KR101249335B1 - By painting spray way coating cover board and the making method processed - Google Patents

By painting spray way coating cover board and the making method processed Download PDF

Info

Publication number
KR101249335B1
KR101249335B1 KR1020100112686A KR20100112686A KR101249335B1 KR 101249335 B1 KR101249335 B1 KR 101249335B1 KR 1020100112686 A KR1020100112686 A KR 1020100112686A KR 20100112686 A KR20100112686 A KR 20100112686A KR 101249335 B1 KR101249335 B1 KR 101249335B1
Authority
KR
South Korea
Prior art keywords
paint layer
cover plate
coated
plate material
spray method
Prior art date
Application number
KR1020100112686A
Other languages
Korean (ko)
Other versions
KR20120051307A (en
Inventor
정희진
Original Assignee
주식회사 디테일베이스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 디테일베이스 filed Critical 주식회사 디테일베이스
Priority to KR1020100112686A priority Critical patent/KR101249335B1/en
Publication of KR20120051307A publication Critical patent/KR20120051307A/en
Application granted granted Critical
Publication of KR101249335B1 publication Critical patent/KR101249335B1/en

Abstract

본 발명은 알루미늄(AL) 진공 증착 방식을 대체할 수 있도록 한 도료 스프레이 방식으로 코팅 처리되는 커버판재 및 그 제조방법에 관한 것이다.
본 발명은 이를 위하여 도료 스프레이 방식으로 코팅 처리되는 커버판재(10)를 제조함에 있어서, 다양한 형상과 모양을 갖는 투명판재(12)를 사전에 제작 준비하는 단계와, 상기 투명판재를 순차적으로 이송시키면서 이면(裏面)에 대해 알루미늄색상을 제공하는 우레탄 도료를 스프레이 방식으로 코팅 처리하여 우레탄 도료층(16)을 형성하는 단계, 상기 우레탄 도료층(14)을 60~65℃의 온도에서 40~50분 정도 자연 건조 처리하는 단계, 및 상기 우레탄 도료층의 표면에 대해 미러 효과를 제공하기 위하여 블랙 도료층(16)을 스프레이 방식으로 형성하는 단계를 포함하여 제조함으로써 종래 알루미늄 진공 증착 방식에 의해 제작되는 투명판재의 미러 장식 효과를 그대로 살리면서도 제조 공정을 현저하게 단축할 수 있기 때문에 고 효율 저 비용으로 커버판재의 제작이 가능하게 되며, 또한, 진공 증착 방식을 완전히 배제함으로써 증착에 따른 제품의 불량률을 95%이상 감소시킬 수 있는 제조 공정상의 현저한 이점을 제공하는 것이 가능하게 된다.The present invention relates to a cover plate material which is coated by a paint spray method, and a method of manufacturing the same, to replace an aluminum (AL) vacuum deposition method.
In the present invention, in preparing the cover plate material 10 coated with a coating spray method for this purpose, preparing and preparing a transparent plate material 12 having various shapes and shapes in advance, while sequentially transporting the transparent plate material Coating a urethane paint that provides an aluminum color to the back surface by spraying to form a urethane paint layer 16, and the urethane paint layer 14 at a temperature of 60 to 65 ° C. for 40 to 50 minutes Transparent natural fabricated by conventional aluminum vacuum deposition by manufacturing a degree of natural drying treatment, and forming the black paint layer 16 by spraying to provide a mirror effect on the surface of the urethane paint layer. It is possible to significantly shorten the manufacturing process while maintaining the mirror decoration effect of the plate, so that the efficiency of the cover plate is high. The smaller is possible, also, it is possible to provide significant advantages in the manufacturing process which can reduce the defect rate of the products according to the evaporation 95% or more by completely rule out the vacuum deposition method.

Description

도료 스프레이 방식으로 코팅 처리되는 커버 판재 및 그 제조방법{By painting spray way coating cover board and the making method processed}By painting spray way coating cover board and the making method processed}

본 발명은 알루미늄(AL) 진공 증착 방식을 대체하여 도료 스프레이 방식으로 커버판재를 제조할 수 있도록 한 도료 스프레이 방식으로 코팅 처리되는 커버 판재 및 그 제조방법에 관한 것이다.The present invention relates to a cover plate material coated with a paint spray method and a method for manufacturing the cover plate material to replace the aluminum (AL) vacuum deposition method to produce a cover plate material by a paint spray method.

세탁기나 청소기, 건조기 등의 각종 전자 제품에는 필요에 따라 장식이나 용도, 기능에 맞추어 투명 재질의 판재에 대하여 이면으로 각종 색상이나 밀러 효과가 부여되도록 알루미늄(AL)을 진공증착(眞空蒸着) 방식으로 코팅 처리하여 사용하고 있다.Various kinds of electronic products such as washing machines, vacuum cleaners and dryers are vacuum-deposited on aluminum (AL) so that various colors and miller effects can be applied to the back surface of transparent materials according to decoration, use, and function. It is used by coating.

그러나 종래 진공증착 방식에 의해 제작되는 커버 판재는, 과도한 작업 공정이 소요됨은 물론 불량률의 증가로 인해 생산량의 감소를 비롯하여 제작 단가가 부득이 하게 증가되는 문제를 피할 수 없다.However, the cover plate material manufactured by the conventional vacuum deposition method, it is inevitable that the excessive work process takes, as well as the unavoidably increase the production cost, including the reduction of the production due to the increase of the defective rate.

이를 좀더 구체적으로 살펴보면, 종래 알루미늄 진공 증착방식으로 제작되는 커버판재의 제작 과정을 살펴보면, 커버 판재 입고 검사단계→초음파 자동 세척단계→1차 제진(除塵)단계→제품이송단계→스프레이도장단계→프라이머(PRIMER)처리 단계→제품 중간 검사단계→1차 자외선 건조단계→알루미늄 진공증착단계→2차 제진단계→2차 자외선 건조단계→클리어스프레이 도장단계→제품출하품질검사단계→포장 및 운반단계라는 많은 작업 공정을 통해 제작되고 있는 실정이다.In more detail, when looking at the manufacturing process of the cover plate made of a conventional aluminum vacuum deposition method, the cover plate wearing inspection step → ultrasonic automatic cleaning step → primary vibration damping (除塵) step → product transfer step → spray coating step → primer (PRIMER) processing stage → intermediate product inspection stage → primary ultraviolet drying stage → aluminum vacuum deposition stage → secondary dust removal stage → secondary ultraviolet drying stage → clear spray coating stage → product shipment quality inspection stage → packaging and transportation stage The situation is being produced through the work process.

따라서, 상기한 작업 단계를 거쳐 제작되는 커버 판재는 당연히 작업 공수의 증가로 인한 제품의 제작 단가 상승 초래는 물론 복잡한 작업 공정을 거쳐 생산되는 관계로 인해 생산율의 저하를 비롯하여 제품의 불량률이 40% 이상 증가한다는데 큰 문제를 야기하고 있다. 특히 상기한 작업 공정에서 불량률이 증가하게 되는 이유는 먼지 잔존으로 인한 증착률이 저하되는데 기인하고 있는 실정이어서, 이에 대한 대책이나 작업 방식의 구조 개선이 시급히 요구되고 있는 실정이라고 하겠다.Therefore, the cover plate produced through the above work steps, of course, increases the manufacturing cost of the product due to the increase in the number of work, as well as the production rate due to the relationship between the production process and the defective rate of the product is more than 40% or more It is causing a big problem to increase. In particular, the reason why the failure rate increases in the above-described work process is due to the fact that the deposition rate due to the residual dust is reduced, and therefore, it is urgently required that the countermeasure or structural improvement of the working method is required.

본 발명은 상기한 종래 문제점을 해결하고자 발명한 것으로서, 본 발명의 목적은 알루미늄 색상이 나는 우레탄도료를 스프레이 방식으로 간단한 코팅 처리함으로써 기존의 알루미늄 진공증착 방식을 대체하면서도 그 효과는 동일하게 제공하게됨은 물론 진공 증착 방식에 비해 제작 공정을 현저하게 줄임으로 인해 저비용으로 제품의 대량생산이 가능하고, 또 제품의 불량률을 현저하게 감소시킬 수 있도록 하여 제품의 품질은 물론 생산 경쟁력을 높일 수 있도록 한 도료 스프레이 방식으로 코팅 처리되는 커버 판재 및 그 제조방법을 제공함에 있다.The present invention has been invented to solve the above-mentioned conventional problems, the object of the present invention is to provide a similar effect while replacing the existing aluminum vacuum deposition method by a simple coating treatment by spraying the aluminum-colored urethane paint Of course, by significantly reducing the manufacturing process compared to the vacuum deposition method, it is possible to mass-produce the product at low cost and to significantly reduce the defect rate of the product, thereby improving the product quality and production competitiveness. It is to provide a cover plate material and a method of manufacturing the coating treatment in a manner.

상기한 목적을 달성하기 위한 도료 스프레이 방식으로 코팅 처리되는 커버 판재는, 다양한 형상과 모양을 갖도록 사전에 사출 제작되는 투명판재와, 상기 투명판재의 이면(裏面)에 알루미늄 색상을 제공하도록 스프레이 방식으로 코팅 처리하되 그라데이션(gradation) 효과를 제공하기 위하여 그 코팅 두께를 달리하는 우레탄 도료층 및 상기 우레탄 도료층의 표면에 미러(Mirror) 효과를 제공하기 위하여 스프레이 방식으로 코팅 처리되는 블랙 도료층을 포함하여 구성된 것이다.The cover plate coated with a paint spray method for achieving the above object is a transparent plate material which is pre-injected and manufactured to have various shapes and shapes, and is sprayed to provide an aluminum color on the back surface of the transparent plate material. Including a coating coating, but the urethane paint layer having a different coating thickness to provide a gradation effect and a black paint layer coated by a spray method to provide a mirror effect on the surface of the urethane paint layer It is composed.

삭제delete

상기한 목적을 달성하기 위한 도료 스프레이 방식으로 코팅 처리되는 커버 판재의 제조방법은, 다양한 형상과 모양을 갖도록 사전에 투명판재를 준비하는 단계와, 먼지가 제거된 투명판재를 순차적으로 이송시키면서 이면에 대해 알루미늄색상을 제공하는 우레탄 도료를 스프레이 방식으로 코팅 처리하되 그라데이션(gradation) 효과가 발휘되도록 그 코팅 두께를 달리하는 우레탄 도료층을 형성하는 단계, 상기 우레탄 도료층을 60~65℃의 온도에서 40~50분 정도 자연 건조 처리하는 단계, 및 상기 우레탄 도료층의 표면에 대해 미러 효과를 제공하기 위하여 블랙 도료층을 스프레이 방식으로 형성하는 단계를 포함하여 이루어 짐을 특징으로 한다.In order to achieve the above object, a method of manufacturing a cover plate coated with a paint spray method includes preparing a transparent plate material in advance to have various shapes and shapes, and sequentially transferring the transparent plate material from which dust is removed. Coating a urethane paint that provides an aluminum color with a spray method, but forming a urethane paint layer having a different coating thickness such that a gradation effect is exerted, and forming the urethane paint layer at a temperature of 60 to 65 ° C. Natural drying for about 50 minutes, and forming a black paint layer in a spray method to provide a mirror effect on the surface of the urethane paint layer.

삭제delete

본 발명에 따르면, 알루미늄 색상이 제공되는 우레탄 도료를 이용하여 투명판재의 이면을 스프레이 방식으로 코팅 처리하더라도 종래 알루미늄 진공 증착 방식에 의해 제작되는 투명판재의 미러 장식 효과를 그대로 살리면서도 제조 공정을 현저하게 단축할 수 있기 때문에 고 효율 저 비용으로 커버판재의 제작이 가능하게 되며, 또한, 진공 증착 방식을 완전히 배제함으로써 증착에 따른 제품의 불량률을 95%이상 감소시킬 수 있는 제조 공정상의 현저한 이점을 제공하게 된다.According to the present invention, even though the back surface of the transparent plate is sprayed using a urethane paint provided with aluminum color, the manufacturing process is remarkably maintained while maintaining the mirror decoration effect of the transparent plate produced by the aluminum vacuum deposition method. Since it can be shortened, it is possible to manufacture the cover plate at high efficiency and low cost, and also to provide a significant advantage in the manufacturing process that can reduce the defective rate of the product by more than 95% by completely eliminating the vacuum deposition method. do.

또한, 우레탄 도료층의 스프레이 코팅 두께를 달리함으로써 미러 효과에 더하여 그라데이션 효과가 더해짐으로써 저비용으로도 제품의 품질을 향상시킬 수 있음은 물론 고급화가 가능하게 되는 이점을 제공하게 되는 것이다.In addition, by varying the spray coating thickness of the urethane paint layer is added to the gradation effect in addition to the mirror effect to improve the quality of the product at a low cost as well as to provide an advantage that can be advanced.

도 1a 및 도 1b는 본 발명에 따른 제조 방법에 의해 제조된 커버판재의 평면 도 및 이면도이다.
도 2는 본 발명에 따른 제조방법에 의해 제조된 커버 판재의 측 단면도이다.
도 3은 본 발명에 따른 제조 공정을 나타내는 블록도이다.1A and 1B are a plan view and a rear view of a cover plate material produced by the manufacturing method according to the present invention.
Figure 2 is a side cross-sectional view of a cover plate produced by the manufacturing method according to the present invention.
3 is a block diagram showing a manufacturing process according to the present invention.

이하, 본 발명에 따른 바람직한 실시 예에 대하여 첨부한 도면을 참조하여 상세하게 설명하면 다음과 같다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

먼저, 도 1a 및 도 1b를 참조하면, 도 1a 및 도 1b에는 본 발명의 제조 방법에 의해 제조된 커버판재(10)가 도시되어 있다.First, referring to FIGS. 1A and 1B, a cover plate 10 manufactured by the manufacturing method of the present invention is illustrated in FIGS. 1A and 1B.

커버판재(10)는 청소기나 세탁기, 건조기 등 각종 제품의 장식 커버체로 사용되는 것으로서, 미러 효과가 제공되도록 도료에 의해 코팅 처리되어 내부 투시가 불가능하게 제작된다는 점에 기술적인 특징이 있다.The cover plate 10 is used as a decorative cover body for various products such as a cleaner, a washing machine, a dryer, and has a technical feature in that the inside is impossible to be coated by coating to provide a mirror effect.

또한, 커버판재(10)는, 비록 도 1a 및 도 1b에 특정 형태가 예시되어 있기는 하나, 이는 특정의 형태에 제한되는 것이 아니라 커버판재가 이용되는 각종 제품의 형태나 용도, 기능에 따라 다양한 형상과 모양을 가지도록 제작됨은 물론이다.In addition, the cover plate 10, although a specific form is illustrated in Figures 1a and 1b, which is not limited to a specific form, but varies depending on the form, use, function of the various products in which the cover plate is used Of course, it is manufactured to have a shape and shape.

도 2를 참조하면, 본 발명에 따른 커버판재(10)는, 투명 소재로 사출 제작되는 투명판재(12)와, 상기 투명판재의 이면(裏面)에 알루미늄 색상을 제공하도록 스프레이 방식으로 코팅 처리되는 우레탄 도료층(14), 및 상기 우레탄 도료층의 표면에 미러(Mirror) 효과를 제공하기 위하여 스프레이 방식으로 코팅 처리되는 블랙 도료층(16)을 포함하여 구성된 것이다.Referring to Figure 2, the cover plate 10 according to the present invention, the transparent plate material 12 is produced by injection molding a transparent material, and the coating treatment by spraying to provide an aluminum color on the back surface of the transparent plate material It comprises a urethane paint layer 14, and a black paint layer 16 that is spray-coated in order to provide a mirror effect on the surface of the urethane paint layer.

본 발명에 따르면, 상기 투명판재(10)의 이면 코팅 처리되는 우레탄 도료층(14)은, 블랙 도료층(16)의 코팅 처리시 도 1a에서 알 수 있는 바와 같이 그라데이션(gradation) 효과를 제공하기 위하여 그 코팅 두께를 달리함이 바람직하다.According to the present invention, the urethane paint layer 14 coated on the back surface of the transparent plate 10 provides a gradation effect as can be seen in FIG. 1A during the coating process of the black paint layer 16. In order to change the coating thickness, it is preferable.

그리고, 커버판재(10)에 미러 효과를 제공하기 위하여 도료에 의해 코팅 처리되는 부분은 도 1a 및 도 1b에서 알 수 있는 바와 같이 투명처리가 요구되는 부분(12a)이 있는 구조라면, 이를 제외한 나머지 부분으로만 형성되는 것으로서, 투명처리가 요구되는 부분은 커버판재의 형상이나 모양 등에 의해 달리 제작될 수 있음은 물론이다.In addition, if the portion to be coated by the coating to provide a mirror effect to the cover plate 10, as shown in Figures 1a and 1b is a structure having a portion 12a that requires a transparent treatment, except for this As only formed as a part, the part requiring the transparent treatment may be manufactured differently by the shape or shape of the cover plate material.

또한, 투명판재(12)로는 필요에 따라 요철 형상의 다양한 장식문양(12b)이 갖추어 질 수도 있고, 이 경우 장식문양은 투명처리가 요구되는 부분(12a)을 제외한 나머지 부분에 적정하게 형성되어 질 수 있다.In addition, the transparent plate 12 may be provided with a variety of decorative patterns (12b) of the irregular shape, if necessary, in this case, the decorative pattern is appropriately formed in the remaining portion except for the portion 12a is required to be transparent. Can be.

본 발명에 있어서, 투명판재(12)는 다양한 소재가 이용될 수 있다. 예컨대, 투명 재질의 폴리카보네이트(polycarbonate), 아크릴수지(acrylic), ABS수지 (acrylonitrile butadiene styrene copolymer) 등이 이용될 수 있다.In the present invention, the transparent plate 12 may be used in a variety of materials. For example, a polycarbonate, an acrylic resin, or an ABS resin (acrylonitrile butadiene styrene copolymer) of a transparent material may be used.

상기와 같이 구성된 본 발명에 따른 커버판재(10)는 투명판재(12)의 이면에 순차적으로 코팅 처리되는 우레탄 도료층(14) 및 블랙 도료층(16)의 구성에 의해 특히, 커버판재(10)의 표면으로는 알루미늄 색상이 은은하게 반사됨과 동시에 미러 효과가 발휘되는 것이다.Cover plate 10 according to the present invention configured as described above, in particular by the structure of the urethane paint layer 14 and the black paint layer 16 which is sequentially coated on the back surface of the transparent plate 12, cover plate 10 ), The aluminum color is softly reflected and the mirror effect is exerted.

도 3을 참조하여, 본 발명에 따른 도료 스프레이 방식으로 코팅 처리되는 커버판재(10)가 제조되는 방법에 대하여 설명한다.With reference to FIG. 3, the method by which the cover plate material 10 coated by the coating spray method which concerns on this invention is manufactured is demonstrated.

본 발명에 따르면, 도료 스프레이 방식으로 코팅 처리되는 커버판재(10)는,According to the present invention, the cover plate material 10 is coated by a paint spray method,

다양한 형상과 모양을 갖는 투명판재(12)를 사전에 제작 준비하는 단계와, 투명판재를 순차적으로 이송시키면서 이면에 대해 알루미늄색상을 제공하는 우레탄 도료를 스프레이 방식으로 코팅 처리하여 우레탄 도료층(16)을 형성하는 단계, 상기 우레탄 도료층(14)을 60~65℃의 온도에서 40~50분 정도 자연 건조 처리하는 단계, 및 상기 우레탄 도료층의 표면에 대해 미러 효과를 제공하기 위하여 블랙 도료층(16)을 스프레이 방식으로 형성하는 단계를 포함하여 이루어진다.Preparing and preparing a transparent plate member 12 having various shapes and shapes in advance, and urethane paint layer 16 by coating a urethane paint that provides an aluminum color to the back surface while sequentially transferring the transparent plate member by spraying. Forming a step, naturally drying the urethane paint layer 14 at a temperature of 60 to 65 ° C. for about 40 to 50 minutes, and providing a mirror effect on the surface of the urethane paint layer (a black paint layer ( 16) is formed by a spray method.

또한, 본 발명에 따르면, 우레탄 도료층(14)을 형성하는 단계에서 우레탄 도료는 그라데이션 효과가 발휘되도록 그 코팅 두께를 다르게 함이 바람직하다.In addition, according to the present invention, the urethane paint in the step of forming the urethane paint layer 14, it is preferable to vary the coating thickness so that the gradation effect is exhibited.

본 발명에 따르면, 투명판재(12)를 준비 제작하는 단계에서, 부수적으로 사출 작업을 통해 제작된 투명판재의 이상 유무 등을 사전에 검사하고, 또 표면에 묻은 먼지를 제진(除塵) 작업을 통해 깨끗하게 제거하는 등의 작업이 수반되어 질 수 있음은 물론이다.According to the present invention, in the step of preparing and manufacturing the transparent plate 12, incidentally inspect the presence of abnormality of the transparent plate produced by the incidental work in advance, and the dust on the surface through the dust removal operation Of course, this may be accompanied by a clean removal.

상기와 같은 방법에 의해 제작되는 본 발명의 커버판재(10)는 투명판재(12)의 이면으로 코팅처리되는 우레탄 도료층(14)이 블랙 도료층(16)에 의해 불투명 상태로 커버되기 때문에 상기 알루미늄 색상을 제공하는 우레탄 도료층(14)이 투명판재(12)의 표면으로 반사되는 장식효과를 비롯하여 미러 효과를 동시에 제공하게 되는 것이다.The cover plate material 10 of the present invention produced by the above method is because the urethane paint layer 14 coated on the back surface of the transparent plate material 12 is covered in an opaque state by the black paint layer 16 The urethane paint layer 14 providing the aluminum color simultaneously provides the mirror effect, including the decorative effect reflected to the surface of the transparent plate 12.

또한, 우레탄 도료층(14)의 스프레이 두께를 달리함으로써 투명판재(12)의 표면으로 표출되는 색상을 달리함으로써, 예컨대 도 1a에서와 같이 가장자리부분은 진하고 그로부터 내측으로 향할수록 엷어지는 그라데이션 효과를 제공하게 됨으로써 미러 효과에 더하여 그라데이션 효과가 더해짐으로써 저비용으로도 제품의 품질을 향상시킬 수 있음은 물론 고급화가 가능하게 되는 것이다.In addition, by varying the spray thickness of the urethane paint layer 14 by varying the color expressed on the surface of the transparent plate 12, for example, as shown in Figure 1a the edge portion is darker and provides a gradient effect that becomes thinner toward the inner side By adding the gradation effect in addition to the mirror effect, it is possible to improve the quality of the product at a low cost as well as to enhance the quality.

따라서, 본 발명에 따른 커버판재(10)는 알루미늄 색상을 제공하는 우레탄 도료를 스프레이 방식으로 코팅 처리함으로써 종래 알루미늄 진공 증착 방식에 의해 미러 효과가 제공되도록 제작되던 것에 비하여 작업 공정의 현저한 단축을 비롯하여 진공 증착이 아닌 도료의 스프레이 방식을 통해 제작함으로써 알루미늄 증착에 따른 불량률을 95% 이상 감소시킬 수 있어 제품의 대량 생산이 가능하게 되고, 제품의 제작 단가를 현저하게 낮추는 것이 가능하게 되는 것이다.Therefore, the cover plate 10 according to the present invention is a vacuum treatment, including a significant shortening of the work process as compared to the production of a mirror effect by a conventional aluminum vacuum deposition method by coating a urethane coating providing an aluminum color in a spray method It is possible to reduce the defect rate due to aluminum deposition by 95% or more by manufacturing the spray method of the coating rather than the deposition, thereby enabling mass production of the product and significantly lowering the manufacturing cost of the product.

10: 커버판재 12: 투명판재
14: 우레탄 도료층 16: 블랙 도료층10: cover plate 12: transparent plate
14: urethane paint layer 16: black paint layer

Claims (4)

도료 스프레이 방식으로 코팅 처리되는 커버판재(10)를 구성함에 있어서,
투명 소재로 사출 제작되는 투명판재(12)와,
상기 투명판재의 이면(裏面)에 알루미늄 색상을 제공하도록 스프레이 방식으로 코팅 처리되되 그라데이션(gradation) 효과가 발휘되도록 그 코팅 두께가 다르게 도포되는 우레탄 도료층(14), 및
상기 우레탄 도료층의 표면에 미러(Mirror) 효과를 제공하기 위하여 스프레이 방식으로 코팅 처리되는 블랙 도료층(16)을 포함하여 구성됨을 특징으로 하는 도료 스프레이 방식으로 코팅 처리되는 커버판재.In constructing the cover plate 10 which is coated by a paint spray method,
The transparent plate 12 which is injection-molded with a transparent material,
A urethane coating layer 14 coated with a spray method to provide an aluminum color on the back surface of the transparent plate material, but having a different coating thickness to exert a gradation effect, and
A cover plate material coated by a paint spray method, comprising a black paint layer (16) coated by a spray method to provide a mirror effect on the surface of the urethane paint layer. 삭제delete 도료 스프레이 방식으로 코팅 처리되는 커버판재(10)를 제조함에 있어서,
다양한 형상과 모양을 갖는 투명판재(12)를 사전에 제작 준비하는 단계와,
상기 투명판재를 순차적으로 이송시키면서 이면(裏面)에 대해 알루미늄색상을 제공하는 우레탄 도료를 스프레이 방식으로 코팅 처리하되 그라데이션(gradation) 효과가 발휘되도록 그 코팅 두께가 다르게 도포되는 우레탄 도료층(16)을 형성하는 단계,
상기 우레탄 도료층(14)을 60~65℃의 온도에서 40~50분 정도 자연 건조 처리하는 단계, 및
상기 우레탄 도료층의 표면에 대해 미러 효과를 제공하기 위하여 블랙 도료층(16)을 스프레이 방식으로 형성하는 단계를 포함하여 제조됨을 특징으로 하는 도료 스프레이 방식으로 코팅 처리되는 커버판재의 제조방법.In manufacturing the cover plate 10 which is coated by a paint spray method,
Preparing and preparing a transparent plate member 12 having various shapes and shapes in advance;
The urethane paint layer 16 is coated with a different coating thickness so that a gradation effect is exerted, while the urethane paint that provides aluminum color to the back surface while sequentially transferring the transparent plate material is sprayed. Forming step,
Naturally drying the urethane paint layer 14 at a temperature of 60 to 65 ° C. for about 40 to 50 minutes, and
Method of manufacturing a cover plate coating is coated by a paint spray method, characterized in that it comprises the step of forming a black paint layer (16) in a spray method to provide a mirror effect on the surface of the urethane paint layer. 삭제delete
KR1020100112686A 2010-11-12 2010-11-12 By painting spray way coating cover board and the making method processed KR101249335B1 (en)