KR101795356B1 - Heat Reflection and Insulation Waterproof Paint Composition Comprising Metal Powder and Waterproofing Methods Using Thereof - Google Patents
Heat Reflection and Insulation Waterproof Paint Composition Comprising Metal Powder and Waterproofing Methods Using Thereof Download PDFInfo
- Publication number
- KR101795356B1 KR101795356B1 KR1020170060807A KR20170060807A KR101795356B1 KR 101795356 B1 KR101795356 B1 KR 101795356B1 KR 1020170060807 A KR1020170060807 A KR 1020170060807A KR 20170060807 A KR20170060807 A KR 20170060807A KR 101795356 B1 KR101795356 B1 KR 101795356B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- heat
- polyisocyanate
- amount
- Prior art date
Abstract
Description
본 발명은 금속분말을 포함하는 열반사 및 차열 방수도료 조성물 및 이의 시공방법에 관한 것으로서, 보다 상세하게는 방수제를 시공표면에 도포하여 도막을 형성함으로써, 방수성능을 제공하는 동시에 유입되는 빛을 반사, 분산 및/또는 산란시켜 도막된 표면에 열이 전달되는 것을 감소시키고 내부의 온도가 외부로 빠져나가지 못하도록 하는 차열기능을 갖는 열반사 및 차열 방수도료 조성물 및 이의 시공방법에 관한 것이다.
The present invention relates to a heat-reflective and heat-resistant waterproof coating composition comprising a metal powder and a method of applying the same, and more particularly, to a waterproof coating composition comprising a water- And a heat-shrinkable and heat-resistant waterproof coating composition and a method of applying the same, which have a heat shielding function that reduces the transfer of heat to a surface coated and dispersed and / or scattered and prevents the internal temperature from escaping to the outside.
일반적으로 방수도료 조성물이라 함은 수성 또는 유성의 액상 형태의 방수제를 각종 건축물 및 구조벽의 표면에 도포하고 수분 또는 용제가 증발되고 남은 피막을 이용하여 방수효과를 거두는 조성물을 지칭한다.Generally, a waterproof paint composition refers to a composition that applies an aqueous or oily liquid waterproofing agent to the surfaces of various buildings and structural walls, and water or solvent is evaporated and water-repellent effect is obtained by using the remaining coating.
이러한 방수도료 조성물은 통상적으로 건축 또는 토목 구조물의 옥상방수, 외부방수, 지하 구조물의 옹벽 내지 천정 방수 또는 화장실, 욕실, 베란다 등의 실내방수 등을 위해 사용되고 있다.Such a waterproof coating composition is conventionally used for roof waterproofing of an architectural or civil structure, external waterproofing, waterproofing of a retaining wall or ceiling of an underground structure, or indoor waterproofing of a toilet, a bathroom, and a verandah.
현재 널리 보급된 방수도료 조성물로는 고무화 아스팔트, 아크릴고무 또는 아크릴 수지 등을 주성분으로 하는 에멀젼형과 클로로프렌이나 클로로설폰화 폴리에틸렌을 포함하거나 우레탄이나 에폭시수지가 주성분인 반응형이 있으며, 이들 중 가장 널리 사용되는 것이 우레탄계 방수도료 조성물과 고무화 아스팔트계 방수도료 조성물이다.Currently widely used waterproof coating compositions include emulsion type which is composed mainly of rubberized asphalt, acrylic rubber or acrylic resin, reaction type which contains chloroprene or chlorosulfonated polyethylene or urethane or epoxy resin as main component, Widely used are urethane-based waterproof coating compositions and rubberized asphalt-based waterproof coating compositions.
고무화 아스팔트계 방수도료 조성물은 아스팔트에 스티렌 계통의 중합체, 에틸렌-비닐 아세테이트 또는 스티렌-부타디엔 라텍스 등을 혼합함으로써 아스팔트가 가질 수 없는 성질, 즉 우수한 신장율, 내균열성, 내한성, 접합성 등을 갖도록 개질시킨 것이다.The rubberized asphalt-based waterproof coating composition is prepared by mixing a styrene-based polymer, ethylene-vinyl acetate or styrene-butadiene latex or the like with asphalt to modify the asphalt so as to have properties that the asphalt can not have, that is, excellent elongation, crack resistance, cold resistance, It is.
또한, 방수도료 조성물은 내열성, 강도 및 경도를 강화시키기 위해 계면활성제나 경화촉진제 등을 첨가하기도 하며, 열가소성 엘라스토머 등을 첨가하는 경우도 있다.In addition, a surfactant, a hardening accelerator, etc. may be added to the waterproof coating composition in order to enhance heat resistance, strength and hardness, and a thermoplastic elastomer or the like may be added.
하지만, 전술한 고무화 아스팔트계 방수도료 조성물은 신장율, 내균열성, 접합성이 우수한 장점이 있지만, 복원력이 약하며 내화학성, 내오존성, 내자외선성이 좋지 않다.However, the above-mentioned rubberized asphalt-based waterproof coating composition has an advantage of excellent elongation, crack resistance and bonding property, but has weak restorative force and is not good in chemical resistance, ozone resistance and ultraviolet ray resistance.
특히, 스티렌부타디엔 고무를 주성분으로 하는 방수도료 조성물은 복원력이 매우 약하여 반복적으로 신장될 경우 열화현상이 발생되며 고유의 물리적 특성을 잃게 되는 문제점이 있다.Particularly, a waterproof coating composition containing a styrene butadiene rubber as a main component has a very weak restorative force, and when it is stretched repeatedly, deterioration occurs and inherent physical properties are lost.
더욱이, 방수도료 조성물이 콘크리트 구조물의 외벽이나 옥외, 특히 옥상 등에 시공되는 경우, 지속적인 자외선 노출 및 오염 등에 따라 방수도료의 물성이 저하되어 방수성이 급격히 감소하는 문제점이 지속적으로 발생하고 있다.Further, when the waterproof coating composition is applied to the outer wall of the concrete structure or outdoors, especially on the roof, there is a problem that the waterproof property of the waterproof paint is decreased due to continuous exposure to ultraviolet rays and contamination and the water resistance is drastically reduced.
이러한, 문제점을 극복하기 위해 대한민국 특허 제10-0731614호에는 고복원력을 갖고 내화학성, 내오존성 및 내자외선성을 향상시킬 수 있도록 수계 클로로프렌 고무와 유화 아스팔트 및 첨가제를 혼합한 방수도료 조성물이 개시되어 있다.
In order to overcome such a problem, Korean Patent No. 10-0731614 discloses a waterproof coating composition comprising water-based chloroprene rubber, emulsified asphalt, and additives so as to have high resilience and improve chemical resistance, ozone resistance and ultraviolet ray resistance have.
본 발명은 상기와 같은 문제점을 해결하기 위해 창출한 것으로 방수 시공에 사용하는 방수도료 조성물에 빛을 반사, 분산 및/또는 산란시키는 금속분말을 포함시켜, 방수도료의 수명을 연장시키고, 내구성을 향상시킬 뿐만 아니라, 방수도료가 적용되는 구조물에 전달되는 열을 감소시키고 내부의 열이 외부로 빠져나가지 못하도록 함으로써 구조물의 온도가 상승하는 것을 방지할 수 있도록 하는 것을 제공한다.
Disclosure of the Invention The present invention has been made in order to solve the above problems, and it is an object of the present invention to provide a waterproof coating composition for use in waterproof construction, which comprises a metal powder for reflecting, dispersing and / or scattering light to prolong the life of the waterproof paint, Not only does it reduce the heat transmitted to the structure to which the waterproof paint is applied, and prevent the internal heat from escaping to the outside, thereby preventing the temperature of the structure from rising.
본 발명은The present invention
폴리 이소시아네이트 프리 폴리머 100중량부;100 parts by weight of a polyisocyanate-free polymer;
에틸렌 초산 비닐 10 내지 60중량부;10 to 60 parts by weight of ethylene vinyl acetate;
음이온 유화제 5 내지 30중량부;5 to 30 parts by weight of an anionic emulsifier;
고무 화합물 5 내지 20중량부; 5 to 20 parts by weight of a rubber compound;
가성소다 1 내지 20중량부;1 to 20 parts by weight of caustic soda;
경화제 1 내지 30중량부;1 to 30 parts by weight of a curing agent;
옥틸페놀 에톡실레이트 0.1 내지 10중량부;0.1 to 10 parts by weight of octylphenol ethoxylate;
질산칼슘 5 내지 35중량부;5 to 35 parts by weight of calcium nitrate;
금속분말 10 내지 30중량부;10 to 30 parts by weight of a metal powder;
수용성 아크릴 수지 5 내지 30중량부;5 to 30 parts by weight of a water-soluble acrylic resin;
증점제 1 내지 20중량부; 및1 to 20 parts by weight of a thickener; And
용제 50 내지 1,000중량부를 포함하는 열반사 및 차열 방수도료 조성물을 제공한다.
And 50 to 1,000 parts by weight of a solvent.
또한, 본 발명은In addition,
열반사 및 차열 방수도료 조성물을 시공하기 위한 시공표면을 처리하는 표면처리단계; 및A surface treatment step of treating the application surface for applying the heat reflection and heat shielding waterproofing paint composition; And
상기 시공표면에 폴리 이소시아네이트 프리 폴리머 100중량부, 에틸렌 초산 비닐 10 내지 60중량부, 음이온 유화제 5 내지 30중량부, 고무 화합물 5 내지 20중량부, 가성소다 1 내지 20중량부, 경화제 1 내지 30중량부, 옥틸페놀 에톡실레이트 0.1 내지 10중량부, 질산칼슘 5 내지 35중량부, 금속분말 10 내지 30중량부, 수용성 아크릴 수지 5 내지 30중량부, 증점제 1 내지 20중량부, 및 용제 50 내지 1,000중량부를 포함하는 열반사 및 차열 방수도료 조성물을 최소 건조 도막두께 0.1mm 이상이 될 때까지 도포하는 도포단계를 포함하는 열반사 및 차열 방수도료 조성물의 시공방법을 제공한다.
Wherein the polyisocyanate prepolymer is contained in an amount of 100 parts by weight, 10 to 60 parts by weight of ethylene vinyl acetate, 5 to 30 parts by weight of an anionic emulsifier, 5 to 20 parts by weight of a rubber compound, 1 to 20 parts by weight of caustic soda, 0.1 to 10 parts by weight of octylphenol ethoxylate, 5 to 35 parts by weight of calcium nitrate, 10 to 30 parts by weight of a metal powder, 5 to 30 parts by weight of a water-soluble acrylic resin, 1 to 20 parts by weight of a thickener, And a coating step of applying the heat reflecting and heat-resistant waterproof coating composition containing the water-repellent and heat-resistant waterproof coating composition to a minimum dry film thickness of 0.1 mm or more.
본 발명에 따른 열반사 및 차열 방수도료 조성물은 방수 시공시 빠른 양생으로 공기를 단축시킬 수 있고, 균일한 방수도막을 형성할 수 있으며, 신장력과 유동성이 좋다.The heat-reflective and heat-resistant waterproof coating composition according to the present invention can shorten the air by quick curing in the waterproofing process, can form a uniform waterproof coating film, and has excellent tensile strength and fluidity.
또한, 상기 열반사 방수도료 조성물은 접착력이 우수하고, 도포된 방수도료에 조사되는 빛을 반사, 분산 및/또는 산란시키고, 내부의 열이 외부로 빠져나가지 못하게 함으로써 내구성이 높을 뿐만 아니라, 방수도료가 적용되는 구조물에 전달되는 열을 감소시켜 구조물의 표면온도가 상승하는 것을 방지할 수 있도록 한다.
In addition, the heat-reflective waterproof coating composition is excellent in adhesion and reflects, disperses and / or scatters light irradiated to the applied waterproof paint and prevents internal heat from escaping to the outside, Thereby reducing the heat transmitted to the structure to prevent the surface temperature of the structure from rising.
이하, 본 발명을 구체적으로 설명한다.Hereinafter, the present invention will be described in detail.
한 가지 관점에서, 본 발명은 폴리 이소시아네이트 프리 폴리머 100중량부, 에틸렌 초산 비닐 10 내지 60중량부, 음이온 유화제 5 내지 30중량부, 고무 화합물 5 내지 20중량부, 가성소다 1 내지 20중량부, 경화제 1 내지 30중량부, 옥틸페놀 에톡실레이트 0.1 내지 10중량부, 질산칼슘 5 내지 35중량부, 금속분말 10 내지 30중량부, 수용성 아크릴 수지 5 내지 30중량부, 증점제 1 내지 20중량부, 및 용제 50 내지 1,000중량부를 포함하는 열반사 및 차열 방수도료 조성물을 제공한다.In one aspect, the present invention provides a process for producing a polyurethane foam, comprising: mixing 100 parts by weight of a polyisocyanate-free polymer, 10 to 60 parts by weight of ethylene vinyl acetate, 5 to 30 parts by weight of an anionic emulsifier, 5 to 20 parts by weight of a rubber compound, 1 to 20 parts by weight of caustic soda, 0.1 to 10 parts by weight of octylphenol ethoxylate, 5 to 35 parts by weight of calcium nitrate, 10 to 30 parts by weight of a metal powder, 5 to 30 parts by weight of a water-soluble acrylic resin, 1 to 20 parts by weight of a thickener, And 50 to 1,000 parts by weight of a solvent.
다른 관점에서, 본 발명은 열반사 및 차열 방수도료 조성물을 시공하기 위한 시공표면을 처리하는 표면처리단계; 및 상기 시공표면에 폴리 이소시아네이트 프리 폴리머 100중량부, 에틸렌 초산 비닐 10 내지 60중량부, 음이온 유화제 5 내지 30중량부, 고무 화합물 5 내지 20중량부, 가성소다 1 내지 20중량부, 경화제 1 내지 30중량부, 옥틸페놀 에톡실레이트 0.1 내지 10중량부, 질산칼슘 5 내지 35중량부, 금속분말 10 내지 30중량부, 수용성 아크릴 수지 5 내지 30중량부, 증점제 1 내지 20중량부, 및 용제 50 내지 1,000중량부를 포함하는 열반사 및 차열 방수도료 조성물을 최소 건조 도막두께 0.1mm 이상이 될 때까지 도포하는 도포단계를 포함하는 열반사 및 차열 방수도료 조성물의 시공방법을 제공한다.In another aspect, the present invention relates to a surface treatment step of treating a work surface for applying a heat reflecting and heat shielding waterproof paint composition; And 10 to 60 parts by weight of an ethylene-vinyl acetate copolymer, 5 to 30 parts by weight of an anionic emulsifier, 5 to 20 parts by weight of a rubber compound, 1 to 20 parts by weight of caustic soda, and 1 to 30 parts by weight of a polyisocyanate- 0.1 to 10 parts by weight of octylphenol ethoxylate, 5 to 35 parts by weight of calcium nitrate, 10 to 30 parts by weight of a metal powder, 5 to 30 parts by weight of a water-soluble acrylic resin, 1 to 20 parts by weight of a thickener, And 1,000 parts by weight of a water-repellent and water-repellent coating composition to a minimum dry film thickness of 0.1 mm or more.
본 발명에 따른 열반사 및 차열 방수도료 조성물은 건축물의 내/외부의 균열로 인한 누수 및 결로현상을 방지하기 위해 표면, 바람직하게는 방수를 시공하고자 하는 표면에 도막을 형성할 수 있도록 한다.The heat-reflective and heat-resistant waterproof coating composition according to the present invention can form a coating on a surface, preferably a surface to be waterproofed, in order to prevent leakage and condensation due to internal / external cracks in the building.
특정적으로, 본 발명에 따른 열반사 및 차열 방수도료 조성물은 방수성 외에 빛을 반사, 분산 및/또는 산란시켜 방수도료가 적용되는 구조물, 특정적으로 옥상, 지붕 등에 전달되는 열을 감소시킴으로써 구조물의 표면온도가 종래 방수도료 조성물을 사용할 경우보다 5 내지 10℃정도 낮도록 하고, 이에 따라 옥상, 지붕 등을 통해 실내로 전달되는 열을 감소시킬 수 있을 뿐만 아니라, 도막의 형성되는 건축물의 내부와 외부가 단절되게 함으로써 내부의 열은 외부로 방출되지 않도록 한다.Particularly, the heat reflecting and heat shielding waterproof coating composition according to the present invention is not only waterproof, but also reflects, disperses and / or scatters light to reduce the heat transferred to a structure to which a waterproof coating is applied, specifically rooftops and roofs, The surface temperature is lower than that of the conventional waterproof coating composition by 5 to 10 ° C so that the heat transferred to the room through the roof and the roof can be reduced, So that the internal heat is not released to the outside.
본 발명에 따른 폴리 이소시아네이트 프리 폴리머는 후술하는 경화제와 반응함으로써 폴리 우레아를 형성시켜 방수성, 접착성 등을 제공하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 폴리머, 특정적으로 폴리 이소시아네이트 프리 폴리머라면 어떠한 것을 사용하여도 무방하며, 추천하기로는 톨루엔 다이이소시아네이트(Toluene diisocyanate, TDI), p-페닐렌 다이이소시아네이트(p-phenylene diisocyanate, PPDI), 4,4-다이페닐메탄 다이이소시아네이트(4,4-Diphenylmethane diisocyanate, MDI), 1,5-나프탈렌 다이이소시아네이트(1,5-Naphthalene diisocyanate, NDI), 이소포론 다이이소시아네이트(Isoporon diisocyanate, IPDI) 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다.The polyisocyanate prepolymer according to the present invention is to provide a polyurea by reacting with a curing agent to be described later to provide a waterproof property and an adhesive property, and it is an object of the present invention to provide a polyisocyanate- Any one may be used, and toluene diisocyanate (TDI), p-phenylene diisocyanate (PPDI), 4,4-diphenylmethane diisocyanate (4,4- 1,5-naphthalene diisocyanate (NDI), isophorone diisocyanate (IPDI), or a mixture of at least one of them.
본 발명에 따른 방수도료 조성물, 특정적으로 열반사 및 차열 방수도료 조성물은 폴리 이소시아네이트 프리 폴리머 외 나머지 성분들의 함량은 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 한다.The waterproof coating composition according to the present invention, specifically the heat reflecting and heat shielding waterproofing coating composition, is based on 100 parts by weight of the polyisocyanate prepolymer and the other components in addition to the polyisocyanate prepolymer.
본 발명에 따른 에틸렌 초산 비닐(EVA)는 열반사 및 차열 방수도료 조성물 내부에 필름을 형성하여 휨 및 부착강도를 향상시키며, 보수성이 개선되어 중성화, 염화물 이온 침투, 동결융해 등에 대한 내구성을 향상시킬 수 있도록 하기 위한 것으로서, 그 사용량은 특별히 한정되지 않지만, 추천하기로는 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 10 내지 60중량부인 것이 좋다.The ethylene vinyl acetate (EVA) according to the present invention improves the warpage and adhesion strength by forming a film inside the heat reflection and waterproof coating composition, and improves the water retention, thereby improving durability against neutralization, chloride ion penetration, freezing and thawing The amount of the polyisocyanate prepolymer to be used is not particularly limited, but is preferably 10 to 60 parts by weight based on 100 parts by weight of the polyisocyanate-free polymer.
바람직한 에틸렌 초산 비닐(EVA)은 겉보기 비중은 475ㅁg/l, 입도는 max,2%>400㎛이고, 물에 재분산 시 0.3 내지 9㎛의 입도분포를 나타는 것을 추천한다.The preferred ethylene vinyl acetate (EVA) has an apparent specific gravity of 475? G / l, a particle size of max, 2%> 400 占 퐉, and a particle size distribution of 0.3 to 9 占 퐉 on redispersion in water.
본 발명에 따른 음이온 유화제(Anionic emulsifier)는 방수도료 조성물을 구성하는 용제, 즉 물속에서 고형분이 미립자 형태로 분산되도록 하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 음이온 유화제라면 어떠한 것을 사용하여도 무방하다.The anionic emulsifier according to the present invention is used for dispersing the solid component in the form of a solvent constituting the waterproof coating composition, that is, in the form of particles in the water, and any anionic emulsifier conventionally used in the art having such a purpose can be used It is acceptable.
바람직한 음이온 유화제로는 수지산나트륨염, 리그닌술폰산알카리금속염, 나프탈렌 설포닉 산(Naphthalene Sulfonic acid) 유도체, 클로로벤젠(Chlorobenzene) 유도체, 고급지방산알카리금속염, 알킬벤젠술폰산염, 알파-올레핀술폰산염, 폴리옥시에틸렌페닐에테르류, 알킬아릴술폰산나트륨류 또는 이들의 혼합물을 사용할 수 있다.Preferable examples of the anionic emulsifier include sodium methacrylate, sodium ligninsulfonate alkali metal salts, naphthalene sulfonic acid derivatives, chlorobenzene derivatives, higher fatty acid alkali metal salts, alkylbenzenesulfonates, alpha-olefin sulfonates, poly Oxyethylene phenyl ethers, sodium alkylaryl sulfonates, or mixtures thereof.
상기 음이온 유화제의 사용량은 열반사 및 차열 방수도료 조성물을 구성하는 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 30중량부인 것이 좋다.The amount of the anionic emulsifier to be used is preferably 5 to 30 parts by weight based on 100 parts by weight of the polyisocyanate-free polymer constituting the heat reflecting and waterproof coating composition.
본 발명에 따른 고무 화합물은 열반사 및 차열 방수도료 조성물의 접착력, 내화학성, 내오존성, 내자외선성 및/또는 탄성력 등을 제공한다.The rubber compound according to the present invention provides adhesion, chemical resistance, ozone resistance, ultraviolet ray resistance and / or elasticity and the like of the heat reflecting and waterproof coating composition.
바람직한 고무 화합물은 클로로프렌 고무, 부틸고무, 스티렌부타디엔 고무, 부타디엔 고무 또는 이들의 혼합물을 사용하는 것이 좋다.Preferred rubber compounds are chloroprene rubber, butyl rubber, styrene butadiene rubber, butadiene rubber, or mixtures thereof.
본 발명에 따른 고무 화합물은 합성고무를 사용할 수도 있다.The rubber compound according to the present invention may also be a synthetic rubber.
이러한 경우, 바람직한 합성고무는 클로로프렌 고무, 특정적으로 수계 클로로프렌 고무, 부틸고무, 스티렌부타디엔 고무, 부타디엔 고무 또는 이들의 혼합물일 수 있지만, 고복원력을 가지며, 내화학성, 내오존성 및 내자외선성이 우수한 클로로프렌 고무를 사용하는 것을 추천한다.In this case, the preferable synthetic rubber may be chloroprene rubber, specifically waterborne chloroprene rubber, butyl rubber, styrene butadiene rubber, butadiene rubber or a mixture thereof, but it has a high resilience and is excellent in chemical resistance, ozone resistance and ultraviolet ray resistance It is recommended to use chloroprene rubber.
상기 고무 화합물의 사용량은 열반사 및 차열 방수도료 조성물을 구성하는 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 20중량부인 것이 좋다.The rubber compound is preferably used in an amount of 5 to 20 parts by weight based on 100 parts by weight of the polyisocyanate-free polymer constituting the heat reflection and waterproof coating composition.
본 발명에 따른 가성소다는 열반사 및 차열 방수도료 조성물의 적정 pH, 예를 들면 pH 7 내지 12로 유지되도록 하는 것으로서, 상기 pH가 7 미만이면 질산칼슘이 반응되지 않는다.The caustic soda according to the present invention allows the thermal reflection and the heat and waterproof coating composition to be maintained at an appropriate pH, for example, a pH of 7 to 12. When the pH is less than 7, calcium nitrate is not reacted.
상기 가성소다의 사용량은 열반사 및 차열 방수도료 조성물을 구성하는 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 1 내지 20중량부인 것이 좋다. The amount of the caustic soda to be used is preferably 1 to 20 parts by weight based on 100 parts by weight of the polyisocyanate-free polymer constituting the thermal reflection and waterproof coating composition.
본 발명에 따른 경화제는 방수도료 조성물, 특정적으로 열반사 및 차열 방수도료 조성물, 특정적으로 폴리 이소시아네이트 프리 폴리머를 경화시켜 폴리우레아를 제조하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 경화제라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 아민혼합물 예를 들면, 폴리옥시에테르 폴리아민 혼합물, 트리에탄올아민, 메틸디에탄올아민, 트리이소프로판올 아민, 4-디메틸아미노벤조산메틸, 4-디메틸아미노벤조산에틸, 4-디메틸아미노벤조산이 소아밀, 4-디메틸아미노벤조산2-에틸헥실, 벤조산2-디메틸아미노에틸, N,N-디메틸파라톨루이딘, 4,4'-비스(디메틸아미노)벤조페논, 4,4'-비스(디에틸아미노)벤조페논 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용할 수 있다.The curing agent according to the present invention is used for producing a waterproof coating composition, specifically a heat reflecting and heat shielding waterproofing coating composition, specifically a polyisocyanate prepolymer to produce a polyurea, and a conventional curing agent Any amine can be used, but preferably an amine mixture such as a polyoxyetherpolyamine mixture, triethanolamine, methyldiethanolamine, triisopropanolamine, methyl 4-dimethylaminobenzoate, ethyl 4-dimethylaminobenzoate, Dimethylaminobenzoic acid, 2-ethylhexyl 4-dimethylaminobenzoate, 2-dimethylaminoethyl benzoate, N, N-dimethylparatoluidine, 4,4'-bis (dimethylamino) benzophenone, 4,4 ' -Bis (diethylamino) benzophenone or a mixture of at least one selected from these may be used.
바람직한 경화제의 사용량은 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 1 내지 30중량부인 것이 좋다.The amount of the curing agent to be used is preferably 1 to 30 parts by weight based on 100 parts by weight of the polyisocyanate-free polymer.
본 발명에 따른 옥틸페놀 에톡실레이트는 에톡실화된 옥틸페놀 유도체로서, 열반사 및 차열 방수도료 조성물을 용이하게 경화시키기 위한 것이다.The octylphenol ethoxylate according to the present invention is an ethoxylated octylphenol derivative for easily curing a heat reflecting and heat shielding waterproofing paint composition.
바람직한 옥틸페놀 에톡실레이트의 사용량은 열반사 및 차열 방수도료 조성물을 구성하는 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 0.1 내지 10중량부인 것이 좋다. The preferred amount of the octyl phenol ethoxylate to be used is 0.1 to 10 parts by weight based on 100 parts by weight of the polyisocyanate-free polymer constituting the heat reflecting and waterproof coating composition.
본 발명에 따른 질산칼슘은 열반사 및 차열 방수도료 조성물의 내후성 등을 향상시키기 위한 것으로서, 그 사용량은 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 35중량부인 것이 좋다.The calcium nitrate according to the present invention is used for improving the weather resistance and the like of the heat reflecting and heat shielding waterproof coating composition and is preferably used in an amount of 5 to 35 parts by weight based on 100 parts by weight of the polyisocyanate prepolymer.
본 발명에 따른 금속분말은 방수도료 조성물, 특정적으로 열반사 및 차열 방수도료 조성물에 포함되어 도막 형성 후 외부로부터 조사되는 빛, 특정적으로 자외선 등의 빛을 반사, 분산 및/또는 산란시켜 열반사하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 금속분말이라면 어떠한 것을 사용하여도 무방하며, 그 사용량은 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 10 내지 30중량부인 것을 추천한다.The metal powder according to the present invention can be applied to a waterproof coating composition, specifically a heat reflecting and heat shielding waterproof coating composition, to reflect, disperse and / or scatter light such as ultraviolet light, Any conventional metal powder having such a purpose may be used. It is recommended that the metal powder be used in an amount of 10 to 30 parts by weight based on 100 parts by weight of the polyisocyanate-free polymer.
바람직한 금속분말은 알미늄분말, 아연분말, 황동분말, 스테인리스분말, 동분말 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다.Preferred metal powders are aluminum powder, zinc powder, brass powder, stainless steel powder, copper powder, or a mixture of at least one selected from these.
본 발명에 따른 수용성 아크릴 수지는 열반사 및 차열 방수도료 조성물의 내구성, 접착성 등을 향상시키기 위한 것으로서, 그 사용량은 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 30중량부인 것이 좋다.The water-soluble acrylic resin according to the present invention is used for improving the durability, adhesiveness and the like of the heat reflection and heat and waterproof coating composition, and it is preferably used in an amount of 5 to 30 parts by weight based on 100 parts by weight of the polyisocyanate-free polymer.
본 발명에 따른 증점제는 방수도료 조성물의 사용이 용이하도록 점도를 조절하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 증점제라면 특별히 한정되지 않지만, 추천하기로는 하이드록시 에틸 셀룰로오스(HydroxyEthyl Cellulose), 소수성 우레탄변성계 증점제 또는 이들의 혼합물을 사용하는 것을 추천한다.The thickener according to the present invention is for controlling the viscosity to facilitate the use of the waterproof coating composition and is not particularly limited as long as it is a conventional thickener in the related art having such a purpose. However, it is recommended to use hydroxyethyl cellulose, Urethane modifier thickener or a mixture thereof is preferably used.
바람직한 증점제의 사용량은 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 1 내지 20중량부인 것을 추천한다.The amount of the thickener to be used is preferably 1 to 20 parts by weight based on 100 parts by weight of the polyisocyanate-free polymer.
본 발명에 따른 용제는 열반사 및 차열 방수도료 조성물이 용해되는 것으로서, 당업계의 통상적인 용제라면 어떠한 것이라도 무장하지만, 바람직하게는 물을 사용하는 것이 좋고, 그 사용량은 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 50 내지 1,000중량부인 것이 좋다.The solvent according to the present invention dissolves the heat-reflecting and heat-resistant and waterproof coating composition, and any conventional solvent in the art may be used. Preferably, water is used. The amount of the solvent is 100 parts by weight of the polyisocyanate- Preferably 50 to 1,000 parts by weight.
특정 양태로서, 본 발명에 따른 열반사 및 차열 방수도료 조성물, 특정적으로 금속분말을 포함하는 열반사 및 차열 방수도료 조성물은 방수도료 조성물이 시공되는 접촉면에 보다 용이하게 접착할 수 있도록 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 25중량부의 부착증진제를 더 포함할 수 있다.In a particular embodiment, the heat-reflective and heat-resistant waterproof coating compositions according to the present invention, including heat-reflective and heat-resistant waterproof coating compositions, specifically metal powders, are prepared by coating polyisocyanate- And 5 to 25 parts by weight of an adhesion promoter based on 100 parts by weight of the polymer.
바람직한 부착증진제는 하이드록시 에틸 아크릴로일 포스페이트, 하이드록시 에틸 메타 아크릴레이트 포스페이트 또는 이들의 혼합물을 사용할 수 있다.Preferred adhesion promoters are hydroxyethyl acryloyl phosphate, hydroxyethyl methacrylate phosphate or mixtures thereof.
다른 특정 양태로서, 본 발명에 따른 열반사 및 차열 방수도료 조성물은 접착성을 향상시키기 위하여 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 1 내지 10중량부의 옥틸트리에톡시실란을 더 포함할 수 있다.In another specific embodiment, the heat reflecting and heat shielding waterproof coating composition according to the present invention may further comprise 1 to 10 parts by weight of octyltriethoxysilane based on 100 parts by weight of the polyisocyanate-free polymer to improve adhesion.
여기서, 상기 옥틸트리에톡시실란은 단량체 형태로 사용 가능하며, 상기 단량체의 분자량은 특별히 한정되는 것은 아니지만, 바람직하게는 150 내지 450Da인 것이 좋다.The octyltriethoxysilane can be used in the form of a monomer, and the molecular weight of the monomer is not particularly limited, but is preferably 150 to 450 Da.
또 다른 특정 양태로서, 본 발명에 따른 열반사 및 차열 방수도료 조성물은 조성물의 산화를 방지하기 위하여 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 3 내지 15중량부의 산화방지제를 더 포함할 수 있다.In another specific embodiment, the heat-reflecting and heat-resistant waterproof coating composition according to the present invention may further comprise 3 to 15 parts by weight of an antioxidant based on 100 parts by weight of the polyisocyanate-free polymer to prevent oxidation of the composition.
바람직한 산화방지제는 아민계, 비스페놀계, 모노페놀계 및 유황계 산화방지제가 사용될 수 있지만, 보다 구체적으로 2.2-메틸렌비스(4-메틸-6-t-부틸페놀)[2 . 2 - M e t h y l e n e b i s ( 4 - m e t h y l - 6 - t - b u t y l p h e n o l )], 2.6-디-t-부틸-4-메틸페놀(2.6-di -t-Butyl-4-methylphenol) 또는 이들의 혼합물을 사용하는 것을 추천한다. Preferred antioxidants include amine-based, bisphenol-based, monophenol-based and sulfur-based antioxidants, but more specifically, 2.2-methylenebis (4-methyl-6-t-butylphenol). 2 - M ethylenebis (4 - methyl - 6 - t - butylphenol), 2.6 - di - t - Butyl - 4 - methylphenol or mixtures thereof I recommend you.
또 다른 특정 양태로서, 본 발명에 따른 열반사 및 차열 방수도료 조성물은 조성물을 자외선으로부터 보호하여 안정성을 제공하기 위하여 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 1 내지 10중량부의 안정제를 더 포함할 수 있다.In another specific embodiment, the heat-reflecting and heat-resistant waterproof coating composition according to the present invention may further comprise 1 to 10 parts by weight of a stabilizer based on 100 parts by weight of the polyisocyanate-free polymer in order to protect the composition from ultraviolet rays to provide stability .
바람직한 안정제로는 아크릴 폴리올 수지, 무황변 폴리 우레아수지, 폴리이소시아네이트 또는 이들의 혼합물을 사용하는 것이 좋다.Preferred stabilizers are acrylic polyol resins, non-yellowing polyurea resins, polyisocyanates or mixtures thereof.
또 다른 특정 양태로서, 본 발명에 따른 열반사 및 차열 방수도료 조성물은 시공 대상면으로부터 쉽게 박리되는 것을 방지하기 위하여 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 30중량부의 박리방지제를 더 포함할 수 있다.In another specific embodiment, the heat-reflecting and heat-resistant waterproof coating composition according to the present invention may further comprise 5 to 30 parts by weight of an anti-peeling agent based on 100 parts by weight of the polyisocyanate-free polymer in order to prevent easy peeling from the surface to be applied have.
바람직한 박리방지제는 폴리인산계, 아민계, 또는 인산 에스테르계 박리방지제를 사용하는 것이 좋다.As the preferable peeling inhibitor, it is preferable to use a polyphosphoric acid type, an amine type, or a phosphoric acid ester type peeling inhibitor.
특정적으로, 상기 박리방지제는 액상형으로 비중이 1.0 이상이고 60℃ 점도가 110 cPs인 폴리인산계 박리방지제; 산가가 10 ㎎KOH/g 이하이고, 총 아민가가 140 내지 400㎎HCl/g인 아민계 박리방지제일 수 있다.Specifically, the anti-peeling agent is a liquid phase anti-peeling agent having a specific gravity of 1.0 or more and a viscosity at 60 DEG C of 110 cPs; The acid value is 10 mgKOH / g or less, and the total amine value is 140 to 400 mg HCl / g.
또 다른 특정 양태로서, 본 발명에 따른 열반사 및 차열 방수도료 조성물은 균열발생을 억제하고, 접착력 및 내구성을 향상시키기 위하여 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 20중량부의 바이오 수지를 더 포함할 수 있다.In another specific embodiment, the heat-reflecting and heat-resistant waterproof coating composition according to the present invention further comprises 5 to 20 parts by weight of a bio-resin based on 100 parts by weight of the polyisocyanate-free polymer in order to suppress cracking and improve adhesion and durability can do.
바람직한 바이오 수지는 유변성 알키드 수지, 유변성 우레탄 수지, 유변성 우레탄 수지의 지방산 에스테르, 유변성 에폭시 수지, 유변성 에폭시 수지의 지방산 에스테르, 바이오 폴리에틸렌 수지, L-폴리락트산 또는 이들의 혼합물로 이루어진 것을 사용하는 것이 좋고, 추천하기로는 유변성 알키드 수지를 사용하는 것이 좋다.Preferable bio-resins include those made of a rubidic alkyd resin, a rubidic urethane resin, a fatty acid ester of a rubidic urethane resin, a rubidic epoxy resin, a fatty acid ester of a rubidic epoxy resin, a biopolyethylene resin, L-polylactic acid or a mixture thereof It is recommended to use a rubidic alkyd resin.
여기서, 상기 유변성은 지방산 등의 유성분을 분자 중에 함유하는 수지를 지칭하는 것으로서, 이러한 유변성 수지를 사용하게 되면 분산성, 기계적 성질, 경화성, 피막 형성성을 제어하기 용이하다.Here, the rheological property refers to a resin containing a oil component such as a fatty acid in a molecule. When such a rheological resin is used, it is easy to control the dispersibility, the mechanical properties, the curability, and the film formability.
특정적으로, 상기 바이오 수지는 식물성 오일, 예를 들면 식물 또는 식물의 씨로부터 추출된 오일로, 쌀 기름, 팜 오일, 코코넛 오일, 피마자 오일, 포도씨 오일, 호호바 오일, 홍화 오일, 마카데미아너츠 오일, 올리브씨 오일, 및 이들의 혼합 오일과 혼합하여 사용할 수 있다.Specifically, the bio-resin is an oil extracted from a vegetable oil, for example, a plant or a plant seed, and is preferably selected from the group consisting of rice oil, palm oil, coconut oil, castor oil, grape seed oil, jojoba oil, safflower oil, Oil, olive seed oil, and mixed oil thereof.
이때, 상기 바이오 수지와 식물성 오일의 혼합비는 사용자의 선택에 따라 변경 가능하지만, 추천하기로는 바이오 수지와 식물성 오일의 중량비율로서 1:9 내지 9:1인 것이 좋다.At this time, the mixing ratio of the bio resin and the vegetable oil can be changed according to the user's choice, but it is recommended that the weight ratio of the bio resin and the vegetable oil is 1: 9 to 9: 1.
또 다른 특정 양태로서, 본 발명에 따른 열반사 및 차열 방수도료 조성물은 코팅 도막의 점탄성을 높이기 위하여 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 0.1 내지 1중량부의 소듐 벤조 에이트(sodium benzoate)를 더 포함할 수 있는데, 소듐 벤조 에이트가 0.1중량부 보다 적을 경우 효과가 미미하며, 1중량부를 초과할 경우 과량이 되어 물성을 저하시킬 수 있다.In another specific embodiment, the heat-reflecting and heat-resistant waterproof coating composition according to the present invention further comprises 0.1 to 1 part by weight of sodium benzoate based on 100 parts by weight of the polyisocyanate-free polymer in order to increase the viscoelasticity of the coating film If sodium benzoate is less than 0.1 part by weight, the effect is insignificant. If it exceeds 1 part by weight, excessive amount of sodium benzoate may deteriorate physical properties.
또 다른 특정 양태로서, 본 발명에 따른 열반사 및 차열 방수도료 조성물은 색상을 부가하기 위하여 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 30중량부의 안료를 더 포함할 수 있다.In another specific embodiment, the heat-reflecting and heat-resistant waterproof coating composition according to the present invention may further comprise 5 to 30 parts by weight of pigment based on 100 parts by weight of the polyisocyanate-free polymer in order to add color.
바람직한 안료로는 무기계 안료 및/또는 유기계 안료를 사용하는 것이 좋다.As the preferable pigment, it is preferable to use an inorganic pigment and / or an organic pigment.
상기 무기계 안료는 산화철, 수산화철, 산화크롬, 산화티탄 또는 이들의 혼합물을 포함한다.The inorganic pigments include iron oxide, iron hydroxide, chromium oxide, titanium oxide, or mixtures thereof.
이때, 산화철, 수산화철은 적갈색을 나타내고, 산화크롬은 녹색을 나타내고, 산화티탄은 백색을 나타낸다.At this time, iron oxide and iron hydroxide show reddish brown color, chromium oxide shows green, and titanium oxide shows white.
상기 유기계 안료는 카본 블랙, 아조피그먼트 또는 이들의 혼합물을 사용하는 것이 좋다.The organic pigments may be carbon black, azo pigments or mixtures thereof.
또 다른 특정 양태로서, 본 발명에 따른 열반사 및 차열 방수도료 조성물은 금속분말에 의해 발생하는 눈부심을 감소시키기 위하여 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 15중량부 규사, 모래, 고분자 수지 입자, 세라믹 입자 또는 이들의 혼합물을 더 포함시킬 수 있다.In another specific embodiment, the heat-reflecting and heat-shrinkable waterproof coating composition according to the present invention comprises 5 to 15 parts by weight of silica, sand, and polymer resin particles based on 100 parts by weight of the polyisocyanate-free polymer in order to reduce the glare caused by the metal powder , Ceramic particles, or a mixture thereof.
여기서, 상기 고분자 수지 입자는 고분자 수지로 이루어진 당업계의 통상적인 입자라면 어떠한 것을 사용하여도 무방하다.Here, the polymeric resin particles may be any conventional particles made of a polymer resin in the art.
또 다른 특정 양태로서, 본 발명에 따른 열반사 및 차열 방수도료 조성물은 점도증진 및 부착력 강화를 위하여 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 10중량부의 알긴산 나트륨을 더 포함할 수 있는데, 폴리 이소시아네이트 프리 폴리머 100중량부에 대하여 함량이 5중량부 미만이면 소수성이 저하되고, 함량이 10중량부를 초과하면 과도하게 점도가 상승되어 좋지 않다.In another specific embodiment, the heat-reflecting and heat-resistant waterproof coating composition according to the present invention may further comprise sodium alginate in an amount of 5 to 10 parts by weight based on 100 parts by weight of the polyisocyanate-free polymer for enhancing viscosity and enhancing adhesion, When the content is less than 5 parts by weight based on 100 parts by weight of the prepolymer, the hydrophobicity decreases. When the content exceeds 10 parts by weight, the viscosity is excessively increased.
상기 알긴산 나트륨은(C6H8O6)n으로 표시되는 다당류의 하나로서 카르복실기를 가지고 있으며, 다시마류를 소다회 처리하여 만들 수 있는데, 알긴산 나트륨 자체에 점성을 갖고 있어 이를 열반사 및 차열 방수도료 조성물에 혼입되면 점도증진 및 부착력을 강화하게 된다.The sodium alginate is one of the polysaccharides represented by (C 6 H 8 O 6 ) n and has a carboxyl group and can be made by soda ash treatment of seaweed. Since sodium alginate itself has a viscosity, it is heat- The incorporation into the composition enhances viscosity enhancement and adhesion.
또 다른 특정 양태로서, 본 발명에 따른 열반사 및 차열 방수도료 조성물은 조성물의 표면에 수분침투를 방지하면서 통기성을 확보하기 위하여 폴리 이소시아네이트 프리 폴리머 100중량부를 기준으로 1 내지 5중량부의 소디윰스테아레이트를 더 포함할 수 있는데, 폴리 이소시아네이트 프리 폴리머 100중량부를 기준으로 1중량부 미만이면 목적한 수분침투 방지기능을 얻을 수 없고, 5중량부를 초과하면 조성물의 강도 저하현상을 나타내어 좋지 않다.In another specific embodiment, the heat-reflecting and heat-resistant waterproof coating composition according to the present invention comprises 1 to 5 parts by weight of sodium dodecyl stearate, based on 100 parts by weight of the polyisocyanate-free polymer, in order to ensure permeability while preventing moisture penetration on the surface of the composition. If the amount is less than 1 part by weight based on 100 parts by weight of the polyisocyanate-free polymer, desired moisture permeation preventing function can not be obtained. If the amount is more than 5 parts by weight, the strength of the composition is lowered.
또 다른 특정 양태로서, 본 발명에 따른 열반사 및 차열 방수도료 조성물은 분산성을 향상시키기 위하여 폴리 이소시아네이트 프리 폴리머 100중량부를 기준으로 5 내지 15중량부의 이소보닐아크릴레이트를 더 포함할 수 있다.In another specific embodiment, the heat-reflecting and heat-resistant waterproof coating composition according to the present invention may further include 5 to 15 parts by weight of isobornyl acrylate based on 100 parts by weight of the polyisocyanate-free polymer in order to improve dispersibility.
또 다른 특정 양태로서, 열반사 및 차열 방수도료 조성물은 조성물이 접착되는 피접착면에 존재하는 유해 성분들이 외부로 용출되는 것을 방지함으로써 환경오염을 유발되는 것을 방지하기 위하여 폴리 이소시아네이트 프리 폴리머 100중량부를 기준으로 5 내지 15중량부의 디메틸 암모늄 클로라이드를 더 포함할 수 있다.In another specific embodiment, the heat-reflecting and heat-resistant waterproof coating composition is prepared by dissolving 100 parts by weight of a polyisocyanate-free polymer in order to prevent environmental pollution by preventing harmful components present on the surface to be bonded, 5 to 15 parts by weight of dimethyl ammonium chloride may be further included.
전술한 구성을 갖는 본 발명에 따른 열반사 및 차열 방수도료 조성물을 이용하여 도막을 형성하기 위한 대상면에 방수도료 조성물을 시공하는 방법, 예를 들면 방수 시공방법을 설명하면 다음과 같다.A method of applying a waterproof coating composition to a target surface for forming a coating film using the heat reflecting and heat shielding waterproofing coating composition according to the present invention having the above-described structure, for example, a waterproofing method will be described below.
이때, 상기 방수 시공방법은 당업계의 통상적인 방법이라면 특별히 한정되지 않지만, 본 발명을 보다 용이하게 설명하기 위해 상기 방수 시공방법의 일례를 설명하면 다음과 같다.At this time, the waterproof construction method is not particularly limited as long as it is a conventional method in the related art, but an example of the waterproof construction method will be described below to explain the present invention more easily.
본 발명에 따른 방수 시공방법은 열반사 및 차열 방수도료 조성물을 시공하기 위한 시공표면을 처리하는 표면처리단계; 및The waterproofing method according to the present invention includes: a surface treatment step of treating a construction surface for applying a heat reflecting and waterproofing paint composition; And
상기 시공표면에 폴리 이소시아네이트 프리 폴리머 100중량부, 에틸렌 초산 비닐 10 내지 60중량부, 음이온 유화제 5 내지 30중량부, 고무 화합물 5 내지 20중량부, 가성소다 1 내지 20중량부, 경화제 1 내지 30중량부, 옥틸페놀 에톡실레이트 0.1 내지 10중량부, 질산칼슘 5 내지 35중량부, 금속분말 10 내지 30중량부, 수용성 아크릴 수지 5 내지 30중량부, 증점제 1 내지 20중량부, 및 용제 50 내지 1,000중량부를 포함하는 열반사 방수도료 조성물을 최소 건조 도막두께 0.1mm 이상, 바람직하게는 0.1mm 내지 6mm, 보다 바람직하게는 0.1mm 내지 2mm가 될 때까지 도포하는 도포단계를 포함한다.Wherein the polyisocyanate prepolymer is contained in an amount of 100 parts by weight, 10 to 60 parts by weight of ethylene vinyl acetate, 5 to 30 parts by weight of an anionic emulsifier, 5 to 20 parts by weight of a rubber compound, 1 to 20 parts by weight of caustic soda, 0.1 to 10 parts by weight of octylphenol ethoxylate, 5 to 35 parts by weight of calcium nitrate, 10 to 30 parts by weight of a metal powder, 5 to 30 parts by weight of a water-soluble acrylic resin, 1 to 20 parts by weight of a thickener, By weight of a heat-reflective waterproof coating composition containing a water-insoluble portion and a water-insoluble portion in an amount of not less than 0.1 mm, preferably 0.1 to 6 mm, more preferably 0.1 to 2 mm.
여기서, 상기 표면처리 단계는 시공표면에 붙어 있는 먼지, 오염물, 또는 오일 등의 이물질을 제거하고, 시공표면의 돌출부를 매끄럽게 처리하는 것을 지칭한다.Here, the surface treatment step refers to the removal of foreign matter such as dust, contaminants, or oil adhering to the application surface, and smooth treatment of protrusions on the application surface.
또한, 상기 도막두께는 습윤상태에서 최대 10mm를 초과하지 않도록 하는 것이 좋다.In addition, it is preferable that the coating film thickness does not exceed a maximum of 10 mm in the wet state.
특정 양태로서, 본 발명에 따른 방수 시공방법은 도포단계의 전단으로 프라이머를 도포하는 프라이머 도포단계를 더 포함할 수 있다.In a specific embodiment, the waterproofing method according to the present invention may further comprise a primer applying step of applying a primer to the front end of the applying step.
여기서, 상기 프라이머 도포단계에 사용되는 프라이머는 에폭시 접착제를 사용하는 것을 추천하지만, 이에 한정되는 것이 아니라 당업계에서 통상적으로 사용하는 프라이머라면 어떠한 것을 사용하여도 무방하다.Although it is recommended to use an epoxy adhesive as the primer to be used in the primer coating step, it is not limited thereto, and any primer commonly used in the art may be used.
다른 특정 양태로서, 본 발명에 따른 방수 시공방법은 도포단계의 후단으로 도포가 종료된 시공표면을 보호하기 위한 보호층을 형성하는 보호층 형성단계를 더 포함할 수 있다.In another specific embodiment, the waterproofing method according to the present invention may further include a protective layer forming step of forming a protective layer for protecting the applied surface, which is applied to the rear end of the applying step.
이때, 상기 보호층은 부직포, 시멘트몰탈, 타일 또는 보호판재를 포함할 수 있으며, 차열기능을 향상하기 위하여 상기 보호층의 표면에 중공세라믹을 코팅하여 사용할 수 도 있다.
At this time, the protective layer may include a nonwoven fabric, a cement mortar, a tile or a protective plate, and a hollow ceramic may be coated on the surface of the protective layer to improve the heat shielding function.
이하에서 실시예를 통하여 본 발명을 구체적으로 설명하기로 한다. 그러나 하기의 실시예는 오로지 본 발명을 구체적으로 설명하기 위한 것으로 이들 실시예에 의해 본 발명의 범위를 한정하는 것은 아니다.
Hereinafter, the present invention will be described in detail by way of examples. However, the following examples are for illustrative purposes only and are not intended to limit the scope of the present invention.
[실시예 1][Example 1]
톨루엔 다이이소시아네이트 100g, 에틸렌 초산 비닐 30g, 음이온 유화제로서 수지산나트륨염 15g, 고무 화합물로서 수계 클로로프렌 고무 10g, 가성소다 10g, 트리에탄올아민과 메틸디에탄올아민이 1:1의 중량비로 혼합된 경화제 15g, 옥틸페놀 에톡실레이트 5g, 질산칼슘 20g, 알루미늄분말 15g; 수용성 아크릴 수지 15g, 하이드록시 에틸 셀룰로오스 10g, 물 100g을 혼합하여 열반사 및 차열 방수도료 조성물을 제조하였다.
15 g of a curing agent prepared by mixing 100 g of toluene diisocyanate, 30 g of ethylene vinyl acetate, 15 g of sodium acid salt as an anionic emulsifier, 10 g of waterborne chloroprene rubber as a rubber compound, 10 g of caustic soda, triethanolamine and methyl diethanolamine in a weight ratio of 1: 5 g of octylphenol ethoxylate, 20 g of calcium nitrate and 15 g of aluminum powder; 15 g of water-soluble acrylic resin, 10 g of hydroxyethylcellulose, and 100 g of water were mixed to prepare a heat-reflective and heat-resistant waterproof coating composition.
[실시예 2][Example 2]
실시예 1과 동일한 방법으로 실시하되, 하이드록시 에틸 아크릴로일 포스페이트 10g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 10 g of hydroxyethyl acryloyl phosphate was further added.
[실시예 3][Example 3]
실시예 1과 동일한 방법으로 실시하되, 옥틸트리에톡시실란 5g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated except that 5 g of octyltriethoxysilane was further added.
[실시예 4][Example 4]
실시예 1과 동일한 방법으로 실시하되, 2.6-디-t-부틸-4-메틸페놀 7g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated except that 7 g of 2,6-di-t-butyl-4-methylphenol was further added.
[실시예 5][Example 5]
실시예 1과 동일한 방법으로 실시하되, 무황변 폴리 우레아수지 5g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 5 g of non-yellowing polyurea resin was further added.
[실시예 6][Example 6]
실시예 1과 동일한 방법으로 실시하되, 액상형으로 비중이 1.0 이상이고 60℃ 점도가 110 cPs인 폴리인산계 박리방지제 15g을 더 부가하여 실시하였다.
15 g of a polyphosphoric acid-based anti-peeling agent having a specific gravity of 1.0 or more and a viscosity of 60 c of 110 cPs was further added in the same manner as in Example 1.
[실시예 7][Example 7]
실시예 1과 동일한 방법으로 실시하되, L-폴리락트산 10g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 10 g of L-polylactic acid was further added.
[실시예 8][Example 8]
실시예 1과 동일한 방법으로 실시하되, 소듐 벤조 에이트 0.5g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 0.5 g of sodium benzoate was further added.
[실시예 9][Example 9]
실시예 1과 동일한 방법으로 실시하되, 알긴산 나트륨 7g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 7 g of sodium alginate was further added.
[실시예 10][Example 10]
실시예 1과 동일한 방법으로 실시하되, 소디윰스테아레이트 3g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 3 g of sodium dodecyl stearate was further added.
[실시예 11][Example 11]
실시예 1과 동일한 방법으로 실시하되, 이소보닐아크릴레이트 10g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 10 g of isobornyl acrylate was further added.
[실시예 12][Example 12]
실시예 1과 동일한 방법으로 실시하되, 디메틸 암모늄 클로아이드 10g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 10 g of dimethylammonium chloride was added.
[실시예 13][Example 13]
먼저, 방수 도막을 형성하기 위한 시공표면인 콘크리트의 표면을 세척하여 오염물질을 제거하였다. First, the surface of concrete, which is a construction surface for forming a waterproof coating, was washed to remove contaminants.
그 다음, 상기 시공표면에 실시예 1에 따라 제조된 열반사 및 차열 방수도료 조성물을 도막 두께 2mm로 도포하여 방수 도막을 형성시켰다.Next, the heat-reflective and heat-resistant waterproof coating composition prepared according to Example 1 was coated on the applied surface with a coating film thickness of 2 mm to form a waterproof coating film.
[실시예 14][Example 14]
실시예 13과 동일한 방법으로 실시하되, 실시예 1에 따라 제조된 열반사 및 차열 방수도료 조성물 대신 실시예 2에 따라 제조된 열반사 및 차열 방수도료 조성물을 사용하였다.
Except that the heat-reflective and heat-resistant waterproof coating compositions prepared according to Example 2 were used instead of the heat-reflective and heat-resistant waterproof coating compositions prepared according to Example 1,
[실시예 15][Example 15]
실시예 13과 동일한 방법으로 실시하되, 실시예 1에 따라 제조된 열반사 및 차열 방수도료 조성물 대신 실시예 3에 따라 제조된 열반사 및 차열 방수도료 조성물을 사용하였다.
The heat-reflective and heat-resistant waterproof coating composition prepared in Example 3 was used instead of the heat-reflective and heat-resistant waterproof coating composition prepared in Example 1,
[실시예 16][Example 16]
실시예 13과 동일한 방법으로 실시하되, 실시예 1에 따라 제조된 열반사 및 차열 방수도료 조성물 대신 실시예 4에 따라 제조된 열반사 및 차열 방수도료 조성물을 사용하였다.
Except that the heat-reflecting and heat-resistant waterproof coating composition prepared according to Example 4 was used instead of the heat-reflective and heat-resistant waterproof coating composition prepared in Example 1, in the same manner as in Example 13.
[실시예 17][Example 17]
실시예 13과 동일한 방법으로 실시하되, 실시예 1에 따라 제조된 열반사 및 차열 방수도료 조성물 대신 실시예 5에 따라 제조된 열반사 및 차열 방수도료 조성물을 사용하였다.
Except that the heat-reflecting and heat-resistant waterproof coating compositions prepared according to Example 5 were used instead of the heat-reflective and heat-resistant waterproof coating compositions prepared according to Example 1,
[실시예 18][Example 18]
실시예 13과 동일한 방법으로 실시하되, 실시예 1에 따라 제조된 열반사 및 차열 방수도료 조성물 대신 실시예 6에 따라 제조된 열반사 및 차열 방수도료 조성물을 사용하였다.
The heat-reflecting and heat-resistant waterproof coating composition prepared in Example 6 was used instead of the heat-reflective and heat-resistant waterproof coating composition prepared in Example 1,
[실시예 19][Example 19]
실시예 13과 동일한 방법으로 실시하되, 실시예 1에 따라 제조된 열반사 및 차열 방수도료 조성물 대신 실시예 7에 따라 제조된 열반사 및 차열 방수도료 조성물을 사용하였다.
The heat-reflecting and heat-resistant waterproof coating composition prepared in Example 7 was used instead of the heat-reflective and heat-resistant waterproof coating composition prepared in Example 1,
[실시예 20][Example 20]
실시예 13과 동일한 방법으로 실시하되, 실시예 1에 따라 제조된 열반사 및 차열 방수도료 조성물 대신 실시예 8에 따라 제조된 열반사 및 차열 방수도료 조성물을 사용하였다.
Except that the heat-reflective and heat-resistant waterproof coating compositions prepared according to Example 8 were used instead of the heat-reflective and heat-resistant waterproof coating compositions prepared according to Example 1,
[실시예 21][Example 21]
실시예 13과 동일한 방법으로 실시하되, 실시예 1에 따라 제조된 열반사 및 차열 방수도료 조성물 대신 실시예 9에 따라 제조된 열반사 및 차열 방수도료 조성물을 사용하였다.
The heat-reflecting and heat-resistant waterproof coating composition prepared according to Example 9 was used instead of the heat-reflective and heat-resistant waterproof coating composition prepared in Example 1, in the same manner as in Example 13.
[실시예 22][Example 22]
실시예 13과 동일한 방법으로 실시하되, 실시예 1에 따라 제조된 열반사 및 차열 방수도료 조성물 대신 실시예 10에 따라 제조된 열반사 및 차열 방수도료 조성물을 사용하였다.
The heat-reflecting and heat-resistant waterproof coating composition prepared in Example 10 was used instead of the heat-reflective and heat-resistant waterproof coating composition prepared in Example 1,
[실시예 23][Example 23]
실시예 13과 동일한 방법으로 실시하되, 실시예 1에 따라 제조된 열반사 및 차열 방수도료 조성물 대신 실시예 11에 따라 제조된 열반사 및 차열 방수도료 조성물을 사용하였다.
Except that the heat-reflective and heat-resistant waterproof coating compositions prepared according to Example 11 were used in place of the heat-reflective and heat-resistant waterproof coating compositions prepared according to Example 1,
[실시예 24][Example 24]
실시예 13과 동일한 방법으로 실시하되, 실시예 1에 따라 제조된 열반사 및 차열 방수도료 조성물 대신 실시예 12에 따라 제조된 열반사 및 차열 방수도료 조성물을 사용하였다.
The heat-reflecting and heat-resistant waterproof coating composition prepared according to Example 12 was used in place of the heat-reflective and heat-resistant waterproof coating composition prepared in Example 1,
[실험][Experiment]
실시예 13 내지 실시예 24에 따라 형성된 도막의 인장성능, 인열성능, 온도 의존성, 가열 신축성상, 인장성능, 열화성상 및 경화시간을 측정하여 그 결과를 표 1로 나타냈다.
Tensile performance, tear performance, temperature dependency, heat stretchability, tensile performance, deteriorated properties and curing time of the coating film formed according to Examples 13 to 24 were measured and the results are shown in Table 1. [
표 1에 나타난 바와 같이, 실시예 13 내지 실시예 24에 따라 제조된 방수 도막의 인장성능, 신축률, 열화성상, 신장율이 기준치에 부합되는 것을 알 수 있었으며, 빛에 대한 반사도가 30% 이상이라는 것을 알 수 있었다.
As shown in Table 1, it was found that the tensile performance, the expansion / contraction ratio, the deterioration property and the elongation percentage of the waterproof coating film prepared according to Examples 13 to 24 corresponded to the reference values, and the reflectance to light was 30% or more .
이상에서 설명한 바와 같이, 본 발명이 속하는 기술 분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예는 모두 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위의 의미 및 범위 그리고 그 등가개념으로부터 도출되는 모두 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.
As described above, those skilled in the art will understand that the present invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. It is therefore to be understood that the embodiments described above are all illustrative and not restrictive. The scope of the present invention should be construed as being included in the scope of the present invention without departing from the scope of the present invention.
Claims (6)
에틸렌 초산 비닐 10 내지 60중량부;
음이온 유화제 5 내지 30중량부;
고무 화합물 5 내지 20중량부;
가성소다 1 내지 20중량부;
경화제 1 내지 30중량부;
옥틸페놀 에톡실레이트 0.1 내지 10중량부;
질산칼슘 5 내지 35중량부;
금속분말 10 내지 30중량부;
수용성 아크릴 수지 5 내지 30중량부;
증점제 1 내지 20중량부; 및
용제 50 내지 1,000중량부를 포함하는 열반사 및 차열 방수도료 조성물에,
바이오 수지를 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 20중량부로 더 포함하고,
소듐 벤조 에이트를 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 0.1 내지 1중량부로 더 포함하며,
알긴산 나트륨을 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 10중량부로 더 포함하고,
소디윰스테아레이트를 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 1 내지 5중량부로 더 포함하며,
이소보닐아크릴레이트를 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 15중량부로 더 포함하고,
디메틸 암모늄 클로라이드를 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 15중량부로 더 포함하며,
부착증진제를 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 25중량부로 더 포함하고,
산화방지제를 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 3 내지 15중량부로 더 포함하며,
박리방지제를 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 30중량부로 더 포함하는 열반사 및 차열 방수도료 조성물.
100 parts by weight of a polyisocyanate-free polymer;
10 to 60 parts by weight of ethylene vinyl acetate;
5 to 30 parts by weight of an anionic emulsifier;
5 to 20 parts by weight of a rubber compound;
1 to 20 parts by weight of caustic soda;
1 to 30 parts by weight of a curing agent;
0.1 to 10 parts by weight of octylphenol ethoxylate;
5 to 35 parts by weight of calcium nitrate;
10 to 30 parts by weight of a metal powder;
5 to 30 parts by weight of a water-soluble acrylic resin;
1 to 20 parts by weight of a thickener; And
And 50 to 1,000 parts by weight of a solvent,
Further comprising 5 to 20 parts by weight of a bio-resin based on 100 parts by weight of the polyisocyanate-free polymer,
Further comprising sodium benzoate in an amount of 0.1 to 1 part by weight based on 100 parts by weight of the polyisocyanate prepolymer,
Further comprising sodium alginate in an amount of 5 to 10 parts by weight based on 100 parts by weight of the polyisocyanate-free polymer,
Further comprising 1 to 5 parts by weight, based on 100 parts by weight of the polyisocyanate-free polymer,
Further comprises isobornyl acrylate in an amount of 5 to 15 parts by weight based on 100 parts by weight of the polyisocyanate prepolymer,
Further comprising 5 to 15 parts by weight of dimethyl ammonium chloride based on 100 parts by weight of the polyisocyanate prepolymer,
Further comprising an adhesion promoter in an amount of 5 to 25 parts by weight based on 100 parts by weight of the polyisocyanate-free polymer,
Further comprising an antioxidant in an amount of 3 to 15 parts by weight based on 100 parts by weight of the polyisocyanate-free polymer,
Further comprising 5 to 30 parts by weight of an anti-peeling agent based on 100 parts by weight of the polyisocyanate-free polymer.
상기 시공표면에 폴리 이소시아네이트 프리 폴리머 100중량부, 에틸렌 초산 비닐 10 내지 60중량부, 음이온 유화제 5 내지 30중량부, 고무 화합물 5 내지 20중량부, 가성소다 1 내지 20중량부, 경화제 1 내지 30중량부, 옥틸페놀 에톡실레이트 0.1 내지 10중량부, 질산칼슘 5 내지 35중량부, 금속분말 10 내지 30중량부, 수용성 아크릴 수지 5 내지 30중량부, 증점제 1 내지 20중량부, 및 용제 50 내지 1,000중량부를 포함하는 열반사 및 차열 방수도료 조성물에, 바이오 수지를 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 20중량부로 더 포함하고, 소듐 벤조 에이트를 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 0.1 내지 1중량부로 더 포함하며, 알긴산 나트륨을 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 10중량부로 더 포함하고, 소디윰스테아레이트를 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 이소보닐아크릴레이트를 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 15중량부로 더 포함하고, 디메틸 암모늄 클로라이드를 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 15중량부로 더 포함하며, 부착증진제를 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 25중량부로 더 포함하고, 산화방지제를 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 3 내지 15중량부로 더 포함하며, 박리방지제를 폴리 이소시아네이트 프리 폴리머 100중량부 기준으로 5 내지 30중량부로 더 포함하는 열반사 및 차열 방수도료 조성물을 최소 건조 도막두께 0.1mm 이상이 될 때까지 도포하는 도포단계를 포함하는 열반사 및 차열 방수도료 조성물의 시공방법.A surface treatment step of treating the application surface for applying the heat reflection and heat shielding waterproofing paint composition; And
Wherein the polyisocyanate prepolymer is contained in an amount of 100 parts by weight, 10 to 60 parts by weight of ethylene vinyl acetate, 5 to 30 parts by weight of an anionic emulsifier, 5 to 20 parts by weight of a rubber compound, 1 to 20 parts by weight of caustic soda, 0.1 to 10 parts by weight of octylphenol ethoxylate, 5 to 35 parts by weight of calcium nitrate, 10 to 30 parts by weight of a metal powder, 5 to 30 parts by weight of a water-soluble acrylic resin, 1 to 20 parts by weight of a thickener, By weight based on 100 parts by weight of the polyisocyanate prepolymer and sodium benzoate in an amount of 0.1 to 1 part by weight based on 100 parts by weight of the polyisocyanate prepolymer, Further comprising sodium alginate in an amount of 5 to 10 parts by weight based on 100 parts by weight of the polyisocyanate prepolymer, Further comprising diisostearate in an amount of 1 to 5 parts by weight based on 100 parts by weight of the polyisocyanate prepolymer and further containing isobornyl acrylate in an amount of 5 to 15 parts by weight based on 100 parts by weight of the polyisocyanate prepolymer, 5 to 15 parts by weight based on 100 parts by weight of an isocyanate-free polymer, wherein the adhesion-promoting agent is further contained in an amount of 5 to 25 parts by weight based on 100 parts by weight of the polyisocyanate-free polymer, Further comprising 3 to 15 parts by weight of a heat-resistant and heat-resistant waterproof coating composition further comprising 5 to 30 parts by weight of an anti-peeling agent based on 100 parts by weight of the polyisocyanate-free polymer, until the minimum dry film thickness is 0.1 mm or more Thermal reflection including the application step Construction method of water heat shield coating composition.