KR101302090B1 - the composite of concrete with soil and of metallic slag - Google Patents
the composite of concrete with soil and of metallic slag Download PDFInfo
- Publication number
- KR101302090B1 KR101302090B1 KR20110026329A KR20110026329A KR101302090B1 KR 101302090 B1 KR101302090 B1 KR 101302090B1 KR 20110026329 A KR20110026329 A KR 20110026329A KR 20110026329 A KR20110026329 A KR 20110026329A KR 101302090 B1 KR101302090 B1 KR 101302090B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- soil
- concrete composition
- less
- Prior art date
Abstract
본 발명은 흙과 금속성 슬래그를 주재로 하는 콘크리트 조성물에 관한 것으로, 10㎜ 이하 크기의 흙 800 내지 1200 중량부에 대해, 40㎜ 이하 크기의 철강 슬래그 200 내지 600 중량부, 25㎜ 이하 크기의 쇄석 300 내지 700 중량부, 시멘트 250 내지 450 중량부, 200mesh 이상 크기의 황토 분말 5 내지 20 중량부, 3㎜ 이하 크기의 제오라이트 5 내지 20 중량부, 혼화제 0.75 내지 1.35 중량부, 토양 경화제 0.8 내지 1.2 중량부가 균일하게 혼합된 콘크리트 조성물이 구성되어, 상기 콘크리트 조성물을 이용하여, 인공어초, 테트라포트, 인공해림초와 같은 바다투입물 및 호안블록 등으로 제공하여, 철강 슬래그와 동 슬래그와 같은 금속성 슬래그로 인해서 강도가 우수하고, 자원을 재활용하며, 콘크리트 조성물에 의해 자연친화적이고, 철강 슬래그는 수중에 철 농도를 높이고, 수질을 개선할 수 있는 것이다.The present invention relates to a concrete composition mainly composed of soil and metallic slag, 200 to 600 parts by weight of steel slag of 40 mm or less, crushed stone of 25 mm or less with respect to 800 to 1200 parts by weight of soil of 10 mm or less 300 to 700 parts by weight, cement 250 to 450 parts by weight, 5 to 20 parts by weight of ocher powder of 200 mesh or more, 5 to 20 parts by weight of zeolite of 3 mm or less, 0.75 to 1.35 parts by weight of admixture, 0.8 to 1.2 parts by weight of soil hardener An additional uniformly mixed concrete composition is constructed, by using the concrete composition, and provided as sea inputs such as artificial reefs, tetrapots, artificial seaweeds and raft blocks, due to the metal slag such as steel slag and copper slag Excellent strength, recycling resources, nature friendly by concrete composition, steel slag increases iron concentration in water, The will to improve.
Description
본 발명은 흙과 금속성 슬래그를 주재로 하는 콘크리트 조성물에 관한 것으로, 10㎜ 이하 크기의 흙 800 내지 1200 중량부에 대해, 40㎜ 이하 크기의 철강 슬래그 200 내지 600 중량부, 25㎜ 이하 크기의 쇄석 300 내지 700 중량부, 시멘트 250 내지 450 중량부, 200mesh 이상 크기의 황토 분말 5 내지 20 중량부, 3㎜ 이하 크기의 제오라이트 5 내지 20 중량부, 혼화제 0.75 내지 1.35 중량부, 토양 경화제 0.8 내지 1.2 중량부가 균일하게 혼합된 콘크리트 조성물이 구성되어, 상기 콘크리트 조성물을 이용하여, 인공어초, 테트라포트, 인공해림초와 같은 바다투입물 및 호안블록 등으로 제공하여, 철강 슬래그와 동 슬래그와 같은 금속성 슬래그로 인해서 강도가 우수하고, 자원을 재활용하며, 콘크리트 조성물에 의해 자연친화적이고, 철강 슬래그는 수중에 철 농도를 높이고, 수질을 개선할 수 있는 것이다.
The present invention relates to a concrete composition mainly composed of soil and metallic slag, 200 to 600 parts by weight of steel slag of 40 mm or less, crushed stone of 25 mm or less with respect to 800 to 1200 parts by weight of soil of 10 mm or less 300 to 700 parts by weight, cement 250 to 450 parts by weight, 5 to 20 parts by weight of ocher powder of 200 mesh or more, 5 to 20 parts by weight of zeolite of 3 mm or less, 0.75 to 1.35 parts by weight of admixture, 0.8 to 1.2 parts by weight of soil hardener An additional uniformly mixed concrete composition is constructed, by using the concrete composition, and provided as sea inputs such as artificial reefs, tetrapots, artificial seaweeds and raft blocks, due to the metal slag such as steel slag and copper slag Excellent strength, recycling resources, nature friendly by concrete composition, steel slag increases iron concentration in water, The will to improve.
일반적으로 콘크리트는 시멘트가 물과 반응하여 굳어지는 수화반응을 이용하여 시멘트에 모래와 자갈, 골재 따위를 적당히 섞고 물에 반죽한 혼합물을 말하는 것으로, 만드는 방법이 간단하고 내구성이 커서 토목 공사나 건축의 주요 재료로 사용되며, 순수한 콘크리트는 인장력에 약하기 때문에, 주로 철근을 이용하여 보강하며, 이러한 콘크리트를 이용하여, 주택, 건물 등의 건축 구조물은 물론, 댐이나 도로포장·교량 등의 토목 공사는 물론, 개·관수로관이나 호안블록에 이용하거나, 또는, 인공어초, 인공해림초, 테트라포트 등과 같은 일정 강도를 가진 바다투입물에 사용되고 있다.
In general, concrete refers to a mixture of cement, sand, gravel, aggregate, etc. mixed with water and kneaded in water by using a hydration reaction in which cement reacts with water, and the method of making concrete is simple and durable. It is used as a main material, and pure concrete is weak in tensile strength, so it is mainly reinforced with reinforcing bars. Using this concrete, as well as civil works such as dams, road pavements and bridges, as well as building structures such as houses and buildings In addition, it is used for open-water irrigation pipes and shore banks, or for sea input having a certain strength such as artificial reefs, artificial seaweeds, and tetraports.
아울러, 바다의 해조류는, 다른 수중 생물의 먹이와 서식지를 제공하고, 이산화탄소(CO2)를 흡수하여 지구 온난화 방지에 도움이 된다.
In addition, sea algae provide food and habitat for other aquatic organisms and absorb carbon dioxide (CO 2 ) to help prevent global warming.
그러나 종래 콘크리트의 경우 주재료가 시멘트를 사용하는데, 이들을 시공한 후에는 이들로부터 발생하는 시멘트의 독성(예를 라돈과 같은 기타 중금속)들이 배출되어, 강가의 호안블록이나 바다투입물에 사용하면서, 식물, 어류, 동물 등에 유해한 문제점이 있었다.
However, in the case of conventional concrete, the main material is cement, and after construction, the toxins of cement (e.g., other heavy metals such as radon) generated from them are discharged, and used in river banks and sea inputs, plants, There was a problem that is harmful to fish, animals and the like.
아울러, 일반 콘크리트로 토목 구조물로 사용하면 시간이 지나면서 레이턴스의 발생으로 표면이 깨끗하지 못한 문제점이 있었으며, 종래 콘크리트를 폐기할 때에는, 환경에 대한 유해성으로 별로로 수집하여 폐기처분하여야 하므로, 처리 비용이 높고, 매립시에는 각종 환경 오염을 유발하는 문제점이 있으므로, 친환경적인 콘크리트 조성물의 개발이 요구되고 있다.
In addition, when used as a civil engineering structure as a general concrete, there was a problem that the surface is not clean due to the generation of latencies over time, and when the conventional concrete is disposed, it must be collected and disposed of separately as hazardous to the environment, Since the cost is high and there is a problem of causing various environmental pollution during landfill, the development of environmentally friendly concrete composition is required.
또한, 근래에 바다에 성게가 급증하는 현상(해조류는 성게의 먹이가 되므로, 성게가 급증하면 해조류의 생육에 큰 타격이 된다)이나, 바닷물의 철 농도 감소 등으로 인해서 해조류가 감소하거나 사멸하고, 이에 따라, 해조의 이산화탄소의 흡수율 및 수중 생물이 감소하게 되므로, 해조류의 번식과 생육을 위해서 해조류에 인위적으로 철 성분을 제공하는 방법이 필요하다.
In addition, in recent years, sea urchins are rapidly increasing in the sea (seaweed is a prey of sea urchins, so the increase in sea urchins are a major blow to the growth of seaweeds), or sea salt is reduced or killed due to a decrease in the iron concentration of the sea, Accordingly, the rate of absorption of carbon dioxide and aquatic life of seaweeds are reduced, and thus, there is a need for a method of artificially providing iron to seaweeds for breeding and growing seaweeds.
따라서 본 발명은 상기의 문제점을 해결하고자, 흙 800 내지 1200 중량부에 대해, 철강 슬래그 또는 동 슬래그 200 내지 600 중량부, 쇄석 300 내지 700 중량부, 시멘트 250 내지 450 중량부, 황토 분말 5 내지 20 중량부, 제오라이트 5 내지 20 중량부, 혼화제 0.75 내지 1.35 중량부, 토양 경화제 0.8 내지 1.2 중량부가 균일하게 혼합된 콘크리트 조성물이 구성되어, 상기 콘크리트 조성물을 이용하여, 인공어초, 테트라포트, 인공해림초와 같은 바다투입물은 물론, 호안블록 등으로 제공하여, 철강 슬래그와 동 슬래그와 같은 금속 슬래그로 강도가 우수하고, 자원을 재활용하며, 콘크리트 조성물에 의해 자연친화적이고, 수중에서 생태계의 환경을 개선할 수 있는 것이다.
Therefore, the present invention to solve the above problems, with respect to soil 800 to 1200 parts by weight, steel slag or copper slag 200 to 600 parts by weight, crushed stone 300 to 700 parts by weight, cement 250 to 450 parts by weight, ocher powder 5 to 20 Part by weight, 5 to 20 parts by weight of zeolite, 0.75 to 1.35 parts by weight of admixture, 0.8 to 1.2 parts by weight of soil hardener is composed of a concrete composition, artificial reefs, tetrapots, artificial seaweeds using the concrete composition As well as providing sea inputs such as sea block, such as steel slag and metal slag such as copper slag, it has high strength, recycles resources, is eco-friendly by concrete composition, and improves the environment of the ecosystem underwater. It can be.
또, 상기 콘크리트 조성물에는 흙 800 내지 1200 중량부에 대해, 바텀 애쉬 200 내지 300 중량부가 추가되어, 강도를 높이면서 부피 대비 중량을 줄일 수 있도록 한다.In addition, to the concrete composition 800 to 1200 parts by weight of the soil, 200 to 300 parts by weight of the bottom ash is added, so as to reduce the weight to volume while increasing the strength.
추가로, 상기 콘크리트 조성물에는 흙 800 내지 1200 중량부에 대해, 천연광물, 일라이트, 천매암, 게르마늄, 맥반석 중에서 적어도 하나 선택한 기능성 물질 1 내지 5 중량부가 추가되어, 수중에서 생태계 환경을 더욱 개선할 수 있도록 한다.In addition, the concrete composition may be added to 1 to 5 parts by weight of a functional material selected from at least one selected from natural minerals, illite, feldspar, germanium and elvanite with respect to 800 to 1200 parts by weight of soil, further improving the ecosystem environment in water. Make sure
그리고 상기 콘크리트 조성물에는 흙 800 내지 1200 중량부에 대해, 속경성 고강도 혼화제 5 내지 25 중량부가 추가되어, 콘크리트 조성물로 제품을 만들 때, 경화 속도를 높여 제조 시간을 단축하고, 콘크리트 조성물로 만든 제품의 강도를 높이도록 한다.
And the concrete composition is added to 5 to 25 parts by weight of a high-speed high strength admixture with respect to 800 to 1200 parts by weight of soil, when making a product with a concrete composition, to increase the curing speed to shorten the manufacturing time, of the product made of the concrete composition Try to increase the strength.
이와 같이 본 발명은, 흙 800 내지 1200 중량부에 대해, 철강 슬래그 또는 동 슬래그 200 내지 600 중량부, 쇄석 300 내지 700 중량부, 시멘트 250 내지 450 중량부, 황토 분말 5 내지 20 중량부, 제오라이트 5 내지 20 중량부, 혼화제 0.75 내지 1.35 중량부, 토양 경화제 0.8 내지 1.2 중량부가 균일하게 혼합된 콘크리트 조성물이 구성되어, 상기 콘크리트 조성물을 이용하여, 인공어초, 테트라포트, 인공해림초와 같은 바다투입물은 물론, 호안블록 등으로 제공하여, 철강 슬래그와 동 슬래그와 같은 금속 슬래그로 강도가 우수하고, 자원을 재활용하며, 콘크리트 조성물에 의해 자연친화적이고, 수중에서 생태계의 환경을 개선하는 효과가 있다.
As described above, the present invention is based on 800 to 1200 parts by weight of soil, 200 to 600 parts by weight of steel slag or copper slag, 300 to 700 parts by weight of crushed stone, 250 to 450 parts by weight of cement, 5 to 20 parts by weight of ocher powder, zeolite 5 To 20 parts by weight, admixture 0.75 to 1.35 parts by weight, a concrete composition of 0.8 to 1.2 parts by weight of the soil hardener is composed uniformly, by using the concrete composition, sea inputs such as artificial reefs, tetrapots, artificial seaweeds Of course, it is provided as a raft block, such as steel slag and metal slag, such as copper slag, the strength is excellent, recycling resources, nature-friendly by the concrete composition, there is an effect of improving the environment of the ecosystem underwater.
또, 상기 콘크리트 조성물에는 흙 800 내지 1200 중량부에 대해, 바텀 애쉬 200 내지 300 중량부가 추가되어, 강도를 높이면서 부피 대비 중량이 낮은 효과가 있다.
In addition, to the concrete composition 800 to 1200 parts by weight of the soil, the bottom ash 200 to 300 parts by weight is added, there is an effect of lowering the weight to volume while increasing the strength.
추가로, 상기 콘크리트 조성물에는 흙 800 내지 1200 중량부에 대해, 천연광물, 일라이트, 천매암, 게르마늄, 맥반석 중에서 적어도 하나 선택한 기능성 물질 1 내지 5 중량부가 추가되어, 수중에서 생태계 환경을 더욱 개선하는 효과가 있다.
In addition, the concrete composition is added to 1 to 5 parts by weight of a functional material selected from at least one selected from natural minerals, illite, chalcedony, germanium, ganbanite with respect to 800 to 1200 parts by weight of soil, further improving the ecosystem environment in water There is.
그리고 상기 콘크리트 조성물에는 흙 800 내지 1200 중량부에 대해, 속경성 고강도 혼화제 5 내지 25 중량부가 추가되어, 콘크리트 조성물로 제품을 만들 때, 경화 속도를 높여 제조 시간을 단축하고, 콘크리트 조성물로 만든 제품의 강도가 높은 효과가 있다.
And the concrete composition is added to 5 to 25 parts by weight of a high-speed high strength admixture with respect to 800 to 1200 parts by weight of soil, when making a product with a concrete composition, to increase the curing speed to shorten the manufacturing time, of the product made of the concrete composition It has a high strength effect.
본 발명은 흙과 금속성 슬래그를 주재로 하는 콘크리트 조성물에 관한 것으로, 10㎜ 이하 크기의 흙 800 내지 1200 중량부에 대해, 40㎜ 이하 크기의 철강 슬래그 200 내지 600 중량부, 25㎜ 이하 크기의 쇄석 300 내지 700 중량부, 시멘트 250 내지 450 중량부, 200mesh 이상 크기의 황토 분말 5 내지 20 중량부, 3㎜ 이하 크기의 제오라이트 5 내지 20 중량부, 혼화제 0.75 내지 1.35 중량부, 토양 경화제 0.8 내지 1.2 중량부가 균일하게 혼합된 콘크리트 조성물이 구성되어, 상기 콘크리트 조성물을 이용하여, 인공어초, 테트라포트, 인공해림초와 같은 바다투입물 및 호안블록 등으로 제공하여, 철강 슬래그와 동 슬래그와 같은 금속성 슬래그로 인해서 강도가 우수하고, 자원을 재활용하며, 콘크리트 조성물에 의해 자연친화적이고, 철강 슬래그는 수중에 철 농도를 높이고, 수질을 개선할 수 있는 것이다.
The present invention relates to a concrete composition mainly composed of soil and metallic slag, 200 to 600 parts by weight of steel slag of 40 mm or less, crushed stone of 25 mm or less with respect to 800 to 1200 parts by weight of soil of 10 mm or less 300 to 700 parts by weight, cement 250 to 450 parts by weight, 5 to 20 parts by weight of ocher powder of 200 mesh or more, 5 to 20 parts by weight of zeolite of 3 mm or less, 0.75 to 1.35 parts by weight of admixture, 0.8 to 1.2 parts by weight of soil hardener An additional uniformly mixed concrete composition is constructed, by using the concrete composition, and provided as sea inputs such as artificial reefs, tetrapots, artificial seaweeds and raft blocks, due to the metal slag such as steel slag and copper slag Excellent strength, recycling resources, nature friendly by concrete composition, steel slag increases iron concentration in water, The will to improve.
본 발명에 따른 콘크리트 조성물과 그 콘크리트 조성물로 제조된 바다투입물 및 호안블록을 순차로 설명하면 다음과 같다.
Referring to the concrete composition according to the present invention and the sea inputs and shore blocks prepared from the concrete composition in order as follows.
먼저, 본 발명에 따른 콘크리트 조성물은, 10㎜ 이하 크기의 흙 800 내지 1200 중량부에 대해, 40㎜ 이하 크기의 금속성 슬래그 200 내지 600 중량부, 25㎜ 이하 크기의 쇄석 300 내지 700 중량부, 시멘트 250 내지 450 중량부, 200mesh 이상 크기의 황토 분말 5 내지 20 중량부, 3㎜ 이하 크기의 제오라이트 5 내지 20 중량부, 혼화제 0.75 내지 1.35 중량부, 토양 경화제 0.8 내지 1.2 중량부가 균일하게 혼합되어 구성한다.First, the concrete composition according to the present invention, 200 to 600 parts by weight of metal slag of 40 mm or less, 300 to 700 parts by weight of crushed stone of 25 mm or less, with respect to 800 to 1200 parts by weight of soil of 10 mm or less, cement 250 to 450 parts by weight, 5 to 20 parts by weight of ocher powder of 200 mesh or more, 5 to 20 parts by weight of zeolite of 3 mm or less, 0.75 to 1.35 parts by weight of admixture, 0.8 to 1.2 parts by weight of soil hardener .
상기 콘크리트 조성물 중에서, 금속성 슬래그는, 철강 슬래그 동 슬래그 중에서 선택하여 적용한다.In the concrete composition, metallic slag is selected from steel slag copper slag and applied.
추가로, 상기 콘크리트 조성물에는 흙 800 내지 1200 중량부에 대해, 40㎜ 이하 크기의 바텀 애쉬 200 내지 300 중량부가 추가되어, 쇄석과 같은 기능을 하면서, 부피 대비 중량을 줄일 수 있다.
In addition, the concrete composition may be added to 200 to 300 parts by weight of the bottom ash of 40 mm or less with respect to 800 to 1200 parts by weight of soil, while functioning as crushed stone, it is possible to reduce the weight to volume.
그리고 상기 콘크리트 조성물에는 흙 800 내지 1200 중량부에 대해, 천연광물, 일라이트, 천매암, 게르마늄, 맥반석 중에서 적어도 하나 선택한 기능성 물질 1 내지 5 중량부가 추가되어, 수중에서 생태계 환경을 더욱 개선할 수 있도록 하는데, 상기 기능성 물질은 5㎜ 이하 크기를 가지는 것으로 사용한다.
And to the concrete composition 800 to 1200 parts by weight of soil, 1 to 5 parts by weight of a functional material selected from at least one selected from natural minerals, illite, chalcedony, germanium, ganbanite is added, to further improve the ecosystem environment in water The functional material is used to have a size of 5 mm or less.
또한, 상기 콘크리트 조성물에는 흙 800 내지 1200 중량부에 대해, 속경성 고강도 혼화제 5 내지 25 중량부가 추가되어, 콘크리트 조성물과 물이 혼합·교반된 모르타르로 제품을 만들 때, 경화 속도를 높여 제조 시간을 단축하고, 콘크리트 조성물로 만든 제품의 강도를 높이도록 한다.
In addition, 5 to 25 parts by weight of the high-hardness high strength admixture is added to the concrete composition from 800 to 1200 parts by weight of soil, and when the product is made of mortar mixed and stirred with the concrete composition, the curing speed is increased to increase the production time. Shorten and increase the strength of products made of concrete compositions.
아울러, 콘크리트 조성물에 대한 배합 비율과 혼합 예시를 다음 [표 1]에 나타내었다.
In addition, the mixing ratio and mixing examples for the concrete composition are shown in the following [Table 1].
Kinds
(중량부)Compounding ratio
(Parts by weight)
(㎏)Formulation example
(Kg)
(크기, 형태)Remarks
(Size, shape)
기본
구성물
basic
edifice
Metallic slag
200 to 600
200 to 600
40 mm or less
선택 추가
구성물
Add selection
edifice
또한, 상기 포함되는 콘크리트 조성물에 대해서 간단히 설명하면 다음과 같다.In addition, the concrete composition included above will be described briefly as follows.
먼저, 흙은 일반적으로 구할 수 있는 것으로 사용하되, 주로, 10㎜ 이하 크기의 마사토를 사용하는 것이 바람직한데, 상기 마사토(진사토-眞砂土, 화강토)는, 화강암이 풍화하여 모래로 변한 흙(풍화 화강토)을 말하며, 친환경적인 특징이 있다.
First of all, the soil is generally available, but preferably, it is preferable to use a Masato having a size of 10 mm or less. The Masato (Jinsato- 眞 砂土, granite soil) is a granite that is weathered and turned into sand. It refers to soil (weather granite soil) and has eco-friendly features.
또, 금속성 슬래그는 금속 물질의 제련 과정에서 발생하는 부산물(찌꺼기, 천연 광석에서 특정한 금속을 채치하고 남은 무기질 부산물)이고, 이러한 금속성 슬래그는 몇 가지 과정을 거쳐, 골재 대용으로 사용되어 콘크리트 제품의 밀도와 강도를 높이는데 사용하고 있으며, 우선, 철강 슬래그는 쇳물로부터 금속을 빼내고 남은 부산물을 말하는 것으로, 시중에 골재 대용으로 사용할 수 있는 철강 슬래그가 판매되고 있으며, 이러한 철강 슬래그가 콘크리트 조성물에 포함되고, 그 콘크리트 조성물로 만들어진 제품(바다투입물, 호안블록 등)이 수중에 있으면, 철강 슬래그의 철 성분이 녹아서 수중의 철 농도를 높이는 특징이 있으며, 40㎜ 이하 크기를 사용하는 것이 바람직하다.In addition, metallic slag is a by-product generated from the smelting process of metallic materials (remains, inorganic by-products left after smelting certain metals from natural ore) .The metallic slag is used as a substitute for aggregates through several processes, and the density of concrete products It is used to increase the strength of steel slag. First of all, steel slag refers to a by-product remaining after removing metal from water, and steel slag that can be used as a substitute for aggregate is sold on the market, and such steel slag is included in a concrete composition. If a product made of the concrete composition (sea input, shore block, etc.) is in the water, the iron component of the steel slag is melted to increase the iron concentration in the water, and it is preferable to use a size of 40 mm or less.
그리고 동 슬래그는 동의 제련 과정에서 발생하는 부산물로, 골재 대용으로 사용할 수 있는 동 슬래그가 판매되고 있으며, 이러한 동 슬래그는 40㎜ 이하 크기를 사용하는 것이 바람직하다.
And copper slag is a by-product of the copper smelting process, copper slag that can be used as a substitute for the sale is sold, such a copper slag is preferred to use a size of 40mm or less.
또한, 쇄석은 잘게 부숴서 깨뜨린 것으로, 25㎜ 이하 크기의 크기를 사용하여, 밀도를 높이고 강도를 높인다.
In addition, the crushed stone is crushed and broken, using a size of 25 mm or less, to increase the density and increase the strength.
그리고 시멘트는 석회, 실리카, 알루미나, 산화철 등이 주성분인 포틀랜드 시멘트를 사용한다.
As cement, portland cement, which is mainly composed of lime, silica, alumina and iron oxide, is used.
그리고 황토 분말은, 일반적인 황토를 200 메시(mesh) 이상으로 분말화 한 것으로, 상기 황토는, 실리카(SiO2), 알루미나(Al2O3), 철분, 마그네슘(Mg), 나트륨(Na), 카리 등 수많은 무기질이 함유된 미세입자로, 다량의 미네랄을 포함하고, 원적외선을 다량 방사하며, 축적된 토양 미생물과 효소작용에 의한 항균·방충·탈취효과 및 오염 물질 제거 효과가 있다.
The ocher powder is a powder of general ocher at 200 mesh or more, and the ocher is composed of silica (SiO 2 ), alumina (Al 2 O 3 ), iron, magnesium (Mg), sodium (Na), It is a fine particle containing many minerals such as Kari, and contains a large amount of minerals, emits a large amount of far infrared rays, and has antibacterial, insect repellent, deodorizing effect and pollutant removal effect by accumulated soil microorganism and enzyme action.
그리고 제오라이트(Zeolite)는 신생대 3기의 화산회가 열수에 의한 속성작용을 받아 생성된 광물로, 물 분자가 결정수 형태로 구조 중에 존재하는 함수(含水) 알루미늄의 규산염 광물이며, 상기 구조 중에 존재하는 결정수는, 일반 구조수와는 달리 분자로 존재하기 때문에 제오라이트를 비석수라 불리기도 하는데, 이는 가열에 따라 탈수하여도 그 구조는 파괴되지 않고, 물분자가 있던 곳은 그대로 세공으로 남아 마치 스펀지와 같은 구조가 되었다가, 다시 그 세공에 수분이나 가스를 흡착하여 원상으로 복귀하는데, 이러한 물리적 흡착성과 화학적인 양이온 치환작용 인해서, 해양 오염 방지와 수질 정화 등에 효과가 있으며, 3㎜ 이하 크기의 크기를 사용하는 것이 바람직하다.
Zeolite is a mineral produced by the volcanic ash of the three Epoch volcanoes under the action of hot water, and is a silicate mineral of hydrous aluminum in which water molecules exist in the form of crystalline water. Unlike regular structured water, crystalline water is called zeolite because it exists as a molecule, and even if it is dehydrated by heating, its structure is not destroyed, and the water molecules remain as pores. After the same structure, it adsorbs water or gas into the pores and returns to the original state. Due to the physical adsorption and chemical cation substitution, it is effective for preventing marine pollution and water purification, and the size of 3 mm or less It is preferable to use.
그리고 혼화제는 토목용 조성물과 물과 혼합·교반한 후에, 경화(硬化) 전후의 성질을 개량하기 위한 목적으로 사용된다.
And a admixture is used for the purpose of improving the property before and after hardening after mixing and stirring with a composition for civil engineering and water.
이어서, 선택으로 추가되는 바텀 애쉬, 천연광물, 일라이트, 천매암를 순차로 설명하면 다음과 같다.Subsequently, the bottom ash, natural mineral, illite, and natural stone added as an option will be described sequentially.
먼저, 바텀 애쉬(Bottom Ash)는 석탄이 연소할 때 노안에서 직접 보일러 바닥으로 떨어지는 재를 말하는 것(산업자원부 고시 제 2004 - 32호)으로, 규산질이 60％ 이상 함유된 다공질로 형성되어 가벼운(경량) 특성이 있으며, 40㎜ 이하의 크기를 사용하는 것이 바람직하다.
First, Bottom Ash refers to ash falling directly from the presbyopia to the boiler floor when coal is burned (Ministry of Commerce, Industry and Energy Notice No. 2004-32), which is formed of porous material containing more than 60% of siliceous and light ( Lightweight), and it is preferable to use a size of 40 mm or less.
또한, 천연광물은, 자연에서 채취되는 천연 광물 중에 수질 정화에 우수한 천연광물을 5㎜ 이하로 분쇄하여 사용하는데, 그중에서도 국내 회사인 가이아스톤에서 생산되는 가이아토나 가이아토파우더를 투입하는데, 이러한 가이아스톤 제품은, 항균 작용으로 물의 부패를 막고, 수질을 정화하는 효과가 있다.
In addition, natural minerals are used to crush natural minerals, which are excellent in water quality, from natural minerals collected from nature to 5 mm or less, and among them, the Gaia Stones or the Gaia Powders, which are produced by Gaia Stone, a domestic company, are introduced. The product has the effect of preventing the decay of water and purifying the water quality by antibacterial action.
또, 일라이트(illite)는, 단사정계에 속하는 운모족 광물로, 알루미늄이 풍부한 이질(泥質) 또는 응회암질(凝灰岩質) 퇴적암 중에 산출되며, 열수성(熱水性) 광상모암의 변질광물로서 산출되는데, 일라이트는, 구리와 아연, 철, 납 등 중금속의 흡착률이 뛰어나고, 원적외선을 방사하므로, 오염된 수질을 정화하는 효과가 월등한 것으로 알려져 있다.
In addition, illite is a mica-based mineral belonging to a monoclinic system, and is produced in aluminum-rich heterogeneous or tuff sedimentary rocks, and is a metamorphic mineral of hydrothermal mineral deposit. It is known that the illite has an excellent adsorption rate of heavy metals such as copper, zinc, iron, and lead, and emits far infrared rays, so that the effect of purifying contaminated water is excellent.
그리고 천매암(千枚岩, phyllite)은 석영, 세리사이트질운모, 녹니석으로 구성된 엽리상 변성암의 한 종류로, 천매암의 변성 정도는 슬레이트와 운모 편암 사이 단계이고, 주성분은 석영, 견운모, 흑운모, 녹니석 등이고, 잎 모양으로 부서지는 성질이 있는 암석인데, 내부에 나노 크기의 미세한 공간들을 많이 형성하고 있어 물리적 흡착력과 화학적 양이온 치완 작용 등이 아주 탁월하며, 수중 생물에 다양한 미네랄을 공급하고, 유해 물질을 흡착, 중화하는 특징이 있다.Phyllite is a type of foliated metamorphic rock composed of quartz, sericite mica, and chlorite. The degree of metamorphosis is between slate and mica schist, and its main components are quartz, mica, biotite, and chlorite. It is a rock shaped like a leaf, which is broken in the shape of a leaf. It has many nano-sized microcavities inside, so it has excellent physical adsorption and chemical cation repair effect. It supplies various minerals to aquatic organisms, It is characterized by adsorption and neutralization.
다음으로, 게르마늄과 맥반석은 모두 원적외선을 방출하고, 맥반석의 경우, 유해물질을 제거하고, 중금속 분해 작용을 하며, 수중에서 미네랄을 공급(미네랄 용출)해주며, 세균 번식을 억제하는 특징이 있다.
Next, both germanium and elvan rock emit far infrared rays, and elvan rock removes harmful substances, decomposes heavy metals, supplies minerals (mineral elution) in water, and inhibits bacterial growth.
상기와 같은 특징이 있는 재료로 구성되는 콘크리트 조성물은, 단순한 모양, 인공어초, 테트라포트, 인공해림초와 같은 바다투입물, 또는, 호안블록 등의 물건으로 제조되는데, 간단히 제조 방법을 설명하면, 상기 콘크리트 조성물에 물을 부어 충분히 교반한 모르타르를 구비하고, 만들려고 하는 형상의 거푸집 내부에 철근을 배근하며, 상기 구비한 모르타르를 거푸집에 타설하면서 충분히 다진 다음, 일정 시간을 양생한 후에 탈형하면, 바다투입물, 호안블록의 제조가 완료된다.
Concrete composition composed of a material having the characteristics as described above, a simple shape, artificial reefs, tetrapots, sea inputs, such as artificial seaweeds, or is prepared from an article, such as a raft block, briefly described the manufacturing method, Water is poured into the concrete composition, and the mortar is sufficiently stirred, the reinforcing bar is placed inside the formwork to be made, the mortar is sufficiently chopped while pouring the provided mortar into the formwork, and after curing for a predetermined time, The preparation of the inputs, the relief block is completed.
이렇게 본 발명에 따른 콘크리트 조성물로 제조하는 바다투입물은, 구형, 원통형, 삼각뿔형 형상과 같은 간단한 모양으로 제조하거나, 테트라포트(tetrapod), 인공해림초 등으로 제조되어 바다에 투입하여 사용하는데, 친환경적이며, 콘크리트 조성물 중에서 철강 슬래그의 철분 성분이 바닷물에 녹아들어 철 농도를 증가시켜 해조류의 생육을 돕고, 기타 바다 생물의 서식처가 되도록 하며, 기타 조성물에 의해 항균 작용, 오염 방지 및 수질 정화 효과를 가진다.
Thus, the sea input prepared by the concrete composition according to the present invention is produced in a simple shape, such as spherical, cylindrical, triangular pyramidal shape, or manufactured by using tetrapod, artificial seaweed grass, etc. In the concrete composition, the iron component of the steel slag is dissolved in seawater to increase the iron concentration to help the growth of seaweeds, to be a habitat for other sea creatures, and to have antimicrobial effect, pollution prevention and water purification effect by other compositions. .
또한, 본 발명에 따른 콘크리트 조성물로 제조하는 호안블록은, 해안가, 강가 및 부둣가 등에 설치되어 사용되는데, 친환경적이고, 주변의 오염물을 흡착하면서 수질을 정화하는 효과가 있다.
In addition, the revetment block prepared from the concrete composition according to the present invention is used to be installed on the shore, riverside and dockside, etc., is environmentally friendly, and has the effect of purifying the water quality while adsorbing the surrounding contaminants.
이외에도, 상기 콘크리트 조성물은, 직육면체, 원기둥 모양 등 다양한 모양으로 제작되어, 수족관 및 어항에 투입하여 사용하거나, 또는, 바다, 저수지 또는 호수 등에 그대로 투입하거나, 또는, 수면 근처에서 떠 있는 상태를 유지하도록, 공과 같이 속이 빈 구, 또는 발포폴리스티렌과 같이 물에 뜨는 부체(浮體, floating body)에 연결하여 수심이 깊은 호수, 저수지 등에 투입하면, 수중의 오염물을 흡착하여 수질을 정화할 수 있는 것이다.In addition, the concrete composition is manufactured in various shapes such as a rectangular parallelepiped and a cylindrical shape, and used in an aquarium and a fishbowl, or used as it is in the sea, a reservoir or a lake, or to remain floating near the surface of the water. If it is connected to a hollow body such as a ball or a floating body such as expanded polystyrene and floats in a deep lake or reservoir, it can adsorb contaminants in the water to purify the water quality.
Claims (6)