KR101017909B1 - 전지 제조용 원통형 전지캔 및 그것의 제조방법 - Google Patents
전지 제조용 원통형 전지캔 및 그것의 제조방법 Download PDFInfo
- Publication number
- KR101017909B1 KR101017909B1 KR1020090004861A KR20090004861A KR101017909B1 KR 101017909 B1 KR101017909 B1 KR 101017909B1 KR 1020090004861 A KR1020090004861 A KR 1020090004861A KR 20090004861 A KR20090004861 A KR 20090004861A KR 101017909 B1 KR101017909 B1 KR 101017909B1
- Authority
- KR
- South Korea
- Prior art keywords
- battery
- cylindrical
- inner diameter
- main body
- body portion
- Prior art date
Abstract
Description
불량률 | 평균 전지용량 | |
실시예 1 | 0.1% | 2605mAh |
실시예 2 | 0.1% | 2623mAh |
비교예 1 | 0.5% | 2215mAh |
비교예 2 | 0.2% | 2220mAh |
비교예 3 | 0.2% | 2605mAh |
전류차단 부재 단락煎 leakage 발생 |
단락後 leakage 발생 |
Leakage 미발생 |
|
실시예 1 | 0/30 | 0/30 | 30/30 |
실시예 2 | 0/30 | 0/30 | 30/30 |
비교예 1 | 0/30 | 10/30 | 20/30 |
비교예 2 | 0/30 | 3/30 | 27/30 |
비교예 3 | 0/30 | 22/30 | 19/30 |
전압(V) | 저항(mΩ) | 누액 | ||||||
실험전 | 실험후 | 변화율 | 실험전 | 실험후 | 변화율 | 발생개수 | 발생 cycle | |
실시예 1 | 4.179 | 4.179 | 0% | 49.4 | 49.6 | 0.4% | 0/30 | - |
실시예 2 | 4.179 | 4.179 | 0% | 48.9 | 49.0 | 0.2% | 0/30 | - |
비교예 1 | 4.179 | 4.179 | 0% | 58.6 | 58.9 | 0.51% | 1/30 | 9cycle |
비교예 2 | 4.179 | 4.179 | 0% | 58.7 | 58.9 | 0.34% | 3/30 | 8/8/9cycle |
비교예 3 | 4.179 | 4.179 | 0% | 48.6 | 48.9 | 0.62% | 2/30 | 8/9cycle |
Claims (15)
- 개방된 상부, 원통을 이루는 측벽 및 원통의 하부를 이루는 하면으로 이루어진 전지 제조용 원통형 캔에 있어서, 상기 측벽은 전극조립체가 삽입되는 본체부와, 캡 어셈블리의 장착을 위해 비딩부 및 클림핑부가 형성되는 상단부로 이루어져 있고, 상기 원통형 캔의 길이는 50 내지 100 mm이고, 상기 상단부의 길이는 7 내지 10 mm이며, 상기 상단부의 두께(t2)는 본체부의 두께(t1) 보다 크고, 상기 상단부의 외경(R2)은 본체부의 외경(r2) 보다 크며, 상기 상단부의 내경(R1)은 본체부의 내경(r1) 보다 작은 것을 특징으로 하는 원통형 전지캔.
- 제 1 항에 있어서, 상기 본체부의 두께(t1)는 0.1 내지 0.3 mm이고, 상기 상단부의 두께(t2)는 본체부의 두께(t1)에 대하여 100% 초과 내지 180% 이하인 것을 특징으로 하는 원통형 전지캔.
- 제 1 항에 있어서, 상기 본체부의 내경(r1)은 17.5 초과 내지 17.9 mm 이고, 상기 상단부의 내경(R1)은 본체부의 내경(r1)보다 작은 범위에서 17.5 내지 17.7 mm 이며, 상기 본체부의 외경(r2)은 17.6 내지 18.2 mm이고, 상단부의 외경(R2)은 상기 본체부의 외경(r2)보다 큰 범위에서 17.9 내지 18.3 mm인 것을 특징으로 하는 원통 형 전지캔.
- 제 1 항에 있어서, 상기 본체부의 직경(r)은 하기 식을 만족하는 것을 특징으로 하는 원통형 전지캔.r = (R2 + R1) / 2
- 삭제
- 제 1 항에 있어서, 상기 원통형 캔은 스테인리스 스틸, 스틸, 알루미늄 또는 그 합금 중 어느 하나의 소재로 이루어진 것을 특징으로 하는 원통형 전지캔.
- 제 1 항 내지 제 4 항 및 제 6 항 중 어느 하나에 따른 원통형 전지캔을 제조하는 방법으로서,(a) 금속 판재를 소정의 다이와 펀치를 사용하여 딥 드로잉함으로써, 두께(t1)의 상단부와 두께(t2)의 본체부를 포함하고 상기 상단부와 본체부의 내경이 동일한 원통형 캔 구조의 중간 가공체를 제조하는 과정; 및(b) 상기 중간 가공체를 소정의 다이와 펀치를 사용하여 가공함으로써, 두께(t1)의 본체부와 두께(t2)의 상단부를 포함하고 상기 상단부의 외경이 본체부의 외경보다 크며 동시에 상단부의 내경이 본체부의 내경 보다 작은 원통형 캔을 제조하는 과정;을 포함하는 것을 특징으로 하는 원통형 전지캔의 제조방법.
- 제 7 항에 있어서, 상기 과정(a)의 딥 드로잉은,외경(Rp)이 원통형 캔의 본체부의 내경(r1)에 대응하는 크기인 펀치; 및원통형 캔의 상단부에 대응하는 내경(Ra)이 r1+t2이고, 본체부에 대응하는 내경(Rb)이 r1+t1인 다이;를 사용하여 수행하는 것을 특징으로 하는 원통형 전지캔의 제조방법.
- 제 7 항에 있어서, 상기 과정(b)의 가공은,외경(Rp')이 원통형 캔의 본체부의 내경(r1) 보다 작은 펀치; 및원통형 캔의 상단부에 대응하는 내경(Ra ')이 r1+t2 보다 작고 r1+t1 보다 큰 다이;를 사용하여 수행하는 것을 특징으로 하는 원통형 전지캔의 제조방법.
- 제 9 항에 있어서,상기 펀치의 외경(Rp')는 Rp-(t2- t1)/2이고,상기 다이의 상단부 내경(Ra ')는 Ra-(t2-t1)/2이고 본체부 내경(Rb ')은 R+t1인 것을 특징으로 하는 원통형 전지캔의 제조방법.
- 제 7 항에 있어서, 상기 과정(b)의 가공은,외경(Rp')이 원통형 캔의 본체부의 내경(r1) 보다 작은 펀치; 및원통형 캔의 본체부에 대응하는 내경(Rb ')이 Ra' 보다 작고 r1+t1과 동일하거나 그 보다 큰 다이;를 사용하여 수행하는 것을 특징으로 하는 원통형 전지캔의 제조방법.
- 제 7 항에 있어서, 상기 과정(a) 이전에, 내경이 일정한 다이와 펀치를 사용하여 원통형 캔의 본체부에 대응하는 깊이로 딥 드로잉 하는 과정(a-1)을 추가로 포함하는 것을 특징으로 하는 원통형 전지캔의 제조방법.
- 제 12 항에 있어서, 상기 과정(a-1)은 깊이가 순차적으로 깊어지는 순서로 다수의 다이 및 펀치들을 사용하여 수행하는 것을 특징으로 하는 원통형 전지캔의 제조방법.
- 제 13 항에 있어서, 상기 과정(a-1)은 내경이 순차적으로 작아지는 다이와 외경이 순차적으로 작아지는 펀치로 구성된 일련의 다수의 다이들과 펀치들을 사용하여 수행하는 것을 특징으로 하는 원통형 전지캔의 제조방법.
- 제 1 항 내지 제 4 항 및 제 6 항 중 어느 하나에 따른 원통형 전지캔을 포함하는 이차전지.