KR101460320B1 - Environment friendly ink for marker pen - Google Patents
Environment friendly ink for marker pen Download PDFInfo
- Publication number
- KR101460320B1 KR101460320B1 KR1020130058983A KR20130058983A KR101460320B1 KR 101460320 B1 KR101460320 B1 KR 101460320B1 KR 1020130058983 A KR1020130058983 A KR 1020130058983A KR 20130058983 A KR20130058983 A KR 20130058983A KR 101460320 B1 KR101460320 B1 KR 101460320B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- ink
- marker pen
- pigment
- Prior art date
Abstract
Description
본 발명은 칠판에 필기를 위해 사용되는 마커펜용 잉크에 관한 것으로, 보다 상세하게는 친환경 마커펜용 잉크에 관한 것이다.
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an ink for a marker pen used for writing on a blackboard, and more particularly to an ink for an eco-friendly marker pen.
마커펜은 칠판에 필기를 위해 사용되는 펜으로서, 내부에 안료를 포함하는 잉크가 있고, 외부로 돌출된 섬유 재질의 펜촉을 구비한다. The marker pen is a pen used for writing on a blackboard. The marker pen has an ink containing a pigment therein, and has a pen tip of a fiber material protruding outward.
마커펜용 잉크는 주로 안료, 저분자량 수지, 이형제 및 용매를 포함한다. 이는 펜촉에서의 잉크 유출을 원활하게 할 수 있고, 칠판에서 용이하게 지울 수 있도록 하기 위함이다.The ink for the marker pen mainly includes a pigment, a low molecular weight resin, a release agent and a solvent. This is to make the ink outflow from the pen tip smooth and to be easily erased from the blackboard.
그러나, 상기와 같은 저분자량 수지를 이용한 마커펜용 잉크를 이용할 경우, 칠판에 필기시 혹은 칠판에서 지울 때 미세한 안료가루가 날려 인체에 유해한 문제점이 있다.
However, when using the ink for a marker pen using such a low-molecular-weight resin as described above, there is a problem that fine powder is blown when writing on the blackboard or erased from the blackboard, which is harmful to the human body.
본 발명에 관련된 배경기술로는 대한민국 등록특허공보 제10-0854649호(2008.08.27. 공고)에 개시된 필기 보드용 잉크펜이 있다.
As a background art related to the present invention, there is an ink pen for a writing board disclosed in Korean Patent Registration No. 10-0854649 (published on Aug. 27, 2008).
본 발명의 목적은 칠판에 필기시 혹은 칠판에서 지울 때 미세한 안료가루가 날리는 것을 억제할 수 있는 친환경 마커펜용 잉크를 제공하는 것이다.
SUMMARY OF THE INVENTION An object of the present invention is to provide an ink for an eco-friendly marker pen capable of suppressing fine pigment powder from being blown when written on a chalkboard or erased from a chalkboard.
상기 하나의 목적을 달성하기 위한 본 발명의 실시예에 따른 친환경 마커펜용 잉크는 용매 100중량부에 대하여, 비프탈레이트계 가소제 10~20중량부, 중량평균분자량이 20,000 이상인 고분자량 수지 5~15중량부, 안료 5~10 중량부, 이형제 2~10중량부 및 오일 1~5중량부를 포함한다. In order to achieve the above object, an ink for an eco-friendly marker pen according to an embodiment of the present invention comprises 10 to 20 parts by weight of a nonphthalate plasticizer, 5 to 15 parts by weight of a high molecular weight resin having a weight average molecular weight of 20,000 or more 5 to 10 parts by weight of pigment, 2 to 10 parts by weight of release agent and 1 to 5 parts by weight of oil.
이때, 상기 오일은 식물성 오일을 이용하는 것이 바람직하다. At this time, the oil is preferably a vegetable oil.
또한, 상기 고분자량 수지는 에틸렌비닐 아세테이트(Ethylene Vinyl Acetate: EVA) 및 폴리비닐부티랄(Poly Vinyl Butyral: PVB) 중 1종 이상을 포함할 수 있다.The high molecular weight resin may include at least one of ethylene vinyl acetate (EVA) and polyvinyl butyral (PVB).
또한, 상기 이형제는 폴리옥시에틸렌 디라우레이트(polyoxyethylene dilaurate), 부틸 스테아레이트(butyl stearate) 및 액상 파라핀 중 1종 이상을 포함할 수 있다. Also, the release agent may include at least one of polyoxyethylene dilaurate, butyl stearate, and liquid paraffin.
또한, 상기 가소제는 벤조에이트계 가소제를 이용하는 것이 바람직하다.
The plasticizer is preferably a benzoate-based plasticizer.
본 발명에 따른 친환경 마커펜용 잉크에 의하면, 우수한 필기성을 제공하며, 특히 필기시 및 지울 때 안료가루가 날리지 않아 인체에 유해함을 억제할 수 있는 친환경성을 제공할 수 있는 장점이 있다.The ink for an eco-friendly marker pen according to the present invention has an advantage that it can provide excellent writing performance, and in particular, it can provide environment-friendliness that can suppress harmfulness to the human body because the pigment powder does not fly at the time of writing and erasing.
본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. 그러나 본 발명은 이하에서 개시되는 실시예들에 의해 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다. 또한, 본 발명을 설명함에 있어 관련된 공지 기술 등이 본 발명의 요지를 흐리게 할 수 있다고 판단되는 경우 그에 관한 자세한 설명은 생략하기로 한다.Advantages and features of the present invention and methods of achieving them will become apparent with reference to the embodiments described in detail below. The present invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art. To fully disclose the scope of the invention to those skilled in the art, and the invention is only defined by the scope of the claims. In the following description, well-known functions or constructions are not described in detail since they would obscure the invention in unnecessary detail.
이하, 본 발명의 바람직한 실시예에 따른 친환경 마커펜용 잉크에 관하여 상세히 설명하면 다음과 같다.
Hereinafter, an ink for an eco-friendly marker pen according to a preferred embodiment of the present invention will be described in detail as follows.
본 발명에 따른 친환경 마커펜용 잉크는 용매, 비프탈레이트계 가소제, 고분자량 수지, 안료, 이형제 및 오일을 포함한다.
The ink for an eco-friendly marker pen according to the present invention includes a solvent, a non-phthalate plasticizer, a high molecular weight resin, a pigment, a release agent and an oil.
용매는 비프탈레이트계 가소제, 고분자량 수지, 안료 등을 분산시킬 수 있는 것이라면 제한없이 이용할 수 있다. 이러한 용매는 아세톤과 같은 케톤계 용매, 이소프로필 알코올과 같은 알코올계 용매 등 공지된 용매를 이용할 수 있다.
The solvent can be used without limitation as long as it can disperse nonphthalate plasticizers, high molecular weight resins, pigments and the like. Such a solvent may be a known solvent such as a ketone-based solvent such as acetone or an alcohol-based solvent such as isopropyl alcohol.
비프탈레이트계 가소제는 수지를 가소화시켜 필기성을 향상시키며, 필기시 및 지울 때 안료가루가 날리지 않도록 하는 역할을 한다. Non-phthalate plasticizers improve the writing performance by plasticizing the resin and prevent the pigment powder from being blown off during writing and erasing.
이러한 비프탈레이트계 가소제는 벤조에이트계 가소제를 이용하는 것이 바람직하다. 일반적인 프탈레이트계 가소제의 경우, 환경 오염, 인체 유해성 등의 문제점이 있다. 비프탈레이트계 가소제는 시트레이트계 가소제와 벤조에이트계 가소제를 고려할 수 있다. 이 중 시트레이트계 가소제의 경우, 가소화 효율이 높지 않은 단점이 있다. 따라서, 비프탈레이트계 가소제 중에서도 친환경성 및 가소화 효율을 고려할 때 벤조에이트계 가소제를 이용하는 것이 가장 바람직하다. 벤조에이트계 가소제는 글리세릴 트리벤조에이트, 트리메틸올프로판 트리 벤조에이트, 트리메틸올 프로판트리벤조에이트 등이 이용될 수 있다.The nonphthalate plasticizer is preferably a benzoate plasticizer. In the case of general phthalate plasticizers, there are problems such as environmental pollution and human harmfulness. Non-phthalate plasticizers may be citrate plasticizers and benzoate plasticizers. Among them, the citrate-based plasticizer has a disadvantage in that the plasticizing efficiency is not high. Therefore, among the non-phthalate plasticizers, it is most preferable to use a benzoate plasticizer in consideration of environment friendliness and plasticization efficiency. As the benzoate-based plasticizer, glyceryl tribenzoate, trimethylol propane tribenzoate, trimethylol propane tribenzoate and the like can be used.
상기 비프탈레이트계 가소제는 용매 100중량부에 대하여, 10~20중량부로 포함되는 것이 바람직하다. 비프탈레이트 가소제의 함량이 10중량부 미만일 경우, 필기성이 저하될 수 있다. 반대로, 비프탈레이트 가소제 함량이 20중량부를 초과하는 경우, 칠판에서 지울 때 잔상이 남는 문제점이 있다.
The nonphthalate plasticizer is preferably contained in an amount of 10 to 20 parts by weight based on 100 parts by weight of the solvent. When the content of the non-phthalate plasticizer is less than 10 parts by weight, the writing performance may be lowered. On the contrary, when the content of the naphthalate plasticizer exceeds 20 parts by weight, there is a problem that afterimage is left on the blackboard.
고분자량 수지는 안료를 코팅하여 적절한 점착성을 갖도록 하여 필기된 상태의 유지 및 지우개에 의해 지워지는 것을 용이하게 하며, 필기시 및 지울 때 안료가루가 날리는 것을 방지하는 역할을 한다. The high molecular weight resin facilitates the maintenance of the written state by erasing the written state and erasing by the eraser by coating the pigment so as to have appropriate adhesiveness, and to prevent the pigment powder from being blown when writing and erasing.
이러한 고분자량 수지는 중량평균분자량이 20,000 이상인 것을 이용하는 것이 바람직하며, 에틸렌비닐 아세테이트(Ethylene Vinyl Acetate: EVA) 및 폴리비닐부티랄(Poly Vinyl Butyral: PVB) 중 1종 이상을 이용할 수 있다.The high molecular weight resin preferably has a weight average molecular weight of 20,000 or more, and at least one of ethylene vinyl acetate (EVA) and polyvinyl butyral (PVB) may be used.
상기 고분자량 수지는 용매 100중량부에 대하여, 5~15중량부로 포함되는 것이 바람직하다. 고분자량 수지의 함량이 5중량부 미만일 경우, 칠판에서 필기된 상태가 지속되기 어려워질 수 있으며, 필기시 및 지울 때 안료가루가 날릴 수 있다. 반대로, 분자량 수지의 함량이 15중량부를 초과하는 경우, 접착력의 증가로 펜촉에서의 잉크 유출이 느려져 필기성이 저하되는 문제점이 있다.
The high molecular weight resin is preferably contained in an amount of 5 to 15 parts by weight based on 100 parts by weight of the solvent. If the content of the high molecular weight resin is less than 5 parts by weight, the state written on the blackboard may become difficult to sustain and the pigment powder may be blown off when written and erased. On the other hand, when the content of the molecular weight resin exceeds 15 parts by weight, an increase in the adhesive force slows the ink outflow in the pen tip, resulting in a problem that writing performance is deteriorated.
안료는 TiO2 백색 안료와 같이, 각종 색상마다 공지된 안료를 이용할 수 있다. 상업적으로는, C.I pigment 시리즈를 이용할 수 있다. The pigment may be a pigment known for each color, such as a TiO 2 white pigment. Commercially, the CI pigment series can be used.
이러한 안료는 용매 100중량부에 대하여, 5~10 중량부로 포함되는 것이 바람직하다. 안료의 함량이 5중량부 미만일 경우, 필기시 선명성이 떨어질 수 있다. 반대로, 안료의 함량이 10중량부를 초과하면 필기성이 저하될 수 있다.
Such a pigment is preferably contained in an amount of 5 to 10 parts by weight based on 100 parts by weight of the solvent. If the content of the pigment is less than 5 parts by weight, sharpness may be deteriorated at the time of writing. On the contrary, if the content of the pigment exceeds 10 parts by weight, the writing performance may be lowered.
이형제는 지울 때 칠판으로부터 용이하게 이형 분리될 수 있도록 하는 역할을 한다. The release agent serves to facilitate release from the board when erasing.
이러한 이형제는 폴리옥시에틸렌 디라우레이트(polyoxyethylene dilaurate), 부틸 스테아레이트(butyl stearate) 및 액상 파라핀 중 1종 이상을 사용할 수 있다.These releasing agents may be at least one selected from the group consisting of polyoxyethylene dilaurate, butyl stearate and liquid paraffin.
상기 이형제는 용매 100중량부에 대하여, 2~10중량부로 포함되는 것이 바람직하다. 이형제의 함량이 2중량부 미만일 경우, 그 첨가 효과가 불충분하다. 반대로, 이형제의 함량이 10중량부를 초과하는 경우, 필기된 상태가 지속되기 어려운 문제점이 있다.
The releasing agent is preferably contained in an amount of 2 to 10 parts by weight based on 100 parts by weight of the solvent. When the content of the releasing agent is less than 2 parts by weight, the effect of the addition is insufficient. On the other hand, when the content of the releasing agent exceeds 10 parts by weight, there is a problem that the written state is difficult to continue.
오일은 잉크 토출을 용이하게 하여, 필기성을 향상시키는 역할을 하며, 부드러운 향기를 제공한다. 또한, 오일은 필기된 잉크가 잔상없이 지워질 수 있도록 한다. The oil facilitates ink ejection, improves writing performance, and provides a soft fragrance. Also, the oil allows the written ink to be erased without afterimage.
이러한 오일은 친환경성을 고려할 때, 달맞이유, 포도씨유 등과 같이 각종 식물로부터 추출된 식물성 오일을 이용하는 것이 바람직하다. Considering environment friendliness, it is preferable to use vegetable oil extracted from various plants such as evening primrose oil, grape seed oil and the like.
상기 오일은 용매 100중량부에 대하여, 1~5중량부로 포함되는 것이 바람직하다. 오일의 함량이 1중량부 미만일 경우, 그 첨가 효과가 불충분하다. 반대로, 오일이 5중량부를 초과하는 경우, 필기시 번짐 등의 현상이 발생하는 문제점이 있다.
The oil is preferably contained in an amount of 1 to 5 parts by weight based on 100 parts by weight of the solvent. When the content of the oil is less than 1 part by weight, the effect of the addition is insufficient. On the contrary, when the oil is more than 5 parts by weight, a phenomenon such as smearing occurs at the time of writing.
실시예Example
이하, 본 발명의 바람직한 실시예를 통해 본 발명의 구성 및 작용을 더욱 상세히 설명하기로 한다. 다만, 이는 본 발명의 바람직한 예시로 제시된 것이며 어떠한 의미로도 이에 의해 본 발명에 제한되는 것으로 해석될 수는 없다.Hereinafter, the configuration and operation of the present invention will be described in more detail with reference to preferred embodiments of the present invention. It should be understood, however, that the present invention is not limited to the disclosed embodiments.
여기에 기재되지 않은 내용은 이 기술 분야에서 숙련된 자이면 충분히 기술적으로 유추할 수 있는 것이므로 그 설명을 생략하기로 한다.
The contents not described here are sufficiently technically inferior to those skilled in the art, and a description thereof will be omitted.
1. 마커펜용 잉크의 제조 1. Preparation of ink for marker pen
(1) 실시예 1(1) Example 1
이소프로필 알콜 100중량부에 대하여, 글리세릴 트리벤조에이트 15중량부, 중량평균분자량이 30,000인 폴리비닐부티랄 10중량부, TiO2 분말 8중량부, 액상 파라핀 5중량부 및 달맞이유 3중량부로 이루어진 마커펜용 잉크를 제조하였다.
15 parts by weight of glyceryl tribenzoate, 10 parts by weight of polyvinyl butyral having a weight average molecular weight of 30,000, 8 parts by weight of TiO2 powder, 5 parts by weight of liquid paraffin and 3 parts by weight of evening primrose oil were added to 100 parts by weight of isopropyl alcohol. To prepare an ink for a marker pen.
(2) 실시예 2(2) Example 2
아세톤 100중량부에 대하여, 트리메틸올 프로판트리벤조에이트 가소제 15중량부, 중량평균분자량이 50,000인 에틸렌비닐 아세테이트 10중량부, TiO2 분말 8중량부, 폴리옥시에틸렌 디라우레이트 5중량부 및 포도씨유 2중량부로 이루어진 마커펜용 잉크를 제조하였다.
15 parts by weight of trimethylolpropane tribenzoate plasticizer, 10 parts by weight of ethylene vinyl acetate having a weight average molecular weight of 50,000, 8 parts by weight of TiO 2 powder, 5 parts by weight of polyoxyethylene dilaurate, 2 parts by weight were prepared.
(3) 비교예 1(3) Comparative Example 1
이소프로필 알콜 100중량부에 대하여, 프탈레이트계 가소제인 DOP(Dioctyl Phthalate) 15중량부, 중량평균분자량이 10,000인 폴리비닐피놀리돈 10중량부, TiO2 분말 8중량부, 폴리옥시에틸렌 디라우레이트 5중량부로 이루어진 마커펜용 잉크를 제조하였다.
15 parts by weight of DOP (Dioctyl Phthalate) as a phthalate plasticizer, 10 parts by weight of polyvinylpyrrolidone having a weight average molecular weight of 10,000, 8 parts by weight of TiO 2 powder, 10 parts by weight of polyoxyethylene dilaurate 5 parts by weight were prepared.
2. 물성 평가 방법2. Property evaluation method
(1) 지움성 시험 확인(1) Check for erasure test
녹색 무광 보드를 바닥에서 70° 각도로 세워놓고, 제조된 잉크를 조립하여 상온과 상대습도 70%에서 직경 3cm 정도의 원으로 그리면서 30cm를 필기한 후 20분 경과한 다음 전용지우개로 약 200g 하중으로 지웠을 때 필기된 잉크가 완전히 제거되는지의 여부로 다음과 같이 판단하였다.A green matte board was laid at an angle of 70 ° from the floor, and the prepared ink was assembled and drawn in a circle with a diameter of 3 cm at a room temperature and relative humidity of 70%. After writing 20 cm, a dedicated eraser was applied at a load of about 200 g It was judged whether or not the written ink was completely removed when erased.
보통 : 필기된 잉크가 완전히 제거되지 않음Normal: Handwritten ink is not removed completely
양호 : 필기된 잉크가 완전히 제거됨
Good: written ink is completely removed
(2) 필기 글자의 건조속도 확인(2) Check the drying speed of handwritten letters
상온과 상대습도 70%에서 녹색 무광 보드에서 마커펜으로 초기부터 필기하는 시간을 측정 후 즉시 필기된 선이 몇 초에 건조되어 지우개에 의하여 몇 초만에 지워지는지 시간을 측정하여 다음과 같이 평가하였다. After measuring the writing time from the beginning with the marker pen on the green matte board at room temperature and relative humidity of 70%, the time taken for the written line to be dried in a few seconds and erased by the eraser in a few seconds was measured and evaluated as follows.
보통 : 5초 이상Medium: more than 5 seconds
양호 : 5초 미만
Good: less than 5 seconds
(3) 필기선의 말림성 확인(3) Checking the curl of writing lines
상온과 상대습도 70%에서 녹색 무광 보드에서 선을 그려 필기한 후 약 20분간 충분히 건조한 다음 하중 약 80g 정도의 힘으로, 문질러서 글자가 말리면서 지워지는지 아니면 칠판에 잉크가 오염되면서 지워지는지 여부를 육안으로 확인하여, 다음과 같이 평가하였다.After drawing a line on a green matte board at room temperature and relative humidity of 70%, dry it thoroughly for about 20 minutes. Then, with a load of about 80 g, rub the ink on the blackboard , And evaluated as follows.
보통 : 칠판에 잉크 잔상이 남음Normal: ink residue left on blackboard
양호 : 칠판에 잉크 잔상이 남지 않음
Good: no ink residue left on the blackboard
3. 물성 평가 결과3. Results of physical property evaluation
실시예 1~2 및 비교예 1에 따라 제조된 마커펜용 잉크를 마커펜(에코지트랙 제조) 내에 충진한 후, 무광 보드(에코지트랙 제조)에 필기를 수행하였으며, 그 결과를 표 1에 나타내었다.The marking pen ink prepared according to Examples 1 and 2 and Comparative Example 1 was filled in a marker pen (manufactured by Eco Paper Co.), and then written on a matte board (Eco Paper Track). The results are shown in Table 1 Respectively.
[표 1][Table 1]
상기 표 1을 참조하면, 실시예 1~2에 따라 제조된 마커펜용 잉크의 경우, 지움성, 건조속도, 말림성 등 모든 물성이 양호하였으며, 더불어 식물성 오일을 이용한 결과 좋은 향과 함께 쉽게 필기가 가능한 효과를 제공할 수 있었으며, 아래 표 2와 같이, 전체적으로 독성이 없는 물질들을 이용함으로서 친환경성이 우수한 장점이 있다.Referring to Table 1, all of the inks for marker pens prepared according to Examples 1 and 2 had good physical properties such as erosion, drying speed and curling ability, As shown in Table 2 below, it is advantageous to use environmentally friendly substances by using materials which are totally non-toxic.
반면, 비교예 1에 따라 제조된 마커펜용 잉크의 경우, 지울 때 칠판에 약간의 흔적이 남는 문제점이 있었으며, 프탈레이트계 가소제를 사용에 따라 친환경성이 다소 떨어진다고 볼 수 있다.
On the other hand, in the case of the ink for marker pen manufactured according to Comparative Example 1, there was a problem that some mark remained on the blackboard when erased, and the eco-friendliness was somewhat lowered by using the phthalate plasticizer.
표 2는 실시예 1~2에 따른 마커펜용 잉크에 유해물질이 있는지 여부를 나타낸 것이다. 유해물질 검출여부 판단은 KS M ISO 3856-1 : 2007 시험법에 의거하였다.Table 2 shows whether there is any harmful substance in the ink for marker pen according to Examples 1 and 2. The determination of whether or not to detect harmful substances was made in accordance with KS M ISO 3856-1: 2007.
[표 2] [Table 2]
본 발명은 실시예를 중심으로 설명하였지만, 당업자의 수준에서 다양한 변경이나 변형을 가할 수 있다. 이러한 변경과 변형이 본 발명의 범위를 벗어나지 않는 한 본 발명에 속한다고 할 수 있다. 따라서 본 발명의 권리범위는 이하에 기재되는 특허청구범위에 의해 판단되어야 할 것이다.While the present invention has been described with reference to exemplary embodiments, it is to be understood that various changes and modifications may be made by those skilled in the art. Such changes and modifications are intended to fall within the scope of the present invention unless they depart from the scope of the present invention. Accordingly, the scope of the present invention should be determined by the following claims.
Claims (5)
필기성 및 지움성 향상을 위하여 용매 100중량부에 대하여, 달맞이유 및 포도씨유 중에서 선택되는 식물성 오일 1~5중량부를 더 포함하는 것을 특징으로 하는 친환경 마커펜용 잉크.10 to 20 parts by weight of at least one of glyceryl tribenzoate and trimethylolpropane tribenzoate, 5 to 15 parts by weight of ethylene vinyl acetate (EVA) having a weight average molecular weight of 20,000 or more, 5 to 10 parts by weight of pigment, 2 to 10 parts by weight of at least one of butyl stearate and liquid paraffin,
Further comprising 1 to 5 parts by weight of a vegetable oil selected from evening primrose oil and grape seed oil based on 100 parts by weight of the solvent for improving handwriting and erasing properties.