KR101675005B1 - High frequency heating equipment and method using the same - Google Patents

High frequency heating equipment and method using the same Download PDF

Info

Publication number
KR101675005B1
KR101675005B1 KR1020150023522A KR20150023522A KR101675005B1 KR 101675005 B1 KR101675005 B1 KR 101675005B1 KR 1020150023522 A KR1020150023522 A KR 1020150023522A KR 20150023522 A KR20150023522 A KR 20150023522A KR 101675005 B1 KR101675005 B1 KR 101675005B1
Authority
KR
South Korea
Prior art keywords
induction heating
frequency induction
high frequency
base material
heating apparatus
Prior art date
Application number
KR1020150023522A
Other languages
Korean (ko)
Other versions
KR20160100704A (en
Inventor
권한상
Original Assignee
부경대학교 산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 부경대학교 산학협력단 filed Critical 부경대학교 산학협력단
Priority to KR1020150023522A priority Critical patent/KR101675005B1/en
Publication of KR20160100704A publication Critical patent/KR20160100704A/en
Application granted granted Critical
Publication of KR101675005B1 publication Critical patent/KR101675005B1/en

Abstract

본 발명은 고주파 유도가열 장치 및 이를 이용한 방법에 관한 것으로서, 서로 이웃하는 모재의 양단부를 연결하는 고주파 유도 가열 장치에 관한 것으로서, 고주파 유도 가열부 및 제어부를 포함한다. 고주파 유도 가열부는 서로 이웃하는 모재 사이에 용가재가 마련되고, 용가재와 서로 이웃하는 모재의 양단부에 열을 가하여 양단부를 접합시킨다. 제어부는 모재와 용가재의 재질에 따라 고주파 유도 가열부에 인가되는 유도전류의 크기와 주파수를 제어한다.
본 발명에 의하면, 고주파 유도 가열부를 열원으로 하여 서로 맞닿는 모재의 양단부에 국부적인 열을 인가하여 서로 맞닿는 모재의 손상없이 정교하게 용접할 수 있으며 불량률을 감소시키고 용가재의 사용량을 감소시켜 차량의 머플러 등에 사용될 때 중량을 감소시켜 차량의 연비를 증가시킬 수 있다.
또한, 고주파 유도가열 장치를 이용한 가공방법은 용접 결합되는 각 모재들을 준비하고, 가열 장치에 동시에 유도 브레이징을 실시하여 공정시간을 단축하여 공정시간을 단축할 수 있다.The present invention relates to a high-frequency induction heating apparatus and a method using the same, and more particularly, to a high-frequency induction heating apparatus connecting both ends of a neighboring parent material, including a high-frequency induction heating unit and a control unit. The high frequency induction heating unit is provided with a filler between neighboring base materials, and heat is applied to both ends of the base material adjacent to the filler material to bond both ends. The control unit controls the magnitude and frequency of the induced current applied to the high frequency induction heating unit according to the material of the base material and the consumable material.
According to the present invention, local heat is applied to both end portions of the base material contacting each other by using the high frequency induction heating portion as a heat source, so that the welding can be precisely performed without damaging the base material abutting each other, and the defective rate is reduced, When used, the weight can be reduced to increase the fuel economy of the vehicle.
In addition, the processing method using the high frequency induction heating apparatus can shorten the processing time by preparing each of the base materials to be welded and simultaneously conducting induction brazing to the heating apparatus, thereby shortening the processing time.

Description

고주파 유도가열 장치 및 이를 이용한 방법{High frequency heating equipment and method using the same}TECHNICAL FIELD The present invention relates to a high frequency induction heating apparatus and a method using the same,

본 발명은 고주파 유도가열 장치 및 이를 이용한 방법에 관한 것으로서, 유도가열을 이용하여 금속 배기계 모재를 견고하게 연결할 수 있는 고주파 유도가열 장치 및 이를 이용한 방법에 관한 것이다.The present invention relates to a high frequency induction heating apparatus and a method of using the same, and more particularly, to a high frequency induction heating apparatus and a method using the induction heating apparatus capable of firmly connecting a metal exhaust system base material by induction heating.

일반적으로 금속이나 비금속의 접합부위를 가열하여 용융상태 또는 반용융상태에서 접합시키는 것을 용접이라고 하며, 용접방법으로는 융접(Fusion Welding), 압접(Pressure Welding) 및 납접의 방법이 사용되고 있다.In general, welding is performed by welding a metal or non-metal joint at a molten or semi-molten state. Welding methods include fusion welding, pressure welding, and brazing.

용접은 모재의 접합부위를 용융상태로 가열하여 접합하거나 용융체를 주입하여 융착시키는 방법이고, 압접은 접합부위를 반용융상태로 가열하거나 냉간상태에서 기계적인 압력을 가하여 접합시키는 방법이며, 납접은 접합재인 금속보다 낮은 온도에서 녹는 용가재를 접합부위에 유입시켜 용가재의 표면장력에 의해 생기는 흡입력을 이용하여 접합시키는 방법이다.Welding is a method in which a joint portion of a base material is heated in a molten state to be bonded or a melt is injected and fused. Pressure welding is a method of bonding a joint portion by heating in a semi-molten state or applying a mechanical pressure in a cold state, And the joining is carried out by using the suction force generated by the surface tension of the filler material.

이중 모재의 접합부위를 용융상태로 가열하여 접합하거나 용융체를 주입하여 융착시키는 용접방법 중에서 가장널리 사용되는 방법이 아크용접이다.Arc welding is the most widely used welding method in which the joints of the double base materials are heated in the molten state to bond them or to melt the molten material.

아크용접은 모재와 토치의 사이에 전류를 인가하여 아크를 발생시키고 이때 발생하는 열을 이용하여 접합부위를 용융시켜 접합하는 것으로, 자동차, 조선, 건설산업에 널리 사용되고 있으나, 작업속도가 느리며 용접봉의 손실율이 높으며 용접덧살에 의한 접합부의 무게가 늘어날 수 있다. 이로 인해, 최근에 자동차 배기계 모재에는 환경문제 대응을 위한 정화성능 향상과 함께 연비개선에 유효한 경량화가 꾸준히 요구됨에 따라 머플러 구성 소재 두께가 1.5mm 이하의 박판 소재에는 적용하기 어려운 측면이 있다.Arc welding is widely used in the automobile, shipbuilding, and construction industries by welding an arc between a base material and a torch to generate an arc and melting the joint by using the heat generated at that time. The loss rate is high and the weight of the joint due to the welding process can be increased. As a result, the automobile exhaust system base material has recently been required to be lightweight, which is effective in improving the purification performance to cope with environmental problems and improving the fuel efficiency. Therefore, it is difficult to apply to a thin plate material having a muffler component thickness of 1.5 mm or less.

특히 스테인리스강의 경우 일반강 대비 높은 열팽창 계수와 낮은 열전도도의 소재특성으로 용접 후 과도한 열변형이 발생하여 공정별 최종 제품 치수에서 오차가 발생할 수 있으며, 특히 소재두께 1.5mm 이하의 박판 소재 용접 시 접합 불량이 심하여 경량화에 어려움이 많은 실정이다.Especially, in case of stainless steel, due to high thermal expansion coefficient and low thermal conductivity material characteristic compared to general steel, excessive thermal deformation after welding may cause errors in the final product dimensions per process. Especially, There are many defects and difficulty in weight reduction.

한국 공개특허 제2000-0063779호에는 로브레이징에 의한 스테인레스 스틸 용접 및 열처리 가공방법이 개시한 바 있다. 한국 공개특허 제2000-0063779호에 개시되어 있는 브레이징에 의한 스테인레스 스틸 용접은 컨베이어벨트와 같이 공정이 연속적으로 이루어져 공정시간이 길어질 수 있는 문제점이 있다.Korean Unexamined Patent Publication No. 2000-0063779 discloses a stainless steel welding and heat treatment method by roving. Korean Unexamined Patent Application Publication No. 2000-0063779 has a problem in that stainless steel welding by brazing may be performed continuously as a conveyor belt, which may prolong the process time.

본 발명의 목적은 고주파 유도 가열부를 열원으로 하여 서로 맞닿는 모재의 양단부에 국부적인 열을 인가하여 서로 맞닿는 모재를 손상없이 정교하게 접합하여 불량률을 감소시키며, 용접량의 중량을 감소시킬 수 있는 고주파 유도가열 장치를 제공함에 있다.An object of the present invention is to provide a high frequency induction heating device capable of reducing defective rate by applying local heat to both ends of a base material contacting each other with a high frequency induction heating part as a heat source, And a heating device.

본 발명의 다른 목적은 용접 결합되는 각 모재들을 준비하고, 고주파 유도가열 장치를 이용하여 준비된 모재들을 동시에 유도 가열을 실시하여 생산공정을 단축하여 공정시간을 줄일 수 있는 고주파 유도가열 장치를 이용한 가공방법을 제공함에 있다.Another object of the present invention is to provide a method of manufacturing a high-frequency induction heating apparatus capable of reducing the processing time by preparing each of the base materials to be welded together and simultaneously inducing heating of the base materials prepared by using the high- .

위와 같은 목적을 달성하기 위하여, 본 발명의 실시예에 따른 고주파 유도 가열 장치는 서로 이웃하는 모재의 양단부를 연결하는 고주파 유도 가열 장치에 관한 것으로서, 고주파 유도 가열부 및 제어부를 포함한다. 고주파 유도 가열부는 서로 이웃하는 모재 사이에 용가재가 마련되고, 용가재와 서로 이웃하는 모재의 양단부에 열을 가하여 양단부를 접합시킨다. 제어부는 모재와 용가재의 재질에 따라 고주파 유도 가열부에 인가되는 유도전류의 크기와 주파수를 제어한다.In order to achieve the above object, a high frequency induction heating apparatus according to an embodiment of the present invention is a high frequency induction heating apparatus for connecting both ends of neighboring parent materials, and includes a high frequency induction heating unit and a control unit. The high frequency induction heating unit is provided with a filler between neighboring base materials, and heat is applied to both ends of the base material adjacent to the filler material to bond both ends. The control unit controls the magnitude and frequency of the induced current applied to the high frequency induction heating unit according to the material of the base material and the consumable material.

본 발명의 실시예에 따른 고주파 유도 가열 장치의 고주파 유도 가열부는 모재의 외경보다 직경이 크게 형성되고, 나선형상으로 형성되어 모재를 감싸도록 형성될 수 있다.The high frequency induction heating unit of the high frequency induction heating apparatus according to the embodiment of the present invention may be formed to have a larger diameter than the outer diameter of the base material and be formed in a spiral shape to enclose the base material.

본 발명의 실시예에 따른 고주파 유도 가열 장치의 고주파 유도 가열부의 용가재의 재질은 니켈 계열로 형성될 수 있다.The material of the high-frequency induction heating unit of the high-frequency induction heating apparatus according to the embodiment of the present invention may be formed of a nickel-based material.

본 발명의 실시예에 따른 고주파 유도 가열 장치를 이용한 접합 방법은 모재 배열단계, 용가재 배치단계, 유도 가열부 배치단계 및 모재 접합단계를 포함한다. 모재 배열단계는 복수로 마련된 모재의 양단부를 서로 이웃하게 배열한다. 용가재 배치단계는 이웃하게 배열된 모재 사이에 용가재를 배치한다. 유도 가열부 배치단계는 용가재가 배치된 위치에 고주파 유도 가열부를 배치한다. 모재 접합단계는 고주파 유도 가열부에 전류를 인가하여 용가재와 서로 이웃하게 배치된 모재의 양단부를 접합한다. 그리고, 모재 배열 단계에서 외측 모재의 단부에 확관부를 형성하고 내측 모재의 단부를 상기 확관부를 통해 외측 모재의 단부 내로 끼워 배열하고, 용가재 배치단계에서 용가재를 확관부의 내면에 밀착하는 한편 외측 모재의 단부와 내측 모재 단부 사이로 끼워지게 배치한다. The bonding method using the high frequency induction heating apparatus according to the embodiment of the present invention includes a base material arranging step, a consumable material arranging step, an induction heating part disposing step, and a base material bonding step. The base material arranging step arranges the both end portions of the base material arranged in plural adjacent to each other. The disposing material step arranges the filler material between the neighboring arranged base materials. The step of arranging the induction heating part arranges the high frequency induction heating part at the position where the consumable material is disposed. In the base material bonding step, a current is applied to the high frequency induction heating unit to bond both ends of the base material disposed adjacent to the meltable material. In the step of arranging the base material, an expanded portion is formed at the end of the outer base material, and an end portion of the inner base material is fitted into the end portion of the outer base material through the expanded portion. And is disposed between the end portion of the base material and the end portion of the inner base material.

본 발명의 실시예에 따른 고주파 유도 가열 장치를 이용한 접합 방법의 접합단계는 용가재 및 서로 이웃게 배치된 모재의 재질에 따라 고주파 전류를 설정하여 접합할 수 있다. The joining step of the joining method using the high-frequency induction heating apparatus according to the embodiment of the present invention can be performed by setting a high-frequency current according to the material of the matrix and the neighboring matrix.

본 발명에 의한 고주파 유도가열 장치는 고주파 유도 가열부를 열원으로 하여 서로 맞닿는 모재의 양단부에 국부적인 열을 인가하여 서로 맞닿는 모재의 손상없이 정교하게 접합할 수 있으며 불량률을 감소시키고 용가재의 사용량을 감소시켜 차량의 머플러 등에 사용될 때 중량을 감소시켜 차량의 연비를 증가시킬 수 있다.The high frequency induction heating apparatus according to the present invention can precisely bond the base materials to each other by applying heat locally to both ends of the base material contacting each other by using the high frequency induction heating unit as a heat source to reduce the defect rate and reduce the amount of the smear materials When used in a muffler or the like of a vehicle, the weight of the vehicle can be reduced to increase the fuel efficiency of the vehicle.

본 발명에 의한 고주파 유도가열 장치를 이용한 가공방법은 결합되는 각 모재들을 준비하고, 가열 장치에 의해서 동시에 유도가열을 할 수 있어 공정시간을 단축하여 공정시간을 줄일 수 있어 생산능율을 증가시킬 수 있다.The method of using the high frequency induction heating apparatus according to the present invention can prepare the respective base materials to be combined and induction heating can be performed simultaneously by the heating apparatus, thereby shortening the processing time, thereby shortening the processing time and increasing the production efficiency .

도 1은 본 발명의 일 실시예에 따른 고주파 유도가열 장치를 나타내는 도면이다.
도 2는 본 발명의 일 실시예에 따른 도 1의 A-A의 단면도이다.
도 3은 본 발명의 일 실시예에 따른 고주파 유도 가열부를 나타내는 다양한 실시예를 나타내는 사진이다.
도 4a는 종래의 아크 용접을 이용하여 모재를 연결한 상태도이다.
도 4b는 본 발명의 일 실시예에 따른 고주파 유도가열 장치를 이용하여 모재를 연결한 상태도이다.
도 5는 본 발명의 일 실시예에 따른 고주파 유도가열 장치를 이용하여 자동차의 머플러에 적용 가능한 위치는 나타내는 도면이다.
도 6은 본 발명의 일 실시예에 따른 고주파 유도가열 장치를 이용한 가공방법의 플로우차트이다.1 is a view showing a high frequency induction heating apparatus according to an embodiment of the present invention.
Figure 2 is a cross-sectional view of AA of Figure 1 according to one embodiment of the present invention.
3 is a photograph showing various embodiments showing a high frequency induction heating unit according to an embodiment of the present invention.
FIG. 4A is a state in which the base material is connected using conventional arc welding.
FIG. 4B is a state in which a base material is connected using a high frequency induction heating apparatus according to an embodiment of the present invention.
5 is a view showing a position applicable to a muffler of an automobile using a high frequency induction heating apparatus according to an embodiment of the present invention.
6 is a flowchart of a processing method using a high frequency induction heating apparatus according to an embodiment of the present invention.

이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 상세히 설명한다. 이 때, 첨부된 도면에서 동일한 구성 요소는 가능한 동일한 부호로 나타내고 있음에 유의한다. 또한, 본 발명의 요지를 흐리게 할 수 있는 공지 기능 및 구성에 대한 상세한 설명은 생략할 것이다. 마찬가지 이유로 첨부 도면에 있어서 일부 구성요소는 과장되거나 생략되거나 개략적으로 도시되었다.
Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. Note that, in the drawings, the same components are denoted by the same reference symbols as possible. Further, the detailed description of known functions and configurations that may obscure the gist of the present invention will be omitted. For the same reason, some of the components in the drawings are exaggerated, omitted, or schematically illustrated.

도 1은 본 발명의 일 실시예에 따른 고주파 유도가열 장치를 나타내는 도면이며, 도 2는 본 발명의 일 실시예에 따른 도 1의 A - A의 단면도이며, 도 3은 본 발명의 일 실시예에 따른 고주파 유도 가열부를 나타내는 다양한 실시예를 나타내는 사진이다.2 is a cross-sectional view taken along the line A-A in FIG. 1 according to an embodiment of the present invention, and FIG. 3 is a cross-sectional view of a high frequency induction heating apparatus according to an embodiment of the present invention Frequency induction heating unit according to the first embodiment of the present invention.

도 1 내지 도 3을 참조하여 설명하면, 본 발명의 일 실시예에 따른 고주파 유도가열 장치는 고주파 유도 가열부(100) 및 제어부(200)를 포함한다.1 to 3, a high frequency induction heating apparatus according to an embodiment of the present invention includes a high frequency induction heating unit 100 and a control unit 200.

고주파 유도 가열부(100)는 모재(10, 11) 사이에 마련된 용가재(12)를 감싸도록 형성된다. 고주파 유도 가열부(100)는 유도 가열에 의해서 열을 발생시킨다. 유도 가열은 전자유도 작용에 의한 것으로서, 교류 전류가 흐르는 코일속에 위치하는 금속 등의 도전체는 와전류 손실과 히스테리시트(Hysteresis) 손실의 저항에 의하여 열이 발생한다. 이와 같이 발생하는 열에너지를 이용하여 모재를 가열하는 것을 말한다. 특히 고주파 전류를 이용하는 것을 고주파 유도 가열(high-frequency induction heating)이라 한다. 이러한 고주파 유도 가열은 도체의 직접가열 또는 국부가열이 가능하고, 에너지 밀도가 높으며, 불꽃이 방출되지 않으며 용접 중 발생하는 퓸(fume)이 저감되는 특징이 있다.The high frequency induction heating unit 100 is formed so as to surround the filler material 12 provided between the base materials 10 and 11. The high frequency induction heating unit 100 generates heat by induction heating. Induction heating is caused by an electromagnetic induction action, and a conductor such as a metal placed in a coil through which an alternating current flows generates heat due to resistance of eddy current loss and hysteresis loss. And heating the base material by using the heat energy generated in this manner. In particular, the use of a high frequency current is referred to as high-frequency induction heating. This high frequency induction heating is capable of direct heating of the conductor or locally heating, has high energy density, does not emit flame, and reduces fumes generated during welding.

고주파 유도 가열부(100)는 모재(10, 11)의 직경보다 크게 형성되어 모재(10, 11)의 축을 따라 나선형상(110)으로 소정 깊이 만큼 감싸도록 형성될 수 있다. 고주파 유도 가열부(100)의 형상이 나선형상(110)으로 형성되면, 고주파의 용량이나 주파수가 부족할 때 모재(10, 11)의 소정의 깊이까지 전달하여 급속하게 모재(10, 11)와 용가재(12)를 효과적으로 유도가열할 수 있다.The high frequency induction heating unit 100 may be formed to have a diameter larger than the diameter of the base materials 10 and 11 so as to surround the base materials 10 and 11 by a predetermined depth in a spiral shape 110. When the high frequency induction heating unit 100 is formed in the shape of the spiral 110, the high frequency induction heating unit 100 may transmit the high frequency induction heating unit 100 to a predetermined depth of the base materials 10 and 11, (12) can be effectively induced and heated.

고주파 유도 가열부(100)는 일반적으로 모재(10, 11)와 용가재(12)의 크기 또는 재질에 따라 변경될 수 있다. 일반적으로 철 계열은 10 ~ 50kHz 정도가 많이 사용되어지며, 비철금속의 경우(황동, 알루미늄, 스텐, 동 등)는 50 ~ 400kHz 대의 비교적 높은 주파수가 사용될 수 있다. 출력용량(kHz)은 모재(10, 11)의 크기가 크고 짧은 가열시간이면 큰 용량이 필요하며, 모재가 작고 긴 가열시간이 필요하면 작은 용량으로 적용하는 것이 바람직하다. 고주파 유도 가열부(100)는 모재의 재질, 크기, 형상 등에 따라 형상이 변경될 수 있는 것으로 그 형상에 이에 한정되는 것은 아니며, 도 3에 나타난 다양한 형성을 선택적으로 적용할 수 있다.The high frequency induction heating unit 100 may be generally changed depending on the size or material of the base materials 10 and 11 and the filler material 12. [ Generally, iron type is used in the range of 10 to 50 kHz, and in case of nonferrous metal (brass, aluminum, stent, copper, etc.), a relatively high frequency of 50 to 400 kHz band can be used. The output capacity (kHz) is required to be large when the base materials 10 and 11 are large and short heating time. If the base material is small and long heating time is required, it is preferable to apply the small capacity. The high frequency induction heating unit 100 may be modified in shape depending on the material, size, and shape of the base material, and is not limited thereto, and various forms shown in FIG. 3 may be selectively applied.

용가재(12)는 모재(10, 11)를 접합하기 위하여 첨가되는 금속으로서, 모재(10, 11)의 간격, 형상, 강도, 재질에 따라 재질을 선택적으로 적용할 수 있다. 선택할 수 있는 용가재(12)의 재질은 wire, washer, sheet, 파우더, 페이스트 형태 중 하나일 수 있다.The filler material 12 is a metal added for bonding the base materials 10 and 11 and can be selectively applied depending on the spacing, shape, strength, and material of the base materials 10 and 11. The material of the optional filler (12) can be one of wire, washer, sheet, powder, paste type.

제어부(200)는 모재(10, 11)와 용가재(12)의 재질에 따라 고주파 유도 가열부(100)와 유도전류의 크기와 주파수를 제어할 수 있으며, 모재(10, 11)의 종류 및 용가재(12)의 재질에 따라 유도 전류의 시간을 자동으로 설정시간을 할 수 있다. 따라서 과도한 유도전류로 인해 모재(10, 11)에 손상이 발생하거나 모재의 접합이 불량하게 되는 것을 방지할 수 있다. The control unit 200 can control the magnitude and frequency of the induction current with the high frequency induction heating unit 100 according to the materials of the base materials 10 and 11 and the sparse material 12, The time of the induction current can be set automatically according to the material of the coil 12. Therefore, it is possible to prevent damage to the parent materials 10 and 11 due to excessive induction currents and poor parent material joining.

본 발명의 일 실시예에 따른 고주파 유도가열 장치는 전류감지 트랜스(300)를 포함할 수 있다. 전류감지 트랜스(300)는 고주파 유도 가열부(100)에 유도전류가 유도될 때, 사용전력을 표시하며, 고주파 유도 가열부(100)에 과부하를 방지하여 과도한 유도전류가 흘러 모재(10, 11)에 손상이 발생하거나 모재의 접합이 불량해 지는 것을 방지할 수 있다.The high frequency induction heating apparatus according to an embodiment of the present invention may include a current sensing transformer 300. The current sensing transformer 300 indicates the used electric power when the induction current is induced in the high frequency induction heating unit 100. The excessive induction current flows to the high frequency induction heating unit 100, It is possible to prevent damage to the base material and deterioration of bonding of the base material.

본 발명의 일 실시예에 따른 고주파 유도가열 장치는 냉각기(400)를 포함할 수 있다. 냉각기(400)는 고주파 유도 가열부(100) 및 모재(10, 11)에 일정온도 이상 상승할 때, 고주파 유도 가열부(100) 및 모재(10, 11)를 설정된 온도 이하가 되도록 낮출 수 있다. 냉각기(400)는 제어부(200)에 의해서 동작이 제어될 수 있다.
The high frequency induction heating apparatus according to an embodiment of the present invention may include a cooler 400. The cooler 400 can lower the high frequency induction heating unit 100 and the base materials 10 and 11 to a temperature lower than a predetermined temperature when they rise to a predetermined temperature or higher in the high frequency induction heating unit 100 and the base materials 10 and 11 . The operation of the cooler 400 can be controlled by the control unit 200.

도 4a는 종래의 아크 용접을 이용하여 모재를 연결한 상태도이며, 도 4b는 본 발명의 일 실시예에 따른 고주파 유도가열 장치를 이용하여 모재를 연결한 상태도이다.FIG. 4A is a state in which base materials are connected using conventional arc welding, and FIG. 4B is a state in which base materials are connected using a high frequency induction heating apparatus according to an embodiment of the present invention.

도 4a에 도시된 바와 같이, 일반 아크 용접을 통한 모재의 용접면은 불규칙한 것으로 나타났다. 이와 같이, 접합면이 불규칙으로 형성되면 용접면을 매끄럽게 하기 위하여 추가적인 용접이 필요하며, 용접면을 마무리하기 위한 추가적인 작업이 발생하게 된다. 추가적인 용접은 모재의 손상시킬 수 있으며, 용가재가 추가로 사용되어 모재의 중량이 증가하고 고정이 추가되어 작업시간이 증가하는 문제점이 발생할 수 있다.As shown in FIG. 4A, the weld surface of the base material through the general arc welding was found to be irregular. As such, if the bonding surface is irregularly formed, additional welding is required to smooth the welding surface, and further work is required to finish the welding surface. Additional welding may damage the base material, and additional materials may be used to increase the weight of the base material and increase the work time due to the addition of fixing.

이에 반해, 도 4b의 본 발명의 일 실시예에 따른 고주파 유도가열 장치는 접합면이 매끄럽고 우수한 것으로 나타났다. 고주파 유도 가열부(100)는 모재(10, 11) 사이에 마련된 용가재(12)를 감싸도록 형성된다. 모재(10, 11) 사이에 마련된 용가재(12)는 고주파 유도 가열부(100)의 유도가열에 의해서 용융되고, 모재(10, 11)와 모재사이에 모세관 현상을 통하여 스며들게 된다. 모재(10, 11)는 용가재(12)에 의해서 견고하게 접합됨으로써, 아크용접시 사용되는 용접량보다 적은 용가재(12)로 견고하게 접합될 수 있다. 따라서 모재(10, 11) 연결 시, 제품의 중량을 줄일 수 있으므로 제품이 차량의 머플러로 사용될 때 중량이 감소되어 연비효율을 증가시킬 수 있다.
On the other hand, the high frequency induction heating apparatus according to an embodiment of the present invention shown in FIG. 4B has a smooth and excellent bonding surface. The high frequency induction heating unit 100 is formed so as to surround the filler material 12 provided between the base materials 10 and 11. The filler material 12 provided between the base materials 10 and 11 is melted by the induction heating of the high frequency induction heating unit 100 and permeated between the base materials 10 and 11 and the base material through a capillary phenomenon. The base materials 10 and 11 are firmly joined by the filler metal 12 so that they can be firmly bonded to the filler metal 12 less than the amount of welding used in arc welding. Therefore, when the base material 10, 11 is connected, the weight of the product can be reduced, so that the weight is reduced when the product is used as a muffler of a vehicle, thereby increasing fuel efficiency.

도 5는 본 발명의 일 실시예에 따른 고주파 유도가열 장치를 이용하여 자동차의 머플러에 적용 가능한 위치는 나타내는 도면이다.5 is a view showing a position applicable to a muffler of an automobile using a high frequency induction heating apparatus according to an embodiment of the present invention.

자동차의 머플러는 프론트(13), 센터 머플러(14) 및 메인 머플러(15)로 형성될 수 있다. 각각의 부품들은 제품의 유지 관리 등을 위해서 조인트로 형성되어 있다. 자동차의 머플러의 각각의 부품들이 본 발명에 의한 고주파 유도가열 장치에 의해서 단부가 연결되면, 연결부의 접합강도를 견고하게 하면서 접합부의 중량을 감소할 수 있어 자동차의 중량감소로 인한 연비를 향상시킬 수 있다.
The muffler of the automobile may be formed of the front 13, the center muffler 14, and the main muffler 15. Each part is formed as a joint for the maintenance of the product. When the ends of the muffler of the automobile are connected by the high-frequency induction heating apparatus according to the present invention, the joint strength of the connection portion can be made firm while the weight of the joint portion can be reduced, have.

도 6은 본 발명의 일 실시예에 따른 고주파 유도가열 장치를 이용한 가공방법의 플로우차트이다.6 is a flowchart of a processing method using a high frequency induction heating apparatus according to an embodiment of the present invention.

고주파 유도가열 장치를 이용한 가공방법은 모재 배열단계(S100), 용가재 배치단계(S200), 유도 가열부 배치단계(S300) 및 모재 접합단계(S400)를 포함한다.The processing method using the high frequency induction heating apparatus includes a base material arranging step (S100), a filler material arranging step (S200), an induction heating part arranging step (S300), and a base material bonding step (S400).

모재 배열단계(S100)는 복수로 마련된 모재의 양단부를 서로 이웃하게 배열하는 단계이다. 용가재 배치단계(S200)는 모재 배열단계(S100)시 모재의 형상, 강도, 재질 등을 고려하여 모재의 서로 이웃하는 양단부 사이에 이웃하게 배치한다. 이때 사용하는 용가재의 재질은 wire, washer, sheet, 파우더, 페이스트 형태 중 하나일 수 있다.The base material arranging step S100 is a step of arranging both ends of a plurality of base materials adjacent to each other. The fugitive material placement step (S200) is arranged adjacent to both adjacent ends of the base material in consideration of the shape, strength, and material of the base material in the base material arrangement step (S100). The material used may be wire, washer, sheet, powder or paste.

유도 가열부 배치단계(S300)는 용가재 배치단계(S200) 후에, 고주파 유도 가열부를 배치하는 단계이다. 고주파 유도 가열부는 모재의 접합형식 및 접합 형태에 따라 다양하게 적용될 수 있으며, 복수로 구비되어 각각의 이웃하는 모재 단부에 마련될 수 있다. 복수로 구비된 고주파 유도 가열부는 동시에 제어될 수 있다.The step of arranging the induction heating part (S300) is a step of arranging the high frequency induction heating part after the step of arranging the consumable material (S200). The high frequency induction heating unit may be variously applied depending on the bonding type and the bonding type of the base material, and may be provided in plural and provided at the end portions of the neighboring base materials. The plurality of high frequency induction heating units can be simultaneously controlled.

모재 접합단계(S400)는 고주파 유도 가열부에 유도 전류를 인가하여 용가재와 서로 이웃하게 배치된 모재의 양단부를 접합하는 단계이다. 고주파 유도 가열부가 동시에 마련되면, 복수로 마련된 고주파 유도 가열부에 동시에 유도 전류를 인가하여 접합할 수 있으므로 모재의 양단부를 접합함으로써 접합시간을 단축할 있다.
In the base material joining step (S400), an induction current is applied to the high-frequency induction heating unit to bond both ends of the base material disposed adjacent to the meltable material. If the high frequency induction heating unit is provided at the same time, the induction current can be applied to the plurality of high frequency induction heating units at the same time, so that the bonding time can be shortened by joining both ends of the base material.

한편, 본 명세서와 도면에 개시된 본 발명의 실시예들은 본 발명이 기술 내용을 쉽게 설명하고 본 발명의 이해를 돕기 위해 특정 예를 제시한 것일 뿐이며, 본 발명의 범위를 한정하고자 하는 것은 아니다. 여기에 개시된 실시예들 이외에도 본 발명의 기술적 사상에 바탕을 둔 다른 변형예들이 실시 가능하다는 것은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 자명한 것이다.It should be noted that the embodiments of the present invention disclosed in the present specification and drawings are only illustrative of the present invention in order to facilitate description of the present invention and to facilitate understanding of the present invention and are not intended to limit the scope of the present invention. It will be apparent to those skilled in the art that other modifications based on the technical idea of the present invention are possible in addition to the embodiments disclosed herein.

10, 11 : 모재 12 : 용가재
100 : 고주파 유도 가열장치 200 : 제어부 10, 11: base material 12:
100: high frequency induction heating apparatus 200:

Claims (5)

삭제delete 삭제delete 삭제delete 복수로 마련된 모재의 양단부를 서로 이웃하게 배열하는 모재 배열단계;
상기 이웃하게 배열된 모재 사이에 용가재를 배치시키는 용가재 배치단계;
상기 용가재가 배치된 위치에 고주파 유도 가열부를 배치시키는 유도 가열부 배치단계; 및
상기 고주파 유도 가열부에 전류를 인가하여 상기 용가재와 상기 서로 이웃하게 배치된 모재의 양단부를 접합시키는 모재 접합단계;를 포함하고,
상기 모재 배열 단계에서 외측 모재의 단부에 확관부를 형성하고 내측 모재의 단부를 상기 확관부를 통해 상기 외측 모재의 단부 내로 끼워 배열하고,
상기 용가재 배치단계에서 상기 용가재를 상기 확관부의 내면에 밀착하는 한편 상기 외측 모재의 단부와 상기 내측 모재 단부 사이로 끼워지게 배치하는 것을 특징으로 하는 고주파 유도 가열 장치를 이용한 접합 방법.A base material arranging step of arranging both end portions of a plurality of base materials adjacent to each other;
Placing a filler material between the neighboring arranged base materials;
A step of arranging an induction heating section for disposing a high frequency induction heating section at a position where the above-mentioned excipients are disposed; And
And a base material joining step of applying a current to the high frequency induction heating unit to bond both ends of the base material disposed adjacent to the filler material,
Wherein an expansion portion is formed at an end of the outer base material in the base material arranging step and an end portion of the inner base material is inserted into the end portion of the outer base material through the expansion portion,
Wherein the flexible material is placed in close contact with the inner surface of the expanded portion and is sandwiched between the end of the outer preform and the end of the inner preform. 제4항에 있어서,
상기 접합단계는,
상기 용가재 및 서로 이웃게 배치된 모재의 재질에 따라 고주파 전류를 설정하여 접합시키는 것을 특징으로 하는 고주파 유도 가열 장치를 이용한 접합 방법.
5. The method of claim 4,
In the joining step,
Wherein a high-frequency current is set and bonded according to the material of the filler and the neighboring base material.
KR1020150023522A 2015-02-16 2015-02-16 High frequency heating equipment and method using the same KR101675005B1 (en)