, 트리클로로하이드록시디페닐에테르(트리클로산), 메틸클로로이소티아졸리논, 메틸이소티아졸리논, 비사보롤, 염산알킬디아미노에틸글리신 등이 사용될 수 있으며, 그 함량은 조성물 총 100중량부에 대하여 0.001~3중량부로 포함될 수 있다. The preservatives are benzoic acid, benzoate, salicylic acid, salicylate, phenol, sorbic acid and its salts, dihydroacetic acid and its salts, paraoxybenzoic acid ester (paraben), chlorocresol, hexachlorophene, resorcin, isopropylmethyl phenol , Orthophenyl phenol, benzalkonium chloride, chlorohexidine hydrochloride, chlorohexidine gluconate, alkyl isoquisolium bromide, trichlorocarvanilide, halocarban, photosensitive spot 201, phenoxy ethanol, trichloro Hydroxydiphenyl ether (triclosan), methylchloroisothiazolinone, methylisothiazolinone, bisabolol, alkyldiaminoethylglycine hydrochloride, etc. may be used, and the content is 0.001~ based on 100 parts by weight of the total composition. It may be included in 3 parts by weight.
상기 보습제는 알킬화, 아릴화, 복소환화, 에스테르화, 에테르화, 할로겐화, 아미드화,히드록실화, 아미노화 등이 치환된 다가알코올유도체, 글리콜에테르유도체, 알킬아민유도체, 요소유도체, 카르복실산 및그염의유도체, 아미노산및그염의유도체, 당유도체 등의 유도체; 수산기가 1개 또는 2개인 보습제로, 에틸렌글리콜, 프로필렌글리콜, 디에틸렌글리콜, 트리에틸렌글리콜, 테트라에틸렌글리콜, 폴리에틸렌글리콜, 티오디에틸렌글리콜, 디티오디글리콜, 2-메틸-1,3-프로판디올 등의 다가알코올류; 에틸렌글리콜모노메틸에테르, 에틸렌글리콜모노에틸에테르, 디에틸렌글리콜모노메틸에테르, 디에틸렌글리콜모노에틸에테르, 트리에틸렌글리콜모노에틸에테르, 트리에틸렌글리콜모노부틸에테르 등의 다가알코올의 저급알킬에테르류; 에탄올아민, 디에탄올아민, N-메틸디에탄올아민, N-에틸디에탄올아민, 세린, 호모세린 등의 아민류; 2-히드록시에틸-2-피롤리돈 등의 복소환류; 수산기가 3개 이상인 보습제로, 글리세린, 에리스리톨, 시클로헥산트리올, 부탄트리올, 트리스히드록시메틸에탄, 트리메티롤프로판, 트리메티롤에탄, 1,2,6-헥산트리올, 헵탄트리올, 트레이톨, 아도니톨, 크실리톨, 소르비톨, 만니톨, 이노시톨, 벤젠트리올 등의 다가알코올류; 디펜타에리스리톨 등의 에테르유도체; 트리에탄올아민, 트리스히드록시메틸아미노메탄, 테트라키스히드록시프로필에틸렌디아민, 펜트롤, 글루코사민, 히알루론산나트륨 등의 알코올아민류; 테트라히드록시에틸요소 등의 요소유도체 등;이 사용될 수 있다. 상기 보습제는 조성물 총 100중량부에 대하여 0.05~1중량부로 포함될 수 있다. The moisturizing agent is a polyhydric alcohol derivative substituted with alkylation, arylation, heterocyclization, esterification, etherification, halogenation, amidation, hydroxylation, amination, etc., glycol ether derivatives, alkylamine derivatives, urea derivatives, carboxylic acids And derivatives of the salt, amino acids and derivatives of the salt, and derivatives such as sugar derivatives; Moisturizing agent with one or two hydroxyl groups, ethylene glycol, propylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, polyethylene glycol, thiodiethylene glycol, dithiodiglycol, 2-methyl-1,3-propanediol Polyhydric alcohols such as; Lower alkyl ethers of polyhydric alcohols such as ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, triethylene glycol monoethyl ether, and triethylene glycol monobutyl ether; Amines such as ethanolamine, diethanolamine, N-methyl diethanolamine, N-ethyl diethanolamine, serine, and homoserine; Hetero-reflux, such as 2-hydroxyethyl-2-pyrrolidone; As a moisturizing agent with three or more hydroxyl groups, glycerin, erythritol, cyclohexanetriol, butanetriol, trishydroxymethylethane, trimethyrolpropane, trimethyrolethane, 1,2,6-hexanetriol, heptanetriol , Polyhydric alcohols such as traitol, adonitol, xylitol, sorbitol, mannitol, inositol, and benzenetriol; Ether derivatives such as dipentaerythritol; Alcohol amines such as triethanolamine, trishydroxymethylaminomethane, tetrakishydroxypropylethylenediamine, pentrol, glucosamine and sodium hyaluronate; Urea derivatives such as tetrahydroxyethyl urea, etc.; can be used. The moisturizing agent may be included in an amount of 0.05 to 1 parts by weight based on 100 parts by weight of the total composition.
상기 분산제는 나프탈렌술폰산나트륨-포르말린 축합물, 알킬나프탈렌술폰산나트륨 또는 그의 포르말린축합물, 페놀술폰산나트륨과나프톨술폰산나트륨의 포르말린축합물(Tamol계), 알킬디페닐 에테르 디술폰산 나트륨, 리그닌술폰산 나트륨, 비이온계 계면활성제 폴리옥시에틸렌 알킬(알릴)에테르, 비이온계 계면활성제+음이온 계면활성제 혼합조제, 비이온계 계면활성제와 술폰(sulphone)화물, 폴리아크릴산나트륨, 올레핀-말레인산나트륨 공중합체, 축합인산염, 카르복시메틸셀룰로스, 알킬벤젠(나프탈렌)술폰산염, 디옥틸술폰말레인산나트륨, 스티렌-무수말레인산 공중합체의부분아미드화/부분에스테르화물, 아민유도체 등이 사용될 수 있으며, 그 함량은 조성물 총 100중량부에 대하여 0.01~5중량부로 사용될 수 있다. The dispersant is sodium naphthalene sulfonate-formalin condensate, sodium alkylnaphthalene sulfonate or formalin condensate thereof, formalin condensate of sodium phenol sulfonate and sodium naphthol sulfonate (Tamol system), alkyldiphenyl ether disulfonate sodium, lignin sulfonate sodium, bi Ionic surfactant polyoxyethylene alkyl (allyl) ether, nonionic surfactant + anionic surfactant mixing aid, nonionic surfactant and sulfone product, sodium polyacrylate, olefin-sodium maleate copolymer, condensed phosphate , Carboxymethylcellulose, alkylbenzene (naphthalene) sulfonate, sodium dioctyl sulfone maleate, partial amidation/partial esterification of styrene-maleic anhydride copolymer, amine derivatives, etc. can be used, the content of which is a total of 100 parts by weight of the composition It can be used in an amount of 0.01 to 5 parts by weight.
상기 안료는 Pigment Blue(15, 60, 16, 7, 61, 29, 28), Pigment Orange(34, 36, 13, 73, 71, 86, 43, 67), Pigment Green(58, 7, 36, 8, 17, 21), Pigment Red(254, 122, 177, 269, 104, 101, 185, 81), Pigment Yellow(138, 139, 83, 183, 34, 180, 12, 14, 150), Pigment Violet(23, 19, 15, 3, 27, 29), Pigment Black(7, 1, 28, 6, 26, 11), 카본블랙 등이 사용될 수 있으며, 그 함량은 조성물 총 100중량부에 대하여 0.1~40중량부로 사용될 수 있다. The pigments are Pigment Blue (15, 60, 16, 7, 61, 29, 28), Pigment Orange (34, 36, 13, 73, 71, 86, 43, 67), Pigment Green (58, 7, 36, 8, 17, 21), Pigment Red(254, 122, 177, 269, 104, 101, 185, 81), Pigment Yellow(138, 139, 83, 183, 34, 180, 12, 14, 150), Pigment Violet (23, 19, 15, 3, 27, 29), Pigment Black (7, 1, 28, 6, 26, 11), carbon black, etc. can be used, and the content is 0.1 per 100 parts by weight of the total composition. It can be used in ~40 parts by weight.
이상과 같은 성분으로 이루어진 본 발명의 저온경화형 세라믹 마카 조성물은 저온에서도 경화가 가능하며, 특히 250~2,000W의 마이크로웨이브에 2~30분간 노출하여도 경화가 가능하다.The low-temperature curing type ceramic marker composition of the present invention made of the above components can be cured even at low temperatures, and in particular, can be cured even when exposed to a microwave of 250 to 2,000 W for 2 to 30 minutes.
이에 본 발명은 상기 저온경화형 세라믹 마카 조성물을 이용한 도자기 표면의 인쇄방법을 제공하는 바, 상기 방법은 전술한 저온경화형 세라믹 마카 조성물을 이용하여 도자기 표면에 이미지를 인쇄하는 단계 및 상기 이미지가 인쇄된 도자기를 마이크로웨이브에서 경화시키는 단계를 포함한다.Accordingly, the present invention provides a method for printing a surface of porcelain using the low-temperature curing type ceramic marker composition, the method comprising: printing an image on the surface of porcelain using the aforementioned low-temperature curing type ceramic marker composition, and the porcelain on which the image is printed Curing in a microwave.
상기 저온경화형 세라믹 마카 조성물을 이용한 이미지 인쇄방법은 통상의 마카를 이용하여 도자기 표면에 이미지를 인쇄하는 방법과 동일한 방법으로 수행될 수 있음은 물론이며, 이렇게 본 발명의 저온경화형 세라믹 마카 조성물로 이미지가 인쇄된 도자기는 마이크로웨이브를 이용한 저온경화가 가능하다. 즉, 상기 저온경화형 세라믹 마카 조성물로 이미지가 인쇄된 도자기는 250~2,000W의 마이크로웨이브에서 2~30분간의 작업으로 완전히 경화될 수 있으며, 이렇게 형성된 이미지는 도자기에의 접착력이 우수하여 제조 후에도 이미지의 들뜸이나 탈락이 없으며, 보다 정밀하고 선명한 이미지를 유지할 수 있다. The image printing method using the low-temperature curing type ceramic marker composition can be performed in the same manner as the method of printing an image on the surface of porcelain using a conventional marker. In this way, the image is obtained with the low-temperature curing type ceramic marker composition of the present invention. Printed ceramics can be cured at low temperatures using microwaves. That is, the ceramics printed with the image with the low-temperature curing type ceramic marker composition can be completely cured in a microwave of 250 to 2,000 W for 2 to 30 minutes, and the image formed in this way has excellent adhesion to ceramics and is therefore an image after manufacture. There is no lifting or dropping of the image, and more precise and clear images can be maintained.
또한 본 발명의 저온경화형 세라믹 마카 조성물을 이용한다면 기존의 160~1705℃ 정도까지 예열한 후 도자기를 넣고 30~50분간 가열하여 식히는 과정을 요하는 오븐을 이용한 도자기의 제조방법과는 달리, 마이크로웨이브를 이용한 저온경화로 경화시간을 단축할 수 있고 사용접근성 및 소비자 불편을 해소할 수 있어 보다 용이한 방법으로 도자기의 제조가 가능하다.In addition, if the low-temperature curing type ceramic marker composition of the present invention is used, unlike the conventional method of manufacturing ceramics using an oven that requires preheating to about 160 to 1705°C and then heating and cooling for 30 to 50 minutes, microwave It is possible to shorten the curing time by using low temperature curing, and to eliminate the user's inconvenience and accessibility to use, so that it is possible to manufacture ceramics in an easier way.
이하에서는 실시예를 들어 본 발명에 관하여 더욱 상세하게 설명할 것이나. 이들 실시예는 단지 설명의 목적을 위한 것으로 본 발명의 보호 범위를 제한하고자 하는 것은 아니다.Hereinafter, the present invention will be described in more detail by way of examples. These examples are for illustrative purposes only and are not intended to limit the protection scope of the present invention.
실시예 1Example 1
페놀계 수지 50중량부, 프로필렌글리콜 20중량부, 물 40중량부, 실리카 5중량부, 파라옥시안식향산에스테르 1중량부, 테트라키스히드록시프로필에틸렌디아민 0.1중량부, 카르복시메틸셀룰로스 1중량부 및 카본블랙 15중량부를 혼합하여 저온경화형 세라믹 마카 조성물을 제조하였다. 50 parts by weight of phenolic resin, 20 parts by weight of propylene glycol, 40 parts by weight of water, 5 parts by weight of silica, 1 part by weight of paraoxybenzoic acid ester, 0.1 part by weight of tetrakishydroxypropylethylenediamine, 1 part by weight of carboxymethylcellulose and carbon 15 parts by weight of black was mixed to prepare a low-temperature curing ceramic marker composition.
실시예 2Example 2
멜라민계 수지 45중량부, 이소프로필알코올 18중량부, 물 40중량부, 실리카 5중량부, 파라옥시안식향산에스테르 1중량부, 테트라키스히드록시프로필에틸렌디아민 0.1중량부, 카르복시메틸셀룰로스 1중량부 및 카본블랙 15중량부를 혼합하여 저온경화형 세라믹 마카 조성물을 제조하였다. 45 parts by weight of melamine resin, 18 parts by weight of isopropyl alcohol, 40 parts by weight of water, 5 parts by weight of silica, 1 part by weight of paraoxybenzoic acid ester, 0.1 part by weight of tetrakishydroxypropylethylenediamine, 1 part by weight of carboxymethylcellulose, and 15 parts by weight of carbon black was mixed to prepare a low-temperature curing ceramic marker composition.
실시예 3Example 3
폴리우레탄계 수지 48중량부, 글리세린 18중량부, 물 40중량부, 실리카 5중량부, 파라옥시안식향산에스테르 1중량부, 테트라키스히드록시프로필에틸렌디아민 0.1중량부, 카르복시메틸셀룰로스 1중량부 및 카본블랙 15중량부를 혼합하여 저온경화형 세라믹 마카 조성물을 제조하였다. 48 parts by weight of polyurethane resin, 18 parts by weight of glycerin, 40 parts by weight of water, 5 parts by weight of silica, 1 part by weight of paraoxybenzoic acid ester, 0.1 part by weight of tetrakishydroxypropylethylenediamine, 1 part by weight of carboxymethylcellulose, and carbon black 15 parts by weight was mixed to prepare a low-temperature curing ceramic marker composition.
실시예 4Example 4
아크릴계 수지 50중량부, 프로필렌글리콜 20중량부, 물 40중량부, 실리카 5중량부, 파라옥시안식향산에스테르 1중량부, 테트라키스히드록시프로필에틸렌디아민 0.1중량부, 카르복시메틸셀룰로스 1중량부 및 카본블랙 15중량부를 혼합하여 저온경화형 세라믹 마카 조성물을 제조하였다. Acrylic resin 50 parts by weight, propylene glycol 20 parts by weight, water 40 parts by weight, silica 5 parts by weight, paraoxybenzoic acid ester 1 part by weight, tetrakishydroxypropylethylenediamine 0.1 parts by weight, carboxymethylcellulose 1 part by weight and carbon black 15 parts by weight was mixed to prepare a low-temperature curing ceramic marker composition.
실시예 5Example 5
테플론계 수지 50중량부, 이소프로필알코올 20중량부, 물 40중량부, 실리카 5중량부, 파라옥시안식향산에스테르 1중량부, 테트라키스히드록시프로필에틸렌디아민 0.1중량부, 카르복시메틸셀룰로스 1중량부 및 카본블랙 15중량부를 혼합하여 저온경화형 세라믹 마카 조성물을 제조하였다. Teflon-based resin 50 parts by weight, isopropyl alcohol 20 parts by weight, water 40 parts by weight, silica 5 parts by weight, paraoxybenzoic acid ester 1 part by weight, tetrakishydroxypropylethylenediamine 0.1 part by weight, carboxymethylcellulose 1 part by weight and 15 parts by weight of carbon black was mixed to prepare a low-temperature curing ceramic marker composition.
실시예 6~10Examples 6-10
상기 실시예 1 내지 5에서 제조한 저온경화형 세라믹 마카 조성물을 각각 이용하여 도자기 표면에 이미지를 인쇄하였다. 그 다음 상기 도자기를 1,000W의 마이크로웨이브에서 15분간 경화시키고, 10분간 식힌 후 마이크로웨이브에서 꺼내었다.Images were printed on the surface of ceramics using each of the low-temperature curing ceramic marker compositions prepared in Examples 1 to 5 above. Then, the ceramics were cured in a microwave of 1,000 W for 15 minutes, cooled for 10 minutes, and then removed from the microwave.
비교예 1Comparative Example 1
통상의 마카를 이용하여 이미지가 인쇄된 도자기를 기존의 방법에 따라 오븐을 이용하여 경화시켰다. 오븐을 165℃로 예열한 후, 165℃의 온도에 도달하면 상기 도자기를 넣고 40분간 가열하였다. 시간이 경과한 후 도자기를 식힌 후 오븐에서 꺼내었다. Porcelain on which the image was printed using a conventional marker was cured using an oven according to a conventional method. After preheating the oven to 165° C., when the temperature reached 165° C., the ceramics were placed and heated for 40 minutes. After a period of time, the ceramics were cooled and removed from the oven.
상기와 같이 본 발명에 따라 저온경화형 세라믹 마카 조성물을 이용하여 이미지를 형성한 실시예 6~10의 경우에는 165℃라는 고열을 요하는 오븐을 사용하지 않고도 마이크로웨이브를 이용하여 간단한 방법으로 저온경화하여 도자기를 제조할 수 있었으며, 그 시간 또한 기존의 오븐을 이용한 비교예 1과 대비하여 현저히 단축할 수 있었다. 반면, 기존의 방법에 따라 통상의 마카로 이미지가 형성된 비교예 1의 도자기는 고열의 오븐을 이용하여야만 경화가 가능하였으며, 오븐의 예열, 가열시간 등의 복잡한 공정과 장시간이 소요되었다. In the case of Examples 6 to 10 in which the image was formed using the low-temperature curing type ceramic marker composition according to the present invention as described above, the low-temperature curing was performed using a microwave without using an oven requiring high heat of 165°C. Ceramics could be manufactured, and the time could also be significantly shortened compared to Comparative Example 1 using a conventional oven. On the other hand, the porcelain of Comparative Example 1, in which the image of a conventional maca was formed according to the existing method, was cured only by using a high-heat oven, and it took a long time and complicated processes such as preheating and heating time of the oven.
이렇게 본 발명에 따른 저온경화형 세라믹 마카 조성물을 이용한다면 마이크로웨이브를 이용하여 저온에서 단시간 동안의 경화가 가능하여 도자기 제조시간을 단축할 수 있으며, 사용 및 제조가 용이하여 소비자의 접근성을 높이고, 불편을 해소할 수 있어 보다 용이한 방법으로 도자기의 제조가 가능하다. 뿐만 아니라, 본 발명에 따른 저온경화형 세라믹 마카 조성물로 형성된 이미지는 도자기에의 접착력이 우수하여 제조 후 일상에서 사용 시에도 장기간이 지나도 이미지의 들뜸이나 탈락이 없으며, 보다 정밀하고 선명한 이미지를 유지할 수 있다. In this way, if the low-temperature curing type ceramic marker composition according to the present invention is used, it is possible to cure at a low temperature for a short period of time using microwaves, thereby reducing the time to manufacture ceramics, and increasing the accessibility of consumers and reducing inconvenience due to ease of use and manufacturing. Since it can be solved, it is possible to manufacture ceramics in an easier way. In addition, the image formed with the low-temperature curing type ceramic marker composition according to the present invention has excellent adhesion to ceramics, so there is no lifting or dropping of the image even after a long period of time even when used in daily life after manufacture, and a more precise and clear image can be maintained. .
비록 본 발명이 상기에 언급된 바람직한 실시예로서 설명되었으나, 발명의 요지와 범위로부터 벗어남이 없이 다양한 수정이나 변형을 하는 것이 가능하다. 또한 첨부된 청구 범위는 본 발명의 요지에 속하는 이러한 수정이나 변형을 포함한다.Although the present invention has been described as the above-mentioned preferred embodiment, it is possible to make various modifications or variations without departing from the gist and scope of the invention. In addition, the appended claims include such modifications or variations that fall within the gist of the present invention.
Claims (7)
상기 세라믹 마카 조성물은, 조성물 총 100중량부에 대하여
열경화성 수지 5~80중량부, 극성용매 1~40중량부, 물 2~60중량부, 표면장력조절제 0.01~10중량부, 방부제 0.001~3중량부, 보습제 0.05~1중량부, 분산제 0.01~5중량부 및 안료 0.1~40중량부를 포함하며;
상기 열경화성 수지는 페놀계 수지, 폴리에스테르계 수지, 베이클라이트 수지, 아미노계 수지, 테플론계 수지, 멜라민계 수지, 폴리우레탄계 수지, 에폭시계 수지 및 아크릴계 수지 중 선택된 어느 하나 이상이며;
상기 극성용매는 에틸렌글리콜, 프로필렌글리콜, 다이에틸렌글리콜, 트라이에틸렌글리콜, 다이프로필렌글리콜, 글리세린, 폴리에틸렌글리콜, 부틸렌글리콜 및 폴리프로필렌글리콜 중 선택되는 어느 하나 이상의 글리콜류 또는 에탄올, 프로판올 및 이소프로필알코올 중 선택되는 어느 하나 이상의 알코올류이고;
상기 저온경화형 세라믹 마카 조성물은 250~2,000W의 마이크로웨이브에서 2~30분간 노출 시 경화되는 것으로 이루어진 것을 특징으로 하는 도자기 표면의 인쇄방법.Printing an image on the surface of ceramics using a low-temperature curing type ceramic marker composition containing a thermosetting resin, a polar solvent, water, a surface tension control agent, a preservative, a moisturizing agent, a dispersant, and a pigment, and the ceramic on which the image is printed in a microwave To cure, the curing is carried out in a microwave of 250 ~ 2,000W for 2 ~ 30 minutes;
The ceramic maca composition, based on a total of 100 parts by weight of the composition
Thermosetting resin 5 to 80 parts by weight, polar solvent 1 to 40 parts by weight, water 2 to 60 parts by weight, surface tension control agent 0.01 to 10 parts by weight, preservative 0.001 to 3 parts by weight, moisturizer 0.05 to 1 parts by weight, dispersant 0.01 to 5 Includes 0.1 to 40 parts by weight and pigment;
The thermosetting resin is at least one selected from a phenolic resin, a polyester resin, a bakelite resin, an amino resin, a Teflon resin, a melamine resin, a polyurethane resin, an epoxy resin and an acrylic resin;
The polar solvent is any one or more glycols selected from ethylene glycol, propylene glycol, diethylene glycol, triethylene glycol, dipropylene glycol, glycerin, polyethylene glycol, butylene glycol and polypropylene glycol, or ethanol, propanol and isopropyl alcohol Any one or more alcohols selected from among;
The low-temperature curing ceramic marker composition is cured when exposed to a microwave of 250 to 2,000 W for 2 to 30 minutes.