KR101996727B1 - Method for manufacturing a laminated glass with an inserted film - Google Patents

Method for manufacturing a laminated glass with an inserted film Download PDF

Info

Publication number
KR101996727B1
KR101996727B1 KR1020170115716A KR20170115716A KR101996727B1 KR 101996727 B1 KR101996727 B1 KR 101996727B1 KR 1020170115716 A KR1020170115716 A KR 1020170115716A KR 20170115716 A KR20170115716 A KR 20170115716A KR 101996727 B1 KR101996727 B1 KR 101996727B1
Authority
KR
South Korea
Prior art keywords
transparent plastic
layer
glass
soft
soft transparent
Prior art date
Application number
KR1020170115716A
Other languages
Korean (ko)
Other versions
KR20190028884A (en
Inventor
첸 스티븐
Original Assignee
이-리드 일렉트로닉 코포레이션, 리미티드
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이-리드 일렉트로닉 코포레이션, 리미티드 filed Critical 이-리드 일렉트로닉 코포레이션, 리미티드
Priority to KR1020170115716A priority Critical patent/KR101996727B1/en
Publication of KR20190028884A publication Critical patent/KR20190028884A/en
Application granted granted Critical
Publication of KR101996727B1 publication Critical patent/KR101996727B1/en

Abstract

제1 연질 투명 플라스틱층에 수용 홀을 형성하는 단계; 제1 유리층 상에 제1 연질 투명 플라스틱층을 배치하는 단계; 삽입 된 필름을 포함하는 연질 플라스틱 샌드위치를 수용 홀에 넣고, 상기 연질 플라스틱 샌드위치의 두께는 상기 수용 홀의 깊이 이하로 하는 단계; 제2 유리층으로 피복하고, 제1 유리층 및 제2 유리층을 공구로 클램핑하는 단계; 버블 링; 고온 고압으로 접착하는 방법. 이 방법은 접합 유리의 넓은 영역 대신에 작은 영역에 필름을 삽입할 수 있어서 생산 비용을 절감할 수 있다.Forming a receiving hole in the first soft transparent plastic layer; Disposing a first flexible transparent plastic layer on the first glass layer; Inserting a soft plastic sandwich comprising the inserted film into a receiving hole and making the thickness of the soft plastic sandwich less than or equal to the depth of the receiving hole; Clad with a second glass layer, and clamping the first glass layer and the second glass layer with a tool; Bubbling; A method of bonding at high temperature and high pressure. This method can reduce the production cost by allowing the film to be inserted into a small area instead of the wide area of the laminated glass.

Description

삽입 필름을 갖는 접합 유리의 제조 방법{METHOD FOR MANUFACTURING A LAMINATED GLASS WITH AN INSERTED FILM}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a laminated glass having an insert film,

본 발명은 접합 유리에 관한 것으로, 특히 삽입 필름을 갖는 접합 유리의 제조 방법에 관한 것이다.The present invention relates to a bonded glass, and more particularly, to a method for producing a bonded glass having an inserted film.

도 1a에 도시된 바와 같이, 접합 유리의 제조 방법은 제1 유리층(11) 상에 연질 투명 플라스틱(예: PVB) 층(12)을 놓은 다음 연질 투명 플라스틱층(12) 상에 제2 유리층(13)을 놓는 단계를 포함한다. 3개는 함께 고정되고, 잔류 기포를 제거하기 위해 가압 하에서 약간 가열되는 제1 가공 단계를 거치며, 고온 및 고압에서 추가로 가열되어 유리(11, 13)의 제1층 및 제2층이 연질의 투명 플라스틱층(12)에 결합되도록 하는 제2 가공 단계를 거치게 된다.1A, a method of manufacturing a bonded glass comprises placing a layer of soft transparent plastic (e.g., PVB) 12 on a first glass layer 11 and then placing a second glass (13). ≪ / RTI > The three are fixed together and undergo a first processing step which is slightly heated under pressure to remove residual bubbles and are further heated at high temperature and high pressure so that the first and second layers of glass 11, And then bonded to the transparent plastic layer 12.

접합 유리 내의 특정 위치에 기능성 필름을 놓고, 필름이 유리와 연성 플라스틱 사이에 직접 배치되는 경우, 유리에 대한 연성 플라스틱의 접착에 악영향을 미칠 것이며, 결과적으로 접합 유리의 안전성에 영향을 미친다. 예를 들어, 도 1b에 도시된 바와 같이, 대만 특허 제 M481234 호에 개시된 기능성 필름을 갖는 접합 유리는 두 층의 유리(16) 사이에 배치된 동일한 두께의 2개의 연성 플라스틱층(17)을 필수로 포함하고, 필름(18)을 2개의 연성 플라스틱층(17) 사이에 삽입하여 접합 유리의 안전성을 향상시키도록 삽입된다. 그러나 잔류 기포의 위험을 증가시킬 뿐 아니라, 2개의 접합 연성 플라스틱층(17)은 접합 유리의 수율에도 영향을 미친다. If the functional film is placed at a specific position in the laminated glass and the film is disposed directly between the glass and the flexible plastic, the adhesion of the flexible plastic to the glass will be adversely affected and consequently the safety of the laminated glass is affected. For example, as shown in Fig. 1B, a laminated glass having a functional film disclosed in Taiwan Patent No. M481234 has two flexible plastic layers 17 of the same thickness disposed between two glass layers 16, And the film 18 is inserted between the two soft plastic layers 17 so as to improve the safety of the bonded glass. In addition to increasing the risk of residual bubbles, however, the two bonded soft plastic layers 17 also affect the yield of bonded glass.

또한, 접합 유리는 큰 사이즈로 제조되는 경우가 많고, 결과적으로 낮은 수율로 인해 제조 비용이 상대적으로 높아진다.In addition, the bonded glass is often manufactured in a large size, resulting in a relatively high manufacturing cost due to a low yield.

본 발명은 전술한 단점을 완화 및/또는 방지하기 위해 개발되었다.The present invention has been developed to alleviate and / or prevent the above-mentioned disadvantages.

대만 특허 제M481234호Taiwan Patent No. M481234

본 발명의 하나의 목적은 제조 비용을 감소시킬 수 있는 삽입 필름을 갖는 접합 유리의 제조 방법을 제공하는 것이다.It is an object of the present invention to provide a method of manufacturing a bonded glass having an insertion film capable of reducing manufacturing costs.

본 발명의 하나의 목적은 제조 비용을 감소시킬 수 있는 삽입 필름을 갖는 접합 유리의 제조 방법을 제공하는 것이다.It is an object of the present invention to provide a method of manufacturing a bonded glass having an insertion film capable of reducing manufacturing costs.

상기 목적을 달성하기 위해, 본 발명에 의해 제공되는 삽입 필름을 갖는 접합 유리의 제조 방법은 다음 단계를 포함한다 : In order to achieve the above object, a method for producing a laminated glass having an insert film provided by the present invention comprises the following steps:

제1 연질 투명 플라스틱층에 수용홀을 형성하는 단계 A;Forming a receiving hole in the first soft transparent plastic layer;

제1 유리층 상에 제1 연질 투명 플라스틱층을 배치하는 단계 B;A step B of disposing a first flexible transparent plastic layer on the first glass layer;

삽입 필름을 포함하는 연질의 플라스틱 샌드위치를 수용홀에 넣는 단계 C; 이때, 연질 투명 플라스틱 샌드위치는 수용홀의 깊이와 동일하거나 더 작은 두께를 가지며;Placing a soft plastic sandwich comprising an insert film in a receiving hole; At this time, the soft transparent plastic sandwich has a thickness equal to or smaller than the depth of the receiving hole;

제2 유리층으로 피복하고, 제1 유리층 및 제2 유리층을 공구로 클램핑하는 단계 D;A step D of coating with a second glass layer and clamping the first glass layer and the second glass layer with a tool;

기포를 제거하는 단계 E; 및Step E for removing air bubbles; And

고온 및 고압으로 본딩하는 단계 F.Step F. bonding at high temperature and high pressure.

바람직하게는, 단계 B 후에, 제1 연질 플라스틱층이 평평하게 당겨지고 수용홀이 적절한 위치로 조정된다.Preferably, after step B, the first soft plastic layer is pulled flat and the receiving hole is adjusted to the proper position.

바람직하게는, 연질의 투명 플라스틱 샌드위치는, 2개의 제2 연질 투명 플라스틱층 사이에 삽입 필름을 삽입함으로써 형성된다.Preferably, the soft transparent plastic sandwich is formed by inserting an interleaving film between the two second soft transparent plastic layers.

바람직하게는, 두 개의 제2 연질 투명 플라스틱층은 폴리비닐 부티랄(polyvinyl butyral)로 제조된다.Preferably, the two second soft transparent plastic layers are made of polyvinyl butyral.

바람직하게는, 삽입 필름은 환상(cyclic) 올레핀 중합체로 이루어진다.Preferably, the insert film is comprised of a cyclic olefin polymer.

바람직하게는, 제1 연질 투명 플라스틱층은 폴리비닐 부티랄로 제조된다.Preferably, the first soft transparent plastic layer is made of polyvinyl butyral.

바람직하게는, 삽입 필름은 반사면을 제공하기 위한 반사층이다.Preferably, the insertion film is a reflective layer for providing a reflective surface.

본 발명의 다른 목적과, 본 발명을 특징짓는 다양한 신규 특징이 함께 본 명세서에 첨부되고 본 개시의 일부를 형성하는 특허청구범위에 구체적으로 지적되어있다.Other objects of the invention and various novel features which characterize the invention are pointed out with particularity in the claims annexed to and forming a part of this disclosure.

본 발명과 본 발명의 작용 이점 및 그 용도에 의해 달성되는 특정 목적을 더 잘 이해하기 위해, 본 발명의 바람직한 실시 예가 도시된 첨부 도면 및 설명을 참조하여야 한다.BRIEF DESCRIPTION OF THE DRAWINGS For a better understanding of the present invention, its operational advantages, and the particular objects attained by its use, reference is made to the accompanying drawings and description which show preferred embodiments of the invention.

본 발명에 따른 삽입 필름을 갖는 접합 유리의 제조 방법은, 접합 유리의 넓은 영역 대신 좁은 영역에 필름을 삽입할 수 있다. 즉, 삽입된 필름은 소형 연질 투명 플라스틱 샌드위치에 먼저 삽입되어 제조 비용을 감소시킨다.The method of producing a bonded glass having an insertion film according to the present invention can insert a film into a narrow region instead of a wide region of the bonded glass. That is, the inserted film is first inserted into a small soft transparent plastic sandwich to reduce manufacturing costs.

한편, 수율에 영향을 줄 수 있는 잔류 기포는 연질 투명 플라스틱 샌드위치에서 처리되며, 기포가 발생하더라도 결함있는 제품은 전체 접합 유리 대신 연질 투명 플라스틱 샌드위치가 되므로 생산 원가는 효과적으로 감소한다.On the other hand, residual bubbles which may affect the yield are treated in a soft transparent plastic sandwich, and even if bubbles are generated, the production cost is effectively reduced because the defective product becomes a soft transparent plastic sandwich instead of the whole bonded glass.

게다가, 작은 사이즈의 연질 투명 플라스틱 샌드위치는 불균일한 두께의 문제를 다루기 쉽고, 이는 생산 비용을 더욱 감소시키는 효과를 제공한다.In addition, small sized soft transparent plastic sandwiches are easy to handle the problem of non-uniform thickness, which provides the effect of further reducing production costs.

도 1a는 종래의 접합 유리의 단면도이다.
도 1b는 다른 종래의 접합 유리의 단면도이다.
도 2는 본 발명의 바람직한 실시 예에 따른 삽입 필름을 갖는 접합 유리 제조 방법의 단계들을 도시하는 순서도이다.
도 3a는 제1 연질 투명 플라스틱층에 수용홀이 형성된 것을 보여주는 본 발명의 설명도이다.
도 3b는 제1 연질 투명 플라스틱층이 제1 유리층 상에 배치된 다음, 연질 투명 플라스틱 샌드위치와 제2 유리층이 순차적으로 배치되는 것을 보여주는 본 발명의 설명도이다.
도 3c는 제1 유리층, 제1 연질 투명 플라스틱층, 연질 투명 플라스틱 샌드위치 및 제2 유리층이 함께 접합되어 접합 유리를 형성하는 것을 보여주는 본 발명의 예시적인 도면이다.1A is a cross-sectional view of a conventional bonded glass.
1B is a cross-sectional view of another conventional bonded glass.
2 is a flow chart illustrating the steps of a method of manufacturing a bonded glass with an interposer film according to a preferred embodiment of the present invention.
3A is an explanatory view of the present invention showing a receiving hole formed in the first soft transparent plastic layer.
Figure 3b is an illustration of the present invention showing that a first soft transparent plastic layer is disposed on a first glass layer and then a soft transparent plastic sandwich and a second glass layer are sequentially disposed.
3C is an exemplary illustration of the present invention showing that a first glass layer, a first soft transparent plastic layer, a soft transparent plastic sandwich, and a second glass layer are joined together to form a bonded glass.

본 발명은, 단지 예시를 목적으로 본 발명에 따른 바람직한 실시 예를 도시하는 첨부된 도면과 함께 볼 때 다음의 설명으로부터 명확해질 것이다.BRIEF DESCRIPTION OF THE DRAWINGS The invention will be apparent from the following description, taken in conjunction with the accompanying drawings, illustrating preferred embodiments of the invention, for purposes of illustration only.

도 2 및 도 3a 내지 도 3c를 참조하면, 본 발명의 바람직한 실시 예에 따른 삽입 필름을 갖는 접합 유리의 제조 방법은 다음 단계를 포함한다 :Referring to Figures 2 and 3A to 3C, a method of manufacturing a bonded glass with an interposer film according to a preferred embodiment of the present invention comprises the following steps:

도 2 및 도 3a에 도시된 바와 같이, 제1 연질 투명 플라스틱층(20)에 수용홀(21)을 형성하는 단계 A; 본 실시 예에서, 제1 연질 투명 플라스틱층(20)은 PVB(폴리비닐 부티랄: Polyvinyl　butyral)이고, 수용홀(21)은 직사각형 모양이며 제1 연질 투명 플라스틱층(20)의 일부를 절취하여 형성될 수 있고;As shown in Figs. 2 and 3A, the step A of forming the receiving hole 21 in the first soft transparent plastic layer 20; In this embodiment, the first soft transparent plastic layer 20 is PVB (polyvinyl butyral), the receiving hole 21 is rectangular, and a part of the first soft transparent plastic layer 20 is cut ;

도 2 및 도 3b에 도시된 바와 같이, 제 1 연질 투명 플라스틱층(20)을 제1 유리층 상에 놓는 단계 B; 본 실시 예에서, 제 1 연질 플라스틱층(20)은 편평하게 당겨져서 수용홀(21)을 적절한 위치로 조정하기 위해 이동되며; 2 (B) and 3 (B), placing the first flexible transparent plastic layer 20 on the first glass layer; In this embodiment, the first soft plastic layer 20 is flatly pulled and moved to adjust the receiving hole 21 to a proper position;

도 2 및 도 3b에 도시된 바와 같이, 삽입 필름(41)을 포함하는 연질의 투명 플라스틱 샌드위치(40)를 수용홀(21)에 넣는 단계 C; 이때, 연질의 투명 플라스틱 샌드위치(40)는 수용홀(21)의 깊이(21D)와 동일하거나 더 작은 두께(40T)를 갖고; 본 실시 예에서, PVB로 제조된 2개의 제2 연질 투명 플라스틱층(43) 사이에 삽입 필름(41)을 삽입함으로써 연질의 투명 플라스틱 샌드위치(40)가 형성되고, 삽입 필름 (41)은 반사면을 제공하는 반사층이고;As shown in FIGS. 2 and 3B, the step C of inserting the soft transparent plastic sandwich 40 including the insertion film 41 into the receiving hole 21; At this time, the soft transparent plastic sandwich 40 has a thickness 40T equal to or smaller than the depth 21D of the receiving hole 21; In this embodiment, a soft transparent plastic sandwich 40 is formed by inserting the insertion film 41 between the two second soft transparent plastic layers 43 made of PVB, / RTI >

도 2, 도 3b 및 도 3c에 도시된 바와 같이, 제2 유리층(50)으로 피복하고 제1 유리층(30)과 제2 유리층(50)을 공구로 클램핑하는 단계 D; A step D of coating with a second glass layer 50 and clamping the first glass layer 30 and the second glass layer 50 with a tool, as shown in Figures 2, 3b and 3c;

기포를 제거하는 단계 E; 그리고Step E for removing air bubbles; And

고온 고압으로 접합하는 단계 F;를 구비한다. And a step (F) of bonding at a high temperature and a high pressure.

상기의 단계 E 및 단계 F는, 각각 잔류 기포를 제거하기 위해 가압 하에서 약간 가열하는 제1단계를 수행 한 다음, 고압 하의 한층 높은 온도에서 본딩 공정을 수행하여 연질의 투명 플라스틱 샌드위치(40)를 포함하는 제1 연질 투명 플라스틱층(20)에 제1 및 제2 유리층(30, 50)을 접합한다.The above steps E and F are carried out by carrying out a first step of slightly heating under pressure to remove residual bubbles respectively and then carrying out a bonding process at a higher temperature under high pressure to obtain a soft transparent plastic sandwich 40 The first and second glass layers 30 and 50 are bonded to the first soft transparent plastic layer 20.

상기 언급된 것은 본 발명의 방법의 각 단계에 대한 설명이며, 본 발명의 효능은 다음과 같이 기술된다.The above is a description of each step of the method of the present invention, and the efficacy of the present invention is described as follows.

본 발명은 필름을 국부적으로 가공하는 방법을 채택하며, 삽입 필름(41)을 함유하는 연질의 투명 플라스틱 샌드위치(40)의 작은 조각(piece)이 미리 제조된다. 즉, 접합 유리의 제1 연질 투명 플라스틱층(20)의 두께와 동등 또는 그보다 작은 두께를 갖는 연질의 투명 플라스틱 샌드위치(40)를 제조할 수 있도록, 삽입 필름(41)은 전체 두께 차이를 다루기 위해 연질의 투명 플라스틱 샌드위치(40)의 작은 영역(area)에서 처리된다.The present invention adopts a method of locally processing the film and a small piece of soft transparent plastic sandwich 40 containing the insert film 41 is prefabricated. That is, to enable the production of a soft transparent plastic sandwich 40 having a thickness equal to or less than the thickness of the first soft transparent plastic layer 20 of the laminated glass, Is processed in a small area of the soft transparent plastic sandwich (40).

제1 및 제2 유리층(30, 50)이 결합 되기에 앞서, 제1 연질 투명 플라스틱층(20)은 연질의 투명 플라스틱 샌드위치(40)와 동일한 면적을 갖는 수용홀(21)을 형성하도록 부분적으로 절단된다. Before the first and second glass layers 30 and 50 are bonded together, the first soft transparent plastic layer 20 is partly or wholly formed to form a receiving hole 21 having the same area as the soft transparent plastic sandwich 40 .

제1 유리층(30)에 수용홀(21)을 갖는 제1 연질 플라스틱층(20)을 위치시킨 다음, 제1 연질 투명 플라스틱층(20)의 수용홀(21)에 연질의 투명 플라스틱 샌드위치(40)를 넣고 가압하에 가열하여, 연질의 투명 플라스틱 샌드위치(40)가 고온에서 주변의 제1 연질 투명 플라스틱층(20)과 원활하게 용접되게 한다.The first soft plastic layer 20 having the receiving hole 21 is placed in the first glass layer 30 and then the soft plastic transparent sandwich 40 and heated under pressure so that the soft transparent plastic sandwich 40 is welded to the surrounding first soft transparent plastic layer 20 at a high temperature.

따라서, 본 발명은 적어도 다음의 효능을 갖는다.Therefore, the present invention has at least the following effects.

생산 원가를 효과적으로 줄일 수 있다. 본 발명에 따른 삽입 필름을 갖는 접합 유리의 제조 방법은 접합 유리의 넓은 영역 대신 작은 영역에 필름을 삽입할 수 있다. 즉, 삽입 필름(41)은 우선적으로 작은 연질의 투명 플라스틱 샌드위치(40)에 삽입됨으로써 제조 비용을 절감할 수 있다. 한편, 수율(yield rate)에 영향을 줄 수 있는 잔류 기포는 연질의 투명 플라스틱 샌드위치(40)에서 처리되기 때문에, 기포가 발생하더라도, 불량품은 전체 접합 유리 대신 연질 투명 플라스틱 샌드위치(40)에 한정되므로 생산 비용이 효과적으로 절감된다. 게다가, 작은 크기의 연질 투명 플라스틱 샌드위치(40)는 불균일한 두께의 문제도 다루기 쉽고, 이는 생산 비용을 추가로 감소시킨다.The production cost can be effectively reduced. The method of producing a laminated glass having an insert film according to the present invention can insert a film into a small area instead of a wide area of the laminated glass. That is, the insertion film 41 is inserted into the small soft transparent plastic sandwich 40 first, thereby reducing the manufacturing cost. On the other hand, since residual bubbles that may affect the yield rate are treated in the soft transparent plastic sandwich 40, even if bubbles are generated, the defective product is limited to the soft transparent plastic sandwich 40 instead of the entire bonded glass The production cost is effectively reduced. In addition, the small size soft transparent plastic sandwich 40 is easy to handle the problem of non-uniform thickness, further reducing production costs.

본 발명에 따라 다양한 실시 예가 도시되고 설명되었지만, 본 발명의 범주를 벗어나지 않고 다른 실시 예가 만들어질 수 있음은 당업자에게는 자명하다.While various embodiments have been shown and described in accordance with the present invention, it will be apparent to those skilled in the art that other embodiments may be made without departing from the scope of the present invention.

20: 제1 연질 투명 플라스틱층 21: 수용홀
30: 제1 유리층 40: 연질의 투명 플라스틱 샌드위치
41: 삽입 필름 43: 제2 연질 투명 플라스틱층
50: 제2 유리층20: first soft transparent plastic layer 21: receiving hole
30: first glass layer 40: soft transparent plastic sandwich
41: insertion film 43: second soft transparent plastic layer
50: second glass layer

Claims (7)

제1 연질 투명 플라스틱층에 수용홀을 형성하는 단계 A;
제1 유리층 상에 제1 연질 투명 플라스틱층을 배치하는 단계 B;
삽입 필름을 포함하는 연질의 플라스틱 샌드위치를 수용홀에 넣는 단계 C;
제2 유리층으로 피복하고, 제1 유리층 및 제2 유리층을 공구로 클램핑하는 단계 D;
기포를 제거하는 단계 E; 및
고온 및 고압으로 본딩하는 단계 F를 포함하되,
상기 단계 C에 있어서, 상기 연질의 투명 플라스틱 샌드위치는 상기 수용홀의 깊이 이하의 두께를 가지고, 또한 상기 연질의 투명 플라스틱 샌드위치는 2개의 제2 연질 투명 플라스틱층 사이에 삽입 필름을 삽입함으로써 형성되는 것을 특징으로 하는 삽입 필름을 갖는 접합 유리의 제조 방법.Forming a receiving hole in the first soft transparent plastic layer;
A step B of disposing a first flexible transparent plastic layer on the first glass layer;
Step C of inserting a soft plastic sandwich comprising an insert film into the receiving hole;
A step D of coating with a second glass layer and clamping the first glass layer and the second glass layer with a tool;
Step E for removing air bubbles; And
(F) bonding at high temperature and high pressure,
In the step C, the soft transparent plastic sandwich has a thickness equal to or less than the depth of the receiving hole, and the soft transparent plastic sandwich is formed by inserting an insert film between the two second soft transparent plastic layers Wherein the step of forming the laminated glass comprises the steps of: 제1항에 있어서,
상기 단계 B 후에, 제1 연질 플라스틱층이 평평하게 당겨지고 수용홀이 적절한 위치로 조정되는 것을 특징으로 하는 삽입 필름을 갖는 접합 유리의 제조 방법.The method according to claim 1,
And after the step B, the first soft plastic layer is pulled flat and the receiving hole is adjusted to an appropriate position. 삭제delete 제1항에 있어서,
상기 2개의 제2 연질 투명 플라스틱층은 폴리비닐 부티랄(polyvinyl butyral)로 제조되는 것을 특징으로 하는 삽입 필름을 갖는 접합 유리의 제조 방법.The method according to claim 1,
Wherein the two second soft transparent plastic layers are made of polyvinyl butyral. ≪ RTI ID = 0.0 > 11. < / RTI > 제1항에 있어서,
삽입 필름은 환상(cyclic) 올레핀 중합체로 이루어지는 것을 특징으로 하는 삽입 필름을 갖는 접합 유리의 제조 방법.The method according to claim 1,
Wherein the insert film is made of a cyclic olefin polymer. 제1항에 있어서,
제1 연질 투명 플라스틱층은 폴리비닐 부티랄로 제조되는 것을 특징으로 하는 삽입 필름을 갖는 접합 유리의 제조 방법.The method according to claim 1,
Wherein the first soft transparent plastic layer is made of polyvinyl butyral. 제1항에 있어서,
삽입 필름은 반사면을 제공하기 위한 반사층임을 특징으로 하는 삽입 필름을 갖는 접합 유리의 제조 방법.The method according to claim 1,
Wherein the insert film is a reflective layer for providing a reflective surface.
KR1020170115716A 2017-09-11 2017-09-11 Method for manufacturing a laminated glass with an inserted film KR101996727B1 (en)