KR101262358B1 - Coating composit - Google Patents

Coating composit Download PDF

Info

Publication number
KR101262358B1
KR101262358B1 KR1020120124638A KR20120124638A KR101262358B1 KR 101262358 B1 KR101262358 B1 KR 101262358B1 KR 1020120124638 A KR1020120124638 A KR 1020120124638A KR 20120124638 A KR20120124638 A KR 20120124638A KR 101262358 B1 KR101262358 B1 KR 101262358B1
Authority
KR
South Korea
Prior art keywords
weight
agent
pearl
metallic powder
joint coating
Prior art date
Application number
KR1020120124638A
Other languages
Korean (ko)
Inventor
강정아
Original Assignee
강정아
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 강정아 filed Critical 강정아
Priority to KR1020120124638A priority Critical patent/KR101262358B1/en
Application granted granted Critical
Publication of KR101262358B1 publication Critical patent/KR101262358B1/en

Abstract

PURPOSE: A mono-fluid type aqueous masonry joint coating agent using various colored metallic powder is provided to prevent tile lifting, to increase adhesiveness between a tile and a joint and to prevent moisture or water from penetrating into the joint. CONSTITUTION: A mono-fluid type aqueous masonry joint coating agent comprises 55-80 wt% of aqueous acrylic copolymer resin, 10-35 wt% of pearl, 5-10 wt% of mineral for anion or infrared ray discharge, 1-3 wt% of antimicrobial agent, and 0.5-1.5 wt% of thickening agent and has a viscosity of 500-2000. The aqueous acrylic copolymer resin comprises 4 wt% of butyl acrylate monomer, 18 wt% of methyl methacrylate monomer, 18 wt% of 2-ethyl acrylate, 2 wt% of methacrylic acid, 2 wt% of 2-nydroxy methyl methacrylate, 1 wt% of anionic surfactant, and 55 wt% of water.

Description

색상이 다양한 메탈릭 파우더을 이용한 1액 형 수성타입 줄눈 코팅제{COATING COMPOSIT}1-component water-based joint coating using various metallic powders {COATING COMPOSIT}

본 발명은 색상이 다양한 메탈릭 파우더(소위, 빤짝이 펄)을 이용한 1액 형 수성타입 줄눈 코팅제에 관한 것으로The present invention relates to a one-component aqueous joint coating using a variety of colors of metallic powder (so-called pearl).

타일과 타일 사이 줄눈에 코팅하여 타일의 들뜸 현상을 방지함과 동시에 타일과 줄눈의 결합력을 증가시키고, 타일 줄눈 사이로 스며드는 습기 내지 물을 차단하는 방수기능을 가지고, 색상이 다양하며 아름답고 미려하며, 장기간 오랜 시간 햇빛에 노출될 경우에 발생하는 황변 현상을 방지하고, 타일 줄눈 사이로 침투하는 세균 및 곰팡이를 방지하고, 몸에 유익한 음이온 및 원적외선이 방출되며 누구나 쉽게 시공 할 수 있는 색상이 다양한 메탈릭 파우더(빤짝이 펄)을 이용한 1액 형 수성타입 줄눈 코팅제에 관한 것을 목적으로 한다.
It is coated on the joint between the tiles to prevent the lifting of the tiles and at the same time increases the bonding between the tiles and the joints, and it has a waterproof function to block moisture or water that penetrates between the tiles joints. It prevents yellowing caused by long time exposure to the sun, prevents bacteria and mold penetrating between tile joints, releases beneficial anion and far infrared rays to the body, and is a colorful metallic powder that can be easily installed by anyone. A one-component aqueous joint coating using pearl).

타일 줄눈 시공은 타일과 타일 사이의 아주 좁은 간격(약 1-3 mm)을 충진재로 메우는 작업이다. 타일 줄눈은 사용에 의해 오염이 되는 데, 줄눈 오염에 의해 각종 곰팡이, 물때 등 타일이 주는 정결한 미감이 크게 손상된다. 이러한 경우, 통상적으로 타일 전체를 다시 시공하는데, 이는 경제적으로 큰 손실을 야기한다.Tile joint construction is the filling of very narrow gaps (about 1-3 mm) between tiles with filler. Tile joints are contaminated by use, and the joint contamination greatly damages the clean taste of tiles such as various molds and scales. In this case, the entire tile is typically rebuilt, which causes a large economic loss.

따라서 타일 전체를 다시 시공하여야 하는 불편함을 제거하면서도, 타일줄눈을 쉽게 재생시키며, 다양한 색상을 추가 할 수 있는 건축용 조성물에 대한 요구가 당 업계에 있다.
Therefore, there is a need in the art for a construction composition that can easily regenerate tile joints and add various colors while eliminating the inconvenience of having to rebuild the whole tile.

특히 종래에 출시된 제품들은 백색이나 회색 그리고 시멘트 성분으로 국한되어 있어 소비자의 선택에 부각되어 지지 않는 단점이 많다 하겠다.
In particular, conventionally released products are limited to white, gray, and cement components, so there are many disadvantages that do not stand out to the consumer's choice.

이러한 문제점을 개선하고자 다양한 줄눈제가 개발되고 있는데, 이 예로 대한민국 등록특허 제10-0934561호를 들 수 있다. 대한민국 등록특허 제10-0934561호는 주제부로 10~15중량%의 에폭시 수지, 0.1~0.2중량%의 분산제, 0.05~0.1중량%의 소포제, 0.1~0.5중량%의 가소제, 0.5~1.0중량%의 유화제, 3~5중량%의 이산화티탄, 74~80중량%의 무기충전필러, 3~5중량%의 희석용제와, 경화제로 82~85중량%의 에폭시 수지 경화제, 0.5~1.0중량%의 분산제, 14.2~17.2중량%의 물로 구성되며 주제부와 경화제부를 중량비로 주제 95 : 경화제 5의 비율로 혼합하여 사용하는 것을 특징으로 한다.
Various joint agents are being developed to improve this problem, for example, Korean Patent No. 10-0934561. Republic of Korea Patent No. 10-0934561 is a main portion of 10-15% by weight epoxy resin, 0.1-0.2% by weight dispersant, 0.05-0.1% by weight antifoaming agent, 0.1-0.5% by weight plasticizer, 0.5-1.0% by weight of Emulsifier, 3-5 wt% titanium dioxide, 74-80 wt% inorganic filler, 3-5 wt% diluent, 82-85 wt% epoxy resin curing agent, 0.5-1.0 wt% dispersant , 14.2 ~ 17.2% by weight of water, characterized in that the main part and the curing agent used by mixing the ratio of the main portion 95: curing agent 5 in weight ratio.

그러나 상기 특허는 압착 강도나 부착강도가 무용제에폭시 비하여 현저히 떨어지고 겨울철에는 수성 제품이라 영하에서는 시공이 되지 않으며 경화시간이 길어 건설현장에서 시공 시 속도가 느린 문제점이 있으며, 햇빛 등에 장기간 노출될 경우에 발생하는 황변 현상을 방지할 수 있는 사이클로 알리파틱 아민계 경화제를 사용하나 상기 경화제로는 베란다 등과 같이 장기간 햇빛에 노출되는 타일에 적용하는데 한계가 있고, 또한 색상이 백색이나 회색에 국한되어 있어 색상이 다양하지 못해 상품성이 떨어진다는 한계가 있었다.
However, the patent shows that the compressive strength and the adhesive strength are significantly lower than those of solvent-free, and are water-based products in winter, so they are not constructed under subzero, and the curing time is long, so the construction is slow in construction and long-term exposure to sunlight. Cyclo aliphatic amine-based curing agent that can prevent the yellowing phenomenon is used, but the curing agent has a limit to apply to tiles exposed to sunlight for a long time, such as a veranda, and the color is limited to white or gray, so the color varies There was a limit that the merchandise falls.

이에 본 출원인은 상기 등록특허의 한계점을 고려하여 새로운 타입의 줄눈보수제를 개발하여 대한민국 등록특허 제10-1115011호로 등록을 받은바 있다.In this regard, the present applicant has developed a new type of joint repair agent in consideration of the limitations of the registered patent and has been registered as Korean Patent No. 10-1115011.

상기 등록특허 제10-1115011호는 앞서 언급된 줄눈보수제인 등록특허 제10-0934561호에 나타난 문제점을 해결하였다는 장점을 가지고 있으나, 본 출원인이 사용해본 결과 다음과 같은 문제점을 발견하게 되었다.The registered patent No. 10-1115011 has the advantage of solving the problems shown in the above-mentioned joint repair agent No. 10-0934561, but the present inventors have found the following problems.

물론 하기 문제점은 등록특허 제10-0934561호를 비롯한 시중에 소개되고 있는 줄눈보수제에서도 나타나는 문제점이다.
Of course, the following problem is a problem that appears in the joint repair system that is introduced on the market, including registered patent No. 10-0934561.

즉, 상기 앞서 언급된 줄눈제들을 비롯하여 기존 줄눈제들은 주제와 경화제로 구성된 2액형 타입의 수성 또는 유성 에폭시나, 폴리우레탄, 폴리에스테르 폴리올 수지 종류로써, 사용 시 주제와 경화제의 비율을 맞추기 위하여 반드시 전자저울이 필요하며, 만약 비율이 맞지 않으면 경화가 되지 않아 일반 소비자가 사용하기에는 너무 어려워 현실적으로는 전문적으로 시공 하는 시공 팀에게 막대한 비용을 들여 의뢰를 하는 실정이며, 유성의 경우 인체에 유해한 voc가 방출되며, 불쾌한 냄새가 나는 단점이 있고, 오랜 기간 동안 햇빛에 노출될 경우에 도포된 줄눈제에 황변 현상이 발생하고, 타일 사이에 도포된 줄눈제가 너무 강하여 외부 충격에 의하여 파손되는 문제점이 있고, 습기나 물기가 있는 곳에서는 시공이 절대적으로 불가능하며, 한번 시공한 줄눈제가 경화가 되면 수정이나 보수가 불가능 한 실정이다.That is, the above-mentioned joint agents, including the above-mentioned joint agents, are two-component aqueous or oil-based epoxy, polyurethane, or polyester polyol resin types composed of a main agent and a hardener, and in order to match the ratio of the main agent and the hardener in use. Electronic scales are required, and if the ratio is not correct, it is hard to be used by the general consumer because it is not cured, and in reality, it is requested to pay a huge cost to the construction team professionally.In the case of meteor, harmful voc is emitted. It has a disadvantage of having an unpleasant smell, yellowing phenomenon occurs in the applied joints when exposed to sunlight for a long time, the joints applied between the tiles is too strong, there is a problem that is damaged by external impact, moisture It is absolutely impossible to install in the place where there is water. Joint I is the actual circumstances that a modification or repair is not possible when the curing.

또한 주로 액체타입이라 바닥면만 시공이 가능 하며, 벽체는 시공이 불가능한 실정이다.
In addition, it is mainly liquid type, so it can be installed only on the floor, and the wall cannot be installed.

그 외에도 등록특허 제10-1140454호(이하, 비교예 1), 공개특허 제10-2011-138901호(이하, 비교예 2), 공개특허 제10-2012-92536호(이하, 비교예 3), 등록특허 제10-776691호(이하, 비교예 4), 등록특허 제10-495043호(이하, 비교예 5) 등이 있으나 상기 언급된 한계점이 있는 코팅제들이다.
In addition, Patent No. 10-1140454 (hereinafter, Comparative Example 1), Patent Publication No. 10-2011-138901 (hereinafter, Comparative Example 2), Patent Publication No. 10-2012-92536 (hereinafter, Comparative Example 3) , Patent No. 10-776691 (hereinafter referred to as Comparative Example 4), Patent No. 10-495043 (hereinafter referred to as Comparative Example 5) and the like, but are the coatings having the above-mentioned limitations.

이에 당업계에서는 타일과 타일 사이에 도포된 백시멘트와 상기 도포될 타일 줄눈 코팅제를 소형 튜브 용기에 충진 하여 사용함으로서 접착이 용이하고, 시공 후 언제든 수정이나 보수가 용이하며, 습기나 물기가 있어도 시공이 가능하고 1액 형 수성타입이라 누구나 쉽게 시공 할 수 있으며,Therefore, in the art, by filling a small tube container with the back cement applied between the tile and the tile joint coating to be applied to the small tube container, it is easy to adhere, easy to modify or repair at any time after construction, and even when there is moisture or moisture This is a one-component aqueous type, so anyone can easily construct it.

또한 일반 안료에서 표현 할 수 없는 메탈릭 파우더(빤짝이 펄)를 사용함으로써, 타일 색상과 같은 색상의 코팅제를 제공 할 수 있으며, 인체에 유해한 성분이 없으며, 바닥 및 벽면까지 시공이 가능한 색상이 다양한 메탈릭 파우더(빤짝이 펄)를 이용한 1액형 수성타입 줄눈 코팅제의 도입이 절실히 요구되고 있는 실정이다.
In addition, by using metallic powder (Pearl Pearl) that cannot be expressed in general pigments, it is possible to provide a coating of the same color as the tile color, there is no harmful component to the human body, and a variety of metallic powders that can be applied to the floor and walls There is an urgent need for the introduction of one-part aqueous type joint coatings using (Pearl Pearl).

본 발명은 상기한 문제점을 해결하기 위한 것으로, The present invention is to solve the above problems,

본 발명의 제1목적은 욕실, 현관, 베란다, 주방, 거실 등 타일과 타일 사이의 줄눈표면에 ?게 코팅하는 타일 줄눈 코팅제로 액체 타입 또는 크림 타입으로 제조 가능한 1액 형 수성타입 줄눈 코팅제를 제공하는 것이며,
The first object of the present invention is a tile joint coating for coating on the joint surface between tiles such as bathroom, entrance, porch, kitchen, living room, etc. to provide a one-component aqueous type joint coating which can be manufactured in liquid or cream type. To do that,

본 발명의 제2목적은 남녀노소 누구나 쉽게 시공 할 수 있는 소형 튜브 타입으로 제조되어 시공성이 편하며, 내수성, 내구성, 내후성, 강도, 접착성, 유연성, 내약품성 및 내오염성으로 인해 물기나 습기가 있는 곳에서도 시공이 가능한 1액 형 수성타입 줄눈 코팅제를 제공 하는 것이며,The second object of the present invention is manufactured in a small tube type that can be easily installed by anyone, men and women of all ages, the construction is comfortable, water and moisture due to water resistance, durability, weather resistance, strength, adhesiveness, flexibility, chemical resistance and pollution resistance It is to provide a one-component water-based joint coating that can be installed anywhere.

본 발명의 제3목적은 백색이나 회색 및 각종 안료에서 표현 할 수 없는 색상을 메탈릭 파우더(빤짝이 펄)을 사용함으로서 햇볕이나 불빛에 의하여 보는 각도에 따라 줄눈 색상이 변함으로 화려하고 아름다운 줄눈을 누구나 누릴 수 있는 색상이 다양한 메탈릭 파우더(빤짝이 펄)을 이용한 1액 형 수성타입 줄눈 코팅제를 제공하는 것이며,
The third object of the present invention is to enjoy a colorful and beautiful joint by changing the color of the joint according to the angle seen by sunlight or light by using metallic powder (Pearl Pearl) in colors that cannot be expressed in white, gray and various pigments. It is to provide a one-component water-based joint coating using metallic powder (Pearl Pearl) in various colors.

본 발명의 제4목적은 일상생활 중에 인체에 유익한 음이온이 대량 방출되는 토르마린 광물질을 첨가함으로 공기를 정화하고 깨끗하게 유지하여 주는 역할을 하고, 원적외선이 대량 방출 되는 황토나 게르마늄 같은 광물을 첨가는 것을 제공 하는 것이며,The fourth object of the present invention serves to purify and keep the air clean by adding tourmaline minerals in which a large amount of negative ions are released to the human body during daily life, and to provide minerals such as ocher or germanium in which large infrared rays are emitted. To do that,

본 발명의 제5목적은 각종 세균 및 곰팡이 방지를 위하여 유기계 항균제 혼합물과 무기계인 나노화된 셀레늄 이온 물질이 첨가된 1액 형 수성타입 줄눈 코팅제를 제공 하는 것이다.
A fifth object of the present invention is to provide a one-component aqueous type joint coating agent to which an organic antimicrobial mixture and an inorganic nanonized selenium ion material are added to prevent various bacteria and fungi.

상기 언급된 목적을 달성하기 위한 본 발명의 줄눈 코팅제는 다음과 같이 이루어진다.
The joint coating of the present invention for achieving the above-mentioned object is made as follows.

즉 본 발명의 액체 타입 타일 줄눈 코팅제는 1액형으로 이루어진 것으로, 수성 폴리머수지 55-80 중량%, 펄색상 구현을 위한 펄제 10~35 중량%, 토르마린, 음이온 또는 원적외선 방출을 위한 광물 5-10중량%; 항균제 1-3중량%, 점도를 높이는 증점제 0.5-1.5중량%을 혼합한 1액 형 조성물인 것을 특징으로 한다.
That is, the liquid-type tile joint coating agent of the present invention is composed of one-component, 55-80% by weight of the aqueous polymer resin, 10-35% by weight of the pearlescent agent for pearl color, tourmaline, anion or mineral 5-10 for the far infrared emission %; It is a 1-component composition which mixed 1-3 weight% of antibacterial agents and 0.5-1.5 weight% of thickeners which raise a viscosity.

또한, 본 발명의 크림 타입의 타일 줄눈 코팅제는 1액형으로 이루어진 것으로, 수성 폴리머수지 15-30중량%, 체질안료 40-60중량%, 펄색상 구현을 위한 펄제 10-35 중량%, 음이온 또는 원적외선 방출을 위한 광물 5-10중량%; 항균제 1-3중량%, 점도를 높이는 증점제 0.5-1.5중량%을 혼합한 1액 형 조성물을 튜브용기에 충진 하는 것을 특징으로 한다.
In addition, the cream-type tile joint coating of the present invention is composed of one-component, 15-30% by weight of an aqueous polymer resin, 40-60% by weight pigment, 10-35% by weight of a pearl agent for implementing a pearl color, anion or far infrared rays 5-10% by weight mineral for emission; It is characterized in that the tube container is filled with a one-component composition containing 1-3 wt% of the antimicrobial agent and 0.5-1.5 wt% of the thickener to increase the viscosity.

또한, 본 발명에서 액체 및 크림 타입에 사용하는 광물로는 토르마린인 것으로 음이온이 1㎡당 500-1000개 정도 방출되는 것을 사용하며, 또 다른 광물의 예로 들 수 있는 원적의선 및 탈취 기능이 있는 황토나 게르마늄 같은 광물질을 5-10중량%을 포함하여 이루어진 것을 특징으로 한다.
In addition, the mineral used in the liquid and cream type in the present invention is a tourmaline is used that emits about 500-1000 anion per 1㎡, and there is a far-line and deodorizing function, such as another mineral It is characterized by including 5-10% by weight of minerals such as ocher or germanium.

또한, 본 발명에서 액체 및 크림 타입에 사용하는 펄제로서 메탈릭 파우더(빤짝이 펄)은 1/256 ~ 1/32mm 사이의 입자를 사용함을 특징으로 한다.
In addition, in the present invention, as a pearl agent used in the liquid and cream type, metallic powder (Pearl Pearl) is characterized by using particles between 1/256 ~ 1 / 32mm.

또한, 본 발명의 크림 타입에 사용하는 체질 안료로서 글라스 비드(Class Beads)는 알갱이가 일정한 곡면을 취하고 있어 때가 쉽게 끼지 않게 하는 기능을 함과 동시에 코팅제가 밑으로 처지지 않게 하는 기능을 하는 것으로, 상기 글라스비드의 입자 크기는 200메쉬-3000메쉬를 사용하는 것을 특징으로 한다.
In addition, glass beads (Class Beads) as a sieving pigment used in the cream type of the present invention has a function of preventing grains from slipping down while the grains have a constant curved surface. The particle size of the glass beads is characterized in that using 200 mesh-3000 mesh.

본 발명은 욕실, 현관, 베란다, 주방, 거실 등 타일과 타일 사이의 줄눈에 ?게 코팅하는 제품으로 액체 타입 또는 크림 타입으로 제조가 가능함으로 사용자가 선택의 폭을 넓힐 수 있으며, The present invention is a product that can be coated in the joint between the tile, such as bathroom, porch, porch, kitchen, living room, etc. can be manufactured in liquid type or cream type, the user can expand the choice,

튜브 용기에 충전한 1액 형 수성 타입이라 기술이 없는 사람도 쉽고 간단하게 시공이 가능 하고, 시공 중이나 시공 후 수정이나 보수가용이 하며, 시공 면이 습기나 물기가 있어도 시공이 가능하며, 타일 색상에 맞추어 다양한 색을 표현함으로 줄눈을 아름답고 화려하게 연출 할 수 있으며, It is a one-component aqueous type filled in a tube container, so even people without technology can easily and simply apply it, and it can be modified or repaired during or after construction, and it can be applied even if the surface is wet or wet. By expressing a variety of colors to fit the joints beautiful and colorful,

인체에 유익한 음이온 및 원적의선이 방출되며,Good negative ions and enemy lines are released to the human body,

점도를 조절하여 바닥은 물론 벽면 시공 시 흘러내리지 않아 사용이 가능 하며, 유성 제품보다 건조가 1/3 이상 빠르게 설계된 제품으로, By adjusting the viscosity, it can be used because it doesn't flow down when installing floors and walls, and it is designed to dry more than 1/3 faster than oil-based products.

종국적으로 상품성을 극대화시킬 수 있다는 효과를 가진다.
Finally, it has the effect of maximizing the merchandise.

이하 본 발명의 1액 형 수성타입 줄눈 코팅제에 대해 보다 구체적으로 설명하도록 한다.
Hereinafter will be described in more detail with respect to the one-component aqueous joint coating of the present invention.

색상이 다양한 메탈릭 파우더(빤짝이 펄)을 이용한 1액 형 수성타입 줄눈 코팅제를 제조하기 위한 본 발명은 수성 아크릴 공중합물 수지를 액체 타입과 크림 타입 두 가지로 나뉘어 제조가 가능하고, 이 두 가지는 각 중량비의 배합 비율로 혼합하여 튜브 용기에 충전하여 사용 가능하다.
The present invention for preparing a one-component aqueous type joint coating agent using a variety of color metallic powder (Pearl Pearl) can be prepared by dividing an aqueous acrylic copolymer resin into two types, a liquid type and a cream type, each of which has a weight ratio It can be mixed and used in the mixing ratio of the tube container.

이하 자세히 설명한다.
This will be described in detail below.

실시예Example 1 One

색상이 다양한 메탈릭 파우더(빤짝이 펄)를 이용한 1액 형 수성타입 줄눈 코팅제 1-part water-based joint coating using a variety of metallic powder (Pearl Pearl)

(1) 액체 타입(1) liquid type

액체 타입 타일 줄눈 코팅제는 1액형으로 이루어진 수성 폴리머 수지로서 수성 아크릴 공중합체 55-80 중량%, 펄제로서 10-35 중량%, 원적외선 또는 이온 방사물질인 광물 5-10 중량%; 항균제 1-3 중량%, 점도를 높이는 증점제 0.5-1.5 중량%을 혼합한 1액 형 조성물을 완성한다.
Liquid-type tile joint coatings comprise 55-80% by weight of an aqueous acrylic copolymer as a one-part aqueous polymer resin, 10-35% by weight as a pearl agent, and 5-10% by weight of minerals which are far infrared or ion emitting materials; A one-component composition containing 1-3 wt% of the antimicrobial agent and 0.5-1.5 wt% of the thickener to increase the viscosity is completed.

상기 액체 타입의 줄눈 코팅제는 줄눈 부분이 밑으로 관통되지 않는 곳에 주로 사용하며, 바닥은 물론 벽면 시공시 흘러내리지 않게 점도가 500-2000 CP정도로 이루어진 것이며, 유성 제품보다 건조가 1/3이상 빠르게 이루어진 것이다.
The liquid type joint coating agent is mainly used where the joint is not penetrated downward, and has a viscosity of about 500-2000 CP so as not to flow down during construction of the wall as well as the bottom, and drying is more than 1/3 faster than oil-based products. will be.

실시예Example 2 2

(2) 크림타입(2) Cream type

크림 타입의 타일 줄눈 코팅제는 1액형으로 이루어진 수성 폴리머 수지로서 수성 아크릴 공중합체 15~30 중량%, 체질 안료로서 글라스 비드(Class Beads) 40-60 중량%, 펄제 10-35 중량%, 음이온 또는 원적외선이 방출되는 광물 5-10 중량%; 항균제 1-3 중량%, 점도를 높이는 증점제 0.5-1.5 중량%을 혼합한 1액 형 조성물을 완성한다.
The cream-type tile joint coating agent is a one-component aqueous polymer resin 15-30% by weight of an aqueous acrylic copolymer, 40-60% by weight of glass beads (Class Beads) as a sieving pigment, 10-35% by weight of a pearlescent agent, anion or far infrared rays 5-10% by weight of the released minerals; A one-component composition containing 1-3 wt% of the antimicrobial agent and 0.5-1.5 wt% of the thickener to increase the viscosity is completed.

상기 액체타입의 줄눈코팅제와 차이점은 체질 안료로서 글라스 비드를 더 참가하여 사용하는데, 글라스 비드(Glass Beads)는 알갱이가 일정한 곡면을 취하고 있어 때가 쉽게 끼지 않게 하는 기능을 함과 동시에 줄눈제가 밑으로 처지는 것을 방지하는 효과가 기대되며, The difference from the liquid type joint coating agent is that the glass bead is used as a sieving pigment. Particularly, glass beads (Glass Beads) have a function of preventing grains from being caught easily, and at the same time, the joint agent sags downward. It is expected to prevent the effect

점도는 2000-5000CP정도로 이루어진 것이며 역시 유성 제품보다 건조가 1/3이상 빠르게 이루어진다.
Viscosity is 2000-5000CP and drying is 1/3 times faster than oily product.

즉, 본 발명의 크림타입의 경우 은폐력 향상 또는 우수한 색상 구현을 위해 액체타입과 달리 체질안료가 사용되는데, 상기 실시예 2에서는 체질안료 중 글라스 비드(Glass beads)를 사용하여 쳐짐 방지 효과를 추가적으로 기대할 수 있도록 한다.
That is, in the case of the cream type of the present invention, a sieving pigment is used unlike the liquid type in order to improve hiding power or to implement excellent color. In Example 2, an anti-sag effect is additionally expected by using glass beads in the sieving pigment. To help.

그리고 상기 크림타입의 코팅제는 주로 줄눈이 깊게 폐이거나 관통된 곳에 주로사용 하며 벽면 및 바닥면 어디든 사용이 가능하게 이루어진 것이다.
In addition, the cream-type coating agent is mainly used where the joint is deeply lunged or penetrated, and is made to be used anywhere on the wall and the bottom.

이하, 액체타입 내지 크림타입에서 사용하는 성분에 대하여 상세히 설명하면 다음과 같다.
Hereinafter, the components used in the liquid type to the cream type will be described in detail.

상기 1액 형으로 이루어진 수성 폴리머 수지로는 수성 아크릴 에멀젼 폴리머 수지(수성 아크릴 공중합체)가 사용될 수 있는데, As the one-component aqueous polymer resin, an aqueous acrylic emulsion polymer resin (aqueous acrylic copolymer) may be used.

상기 수성 아크릴 에멀젼 폴리머 수지는 Butyl Acrylate Monomer 4중량%, Methyl Methacrylate Monomer 18중량%, 2-Ethyl Acrylate 18중량%, Methacrylic Acid 2중량%, 2-Nydroxy Methyl Methacrylate 2중량%, 음이온계 계면활성제 1중량%, 물 55중량%로 이루어진 아크릴 에멀젼 폴리머 수지를 100중량%으로 사용하며 내수성, 접착성, 유연성, 내후성, 투명성이 뛰어난 수지를 사용하는 것이 바람직하다.The aqueous acrylic emulsion polymer resin is 4 wt% Butyl Acrylate Monomer, 18 wt% Methyl Methacrylate Monomer, 18 wt% 2-Ethyl Acrylate, 2 wt% Methacrylic Acid, 2 wt% 2-Nydroxy Methyl Methacrylate, 1 wt% Anionic Surfactant 100% by weight of the acrylic emulsion polymer resin consisting of 55% by weight of water, it is preferable to use a resin excellent in water resistance, adhesion, flexibility, weather resistance, transparency.

또한 1액 형으로 이루어진 수성 폴리머 수지로는 상기 아크릴 에멀젼 폴리머 수지 외에도 1액 형 수성으로 이루어진 에폭시 수지, 우레탄 수지, 무,유기 하이브리드 수지, 무기질수지, 세라믹 수지, 우레탄 아크릴, 실리콘 에멀젼 등을 들 수 있으며, 이들 중에서 선택된 1종 이상을 선택 사용하는 것이 바람직하다.
In addition to the acrylic emulsion polymer resin, the one-component aqueous polymer resin may be epoxy resin, urethane resin, organic or organic hybrid resin, inorganic resin, ceramic resin, urethane acrylic, silicone emulsion, etc. It is preferable to use one or more selected from these.

다음으로 반짝이 효과를 기대할 수 있는 즉, 펄색상 구현을 위한 펄제로는 메탈릭 파우더(빤짝이 펄)를 들 수 있으며, Next, you can expect the glitter effect, that is, the puljeje to realize the pearl color is metallic powder (Pearl Pearl),

메탈릭 파우더로는 은 펄이나 금 펄 ,백색 펄, 진주 펄 등 각 가지색의 펄이 고려될 수 있는 것으로 소정 량의 펄 파우더를 함유시키는 것이 바람직하다.As the metallic powder, pearls of various colors such as silver pearls, gold pearls, white pearls, pearl pearls and the like may be considered, and it is preferable to contain a predetermined amount of pearl powders.

특히 자연스러운 알루미늄 색상이나 금(金)색을 띠도록 하여 햇볕이나 불빛에 의하여 보는 각도에 따라 줄눈 색상이 변하게 되고, 이를 통해 화려하고, 아름답고, 미려함을 느낄 수 있고 그리고 타제품과의 기능적 차별화를 통한 희소성으로 제품의 고급화와 부가가치를 크게 향상시킬 수 있도록 하기 위해 채택한 성분이다.
In particular, the color of the joint changes according to the angle of view caused by sunlight or light, so that it has a natural aluminum color or gold color, and through this, it is possible to feel gorgeous, beautiful, and beautiful, and its scarcity through functional differentiation from other products. It is an ingredient that has been adopted to greatly improve the quality of products and added value.

상기 메탈릭 파우더의 입자크기는 1/256 ~ 1/32mm 사이의 입자를 선택하여 사용 하는 것이 바람직하다.
Particle size of the metallic powder is preferably used to select the particles between 1/256 ~ 1 / 32mm.

상기 메탈릭 파우더(빤짝이 펄) 외에도 본 발명에서 사용하는 펄제로 글리터 파우더, 피그먼트, 알루미늄 파우더, 알루미늄 페이스트, 형광 안료, 축광 안료, 금속 산화물등 중에서 선택된 1종 이상을 선택 사용하는 것이 좋다.
In addition to the metallic powder (Pearl), it is preferable to use one or more selected from among glitter powder, pigment, aluminum powder, aluminum paste, fluorescent pigment, photoluminescent pigment, metal oxide, etc., as a pearl used in the present invention.

그리고 크림 타입에 사용하는 체질안료는 은폐력 향상, 우수한 색상 구현을 위해 사용되는 것으로 글라스 비드(Class Beads)를 포함하여 알루미늄 옥사이드 , 중탄, 경탄, 세라믹 분말, 진공 세라믹 분말, 경량 골재, 규사, 석영, 탄산칼슘, 제올라이트, 백 아연 ,산화 아연, 산화바륨, 시멘트를 착색하거나 이중에서 선택된 1종 이상을 선택 사용하는 것을 고려할 수 있다.
In addition, the extender pigments used in the cream type are used to improve hiding power and to achieve excellent color. Including glass beads (Class Beads), aluminum oxide, hard coal, hard coal, ceramic powder, vacuum ceramic powder, lightweight aggregate, silica sand, quartz, It may be considered to color calcium carbonate, zeolite, white zinc, zinc oxide, barium oxide, cement or to use one or more selected from them.

특히 글라스 비드(Class Beads)는 알갱이가 일정한 곡면을 취하고 있어 때가 쉽게 끼지 않게 하는 기능을 함과 동시에 코팅제가 밑으로 처지지 않게 하는 기능을 하여 상기 실시예 2에 사용되었다.Particularly, glass beads (Class Beads) were used in Example 2 because they had a function of preventing grains from sticking to each other because the grains had a constant curved surface.

상기 글라스비드의 입자 크기는 200메쉬-3000메쉬 사이의 입자를 선택하여 사용 하는 것이 바람직하다.
The particle size of the glass beads is preferably used to select the particles between 200 mesh-3000 mesh.

다음으로 항균제는 각종 세균 및 곰팡이를 방지하기 위하여 유기계인 항균제 혼합물과 무기계인 나노화된 셀레늄 이온 물질을 혼합하여 사용하는데 유기계 항균제는 가격이 싸고 초기에 항균력은 좋으나 시간이 지나면 효과가 떨어지고 유해성 논란이 있으며, 무기계 항균제는 가격이 비싸고 초기 항균력은 유기계에 비하여 약하나 반영구적인 효과가 있고 인체에 무해하여 유기계인 항균제 혼합물과 무기계인 나노화된 셀레늄 이온 물질을 혼합하여 사용하는 하는 것이 바람직하다.
Next, antimicrobial agents use a mixture of organic antimicrobial agents and inorganic nanonized selenium ionic substances to prevent various bacteria and fungi. Organic antimicrobial agents are cheap and have good antimicrobial activity in the beginning, but the effects are deteriorated over time, and there are debates about harmful effects. Inorganic antimicrobial agents are expensive and the initial antimicrobial activity is weaker than organic ones, but has a semi-permanent effect and is harmless to humans. Therefore, it is preferable to use a mixture of organic antimicrobial agents and inorganic nanonized selenium ion materials.

그리고 상기 항균제 혼합물이란, 프로필렌글리콜(propyleneglycol) 40~50 중량%, 글리세린(glycerine) 30~40증량%, 시트르산(citric acid) 10~20중량%로 이루어진 혼합물이다.
And the antimicrobial mixture is a mixture consisting of 40 to 50% by weight of propylene glycol (propyleneglycol), 30 to 40% by weight of glycerin (glycerine), 10 to 20% by weight of citric acid (citric acid).

본 발명에서 사용하는 항균제는 특별히 한정하지 않으나 구체적으로 이루어진 Au ,Ag, Pt등 무기 항균제와 유기 항균제등 이중에서 선택된 1종 이상을 선택 사용하는 것이 좋다.
The antimicrobial agent used in the present invention is not particularly limited, but it is preferable to use at least one selected from an inorganic antimicrobial agent such as Au, Ag, Pt, and an organic antimicrobial agent.

그리고 본 발명에서는 음이온 방출 내지 원적외선 방출츨 위한 광물이 사용되는데, 음이온 방출 목적으로는 토르마린을 그리고 원적외선 방출 목적으로는 황토 내지 게르마늄을 고려해 볼 수 있다.
In the present invention, minerals for anion emission to far infrared emission are used, tourmaline for anion emission and ocher to germanium for far infrared emission can be considered.

음이온이 대량 방출되는 토르마린 광물질은 지구상에서 가장 많은 음이온을 방출한다는 연구 결과와 논문이 있고, 토르마린 광물질을 첨가함으로 일상 생활중에 인체에 유익한 음이온이 대량 방출되어, 공기를 정화하고, 깨끗하게 유지하여 주는 역할을 하고, There are research results and papers showing that tourmaline minerals that release large amounts of negative ions release the most negative ions on earth, and by adding tourmaline minerals, large amounts of negative ions are released to the human body in daily life, purifying the air and keeping it clean. And

이에 원적외선이 대량 방출 되는 황토나 게르마늄 같은 광물을 첨가하여 탈취와 항균 효과를 기대하는 것이 바람직하다.
Therefore, it is desirable to expect deodorization and antibacterial effect by adding minerals such as ocher or germanium that emit large amounts of far infrared rays.

본 발명에서 사용하는 토르마린이나 황토 및 게르마늄 외에도 동일한 기능 구현을 위해 옥가루, 수정가루, 숯가루, 맥반석 등 이중에서 선택된 1종 이상을 선택하여 사용하는 것이 좋다.
In addition to the tourmaline or ocher and germanium used in the present invention, it is preferable to use at least one selected from jade powder, quartz powder, charcoal powder, ganban stone and the like for implementing the same function.

실험예Experimental Example

실시 예를 비교 예와 실험을 통하여 본 발명의 구성 및 발명 효과를 보다 상세하게 설명하고자 한다. 물론 본 실험 예는 본 발명을 예시하기 위한 것으로 본 발명의 내용이 이에 한정되는 것은 아니다.
Examples will be described in more detail the configuration and effects of the present invention through comparative examples and experiments. Of course, this experimental example is for illustrating the present invention is not limited to the content of the present invention.

비교예Comparative example

본 발명의 실시예 1, 2에 대비하기 위하여 종래의 기술인 대한민국 등록특허 제10-1140454를 비교예 1로 선정 하고, 공개특허 제10-2011-138901호를 비교예 2로 선정 하고, 공개특허 제10-2012-92536호를 비교예 3으로 선정 하고, 등록특허 제10-776691호를 비교예 4로 선정 하고, 등록특허 제10-495043호를 비교예 5로 선정 하여 각각 비교 하였다
In order to prepare for Examples 1 and 2 of the present invention, Korean Patent Registration No. 10-1140454, which is a conventional technology, is selected as Comparative Example 1, and Patent Publication No. 10-2011-138901 is selected as Comparative Example 2, and 10-2012-92536 was selected as Comparative Example 3, Patent No. 10-776691 was selected as Comparative Example 4, and Patent No. 10-495043 was selected as Comparative Example 5 and compared.

비교예Comparative example 1 One

폴리에스터 폴리올 40 내지 50 중량%와, 상기 폴리에스터 폴리올을 경화시키기 위한 폴리에스테르 경화제 40 내지 50 중량%와, 생성되는 줄눈의 색상을 원하는 색상으로 형성하기 위한 안료 4 내지 8 중량%와, 상기 폴리에스터 폴리올과 경화제 그리고 안료를 용이하게 혼합하기 위한 신나 등의 희석제 1 내지 4 중량%로 구성된다.
40 to 50% by weight of polyester polyol, 40 to 50% by weight of polyester curing agent for curing the polyester polyol, 4 to 8% by weight of pigment for forming the color of the resulting joint into a desired color, and the poly It is composed of 1 to 4% by weight of a diluent such as thinner for easily mixing the ester polyol, the curing agent and the pigment.

비교예Comparative example 2 2

우선 주제부로서, 10~15중량%의 에폭시 수지, 0.1~0.2중량%의 분산제, 0.05~0.1중량%의 소포제, 0.1~0.5중량%의 가소제, 0.5~1.0중량%의 유화제, 3~5중량%의 이산화티탄, 60~80중량%의 무기충전필러, 3~5중량%의 희석용제로 구성하고, First, as the main part, 10 to 15% by weight epoxy resin, 0.1 to 0.2% by weight dispersant, 0.05 to 0.1% by weight antifoaming agent, 0.1 to 0.5% by weight plasticizer, 0.5 to 1.0% by weight emulsifier, 3 to 5 weight Consisting of% titanium dioxide, 60 to 80% by weight inorganic filler, 3 to 5% by weight diluent solvent,

경화제부로서, 55~85중량%의 에폭시 수지 경화제, 0.5~1.0중량%의 분산제, 13~18중량%의 물로 구성된다.
As a hardening | curing agent part, it consists of 55-85 weight% epoxy resin hardening | curing agent, 0.5-1.0 weight% dispersing agent, and 13-18 weight% water.

비교예Comparative example 3 3

겔 형태의 에폭시를 이용한 수직 타일 줄눈 마감제로서 비스패놀 A형 에폭시 수지 95 내지 80 중량%와 FUMED 실리카 5 내지 20 중량%를 혼합한 주제와 경화제인 부제로 구성된다.
It is a vertical tile joint finish using gel-type epoxy, and is composed of a main agent and a hardener which mix 95 to 80% by weight of bispanol type A epoxy resin and 5 to 20% by weight of FUMED silica.

비교예Comparative example 4 4

(a) 계면활성제 1-20 중량%, 식물성 오일 1-20 중량%, 폴리옥시에틸렌 글리콜 0.5-10 중량%, 알킬아릴 폴리에틸렌 알코올 0.5-10 중량%, 부식 억제제 0.5-3 중량%, 에틸렌디아민 테트라아세트산 소듐 0.1-1 중량%, 고분자 수지 10-40 중량% 및 물 40-70 중량%를 포함하는 타일재생 액제; 그리고,(a) 1-20 wt% surfactant, 1-20 wt% vegetable oil, 0.5-10 wt% polyoxyethylene glycol, 0.5-10 wt% alkylaryl polyethylene alcohol, 0.5-3 wt% corrosion inhibitor, ethylenediamine tetra Tile regeneration liquid containing 0.1-1% by weight of sodium acetate, 10-40% by weight of polymer resin, and 40-70% by weight of water; And,

(b) 세라믹 분말 40-70 중량%, 백시멘트 20-40 중량%, 규사 0.05-3 중량% 및 혼화제 0.05-3 중량%를 포함하는 타일줄눈 코팅용 조성물을 포함하고,(b) a composition for tile joint coating comprising 40-70% by weight of ceramic powder, 20-40% by weight of cement, 0.05-3% by weight of silica sand and 0.05-3% by weight of admixture,

상기 타일재생 액제 및 타일줄눈 삽입용 조성물의 비율이 1:0.5-1:4로 이루어진 타일재생 및 타일줄눈 시공용조성물을 비교예 4로 한다.
A composition for tile regeneration and tile joint construction, in which the ratio of the tile regeneration solution and the tile joint insertion composition is 1: 0.5-1: 4, is set as Comparative Example 4.

비교예Comparative example 5 5

시멘트 50 - 75 중량 %, 모래 5 - 20 중량 %, 스테아린산아연 0.2 - 30 중량 %, 무기질계 미분체 광물 0.2 - 30 중량 %, 메도로스 0.1 - 2.0 중량 %로 이루어진다.
It consists of 50-75% by weight of cement, 5-20% by weight of sand, 0.2-30% by weight of zinc stearate, 0.2-30% by weight of inorganic fine minerals, and 0.1-2.0% by weight of medorose.

측정 방법How to measure

측정 방법은 한국 산업 규격에서 KS L 1592의 줄눈부분을 기준으로 인용하였으며, 한국 산업 규격에 측정 방법이 나와 있지 않는 시험방법은 통상의 이해 할수 있는 방법으로 실시하였다.
The measurement method was cited based on the joint part of KS L 1592 in the Korean Industrial Standards, and the test method that does not include the measuring method in the Korean Industrial Standards was conducted in a generally understandable manner.

시험의 일반 조건은 다음과 같다.General conditions of the test are as follows.

1. 시료 및 시험 체의 제작 및 시험조건은 특별히 지정하지 않는 한 온도 , ?습도 60?5％를 따르고,1. The preparation and test conditions of the sample and test body shall follow the temperature, humidity and humidity of 60-5%, unless otherwise specified.

2. 시험에 사용하는 재료는 시험조건에 제작 전 12시간 동안 방치해 두었으며, 2. The materials used for the test were left under test conditions for 12 hours before production.

3. 주제와 경화제는 시험 전 잘 교반해야 사용하였다.3. The subject and hardener were used after stirring well before the test.

4. 타일 줄눈에 줄눈 보수제를 3mm 두께로 도포하고 72 시간 경화시킨 후 그 결과치를 측정하였다.4. The joint repair agent was applied to the tile joints with a thickness of 3 mm and cured for 72 hours, and the result was measured.

5. ks m 5982 자외선에 의한 황변에 대한 저항성 측정은 UV-B램프 중 20와트에 자외선 파장이 280nm - 360nm 램프 로 24시간 방치 하는 것을 1사이클로 하여 1개월간 총 10싸이클을 실시하여 변색되는 정도를 측정하였다.5. ks m 5982 The resistance to yellowing caused by UV rays is measured by changing the color of light by discharging 10 cycles for one month, using 20 cycles of UV-B lamps for 24 hours in a 280-360 nm lamp. Measured.

6. 접착강도는 KS F 4918에 의거 측정하였고, 내마모성은 CS-17휠/1000g/100회 반복하여 측정하였다.6. Adhesion strength was measured according to KS F 4918, and wear resistance was repeatedly measured CS-17 wheel / 1000g / 100 times.

7. 발수성은 72시간 경과 후 경화된 방수층에 물을 뿌려 비딩(beading) 효과를 육안으로 관찰하여 측정하여 비교하였다.
7. Water repellency was compared by measuring the beading effect visually by spraying water on the cured waterproofing layer after 72 hours.

실시예 1Example 1 실시예 2Example 2 압축강도 N/㎟Compressive strength N / ㎡ 20.6520.65 25.425.4 흡수율 %Water absorption% 44 33 길이변화율 %Length change rate% 0.110.11 0.090.09 보수율 %% Remuneration 8585 7777 UV저항성UV resistance 변색없음No discoloration 변색없음No discoloration 내수성Water resistance 이상없음clear 이상없음clear 내산성Acid resistance 이상없음clear 이상없음clear 오염성Pollutant 이상없음clear 이상없음clear 항곰팡이성 %Antifungal% 99%99% 99%99% 건조시간Drying time 3시간3 hours 3시간3 hours 시공시 혼합성Mixability during construction 1액형1 component 1액형1 component 습윤면시공성Wet cotton workability 가능possible 가능possible 색상수Number of colors 다양함Various 다양함Various 냄새smell 저취Low 저취Low 음이온및원적외선Anion and far infrared 방출Release 방출Release 시공후 보수성Conservativeness after construction 가능possible 가능possible 수직면 시공성Vertical surface workability 가능possible 가능possible

비교예 1Comparative Example 1 비교예 2Comparative Example 2 비교예 3Comparative Example 3 비교예 4Comparative Example 4 비교예 5Comparative Example 5 압축강도 N/㎟Compressive strength N / ㎡ 24.524.5 3737 35.535.5 18.618.6 19.919.9 흡수율 %Water absorption% 33 1One 1One 44 44 길이변화율 %Length change rate% 0.320.32 0.010.01 0.010.01 0.130.13 0.110.11 보수율 %% Remuneration 6565 5050 5050 8383 8787 UV저항성UV resistance 5싸이클 이후
변색After 5 cycles
discoloration 3싸이클 이후
변색After 3 cycles
discoloration 2싸이클 이후
변색After 2 cycles
discoloration 변색없음No discoloration 변색없음No discoloration 내수성Water resistance 이상없음clear 이상없음clear 이상없음clear 이상있음There is a problem 이상없음clear 내산성Acid resistance 이상있음There is a problem 이상있음There is a problem 이상있음There is a problem 이상없음clear 이상없음clear 오염성Pollutant 이상없음clear 이상없음clear 이상없음clear 이상있음There is a problem 이상없음clear 항곰팡이성 %Antifungal% 56%56% 10%10% 60%60% 0%0% 0%0% 건조시간Drying time 12시간12 hours 12시간12 hours 12시간12 hours 24시간24 hours 24시간24 hours 시공시 혼합성Mixability during construction 2액형2-part 2액형2-part 2액형2-part 1액형1 component 1액형1 component 습윤면시공성Wet cotton workability 불가능impossible 불가능impossible 불가능impossible 가능possible 가능possible 색상수Number of colors 다양함Various 다양함Various 다양함Various 단색Monochromatic 단색Monochromatic 냄새smell 많이 남A lot 많이 남A lot 많이 남A lot 저취Low 저취Low 음이온및원적외선Anion and far infrared 방출안됨No emission 방출Release 방출안됨No emission 방출Release 방출안됨No emission 시공후 보수성Conservativeness after construction 불가능impossible 불가능impossible 불가능impossible 가능possible 가능possible 수직면 시공성Vertical surface workability 불가능impossible 불가능impossible 가능possible 불가능impossible 불가능impossible

본 발명의 실시 예 1 및 2와 비교 예 1, 2, 3, 4, 5 비교 시,When comparing Examples 1 and 2 of the present invention and Comparative Examples 1, 2, 3, 4, 5,

본 발명의 실시 예 1 및 2는 비교 예 1, 2, 3에 비하여 UV저항성이 뛰어나며 비교 예 1, 2, 4, 5에 비하여 항 곰팡이성이 우수 하고, 비교 예 1, 2, 3, 4, 5에 비하여 건조 시간이 빠른 것을 알 수 있었다.
Examples 1 and 2 of the present invention are excellent in UV resistance compared to Comparative Examples 1, 2 and 3, and excellent in anti-mildew compared to Comparative Examples 1, 2, 4 and 5, Comparative Examples 1, 2, 3, 4, It turned out that drying time is quick compared with 5.

본 발명의 실시 예 1 내지 2와 비교 예 1, 2, 3을 비교 시 시공시 혼합성이 간편하고, 습윤면 시공 시 용이 한 것을 알 수 있고, 냄새 또한 차이가 나며, 시공 후 보수성도 월등 한 것을 알 수 있었다.
When comparing Examples 1 to 2 and Comparative Examples 1, 2, and 3 of the present invention, it can be seen that the mixing properties are simple at the time of construction, and are easy at the time of construction when wet, and the smells are also different, and the water retention is excellent after construction. I could see that.

본 발명의 실시 예 1 내지 2와 비교 예 4, 5에 비하여 색상이 다양하고 다체로와 타일 색상과 같게 시공 할 수 있으며, 실시 예 1 및 2는 비교 예1, 2, 5에 비하여 수직 시공이 가능한 것을 알 수 있습니다.
Compared to Examples 1 and 2 and Comparative Examples 4 and 5 of the present invention, the color may be varied and may be constructed in the same manner as the multi-body and tile colors, and Examples 1 and 2 may have a vertical construction compared to Comparative Examples 1 and 2 and 5. You can see what's possible.

이상의 설명에서 각종 수지의 특성과 안료 및 메탈릭 파우더(빤짝이 펄)을 구체 입수 방법 등과 관련된 통상의 공지된 기술을 생략되어 있으나, 당업자라면 용이하게 이를 추측 및 추론하고 재현할 수 있다.
In the above description, the conventionally known techniques related to the properties of various resins and pigments and metallic powders (spray pearls), etc. are omitted, but those skilled in the art can easily infer, infer, and reproduce them.

또 이상에서 본 발명을 설명함에 있어 특정 조성을 위주로 설명하였으나 본 발명은 당업자에 의하여 다양한 수정, 변경 및 치환이 가능하고, 이러한 수정, 변경 및 치환은 본 발명의 보호범위에 속하는 것으로 해석되어야 한다.
In addition, in the above description of the present invention, a specific composition has been described, but the present invention may be modified, changed, and replaced by those skilled in the art, and such modifications, changes, and substitutions should be construed as falling within the protection scope of the present invention.

Claims (6)

액체 타입의 줄눈코팅제로서,
수성 아크릴 공중합체 수지 55~80 중량%,
펄색상 구현을 위한 펄제 10~35 중량%,
음이온 또는 원적외선 방출을 위한 광물 5-10중량%,
항균제 1-3중량%, 그리고
점도를 높이는 증점제 0.5-1.5 중량%를 포함하여 이루어지되,
상기 줄눈코팅제는 1액 형 수성타입이고, 점도는 500~2000CP인 것을 특징으로 하고,
상기 수성 아크릴 공중합체 수지는, Butyl Acrylate Monomer 4중량%, Methyl Methacrylate Monomer 18중량%, 2-Ethyl Acrylate 18중량%, Methacrylic Acid 2중량%, 2-Nydroxy Methyl Methacrylate 2중량%, 음이온계 계면활성제 1중량%, 물 55중량%로 이루어지는 것을 특징으로 하고,
상기 항균제는 유기계 항균제 혼합물과 무기계 나노화된 셀레늄 이온 물질을 혼합하여 사용하되,
상기 유기계 항균제 혼합물은 프로필렌글리콜(propyleneglycol) 40~50 중량%, 글리세린(glycerine) 30~40증량%, 시트르산(citric acid) 10~20중량%으로 이루어진 것을 특징으로 하고,
상기 광물로는 토르마린이 사용되며, 상기 토르마린은 음이온이 1㎡당 500-1000개 방출되는 것을 특징으로 하는 색상이 다양한 메탈릭 파우더를 이용한 1액 형 수성타입 줄눈 코팅제.As a liquid type joint coating,
55-80% by weight of aqueous acrylic copolymer resin,
10 to 35% by weight of a pearl agent for pearl color,
5-10% by weight minerals for anionic or far infrared emission,
1-3 wt% antibacterial agent, and
It contains 0.5-1.5% by weight thickener to increase the viscosity,
The joint coating agent is a one-component aqueous type, the viscosity is characterized in that 500 ~ 2000CP,
The aqueous acrylic copolymer resin, 4% by weight of Butyl Acrylate Monomer, 18% by weight of Methyl Methacrylate Monomer, 18% by weight of 2-Ethyl Acrylate, 2% by weight of Methacrylic Acid, 2% by weight of 2-Nydroxy Methyl Methacrylate, anionic surfactant 1 It consists of 55% by weight of water, 55% by weight,
The antimicrobial agent may be used by mixing an organic antimicrobial agent mixture with an inorganic nanonized selenium ion material.
The organic antimicrobial mixture is propylene glycol (propyleneglycol) 40 to 50% by weight, glycerin (glycerine) 30 to 40% by weight, citric acid (citric acid) is characterized in that consisting of 10 to 20% by weight,
Tourmaline is used as the mineral, and the tourmaline is a one-component aqueous type joint coating agent using a variety of metallic powder, characterized in that the anion is released 500-1000 pieces per 1㎡. 크림 타입의 줄눈코팅제로서,
수성 아크릴 공중합체 수지 15~30 중량%,
체질안료 40-60중량%,
펄색상 구현을 위한 펄제 10~35 중량%,
음이온 또는 원적외선 방출을 위한 광물 5-10중량%,
항균제 1-3중량%, 그리고
점도를 높이는 증점제 0.5-1.5 중량%를 포함하여 이루어지되,
상기 줄눈코팅제는 1액 형 수성타입이고, 점도는 2000~5000CP인 것을 특징으로 하고,
상기 수성 아크릴 공중합체 수지는, Butyl Acrylate Monomer 4중량%, Methyl Methacrylate Monomer 18중량%, 2-Ethyl Acrylate 18중량%, Methacrylic Acid 2중량%, 2-Nydroxy Methyl Methacrylate 2중량%, 음이온계 계면활성제 1중량%, 물 55중량%로 이루어지는 것을 특징으로 하고,
상기 항균제는 유기계 항균제 혼합물과 무기계 나노화된 셀레늄 이온 물질을 혼합하여 사용하되,
상기 유기계 항균제 혼합물은 프로필렌글리콜(propyleneglycol) 40~50 중량%, 글리세린(glycerine) 30~40증량%, 시트르산(citric acid) 10~20중량%으로 이루어진 것을 특징으로 하고,
상기 광물로는 토르마린이 사용되며, 상기 토르마린은 음이온이 1㎡당 500-1000개 방출되는 것을 특징으로 하는 색상이 다양한 메탈릭 파우더를 이용한 1액 형 수성타입 줄눈 코팅제.As a cream type joint coating agent,
15-30% by weight of aqueous acrylic copolymer resin,
Sieving pigment 40-60% by weight,
10 to 35% by weight of a pearl agent for pearl color,
5-10% by weight minerals for anionic or far infrared emission,
1-3 wt% antibacterial agent, and
It contains 0.5-1.5% by weight thickener to increase the viscosity,
The joint coating agent is a one-component aqueous type, the viscosity is characterized in that 2000 ~ 5000CP,
The aqueous acrylic copolymer resin, 4% by weight of Butyl Acrylate Monomer, 18% by weight of Methyl Methacrylate Monomer, 18% by weight of 2-Ethyl Acrylate, 2% by weight of Methacrylic Acid, 2% by weight of 2-Nydroxy Methyl Methacrylate, anionic surfactant 1 It consists of 55% by weight of water, 55% by weight,
The antimicrobial agent may be used by mixing an organic antimicrobial agent mixture with an inorganic nanonized selenium ion material.
The organic antimicrobial mixture is propylene glycol (propyleneglycol) 40 to 50% by weight, glycerin (glycerine) 30 to 40% by weight, citric acid (citric acid) is characterized in that consisting of 10 to 20% by weight,
Tourmaline is used as the mineral, and the tourmaline is a one-component aqueous type joint coating agent using a variety of metallic powder, characterized in that the anion is released 500-1000 pieces per 1㎡. 삭제delete 제1항 또는 제2항에 있어서,
상기 펄제로는 메탈릭 파우더가 사용되며,
상기 메탈릭 파우더는 1/256 ~ 1/32 mm 사이의 입자를 사용하는 것을 특징으로 하는 색상이 다양한 메탈릭 파우더를 이용한 1액 형 수성타입 줄눈 코팅제.The method according to claim 1 or 2,
Metallic powder is used as the pearl agent,
The metallic powder is a one-component aqueous type joint coating using a variety of metallic powder, characterized in that the use of particles between 1/256 ~ 1/32 mm. 제2항에 있어서,
상기 체질안료로는 글라스 비드가 사용되며,
글라스 비드는 알갱이가 일정한 곡면을 취하고 있어 때가 쉽게 끼지 않게 하고 코팅제가 밑으로 처지지 않게 하는 것으로, 입자 크기는 200메쉬-3000메쉬 인 것을 특징으로 하는 색상이 다양한 메탈릭 파우더를 이용한 1액형 수성타입 줄눈 코팅제.The method of claim 2,
Glass sieve is used as the extender pigment,
Glass bead is a one-component aqueous type joint using a variety of metallic powder, characterized in that the particle has a constant curved surface so that it does not easily get caught and the coating does not sag down, and the particle size is 200 mesh-3000 mesh. Coating agent. 삭제delete
KR1020120124638A 2012-11-06 2012-11-06 Coating composit KR101262358B1 (en)