KR101016774B1 - Epoxy adhesive for repairing water supply and sewage pipe - Google Patents
Epoxy adhesive for repairing water supply and sewage pipe Download PDFInfo
- Publication number
- KR101016774B1 KR101016774B1 KR1020100028342A KR20100028342A KR101016774B1 KR 101016774 B1 KR101016774 B1 KR 101016774B1 KR 1020100028342 A KR1020100028342 A KR 1020100028342A KR 20100028342 A KR20100028342 A KR 20100028342A KR 101016774 B1 KR101016774 B1 KR 101016774B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- epoxy
- sewage pipe
- water
- Prior art date
Abstract
Description
본 발명은 콘크리트나 플라스틱으로 이루어진 상하수도 관을 보수하는데 사용되는 상하수도관 보수용 에폭시 접착제에 관한 것으로, 더욱 상세하게는 에폭시 혼합물, 희석제, 경화제, 소포제, 첨가제, 산화방지제, 사슬확장제 및 충전제를 포함하여 이루어진다.
The present invention relates to an epoxy adhesive for water and sewage pipe repair used to repair a water and sewage pipe made of concrete or plastic, and more specifically, including an epoxy mixture, a diluent, a curing agent, an antifoaming agent, an additive, an antioxidant, a chain extender and a filler. Is done.
본 발명은 휘발성 유기화합물 이나 포르말린을 함유하지 않고도 기계적 및 화학적 물성이 우수한 상하수도관 보수용 에폭시 접착제에 관한 것으로, 더욱 상세하게는 에폭시 혼합물, 희석제, 경화제, 소포제, 첨가제, 산화방지제, 사슬확장제 및 충전제를 포함하여 이루어진다.The present invention relates to an epoxy adhesive for water and sewage pipe repair having excellent mechanical and chemical properties without containing volatile organic compounds or formalin. It is made, including.
에폭시 접착제는 페놀수지계, 요소수지계, 멜라닌수지계, 우레탄 수지계, 크실렌수지계 및 아세트산비닐계 등의 합성 고분자계 접착제가 있으며, 이들은 각종 산업에 접착제로 많이 사용되고 있다.Epoxy adhesives include synthetic polymer adhesives such as phenol resins, urea resins, melanin resins, urethane resins, xylene resins and vinyl acetates, which are widely used as adhesives in various industries.
일반적인 에폭시 접착제는 비스페놀-A 혹은 F 타입의 에폭시 수지를 많이 사용하고 있고 이들을 경화시키기 위한 경화제 및 소포제 등이 사용되고 있으며, 이들의 상용성을 위해 희석제를 통해 점도를 조절한다.In general epoxy adhesives, bisphenol-A or F type epoxy resins are used a lot, and a curing agent and an antifoaming agent for curing them are used, and the viscosity is adjusted through a diluent for their compatibility.
기존의 비스페놀 타입의 에폭시수지로는 diglycidyl ether of bisphenol-F와 diglycidyl ether of bisphenol-A 두 가지 타입이 상업적으로 폭넓게 사용되고 있다.Existing bisphenol type epoxy resins are widely used commercially with diglycidyl ether of bisphenol-F and diglycidyl ether of bisphenol-A.
그러나 전술한 두 가지 에폭시 수지는 고온에서의 열 안정성이 낮아 구조재의 재료로는 적합하지 못한 문제점이 있었다.
However, the two epoxy resins described above have a problem that the thermal stability at high temperature is not suitable as a material of the structural material.
본 발명의 목적은 기존의 비스페놀-F 타입의 에폭시 수지에 폴리우레탄 또는 폴리우레아를 첨가하여 고온에서의 열적 안정성을 갖는 상하수도관 보수용 에폭시 접착제를 제공하는 것이다.It is an object of the present invention to provide an epoxy adhesive for water and sewage pipe repair having thermal stability at high temperature by adding polyurethane or polyurea to an existing bisphenol-F type epoxy resin.
본 발명의 다른 목적은 기계적 물성, 경화효율 및 수도관 내부와의 접착성이 우수한 상하수도관 보수용 에폭시 접착제를 제공하는 것이다.Another object of the present invention is to provide an epoxy adhesive for water and sewage pipe repair excellent in mechanical properties, curing efficiency and adhesion to the inside of the water pipe.
본 발명의 다른 목적은 유해물질의 용출량이 기준치 이하인 상하수도관 보수용 에폭시 접착제를 제공하는 것이다.
Another object of the present invention is to provide an epoxy adhesive for repairing water and sewage pipes in which the amount of harmful substances eluted is less than the reference value.
본 발명의 목적은 에폭시 혼합물 10 내지 90 중량부, 희석제 0.1 내지 50 중량부, 경화제 10 내지 90 중량부, 소포제 0.1 내지 10 중량부, 첨가제 0.1 내지 20 중량부, 산화방지제 0.1 내지 1 중량부, 사슬확장제 0.01 내지 5 중량부 및 충전제 0.5 내지 3 중량부를 포함하여 이루어지는 것을 특징으로 하는 상하수도관 보수용 에폭시 접착제를 제공함에 의해 달성된다.An object of the present invention is 10 to 90 parts by weight of epoxy mixture, 0.1 to 50 parts by weight of diluent, 10 to 90 parts by weight of curing agent, 0.1 to 10 parts by weight of antifoaming agent, 0.1 to 20 parts by weight of additive, 0.1 to 1 parts by weight of antioxidant, chain It is achieved by providing an epoxy adhesive for water and sewage pipe repair, characterized in that it comprises 0.01 to 5 parts by weight of the expanding agent and 0.5 to 3 parts by weight of the filler.
본 발명의 바람직한 특징에 따르면, 상기 첨가제는 폴리우레탄 또는 폴리우레아로 이루어진 그룹으로부터 선택된 하나 이상을 포함하여 이루어지는 것으로 한다.According to a preferred feature of the invention, the additive is to comprise at least one selected from the group consisting of polyurethane or polyurea.
본 발명의 더 바람직한 특징에 따르면, 상기 에폭시 혼합물은 액체상의 에폭시 및 고체상의 에폭시를 포함하여 이루어지며, 상기 액체상의 에폭시는 150 내지 400의 에폭시 당량을 가지며, 상기 고체상의 에폭시는 400 내지 500의 당량을 갖는 것으로 한다.According to a more preferred feature of the invention, the epoxy mixture comprises a liquid epoxy and a solid epoxy, the liquid epoxy has an epoxy equivalent of 150 to 400, the solid epoxy is 400 to 500 equivalents It shall have.
본 발명의 더욱 바람직한 특징에 따르면, 상기 희석제는 지방족 글리시딜 에테르를 포함하여 이루어지는 것으로 한다.According to a further preferred feature of the invention, the diluent comprises aliphatic glycidyl ether.
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 경화제는 구아니딘, 우레아 및 방향족아민으로 이루어진 그룹으로부터 선택된 하나 이상을 포함하여 이루어지거나, 디시안아마이드를 포함하여 이루어지는 것으로 한다.According to a still further preferred feature of the present invention, the curing agent comprises at least one selected from the group consisting of guanidine, urea and aromatic amines, or comprises dicyamide.
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 충전제는 알루미늄 및 탄산칼슘으로 이루어진 그룹으로부터 선택된 하나 이상을 포함하여 이루어지는 것으로 한다.According to a still further preferred feature of the invention, the filler comprises at least one selected from the group consisting of aluminum and calcium carbonate.
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 산화방지제는 Tris(2,4-di-tert-butylphenyl)phosphite를 포함하여 이루어지는 것으로 한다.According to a further preferred feature of the invention, the antioxidant is to comprise Tris (2,4-di-tert-butylphenyl) phosphite.
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 사슬확장제는 1,4-부탄디올, 글리세롤, 1,2,6-헥산트리올 및 1,1,1-트리메틸올프로판으로 이루어진 그룹으로부터 선택된 하나 이상을 포함하여 이루어지는 것으로 한다.
According to a still further preferred feature of the invention, the chain extender comprises at least one selected from the group consisting of 1,4-butanediol, glycerol, 1,2,6-hexanetriol and 1,1,1-trimethylolpropane It shall be made by.
본 발명에 따른 상하수도관 보수용 에폭시 접착제는 비스페놀-F 타입의 에폭시 수지에 폴리우레탄 또는 폴리우레아를 첨가하여 고온에서도 열적 안정성이 탁월한 효과를 나타낸다.Water and sewage pipe repair epoxy adhesive according to the present invention by adding a polyurethane or polyurea to the bisphenol-F type epoxy resin exhibits excellent thermal stability at high temperatures.
또한, 기계적 물성, 경화효율 및 수도관 내부와의 접착성이 탁월한 효과를 나타낸다.In addition, mechanical properties, curing efficiency and adhesion to the inside of the water pipe exhibits an excellent effect.
또한, 유해물질의 용출량이 기준치 이하인 탁월한 효과를 나타낸다.
In addition, the elution amount of the hazardous substance is excellent below the reference value.
도 1은 실시예 1 및 비교예 1 내지 3을 통해 제조된 상하수도관 보수용 에폭시 접착제의 시간에 따른 경화정도를 나타낸 그래프.
도 2는 실시예 1 및 비교예 1 내지 3을 통해 제조된 상하수도관 보수용 에폭시 접착제의 시간에 따른 강도변화를 나타낸 그래프.1 is a graph showing the degree of curing with time of the epoxy adhesive for water and sewage pipe repair prepared through Example 1 and Comparative Examples 1 to 3.
Figure 2 is a graph showing the change in strength over time of the water and sewage pipe repair epoxy adhesive prepared in Example 1 and Comparative Examples 1 to 3.
이하에는, 본 발명의 바람직한 실시예와 각 성분의 물성을 상세하게 설명하되, 이는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 발명을 용이하게 실시할 수 있을 정도로 상세하게 설명하기 위한 것이지, 이로 인해 본 발명의 기술적인 사상 및 범주가 한정되는 것을 의미하지는 않는다.
In the following, preferred embodiments of the present invention and the physical properties of each component will be described in detail, which is intended to explain in detail enough to be able to easily carry out the invention by one of ordinary skill in the art, This does not mean that the technical spirit and scope of the present invention is limited.
본 발명에 따른 상하수도관 보수용 에폭시 접착제는 에폭시 혼합물 10 내지 90 중량부, 희석제 0.1 내지 50 중량부, 경화제 10 내지 90 중량부, 소포제 0.1 내지 10 중량부, 첨가제 0.1 내지 20 중량부, 산화방지제 0.1 내지 1 중량부, 사슬확장제 0.01 내지 5 중량부 및 충전제 0.5 내지 3 중량부를 포함하여 이루어진다.
Water and sewage pipe repair epoxy adhesive according to the present invention is 10 to 90 parts by weight of epoxy mixture, 0.1 to 50 parts by weight of diluent, 10 to 90 parts by weight of curing agent, 0.1 to 10 parts by weight of antifoaming agent, 0.1 to 20 parts by weight of additive, 0.1 antioxidant To 1 part by weight, 0.01 to 5 parts by weight of chain extender and 0.5 to 3 parts by weight of filler.
전술한 에폭시 혼합물은 10 내지 90 중량부가 첨가되며, 액체상 및 고체상의 에폭시가 혼합되어 이루어지는데, 전술한 액체상의 에폭시는 비스페놀 F와 에피클로로히드린의 반응을 통해 유도되며 150 내지 400의 에폭시 당량을 갖고, 전술한 고체상의 에폭시는 프리페놀과 에피클로로히드린으로부터 유도되며 400 내지 500의 에폭시 당량을 나타낸다.10 to 90 parts by weight of the above-mentioned epoxy mixture is added, and liquid and solid epoxy are mixed. The above-mentioned liquid epoxy is derived through the reaction of bisphenol F and epichlorohydrin and has an epoxy equivalent of 150 to 400. The solid epoxy described above is derived from prephenol and epichlorohydrin and exhibits an epoxy equivalent of 400 to 500.
전술한 액체상 및 고체상의 에폭시로 이루어진 에폭시 혼합물은 50 내지 80℃의 융점을 나타낸다.
The epoxy mixture consisting of the liquid and solid epoxy described above has a melting point of 50 to 80 ° C.
전술한 희석제는 0.1 내지 50 중량부가 첨가되며, 지방족 글리시딜 에테르를 포함하여 이루어지는데, 이러한 희석제는 상하수도관 보수용 에폭시 접착제의 점도를 일정하게 유지하는 역할을 한다.
The diluent described above is added in an amount of 0.1 to 50 parts by weight, and comprises aliphatic glycidyl ether. The diluent serves to maintain a constant viscosity of the epoxy adhesive for water and sewer repair.
전술한 경화제는 10 내지 90 중량부가 첨가되며, 구아니딘, 우레아 및 방향족아민으로 이루어진 그룹으로부터 선택된 하나 이상을 포함하여 이루어지거나, 디시안아마이드를 포함하여 이루어진다.The above-mentioned hardener is added 10 to 90 parts by weight, and comprises at least one selected from the group consisting of guanidine, urea and aromatic amine, or comprises dicyanide.
전술한 성분들로 이루어진 경화제는 20℃ 이상의 온도로 가열되면 상하수도관 보수용 에폭시 접착제의 가교반응을 유도하는 가교제의 역할을 하여 상하수도관 보수용 에폭시 접착제가 경화되도록 하는 역할을 한다.When the curing agent composed of the above-mentioned components is heated to a temperature of 20 ℃ or more serves as a crosslinking agent to induce the crosslinking reaction of the epoxy adhesive for water and sewage pipe repair serves to cure the epoxy adhesive for water and sewage pipe repair.
전술한 경화제의 함량이 10 중량부 미만이면 경화효과가 미흡하며, 경화제의 함량이 90 중량부를 초과하게 되면 경화가 너무 빠르게 진행되어 가사 시간이 짧아지게 된다.
When the content of the above-mentioned hardener is less than 10 parts by weight, the curing effect is insufficient, and when the content of the hardener exceeds 90 parts by weight, the curing proceeds too fast and the pot life becomes short.
전술한 소포제는 0.1 내지 10 중량부가 첨가되며, 파라핀상 미네랄 오일계 성분이 사용되며, 전술한 상하수도관 보수용 에폭시 접착제의 제조과정에서 발생하는 기포를 제거하는 역할을 한다.
The antifoaming agent described above is added in an amount of 0.1 to 10 parts by weight, a paraffinic mineral oil-based component is used, and serves to remove bubbles generated during the manufacturing process of the epoxy adhesive for water and sewage pipe repair described above.
전술한 첨가제는 0.1 내지 20 중량부가 첨가되며, 폴리우레탄 또는 폴리우레아로 이루어진 그룹으로부터 선택된 하나 이상을 포함하여 이루어지는데, 이러한 첨가제는 0℃ 이하의 유리전이 온도를 가지며, 상하수도관 보수용 에폭시 접착제의 접착력을 증가시키는 역할을 한다.
이때, 전술한 폴리우레탄은 이소시아네이트계 중합체 및 폴리올계 중합체의 반응에 의해 제조된다.
전술한 이소시아네이트계 중합체는 40 내지 60 중량부가 첨가되며, 파라-페닐렌디이소시아네이트, 1,6-헥사메틸렌디이소시아네이트, 톨루엔디이소시아네이트, 1,5-나프탈렌디이소시아네이트, 이소프렌디이소시아네이트, 4,4-디페닐메탄디이소시아네이트, 사이클로헥실메탄디이소시아네이트, 1,4-디이소시아네이트사이클로헥산, 1,3-비스(α,α-디메틸이소시아네이트)메틸벤젠 및 1-이소시아네이트-4-(이소시아네이트메틸)-1-메틸사이클로헥산으로 이루어진 그룹으로부터 선택된 하나로 이루어지는데, 전술한 폴리올계 중합체 성분과의 반응을 통해 폴리우레탄을 제조하는 역할을 한다.
전술한 폴리올계 중합체는 30 내지 60 중량부가 첨가되며, 에틸렌글리콜, 디에틸렌글리콜, 1,2-프로필렌글리콜, 네오펜틸글리콜, 트리메틸올프로판, 아디핀산에스테르, 세바신산에스테르, 이소프탈린산에스테르, 폴리에틸렌글리콜, 폴리프로필렌글리콜, 폴리카프로락톤, 폴리옥시프로필렌트리올 및 폴리테트라메틸렌글리콜로 이루어진 그룹으로부터 선택된 하나로 이루어지는데, 전술한 것처럼 각각 다양한 분자량을 갖는 폴리올류로 이루어진 폴리올계 중합체는 이소시아네이트계 중합체 성분과의 반응을 통해 폴리우레탄을 제조하는 역할을 한다.
The above-mentioned additive is added 0.1 to 20 parts by weight, and comprises at least one selected from the group consisting of polyurethane or polyurea, which has a glass transition temperature of 0 ° C. or less, Serves to increase adhesion.
In this case, the aforementioned polyurethane is prepared by the reaction of an isocyanate polymer and a polyol polymer.
40 to 60 parts by weight of the above-mentioned isocyanate-based polymer is added, and para-phenylene diisocyanate, 1,6-hexamethylene diisocyanate, toluene diisocyanate, 1,5-naphthalene diisocyanate, isoprene diisocyanate, 4,4-di Phenylmethane diisocyanate, cyclohexyl methane diisocyanate, 1,4-diisocyanatecyclohexane, 1,3-bis (α, α-dimethylisocyanate) methylbenzene and 1-isocyanate-4- (isocyanatemethyl) -1-methyl It consists of one selected from the group consisting of cyclohexane, and serves to prepare a polyurethane through the reaction with the aforementioned polyol-based polymer component.
30 to 60 parts by weight of the aforementioned polyol-based polymer is added, and ethylene glycol, diethylene glycol, 1,2-propylene glycol, neopentyl glycol, trimethylol propane, adipic acid ester, sebacic acid ester, isophthalic acid ester, polyethylene It consists of one selected from the group consisting of glycol, polypropylene glycol, polycaprolactone, polyoxypropylene triol, and polytetramethylene glycol. As described above, polyol polymers composed of polyols having various molecular weights are selected from isocyanate polymer components and Through the reaction of serves to prepare a polyurethane.
전술한 산화방지제는 0.1 내지 1 중량부가 첨가되며, Tris(2,4-di-tert-butylphenyl)phosphite를 포함하여 이루어지는데, 상하수도관 보수용 에폭시 접착제가 산화되는 것을 방지하는 역할을 한다.
The above-mentioned antioxidant is added 0.1 to 1 parts by weight, and comprises Tris (2,4-di-tert-butylphenyl) phosphite, which serves to prevent oxidation of the epoxy adhesive for water and sewage pipe repair.
전술한 사슬확장제는 0.01 내지 5 중량부가 첨가되며, 1,4-부탄디올, 글리세롤, 1,2,6-헥산트리올 및 1,1,1-트리메틸올프로판으로 이루어진 그룹으로부터 선택된 하나 이상을 포함하여 이루어지는데, 전술한 첨가제의 분자량을 증가시켜, 상하수도관 보수용 에폭시 접착제의 점도를 조절하는 역할을 한다.
The chain extender described above is added in an amount of 0.01 to 5 parts by weight, including one or more selected from the group consisting of 1,4-butanediol, glycerol, 1,2,6-hexanetriol and 1,1,1-trimethylolpropane It is made, by increasing the molecular weight of the above-described additive, serves to adjust the viscosity of the epoxy adhesive for water and sewage pipe repair.
전술한 충전제는 0.5 내지 3 중량부가 첨가되며, 알루미늄 및 탄산칼슘으로 이루어진 그룹으로부터 선택된 하나 이상을 포함하여 이루어지는데, 상하수도관 보수용 에폭시 접착제의 접착력을 향상시켜 주는 역할을 한다.
The filler is added 0.5 to 3 parts by weight, and comprises at least one selected from the group consisting of aluminum and calcium carbonate, and serves to improve the adhesion of the epoxy adhesive for water and sewage pipe repair.
이하에서는, 본 발명의 상하수도관 보수용 에폭시 접착제의 물성을 실시예를 들어 설명한다.
Below, the physical property of the epoxy adhesive for water and sewage pipe repair of this invention is given and demonstrated to an Example.
<실시예 1>≪ Example 1 >
비스페놀 F 타입의 에폭시(300 당량을 갖는 액체상) 40 중량부, 비스페놀 F타입의 에폭시(450 당량을 갖는 고체상) 40 중량부, 지방족 글리시딜 에테르 5 중량부, 구아니딘 25 중량부, 파라핀상 미네랄 오일 0.2 중량부, 폴리우레탄 5 중량부, Tris(2,4-di-tert-butylphenyl)phosphite 0.5 중량부, 1,4-부탄디올 2.5 중량부 및 알루미늄 1.5 중량부를 혼합하여 상하수도관 보수용 에폭시 접착제를 제조하였다.
40 parts by weight of bisphenol F type epoxy (liquid phase having 300 equivalents), 40 parts by weight of bisphenol F type epoxy (solid phase having 450 equivalents), 5 parts by weight of aliphatic glycidyl ether, 25 parts by weight of guanidine, paraffinic mineral oil 0.2 parts by weight of polyurethane, 5 parts by weight of polyurethane, 0.5 parts by weight of tris (2,4-di-tert-butylphenyl) phosphite, 2.5 parts by weight of 1,4-butanediol and 1.5 parts by weight of aluminum were prepared to prepare an epoxy adhesive for water and sewage pipe repair. It was.
<비교예 1>Comparative Example 1
비스페놀 A 타입의 에폭시(300 당량을 갖는 액체상) 40 중량부, 비스페놀 A 타입의 에폭시(450 당량을 갖는 고체상) 40 중량부, 지방족 글리시딜 에테르 5 중량부, 구아니딘 25 중량부, 파라핀상 미네랄 오일 0.2 중량부, Tris(2,4-di-tert-butylphenyl)phosphite 0.5 중량부, 1,4-부탄디올 2.5 중량부 및 알루미늄 1.5 중량부를 혼합하여 상하수도관 보수용 에폭시 접착제를 제조하였다.
40 parts by weight of bisphenol A type epoxy (liquid phase having 300 equivalents), 40 parts by weight of bisphenol A type epoxy (solid phase having 450 equivalents), 5 parts by weight of aliphatic glycidyl ether, 25 parts by weight of guanidine, paraffinic mineral oil 0.2 parts by weight, 0.5 parts by weight of Tris (2,4-di-tert-butylphenyl) phosphite, 2.5 parts by weight of 1,4-butanediol and 1.5 parts by weight of aluminum were mixed to prepare an epoxy adhesive for repairing the water pipe.
<비교예 2>Comparative Example 2
비교예 1과 동일하게 실시하되, 액체상의 에폭시 35 중량부, 고체상의 에폭시 35 중량부를 혼합하여 상하수도관 보수용 에폭시 접착제를 제조하였다.
In the same manner as in Comparative Example 1, 35 parts by weight of the liquid epoxy and 35 parts by weight of the solid epoxy were mixed to prepare an epoxy adhesive for repairing the water pipe.
<비교예 3>Comparative Example 3
비교예 1과 동일하게 실시하되, 알루미늄을 혼합하지 않고 상하수도관 보수용 에폭시 접착제를 제조하였다.
In the same manner as in Comparative Example 1, an epoxy adhesive for water and sewage pipe repair was prepared without mixing aluminum.
실시예 1을 통해 제조된 상하수도관 보수용 에폭시 접착제의 용출시험 결과를 아래 표 1에 나타내었다.Dissolution test results of the epoxy adhesive for water and sewage pipe repair prepared in Example 1 are shown in Table 1 below.
(단, 본 발명에 따른 상하수도관 보수용 에폭시 접착제에 부직포를 함침 시켜 상하수도관 보수용 에폭시 접착제 도포된 부직포를 수도관에 적용한 후에 수도관을 통과한 물을 바탕으로 시험하였다.)
(However, the non-woven fabric was impregnated with the epoxy adhesive for water and sewage pipe repair according to the present invention, and then applied to the water pipe after testing the water pipe passed through the water pipe.)
<표 1>TABLE 1
위에 표 1에 나타낸 것처럼 본 발명에 따른 상하수도관 보수용 에폭시 접착제는 용출시험 전 항목에 걸쳐 기준치 이하의 검출량을 나타내는 것을 알 수 있다.
As shown in Table 1 above, it can be seen that the epoxy adhesive for water and sewage pipe repair according to the present invention exhibits a detection amount of less than or equal to the reference value throughout the dissolution test.
실시예 1과 비교예 1을 통해 제조된 상하수도관 보수용 에폭시 접착제의 인장전단접착강도를 측정하여 아래 표 2에 나타내었다.
Tensile shear strength of the epoxy adhesive for water and sewage pipe repair prepared in Example 1 and Comparative Example 1 was measured and shown in Table 2 below.
<표 2>TABLE 2
위에 표 2에 나타낸 것처럼 실시예 1에 의해 제조된 상하수도관 보수용 에폭시 접착제는 비교예 1을 통해 제조된 상하수도관 보수용 에폭시 접착제에 비해 우수한 인장전단접착강도를 갖는 것을 알 수 있다.
As shown in Table 2 above, the water supply and drainage pipe repair epoxy adhesive prepared in Example 1 can be seen that has a superior tensile shear bond strength compared to the water supply and drainage pipe repair epoxy adhesive prepared in Comparative Example 1.
실시예 1을 통해 제조된 상하수도관 보수용 에폭시 접착제의 인장강도, 굽힘강도 및 굴곡탄성률을 측정하여 아래 표 3에 나타내었다.
Tensile strength, bending strength and flexural modulus of the watertight and sewage pipe repair epoxy adhesives prepared through Example 1 were measured and shown in Table 3 below.
<표 3>TABLE 3
위에 표 3에 나타낸 것처럼 실시예 1을 통해 제조된 상하수도관 보수용 에폭시 접착제는 인장강도, 굽힘강도 및 굽힘탄성률이 우수한 것을 알 수 있다.
As shown in Table 3 above, it can be seen that the epoxy adhesive for water supply and drainage pipe repair prepared in Example 1 has excellent tensile strength, bending strength, and flexural modulus.
실시예 1 및 비교예 1 내지 3을 통해 제조된 상하수도관 보수용 에폭시 접착제의 시간에 따른 경화정도와 시간에 따른 강도를 측정하여 도 1 및 도 2에 나타내었다.Examples 1 and Comparative Examples 1 to 3 to measure the degree of curing and the time-dependent strength of the epoxy adhesive for water supply and drainage pipe repair over time is shown in Figures 1 and 2.
(단, 경화정도는 상하수도관 보수용 에폭시 접착제가 굳기 시작하는 시점을 기준으로 하였으며, 도 1은 40℃ 이하의 온도 조건에서 측정하고, 도 2는 80℃ 이상의 온도조건에서 측정하였다.)(However, the degree of curing was based on the time when the epoxy adhesive for water and sewage pipe repair starts to harden, Figure 1 is measured at a temperature of 40 ℃ or less, Figure 2 was measured at a temperature of 80 ℃ or more.)
도 1 및 도 2에 나타낸 것처럼 본 발명인 실시예 1에 의해 제조된 상하수도관 보수용 에폭시 접착제는 비교예 1 내지 3을 통해 제조된 상하수도관 보수용 에폭시 접착제에 비해 가사시간이 길며, 짧은 시간에 우수한 접착강도를 나타내는 것을 알 수 있다.1 and 2, the epoxy adhesive for water and sewage pipe repair prepared in Example 1 of the present invention has a longer pot life compared to the epoxy adhesive for water and sewage pipe repair prepared through Comparative Examples 1 to 3, and excellent in a short time. It can be seen that the adhesive strength.
Claims (8)
상기 에폭시 혼합물은 150 내지 400의 당량을 갖는 비스페놀 F 타입의 액체상 에폭시 및 400 내지 500의 당량을 갖는 비스페놀 F 타입의 고체상 에폭시를 포함하여 이루어지고,
상기 첨가제는 폴리우레탄을 포함하여 이루어지는 것을 특징으로 하는 상하수도관 보수용 에폭시 접착제.
10 to 90 parts by weight of epoxy mixture, 0.1 to 50 parts by weight of diluent, 10 to 90 parts by weight of hardener, 0.1 to 10 parts by weight of antifoaming agent, 0.1 to 20 parts by weight of additive, 0.1 to 1 part by weight of antioxidant, 0.01 to 5 parts by weight of chain extender Parts and 0.5 to 3 parts by weight of a filler,
The epoxy mixture comprises a bisphenol F type liquid epoxy having a equivalent weight of 150 to 400 and a bisphenol F type solid epoxy having an equivalent weight of 400 to 500,
Epoxy adhesive for water and sewage pipe repair, characterized in that the additive comprises a polyurethane.
상기 희석제는 지방족 글리시딜 에테르를 포함하여 이루어지는 것을 특징으로 하는 상하수도관 보수용 에폭시 접착제.
The method according to claim 1,
The diluent is an epoxy adhesive for water and sewage pipe repair, characterized in that it comprises an aliphatic glycidyl ether.
상기 경화제는 구아니딘, 우레아 및 방향족아민으로 이루어진 그룹으로부터 선택된 하나 이상을 포함하여 이루어지거나, 디시안아마이드를 포함하여 이루어지는 것을 특징으로 하는 상하수도관 보수용 에폭시 접착제.
The method according to claim 1,
The curing agent comprises at least one selected from the group consisting of guanidine, urea and aromatic amines, or epoxy adhesive for water and sewage pipe repair, characterized in that comprises a dicyanide.
상기 충전제는 알루미늄 및 탄산칼슘으로 이루어진 그룹으로부터 선택된 하나 이상을 포함하여 이루어지는 것을 특징으로 하는 상하수도관 보수용 에폭시 접착제.
The method according to claim 1,
The filler is an epoxy adhesive for water and sewage pipe repair, characterized in that it comprises at least one selected from the group consisting of aluminum and calcium carbonate.
상기 산화방지제는 Tris(2,4-di-tert-butylphenyl)phosphite를 포함하여 이루어지는 것을 특징으로 하는 상하수도관 보수용 에폭시 접착제.
The method according to claim 1,
The antioxidant is a water and sewage pipe repair epoxy adhesive comprising a tris (2,4-di-tert-butylphenyl) phosphite.
상기 사슬확장제는 1,4-부탄디올, 글리세롤, 1,2,6-헥산트리올 및 1,1,1-트리메틸올프로판으로 이루어진 그룹으로부터 선택된 하나 이상을 포함하여 이루어지는 것을 특징으로 하는 상하수도관 보수용 에폭시 접착제.The method according to claim 1,
The chain extender for water and sewage pipe repair, characterized in that it comprises one or more selected from the group consisting of 1,4-butanediol, glycerol, 1,2,6-hexanetriol and 1,1,1-trimethylolpropane Epoxy adhesive.