KR101227060B1 - Ink composition for board marker - Google Patents

Ink composition for board marker Download PDF

Info

Publication number
KR101227060B1
KR101227060B1 KR1020110019799A KR20110019799A KR101227060B1 KR 101227060 B1 KR101227060 B1 KR 101227060B1 KR 1020110019799 A KR1020110019799 A KR 1020110019799A KR 20110019799 A KR20110019799 A KR 20110019799A KR 101227060 B1 KR101227060 B1 KR 101227060B1
Authority
KR
South Korea
Prior art keywords
weight
parts
ink
eco
board
Prior art date
Application number
KR1020110019799A
Other languages
Korean (ko)
Other versions
KR20120101779A (en
Inventor
전계성
박상은
Original Assignee
(주)하이라인
박상은
전계성
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)하이라인, 박상은, 전계성 filed Critical (주)하이라인
Priority to KR1020110019799A priority Critical patent/KR101227060B1/en
Publication of KR20120101779A publication Critical patent/KR20120101779A/en
Application granted granted Critical
Publication of KR101227060B1 publication Critical patent/KR101227060B1/en

Abstract

본 발명은 반사율을 최소화한 무광 칠판용 친환경 보드마카 잉크에 관한 것으로서, 분자량이 큰 고분자량 수지를 사용하고 이 수지에 점착성을 부여하며 첨가제로 굴절률이 적은 물질을 선택 사용함으로써 보드판이나 칠판에 필기한 것을 지웠을 때 지움성을 좋게 하면서 안료가루가 날리는 현상을 없앨 수 있어 인체 유해요소를 제거한 친환경 보드마카를 생산할 수 있고, 필기면으로부터 잉크가 원활하게 제거되어 잔상이 남지 않는 깨끗함은 물론 잉크가 쉽게 건조되지 않고 필기 후 장시간 경과 후에도 소거를 용이하게 수행할 수 있으며, 칠판의 오염을 방지 및 칠판의 반사율에 영향을 끼치지 않는 특성을 발휘하므로 프로젝터 스크린용으로 사용시 프로젝터를 통해 조사되는 상을 제대로 형성 및 표출시킬 수 있는 반사율을 최소화한 무광 칠판용 친환경 보드마카 잉크에 관한 것이다.The present invention relates to an eco-friendly board marker ink for matte boards with minimal reflectance, and uses high molecular weight resins with high molecular weight, gives adhesiveness to these resins, and uses materials with low refractive index as additives. It can remove the phenomenon of pigment powder while removing the goodness when you erase things, and can produce eco-friendly board maca that removes harmful elements of the human body.In addition, the ink is smoothly removed from the writing surface so that afterimages remain clean and ink easily. It does not dry and can be easily erased even after a long time after writing, and it prevents contamination of the board and does not affect the reflectivity of the board, thus forming an image irradiated through the projector properly when used for a projector screen. For matte blackboards with minimal reflectance It relates to eco-friendly vodka ink.

Description

반사율을 최소화한 무광 칠판용 친환경 보드마카 잉크{INK COMPOSITION FOR BOARD MARKER}Eco-friendly board marker ink for matte boards with minimal reflectance {INK COMPOSITION FOR BOARD MARKER}

본 발명은 보드마카용 잉크 조성물에 관한 것으로서, 더욱 상세하게는 분자량이 큰 수지를 사용하여 안료를 코팅하고 굴절률이 적은 물질(원료)을 선택 사용하며 수지에 점착성을 부여함으로써 보드판이나 칠판에 필기한 것을 지웠을 때 지움성을 좋게 하면서 안료가루가 날리는 현상을 제거할 수 있도록 함은 물론 필기면으로부터 잉크가 원활하게 제거되어 잔상이 남지 않도록 하며 반사율을 최소화한 무광 칠판용 친환경 보드마카 잉크에 관한 것이다.
The present invention relates to an ink composition for a board marker, and more particularly, to coat a pigment using a resin having a high molecular weight, and to select a material (raw material) having a low refractive index, and to give adhesiveness to the resin to write on a board or a blackboard. It relates to an eco-friendly board marker ink for matte boards that minimizes the reflectance and improves the eraseability and eliminates the phenomena of the pigment powder. .

일반적으로 보드마카는 마커펜(marker pen), 마커(marker), 마킹펜(marking pen), 펠트펜(felt pen)이라고도 하며, 자체 잉크 공급원이 있고 폴리에스터나 폴리아크릴레이트 등의 섬유재질 펜촉(nib)이 있는 펜으로서, 안료를 사용해 만든 잉크를 통해 화이트보드 등의 보드판이나 칠판 등에 필기를 가능하게 하면서 이를 쉽게 지울 수 있도록 한 필기도구이다.Generally, board markers are also called marker pens, markers, marking pens, felt pens, have their own ink source, and are made of fiber nibs, such as polyester or polyacrylates. Pen is a writing tool that makes writing on a board or blackboard such as a white board easy to erase with ink made using pigment.

이와 같은 보드마카에 적용된 기존의 보드마카용 잉크는 대부분이 안료와 저분자량 수지를 활용하여 만들어지고 있는데, 이는 보드마카용 잉크에 함유된 안료를 수지로 코팅할 때 저분자량의 수지로 안료에 적합한 양을 코팅하여야만 펜촉에서의 잉크 유출을 원활하게 할 수 있고 지울 때 번짐없이 보드판에서 지워지게 하기 위함이다.Most of the inks for baud markers are made using pigments and low molecular weight resins, which are suitable for pigments with low molecular weight resins when coating pigments contained in inks for pigments with resins. The amount must be coated to smooth out the ink outflow from the pen tip and to remove it from the board without smearing when erased.

하지만, 기존 보드마카용 잉크는 지울 때 미세한 안료가루가 날려 인체에 유해한 환경을 조성시킬 수 있는데, 이는 저분자량 수지와 안료의 사용에 의해 기인되는 것이며, 부연하면 용제가 증발된 상태에서 보드마카로 필기한 것을 지웠을 때 지우개의 섬유면에 잉크에 함유된 이형제(stripping agent)가 흡수되고 최소한의 수지가 코팅된 안료만이 지우개 표면에 남게 되므로 미세한 안료가루가 날리는 현상을 일으키게 되는 것이다.However, the existing ink for board markers can create a harmful environment by blowing off fine pigments when erased, which is caused by the use of low molecular weight resins and pigments. When writing is erased, a stripping agent contained in the ink is absorbed on the fiber surface of the eraser, and only a minimum resin-coated pigment remains on the surface of the eraser, causing fine pigment powder to fly.

또한, 현재 사용하는 칠판(주로 MDF판)은 반사율이 높아 반사광에 의해 피로감을 높이므로 법적으로 반사율을 규제하고 있는 실정에 있으며, 이에 따라 반사율을 줄인 무광 칠판이 개발되어 판서용과 프로젝터 스크린(Projector screen)용으로 겸용해서 사용할 수 있도록 출시되고 있으나, 이러한 칠판에 기존 보드마카용 잉크를 사용했을 때 지움성이 현저하게 떨어지는 문제점이 있다.In addition, the current blackboard (mainly MDF board) has a high reflectance, which increases the fatigue caused by the reflected light, so that the law regulates the reflectivity. Although it is released to be used in combination, but there is a problem that the eraseability is remarkably inferior when using the ink for the existing board marker on the board.

이를 개선하기 위해 이형제(stripping agent)를 더 많이 첨가하게 되는데, 이와 같이 이형제가 과도하게 함유된 보드마카 잉크는 필기한 것을 지웠을 때 칠판을 오염시키는 요인이 되고, 또한 무광 칠판의 반사율을 높이는 작용을 하게 되므로 무광 칠판으로서의 기능을 상실시키는 문제점이 있으며, 프로젝터 조사시 상이 제대로 형성되지 못하는 문제점을 가지고 있다.
To improve this, more stripping agent is added. Thus, vodka ink containing excessive release agent contaminates the board when writing is erased, and also increases the reflectivity of the matte board. There is a problem that the function as a matte blackboard loses, and the image is not properly formed when irradiating the projector.

본 발명은 상술한 문제점 등을 감안하여 안출된 것으로서, 분자량이 큰 수지를 사용하여 안료를 코팅하고 굴절률이 적은 물질(원료)을 선택 사용하며 수지에 점착성을 부여함으로써 보드판이나 칠판에 필기한 것을 지웠을 때 지움성을 좋게 하면서 안료가루가 날리는 현상을 제거할 수 있도록 함은 물론 필기면으로부터 잉크가 원활하게 제거(stripping)되어 잔상이 남지 않도록 하며, 반사율을 최소화한 무광 칠판용 친환경 보드마카 잉크를 제공하는데 그 목적이 있다.The present invention has been made in view of the above-described problems, such as coating a pigment using a resin having a large molecular weight, using a material (raw material) having a low refractive index, and giving adhesive to the resin to support writing on a board or a blackboard. It is an eco-friendly board marker ink for matte boards that minimizes the reflectance and improves ergonomics while removing pigment powder.It also removes ink from the writing surface to prevent afterimages. The purpose is to provide.

본 발명은 필기와 지움의 반복동작에 의해 칠판의 필기면이 오염되는 것을 방지하고 칠판의 반사율에 영향을 끼치지 않도록 하며, 필기 후 장시간 경과 후에도 소거를 용이하게 수행할 수 있는 반사율을 최소화한 무광 칠판용 친환경 보드마카 잉크를 제공하는데 있다.
The present invention prevents the writing surface of the board from being contaminated by the repeated operation of writing and erasing, and does not affect the reflectivity of the board, and minimizes the reflectance to minimize erasure even after a long time after writing. To provide eco-friendly board marker ink for blackboards.

상술한 목적을 달성하기 위한 본 발명의 반사율을 최소화한 무광 칠판용 친환경 보드마카 잉크는, 안료 2~8중량부, 수지 2~8중량부, 용제 65~85중량부, 가소제 5~15중량부, 이형제 1~5중량부, 점착제 0.5~3중량부, 분산제 0.1~1중량부의 조성으로 이루어지되,Eco-friendly board marker ink for matte blackboards with minimal reflectance of the present invention for achieving the above object, pigments 2 to 8 parts by weight, resins 2 to 8 parts by weight, solvents 65 to 85 parts by weight, plasticizer 5 to 15 parts by weight , 1 to 5 parts by weight of the release agent, 0.5 to 3 parts by weight of the pressure-sensitive adhesive, 0.1 to 1 part by weight of the dispersant,

상기 수지는 폴리비닐부티랄(polyvinyl butyral)을 사용하고,The resin uses polyvinyl butyral,

상기 용제는 에탄올(ethanol)과 이소프로필 알코올(isopropyl alcohol)이 혼합된 것을 사용하고,The solvent uses a mixture of ethanol and isopropyl alcohol,

상기 가소제는 디부틸 세바케이트(dibutyl sebacate) 또는 디옥틸 세바케이트(dioctyl sabacate) 중에서 단독 또는 혼합하여 사용하고,The plasticizer is used alone or mixed in dibutyl sebacate or dioctyl sabacate,

상기 이형제는 폴리옥시에틸렌 디라우레이트(polyoxyethylene dilaurate) 또는 부틸 스테아레이트(butyl stearate) 중에서 단독 또는 혼합하여 사용하고,The release agent is used alone or mixed in polyoxyethylene dilaurate or butyl stearate,

상기 점착제는 폴리에틸렌글리콜 모노부틸에테르(polyethyleneglycol monobutylether) 또는 트리에틸렌글리콜 모노부틸에테르(triethyleneglycol monobutylether) 중에서 단독 또는 혼합하여 사용하고,The pressure-sensitive adhesive is used alone or in mixture of polyethyleneglycol monobutylether or triethyleneglycol monobutylether,

상기 분산제는 알콕시레이트 중합체(polymeric alkoxylate) 또는 디에틸아미노에탄올(diethylaminoethanol) 중에서 단독 또는 혼합하여 사용하는 것을 특징으로 한다.The dispersant is characterized in that it is used alone or mixed in an alkoxylate polymer (polymeric alkoxylate) or diethylaminoethanol (diethylaminoethanol).

바람직하게, 분산 안정제로 폴리옥시에틸렌 코코넛지방산(polyoxyethylene coconut fatty acid) 1~5중량부를 더 첨가하여 구성될 수 있다.Preferably, 1 to 5 parts by weight of polyoxyethylene coconut fatty acid may be further added as a dispersion stabilizer.

바람직하게, 증발 억제제로 폴리옥시에틸렌 알킬에테르염(polyoxyethylene alkylether phosphate) 또는 당 에스테르(sugar ester) 중에서 단독 또는 혼합하여 사용하되, 0.1~1중량부를 더 첨가하여 구성될 수 있다.Preferably, the evaporation inhibitor may be used alone or in a mixture of polyoxyethylene alkylether phosphate or sugar ester, but may be added by adding 0.1 to 1 parts by weight.

바람직하게, 상기 용제는 에탄올과 이소프로필 알코올이 중량대비 6:1~8:2의 비율로 혼합된 것을 사용할 수 있다.
Preferably, the solvent may be a mixture of ethanol and isopropyl alcohol in a ratio of 6: 1 to 8: 2 by weight.

본 발명에 따르면, 보드판이나 칠판에 필기한 것을 지웠을 때 지움성을 좋게 하면서 안료가루가 날리는 현상을 없앨 수 있어 인체 유해요소를 제거한 친환경 보드마카를 생산할 수 있고, 필기면으로부터 잉크가 원활하게 제거되어 잔상이 남지 않는 깨끗함은 물론 잉크가 쉽게 건조되지 않고 필기 후 장시간 경과 후에도 소거를 용이하게 수행할 수 있으며, 칠판의 오염을 방지 및 칠판의 반사율에 영향을 끼치지 않는 특성을 발휘하므로 프로젝터 스크린용으로 사용시 프로젝터를 통해 조사되는 상을 제대로 형성 및 표출시킬 수 있으며, 크게 향상된 기능성을 발휘할 수 있는 유용한 효과가 달성될 수 있다.
According to the present invention, it is possible to remove the phenomenon that the pigment powder is blown while improving the eraseability when the writing on the board or blackboard can be removed to produce an eco-friendly board maca remove the harmful elements of the human body, the ink smoothly removed from the writing surface As a result, it is possible to clean the image without leaving an afterimage, and to easily erase the ink after a long time after writing, and to prevent contamination of the blackboard and not affect the reflectivity of the blackboard. In this case, the image irradiated through the projector can be properly formed and displayed, and a useful effect of exerting a greatly improved functionality can be achieved.

본 발명에 대해 바람직한 실시예를 설명하면 다음과 같으며, 이와 같은 상세한 설명을 통해서 본 발명의 목적과 구성 및 그에 따른 특징들을 보다 잘 이해할 수 있게 될 것이다.Preferred embodiments of the present invention will be described as follows, and through this detailed description, it will be possible to better understand the purpose and configuration of the present invention and its features.

본 발명의 실시예에 따른 반사율을 최소화한 무광 칠판용 친환경 보드마카 잉크는 안료와 수지, 용제, 가소제, 이형제, 점착제, 분산제를 포함하여 이루어지는 것으로서,Eco-friendly board marker ink for the matte blackboard with a minimum reflectance according to an embodiment of the present invention comprises a pigment and a resin, a solvent, a plasticizer, a release agent, an adhesive, a dispersant,

안료 2~8중량부, 수지 2~8중량부, 용제 65~85중량부, 가소제 5~15중량부, 이형제 1~5중량부, 점착제 0.5~3중량부, 분산제 0.1~1중량부의 조성으로 이루어진다.In the composition of 2 to 8 parts by weight of pigment, 2 to 8 parts by weight of resin, 65 to 85 parts by weight of solvent, 5 to 15 parts by weight of plasticizer, 1 to 5 parts by weight of release agent, 0.5 to 3 parts by weight of adhesive, and 0.1 to 1 parts by weight of dispersant. Is done.

또한, 분산 안정제 1~5중량부나 증발 억제제 0.1~1중량부를 더 첨가하여 사용할 수 있다.Moreover, 1-5 weight part of dispersion stabilizers and 0.1-1 weight part of evaporation inhibitors can be further added and used.

상기 안료는 잉크에 색상을 부여하기 위한 것으로서, 8중량부를 초과하게 되면 수지의 코팅이 제대로 이루어지지 않아 필기 후 지울 때에 필기면의 오염이 발생하게 되고, 2중량부 미만일 경우에는 색도가 흐려지는 문제점이 발생된다.The pigment is intended to impart a color to the ink, and if the amount exceeds 8 parts by weight, the coating of the resin is not made properly, the writing surface contamination occurs when erased after writing, if less than 2 parts by weight the color is blurred problem Is generated.

이때, 상기 안료로는 보드마카의 특성상 검정색, 빨간색, 파랑색, 녹색 등이 많이 사용되는데, 검정색의 경우 C.I pigment black 7, 빨간색의 경우 C.I pigment red 254, 파랑색의 경우 C.I pigment blue 15:3, 녹색의 경우 C.I pigment green 7 등을 사용할 수 있으며, 이에 특별히 한정되지 않고 다양하게 적용할 수 있다 할 것이다.In this case, as the pigment, a lot of black, red, blue, green, etc. are used in the characteristics of vodka, CI pigment black 7, black, CI pigment red 254, blue, CI pigment blue 15: 3 In the case of green, CI pigment green 7 may be used, and the present invention is not particularly limited thereto.

상기 수지는 분자량이 큰 고분자량 수지를 사용함으로써 안료를 코팅 및 안료가루가 날리는 것을 방지하고 적절한 점착성을 갖게 하여 잉크 유출의 원활함을 도우면서 필기 후 지움성을 좋게 하며 칠판 오염을 방지할 수 있도록 한 것으로서, 8중량부를 초과하게 되면 접착력의 증가로 펜촉에서의 잉크 유출이 느려지고 필기 후 지움성을 나쁘게 할 수 있으며, 2중량부 미만일 경우에는 칠판 오염을 일으킬 수 있다.The resin is a high molecular weight resin having a high molecular weight to prevent the coating and the coating of the pigment from flying, and to have a proper adhesiveness to facilitate the ink outflow, while improving the eraseability after writing and to prevent contamination of the blackboard As one, if more than 8 parts by weight may increase the adhesive force to slow the ink outflow from the nib and worse erase after writing, if less than 2 parts by weight may cause blackboard contamination.

이때, 상기 수지로는 중량평균분자량(Mw) 50,000~100,000 g/mol를 갖는 폴리비닐부티랄(polyvinyl butyral)을 사용함이 바람직하다.In this case, it is preferable to use polyvinyl butyral having a weight average molecular weight (Mw) of 50,000 to 100,000 g / mol.

상기 용제는 수지 및 첨가원료의 용해를 목적으로 함은 물론 부드러운 냄새와 증발을 억제시키는 작용을 위해 사용한 것으로서, 에탄올(ethanol)과 이소프로필 알코올(isopropyl alcohol)을 혼합하여 함께 사용함이 바람직하다.The solvent is used for the purpose of dissolving the resin and the additive raw material as well as the action of suppressing the soft smell and evaporation, it is preferable to use a mixture of ethanol and isopropyl alcohol (isopropyl alcohol).

이때, 에탄올과 이소프로필 알코올은 중량대비 6:1~8:2의 비율로 혼합하여 첨가함이 바람직하다.At this time, ethanol and isopropyl alcohol is preferably added by mixing at a ratio of 6: 1 to 8: 2 by weight.

여기서, 에탄올은 고분자량 수지인 폴리비닐부티랄 수지의 용해 및 부드러운 냄새를 목적으로 사용한 것이며, 이소프로필 알코올은 에탄올과 공비점을 일으켜 증발을 억제시키는 작용을 하게 함과 더불어 기타 첨가원료들의 용해를 목적으로 사용한 것이다.Here, ethanol is used for the dissolution and soft smell of polyvinyl butyral resin, which is a high molecular weight resin, and isopropyl alcohol causes azeotropy with ethanol to inhibit evaporation and dissolve other additives. It was used for the purpose.

상기 가소제는 수지가 가소성을 갖도록 가소화 작용을 하게 함과 더불어 이형 기능을 발휘하도록 함은 물론 칠판의 반사율에 영향을 미치지 않도록 굴절률이 적은 원료를 사용한 것으로서, 디부틸 세바케이트(dibutyl sebacate) 또는 디옥틸 세바케이트(dioctyl sabacate) 중에서 단독 또는 혼합하여 사용할 수 있다.The plasticizer is a plasticizer to plasticize the resin to have a plasticity and to exhibit a release function, as well as using a raw material having a low refractive index so as not to affect the reflectivity of the board, dibutyl sebacate or di It may be used alone or in combination in octyl sabacate.

이때, 상기 가소제는 15중량부를 초과하는 경우 필기면으로부터 잉크를 지운 후 잔여물이 칠판에서 깨끗이 제거되지 않아 번짐을 일으키게 되고, 5중량부 미만일 경우에는 지움성이 나빠지는 문제점이 발생된다.In this case, when the plasticizer exceeds 15 parts by weight, after the ink is erased from the writing surface, the residue is not removed from the board cleanly, causing smearing, and when the amount is less than 5 parts by weight, the problem of deterioration occurs.

상기 이형제는 필기된 잉크가 필기면으로부터 용이하게 이형 분리될 수 있도록 함은 물론 칠판의 반사율에 영향을 미치지 않도록 굴절률이 적은 원료를 사용한 것으로서, 폴리옥시에틸렌 디라우레이트(polyoxyethylene dilaurate) 또는 부틸 스테아레이트(butyl stearate) 중에서 단독 또는 혼합하여 사용할 수 있다.The release agent is a material that has a low refractive index so that the written ink can be easily released from the writing surface as well as not affecting the reflectivity of the board. The release agent is polyoxyethylene dilaurate or butyl stearate. (butyl stearate) can be used alone or in combination.

상기 점착제는 조성 잉크에 적절한 점착성을 부여하여 필기할 때 부착력을 제공함과 아울러 지울 때에는 안료가루가 날리지 않은 상태로 지울 수 있게 하기 위한 것으로서, 폴리에틸렌글리콜 모노부틸에테르(polyethyleneglycol monobutylether) 또는 트리에틸렌글리콜 모노부틸에테르(triethyleneglycol monobutylether) 중에서 단독 또는 혼합하여 사용할 수 있다.The pressure-sensitive adhesive is to provide an adhesive force when writing by giving an appropriate adhesiveness to the composition ink and to be able to erase in a state that the pigment powder does not fly when erased, polyethyleneglycol monobutylether or triethylene glycol monobutyl It may be used alone or in mixture of ether (triethyleneglycol monobutylether).

이때, 상기 점착제는 3중량부를 초과하는 경우 수지의 접착력을 높이므로 지울 때 찌꺼기가 칠판에 붙어 잘 떨어지지 않는 문제점이 발생될 수 있고, 0.5중량부 미만일 경우에는 칠판 오염을 일으킬 우려가 높다.At this time, the pressure-sensitive adhesive increases the adhesive strength of the resin when it exceeds 3 parts by weight may cause a problem that the residue does not stick well to the blackboard when erased, if less than 0.5 parts by weight is likely to cause blackboard contamination.

상기 분산제는 안료 분산과 안정성을 높이기 위해 사용한 것으로서, 졸스퍼스(solsperse)를 사용함이 바람직한데, 알콕시레이트 중합체(polymeric alkoxylate) 또는 디에틸아미노에탄올(diethylaminoethanol) 중에서 단독 또는 혼합하여 사용할 수 있다.The dispersant is used to improve pigment dispersion and stability, and it is preferable to use solsperse, which may be used alone or in a mixture of alkoxylate polymer (polymeric alkoxylate) or diethylaminoethanol.

이때, 상기 분산제는 1중량부를 초과하는 경우 필기된 잉크를 지울 때 번짐 현상으로 칠판을 오염시키는 문제가 발생될 수 있고, 0.1중량부 미만일 경우에는 분산성의 저하로 안료의 분리를 초래할 수 있다.In this case, when the dispersant exceeds 1 part by weight, a problem may occur that contaminates the blackboard with a smearing phenomenon when the written ink is erased, and when the dispersant is less than 0.1 part by weight, the dispersibility may cause separation of the pigment.

또한, 상기 분산 안정제로는 폴리옥시에틸렌 코코넛지방산(polyoxyethylene coconut fatty acid)을 사용함이 바람직하며, 5중량부를 초과할 경우 칠판에 번짐 등의 오염을 발생시킬 수 있고, 1중량부 미만일 경우에는 시간 경과 후 색 분리가 일으날 수 있어 색이 흐려질 우려가 높다.In addition, it is preferable to use polyoxyethylene coconut fatty acid as the dispersion stabilizer, if it exceeds 5 parts by weight can cause contamination such as smear on the blackboard, if less than 1 part by weight There is a high possibility of color blurring after color separation may occur.

상기 증발 억제제는 잉크의 빠른 증발을 방지하여 쉽게 건조되는 것을 방지하기 위한 것으로서, 폴리옥시에틸렌 알킬에테르염(polyoxyethylene alkylether phosphate) 또는 당 에스테르(sugar ester) 중에서 단독 또는 혼합하여 사용할 수 있다.The evaporation inhibitor is for preventing the evaporation of the ink to prevent the drying easily, it may be used alone or mixed in polyoxyethylene alkylether phosphate or sugar ester (sugar ester).

따라서, 상술한 바와 같은 원료들의 조성으로 이루어진 본 발명에 의한 반사율을 최소화한 무광 칠판용 친환경 보드마카 잉크는 분자량이 큰 고분자량 수지를 사용하고 이 수지에 점착성을 부여하며 첨가제(가소제와 이형제)로 굴절률이 적은 물질을 선택하여 사용함에 따라 보드판이나 칠판에 필기한 것을 지웠을 때 지움성을 좋게 하면서 안료가루가 날리는 현상을 제거할 수 있고 필기면으로부터 잉크가 원활하게 제거되어 잔상이 남지 않는 깨끗함 및 친환경 특성의 장점을 제공할 수 있으며, 잉크가 쉽게 건조되지 않고 필기 후 장시간 경과 후에도 소거를 용이하게 수행할 수 있으며, 칠판의 반사율에 영향을 끼치지 않으므로 프로젝터 스크린용으로 사용시 프로젝터를 통해 조사되는 상을 제대로 형성시킬 수 있는 장점을 제공할 수 있다.
Therefore, the eco-friendly board marker ink for matte boards which minimizes the reflectance according to the present invention having the composition of the raw materials as described above uses a high molecular weight resin of high molecular weight, imparts tackiness to the resin, and is used as an additive (plasticizer and release agent). By selecting and using a material with a low refractive index, it is possible to eliminate the phenomenon that pigment powder is blown while improving eraseability when writing on a board or a blackboard, and ink is smoothly removed from the writing surface, leaving no afterimage It can provide the advantages of eco-friendly characteristics, ink is not easily dried, can be easily erased after a long time after writing, and because it does not affect the reflectance of the board, it is irradiated through the projector when used for the projector screen. It can provide the advantage that can form properly.

이상에서 설명한 실시예는 본 발명의 바람직한 실시예를 설명한 것에 불과하고 이러한 실시예에 한정되는 것은 아니며, 본 발명의 기술적 사상과 특허청구범위 내에서 이 기술분야의 당업자에 의하여 다양한 수정과 변형 또는 치환이 이루어질 수 있다 할 것이며, 이는 본 발명의 기술적 범위에 속한다 할 것이다.The embodiments described above are merely illustrative of the preferred embodiments of the present invention and are not limited to these embodiments, and various modifications, changes or substitutions may be made by those skilled in the art within the spirit and scope of the present invention. This may be done, which will belong to the technical scope of the present invention.

Claims (4)

안료 2~8중량부, 수지 2~8중량부, 용제 65~85중량부, 가소제 5~15중량부, 이형제 1~5중량부, 점착제 0.5~3중량부, 분산제 0.1~1중량부의 조성으로 이루어지되,
상기 수지는 폴리비닐부티랄(polyvinyl butyral)을 사용하고,
상기 용제는 에탄올(ethanol)과 이소프로필 알코올(isopropyl alcohol)이 혼합된 것을 사용하고,
상기 가소제는 디부틸 세바케이트(dibutyl sebacate) 또는 디옥틸 세바케이트(dioctyl sabacate) 중에서 단독 또는 혼합하여 사용하고,
상기 이형제는 폴리옥시에틸렌 디라우레이트(polyoxyethylene dilaurate) 또는 부틸 스테아레이트(butyl stearate) 중에서 단독 또는 혼합하여 사용하고,
상기 점착제는 폴리에틸렌글리콜 모노부틸에테르(polyethyleneglycol monobutylether) 또는 트리에틸렌글리콜 모노부틸에테르(triethyleneglycol monobutylether) 중에서 단독 또는 혼합하여 사용하고,
상기 분산제는 알콕시레이트 중합체(polymeric alkoxylate) 또는 디에틸아미노에탄올(diethylaminoethanol) 중에서 단독 또는 혼합하여 사용하는 것을 특징으로 하는 반사율을 최소화한 무광 칠판용 친환경 보드마카 잉크.In the composition of 2 to 8 parts by weight of pigment, 2 to 8 parts by weight of resin, 65 to 85 parts by weight of solvent, 5 to 15 parts by weight of plasticizer, 1 to 5 parts by weight of release agent, 0.5 to 3 parts by weight of adhesive, and 0.1 to 1 parts by weight of dispersant. But
The resin uses polyvinyl butyral,
The solvent uses a mixture of ethanol and isopropyl alcohol,
The plasticizer is used alone or mixed in dibutyl sebacate or dioctyl sabacate,
The release agent is used alone or mixed in polyoxyethylene dilaurate or butyl stearate,
The pressure-sensitive adhesive is used alone or in mixture of polyethyleneglycol monobutylether or triethyleneglycol monobutylether,
The dispersant is an eco-friendly board marker ink for a matte blackboard minimized reflectance, characterized in that used alone or in a mixture of alkoxylate polymer (polymeric alkoxylate) or diethylaminoethanol (diethylaminoethanol). 제 1항에 있어서,
분산 안정제로 폴리옥시에틸렌 코코넛지방산(polyoxyethylene coconut fatty acid) 1~5중량부를 더 첨가할 수 있는 것을 특징으로 하는 반사율을 최소화한 무광 칠판용 친환경 보드마카 잉크.The method of claim 1,
Eco-friendly board marker ink for matte boards with minimal reflectance, characterized in that 1 to 5 parts by weight of polyoxyethylene coconut fatty acid can be added as a dispersion stabilizer. 제 1항에 있어서,
증발 억제제로 폴리옥시에틸렌 알킬에테르염(polyoxyethylene alkylether phosphate) 또는 당 에스테르(sugar ester) 중에서 단독 또는 혼합하여 사용하되, 0.1~1중량부를 더 첨가할 수 있는 것을 특징으로 하는 반사율을 최소화한 무광 칠판용 친환경 보드마카 잉크.The method of claim 1,
As an evaporation inhibitor, it is used alone or in a mixture of polyoxyethylene alkylether phosphate or sugar ester, but it is possible to add 0.1 to 1 parts by weight, and the reflectance minimized for matte blackboard Eco-friendly Vodka Ink. 제 1항에 있어서,
상기 용제는 에탄올과 이소프로필 알코올이 중량대비 6:1~8:2의 비율로 혼합된 것을 특징으로 하는 반사율을 최소화한 무광 칠판용 친환경 보드마카 잉크.The method of claim 1,
The solvent is an eco-friendly board marker ink for matte blackboards with minimal reflectance, characterized in that ethanol and isopropyl alcohol in a ratio of 6: 1 to 8: 2 by weight.
KR1020110019799A 2011-03-07 2011-03-07 Ink composition for board marker KR101227060B1 (en)