KR101025429B1 - 단열효과를 강화시킨 건축물의 단열방수공법 - Google Patents
단열효과를 강화시킨 건축물의 단열방수공법 Download PDFInfo
- Publication number
- KR101025429B1 KR101025429B1 KR1020100045290A KR20100045290A KR101025429B1 KR 101025429 B1 KR101025429 B1 KR 101025429B1 KR 1020100045290 A KR1020100045290 A KR 1020100045290A KR 20100045290 A KR20100045290 A KR 20100045290A KR 101025429 B1 KR101025429 B1 KR 101025429B1
- Authority
- KR
- South Korea
- Prior art keywords
- coated
- composition
- waterproofing
- perlite
- expanded
- Prior art date
Abstract
본 발명은 건축물의 단열효과를 증대시키기 위한 방수공법에 관한 것으로, 상세하게는 인장강도 및 파단강도를 향상시킨 단열효과를 가진 팽창 퍼라이트 조성물을 이용하여 건축물의 방수공법을 개시하는 것이다.
Description
본 발명은 건축물의 단열효과를 증대시키기 위한 방수공법에 관한 것으로, 상세하게는 인장강도 및 파단강도를 향상시킨 단열효과를 가진 팽창 퍼라이트 조성물을 이용한 건축물의 단열방수공법에 관한 것이다.
각종 건축물의 누수방지를 위한 방수공사는 특히 콘크리트 건축 구조물의 유지 및 보수를 위해서는 필수적인 산업분야이다.
일반적으로 건물 옥상이나 주차장의 상부 등에는 누수를 방지하기 위해 방수공사를 하는데, 시공상 편의로 일정 규격의 방수시트 위에 단열재(예를 들어, 스치로폼)를 이용하는 공사가 널리 채택되고 있다. 그러나, 방수시트는 온도변화에 민감하기 때문에 수축과 팽창이 잘 발생하고 이에 따라 방수성능이 저하될 뿐만 아니라 물의 침투로 인해 단열효과도 현저히 감소시키고 있다.
뿐만 아니라, 방수시트는 규격화된 크기로 인해서 시트 간에 이음부가 발생할 수 있으며, 이러한 이음부로 인해 방수성능이 크게 저하되고 하자의 원인이 되고 있다.
한편으로는, 건축물의 단열공사를 위해서는 상기한 방수공사와 별개로 시공하거나, 방수효과를 가진 시트를 별개로 이용하고 있기 때문에 상기한 바와 같은 종래의 문제점을 피할 수가 없었다.
또한, 종래의 단열 및 방수공사는 여러 공정을 거치는 단계로 구성되는바, 예를 들어, 콘크리트 구조물 위에 시트 방수공사를 하고 그 위에 단열재(예로서, 스치로폼)를 설치하며 그 위에 다시 와이어 매쉬 및 누름몰탈 공사를 수행하는 것이 일반적인 공법이다. 따라서, 공정이 복잡하고 단가가 비싼 단점이 있을 뿐만 아니라 사용되는 단열재에 따라서 화재시에 유독가스가 발생함으로써 심각한 문제점이 있다.
현재, 단열효과의 증대를 위해서 퍼라이트를 이용한 공법이 연구되고 있다.
퍼라이트는 급격한 열에 의하여 희고 기공이 많은 경량의 물질 형태로 팽창될 수 있는 휘발 성분을 함유하고 있는 비정질 암석이다. 상기 퍼라이트를 미세하게 분쇄하여 1000℃ 이상의 고열을 급격히 가하면, 상기 퍼라이트에 함유된 휘발 성분이 가스화되어 연화된 입자의 내부에서 팽창하면서 가스가 빠져나가 내부에 기공이 형성된다. 이때, 상기 퍼라이트 본래 부피보다 대략 10 내지 20배 팽창된 팽창 퍼라이트가 형성된다.
상기 팽창 퍼라이트는 기밀한 소기포가 유리질 피막에 둘러싸인 형상을 갖기 때문에 가볍고, 중성의 무기물 재질로써 독성이 없고 불연성을 가지며, 많은 기공으로 인하여 단열성 및 흡음성이 뛰어난 장점이 있다. 최근 이러한 팽창 퍼라이트의 장점들을 활용하여 다양한 산업 분야에 이용되고 있다. 특히, 팽창 퍼라이트는
천장재, 인테리어재, 칸막이재 및 단열재 등의 건축용 자재, 극장, 공연장, 체육관 등의 음향 시설, 도로, 철도 및 터널 등의 방음벽, 토양 개량 및 인공 토양 등의 농업 분야 등에 사용된다.
그러나 상기 건축용 자재에 상기 팽창 퍼라이트가 사용되는 경우, 친환경 요소 및 경량성 등은 크게 개선되지만, 상기 팽창 퍼라이트 자체의 기공성에 의하여 구조물의 강도가 떨어지는 결함이 있고, 흡수성으로 인해 외장재로는 사용할 수 ㅇ없는 단점이 있다.
본 발명은 상기와 같은 종래의 문제점을 해결코자 하는 것으로, 건축물의 옥상이나 큰 하중을 받는 바닥 등에 단열효과가 큰 퍼라이트 조성물을 사용하여 단열 및 방수공사를 일괄처리할 수 있도록 한 것이다.
특히, 본 발명에 사용되는 퍼라이트는 친환경적 재료로서 단열성, 불연성, 및 흡음성이 탁월하기 때문에 건축자재로서 유용하게 사용할 수 있도록 하는 것이 본 발명의 또 다른 목적이다.
또한 본 발명에 따른 단열방수공법은 종래의 단열 및 방수 공사를 대체하여 일괄처리할 수 있도록 하고 뿐만 아니라 종래의 화재시에 발생하는 유독가스를 방지하는 것이 본 발명의 또 다른 목적이다.
상기한 목적을 달성하기 위해 본 발명에 의한 방수공법은 다음의 수단으로 구성된다:
방수공사를 하기 위한 피도포면을 하지정리하는 단계;
에폭시계, 아크릴계, 또는 우레탄계 수지 중 최소한 하나로 이루어진 프라이머로서 1차 도포하는 단계;
팽창 퍼라이트 분쇄 입자에 수성 에멀젼계, 초산 비닐 수지계, 아크릴수지계, 에폭시수지계, 또는 실리케이트계 접착제 중 하나로 선택한 접착제에 의해서 코팅한 다음, 이러한 접착성 합성수지로 코팅된 퍼라이트 입자를 시멘트, 백토, 또는 황토 등의 분말을 입혀서 인장강도 및 파단강도를 강화시킨 코팅된 강화 퍼라이트 조성물과 에폭시계, 아크릴계, 또는 우레탄계 수지 중 최소한 하나의 수지와 혼합된 혼합물로 30 내지 100 mm의 두께로 도장하는 단계; 및
폴리우레아, 폴리우레탄, 또는 무기질계 방수재로 0.5 내지 3 mm 두께로 코팅하는 단계.
본 발명에 따른 방수공법에 의해서 시공된 건축물은 우수한 단열효과, 불연성 및 흡음성을 가지고 있을 뿐만 아니라 친환경적 소재로서 건축물의 외장 및 바닥 공사에 유용하게 사용할 수 있는 강도를 나타낸다.
뿐만 아니라, 단열 및 방수공사를 일괄처리함으로써 공정이 간단하고 비용이 저렴하며, 화재시에 유독가스를 발생시키지 않는 장점이 있다.
특히, 가건축물에 주로 사용하는 샌드위치 판넬을 본 발명에 따른 단열방수공법을 사용할 경우에는 탁월한 단열효과를 얻을 수 있을 뿐만 아니라 화재시 발생하는 유독가스로부터의 피해를 줄일 수가 있다.
이하 본 발명에 따른 단열방수공법을 설명하기로 한다.
먼저, 퍼라이트 암석을 분쇄하여 소정의 크기로 입자를 만든 다음 이렇게 분쇄된 입자를 고온 가열하여 0.5 내지 5 mm의 직경을 가진 팽창 퍼라이트 입자를 준비한다.
상기한 크기의 퍼라이트 입자에 접착성이 뛰어난 수성 에멀젼계, 초산 비닐 수지계, 아크릴수지계, 에폭시수지계, 또는 실리케이트계 접착제를 사용하여 코팅한다.
상기한 바와 같이 접착제로 코팅된 퍼라이트 입자에 퍼라이트를 강화 시키기 위해 시멘트, 황토, 또는 백토로서 입자를 혼합하여 코팅 강화 퍼라이트 조성물을 준비한다.
먼저, 단열 및 방수공사를 하기 위한 피도포면을 종래의 방법에 의해서 하지 정리한다.
하지정리된 피도포면에 종래의 방법에 의해서 프라이머를 이용하여 1차 도포한다.
1차 도포가 완료된 피도포면에 상기 코팅된 강화 퍼라이트 조성물과 방수재를 혼합한 혼합 방수재를 30 내지 100 mm의 두께로 도포한다. 이때 사용되는 방수재는 초산 비닐계, 아크릴계, 에폭시계, 또는 우레탄계 수지를 사용하되 이는 상기 입자형태의 코팅된 강화 퍼라이트 조성물이 서로 결합하도록 하는 역할을 하도록 하는 것이다.
상기 코팅된 강화 퍼라이트 혼합액으로 도포된 면을 최종 방수재를 종래의 방법에 따라 0.5 내지 3 mm의 두께로 도포한다.
실시예
1. 입경 1 내지 3 mm의 팽창 퍼라이트를 접착제 용액과 섞는다. 이때 사용되는 접착제는 희석된 에폭시 수지계를 사용한다.
2. 상기 코팅된 퍼라이트를 시멘트 분말과 혼합하여 입자형태의 코팅된 강화 퍼라이트 조성물을 준비한다.
3. 방수 및 단열을 위한 피도포면을 하지정리한 후 에폭시계 프라이머로 도포한다.
4. 프라이머로 도포된 피도포면에 상기 준비된 입자형태의 코팅 강화 퍼라이트 조성물과 에폭시 수지를 혼합한 혼합 조성물을 30 내지 100 mm의 두께로 도포한다.
5. 상기 도포된 면에 폴리우레아를 0.5 내지 3 mm 두께로 도포한다.
Claims (2)
- 다음의 단계를 포함하는 단열방수공법:
0.5 내지 5 mm의 직경을 가진 팽창 퍼라이트 입자에 접착성과 방수성이 뛰어난 수성 에멀젼계, 초산 비닐 수지계, 아크릴수지계, 에폭시수지계, 또는 실리케이트계 접착제를 사용하여 코팅한 다음 시멘트, 황토 또는 백토로서 입자를 입혀 강화 퍼라이트 조성물을 준비하는 단계;
단열 및 방수공사를 하기 위한 피도포면을 하지 정리한 후에 프라이머를 이용하여 도포하는 단계;
상기 도포가 완료된 피도포면에 상기 코팅된 강화 퍼라이트 조성물과 방수재를 혼합한 혼합 방수재를 30 내지 100 mm의 두께로 도포하되 방수재는 아크릴계, 에폭시계, 또는 우레탄계 수지를 사용하는 것으로 이는 상기 입자형태의 코팅된 강화 퍼라이트 조성물이 서로 결합하도록 하는 역할을 하도록 하는 도포 단계; 및
상기 코팅된 강화 퍼라이트 조성물로 도포된 면을 폴리우레아, 폴리우레탄, 무기질계 코팅제, 또는 엘라스토머 탄성체를 이용하여 0.5 내지 3 mm의 두께로 최종 도포하는 단계.
- 제 1 항에 있어서, 강화 퍼라이트 조성물을 준비하는 단계에서 팽창 퍼라이트 분쇄 입자를 강화 퍼라이트 조성물과 혼합하여 사용하거나 팽창 퍼라이트 만을 사용하는 단계를 포함하는 단열방수공법.