KR101728716B1 - 우레탄 보드의 마감시트 및 그 제조방법, 상기 마감시트를 사용한 우레탄 보드 및 그 제조방법. - Google Patents
우레탄 보드의 마감시트 및 그 제조방법, 상기 마감시트를 사용한 우레탄 보드 및 그 제조방법. Download PDFInfo
- Publication number
- KR101728716B1 KR101728716B1 KR1020140151867A KR20140151867A KR101728716B1 KR 101728716 B1 KR101728716 B1 KR 101728716B1 KR 1020140151867 A KR1020140151867 A KR 1020140151867A KR 20140151867 A KR20140151867 A KR 20140151867A KR 101728716 B1 KR101728716 B1 KR 101728716B1
- Authority
- KR
- South Korea
- Prior art keywords
- nonwoven fabric
- urethane board
- sheet
- resin
- urethane
- Prior art date
Abstract
본 발명은 부직포 및 상기 부직포의 일면에 형성되는 에틸렌 비닐 아세테이트를 포함하는 공중합체로 이루어진 하나 이상의 고분자층을 포함하는 마감시트를 우레탄 보드에 적용하여 마감시트의 내충격성, 인장강도 및 결합력을 증대시키고, 우레탄 보드의 방음, 방습, 단열 성능을 향상시킬 수 있는 우레탄 보드의 마감시트 및 그 제조방법, 상기 마감시트를 사용한 우레탄 보드 및 그 제조방법을 제공한다.
Description
본 발명은 우레탄 보드의 마감시트 및 그 제조방법, 상기 마감시트를 사용한 우레탄 보드 및 그 제조방법에 관한 것이다.
일반적으로 아파트, 주택, 빌딩 등의 건축 구조물에는 내부의 소리가 외부로 발산되는 것과 함께, 외부의 소리가 내부로 유입되는 것을 방지하고, 또한 외부 습기의 침투를 막고, 외부로의 열 손실이나 열의 유입을 적게 하기 위해, 방음, 단열, 방습 등의 기능을 갖는 우레탄 보드(또는 패널)를 건축물의 천정, 벽면 또는 바닥면 등에 시공하고 있다.
이러한 우레탄 보드는 통상적으로 서로 소정의 간격을 두고 평행하게 설치되는 내판과 외판 사이의 공간에 우레탄액을 주입하고 발포한 후 상하부를 가압함으로써 제조된다.
이때, 우레탄 보드는 외부로부터의 물리적 및 화학적 충격, 특히 자외선에 대하여 그의 기계적 성질을 보호하기 위해, 그 양면에 크라프트지 혹은 아스팔트지 등의 마감시트를 합지하여 사용하고 있다.
그러나, 크라프트지나 아스팔트지는 종이류이기 때문에 습기에 약할 뿐만 아니라 내충격성과 인장강도 등의 기계적 특성이 매우 취약하여 시공 후 충격에 의한 균열이 발생하고 습기로 인하여 결로가 발생함으로써 우레탄 보드가 갖는 본래의 단열 성능 등을 저하시키는 문제가 있다.
이러한 문제를 해결하기 위해 대한민국 등록특허공보 10-1396870호에서는 제1 부직포와 제2 부직포 사이에 폴리에틸렌, 폴리프로필렌, 또는 폴리에스터 용융액을 도포하여 고화함으로써 시트의 강도를 보강한 마감시트를 개시하고 있다.
그러나 우레탄 보드에 사용되는 부직포는 그 재질이 폴레에틸렌 또는 폴리프로필렌으로 용융 고분자액과 상용성이 떨어져 구조적으로 결합하게 되므로 결합력이 충분하지 않은 문제가 있다.
이러한 문제를 해결하기 위해 에틸렌 비닐 아세테이트 수지와 같은 폴리에틸렌, 폴리프로필렌, PVC, 고무 등과 상용성이 높은 수지를 사용하면, 부직포뿐만 아니라, 우레탄 보드와도 화학적으로 결합할 수 있어, 결합력이 증대하여 내충격성, 인장강도, 및 결합력를 향상시킬 수 있고, 우레탄 보드의 성능을 향상시킬 수 있다.
다만, 에틸렌 비닐 아세테이트 수지는 녹는점이(Tm)이 80 ~ 90℃에 불과하여 고화 속도가 느린 문제가 있어, 그 자체로 우레탄 보드의 마감시트에 적용하기 어려운 문제가 있었다.
본 발명은 상기와 같은 문제점을 해결하기 위한 것으로, 내충격성, 인장강도, 및 결합력이 우수하여 우레탄 보드의 방음, 단열, 방습 성능을 향상시킬 수 있는 마감시트 및 그 제조방법을 제공하며, 상기 마감시트를 적용한 우레탄 보드 및 그 제조방법을 제공하는 것을 목적으로 한다.
상기 목적을 달성하기 위해, 본 발명의 우레탄 보드의 마감시트는 부직포 및 상기 부직포의 일면 또는 양면에 형성되는 에틸렌 비닐 아세테이트를 포함하는 공중합체로 이루어진 하나 이상의 고분자층을 포함하는 것을 특징으로 한다.
또한, 본 발명의 일 실시형태에서 우레탄 보드의 마감시트의 제조방법은 제1 부직포를 일정 간격으로 이격된 한 쌍의 롤러 사이로 공급하며, 상기 제1 부직포에 도포되는 에틸렌 비닐 아세테이트를 포함하는 공중합체로 이루어진 고분자 용융액을 상기 한 쌍의 롤러 사이에 공급하여, 상기 한 쌍의 롤러 사이를 통과하는 제1 부직포에 고분자 용융액을 압착하여 고화된 고분자층이 제1 부직포와 화학적으로 결합한 고분자층을 형성하도록 하는 것을 특징으로 한다.
또한, 본 발명의 또 다른 실시형태에서 우레탄 보드의 마감시트의 제조방법은 제1 부직포 및 제2 부직포를 일정 간격으로 이격된 한 쌍의 롤러 사이로 공급하며, 상기 제1 부직포의 일면 및 제2 부직포와 대향하는 타면에 에틸렌 비닐 아세테이트를 포함하는 공중합체로 이루어진 고분자 용융액을 공급하여, 상기 한 쌍의 롤러 사이를 통과하는 제1 부직포 및 제2 부직포 사이에 고분자 용융액을 압착하여 고화된 고분자층이 제1 부직포 및 제2 부직포와 화학적으로 결합한 고분자층을 형성하도록 하는 것을 특징으로 한다.
본 발명의 우레탄 보드의 마감시트에 사용되는 공중합체는 에틸렌 비닐 아세테이트 수지 및 저밀도 폴리에틸렌 수지의 공중합체, 에틸렌 비닐 아세테이트 수지 및 변성 폴리에틸렌 수지의 공중합체, 에틸렌 비닐 아세테이트 수지 및 변성 폴리프로필렌 수지의 공중합체, 에틸렌 비닐 아세테이트 수지, 폴리프로필렌 수지 및 변성 폴리프로필렌 수지의 공중합체 중 어느 하나인 것으로, 상기 변성 폴리에틸렌 수지는 무수말레인산이 그라프트된 폴리에틸렌 수지(PE-g-MAH)이며, 상기 변성 폴리프로필렌 수지는 무수말레인산이 그라프트된 폴리프로필렌 수지(PP-g-MAH)인 것을 특징으로 한다.
또한, 상기 고분자층의 전부 또는 일부가 상기 부직포와 화학적으로 결합할 수 있으며, 상기 부직포 및/또는 고분자층은 난연제를 추가적으로 함유할 수 있다.
본 발명의 우레탄 보드는 상기 마감시트를 우레탄 보드의 양면에 접착하여 형성된다. 이때, 상기 마감시트의 표면과 상기 우레탄 보드의 표면의 전부 또는 일부가 화학적으로 결합된다.
본 발명의 일 실시형태에서 우레탄 보드의 제조방법은 제1 부직포를 일정 간격으로 이격된 한 쌍의 롤러 사이로 공급하며, 상기 제1 부직포에 도포되는 에틸렌 비닐 아세테이트를 포함하는 공중합체로 이루어진 고분자 용융액을 상기 한 쌍의 롤러 사이에 공급하여, 상기 한 쌍의 롤러 사이를 통과하는 제1 부직포에 고분자 용융액을 압착하여 고화된 고분자층이 제1 부직포와 화학적으로 결합한 고분자층을 형성한 마감시트를 우레탄 보드의 양면에 각각 부착하고 압착하여, 상기 마감시트의 표면과 상기 우레탄 보드의 표면의 전부 또는 일부가 화학적으로 결합하는 것을 특징으로 한다.
또한, 본 발명의 또 다른 실시형태에서 우레탄 보드의 제조방법은 제1 부직포 및 제2 부직포를 일정 간격으로 이격된 한 쌍의 롤러 사이로 공급하며, 상기 제1 부직포의 일면 및 제2 부직포와 대향하는 타면에 에틸렌 비닐 아세테이트를 포함하는 공중합체로 이루어진 고분자 용융액을 공급하여, 상기 한 쌍의 롤러 사이를 통과하는 제1 부직포 및 제2 부직포 사이에 고분자 용융액을 압착하여 고화된 고분자층이 제1 부직포 및 제2 부직포와 화학적으로 결합한 고분자층을 형성한 마감시트를 우레탄 보드의 양면에 각각 부착하고 압착하여, 상기 마감시트의 표면과 상기 우레탄 보드의 표면의 전부 또는 일부가 화학적으로 결합하는 것을 특징으로 한다.
본 발명에 의하면, 부직포 및 상기 부직포의 일면 또는 양면에 형성되는 에틸렌 비닐 아세테이트를 포함하는 공중합체로 이루어진 하나 이상의 고분자층을 포함하는 마감시트를 사용함으로써 마감시트의 내충격성, 인장강도 및 결합력을 증대시켜 우레탄 보드의 방음, 방습, 단열 성능을 향상시킬 수 있다.
도 1은 본 발명의 일실시예 따른 우레탄 보드의 마감시트의 층 구조를 나타낸 단면도.
도 2는 본 발명의 일실시예에 따른 우레탄 보드의 마감시트의 층 구조를 나타낸 단면도.
도 3은 본 발명에 일실시예에 따른 우레탄 보드의 마감시트를 적용한 우레탄 보드의 층 구조를 나타낸 단면도.
도 4는 본 발명에 일실시예에 따른 우레탄 보드의 마감시트를 적용한 우레탄 보드의 층 구조를 나타낸 단면도.
도 2는 본 발명의 일실시예에 따른 우레탄 보드의 마감시트의 층 구조를 나타낸 단면도.
도 3은 본 발명에 일실시예에 따른 우레탄 보드의 마감시트를 적용한 우레탄 보드의 층 구조를 나타낸 단면도.
도 4는 본 발명에 일실시예에 따른 우레탄 보드의 마감시트를 적용한 우레탄 보드의 층 구조를 나타낸 단면도.
이하, 첨부한 도면을 참조하여 본 발명에 대하여 상세히 설명한다.
도 1은 본 발명에 일실시예에 따른 우레탄 보드의 마감시트의 층 구조를 나타낸 단면도이며, 도 2는 본 발명의 또다른 실시예에 따른 우레탄 보드의 마감시트의 층 구조를 나타낸 단면도이다.
도 1에 도시한 바와 같이, 본 발명에 일실시예에 따른 우레탄 보드의 마감시트는 우레탄 보드의 양면에 접착되며, 제1 부직포(100), 고분자층(200)으로 이루어져 있다.
또한, 본 발명의 또다른 실시예에 따른 우레탄 보드의 마감시트는 도 2에 도시한 바와 같이 제1 부직포(100)의 양면에 고분자층(200)이 형성되고, 일면의 고분자층(200)에는 제2 부직포(300)가 적층되어 있다.
본 발명의 마감시트에 사용되는 고분자는 에틸렌 비닐 아세테이트 수지를 포함하는 공중합체이며, 특히, 에틸렌 비닐 아세테이트 수지 및 저밀도 폴리에틸렌 수지의 공중합체, 에틸렌 비닐 아세테이트 수지 및 변성 폴리에틸렌 수지의 공중합체, 에틸렌 비닐 아세테이트 수지 및 변성 폴리프로필렌 수지의 공중합체, 에틸렌 비닐 아세테이트 수지, 폴리프로필렌 수지 및 변성 폴리프로필렌 수지의 공중합체 중 어느 하나를 사용하는 것이 바람직하다.
상기 공중합체를 사용하면, 에틸렌 비닐 아세테이트의 말단 부분의 가수분해에 의해 생겨난 하이드록시기가 부직포를 형성하는 폴리프로필렌, 폴리에스터 및 우레탄 보드를 형성하는 우레탄과 화학적으로 결합하여 종래에 사용되던 폴리에틸렌, 폴리프로필렌, 폴리에스터 등의 고분자보다 결합력이 크게 향상됨으로써 부직포 및 우레탄 보드와의 상용성을 높일 수 있고, 또한, 공중합체 형태로 사용함으로써 에틸렌 비닐 아세테이트 단독으로 사용하는 경우보다 녹는점을 높여 우레탄 보드의 발포온도(100~140)에서 고분자층이 녹거나 인접한 시트와 접착되는 현상을 방지할 수 있고, 접착력이 향상됨으로써 마감시트의 강도를 향상시킬 수 있다.
또한, 제1 부직포(100)와 제2 부직포(300)는 동일한 층구조이며, 내화학성, 내후성, 인장강도가 뛰어나고 인체에 무해할 뿐만 아니라 열융착성이 뛰어난 폴리프로필렌 또는 폴리에스터 재질을 사용할 수 있다.
또한, 본 발명의 마감시트는 고분자 10 ~ 40 중량%, 부직포 30 ~ 45 중량%로 이루어진다.
상기 부직포에 적층되는 공중합체의 고분자층은 투습성 및 접착성을 얻기 위해 10 g/㎡ 이하의 평량을 가져야 한다. 예를 들어, 에틸렌 비닐 아세테이트 수지 및 변성 폴리에틸렌 수지의 공중합체의 경우 바람직하게는 5 g/㎡ 이하, 더욱 바람직하게는 3 g/㎡, 특히 바람직하게는 1 ~ 3 g/㎡의 평량으로 형성함으로써 원하는 투습성 및 접착성을 얻을 수 있다.
이와 같이, 본 발명에 의한 시트는 2 또는 4개의 층으로 구성된 시트를 크라프트지나 아스팔트지 등의 종이류로 이루어진 시트 대신에 사용함으로써 시트의 강도를 대폭 보강할 수 있으므로, 충격에 의한 균열 발생과 습기로 인한 결로 발생 등을 방지할 수 있고, 이에 따라 우수한 방음, 방습, 단열 효과를 유지할 수 있다.
즉, 본 발명의 마감시트는 우레탄 보드 표면에 적층되는 제1 부직포와 제1 부직포 상면에 도포되어 고화된 고분자 용융액으로 이루어질 수 있다.
본 발명에서는, 본 발명의 우레탄 보드의 마감시트는 별도의 접착제 없이 우레탄 보드 표면에 접착되도록 압착 방식으로 접착할 수 있다.
또한, 본 발명의 우레탄 보드는 우레탄을 발포시킬 때 난연제를 첨가하여 난연등급에 적합한 건축용 내장재료를 얻을 수 있고, 수용성의 난연제를 우레탄 보드의 표면에 스프레이 방식으로 분사하여 난연 처리를 할 수 있다.
이와 함께, 본 발명의 마감시트는 인계 난연제, 멜라민계 난연제, 금속수산화물계 난연제, 안티몬계 난연제 중 어느 하나 이상의 난연제를 포함함으로써 난연 처리를 할 수 있다. 이 경우, 상기 난연제는 부직포 및/또는 고분자층에 함유될 수 있으며, 스프레이 방식으로 분사하거나 고분자 용융액에 혼합하여 사용할 수 있으며, 마감시트를 난연제 용액에 함침하여 건조함으로써 제조할 수도 있다.
상기 난연제에 있어서, 인계 난연제로는 적인, 암모늄 포스페이트, 암모늄 폴리포스페이트, 할로알킬 포스페이트 등이 있으며, 멜라민계 난연제로는 멜라민 시아누레이트, 멜라민 폴리포스페이트 등이 있고, 금속수산화물계 난연제로는 수산화알루미늄, 수산화마그네슘 등이 있으며, 안티몬계 난연제로는 삼산화안티몬, 오산화안티몬 등을 들 수 있다.
상기 난연제 이외에도 본 발명의 마감시트는, 필요에 따라, 고분자 용융액에 충진제, 블로킹 방지제, 활제, 안정제 등의 첨가제를 부가할 수도 있다. 상기 충진제로는 탄산칼슘, 탈크, 이산화티타늄 등을 들 수 있으며, 블로킹 방지제로는 실리카, 메틸렌 비스스테아라미드, 에틸렌 비스스테아라미드 등을 들 수 있고, 활제로는 칼슘 스테아레이트, 징크 스테아레이트, 스테아릭산 등을 들 수 있다.
본 발명의 우레탄 보드의 마감시트는 제1 부직포를 일정 간격으로 이격된 한 쌍의 롤러 사이로 공급하며, 상기 제1 부직포에 도포되는 에틸렌 비닐 아세테이트를 포함하는 공중합체로 이루어진 고분자 용융액을 상기 한 쌍의 롤러 사이에 공급하여, 상기 한 쌍의 롤러 사이를 통과하는 제1 부직포에 고분자 용융액을 압착하여 고화된 고분자층이 제1 부직포와 화학적으로 결합한 고분자층을 형성하도록 함으로써 제조된다.
또한, 부직포가 적층된 구조에 대해서는, 제1 부직포 및 제2 부직포를 일정 간격으로 이격된 한 쌍의 롤러 사이로 공급하며, 상기 제1 부직포의 일면 및 제2 부직포와 대향하는 타면에 에틸렌 비닐 아세테이트를 포함하는 공중합체로 이루어진 고분자 용융액을 공급하여, 상기 한 쌍의 롤러 사이를 통과하는 제1 부직포 및 제2 부직포 사이에 고분자 용융액을 압착하여 고화된 고분자층이 제1 부직포 및 제2 부직포와 화학적으로 결합한 고분자층을 형성하도록 함으로써 제조된다.
상기 제조공정에 대해 구체적으로 도시하지 않았으나, 일반적인 T 다이 압출 성형에 의해 제조될 수 있다.
예를 들어, 일정 두께의 부직포 및 고분자층, 제1, 제2 부직포 및 고분자층을 형성하기 위한 성형 재료가 순차적으로 적층되도록, 2개의 권취롤러에 권취된 1 또는 2매의 부직포를 한 쌍의 압착롤러 사이에 공급하고, 권취롤러의 상부에서 고분자 용융액을 공급하여 적층시키고, 압착롤러 사이를 통과하여 나오는 시트를 권취하여 마감시트를 제조할 수 있다.
도 3은 본 발명의 일실시예에 따른 우레탄 보드의 마감시트를 적용한 우레탄 보드의 일면의 층 구조를 나타낸 단면도이며, 도 4는 본 발명에 다른 실시예에 따른 우레탄 보드의 마감시트를 적용한 우레탄 보드의 일면의 층 구조를 나타낸 단면도이다.
즉, 본 발명의 우레탄 보드는 마감시트를 우레탄 보드의 양면에 접착하여 형성되는 것으로, 마감시트의 표면과 우레탄 보드의 표면의 전부 또는 일부가 화학적으로 결합하는 것을 특징으로 한다.
상기 우레탄 보드는 제1 부직포를 일정 간격으로 이격된 한 쌍의 롤러 사이로 공급하며, 상기 제1 부직포에 도포되는 에틸렌 비닐 아세테이트를 포함하는 공중합체로 이루어진 고분자 용융액을 상기 한 쌍의 롤러 사이에 공급하여, 상기 한 쌍의 롤러 사이를 통과하는 제1 부직포에 고분자 용융액을 압착하여 고화된 고분자층이 제1 부직포와 화학적으로 결합한 고분자층을 형성한 마감시트를 우레탄 보드의 양면에 각각 부착하고 압착하여, 상기 마감시트의 표면과 상기 우레탄 보드의 표면의 전부 또는 일부가 화학적으로 결합함으로써 제조된다.
또한, 부직포가 적층된 구조에 대해서는, 제1 부직포 및 제2 부직포를 일정 간격으로 이격된 한 쌍의 롤러 사이로 공급하며, 상기 제1 부직포의 일면 및 제2 부직포와 대향하는 타면에 에틸렌 비닐 아세테이트를 포함하는 공중합체로 이루어진 고분자 용융액을 공급하여, 상기 한 쌍의 롤러 사이를 통과하는 제1 부직포 및 제2 부직포 사이에 고분자 용융액을 압착하여 고화된 고분자층이 제1 부직포 및 제2 부직포와 화학적으로 결합한 고분자층을 형성한 마감시트를 우레탄 보드의 양면에 각각 부착하고 압착하여, 상기 마감시트의 표면과 상기 우레탄 보드의 표면의 전부 또는 일부가 화학적으로 결합함으로써 제조된다.
본 발명의 마감시트는 우레탄 보드에 적용하기 위한 것으로, 에틸렌 비닐 아세테이트 수지를 포함하는 공중합체를 사용함으로써 부직포 및 우레탄 보드와의 상용성은 좋으나 녹는점(Tm)이 낮은 에틸렌 비닐 아세테이트 수지의 문제점을 해소하였다.
이에 따라, 본 발명의 마감시트는 시트의 인장강도의 비(MD/TD)가 1.0 내지 1.1의 범위, 신장도의 비가 15 내지 25의 범위, 인열강도의 비가 0.9 내지 3.0의 범위를 만족함으로써 우수한 강도 및 접착력을 얻을 수 있다. 또한, 상기 범위를 벗어나는 경우, 마감시트를 적용한 우레탄 보드에서 마감시트의 박리, 훼손의 정도가 심하여 우레탄 보드를 충분히 보강하는 마감시트를 얻을 수 없다.
상기 인장강도, 신장도, 인열강도는 10㎜×10㎜의 우레탄 보드 시편을 기준으로 180 peeling test기로 500mm/min의 속도로 양쪽으로 잡아당겨 측정한 값으로, 각각의 인장강도는 180 peeling test기로 속도 500mm/min의 속도로 양쪽으로 당겨서 마감시트가 파괴될 때의 힘을 단위면적으로 나눈 값이며, 인열강도는 180° peeling test기로 500㎜/min의 속도로 양쪽으로 잡아당겨서 마감시트가 파괴될 때의 힘을 시트 두께로 나눈 값이며, 신장율은 180° peeling test기로 500㎜/min의 속도로 양쪽으로 잡아당겨서 마감시트가 파괴될 때까지의 연신율로부터 구한 값이다.
또한, 상기 시험 후 우레탄 보드의 외관을 관찰하여 마감시트의 훼손 정도가 심하지 않는 경우를 양호, 마감시트가 심하게 훼손되는 경우를 불량으로 하였다.
또한, 본 발명의 마감시트는 원하는 사용 용도에 따라 재료의 크기, 양을 적절히 설정하여 재료의 투입을 조절함으로써 최종 시트의 폭과 길이를 제어할 수 있고, 가열 및 가압의 정도를 조절하여 두께(t)를 제어할 수 있다. 시트의 운반, 보관 등을 위해, 그 두께(t)는 0.1 ~ 1.0㎜인 것이 바람직하고, 상기 길이 및 폭은 각각 500 ~ 4,500m, 1 ~ 1.5m인 것이 바람직하다.
이 경우, 인장강도의 비(MD/TD)가 1.0 내지 1.1의 범위, 신장도의 비가 15 내지 25의 범위, 인열강도의 비가 0.9 내지 3.0의 범위를 벗어나면 마감시트가 충격에 의해 손상되기 쉽고, 우레탄 보드 적재시 서로 붙어 떨어지지 않는 등 그 품질이 불량하게 되므로, 상기 특성값의 범위에 맞도록 공정조건을 조절할 필요가 있다. 특히, 상기 특성값은 재료의 종류에 의해 영향을 받으므로, 적합한 재료를 사용하는 것이 중요하다.
이하, 본 발명의 바람직한 실시예의 설명을 통해 본 발명을 보다 상세하게 설명한다. 그러나 하기 실시예는 본 발명의 이해를 돕기 위한 일 예에 불과한 것으로 이에 의해 본 발명의 권리범위가 축소되거나 한정되어서는 안 된다.
두께 0.13㎜의 폴리프로필렌 부직포를 각각 좌우로 배치된 한 쌍의 롤러(회전롤러 및 냉각롤러) 사이로 보내면서 에틸렌 비닐 아세테이트 수지 및 저밀도 폴리에틸렌 수지의 공중합체의 용융액을 부직포의 일면에 0.015 ~ 0.3㎜의 두께가 되도록 도포하였다.
또한, 냉각롤러의 온도는 10℃ 미만을 유지하였고, 부직포가 롤러를 통과하는 속도는 100m/분으로 유지하여, 최종적으로 두께(t) 0.12㎜, 길이 1,000m, 폭 1.1m의 시트를 얻었다.
상기 마감시트 2매를 별도의 접착제 없이 우레탄 보드의 양면에 부착하고 압착하여 마감시트가 접합된 우레탄 보드를 제조했다.
에틸렌 비닐 아세테이트 수지 및 변성 폴리에틸렌 수지의 공중합체의 용융액을 사용한 것을 제외하고는 상기 실시예 1과 동일하게 제조하였다.
에틸렌 비닐 아세테이트 수지 및 변성 폴리프로필렌 수지의 공중합체의 용융액을 사용한 것을 제외하고는 상기 실시예 1과 동일하게 제조하였다.
(비교예 1)
폴리에틸렌 수지의 용융액을 사용한 것을 제외하고는 상기 실시예 1과 동일하게 제조하였다.
(비교예 2)
에틸렌 비닐 아세테이트 수지의 용융액을 사용한 것을 제외하고는 상기 실시예 1과 동일하게 제조하였다.
얻어진 시트의 인장강도(kg/㎟), 인열강도(kg/㎜), 신장율(%)을 측정하여 하기 표 1에 나타내었다.
| 실시예 1 | 실시예 2 | 실시예 3 | 비교예 1 | 비교예 2 | ||
| 인장강도 | MD | 3.05 | 3.08 | 3.08 | 3.32 | 3.08 |
| TD | 3.02 | 3.05 | 3.06 | 2.55 | 2.25 | |
| MD/TD | 1.1 | 1.1 | 1.0 | 1.3 | 1.37 | |
| 인열강도 | MD | 19.5 | 9.6 | 8.7 | 15.6 | 18.5 |
| TD | 6.6 | 9.8 | 9.2 | 4.9 | 21.7 | |
| MD/TD | 2.95 | 0.98 | 0.94 | 3.18 | 0.85 | |
| 신장율 | MD | 502 | 510 | 512 | 510 | 504 |
| TD | 33 | 20.5 | 24 | 20 | 37 | |
| MD/TD | 15.2 | 24.9 | 21.3 | 25.5 | 13.6 | |
| 접착성 | 양호 | 양호 | 양호 | 불량 | 불량 |
본 실시예에 있어서 사용 시의 요구에 따라 롤러에 제공되는 부직포, 용융액의 두께는 변형할 수 있으며, 또한 최종 시트의 두께(t), 길이, 폭도 변형 할 수 있다.
이와 같이 얻어진 마감시트는 우레탄 보드의 양면에 접착되어 충격 및 인장강도를 높여 균열 및 습기 침투를 방지하여 단열성능의 저하를 차단할 수 있다.
이상, 바람직한 실시예를 통하여 본 발명에 관하여 상세히 설명하였으나, 본 발명은 이에 한정되는 것은 아니며, 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 다양하게 변경, 응용될 수 있음은 당업자에게 자명하다. 따라서, 본 발명의 진정한 보호 범위는 다음의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술적 사상은 본 발명의 권리 범위에 포함되는 것으로 해석되어야 할 것이다.
100 : 제1 부직포
200 : 제2 부직포
300 : 고분자층
400 : 우레탄 보드
200 : 제2 부직포
300 : 고분자층
400 : 우레탄 보드
Claims (14)
- 우레탄 보드의 양면에 접착되는 우레탄 보드의 마감시트로서,
부직포 및 상기 부직포의 일면 또는 양면에 형성되는 에틸렌 비닐 아세테이트 수지 및 저밀도 폴리에틸렌 수지의 공중합체, 에틸렌 비닐 아세테이트 수지 및 변성 폴리에틸렌 수지의 공중합체, 에틸렌 비닐 아세테이트 수지 및 변성 폴리프로필렌 수지의 공중합체, 에틸렌 비닐 아세테이트 수지, 폴리프로필렌 수지 및 변성 폴리프로필렌 수지의 공중합체 중 어느 하나의 공중합체로 이루어진 하나 이상의 고분자층을 포함하는 것을 특징으로 하는 우레탄 보드의 마감시트. - 삭제
- 청구항 1에 있어서,
상기 변성 폴리에틸렌 수지는 무수말레인산이 그라프트된 폴리에틸렌 수지(PE-g-MAH)이며, 상기 변성 폴리프로필렌 수지는 무수말레인산이 그라프트된 폴리프로필렌 수지(PP-g-MAH)인 것을 특징으로 하는 우레탄 보드의 마감시트. - 청구항 1에 있어서,
상기 고분자층의 전부 또는 일부가 상기 부직포와 화학적으로 결합하는 것을 특징으로 하는 우레탄 보드의 마감시트. - 청구항 1에 있어서,
상기 부직포, 고분자층 또는 부직포와 고분자층은 난연제를 추가적으로 함유하는 것을 특징으로 하는 우레탄 보드의 마감시트. - 청구항 5에 있어서,
상기 난연제는 인계 난연제, 멜라민계 난연제, 금속수산화물계 난연제, 안티몬계 난연제 중 어느 하나 이상인 것을 특징으로 하는 우레탄 보드의 마감시트. - 삭제
- 삭제
- 삭제
- 삭제
- 청구항 1에 기재된 우레탄 보드의 마감시트를 우레탄 보드의 양면에 접착하여 형성되는 우레탄 보드.
- 청구항 11에 있어서,
상기 마감시트의 표면과 상기 우레탄 보드의 표면의 전부 또는 일부가 화학적으로 결합하는 것을 특징으로 하는 우레탄 보드. - 삭제
- 삭제