KR101637500B1 - Method for plating rust-proofing film on ball stud - Google Patents

Method for plating rust-proofing film on ball stud Download PDF

Info

Publication number
KR101637500B1
KR101637500B1 KR1020150021858A KR20150021858A KR101637500B1 KR 101637500 B1 KR101637500 B1 KR 101637500B1 KR 1020150021858 A KR1020150021858 A KR 1020150021858A KR 20150021858 A KR20150021858 A KR 20150021858A KR 101637500 B1 KR101637500 B1 KR 101637500B1
Authority
KR
South Korea
Prior art keywords
ball
stud
bore
sleeve
taper
Prior art date
Application number
KR1020150021858A
Other languages
Korean (ko)
Inventor
정준원
최석
Original Assignee
(주)유진다크로
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)유진다크로 filed Critical (주)유진다크로
Priority to KR1020150021858A priority Critical patent/KR101637500B1/en
Application granted granted Critical
Publication of KR101637500B1 publication Critical patent/KR101637500B1/en

Abstract

Disclosed is a method to plate a ball stud with a rust prevention film which prevents coating liquid for plating a rust prevention film from being coated on a surface of a ball. According to the present invention, the method to plate the ball stud with a rust prevention film plates the ball stud having the ball and a stud extended from the ball with a rust prevention film, and prepares a sleeve comprising: a bore to accommodate a portion of the stud; a first taper bore connected to the bore to prevent the ball from passing; and a second taper bore extended from the first taper bore to be attached to a portion of the stud. The ball is supported on an inner surface of the first taper bore. The stud is inserted to pass through the bore, and the first and the second taper bore accommodates a portion of the stud in the bore. An end cap is mounted on the sleeve to block an inflow of coating liquid for rust prevention film treatment into the bore. The ball stud is immersed in the coating liquid to coat a surface of the stud exposed to the outside of the sleeve with the coating liquid, and the coating liquid coated on the surface of the stud is dehydrated. The coating liquid coated on the surface of the stud is hardened, and the sleeve and an end cap are separated from the ball stud. According to the present invention, the ball is covered with the sleeve and the end cap to prevent the coating liquid for rust prevention film plating from being coated on the surface of the ball, and the ball stud is then immersed to completely eliminate a postprocess of the ball. As such, productivity is able to be improved, and hardness of the ball whose surface is hardened is able to be maintained to guarantee quality. Moreover, the sleeve and the end cap is able to be mounted and disassembled by a simple structure of covering the ball with the sleeve, and the end cap to efficiently plate a rust prevention film.

Description

볼 스터드의 방청피막 도금 방법{METHOD FOR PLATING RUST-PROOFING FILM ON BALL STUD}TECHNICAL FIELD [0001] The present invention relates to a method for plating a rust-preventive film on a ball stud,

본 발명은 방청피막 도금 방법에 관한 것으로, 보다 상세하게는 방청피막(Rust-proofing film)의 도금을 위한 코팅액(Coating fluid)이 볼(Ball)의 표면에 코팅되지 않게 처리할 수 있는 볼 스터드의 방청피막 도금 방법에 관한 것이다.The present invention relates to a rust-preventive coating method, and more particularly, to a rust-proof coating method for coating a rust-proofing film on a ball stud, And a method for plating a rust preventive coating.

자동차, 선박, 토목건축, 전기전자 등 모든 산업분야에서 금속소재의 녹을 방지하기 위한 방청피막의 처리는 매우 중요한 기술이다. 볼 스터드, 볼트, 너트, 와셔(Washer), 샤프트(Shaft) 등과 같은 다양한 기계요소와 기계부품에 발생되는 부식은 수명과 성능에 직접적으로 관계되고, 사고 발생의 원인이 되고 있다. In all industries, such as automobiles, ships, civil engineering, and electronics, the treatment of rust prevention coatings to prevent rust of metallic materials is a very important technology. Corrosion of various mechanical and mechanical components, such as ball studs, bolts, nuts, washers, shafts, etc., is directly related to life and performance, and is causing accidents.

금속소재의 방청피막 처리를 위한 방청제의 일례로 아연-알루미늄 복합피막(Zinc-aluminum complex film)용 코팅액이 있다. 아연-알루미늄 복합피막용 코팅액은 흔히 지오메트(GEOMET, 제품명, Metal Coatings International Inc.,, 미국)로 잘 알려져 있다. 지오메트는 크롬이 없는 친환경적인 수용성 화합물(Water-based chemical solution)로 내식성과 코팅성 등이 우수하고, 수소 취성이 없어 여러 분야에서 광범위하게 사용되고 있다. As an example of the rust inhibitor for the rust-preventive coating treatment of a metal material, there is a coating liquid for a zinc-aluminum complex film. Coating solutions for zinc-aluminum composite coatings are commonly known as GEOMET (product name, Metal Coatings International Inc., USA). Geomet is a chromium-free water-based chemical solution with excellent corrosion resistance and coating properties and is widely used in many fields because of its lack of hydrogen embrittlement.

한편, 방청피막 처리는 코팅액에 금속소재를 침지(Dipping)한 후, 탈수 및 건조 등 여러 공정을 거쳐 실시되고 있다. 금속소재의 방청피막 처리를 대량으로 행하기 위하여 금속소재의 형태에 맞도록 제작되어 있는 지그(Jig) 또는 랙(Rack)에 복수의 금속소재를 탑재하여 각각의 공정에 투입하고 있다. On the other hand, the rust-preventive coating treatment is carried out through various processes such as dipping, dewatering and drying of the metal material in the coating liquid. A plurality of metal materials are mounted on a jig or a rack which is manufactured to conform to the shape of a metal material in order to perform a large amount of rust-preventive coating of the metal material, and the metal materials are put into each process.

한국 등록실용신안 제20-0463910호 '방청피막 처리용 지그'는 볼과 볼의 외면 한쪽으로부터 연장되어 있는 스터드(또는 볼트)를 갖는 복수의 볼 스터드를 복수의 홀더(Holder)에 탑재하여 방청피막을 처리할 수 있도록 구성되어 있다. 볼 스터드는 다단으로 배치되어 있는 홀더들에 탑재되므로, 볼 스터드의 탑재량이 증가되어 생산성을 향상시킬 수 있다. Korean Registered Utility Model No. 20-0463910 A 'rust-preventive film processing jig' includes a plurality of ball studs having studs (or bolts) extending from one side of the outer surface of the ball to a plurality of holders, And the like. Since the ball stud is mounted on the holders arranged in multiple stages, the load of the ball stud can be increased and the productivity can be improved.

상기한 바와 같은 종래의 지그에 볼 스터드를 탑재하여 코팅액에 침지할 경우, 코팅액의 볼 스터드의 표면 전체에 코팅되게 된다. 볼 스터드는 볼 조인트(Ball joint)의 중요한 구성요소로 볼 조인트의 볼은 자유롭게 움직일 수 있도록 소켓(Socket)에 수용되어 구름접촉(Rolling contact)하는 부분이므로, 볼의 표면에 코팅되어 있는 방청피막은 후가공에 의하여 제거해야만 한다. 이러한 방청피막의 제거는 황삭(Rough machining)에 의하여 행해지고 있어 공정수가 늘어나 생산성을 저하시키게 된다. 따라서 볼 스터드의 방청피막에서 황삭을 배제시킬 수 있는 기술의 개발이 요구되고 있다.When the ball stud is mounted on the conventional jig as described above and immersed in the coating liquid, the entire surface of the ball stud of the coating liquid is coated. The ball stud is an important component of the ball joint. Since the ball of the ball joint is accommodated in the socket to make rolling contact, the rust coating film coated on the surface of the ball Must be removed by post-processing. The removal of the rust preventive film is performed by rough machining, which increases the number of processes and deteriorates the productivity. Therefore, it is required to develop a technique that can eliminate roughing in the rust-preventive coating of the ball stud.

본 발명은 상기와 같은 종래 볼 스터드의 방청피막 도금 방법의 여러 가지 문제점을 해결하기 위한 것이다. 본 발명의 목적은, 볼 스터드의 침지 시 코팅액이 볼의 표면에 코팅되지 않고 나머지 부분에만 코팅되어 볼의 후가공을 배제할 수 있으므로, 생산성을 향상시킬 수 있는 새로운 볼 스터드의 방청피막 도금 방법을 제공하는 것이다. The present invention is intended to solve various problems of the above-mentioned conventional rust-preventive coating method of a ball stud. An object of the present invention is to provide a new method of coating a rust-preventive coating of a ball stud which can improve the productivity because the coating liquid is not coated on the surface of the ball when the ball stud is immersed, .

본 발명의 다른 목적은, 표면 경화 처리되어 있는 볼에 대한 후가공의 배제에 의하여 경도를 그대로 유지하여 품질을 보장할 수 있는 볼 스터드의 방청피막 도금 방법을 제공하는 것이다. It is another object of the present invention to provide a method of coating a rust-preventive coating of a ball stud, which can maintain the hardness by the exclusion of the post-hardening process on the surface-hardened ball.

본 발명의 다른 목적은, 볼이 슬리브(Sleeve)와 엔드 캡(End cap)에 의하여 씌워지는 단순한 구성에 의하여 방청피막의 도금을 간편하게 실시할 수 있는 볼 스터드의 방청피막 도금 방법을 제공하는 것이다.It is another object of the present invention to provide a method for plating a rust-preventive coating of a ball stud which can easily perform plating of a rust-preventive coating by a simple structure in which the ball is covered by a sleeve and an end cap.

본 발명의 일 측면에 따르면, 볼 스터드의 방청피막 도금 방법이 제공된다. 본 발명에 따른 볼 스터드의 방청피막 도금 방법은, 볼과 볼로부터 연장되어 있는 스터드를 구비하는 볼 스터드의 방청피막 처리 방법에 있어서, 스터드의 일부분을 수용하는 보어와, 볼이 통과되지 않도록 보어와 연결되어 있는 제1 테이퍼보어와, 스터드의 일부분에 밀착되도록 제1 테이퍼보어로부터 연장되어 있는 제2 테이퍼보어를 구비하는 슬리브를 준비하여 볼이 제1 테이퍼보어의 내면에 지지되고 스터드가 보어, 제1 및 제2 테이퍼보어를 통과하도록 끼워 스터드의 일부분을 보어 안에 수용하는 단계와, 보어 안으로 방청피막 처리용 코팅액의 유입이 차단되도록 슬리브에 엔드 캡을 결합하는 단계와, 볼 스터드를 코팅액에 침지하여 코팅액을 슬리브 밖에 노출되어 있는 스터드의 표면에 코팅하는 단계와, 스터드의 표면에 코팅되어 있는 코팅액을 탈수하는 단계와, 스터드의 표면에 코팅되어 있는 코팅액을 경화시키는 단계와; 볼 스터드로부터 슬리브와 엔드 캡을 분리하는 단계를 포함한다.According to one aspect of the present invention, there is provided a method for plating a rust-preventive coating on a ball stud. A method of coating a rust-preventive coating of a ball stud according to the present invention is a method of rust-inhibiting coating a ball stud having a ball and a stud extending from the ball, the method comprising the steps of: A sleeve having a first taper bore connected thereto and a second taper bore extending from the first taper bore so as to be in close contact with a portion of the stud is prepared so that the ball is supported on the inner surface of the first taper bore, 1 and a second taper bore to allow a portion of the stud to be received in the bore; coupling the end cap to the sleeve such that the coating solution for rust prevention coating is prevented from flowing into the bore; and dipping the ball stud in the coating solution Coating the surface of the stud exposed to the outside of the sleeve with a coating liquid, Dewatering the surface of the stud; curing the coating liquid coated on the surface of the stud; And separating the sleeve and the end cap from the ball stud.

삭제delete

본 발명에 따른 볼 스터드의 방청피막 도금 방법은, 방청피막의 도금을 위한 코팅액이 볼의 표면에 코팅되지 않도록 슬리브와 엔드 캡을 볼에 씌운 후 볼 스터드를 침지하여 볼의 후가공을 완전히 배제할 수 있으므로, 생산성을 향상시킬 수 있으며, 표면 경화 처리되어 있는 볼의 경도를 그대로 유지하여 품질을 보장할 수 있다. 또한, 볼이 슬리브와 엔드 캡에 의하여 씌워지는 단순한 구성에 의하여 슬리브와 엔드 캡을 간편하게 결합 및 분해하여 방청피막의 도금을 효율적으로 실시할 수 있는 효과가 있다. The rust-preventive coating method of the ball stud according to the present invention is characterized in that after the sleeve and the end cap are coated on the ball so that the coating solution for plating the rust-preventive coating is not coated on the surface of the ball, the ball stud is immersed to completely eliminate the post- Therefore, the productivity can be improved, and the hardness of the surface-hardened ball can be maintained as it is and quality can be assured. In addition, there is an effect that plating of the rust-preventive coating can be efficiently performed by simply joining and disassembling the sleeve and the end cap by the simple constitution that the ball is covered by the sleeve and the end cap.

도 1은 본 발명에 따른 볼 스터드의 방청피막 도금 방법을 설명하기 위하여 볼 스터드, 슬리브와 엔드 캡을 분리하여 나타낸 사시도이다.
도 2는 본 발명에 따른 볼 스터드의 방청피막 도금 방법을 설명하기 위하여 볼 스터드, 슬리브와 엔드 캡을 결합하여 나타낸 단면도이다.
도 3은 본 발명에 따른 볼 스터드의 방청피막 도금 방법에 의하여 방청피막이 도금되어 있는 볼스터드를 나타낸 단면도이다.
도 4는 본 발명에 따른 볼 스터드의 방청피막 도금 방법에서 볼 스터드를 침지시키기 위한 지그의 일례를 부분적으로 나타낸 정면도이다.
도 5는 본 발명에 따른 볼 스터드의 방청피막 도금 방법을 설명하기 위하여 나타낸 흐름도이다1 is a perspective view showing a ball stud, a sleeve, and an end cap separated from each other to explain a method of coating a rust preventive coating of the ball stud according to the present invention.
FIG. 2 is a cross-sectional view illustrating a method of plating a rust-preventive coating of a ball stud according to the present invention in combination with a ball stud, a sleeve, and an end cap.
3 is a cross-sectional view showing a ball stud having a rust-preventive coating plated by the rust-preventive coating method of the ball stud according to the present invention.
4 is a front view partially showing an example of a jig for immersing a ball stud in a rust-preventive coating method for a ball stud according to the present invention.
5 is a flow chart for explaining a rust-preventive coating method of a ball stud according to the present invention

본 발명의 그 밖의 목적, 특정한 장점들과 신규한 특징들은 첨부된 도면들과 연관되어지는 이하의 상세한 설명과 바람직한 실시예들로부터 더욱 분명해질 것이다.Other objects, specific advantages and novel features of the present invention will become more apparent from the following detailed description and preferred embodiments with reference to the accompanying drawings.

이하, 본 발명에 따른 볼 스터드의 방청피막 도금 방법에 대한 바람직한 실시예들을 첨부된 도면들에 의거하여 상세하게 설명한다.BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, preferred embodiments of a rust-preventive coating method for a ball stud according to the present invention will be described in detail with reference to the accompanying drawings.

먼저, 도 1 내지 도 3을 참조하면, 본 발명에 따른 방청피막 도금 방법에 의하여 처리되는 볼 스터드(10)는 볼(12)과 볼(12)의 외면 한쪽으로부터 연장되어 있는 스터드(14)를 구비한다. 볼(12)은 볼 조인트의 소켓 또는 볼 시트(Ball seat)에 구름접촉하면서 자유롭게 움직이게 된다. 스터드(14)는 볼(12)과 이웃하는 근위부(Proximal portion: 16)와 볼(12)로부터 떨어져 있는 원위부(Distal portion: 18)를 갖는다. 근위부(16)는 넥(Neck: 20)에 의하여 볼(12)과 연결되어 있다. 스터드(14)는 넥(20)으로부터 연장되어 있는 테이퍼(Taper: 22)를 갖는다. 테이퍼(22)는 원위부(18)로 갈수록 직경이 감소되도록 구성되어 있다. 볼트(24)가 원위부(18)의 외면에 형성되어 있다. 1 to 3, a ball stud 10 to be processed by the rust preventive coating method according to the present invention includes a ball 12 and a stud 14 extending from one side of the outer surface of the ball 12 Respectively. The balls 12 are allowed to freely move in rolling contact with the ball seats of the ball joints. The stud 14 has a proximal portion 16 adjacent the ball 12 and a distal portion 18 remote from the ball 12. The proximal portion 16 is connected to the ball 12 by a neck 20. The stud 14 has a taper 22 extending from the neck 20. The taper 22 is configured to decrease in diameter toward the distal portion 18. A bolt 24 is formed on the outer surface of the distal portion 18.

도 1과 도 2를 참조하면, 본 발명에 따른 방청피막 도금 방법은 볼(12)을 끼워넣어 수용할 수 있는 슬리브(30)와, 슬리브(30)의 말단에 결합되는 엔드 캡(40)을 사용한다. 슬리브(30)는 볼(12)을 수용할 수 있는 보어(Bore: 32)와, 넥(20)과 스터드(14)의 근위부(16)를 수용할 수 있도록 보어(22)로부터 단계적으로 연장되어 있는 제1 테이퍼보어(Tape bore: 34)와 제2 테이퍼보어(36)를 갖는다. 제1 및 제2 테이퍼보어(34, 36) 각각은 말단으로 갈수록 직경이 감소하도록 형성되어 있다. 제1 테이퍼보어(34)의 직경은 볼(12)이 통과되지 않도록 형성되어 있다. 수나사(38)가 슬리브(30)의 외면에 형성되어 있다. 엔드 캡(40)은 수나사(38)에 체결할 수 있도록 형성되어 있는 암나사(42)를 갖는다. 작업자가 엔드 캡(40)을 잡고 수나사(38)에 체결하기 편하도록 한 쌍의 평면부(44)가 엔드 캡(40)의 외면 양쪽에 형성되어 있다. 1 and 2, a rust-preventive coating method according to the present invention includes a sleeve 30 capable of holding a ball 12 therein, an end cap 40 coupled to a distal end of the sleeve 30, use. The sleeve 30 includes a bore 32 capable of receiving the ball 12 and a bore 32 extending stepwise from the bore 22 to receive the neck 16 and the proximal portion 16 of the stud 14 And has a first taper bore (34) and a second taper bore (36). Each of the first and second taper bores 34 and 36 is formed to have a reduced diameter toward the distal end. The diameter of the first taper bore 34 is formed such that the ball 12 does not pass through. A male thread 38 is formed on the outer surface of the sleeve 30. [ The end cap 40 has a female screw 42 which is fastened to the male screw 38. A pair of planar portions 44 are formed on both sides of the outer surface of the end cap 40 so that the worker can hold the end cap 40 and fasten it to the male screw 38.

도 5를 참조하면, 본 발명에 따른 방청피막 도금 방법은 볼(12)의 표면을 경화하기 위하여 볼(12)을 표면 경화 처리한다(S100). 볼(12)의 표면 경화 처리는 고주파 표면 경화(High frequency surface hardening)에 의하여 실시할 수 있다. 다음으로, 전처리 공정(Pretreatment process)으로 볼 스터드(10)의 외면에 오염되어 있는 유분을 유기용재를 사용하여 제거하는 탈지(Degreasing)를 행한다(S102).Referring to FIG. 5, the rust-preventive coating method according to the present invention includes surface-hardening the ball 12 to harden the surface of the ball 12 (S100). The surface hardening treatment of the balls 12 can be performed by high frequency surface hardening. Next, in a pretreatment process, degreasing is performed to remove oil contaminated on the outer surface of the ball stud 10 by using an organic solvent (S102).

도 2와 도 5를 참조하면, 작업자는 볼 스터드(10)의 전처리 공정 후, 슬리브(30)를 준비하여 볼(12)이 슬리브(30)의 보어(32) 안에 수용되도록 넥(20)에 이웃하는 테이퍼(22)의 일부분을 제2 테이퍼보어(36)에 끼운다(S104). 이때, 작업자는 볼(12)이 제1 테이퍼보어(34)의 내면에 지지되어 보어(32)에 수용되고, 스터드(14)가 보어(32), 제1 및 제2 테이퍼보어(34, 36)를 통과하도록 끼운다. 테이퍼(22)의 일부분이 제2 테이퍼보어(36)에 끼워지면, 테이퍼(22)의 외면과 제2 테이퍼보어(36)의 내면이 밀착되어 코팅액(60)의 유입이 차단된다. 2 and 5, the operator prepares the sleeve 30 after the preprocessing step of the ball stud 10 and places the ball 12 on the neck 20 to be received in the bore 32 of the sleeve 30 A portion of the adjacent taper 22 is sandwiched between the second taper bore 36 (S104). At this time, the operator can see that the ball 12 is supported on the inner surface of the first taper bore 34 and received in the bore 32, and the stud 14 is supported by the bore 32, the first and second taper bores 34 and 36 ). The outer surface of the taper 22 and the inner surface of the second taper bore 36 come into close contact with each other to block the inflow of the coating liquid 60. [

작업자는 볼(12)을 슬리브(30)의 보어(32) 안에 수용한 후, 수나사(38)와 암나사(42)를 체결하여 엔드 캡(40)을 슬리브(30)에 결합한다(S106). 엔드 캡(40)이 슬리브(30)에 결합되면, 보어(32) 안은 밀폐된다. 또한, 보어(32) 안은 공기가 체류하는 에어포켓(Air pocket)으로 된다. 몇몇 실시예에 있어서, 볼 스터드(10)는 테이퍼(22) 없이 넥(20)으로부터 볼트(24)까지 단일 직경으로 연장되는 로드(Rod)를 갖도록 구성될 수 있다. 이 경우, 제2 테이퍼보어(36)의 직경은 로드의 외면에 밀착될 수 있는 형태로 구성될 수 있다. The operator inserts the ball 12 into the bore 32 of the sleeve 30 and then tightens the male screw 38 and the female screw 42 to connect the end cap 40 to the sleeve 30 at step S106. When the end cap 40 is coupled to the sleeve 30, the bore 32 is sealed. In addition, the inside of the bore 32 becomes an air pocket in which air stays. In some embodiments, the ball stud 10 may be configured to have a rod extending from the neck 20 to the bolt 24 with a single diameter without a taper 22. In this case, the diameter of the second taper bore 36 may be configured to be in close contact with the outer surface of the rod.

계속해서, 슬리브(30)와 엔드 캡(40)을 볼(12)에 결합한 후, 숏 블라스트(Shot blast)에 의하여 볼 스터드(10)의 녹, 스케일(Scale)을 제거하는 탈청(Descaling)을 행한다(S108). 탈청은 슬리브(30) 안에 수용되어 있는 볼(12)에는 행해지지 않고 볼트(24)와 테이퍼(22)의 노출되어 있는 표면에만 행해지므로, 탈청으로 인하여 볼(12)의 마모가 발생되어 경화가 약화되는 것을 방지할 수 있다. Subsequently, after the sleeve 30 and the end cap 40 are coupled to the ball 12, descaling to remove the rust and scale of the ball stud 10 by shot blasting is performed (S108). The degreasing is not performed on the ball 12 accommodated in the sleeve 30 but on the exposed surfaces of the bolt 24 and the taper 22 so that the ball 12 wears due to deaeration, It can be prevented from being weakened.

도 4에 도시되어 있는 바와 같이, 작업자는 볼 스터드(10)의 대량 생산을 위하여 슬리브(30)와 엔드 캡(40)이 볼(12)에 씌워져 있는 복수의 볼 스터드(10)를 지그(50) 또는 랙의 홀더(52)들 각각에 탑재한다. 볼 스터드(10)는 볼(12)이 홀더(52)의 위쪽에 배치되도록 홀더(52)의 구멍(54)에 스터드(14)를 끼워 탑재한다. 몇몇 실시예에 있어서, 지그(50)는 일례로 한국 등록실용신안 제20-0463910호 '방청피막 처리용 지그'가 사용될 수 있으나, 이에 한정되는 것은 아니다. 지그 또는 랙은 볼 스터드(10)를 대량으로 간편하게 탑재할 수 있는 형태이면 어떠한 것이라도 가능하다.4, a worker inserts a plurality of ball studs 10 with the sleeve 30 and the end cap 40 on the ball 12 for the mass production of the ball stud 10 into the jig 50 Or the racks 52 of the rack. The ball stud 10 mounts the stud 14 in the hole 54 of the holder 52 so that the ball 12 is placed above the holder 52. [ In some embodiments, the jig 50 may be, for example, Korean Registered Utility Model No. 20-0463910 'a rust-preventive film processing jig', but the present invention is not limited thereto. The jig or rack can be any shape that can mount a large number of ball studs 10 easily.

복수의 볼 스터드(10)가 탑재되어 있는 지그(50)는 트롤리(Trolley), 호이스트(Hoist) 등에 의하여 침지(S110), 탈수(S112) 및 건조 공정(S114)으로 순차적으로 운반하면서 볼 스터드(10)의 표면에 방청피막(62)을 도금한다. 침지 공정은 복수의 볼 스터드(10)가 탑재되어 있는 지그(50)가 코팅액(60)에 잠기도록 투입하여 행한다. The jig 50 on which the plurality of ball studs 10 are mounted is sequentially transported to the immersion S110, dehydration S112 and drying step S114 by a trolley, a hoist or the like, 10 is plated with a rust preventive coating 62. The immersion process is performed by inserting the jig 50 on which the plurality of ball studs 10 are mounted so as to be immersed in the coating liquid 60.

도 2에 도시되어 있는 바와 같이, 볼 스터드(10)의 침지 시 코팅액(60)은 보어(32) 안으로의 유입이 차단되어 볼(12), 넥(20)과 슬리브(30)에 끼워져 있는 테이퍼(22)의 일부분에는 전혀 코팅되지 않고, 볼트(24)와 테이퍼(22)의 노출되어 있는 표면에만 코팅된다. 또한, 슬리브(30)의 보어(32) 안에 체류하는 공기에 의하여 형성되는 에어 포켓은 코팅액(60)의 유입을 차단하여 코팅액(60)이 볼(12)에 코팅되는 것을 방지하게 된다. 2, when the ball stud 10 is immersed, the coating liquid 60 is prevented from flowing into the bore 32 and the balls 12, the neck 20, and the taper Is not coated at all on a part of the tapered portion 22 but only on the exposed surface of the bolt 24 and the taper 22. The air pocket formed by the air staying in the bore 32 of the sleeve 30 blocks the inflow of the coating liquid 60 and prevents the coating liquid 60 from being coated on the ball 12. [

한편, 탈수 공정은 지그(50)에 탑재되어 있는 볼 스터드(10)를 원심탈수기에 투입한 후, 원심탈수기의 작동에 의하여 지그(50)를 회전시켜 코팅되어 있는 코팅액(60)을 탈수시킨다. 코팅액(60)은 원심탈수에 의하여 볼트(24)와 테이퍼(22)의 표면에 균일한 두께로 코팅되게 된다. 건조 공정은 탈수 공정을 거친 볼 스터드(10)를 지그(50)에 탑재시킨 상태에서 건조로(Drying oven or Drying furnace)에 투입한 후, 325~370℃의 온도에서 행한다. 도 2에 도시되어 있는 바와 같이, 건조 공정이 완료되면, 코팅액(60)이 경화되어 볼트(24)와 테이퍼(22)의 노출되어 있는 표면에 방청피막(62)이 도금되어 있게 된다. 이러한 방청피막(62)의 도금은 방청피막(62)의 두께, 예를 들면 7㎛ 이상으로 충분해지도록 침지, 탈수 및 건조 공정을 2~5회 반복적으로 실시한다. Meanwhile, in the dewatering step, the ball stud 10 mounted on the jig 50 is inserted into the centrifugal dehydrator, and then the jig 50 is rotated by the operation of the centrifugal dehydrator to dehydrate the coated coating liquid 60. The coating liquid 60 is coated on the surface of the bolt 24 and the taper 22 with a uniform thickness by centrifugal dehydration. In the drying process, the ball stud 10 having undergone the dehydration process is placed in a drying oven or a drying furnace in a state where it is mounted on the jig 50, and then the process is performed at a temperature of 325 to 370 ° C. 2, when the drying process is completed, the coating liquid 60 is hardened and the rust-preventive coating 62 is plated on the exposed surfaces of the bolt 24 and the taper 22. The plating of the anticorrosive coating 62 is repeated 2 to 5 times so that the thickness of the anticorrosive coating 62, for example, 7 mu m or more is sufficient.

작업자는 건조 공정을 완료한 후, 수나사(38)와 암나사(42)의 체결을 풀어 엔드 캡(40)을 분리하고, 볼 스터드(10)와 슬리브(30)를 분리한다(S116). 도 3에 도시되어 있는 바와 같이, 볼 스터드(10)의 볼(12), 넥(20)과 슬리브(30)에 끼워져 있던 테이퍼(22)의 일부분에는 방청피막(62)이 도금되어 있지 않게 된다. 볼 스터드(10), 슬리브(30)와 엔드 캡(40)의 분리 후, 작업자는 볼 스터드(10)를 검사 및 포장한다. 이와 같이 볼(12)의 표면에 방청피막이 도금되지 않는 것에 의하여 종래에 볼(12)의 표면에 도금되었던 방청피막의 제거를 위하여 실시하던 황삭이 불필요하게 된다. 따라서 황삭의 배제에 의하여 볼 스터드(10)의 제조 공정이 단순해져 생산성을 향상시킬 수 있고, 표면 경화 처리되어 있는 볼(12)의 경도를 그대로 유지하여 품질을 보장할 수 있다. After completing the drying process, the operator unlocks the male screw 38 and the female screw 42 to separate the end cap 40 and separate the ball stud 10 and the sleeve 30 (S116). 3, the rust-preventive coating 62 is not plated on the ball 12, the neck 20, and a part of the taper 22 that has been sandwiched between the sleeve 30 and the ball stud 10 . After separating the ball stud 10, the sleeve 30 and the end cap 40, the operator inspects and packs the ball stud 10. As the rust-preventive coating is not plated on the surface of the ball 12 as described above, the roughing which is conventionally performed for removing the rust-preventive coating that has been plated on the surface of the ball 12 becomes unnecessary. Therefore, the manufacturing process of the ball stud 10 is simplified by eliminating the roughing, so that the productivity can be improved and the hardness of the surface hardened ball 12 can be maintained as it is.

이상에서 설명된 실시예는 본 발명의 바람직한 실시예를 설명한 것에 불과하고, 본 발명의 권리범위는 설명된 실시예에 한정되는 것은 아니며, 본 발명의 기술적 사상과 특허청구범위 내에서 이 분야의 당업자에 의하여 다양한 변경, 변형 또는 치환이 가능할 것이며, 그와 같은 실시예들은 본 발명의 범위에 속하는 것으로 이해되어야 한다.While the present invention has been described in connection with what is presently considered to be practical exemplary embodiments, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, It will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the appended claims.

10: 볼 스터드 12: 볼
14: 스터드 22: 테이퍼
30: 슬리브 32: 보어
34: 제1 테이퍼보어 36: 제2 테이퍼보어
40: 엔드 캡 50: 지그
60: 코팅액 62: 방청피막10: Ball Stud 12: Ball
14: Stud 22: Taper
30: sleeve 32: bore
34: first taper bore 36: second taper bore
40: end cap 50: jig
60: coating liquid 62: rustproof coating

Claims (6)

볼과, 상기 볼로부터 연장되어 있는 스터드를 구비하는 볼 스터드의 방청피막 처리 방법에 있어서,
상기 스터드의 일부분을 수용하는 보어와, 상기 볼이 통과되지 않도록 상기 보어와 연결되어 있는 제1 테이퍼보어와, 상기 스터드의 일부분에 밀착되도록 상기 제1 테이퍼보어로부터 연장되어 있는 제2 테이퍼보어를 구비하는 슬리브를 준비하여 상기 볼이 상기 제1 테이퍼보어의 내면에 지지되고 상기 스터드가 상기 보어, 상기 제1 및 제2 테이퍼보어를 통과하도록 끼워 상기 스터드의 일부분을 상기 보어 안에 수용하는 단계와,
상기 보어 안으로 방청피막 처리용 코팅액의 유입이 차단되도록 상기 슬리브에 엔드 캡을 결합하는 단계와,
상기 볼 스터드를 상기 코팅액에 침지하여 상기 코팅액을 상기 슬리브 밖에 노출되어 있는 상기 스터드의 표면에 코팅하는 단계와,
상기 스터드의 표면에 코팅되어 있는 상기 코팅액을 탈수하는 단계와,
상기 스터드의 표면에 코팅되어 있는 상기 코팅액을 경화시키는 단계와;
상기 볼 스터드로부터 상기 슬리브와 엔드 캡을 분리하는 단계를 포함하는 볼 스터드의 방청피막 도금 방법.A rust-preventive film treatment method of a ball stud having a ball and a stud extending from the ball,
A first taper bore connected to the bore to prevent the ball from passing therethrough and a second taper bore extending from the first taper bore so as to be in close contact with a portion of the stud, Preparing a sleeve for receiving a portion of the stud in the bore such that the ball is supported on an inner surface of the first taper bore and the stud passes through the bore, the first and second taper bores,
Coupling the end cap to the sleeve so as to block the inflow of the coating fluid for anti-rust treatment into the bore,
Dipping the ball stud in the coating solution to coat the coating solution on the surface of the stud exposed outside the sleeve;
Dewatering the coating liquid coated on the surface of the stud,
Curing the coating liquid coated on the surface of the stud;
And separating the sleeve and the end cap from the ball stud. 제1항에 있어서,
상기 볼을 상기 슬리브의 보어 안에 수용하는 단계 이전에 상기 볼을 표면 경화 처리하는 단계와;
상기 볼 스터드의 표면에 오염되어 있는 유분의 제거를 위하여 탈지하는 단계를 더 포함하는 볼 스터드의 방청피막 도금 방법.The method according to claim 1,
Subjecting the ball to surface hardening prior to the step of receiving the ball in the bore of the sleeve;
Further comprising the step of degreasing the ball stud to remove oil contaminated on the surface of the ball stud. 제1항에 있어서,
상기 볼 스터드를 상기 코팅액에 침지하기 이전에 상기 슬리브와 상기 엔드 캡이 결합되어 있는 상기 볼 스터드를 탈청하는 단계를 더 포함하는 볼 스터드의 방청피막 도금 방법.The method according to claim 1,
Further comprising the step of removing the ball stud having the sleeve and the end cap coupled thereto before dipping the ball stud in the coating liquid. 삭제delete 제1항 내지 제3항 중 어느 한 항에 있어서,
상기 볼과 상기 스터드는 넥에 의하여 연결되어 있고, 상기 스터드는 상기 넥으로부터 연장되어 있는 테이퍼를 가지며, 상기 테이퍼의 일부분이 상기 제2 테이퍼보어의 내면에 밀착되도록 끼우는 볼 스터드의 방청피막 도금 방법.4. The method according to any one of claims 1 to 3,
Wherein the ball and the stud are connected by a neck and the stud has a taper extending from the neck and a portion of the taper is fitted into the inner surface of the second taper bore so as to be in close contact with the inner surface of the second taper bore. 제1항 내지 제3항 중 어느 한 항에 있어서,
상기 코팅액을 탈수하는 단계는 상기 코팅액이 코팅되어 있는 상기 볼 스터드를 지그에 탑재한 후 상기 지그를 회전시키는 원심탈수로 이루어지고, 상기 코팅액을 경화시키는 단계는 상기 볼 스터드가 탑재되어 있는 지그를 건조로에 투입하여 건조하는 볼 스터드의 방청피막 도금 방법.4. The method according to any one of claims 1 to 3,
Wherein the step of dewatering the coating liquid comprises centrifugal dewatering to rotate the jig after the ball stud coated with the coating liquid is mounted on the jig, and the step of curing the coating liquid includes the step of rotating the jig on which the ball stud is mounted, And then drying the coating.
KR1020150021858A 2015-02-12 2015-02-12 Method for plating rust-proofing film on ball stud KR101637500B1 (en)