KR101152430B1 - artificial floating island for water purification using functional ceramic - Google Patents

artificial floating island for water purification using functional ceramic Download PDF

Info

Publication number
KR101152430B1
KR101152430B1 KR1020090019885A KR20090019885A KR101152430B1 KR 101152430 B1 KR101152430 B1 KR 101152430B1 KR 1020090019885 A KR1020090019885 A KR 1020090019885A KR 20090019885 A KR20090019885 A KR 20090019885A KR 101152430 B1 KR101152430 B1 KR 101152430B1
Authority
KR
South Korea
Prior art keywords
ceramic
functional
weight
water
water purification
Prior art date
Application number
KR1020090019885A
Other languages
Korean (ko)
Other versions
KR20100101410A (en
Inventor
백순기
Original Assignee
백순기
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 백순기 filed Critical 백순기
Priority to KR1020090019885A priority Critical patent/KR101152430B1/en
Publication of KR20100101410A publication Critical patent/KR20100101410A/en
Application granted granted Critical
Publication of KR101152430B1 publication Critical patent/KR101152430B1/en

Abstract

본 발명은 수생식물을 강 또는 담수호의 수면에 유동하지 않도록 배치하여 인공부도를 조성하되, 그 하단에 로도박터미생물세라믹, 바실러스미생물세라믹, 아시네토박터미생물세라믹, 기능성탈질세라믹, 기능성흡착세라믹으로 구성된 기능성세라믹을 종방향으로 다수 연설하여, 상기 기능성세라믹의 작용으로 강 또는 담수호의 수질이 현저히 개선될 수 있도록 하는 기능성세라믹 수질정화부도에 관한 것으로, 장방의 형상으로 내부에 소정의 공간부(110)를 형성하고, 적당한 강도를 구비하는 고정판(100), 상기 고정판(100)의 하단에 고정되며, 수위의 변환에 따라 이동되어 수면에 떠 있도록 발포체를 이용하여 부력을 구비한 부유체(200), 상기 고정판(100)의 공간부(110)를 횡단하도록 고정판(100) 사이에 일개이상 연결되는 연결로프(300), 상기 연결로프(300) 하단에 종방향으로 다수 연결되어 수질을 정화하도록 구비되는 기능성세라믹(400), 상기 연결로프(300) 상단에 고정되며, 천연 섬유질로 이루어져 수생식물(20)을 식재하도록 구비되는 식생매트(500), 상기 부유체(200)의 유동범위를 한정하기 위해, 상기 부유체(200)에 연결되는 중량체(600)로 이루어진 구성이다.The present invention is to arrange the aquatic plants so as not to flow on the surface of the river or freshwater lake to create an artificial buoy, consisting of Rhodobacterium microceramic, Bacillus microbial ceramic, Acinetobacter microbial ceramic, functional denitrification ceramic, functional adsorption ceramic The functional ceramic water purification section for remarkably improving the quality of the river or freshwater lake by the function of the functional ceramic by addressing a large number of functional ceramics, the predetermined space portion 110 inside the rectangular shape. Formed to form a fixed plate 100 having a suitable strength, fixed to the bottom of the fixed plate 100, the floating body 200 with buoyancy using a foam to be floating on the water surface is moved in accordance with the conversion of the water level, One or more connecting ropes 300 connected between the fixing plates 100 to cross the space 110 of the fixing plate 100 and the connecting ropes 300. Functional ceramic 400, which is connected to the bottom in the longitudinal direction to purify the water quality, fixed to the top of the connecting rope 300, made of natural fiber vegetation mat 500 is provided to plant the aquatic plant 20 In order to limit the flow range of the floating body 200, the weight body 600 is connected to the floating body 200.

수질정화, 세라믹, 인공부도, 로도박터, 바실러스, 아시네토박터 Water Purification, Ceramic, Artificial Buoy, Rhodobacter, Bacillus, Acinetobacter

Description

기능성세라믹 수질정화부도{artificial floating island for water purification using functional ceramic}Artificial floating island for water purification using functional ceramic

본 발명은 기능성세라믹 수질정화부도에 관한것으로, 더욱 상세하게는 수생식물을 강 또는 담수호의 수면에 유동하지 않도록 배치하여 인공부도를 조성하되, 그 하단에 로도박터미생물세라믹, 바실러스미생물세라믹, 아시네토박터미생물세라믹, 기능성탈질세라믹, 기능성흡착세라믹으로 구성된 기능성세라믹을 종방향으로 다수 연설하여, 상기 기능성세라믹의 작용으로 강 또는 담수호의 수질이 현저히 개선될 수 있도록 하는 기능성세라믹 수질정화부도에 관한 것이다.The present invention relates to a functional ceramic water purification buoy, and more particularly, to create an artificial buoy by arranging aquatic plants so as not to flow on the surface of the river or freshwater lake, but at the bottom of Rhodobacterium microceramic, Bacillus microceramic, Acineto Functional ceramics, functional denitrification ceramics, functional adsorption ceramics, and a plurality of functional ceramics in the longitudinal direction, the functional ceramics water purification purification function so that the water quality of the river or freshwater lake can be significantly improved by the action of the functional ceramics.

일반적으로 담수호 및 하천에는 지표의 오수와, 생활하수, 농축산 폐수 등이 지속적으로 유입되는 반면 정수의 출입이 활발하지 않기 때문에 수중의 오염물질의 농도가 증가하게 된다. 특히, 질소화합물 및 인산염 등을 포함하는 영양염류의 증가는 수중에서 부영양화 현상을 야기하게 된다.In general, while freshwater lakes and streams continuously receive surface sewage, domestic sewage, and agricultural and livestock wastewater, while the infiltration of purified water is not active. Therefore, the concentration of pollutants in the water increases. In particular, an increase in nutrients, including nitrogen compounds and phosphates, causes eutrophication in water.

상기와 같은 부영양화는 수중의 용존산소량을 낮춰 물의 탁도 저하 또는 부패물에 의한 악취를 발생시키고, 심할 경우 어류를 집단 페사 시키는 등의 심각한 피해를 끼치게 된다. 따라서, 수중생태계에 포함된 질소나 인 등의 영양물질의 양 이 자체 정화능력을 초과하지 않도록 균형을 유지하는 것이 매우 중요하다. The eutrophication as described above lowers the amount of dissolved oxygen in the water, causing deterioration of water turbidity or odor caused by decayed water, and, in severe cases, serious damage such as collective pesa of fish. Therefore, it is very important to maintain a balance so that the amount of nutrients such as nitrogen and phosphorus in the aquatic ecosystem does not exceed its own purification capacity.

수질을 정화하고 다양한 생물의 서식환경을 조성하기 위해서는 가능한 만ㄹ은 식물이 생육할 수 있는 공간을 만들어 주어야 한다. 식물은 물속의 질소와 인을 영양분으로 흡수하여 제거해주며, 물속에 산소를 공급해주고, 미생물이 부착하여 서식할 수 있는 공간을 확보해 주므로, 수질의 정화와 다양한 생물의 서식처를 제공하는 중요한 역할을 수행한다.In order to purify water and to create a habitat for various organisms, it is necessary to create as much space as possible for plants to grow. Plants absorb and remove nitrogen and phosphorus in the water as nutrients, supply oxygen to the water, and secure a space for microorganisms to attach and inhabit, thus playing an important role in purifying water and providing habitat for various organisms. To perform.

종래에 제시된 대부분의 인공부도는 합성수지류 또는 파이프 안에 발포성 물질이 충진된 구조의 부력체와 그 상부에 수생식물을 식재할 수 있는 식재용 매트를 형성한다. 이러한 종래의 인공부도의 구조는 수생식물이 수중의 오염물질을 유기물의 형태로 흡수해여 하므로 수생식물에 의한 수질정화의 효과가 낮다는 문제점이 있다.Most of the artificial buoys proposed in the art form a buoyant body of a structure filled with a foamable material in a synthetic resin or pipe and a mat for planting aquatic plants thereon. The conventional artificial banking structure has a problem in that the water purification effect of water purification by aquatic plants is low because aquatic plants absorb the pollutants in the water in the form of organics.

본 발명은 강 또는 담수호의 수면에 수생식물을 부유하도록 식재하여 녹지를 조성하고, 이의 작용으로 자연경관이 미려해지도록 하며, 물속의 부영양화를 일으키는 영양물질의 흡착을 가능케 하고, 기능성 세라믹의 작용으로, 수중의 질소, 인, 유기물을 흡착, 분해합에 따라 수질정화를 기대할 수 있는 기능성세라믹 수질정화부도를 제공하는 데 그 목적이 있다.The present invention is to plant the aquatic plants to float on the surface of the river or freshwater lake to create a greenery, the natural landscape is beautiful by its action, to enable the adsorption of nutrients that cause eutrophication in the water, by the action of functional ceramics The purpose is to provide a functional ceramic water purification unit that can be expected to purify the water according to the adsorption and decomposition of nitrogen, phosphorus, organic matter in the water.

또한, 수중 미생물의 플록형성을 촉진하여 침강성을 향상시키며, 이에 따라 담수호의 수질이 현저히 개성될 뿐 아니라, 그 구조가 간단하게 이루어져 관리 및 보수가 용이하며, 자연친화 방식으로 수질을 정화토록 하는 기능성세라믹 수질정화부도의 제공을 그 목적으로 한다.In addition, it promotes floc formation of aquatic microorganisms, thereby improving sedimentation. Accordingly, the quality of freshwater lakes is notably remarkable, and its structure is simplified to facilitate management and repair, and to purify water quality in a natural manner. An object of the present invention is to provide a ceramic water purification part.

상기와 같은 목적을 달성하기 위한 본 발명은 내부에 소정의 공간부를 형성하는 고정판과, 상기 고정판의 하단에 고정되는 부유체, 상기 고정판을 횡단하도록 연결되는 연결로프, 상기 연결로프 하단에 구비되는 기능성세라믹, 상기 연결로프 상단에 고정되는 식생매트, 상기 부유체에 연결되는 중량체로 구성된 기능성세라믹 수질정화부도를 제공한다.The present invention for achieving the above object is a fixed plate to form a predetermined space therein, a floating body fixed to the lower end of the fixing plate, a connecting rope connected to cross the fixing plate, the functionality provided at the bottom of the connecting rope It provides a functional ceramic water purification section consisting of a ceramic, a vegetation mat fixed to the top of the connecting rope, a weight connected to the floating body.

본 발명은 또한, 상기 기능성세라믹은 로도박터미생물세라믹, 바실러스미생물세라믹, 아시네토박터미생물세라믹, 기능성탈질세라믹, 기능성 흡착세라믹으로 구성된 기능성세라믹 수질정화부도를 제공한다.The present invention also provides a functional ceramic water purification part comprising Rhodobacterium microceramic, Bacillus microbial ceramic, Acinetobacter microbial ceramic, functional denitrification ceramic, and functional adsorption ceramic.

또한, 상기 각각의 미생물 세라믹(로도박터미생물세라믹, 바실러스미생물세라믹, 아시네토박터미생물세라믹)은 황토 86 ~ 94중량%, 목분 5 ~ 10중량%, 무기바인더 1 ~ 4중량%를 혼합하여 소정의 형태로 성형하고, 상기 성형된 성형체를 건조한 후, 800 ~ 1000℃의 온도에서 90 ~ 150분 동안 가열하여 소성하여 세라믹을 형성하고, 세라믹의 표면에 각각의 미생물 농축액(로도박터미생물농축액, 바실러스미생물농축액, 아시네토박터미생물농축액)을 부착하여 이루어진 기능성세라믹 수질정화부도를 제공한다.In addition, each of the microorganism ceramics (Rhodobacterium microceramic, Bacillus microbial ceramic, Acinetobacter microceramic ceramic) is a mixture of 86 to 94% by weight ocher, 5 to 10% by weight wood powder, 1 to 4% by weight inorganic binder After shaping, the molded body is dried and then heated and baked at a temperature of 800 to 1000 ° C. for 90 to 150 minutes to form a ceramic, and each microorganism concentrate (Rodobacterium microorganism concentrate, Bacillus microorganism) is formed on the surface of the ceramic. It provides a functional ceramic water purification buoy made by attaching a concentrate, an acetobacter microorganism concentrate).

본 발명 기능성세라믹 수질정화부도에 따르면 강 또는 담수호의 수면에 수생식물을 부유하도록 식재하여 녹지를 조성하고, 이의 작용으로 자연경관이 미려해지도록 하며, 물속의 부영양화를 일으키는 영양물질의 흡착을 가능케 하며, 기능성 세라믹의 작용으로, 수중의 질소, 인, 유기물을 흡착, 분해합에 따라 수질정화를 기대할 수 있는 매우 유용한 효과가 있다.According to the functional ceramic water purification budo according to the present invention, aquatic plants are planted to float on the surface of rivers or freshwater lakes to form green areas, and the natural scenery is beautiful by the action thereof, and the adsorption of nutrients causing eutrophication in water is possible. By the action of functional ceramics, there is a very useful effect that can be expected to purify the water according to the adsorption and decomposition of nitrogen, phosphorus, organic matter in the water.

또한, 수중 미생물의 플록형성을 촉진하여 침강성을 향상시키며, 이에 따라 담수호의 수질이 현저히 개성될 뿐 아니라, 그 구조가 간단하게 이루어져 관리 및 보수가 용이하며, 자연친화 방식으로 수질을 정화토록 하는 효과가 있다.In addition, it promotes floc formation of aquatic microorganisms and improves sedimentation. Accordingly, the quality of freshwater lakes is not only remarkably improved, but the structure of the freshwater lake is simple to manage and repair, and to purify water quality in a natural way. There is.

이하 첨부된 도면에 따라 본 발명 기능성세라믹 수질정화부도의 구성 및 작용을 더욱 상세히 설명하면 다음과 같다.Hereinafter, the configuration and operation of the functional ceramic water purification part of the present invention according to the accompanying drawings will be described in more detail.

도 1은 본 발명 기능성세라믹 수질정화부도의 분해사시도이고, 도 2는 기능 성세라믹의 연결되는 과정을 도시한 순서도이며, 도 3은 본 발명 기능성세라믹 수질정화부도의 일실시예를 도시한 사시도이다.1 is an exploded perspective view of the functional ceramic water purification part of the present invention, Figure 2 is a flow chart showing the process of connecting the functional ceramic water purification, Figure 3 is a perspective view showing an embodiment of the functional ceramic water purification part of the present invention. .

본 발명 기능성세라믹 수질정화부도(10)는 내부에 소정의 공간부(110)를 형성하는 고정판(100)과, 상기 고정판(100)의 하단에 고정되는 부유체(200)와, 상기 공간부(110)를 횡단하도록 연결되는 연결로프(300)와, 상기 연결로프(300) 하단에 구비되는 기능성세라믹(400)과, 상기 연결로프(300) 상단에 고정되는 식생매트(500)와, 상기 부유체(200)의 유동범위를 한정하는 중량체(600)로 구성된다.The functional ceramic water purification part 10 of the present invention includes a fixed plate 100 for forming a predetermined space portion 110 therein, a floating body 200 fixed to a lower end of the fixed plate 100, and the space portion ( Connection rope 300 connected to cross 110, the functional ceramic 400 is provided at the bottom of the connection rope 300, the vegetation mat 500 is fixed to the connection rope 300, and the part It is composed of a weight body 600 defining a flow range of the fluid 200.

먼저 상기 고정판(100)은 장방의 형상으로 내부에 소정의 공간부(110)를 형성하고, 적당한 강도를 구비하는 구성이다.First, the fixing plate 100 is formed in a rectangular shape with a predetermined space portion 110 therein, and is configured to have a suitable strength.

고정판(100)은 연결로프(300) 및 그 하단에 연속적으로 꿰어지는 기능성세라믹(400)을 지지하여야 하고, 최종적으로 완성되어 설치된 후에는 사람들이 이동하면서 주변 경관을 감상할 수 있는 산책로 및 관리, 보수를 하기 위한 통로로 이용되어야 하므로, 경량이면서도 고강도의 소재로 구성됨이 마땅하다. 그 형태는 상기한 내용에서 장방형이라고 하였지만 사각형상 뿐 아니라, 원형, 격자형을 비롯한 내부에 공간부(110)를 형성하여 연결로프(300)의 횡단이 가능한 테두리 형상의 모든 다양한 형태로 구성될 수 있음을 밝혀두는 바이고, 소정의 두께를 형성하여 연결로프(300)의 고정이 용이하도록 한다.The fixed plate 100 should support the connecting rope 300 and the functional ceramic 400 sewn continuously at the bottom thereof, and after the final installation is completed, the walkway and management for people to appreciate the surrounding scenery while moving, Since it should be used as a passage for repairing, it should be composed of a light weight and high strength material. The shape is said to be rectangular in the above description, but may be formed in all various forms of a border shape that can be traversed through the connecting rope 300 by forming a space 110 inside the circular, lattice, as well as a rectangular shape. Baigo, which has been found to be present, forms a predetermined thickness to facilitate fixing of the connecting rope 300.

부유체(200)는 상기 고정판(100)의 하단에 고정되며, 수위의 변화에 따라 이동되어 수면에 떠 있도록 발포체를 이용하여 부력을 구비한다.Floating body 200 is fixed to the lower end of the fixed plate 100, has a buoyancy by using a foam to move in accordance with the change in the water level floating on the water surface.

상기 부유체(200)는 일체형으로 구성되거나, 다수의 부유체(200)가 로우 프(210)로 상호 연결되어 구성됨이 바람직 하고, 고정판(100), 기능성세라믹(400), 식생매트(500) 및 식재되는 수생식물(20) 그리고 고정판(100)위를 걷는 사람이 중량에 의해 물속에 가라앉지 않고 떠있는 상태를 유지하도록 부력을 구비한 소재로 구비되며, 통상적으로 사용되는 스티로폼과 같은 발포체를 비롯하여, 부력을 구비한 금속 및 천연의 다양한 소재로 대체될 수 있다.The floating body 200 is formed in one piece, or a plurality of floating bodies 200 are preferably interconnected by a rope 210, the fixed plate 100, functional ceramic 400, vegetation mat 500 And aquatic plants 20 and planted aquatic plants 20 is provided with a buoyant material to maintain a floating state does not sink in the water by weight, the foam such as styrofoam commonly used In addition, it can be replaced with a variety of natural materials and buoyant metal.

부유체(200)의 형상은 사각형상을 갖지만, 이에 한정치 아니하고 오각형, 육각형과 같은 다각형 이나, 원형 등의 다양한 형태로 구비될 수 있다.The floating body 200 may have a quadrangular shape, but is not limited thereto. The floating body 200 may be provided in various forms such as a pentagon, a polygon such as a hexagon, or a circle.

연결로프(300)는 상기 고정판(100)의 공간부(110)를 횡단하도록 고정판(100)을 상호 연결하여 고정되며, 상기 연결로프(300)는 나란히 평행하게 연결되거나, 서로 교차하도록 연결될 수 있고, 밧줄과 같은 끈을 비롯하여, 단단한 소재의 막대나 봉으로도 구비될 수 있다. 상기 연결로프(300)의 하단에는 수직되는 방향으로 기능성세라믹(400)이 다수 고정된다.The connecting rope 300 is fixed by connecting the fixing plate 100 to cross the space portion 110 of the fixing plate 100, the connecting rope 300 may be connected to be parallel to each other or to cross each other and It may also be provided with a rod or rod of a rigid material, including a rope such as a rope. A plurality of functional ceramics 400 are fixed to the lower end of the connection rope 300 in a vertical direction.

상기 기능성세라믹(400)은 침수되어 수질을 정화하도록 구비되는 구성으로, 수질개선능력이 탁월한 다양한 기능성세라믹(400)을 구슬 꿰듯이 로우프(460)에 고정하여 물과 접촉면적을 최대화 하여 수질정화능력을 향상시키고, 그 길이는 장소에 따라 다양하게 변동 가능하며, 하나의 로우프(460)에 다양한 기능성세라믹(400)을 꿸 수 있고, 로우프(460)마다 별도의 기능성세라믹(400)을 꿸 수 있음은 물론이다.The functional ceramic 400 is immersed in a configuration that is provided to purify the water quality, the various functional ceramics 400 having excellent water quality improvement ability to be fixed to the rope 460 as if threading the beads to maximize the water and water purification capacity It is possible to vary the length according to the place, and various functional ceramics 400 can be placed on one rope 460, and a separate functional ceramic 400 can be placed on each rope 460. Of course.

여기서, 상기 기능성세라믹(400)은 로도박터(Rhodobactor)미생물세라믹(410), 바실러스(Bacillus)미생물세라믹(420), 아시네토박터(Acinetobacter)미생 물세라믹(430), 기능성탈질세라믹(440), 기능성 흡착세라믹(450)으로 구성된다.Here, the functional ceramic 400 is Rhodobacter (Rhodobactor) micro-ceramic 410, Bacillus (Bacillus) micro-ceramic 420, Acinetobacter microorganisms ceramic (430), functional denitrification ceramic (440), It consists of a functional adsorption ceramic 450.

일반적으로, 로도박터(Rhodobactor) 미생물은 광합성 세균으로 수중에서 질산성질소를 에너지원으로 사용하여 질소가스 형태로 대기중으로 방출시킴으로써 효과적으로 탈질기능을 수행할 수 있는 특성이 있으며, 동절기와 같이 수온이 낮아 미생물 활성이 저하될 경우 음이온 계열 광물질로 제조된 기능성 탈질세라믹(220)에 의해 질산성질소나 아질산성질소에 결합되어 있는 산소를 광물질에 결합시킴으로써 질소제거가 동시에 이루어지도록 하는 작용을 한다.In general, Rhodobactor microorganism is a photosynthetic bacterium, which uses nitrogen nitrate as an energy source in the water and releases it into the atmosphere in the form of nitrogen gas, which effectively performs denitrification. When the microbial activity is lowered by the functional denitrification ceramic 220 made of anion-based minerals, the oxygen is bonded to the mineral by nitrous nitrate or nitrite nitrogen to the mineral to remove the nitrogen at the same time.

상기 로도박터미생물 세라믹(410)은 황토 86 ~ 94중량%, 목분 5 ~ 10중량%, 무기바인더 1 ~ 4중량%를 혼합하여 소정의 형태로 성형하고, 상기 성형된 성형체를 건조한 후, 800 ~ 1000℃의 온도에서 90 ~ 150분 동안 가열하여 소성하여 세라믹을 형성하고, 세라믹의 표면에 로도박터(Rhodobactor)미생물 농축액을 부착하여 구성되며, 로도박터(Rhodobactor)미생물 농축액에 기공이 형성된 세라믹을 대략 20 ~ 30시간 동안 침전시켜 로도박터(Rhodobactor)미생물이 기공 사이에 집적되어 부착하도록 한다. The Rhodobacterium microorganism ceramic 410 is molded into a predetermined form by mixing 86 to 94% by weight of ocher, 5 to 10% by weight of wood powder, and 1 to 4% by weight of an inorganic binder, and drying the formed molded body, and then 800 to 800%. It is formed by heating and firing at a temperature of 1000 ° C. for 90 to 150 minutes to form a ceramic, and attaching a Rhodobacter microorganism concentrate to the surface of the ceramic, and roughly forming a ceramic having pores in the Rhodobactor microorganism concentrate. Settle for 20-30 hours to allow Rhodobactor microorganisms to accumulate and adhere between the pores.

황토는 세라믹을 전체적인 구성을 위해 구비되며, 살균력이 강한 원적외선의 발산이 큰 특성상 세균의 살균은 물론 극히 미세한 여과공을 형성하여 유해물질의 제거를 완벽하게 할 수 있어, 수중생물의 어병 및 어충을 퇴치하고, 세균을 감소시키기 위해 구성된다. 상기 황토의 혼합량이 86중량% 미만으로 구비될 경우, 내구성이 저하되며, 황토의 다양한 효과를 기대하기 어렵고, 94중량%를 초과하여 구비될 경우 기공의 형성이 러여워져 로도박터(Rhodobactor)미생물 농축액의 집적이 어려워지므로 86 ~94중량%의 황토를 혼합하는 것이 바람직하다.Ocher is provided for the whole composition of the ceramic, and because of the strong dissipation of far-infrared rays with strong sterilizing power, it is possible to sterilize bacteria and form extremely fine filter holes to completely remove harmful substances. To combat and reduce bacteria. When the mixing amount of the loess is provided in less than 86% by weight, the durability is lowered, it is difficult to expect the various effects of the loess, when it is provided in excess of 94% by weight, the formation of pores becomes poor Rhodobactor (Rhodobactor) microbial concentrate It is preferable to mix 86 to 94% by weight of ocher because it becomes difficult to accumulate.

목분은 5 ~ 10중량% 구비되며, 세라믹에 기공을 형성하기 위한 구성으로, 5중량% 미만으로 혼합될 경우 기공이 적어져, 로도박터(Rhodobactor)미생물 농축액의 집적이 어려워지고, 10중량%를 초과하여 혼합될 경우 강도가 낮아져 세라믹의 지속성이 저하되므로, 5 ~ 10중량%의 목분을 혼합하는 것이며, 상기 기공의 크기는 나노단위로 구비될 수 있다.Wood flour is provided with 5 to 10% by weight, the composition for forming pores in the ceramic, when less than 5% by weight is less porosity, it becomes difficult to accumulate Rhodobactor microbial concentrate, 10% by weight When it is mixed in excess, since the strength is lowered and the persistence of the ceramic is lowered, 5 to 10% by weight of wood flour is mixed, and the pore size may be provided in nano units.

무기바인더는 상기 황토와 목분의 접착력을 부여하기 위한 구성으로, 1중량% 미만으로 혼합될 경우 결합력이 저하되고, 4중량%를 초과하여 혼합될 경우 제작단가가 상승하여 경제적이지 못하므로 1 ~4중량%의 무기바인더를 혼합하는 것이다. Inorganic binder is a constitution for imparting the adhesion of the loess and wood powder, when the mixture is less than 1% by weight, the bonding strength is lowered. It is to mix the inorganic binder by weight.

또한, 가열온도는 800 ~ 1000℃로 이루어지는 것이 바람직하며, 가열온도가 800℃ 미만일 경우, 소성이 제대로 이루어지지 않으며, 1000℃를 초과하는 온도로 가열할 경우 황토의 성분이 변질되어 황토의 효능이 제대로 발휘되지 않으므로, 800 ~ 1000℃의 온도로 가열하는 것이며, 가열시간 또한, 90분 미만으로 이루어질 경우 소성이 제대로 이루어지지 않아, 내구성이 견고하지 못하고, 150분을 초과하여 이루어질 경우 황토의 성분이 변질되어 황토의 효능이 제대로 발휘되지 않으므로 90 ~ 150분의 시간 동안 가열시키는 것이 바람직하다.In addition, the heating temperature is preferably made of 800 ~ 1000 ℃, if the heating temperature is less than 800 ℃, the baking is not done properly, when heated to a temperature exceeding 1000 ℃ the component of the loess is deteriorated to improve the efficacy of the loess Since it is not properly exhibited, it is heated to a temperature of 800 ~ 1000 ℃, heating time is also less than 90 minutes when the baking is not done properly, durability is not solid, if it is made for more than 150 minutes of the ocher component It is preferable to heat it for a time of 90 to 150 minutes because it is deteriorated and the efficacy of ocher is not properly exhibited.

상기 로도박터(Rhodobactor) 미생물 농축액은 로도박터(Rhodobactor) 미생물을 추출하여 배양하고, 배양된 로도박터(Rhodobactor) 미생물을 1g당 적어도 15억 ~ 25억 개체가 포함되도록 농축하여 구비되는 구성이다. 상기 로도박터(Rhodobactor) 미생물의 개체수는 다량으로 구비될수록 효과적이지만, 그 효과가 15억 ~ 25억 개체를 전후로 하여 뚜렷한 차이를 보이지 않으므로 경제적인 측면을 고려하여 1g당 15억 ~ 25억 개체가 포함되도록 농축 구성되는 것이다.The Rhodobacter (Rhodobactor) microorganism concentrate is configured to extract and culture the Rhodobacter (Rhodobactor) microorganism, and to concentrate the cultured Rhodobacter (Rhodobactor) microorganism to contain at least 1.5 billion to 2.5 billion individuals per g. The number of Rhodobactor microorganisms is more effective when provided in large quantities, but since the effect does not show a distinct difference between about 1.5 billion to 2.5 billion individuals, it includes 1.5 to 2.5 billion individuals per 1g in consideration of economic aspects. Concentrate as much as possible.

또한, 상기 바실러스 미생물 세라믹(420)은 황토 86 ~ 94중량%, 목분 5 ~ 10중량%, 무기바인더 1 ~ 4중량%를 혼합하여 소정의 형태로 성형하고, 상기 성형된 성형체를 건조한 후, 800 ~ 1000℃의 온도에서 90 ~ 150분 동안 가열하여 소성하여 세라믹을 형성하고, 세라믹의 표면에 바실러스 미생물 농축액을 부착하여 구성되며, 바실러스(Bacillus) 미생물 농축액에 기공이 형성된 세라믹을 대략 20 ~ 30시간 동안 침전시켜 바실러스(Bacillus)미생물이 기공 사이에 부착되어 집적되도록 한다. In addition, the Bacillus microbial ceramic 420 is molded into a predetermined shape by mixing 86 to 94% by weight of ocher, 5 to 10% by weight of wood powder, and 1 to 4% by weight of inorganic binder, and after drying the molded body, 800 It is formed by heating and baking at a temperature of ~ 1000 ℃ for 90 to 150 minutes to form a ceramic, by attaching a Bacillus microbial concentrate on the surface of the ceramic, the pores formed in the Bacillus microbial concentrate about 20 to 30 hours Precipitate to allow Bacillus microorganisms to adhere and accumulate between pores.

참고로, 세라믹에 대한 설명은 상기 로도박터미생물세라믹(410)에서 설명한 바와 같으므로 생략한다. 상기 바실러스(Bacillus) 미생물 농축액은 바실러스(Bacillus) 미생물을 추출하여 배양하고, 배양된 바실러스(Bacillus) 미생물을 1g당 적어도 15억 ~ 25억 개체가 포함되도록 농축하여 구비되는 구성이다. 상기 바실러스(Bacillus) 미생물의 개체수는 다량구비될수록 효과적이지만, 그 효과가 15억 ~ 25억 개체를 전후로 하여 뚜렷한 차이를 보이지 않으므로 경제적인 측면을 고려하여 1g당 15억 ~ 25억 개체가 포함되도록 농축 구성되는 것이다.For reference, the description of the ceramic is the same as described in the Rhodobacterium micro-ceramic 410 is omitted. The Bacillus (Bacillus) microbial concentrate is configured to extract and culture Bacillus (Bacillus) microorganisms, and to concentrate the cultured Bacillus (Bacillus) microorganisms to contain at least 1.5 billion to 2.5 billion individuals per g. The population of the Bacillus microorganism is effective as a large amount, but the effect does not show a distinct difference between about 1.5 billion to 2.5 billion individuals, so concentrated to include 1.5 billion to 2.5 billion individuals per 1g in consideration of economic aspects It is composed.

더불어, 상기 아시네토박터(Acinetobacter) 미생물 세라믹(430)은 황토 86 ~ 94중량%, 목분 5 ~ 10중량%, 무기바인더 1 ~ 4중량%를 혼합하여 소정의 형태로 성형하고, 상기 성형된 성형체를 건조한 후, 800 ~ 1000℃의 온도에서 90 ~ 150분 동안 가열하여 소성하여 세라믹을 형성하고, 세라믹의 표면에 아시네토박터(Acinetobacter) 미생물 농축액을 부착하여 이루어진 구성이다.In addition, the Acinetobacter microbial ceramic 430 is molded in a predetermined form by mixing 86 to 94% by weight of ocher, 5 to 10% by weight of wood powder, and 1 to 4% by weight of inorganic binder, and the molded body After drying, it is heated by heating at a temperature of 800 to 1000 ° C. for 90 to 150 minutes to form a ceramic, and is formed by attaching an acinetobacter microorganism concentrate on the surface of the ceramic.

또한, 상기 상기 아시네토박터(Acinetobacter) 미생물 농축액은 아시네토박터(Acinetobacter) 미생물을 추출하여 배양하고, 배양된 아시네토박터(Acinetobacter) 미생물을 1g당 적어도 15억 ~ 25억 개체가 포함되도록 농축하여 구비되는 것이며, 상기 세라믹(800)에 대한 설명은 상기한 내용에서 확인할 수 있으므로 생략하기로 한다.In addition, the Acinetobacter microbial concentrate is extracted by culturing Acinetobacter microorganisms, and concentrated to contain at least 1.5 billion to 2.5 billion individuals of cultured Acinetobacter microorganisms per 1g Since the description of the ceramic 800 can be confirmed in the above description, it will be omitted.

기능성탈질세라믹(440)은 수중에 함유되어 있는 질소를 효과적으로 제거시키고, 슬러지를 감소시켜 수질을 안정화시키는 효과가 있다. 기능성탈질세라믹(440)의 산화칼슘(CaO)이 수중의 질소를 흡착하여 반응된 질산칼슘(Ca(NO3)2)은 무색의 단사정계의 결정으로 100℃ 이상에서는 무수물이 되며 무수물은 무색의 등축정계의 분말이며, 모두 조해성을 나타내고, 질산염이나 연화(煙火)의 제조에 사용되며, 속효성 비료로서는 질산석회라고 하는 생리적 염기성 비료이며, 질산 상태의 질소 10～12%, 수용성 석회 28%를 함유하고, 흡습성이 대단히 강하기 때문에 그다지 사용되지 않았는데, 최근 시설재배에 점차 많이 사용되고 있어 흡착반응하여 배출된 질산칼슘을 비료로 재활용할 수 있다.The functional denitrification ceramic 440 effectively removes nitrogen contained in water and reduces sludge to stabilize water quality. The calcium nitrate (Ca (NO 3 ) 2 ) reacted by calcium oxide (CaO) of the functional denitrification ceramic 440 adsorbed nitrogen in water is a colorless monoclinic crystal and becomes anhydride at 100 ° C. or higher, and the anhydride is colorless. It is a powder of equiaxed crystal system, all show deliquescent property, and it is used for the production of nitrate and softening. As a fast-acting fertilizer, it is a physiological basic fertilizer called lime nitrate. And, because it is very hygroscopic, it was not used very much, but recently it is increasingly used in plant cultivation, the calcium nitrate discharged by adsorption reaction can be recycled as fertilizer.

또한, 상기 기능성 흡착세라믹(450)은 패각성분, 규조토, 탄산칼슘, 유기 및 무기 바인더를 혼합하고, 소결소성한 다공성 결정체로서, 유기물의 흡착 및 음이온 및 양이온의 흡착 분해, 고농도 미생물의 활성유지 기능과 사상균의 증식 억제 및 규조입자에 의한 미생물 플록(floc)형성에 핵을 제공함으로써, 침강성을 증가시키 는 작용을 하며, 수중에 함유되어 있는 중금속 및 COD성 유기물, 악취성 물질을 효과적으로 흡착하여 수질을 안정화시키는 효과가 있다.In addition, the functional adsorption ceramic 450 is a shell crystal, a mixture of diatomaceous earth, calcium carbonate, organic and inorganic binders, sintering and firing porous crystals, adsorption decomposition of organic matter and adsorption decomposition of anions and cations, maintaining the activity of high concentration microorganisms It provides a nucleus to inhibit the growth of filamentous fungi and to form microbial flocs by diatom particles, thereby increasing sedimentation, and effectively adsorbing heavy metals, COD organic substances, and odorous substances contained in water. It is effective to stabilize.

상기 식생매트(500)는 상기 연결로프(300) 상단에 구비되어 수생식물(20)을 식재하여 식생할 수 있도록 하며, 환경 친화적인 천연소재의 코코넛 등에서 추출한 섬유질로 구성됨이 바람직하다. 이 때, 수생식물(20)의 이탈을 장지하는 그믈망이 별도로 구비될 수 있고, 천연 부직포 및 흙이 채워진 포트가 구비되어 다양한 수생식물(20) 뿐 아니라, 수변식물 및 육상식물의 식생을 용이하도록 할 수 있다.The vegetation mat 500 is provided on the top of the connecting rope 300 to plant the aquatic plant 20, and is preferably composed of fibers extracted from coconut, such as environmentally friendly natural materials. At this time, the gemma to prevent the separation of the aquatic plant 20 may be provided separately, and a natural nonwoven fabric and a soil-filled port is provided to facilitate the vegetation of water plants and terrestrial plants as well as various aquatic plants 20. You can do that.

코코넛섬유로 이루어진 식생매트(500)는 코코넛 섬유가 갖는 고유의 다공성에 기인하여 하천이나 호수 등의 질소와 인 등을 비롯한 각종 영양원을 흡수하여 부영양화를 방지하고, 흡수된 질소와 인은 미생물에 의해 무기물로 분해되어 수생식물(20)의 생육을 촉진시켜 수질정화 기능을 더욱 효과적으로 수행할 수 있다.The vegetation mat 500 made of coconut fiber prevents eutrophication by absorbing various nutrients including nitrogen and phosphorus such as rivers and lakes due to the inherent porosity of coconut fiber, and the absorbed nitrogen and phosphorus are absorbed by microorganisms. Decomposed into inorganic matters to promote the growth of the aquatic plant 20 can perform water purification function more effectively.

상기 수생식물(20)은 일반적으로 다년생 식물 및 정수식물인 갈대, 달뿌리풀, 부들, 노랑꽃창포, 큰고랭이, 세모랭이, 줄, 삿갓사초, 골풀 등이 식재되는 것이 바람직하다. 갈대 또는 창포와 같은 수생식물(20)을 식재할 경우 뿌리공간에서 영양소와 미생물의 상호작용을 돕는 작용을 하고, 수초와의 교체현상을 기대할 수 있으며, 이에 따라 수중의 부영양화를 야기하는 각종 영양물질을 흡착하여, 수질이 정화된다.The aquatic plant 20 is generally a perennial plant and water plants, such as reeds, moon root grass, boulders, yellow irises, larvae, sesame seeds, strings, Satsatsu sedge, it is preferable that the plant is planted. When planting aquatic plants (20) such as reeds or irises can help the interaction of nutrients and microorganisms in the root space, and can be expected to replace the plants with a variety of nutrients that cause eutrophication of the water accordingly Is adsorbed to purify the water quality.

중량체(600)는 상기 부유체의 이동범위를 한정하기 위해, 부유체에 연결되는 것으로, 로우프(610)와 연결되어 하천 및 호수 바닥에 고정시키는 구성이다. 상기 중량체(600)는 쉽게 부식되지 않으면서 적당한 중량을 구비한 앵커, 블록, 추, 자 연석 등의 다양한 형태를 가질 수 있다,The weight body 600 is connected to the float in order to limit the moving range of the float, is connected to the rope 610 is fixed to the river and lake bottom. The weight body 600 may have various forms such as anchors, blocks, weights, magnetites, etc. having appropriate weights without being easily corroded.

상기한 바와 같이, 본 발명 기능성세라믹 수질정화부도(10)에 따르면 강 또는 담수호의 수면에 수생식물을 부유하도록 식재하여 녹지를 조성하고, 이의 작용으로 자연경관이 미려해지도록 하며, 물속의 부영양화를 일으키는 영양물질의 흡착을 가능케 하며, 기능성 세라믹의 작용으로, 수중의 질소, 인, 유기물을 흡착, 분해합에 따라 수질정화를 기대할 수 있고, 수중 미생물의 플록형성을 촉진하여 침강성을 향상시키며, 이에 따라 담수호의 수질이 현저히 개성될 뿐 아니라, 그 구조가 간단하게 이루어져 관리 및 보수가 용이하며, 자연친화 방식으로 수질을 정화토록 하는 장점이 있다.As described above, according to the functional ceramic water purification buoy 10 of the present invention, planting aquatic plants to float on the surface of the river or freshwater lake to create a greenery, the natural landscape is beautiful by its action, and eutrophication in water It enables the adsorption of nutrients that occur, and by the action of functional ceramics, water purification can be expected by adsorption and decomposition of nitrogen, phosphorus and organic matter in water, and it promotes flocculation of microorganisms in the water, thereby improving sedimentation. Accordingly, the fresh water lakes are not only remarkably individualized, but also have a simple structure, which is easy to manage and repair, and has the advantage of purifying water in a natural manner.

도 1은 본 발명 기능성세라믹 수질정화부도의 분해사시도,1 is an exploded perspective view of the functional ceramic water purification buoy of the present invention,

도 2는 기능성세라믹의 연결되는 과정을 도시한 순서도,2 is a flowchart illustrating a process of connecting functional ceramics;

도 3은 본 발명 기능성세라믹 수질정화부도의 일실시예를 도시한 사시도.Figure 3 is a perspective view showing one embodiment of the functional ceramic water purification part of the present invention.

<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>

10 : 기능성세라믹 수질정화부도10: Functional ceramic water purification department

20 : 수생식물20: aquatic plants

100 : 고정판100: fixed plate

110 : 공간부110: space part

200 : 부유체200: floating body

210, 460, 610 : 로우프210, 460, 610: Rope

300 : 연결로프300: connecting rope

400 : 기능성세라믹400: Functional ceramic

410 : 로도박터미생물세라믹410: Rhodobacterium microceramic

420 : 바실러스미생물세라믹420: Bacillus microbial ceramic

430 : 아시네토박터미생물세라믹430: Acinetobacter microbial ceramic

440 : 기능성탈질세라믹440: Functional denitrification ceramic

450 : 기능성흡착세라믹450: functional adsorption ceramic

500 : 식생매트500: Vegetation Mat

600 : 중량체600: weight

Claims (5)

장방의 형상으로 내부에 소정의 공간부(110)를 형성하고, 적당한 강도를 구비하는 고정판(100);A fixed plate 100 having a predetermined space portion 110 formed therein in a rectangular shape and having an appropriate strength; 상기 고정판(100)의 하단에 고정되며, 수위의 변환에 따라 이동되어 수면에 떠 있도록 발포체를 이용하여 부력을 구비한 부유체(200);A floating body 200 fixed to the lower end of the fixing plate 100 and having a buoyancy force by using a foam to be floating on the surface by being moved according to the change of the water level; 상기 고정판(100)의 공간부(110)를 횡단하도록 고정판(100) 사이에 일개이상 연결되는 연결로프(300);One or more connection ropes 300 connected between the fixing plates 100 to traverse the space 110 of the fixing plate 100; 상기 연결로프(300) 하단에 종방향으로 다수 연결되어 수질을 정화하도록 구비되는 기능성세라믹(400);Functional ceramic 400 is connected to the lower portion of the connection rope 300 in the longitudinal direction provided to purify the water quality; 상기 연결로프(300) 상단에 고정되며, 천연 섬유질로 이루어져 수생식물(20)을 식재하도록 구비되는 식생매트(500);Vegetation mat 500 is fixed to the top of the connecting rope 300, made of natural fibers provided to plant the aquatic plant 20; 상기 부유체(200)의 유동범위를 한정하기 위해, 상기 부유체(200)에 연결되는 중량체(600); 로 구성되며,A weight body 600 connected to the float 200 to define a flow range of the float 200; Lt; / RTI &gt; 기능성세라믹(400)은 로도박터(Rhodobactor)미생물세라믹(410), 바실러스(Bacillus)미생물세라믹(420), 아시네토박터(Acinetobacter)미생물세라믹(430), 기능성탈질세라믹(440), 기능성 흡착세라믹(450)으로 구성된 것을 특징으로 하는 기능성세라믹 수질정화부도에 있어서,The functional ceramic 400 is a Rhodobactor microbial ceramic 410, Bacillus microbial ceramic 420, Acinetobacter microceramic 430, functional denitrification ceramic 440, functional adsorption ceramic ( In the functional ceramic water purification section, characterized in that consisting of 450), 상기 로도박터(Rhodobactor)미생물 세라믹(410)은 황토 86 ~ 94중량%, 목분 5 ~ 10중량%, 무기바인더 1 ~ 4중량%를 혼합하여 소정의 형태로 성형하고, 상기 성형된 성형체를 건조한 후, 800 ~ 1000℃의 온도에서 90 ~ 150분 동안 가열하여 소성하여 세라믹을 형성하고, 세라믹의 표면에 로도박터(Rhodobactor)미생물 농축액을 부착하여 이루어진 것을 특징으로 하는 기능성세라믹 수질정화부도.The Rhodobacter (Rhodobactor) microorganism ceramic 410 is molded into a predetermined shape by mixing 86 to 94% by weight of ocher, 5 to 10% by weight of wood powder, and 1 to 4% by weight of an inorganic binder, and after drying the molded body , Functional ceramic water purification unit, characterized in that by heating for 90 to 150 minutes at a temperature of 800 ~ 1000 ℃ to form a ceramic, by attaching the Rhodobacter (Rhodobactor) microbial concentrate on the surface of the ceramic. 삭제delete 삭제delete 제 1항에 있어서, 상기 바실러스(Bacillus) 미생물 세라믹(420)은 황토 86 ~ 94중량%, 목분 5 ~ 10중량%, 무기바인더 1 ~ 4중량%를 혼합하여 소정의 형태로 성형하고, 상기 성형된 성형체를 건조한 후, 800 ~ 1000℃의 온도에서 90 ~ 150분 동안 가열하여 소성하여 세라믹을 형성하고, 세라믹의 표면에 바실러스 미생물 농축액을 부착하여 이루어진 것을 특징으로 하는 기능성세라믹 수질정화부도.According to claim 1, The Bacillus (Bacillus) microbial ceramic 420 is molded in a predetermined form by mixing 86 to 94% by weight of ocher, 5 to 10% by weight of wood powder, 1 to 4% by weight of inorganic binder, the molding After the dried molded body is dried, and heated for 90 to 150 minutes at a temperature of 800 ~ 1000 ℃ to form a ceramic, and functional ceramic water purification unit, characterized in that by attaching the Bacillus microorganism concentrate on the surface of the ceramic. 제 1항에 있어서, 상기 아시네토박터(Acinetobacter) 미생물 세라믹(430)은 황토 86 ~ 94중량%, 목분 5 ~ 10중량%, 무기바인더 1 ~ 4중량%를 혼합하여 소정의 형태로 성형하고, 상기 성형된 성형체를 건조한 후, 800 ~ 1000℃의 온도에서 90 ~ 150분 동안 가열하여 소성하여 세라믹을 형성하고, 세라믹의 표면에 아시네토박터(Acinetobacter) 미생물 농축액을 부착하여 이루어진 것을 특징으로 하는 자연정화습지 기능성세라믹 수질정화부도.According to claim 1, The Acinetobacter microbial ceramic 430 is molded into a predetermined shape by mixing 86 to 94% by weight of ocher, 5 to 10% by weight of wood powder, 1 to 4% by weight of inorganic binder, After drying the molded body, it is heated by heating for 90 to 150 minutes at a temperature of 800 ~ 1000 ℃ to form a ceramic, characterized in that the nature made by attaching the Acinetobacter microorganism concentrate on the surface of the ceramic Purification Wetland Functional Ceramic Water Purification
KR1020090019885A 2009-03-09 2009-03-09 artificial floating island for water purification using functional ceramic KR101152430B1 (en)