KR101175129B1 - Envelope for packing - Google Patents

Envelope for packing Download PDF

Info

Publication number
KR101175129B1
KR101175129B1 KR1020100124597A KR20100124597A KR101175129B1 KR 101175129 B1 KR101175129 B1 KR 101175129B1 KR 1020100124597 A KR1020100124597 A KR 1020100124597A KR 20100124597 A KR20100124597 A KR 20100124597A KR 101175129 B1 KR101175129 B1 KR 101175129B1
Authority
KR
South Korea
Prior art keywords
density polyethylene
weight
low density
antistatic agent
packaging bag
Prior art date
Application number
KR1020100124597A
Other languages
Korean (ko)
Other versions
KR20120063580A (en
Inventor
박윤희
Original Assignee
박윤희
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 박윤희 filed Critical 박윤희
Priority to KR1020100124597A priority Critical patent/KR101175129B1/en
Publication of KR20120063580A publication Critical patent/KR20120063580A/en
Application granted granted Critical
Publication of KR101175129B1 publication Critical patent/KR101175129B1/en

Abstract

본 발명은 포장 봉투에 있어서, 피포장물에 접촉되며, 중밀도폴리에틸렌(MDPE) 80～85 중량%와 대전방지제 15～20 중량%가 포함되는 내층과, 내층의 외측에 형성되며, 메탈로센 선형저밀도폴리에틸렌(MLLDPE)으로 이루어지는 중간층과, 중간층의 외측에 형성되며, 메탈로센 선형저밀도폴리에틸렌(MLLDPE) 18～22 중량%와 저밀도폴리에틸렌(LDPE) 27～33 중량%와 고밀도폴리에틸렌(HDPE) 27～33 중량%와 대전방지제 15～20 중량%가 포함되는 외층을 포함하는 포장용 봉투가 제공된다.
본 발명에 따르면, 피포장물의 포장에 소요되는 시간과 비용을 줄이고, 융합의 용이함으로 인해 즉시 분산 효과가 영구히 지속되며, 마이그레이션(migration)을 방지함으로써 기능성에 대한 신뢰를 높이고, 중밀도폴리에틸렌(MDPE)의 적정량 사용으로 안티 블록킹(anti-blocking) 효과를 가짐으로써 피포장물의 투입을 위하여 쉽게 벌려지며, 습도에 대한 영향이 없으므로 계절이나 기온에 상관없이 피포장물을 안정적으로 보호할 수 있다.The present invention is a packaging bag, in contact with the package, the inner layer containing 80 to 85% by weight of medium density polyethylene (MDPE) and 15 to 20% by weight of the antistatic agent, and formed on the outside of the inner layer, the metallocene linear It is formed on the intermediate layer made of low density polyethylene (MLLDPE) and on the outside of the intermediate layer, 18 to 22 wt% of metallocene linear low density polyethylene (MLLDPE), 27 to 33 wt% of low density polyethylene (LDPE) and high density polyethylene (HDPE) 27 to A packaging bag is provided comprising an outer layer comprising 33% by weight and 15-20% by weight of an antistatic agent.
According to the present invention, it reduces the time and cost required for packaging the package, the immediate dispersing effect is permanently maintained due to the ease of fusion, increase the confidence in functionality by preventing migration, and the medium density polyethylene (MDPE) It has an anti-blocking effect by using a proper amount of), and it is easily opened for the input of the package. Since there is no influence on humidity, the package can be protected stably regardless of season or temperature.

Description

포장용 봉투{ENVELOPE FOR PACKING}Packing Envelopes {ENVELOPE FOR PACKING}

본 발명은 피포장물의 포장에 소요되는 시간과 비용을 줄이고, 기능성이 뛰어나며, 계절이나 기온에 상관없이 피포장물을 안정적으로 보호하도록 하는 포장용 봉투에 관한 것이다.
The present invention relates to a packaging bag for reducing the time and cost required for the packaging of the package, excellent in functionality, and stably protects the package regardless of season or temperature.

일반적으로, 전자제품은 포장 봉투로 씌워짐으로써 충격이나 긁힘 등에 의한 스크래치 등의 손상을 방지하게 된다. In general, electronic products are covered with a packaging bag to prevent damage such as scratches due to impact or scratching.

이러한 전자제품의 포장에 있어서, LED, LCD, PDP 등의 TV 또는 모니터, PMP, 휴대폰, 네비게이션 등과 같은 전자제품은 포장 봉투를 사용하여 포장하더라도 디스플레이면을 제대로 보호하지 못한다. 따라서, 전자제품의 디스플레이면에 스크래치나 이물질 오염 등을 방지하도록 포장 필름을 별도로 부착한 다음, 최종적으로 포장 봉투로 전자제품을 씌워서 포장을 마치게 된다. In the packaging of such electronic products, electronic products such as TVs or monitors such as LEDs, LCDs, PDPs, monitors, PMPs, mobile phones, navigation devices, etc., do not properly protect the display surface even if they are packaged using packaging bags. Therefore, the packaging film is separately attached to the display surface of the electronic product to prevent scratches or foreign matter contamination, and finally the packaging is finished by covering the electronic product with a packaging bag.

이와 같이 전자제품의 디스플레이면을 보호하기 위한 종래의 포장 필름은, 일례로 대한민국 특허청에 출원된 특허출원 제2003-13105호의 "적층형 표면 보호용 기능성 필름"으로서, 자착능력을 가지는 적층형 기능성 필름에 있어 피착체와 직접 접촉하는 내측층에는 선형저밀도폴리에틸렌(LLDPE) 50％ 중량비와 저밀도강화올레핀 50％ 중량비로 혼합된 재료와, 중간층에는 중밀도폴리에틸렌(MDPE)이나 고밀도폴리에틸렌(HDPE) 95 내지 99.5％ 중량비에 전도성 고분자 물질 0.5 내지 5％ 중량비로 혼합된 재료와, 외측층은 저밀도폴리에틸렌(LDPE)을 100％ 중량비로 구성하여 토출량 3：4：3의 비율에 의거 압출하여 소정의 두께로 제조한 다음, 외측층이 응고되기 전에 소정의 크기를 가진 셀룰로우스와 같은 섬유소나 솜털을 외측층 바깥표면에 피착시켜 제조된다.As such, the conventional packaging film for protecting the display surface of the electronic product is, for example, the "functional film for laminated surface protection" of Patent Application No. 2003-13105, filed with the Korean Intellectual Property Office, which is used in the laminated functional film having self-adhesion ability. The inner layer in direct contact with the complex is a mixture of 50% by weight of linear low density polyethylene (LLDPE) and 50% by weight of low density reinforced olefin, and in the middle layer of 95 to 99.5% by weight of medium density polyethylene (MDPE) or high density polyethylene (HDPE). The material mixed with the conductive polymer material at a weight ratio of 0.5 to 5% and the outer layer are made of low density polyethylene (LDPE) at a weight ratio of 100%, extruded to a predetermined thickness based on a discharge ratio of 3: 4: 3, and then Before the layer is solidified, it is produced by depositing fibrous or fuzz such as cellulose having a predetermined size on the outer surface of the outer layer.

그러나, 종래의 전자제품을 포장하는 경우, 포장 봉투는 PET(polyethylene terephthalate)와 PE(Polyethylene)가 서로 적층되는 구조를 가지며, 재활용에 문제를 초래하고 있다. 따라서, 포장 봉투는 이러한 단점을 가지면서도 포장 필름과 함께 사용되어야 함으로써 포장에 소요되는 비용과 시간을 증가시키는 문제점을 가지고 있었다.However, when packaging conventional electronic products, the packaging bag has a structure in which polyethylene terephthalate (PET) and polyethylene (PE) are laminated to each other, causing a problem in recycling. Therefore, the packaging bag has a problem of increasing the cost and time required for packaging by being used with the packaging film while having such disadvantages.

또한, 종래의 포장 봉투와 함께 사용되는 포장 필름은 대전방지를 위하여 대전방지제가 포함되나, 마이그레이션(migration)을 방지하기 위하여 대전방지제가 중간층에 존재할 수밖에 없고, 이로 인해 대전방지의 효율에 한계를 가지며, 디스플레이면으로부터 이탈을 방지하기 위하여 자착능력을 가지게 됨으로써 제조 과정이 복잡해지는 문제점을 가지고 있었다.In addition, the packaging film used with a conventional packaging bag includes an antistatic agent for antistatic, but in order to prevent migration (antistatic agent) to be present in the intermediate layer, which has a limitation in the efficiency of antistatic In order to prevent deviation from the display surface, the self-adhesion ability has a problem in that the manufacturing process is complicated.

또한, 종래의 포장 필름은 점착성으로 인해 낱장 인출이 가능하도록 하는 안티 블록킹(anti blocking)을 위한 과정에 많은 노력과 비용이 소요될 수밖에 없으며, 대전방지를 위해서 40 ～ 50%의 수분을 필요로 함으로써 습도에 의존하게 되는 문제점을 가지고 있었다.
In addition, the conventional packaging film has to take a lot of effort and cost in the process for the anti blocking (blocking) to enable the withdrawal of the sheet due to the adhesiveness, it requires moisture of 40 to 50% to prevent the humidity Had a problem that depended on.

본 발명은 상기한 바와 같은 종래의 기술에 따른 전자제품의 포장 봉투에 대한 문제점을 해결하기 위한 것으로서, 전자제품의 포장에 소요되는 시간과 비용을 줄이도록 하고, 융합의 용이함으로 인해 즉시 분산 효과가 영구히 지속되도록 하며, 마이그레이션(migration)을 방지함으로써 기능성에 대한 신뢰를 높이도록 하고, 제조 과정만으로도 안티 블록킹(anti-blocking) 효과를 가짐으로써 전자제품의 투입을 위하여 쉽게 벌려지도록 하며, 습도에 대한 영향이 없으므로 계절이나 기온에 상관없이 전자제품을 안정적으로 보호하도록 한다.
The present invention is to solve the problem of the packaging bag of the electronic product according to the prior art as described above, to reduce the time and cost required for packaging the electronic product, the immediate dispersion effect due to the ease of fusion It lasts forever, enhances confidence in functionality by preventing migration, and has an anti-blocking effect through the manufacturing process, making it easy to spread for the input of electronic products, and the effect on humidity Because it is not present, it is possible to reliably protect electronic products regardless of season or temperature.

상기 목적을 달성하기 위한 본 발명의 일 측면에 따르면, 포장 봉투에 있어서, 피포장물에 접촉되며, 중밀도폴리에틸렌(MDPE) 80～85 중량%와 대전방지제 15～20 중량%가 포함되는 내층과, 상기 내층의 외측에 형성되며, 메탈로센 선형저밀도폴리에틸렌(MLLDPE)으로 이루어지는 중간층과, 상기 중간층의 외측에 형성되며, 메탈로센 선형저밀도폴리에틸렌(MLLDPE) 18～22 중량%와 저밀도폴리에틸렌(LDPE) 27～33 중량%와 고밀도폴리에틸렌(HDPE) 27～33 중량%와 대전방지제 15～20 중량%가 포함되는 외층을 포함하는 포장용 봉투가 제공된다.According to an aspect of the present invention for achieving the above object, in the packaging bag, the inner layer which is in contact with the packaged material, 80 to 85% by weight of medium density polyethylene (MDPE) and 15 to 20% by weight of the antistatic agent, It is formed on the outside of the inner layer, an intermediate layer made of metallocene linear low density polyethylene (MLLDPE), and formed on the outside of the intermediate layer, 18 to 22% by weight of metallocene linear low density polyethylene (MLLDPE) and low density polyethylene (LDPE) Packaging bags are provided that include an outer layer comprising 27 to 33 weight percent, high density polyethylene (HDPE) 27 to 33 weight percent and an antistatic agent 15 to 20 weight percent.

본 발명의 다른 측면에 따르면, 포장 봉투에 있어서, 피포장물에 접촉되며, 중밀도폴리에틸렌(MDPE) 80～85 중량%와 대전방지제 15～20 중량%가 포함되는 내층과, 상기 내층의 외측에 형성되며, 메탈로센 선형저밀도폴리에틸렌(MLLDPE)으로 이루어지는 중간층과, 상기 중간층의 외측에 형성되며, 저밀도폴리에틸렌(LDPE) 40～42.5 중량%와 고밀도폴리에틸렌(HDPE) 40～42.5 중량%와 대전방지제 15～20 중량%가 포함되는 외층을 포함하는 포장용 봉투가 제공된다.
According to another aspect of the present invention, in the packaging bag, the inner layer which is in contact with the packaged material, containing 80 to 85% by weight of medium density polyethylene (MDPE) and 15 to 20% by weight of the antistatic agent, and formed on the outside of the inner layer And an intermediate layer made of metallocene linear low density polyethylene (MLLDPE) and an outer layer of the intermediate layer, 40 to 42.5 wt% of low density polyethylene (LDPE), 40 to 42.5 wt% of high density polyethylene (HDPE), and an antistatic agent 15 to There is provided a packaging envelope comprising an outer layer comprising 20% by weight.

본 발명에 따른 포장용 봉투에 의하면, 피포장물의 포장에 소요되는 시간과 비용을 줄이고, 융합의 용이함으로 인해 즉시 분산 효과가 영구히 지속되며, 마이그레이션(migration)을 방지함으로써 기능성에 대한 신뢰를 높이고, 중밀도폴리에틸렌(MDPE)의 적정량 사용으로 인해 안티 블록킹(anti-blocking) 효과를 가짐으로써 피포장물의 투입을 위하여 쉽게 벌려지며, 습도에 대한 영향이 없으므로 계절이나 기온에 상관없이 피포장물을 안정적으로 보호할 수 있다.According to the packaging bag according to the present invention, it reduces the time and cost required for packaging the packaged goods, the dispersing effect is permanently immediately due to the ease of fusion, to increase the confidence in functionality by preventing migration, Due to the use of an appropriate amount of high density polyethylene (MDPE), it has an anti-blocking effect, so it is easily opened for the input of the package, and since there is no influence on humidity, it can stably protect the package regardless of season or temperature. Can be.

도 1은 본 발명의 일 실시예에 따른 포장용 봉투를 도시한 도면이다.1 is a view showing a packaging bag according to an embodiment of the present invention.

이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 상세히 설명하기로 한다. 또한, 본 발명의 실시예는 당해 기술 분야에서 통상의 지식을 가진 자에게 본 발명을 더욱 완전하게 설명하기 위하여 제공되는 것이며, 하기 실시예는 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 하기 실시예에 한정되는 것은 아니다. Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings. In addition, the embodiments of the present invention are provided to more fully explain the present invention to those skilled in the art, the following examples may be modified in various other forms, the scope of the present invention Is not limited to the following examples.

도 1은 본 발명의 일 실시예에 따른 포장용 봉투를 도시한 도면이다.1 is a view showing a packaging bag according to an embodiment of the present invention.

도 1에 도시된 바와 같이, 본 발명의 일 실시예에 따른 포장용 봉투(10)는 피포장물에 접촉되는 내층(11)과, 내층(11)의 외측에 형성되는 중간층(12)과, 중간층(12)의 외측에 형성되는 외층(13)을 포함한다. 여기서, 피포장물은 LED, LCD, PDP 등의 텔레비전이나 모니터, 휴대폰, PMP, 네비게이션, 그 밖의 디스플레이면을 가지는 다양한 전자제품이 해당될 수 있으며, 그 외에 대전방지나 스크래치 등의 방지가 필요한 여러 가지의 제품이 해당될 수 있다. 또한, 포장용 봉투(10)는 봉투 형태를 가지기 위하여 양측에 차단을 위한 실링부(14)가 형성될 수 있는데, 이러한 실링부(14)는 제작 방법에 따라 포장용 봉투(10)의 양측뿐만 아니라, 일측에만 형성되거나, 개방 부위를 제외한 모든 부위에 형성될 수도 있다.As shown in FIG. 1, the packaging bag 10 according to an embodiment of the present invention includes an inner layer 11 contacting a packaged object, an intermediate layer 12 formed outside the inner layer 11, and an intermediate layer ( 12, the outer layer 13 is formed outside. Here, the packaged object may correspond to a variety of electronic products having a display panel such as a TV, a monitor, a mobile phone, a PMP, a navigation, and other display surfaces such as LEDs, LCDs, and PDPs. May be the product of In addition, the packaging bag 10 may have a sealing portion 14 for blocking on both sides in order to have a bag shape, such a sealing portion 14, as well as both sides of the packaging bag 10 according to the manufacturing method, It may be formed on only one side, or may be formed on all parts except the open area.

내층(11)은 중밀도폴리에틸렌(MDPE) 80～85 중량%와 대전방지제 15～20 중량%가 포함되며, 일례로 중밀도폴리에틸렌(MDPE) 80 중량%와 대전방지제 20 중량%로 이루어질 수 있다. 여기서, 대전방지제는 15 중량% 미만일 경우 전자제품의 디스플레이면을 보호할 정도의 대전 방지 효과를 기대할 수 없고, 20 중량%를 초과하는 경우 고가인 대전방지제의 사용량이 증가하여 비경제적이다. 즉, 대전방지제는 15 중량% 미만일 경우 디스플레이면의 보호를 위한 기능성을 잃게 되어 디스플레이면을 제대로 보호하지 못하게 된다. 또한, 대전방지제가 20 중량%를 초과하는 경우 디스플레이면에 대한 대전 방지 효과의 상승에 도움을 주지 않는 반면, 고가의 원료 사용량이 늘어나게 됨으로써 제조 단가를 상승시키는 원인을 제공한다.The inner layer 11 may include 80 to 85% by weight of medium density polyethylene (MDPE) and 15 to 20% by weight of an antistatic agent. For example, the inner layer 11 may include 80% by weight of medium density polyethylene (MDPE) and 20% by weight of an antistatic agent. Here, when the antistatic agent is less than 15% by weight can not expect the antistatic effect to protect the display surface of the electronic product, when it exceeds 20% by weight, the use of expensive antistatic agent is uneconomical. That is, when the antistatic agent is less than 15% by weight, the functionality for protecting the display surface is lost, so that the display surface may not be properly protected. In addition, when the antistatic agent exceeds 20% by weight does not help to increase the antistatic effect on the display surface, the use of expensive raw materials is increased, thereby providing a cause of increasing the manufacturing cost.

또한, 중밀도폴리에틸렌(MDPE)은 80 중량% 미만일 경우 원하는 안티 블록킹(anti-blocking) 특성을 발휘하지 못하여 내층(11)간의 벌려짐에 어려움을 초래하고, 85 중량%를 초과하는 경우 대전 방지를 위한 대전방지제의 양을 과도하게 줄여야 한다. In addition, when the medium density polyethylene (MDPE) is less than 80% by weight, it does not exhibit the desired anti-blocking properties, causing difficulty in spreading between the inner layers 11, and when exceeding 85% by weight, antistatic The amount of antistatic agent should be excessively reduced.

중밀도폴리에틸렌(MDPE)은 FB2310(아랍에미리트(UAE)의 보리알리스(Borealis))이 사용될 수 있다. 또한, 대전방지제는 AS500(듀퐁(Dupont)), SD100(듀퐁(Dupont)), 0107M(핀란드 IPE), MK400(듀퐁(Dupont)) 중 어느 하나가 사용될 수 있다. 이와 같은 내층(11)은 안티 블록킹(anti-blocking)이 뛰어나며, 이로 인해 포장용 봉투(10)에서 서로 맞댄 내층(11)이 잘 벌려지도록 하여 피포장물의 삽입이 용이하도록 한다.Medium density polyethylene (MDPE) may be used FB2310 (Borealis of the United Arab Emirates (UAE)). In addition, the antistatic agent may be any one of AS500 (Dupont), SD100 (Dupont), 0107M (Finland IPE), MK400 (Dupont). Such an inner layer 11 is excellent in anti-blocking (anti-blocking), thereby making it easy to insert the inner layer 11 against each other in the packaging bag 10 to spread well.

중간층(12)은 메탈로센 선형저밀도폴리에틸렌(MLLDPE)으로 이루어진다. 여기서, 메탈로센 선형저밀도폴리에틸렌(MLLDPE)은 9200EN(대림)이 사용될 수 있다. 따라서, 중간층(12)은 포장용 봉투(10)에서 있어서 인장 및 인열 강도를 증대시킴과 아울러 강도 보완층으로서 역할을 한다. The intermediate layer 12 is made of metallocene linear low density polyethylene (MLLDPE). Here, 9200EN (Daelim) may be used as the metallocene linear low density polyethylene (MLLDPE). Therefore, the intermediate layer 12 increases the tensile and tear strength in the packaging bag 10 and serves as a strength complement layer.

외층(13)은 일 실시예로서, 메탈로센 선형저밀도폴리에틸렌(MLLDPE) 18～22 중량%와 저밀도폴리에틸렌(LDPE) 27～33 중량%와 고밀도폴리에틸렌(HDPE) 27～33 중량%와 대전방지제 15～20 중량%가 포함될 수 있으며, 바람직하게는 메탈로센 선형저밀도폴리에틸렌(MLLDPE) 20 중량%와 저밀도폴리에틸렌(LDPE) 30 중량%와 고밀도폴리에틸렌(HDPE) 30 중량%와 대전방지제 20 중량%가 함유될 수 있다. 이로 인해 외층(13)은 외측에 대한 인장 및 인열 강도를 어느 정도 높이면서 우수한 가공성으로 인해 커팅 및 치수 안정성이 뛰어나고, 수분 흡수를 차단하여 피포장물을 안정적으로 보호하게 된다. The outer layer 13 is, in one embodiment, 18-22 wt% of metallocene linear low density polyethylene (MLLDPE), 27-33 wt% of low density polyethylene (LDPE), 27-33 wt% of high density polyethylene (HDPE) and antistatic agent 15 20 to 20% by weight, preferably 20% by weight of metallocene linear low density polyethylene (MLLDPE), 30% by weight of low density polyethylene (LDPE), 30% by weight of high density polyethylene (HDPE) and 20% by weight of an antistatic agent Can be. Because of this, the outer layer 13 is excellent in cutting and dimensional stability due to the excellent processability while increasing the tensile and tear strength to the outside to some extent, to block the absorption of water to reliably protect the package.

또한, 외층(13)은 다른 실시예로서, 메탈로센 선형저밀도폴리에틸렌(MLLDPE)을 제외한 구성으로서, 저밀도폴리에틸렌(LDPE) 40～42.5 중량%와 고밀도폴리에틸렌(HDPE) 40～42.5 중량%와 대전방지제 15～20 중량%가 포함될 수 있으며, 바람직하게는 저밀도폴리에틸렌(LDPE) 40 중량%와 고밀도폴리에틸렌(HDPE) 40 중량%와 대전방지제 20 중량%가 함유될 수 있다. 이로 인해 외층(13)은 우수한 가공성으로 인해 커팅 및 치수 안정성이 뛰어나고, 수분 흡수를 차단하여 피포장물을 안정적으로 보호하게 된다.In addition, the outer layer 13, as another embodiment, excluding metallocene linear low density polyethylene (MLLDPE), 40 to 42.5% by weight of low density polyethylene (LDPE) and 40 to 42.5% by weight of high density polyethylene (HDPE) and antistatic agent 15 to 20% by weight may be included, and preferably 40% by weight of low density polyethylene (LDPE), 40% by weight of high density polyethylene (HDPE) and 20% by weight of an antistatic agent. Due to this, the outer layer 13 is excellent in cutting and dimensional stability due to excellent workability, and blocks moisture absorption to stably protect the packaged object.

외층(13)에서 대전방지제는 15 중량% 미만일 경우 전자제품의 디스플레이면을 보호할 정도의 대전 방지 효과를 기대할 수 없고, 20 중량%를 초과하는 경우 고가인 대전방지제의 사용량이 증가하여 비경제적이다. 즉, 대전방지제는 15 중량% 미만일 경우 디스플레이면의 보호를 위한 기능성을 잃게 되어 디스플레이면을 제대로 보호하지 못하게 된다. 또한, 대전방지제가 20 중량%를 초과하는 경우 디스플레이면에 대한 대전 방지 효과의 상승에 도움을 주지 않는 반면, 고가의 원료 사용량이 늘어나게 됨으로써 제조 단가를 상승시키는 원인을 제공한다.If the antistatic agent in the outer layer 13 is less than 15% by weight can not be expected to prevent the antistatic effect to protect the display surface of the electronic product, if it exceeds 20% by weight the use of expensive antistatic agent is uneconomical . That is, when the antistatic agent is less than 15% by weight, the functionality for protecting the display surface is lost, so that the display surface may not be properly protected. In addition, when the antistatic agent exceeds 20% by weight does not help to increase the antistatic effect on the display surface, the use of expensive raw materials is increased, thereby providing a cause of increasing the manufacturing cost.

한편, 외층(13)에서, 메탈로센 선형저밀도폴리에틸렌(MLLDPE)는 9200EN(대림)이 사용될 수 있고, 저밀도폴리에틸렌(LDPE)는 LDPE 5301(한화)가 사용될 수 있으며, 고밀도폴리에틸렌(HDPE)는 F920A(삼성)가 사용될 수 있으며, 대전방지제는 AS500(듀퐁(Dupont)), SD100(듀퐁(Dupont)), 0107M(핀란드 IPE) 중 어느 하나가 사용될 수 있다. On the other hand, in the outer layer 13, metallocene linear low density polyethylene (MLLDPE) 9200EN (Daelim) can be used, low density polyethylene (LDPE) can be used LDPE 5301 (Hanhwa), high density polyethylene (HDPE) is F920A (Samsung) may be used, and the antistatic agent may be any one of AS500 (Dupont), SD100 (Dupont), 0107M (Finland IPE).

이와 같은 본 발명에 따른 포장용 봉투(10)의 제조를 위하여, 펠릿 또는 그 밖의 입상물 형태의 원재료를 용융하여 필름 형태의 내층(11), 중간층(12) 및 외층(13)을 각각 성형한 다음, 이들을 롤러 등에 의해 단일 경로로 이송하여 서로 접착에 의해 단일의 필름 형태를 이루도록 하고, 이러한 필름을 봉투 형태를 이루도록 가공함으로써 포장용 봉투(10)를 제조하게 된다. 이때, 포장용 봉투(10)의 내측면에는 내층(11)이 위치하게 되며, 외측면에는 외층(13)이 위치하게 되며, 내층(11)과 외층(13) 사이에는 중간층(12)이 위치하도록 각각 제조된 필름들을 접합시키게 된다.In order to manufacture the packaging bag 10 according to the present invention, the raw material in the form of pellets or other granules is melted to form the inner layer 11, the intermediate layer 12, and the outer layer 13, respectively, in the form of a film. By transporting them in a single path by a roller or the like to form a single film form by adhering to each other, and processing the film to form an envelope form, the packaging bag 10 is manufactured. At this time, the inner layer 11 is positioned on the inner side of the packaging bag 10, the outer layer 13 is positioned on the outer side, and the intermediate layer 12 is positioned between the inner layer 11 and the outer layer 13. Each prepared film is bonded.

이와 같은 본 발명에 따른 포장용 봉투(10)에 의하면, 피포장물에 씌우기만 하면 되므로, 피포장물, 예컨대 LED, LCD, PDP 등의 텔레비전이나 모니터, 휴대폰, PMP, 네비게이션, 그 밖의 디스플레이면을 가지는 다양한 전자제품의 디스플레이면에 포장 필름을 부착하지 않고서도 디스플레이면을 스크래치나 정전기 등으로부터 보호하게 되며, 이로 인해 피포장물의 포장에 소요되는 시간과 비용을 줄일 수 있다.According to the packaging bag 10 according to the present invention, it is only required to cover the packaged object, such as a variety of packaging, such as a television or monitor, such as LED, LCD, PDP, mobile phone, PMP, navigation, other display surface The display surface is protected from scratches and static electricity without attaching a packaging film to the display surface of the electronic product, thereby reducing the time and cost of packaging the packaged product.

또한, 본 발명에 따른 포장용 봉투(100)는 융합의 용이함으로 인해 즉시 분산 효과가 영구히 지속되며, 마이그레이션(migration)을 방지함으로써 대전방지, 강도 유지 등의 기능성에 대한 신뢰를 높이고, 내층(11)이 중밀도폴리에틸렌(MDPE)을 적정량 포함함으로써 우수한 안티 블록킹(anti-blocking) 효과를 가지며, 이로 인해 내층(11)간의 벌려짐이 용이하여 피포장물인 전자제품의 투입을 용이하도록 한다.In addition, the packaging bag 100 according to the present invention is immediately dispersing effect permanently due to the ease of fusion, by preventing migration (migration) to increase the confidence in the functionality, such as antistatic, strength maintenance, and the inner layer 11 By including the appropriate amount of the medium density polyethylene (MDPE) has an excellent anti-blocking effect, thereby facilitates the spreading between the inner layer 11 to facilitate the introduction of the electronic product as a package.

또한, 본 발명에 따른 포장용 봉투(100)는 대전방지 기능이 습도에 영향을 받지 않으므로 겨울철 등의 계절이나 기온에 상관없이 피포장물을 안정적으로 보호할 수 있다.In addition, since the antistatic function is not affected by humidity, the packaging bag 100 according to the present invention can stably protect the packaged material regardless of season or temperature such as winter time.

이와 같이 첨부된 도면을 참조하여 본 발명을 설명하였으나, 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 다양한 수정 및 변형이 이루어질 수 있음은 물론이다. 그러므로, 본 발명의 범위는 설명된 실시예에 국한되어 정해져서는 안되며, 후술하는 특허청구범위뿐만 아니라 이러한 특허청구범위와 균등한 것들에 의해 정해져야 한다.
As described above, the present invention has been described with reference to the accompanying drawings, but various modifications and changes can be made without departing from the spirit of the present invention. Therefore, the scope of the present invention should not be limited to the described embodiments, but should be determined by the equivalents of the claims, as well as the following claims.

11 : 내층
12 : 중간층
13 : 외층
14 : 실링부11: inner layer
12: middle layer
13: outer layer
14: sealing part

Claims (2)

포장 봉투에 있어서,
피포장물에 접촉되며, 중밀도폴리에틸렌(MDPE) 80～85 중량%와 대전방지제 15～20 중량%가 포함되는 내층;
상기 내층의 외측에 형성되며, 메탈로센 선형저밀도폴리에틸렌(MLLDPE)으로 이루어지는 중간층; 및
상기 중간층의 외측에 형성되며, 메탈로센 선형저밀도폴리에틸렌(MLLDPE) 18～22 중량%와 저밀도폴리에틸렌(LDPE) 27～33 중량%와 고밀도폴리에틸렌(HDPE) 27～33 중량%와 대전방지제 15～20 중량%가 포함되는 외층
을 포함하는 것을 특징으로 하는 포장용 봉투.
In the packaging bag,
An inner layer in contact with the package and including 80 to 85% by weight of medium density polyethylene (MDPE) and 15 to 20% by weight of an antistatic agent;
An intermediate layer formed on an outer side of the inner layer and made of metallocene linear low density polyethylene (MLLDPE); And
It is formed on the outside of the intermediate layer, 18 to 22% by weight of metallocene linear low density polyethylene (MLLDPE), 27 to 33% by weight of low density polyethylene (LDPE), 27 to 33% by weight of high density polyethylene (HDPE) and antistatic agent 15 to 20 Outer layer containing% by weight
Packaging bag, characterized in that it comprises a.
포장 봉투에 있어서,
피포장물에 접촉되며, 중밀도폴리에틸렌(MDPE) 80～85 중량%와 대전방지제 15～20 중량%가 포함되는 내층;
상기 내층의 외측에 형성되며, 메탈로센 선형저밀도폴리에틸렌(MLLDPE)으로 이루어지는 중간층; 및
상기 중간층의 외측에 형성되며, 저밀도폴리에틸렌(LDPE) 40～42.5 중량%와 고밀도폴리에틸렌(HDPE) 40～42.5 중량%와 대전방지제 15～20 중량%가 포함되는 외층
을 포함하는 것을 특징으로 하는 포장용 봉투.In the packaging bag,
An inner layer in contact with the package and including 80 to 85% by weight of medium density polyethylene (MDPE) and 15 to 20% by weight of an antistatic agent;
An intermediate layer formed on an outer side of the inner layer and made of metallocene linear low density polyethylene (MLLDPE); And
It is formed on the outside of the intermediate layer, the outer layer containing 40 to 42.5% by weight of low density polyethylene (LDPE), 40 to 42.5% by weight of high density polyethylene (HDPE) and 15 to 20% by weight of an antistatic agent
Packaging bag, characterized in that it comprises a.
KR1020100124597A 2010-12-08 2010-12-08 Envelope for packing KR101175129B1 (en)