KR101628034B1 - Manufacturing method of flowerpot using kkumugi firing techinique and flowerpot made by the same - Google Patents

Abstract

The present invention relates to a method for producing pollen using a potting and firing technique and a pollen produced thereby, more particularly, Drying the shaped article; Calcining the dried material at 950 to 1,200 ° C; And removing the fired material from the kiln before the kiln is cooled and frying the surface with at least one selected from the group consisting of chaff, straw, sawdust, and wet newspaper, and firing the fired potted plant , Which is excellent in air permeability and aesthetics and can prevent intrusion of harmful bacteria.

Description

TECHNICAL FIELD The present invention relates to a method for producing a flowerpot using a squeeze firing technique and a flowerpot produced by the method.

The present invention relates to a method for producing pots using a potting and firing technique and a pot produced thereby. More specifically, the present invention relates to a potting material having excellent strength and permeability by firing under neutralization conditions and fusing soot on the surface The present invention relates to a method for producing a pollen and a pollen produced thereby.

Recently, indoor plant cultivation is increasing due to improvement of living standard and improvement of residential environment, and pollen market is also expanding accordingly. The most important consideration when choosing a flowerpot is whether it can maintain an ideal soil condition in the roots of the plant, which is represented by the water-wicking or breathability of the flowerpot. Other factors such as strength, appearance, and price of pollen can be considered.

Plastics are the mainstream material for potted plants, and soil and pottery pots using soil are also important. Among these, a plastic flowerpot requires a plurality of ventilation holes on the side and the like for ventilation, and there is a problem that when the water is supplied, the culture soil is leaked together with moisture through the ventilation holes, thereby detracting aesthetics. In addition, the plastic material flowerpot is thin in thickness, and the variation in the soil temperature in the pot is large, and when the plastic is exposed to the sun for a long time, the plastic material flower is broken. For aesthetic reasons and environmental reasons, consumers are more likely to prefer plastic materials.

The soil material pollen can be classified into two types according to the manufacturing method. The soil is fired at a temperature of about 800 ° C, which is good in ventilation and can provide a good environment for plant growth. However, it has a low strength and a drawback that the moisture seeps to the surface of the soil, . In addition, since the color of the soil is reddish, the range of the color of the soil can not be varied. The Onggi has a high strength compared with the soil, but it has insufficient air permeability and it is disadvantageous in that the roots of the plant are easily decomposed and it is not good for the growth of plants.

It is a term that has been used in traditional craftsmen 's workshops and off - farming methods to feed the smoke. In detail, the off-feeding technique burns firewood in the process of burning pottery, and the fuel which can burn a lot of smoke in the end is put into the furnace, incomplete burning of the fuel is caused to generate soot, and the soot becomes fine porcelain So that the ceramics become black. It can be used from a sintering pot having a sintering temperature as low as 800 ° C to a sintering at a high temperature of 1,200 ° C or more. It is excellent in decorative effect because it has excellent appearance to be cut off.

KR 101012127 B1 KR 101076467 B1

It is an object of the present invention to provide a production method capable of producing pollen having excellent strength and air permeability.

It is another object of the present invention to provide a production method capable of protecting a plant from noxious bacteria and producing a pollen having excellent aesthetics.

The present invention also aims to provide pollen having excellent strength, air permeability and appearance.

According to an aspect of the present invention, Drying the shaped article; Calcining the dried material at 950 to 1,200 ° C; And a step of removing the fired material from the kiln before the kiln is cooled and covering the entire or a part of the surface with at least one selected from the group consisting of chaff, straw, sawdust, and wet newspaper. A manufacturing method is provided.

In addition, the method may further include calcining the dried material at 750 to 900 DEG C before sintering at 950 to 1,200 DEG C, and sintering the glaze.

In addition, the glaze may include at least one selected from the group consisting of soda ash, columbite, spodumene, nepheline syenite, ball clay, and EPK kaolin.

According to another aspect of the present invention, there is provided a toasted plastic pot produced by the above-described production method.

The method for producing pollen according to one aspect of the present invention includes a step of firing under neutralization conditions, thereby producing a pollen having excellent air permeability as compared with a pollen which is superior in strength to fired pollen under a low firing condition and fired under a high firing condition can do.

In addition, the method for producing pollen according to one aspect of the present invention includes soot having a similar action to charcoal in the pores of the pollen prepared by including the pouring process, thereby reducing harmful bacteria that inhibit the growth of planted plants The pot can be produced.

In addition, the method for producing a flowerpot according to one aspect of the present invention can express a natural color on the surface of the flowerpot in the step of baking the flowerpot and the step of feeding the flowerpot, so that the flowerpot having an excellent aesthetic effect for enhancing the interior effect can be manufactured.

FIG. 1 is a flowchart showing a method of manufacturing a to-be-fired pollen according to a first embodiment of the present invention,
FIG. 2 is a flowchart illustrating a method of manufacturing a to-beige plastic flower pot according to a second embodiment of the present invention,
FIG. 3 illustrates a tofu plastic pot produced by the manufacturing method according to one aspect of the present invention.

Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. It will be apparent to those skilled in the art that these embodiments are illustrative of the present invention and are not intended to limit the scope of the appended claims and that various changes and modifications may be made to the embodiments within the scope and spirit of the invention , And it is natural that such variations and modifications fall within the scope of the appended claims. In the following description of the present invention, detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present invention rather unclear.

1 is a flowchart showing a method of manufacturing a toasted plastic flower pot according to a first embodiment of the present invention.

Referring to FIG. 1, a method of manufacturing a toasted plastic pot according to a first embodiment of the present invention includes a first step S1 of molding a potted object, a second step S2 drying the formed object, (S5) for firing at a temperature of 0 ° C, and a fourth step (S6) for fusing soot to the surface due to fogging.

First, a method of manufacturing a toasty plastic pot according to a first embodiment of the present invention forms a potted object (S1). The material for molding the article may be soil (sato) capable of producing soil, porcelain and pottery, and the soil may include, for example, kaolin, clay or loess, but is not limited thereto. Preferably, as the material for forming the object, it is preferable to use fine particles of clay that have been sand or impurities removed from the soil. The soil can be prepared by crushing the soil and stirring the soil, separating the upper product while stirring, precipitating the soil particles with the separated upper product, and then drying the precipitated soil in the shade for one to ten days, mixing the prepared soil with water It can be kneaded and shaped into pollen to form vases. The molding may be performed using a mill or a gypsum mold, but is not limited thereto.

The molded article is dried before sintering (S2). The drying may be performed by a method known in the art, for example, by placing the molded article in the shade for a long time or by putting it in a kiln and slowly raising the kiln temperature at a low temperature of 300 DEG C or lower But is not limited thereto. In order to prevent destruction of the material upon firing, it is preferable to dry the material for a sufficient time to completely dry.

Next, the dried material is fired at 950 to 1,200 ° C (S5). More preferably, the firing temperature is 1,050 占 폚. It is possible to obtain a product having improved strength by being fired at the above temperature for 15 to 30 hours. The firing in the art is classified into a reduction degree of firing at 700 to 900 DEG C, a degree of neutralization at firing at 900 to 1,200 DEG C and a firing degree of higher than 1,200 DEG C according to the firing temperature. The sintered material can be included in a higher degree of microporosity than the sintered material in the solidification condition and thus has excellent air permeability and can have an excellent strength as compared with the sintered material in the low sintering condition .

Next, the fired article is fired (S6). In the aspect of shortening the production time of the pollen, it is necessary to remove the material from the kiln before the kiln is fired after the firing of the coal mine, It is preferable that the vegetable carbon-based material is partially or wholly covered with the vegetable carbon-based material. As the vegetable carbon-based material, for example, at least one selected from the group consisting of rice husk, rice straw, barley straw, sawdust, and newspaper can be used. In the case of the above-mentioned newspaper, it is preferable to use the paper in wet state in order to generate more smoke. The manufacturing method of the present invention includes a toasting technique in which the fired product is fogged as described above, so that the pores on the surface of the fired product are soot-coated. The soot acts like charcoal to inhibit the growth of noxious bacteria, so that it is possible to inhibit the infiltration of bacteria into soil and planted plants through the pores of the material. Through this, the growth environment of plants can be improved. In addition, the surface of the flowerpot produced through the fogging may have a natural black light, and the aesthetics may be improved.

2 is a flowchart illustrating a method of manufacturing a toasted plastic flower pot according to a second embodiment of the present invention.

Referring to FIG. 2, a method of manufacturing a toasty plastic pot according to a second embodiment of the present invention includes a first step S1 of molding a potted object, a second step S2 of drying the formed object, (S4) for firing the glaze, a fifth step (S5) for firing at 950 to 1,200 占 폚, and a sixth step (S6) for fusing soot on the surface due to fogging .

According to the second embodiment of the present invention shown in FIG. 2, the manufacturing method of the present invention may further include a step of pre-baking and glazing a product before sintering under neutralization conditions, if necessary. In the following description of the second embodiment of the present invention shown in FIG. 2, a detailed description of parts overlapping with those of the first embodiment will be omitted.

According to a second embodiment of the present invention, the object molded in the shape of a flowerpot can be dried and then sintered at 750 to 900 ° C (S3). More preferably, the pre-firing temperature is 800 to 850 ° C. It is possible to obtain a product having improved strength by being fired in the temperature range for 5 to 25 hours. The superficial firing improves the absorbency and strength of the article, thereby facilitating the coloring operation when the glaze is treated on the article.

Next, the glaze can be applied to the preliminarily fired article (S4). Various colors of pollen can be produced through the glaze treatment, and the glaze to be treated can be selected in consideration of the color of the pollen to be produced and the firing temperature. In the manufacturing method according to the present invention, since the firing of the next step is performed under the neutralization condition, it is preferable that the glaze capable of coloring the article without burning during firing under neutralization condition is selected. For example, at least one selected from the group consisting of soda ash, columbite, spodumine, nepheline syenite, ball clay and EPK kaolin may be used, but is not limited thereto. The method of treating the glaze is not particularly limited and may be selected in consideration of the size and shape of the glaze. For example, a dielectric layer can be formed on the object by immersing, spraying or applying the glaze on the object. It is preferable to dry the object having the water-soluble layer formed thereon before firing the javelin to remove moisture.

Next, the glaze-treated article is sintered at a temperature of 950 to 1,200 ° C., and fired. In this step, the components contained in the glaze treated on the article are oxidized or reduced through the javelin firing, and color change of the surface of the article may occur. The oxidative calcination can be carried out by supplying a sufficient amount of air during the calcination. Reduction firing can be performed by raising the temperature and reducing the amount of oxygen supplied at about 900 ° C to supply incomplete combustion. The pollen prepared by the manufacturing method according to the second embodiment of the present invention may further include a step of squeezing the glaze after the pre-firing, thereby exhibiting more various colors and aesthetics on the pollen surface to be produced.

As described above, according to the first and second embodiments of the invention, the method for producing a toasty plastic flowerpot has excellent strength, air permeability and aesthetics and prevents invasion of various harmful bacteria, thereby allowing plants to grow safely and healthily for a long time The pot can be produced. The pollen produced by the above-described method has high indoor decorating effect and forms an environmental condition favorable to the growth of plants, thereby improving the growth and development of planted plants.

Claims (4)

Molding a potted object;
Drying the shaped article;
Calcining the dried material at 750 to 900 占 폚 and sieving the glaze;
Calcining at 950 to 1,200 占 폚 for 15 to 30 hours; And
Firing the fired material from the kiln before firing, and fusing the soot to the surface of the article by covering at least part of the surface with at least one member selected from the group consisting of chaff, straw, sawdust and wet newspaper, The method of producing a potted plastic pot according to claim 1,
Wherein the glaze is at least one selected from the group consisting of chalcogen, spodumine, nepheline syenite and EPK kaolin.
delete delete A potted plastic pot produced by the method of claim 1.