KR101008855B1 - The manufacturing method of the fishing rod with lacquer paint - Google Patents
The manufacturing method of the fishing rod with lacquer paint Download PDFInfo
- Publication number
- KR101008855B1 KR101008855B1 KR1020080072259A KR20080072259A KR101008855B1 KR 101008855 B1 KR101008855 B1 KR 101008855B1 KR 1020080072259 A KR1020080072259 A KR 1020080072259A KR 20080072259 A KR20080072259 A KR 20080072259A KR 101008855 B1 KR101008855 B1 KR 101008855B1
- Authority
- KR
- South Korea
- Prior art keywords
- lacquer
- fishing rod
- manufacturing
- temperature
- molding
- Prior art date
Abstract
본 발명은 옻칠 낚싯대의 제조방법에 관한 것으로, 더욱 상세하게 설명하면, 접착성과 강도가 뛰어난 옻을 여러 공정을 통해 칠함으로써 낚싯대의 강도를 향상시키고 외관을 미려하게 하는 특징이 있다.The present invention relates to a method of manufacturing a lacquer fishing rod, and in more detail, has a feature of improving the strength of the fishing rod and beautiful appearance by painting a lacquer having excellent adhesiveness and strength through various processes.
본 발명은 크게 네 단계의 공정으로 이루어지는바, 수지가 함침된 유리섬유 또는 카본섬유 등의 원단을 설계된 금형에 접착 롤링시킨 후 원형보존을 위해 외부 테이핑을 한 다음 성형하여 가공되는 소재성형공정과; 가공되어진 낚싯대의 표면에 접착력이 가장 강한 상태인 생옻을 칠함으로서 표면의 굴곡현상과 미세구멍을 제거하는 하도공정과; 상기 공정을 끝난 후 정제한 옻을 칠하고 건조하고 연마하는 작업을 3회 내지 5회 반복하는 중도공정과; 상기 공정을 완료한 후 표면광택을 위해 정제된 옻을 칠하는 상도공정으로 이루어지는 대략적인 구성을 갖는다.The present invention consists of a large four-step process, the material forming process is processed by molding the resin-impregnated glass fiber or carbon fiber, such as adhesive rolls to the designed mold and then external taping for molding and molding; Applying a fresh lacquer in the state of strongest adhesion to the surface of the processed fishing rod to remove the surface bending phenomenon and micropores; A halfway step of repeating three to five times of painting, drying and polishing the purified lacquer after finishing the above process; After completion of the above process has a rough configuration consisting of a top coat step of applying a purified lacquer for surface gloss.
상기와 같이 구성된 본 발명은, 화학성분이 일체 포함되지 않는 친환경적인 원료인 옻과 안료를 이용하여 낚싯대 표면에 옻을 순차적으로 칠함으로써 옻이 낚싯대의 원단에 침투하여 낚싯대의 강도를 더욱 향상시키는 효과가 있다. The present invention configured as described above, by applying lacquer to the surface of the fishing rod sequentially by using lacquer and pigment, which is an environmentally-friendly raw material that does not contain any chemical composition, the lacquer penetrates the fabric of the fishing rod to further improve the strength of the fishing rod. There is.
또한, 완성된 낚싯대의 표면은 시간이 지나도 그 칠의 특성이 변하지 않고 오랫동안 지속되며, 사용할수록 옻칠의 고급스럽고 은은한 광택이 살아나 외관이 미려해질 뿐만 아니라, 소장가치가 증대되는 또 다른 효과가 있다.In addition, the surface of the finished fishing rod lasts for a long time without changing its characteristics over time, and as the use of the lacquer is more luxurious and soft luster, the appearance is not only beautiful but also has an additional effect of increasing the collection value.
옻, 낚싯대, 옻칠 낚싯대의 제조방법 Manufacturing method of lacquer, fishing rod, lacquer fishing rod
Description
본 발명은 옻칠 낚싯대의 제조방법에 관한 것으로, 더욱 상세하게 설명하면, 접착성과 강도가 뛰어난 옻을 여러 공정을 통해 칠함으로써 낚싯대의 강도를 향상시키고 외관을 미려하게 하는 옻칠 낚싯대의 제조방법에 관한 것이다.The present invention relates to a method for manufacturing a lacquer fishing rod, and more specifically, to a method for manufacturing a lacquer fishing rod to improve the strength and beautiful appearance of the fishing rod by painting a lacquer having excellent adhesiveness and strength through various processes. .
일반적으로 낚싯대라 함은 낚시줄을 매어 물고기를 잡을 때 쓰는 가늘고 긴 대를 말하는 것으로, 종래에는 대나무 낚싯대를 주로 사용하였으나, 근래에 들어서는 수지가 함침된 유리섬유 또는 카본섬유 등의 원단으로 제작된 낚싯대가 주목을 받고 있다.Generally, a fishing rod refers to a thin and long rod used to catch a fish by tying a fishing line. In the past, a bamboo fishing rod is mainly used. However, in recent years, a fishing rod made of a glass fiber or carbon fiber impregnated with resin is used. Is getting attention.
상기와 같은 낚싯대는 단지 물고기를 낚는 도구를 뛰어넘어 소장가치도 대단히 높아서 낚싯대 표면의 외관이나 강도 등의 부분도 대단히 중요시되는바, 종래 낚싯대의 성형방법을 살펴보면, 금형에 맞추어 재단된 원단(수지가 함침된 유리섬 유 또는 카본섬유 등)을 낚싯대 본체 제조용 금형에 맞추어 접착후 롤링시키고 롤링된 원단표면에 성형용 고온 테이프를 조밀한 간격으로 감은 후, 이를 120℃의 성형로에서 2~3시간을 가열 성형시키면 롤링된 원단이 성형되면서 원단에 함유된 열가소성수지는 팽창되어져 원단과 함께 성형되고 잔여량의 수지액은 고온 테이프의 틈 사이로 유출되어지면서 성형이 이루어진다. Such a fishing rod is more than just a fish-fishing tool, and its collection value is also very high, so the appearance and strength of the surface of the fishing rod are also very important. Impregnated glass fiber or carbon fiber, etc.) in accordance with the mold for manufacturing the rod body, and then rolled and wound the high temperature tape for molding on the rolled fabric surface at a tight interval. When heat-molding, the rolled fabric is molded and the thermoplastic resin contained in the fabric is expanded to be molded together with the fabric, and the remaining amount of the resin liquid flows out between the gaps of the high temperature tape, thereby forming.
이와 같이 성형된 낚싯대 본체를 금형과 분리시킨 후, 낚싯대 표면의 고온 테이프를 풀어내고 도장작업을 위한 연마공정과 낚싯대 외관의 무늬장식을 위한 도장공정을 통하여 낚싯대가 가공되어진다.After separating the fishing rod body formed in this way from the mold, the fishing rod is processed through a high temperature tape on the surface of the fishing rod, a polishing process for painting and a painting process for decoration of the appearance of the fishing rod.
상기와 같은 방법으로 제조된 종래의 낚싯대 본체는 표면에 도장된 도장피막이 얇고 또한 사용기간이 경과됨에 따라 벗겨지게 되면서 무늬가 지워지는 결점은 물론, 외관상으로도 보기 좋지 않아 오래 소장하지 못하고 상품성이 떨어지는 등의 문제점을 내포하고 있었다.Conventional fishing rod body manufactured by the above method is a paint film coated on the surface is thin and peels off as the use period elapses. It contained problems such as.
이에 본 발명은 상기와 같은 문제점을 감안하여 발명한 것으로, 본 발명은 크게 네 단계의 공정으로 이루어지는바, 수지가 함침된 유리섬유 또는 카본섬유 등의 원단을 설계된 금형에 접착 롤링시킨 후 원형보존을 위해 외부 테이핑을 한 다 음 성형하여 가공되는 소재성형공정과; 가공되어진 낚싯대의 표면에 접착력이 가장 강한 상태인 생옻을 칠함으로서 표면의 굴곡현상과 미세구멍을 제거하는 하도공정과; 상기 공정을 끝난 후 정제한 옻을 칠하고 건조하고 연마하는 작업을 3회 내지 5회 반복하는 중도공정과; 상기 공정을 완료한 후 표면광택을 위해 정제된 옻을 칠하는 상도공정으로 이루어지는 대략적인 구성을 갖는다. Therefore, the present invention was invented in view of the above problems, and the present invention consists of a largely four-step process. A material forming process which is processed by external taping and then molding; Applying a fresh lacquer in the state of strongest adhesion to the surface of the processed fishing rod to remove the surface bending phenomenon and micropores; A halfway step of repeating three to five times of painting, drying and polishing the purified lacquer after finishing the above process; After completion of the above process has a rough configuration consisting of a top coat step of applying a purified lacquer for surface gloss.
상기와 같이 구성된 본 발명은, 화학성분이 일체 포함되지 않는 친환경적인 원료인 옻과 안료를 이용하여 낚싯대 표면에 옻을 순차적으로 칠함으로써 낚싯대의 원단에 침투하여 소재와 일체화되어 낚싯대의 강도를 더욱 향상시키는 효과가 있다. The present invention configured as described above, by applying the lacquer on the surface of the fishing rod sequentially by using lacquer and pigment, which is an environmentally-friendly raw material that does not contain any chemical components, penetrates the fabric of the fishing rod and is integrated with the material to further improve the strength of the fishing rod. It is effective to let.
또한, 완성된 낚싯대의 표면은 시간이 지나도 그 칠의 특성이 변하지 않고 오랫동안 지속되며, 사용할수록 옻칠의 고급스럽고 은은한 광택이 살아나 외관이 미려해질 뿐만 아니라, 소장가치가 증대되는 또 다른 효과가 있다.In addition, the surface of the finished fishing rod lasts for a long time without changing its characteristics over time, and as the use of the lacquer is more luxurious and soft luster, the appearance is not only beautiful but also has an additional effect of increasing the collection value.
본 발명은 옻칠 낚싯대의 제조방법에 관한 것으로, 더욱 상세하게 설명하면, 접착성과 강도가 뛰어난 옻을 여러 공정을 통해 칠함으로써 낚싯대의 강도를 향상시키고 외관이 미려한 특징이 있다.The present invention relates to a method for manufacturing a lacquer fishing rod, and when described in more detail, it is characterized by improving the strength of the fishing rod by applying lacquer having excellent adhesiveness and strength through various processes and having a beautiful appearance.
이하 본 발명의 실시 예를 예시도면을 통해 살펴보면 다음과 같다.An embodiment of the present invention will be described below with reference to the accompanying drawings.
도 1은 본 발명 옻칠 낚싯대의 제조공정도를 나타낸 것이고, 도 2는 본 발명의 단면도를 나타낸 것으로, 도시한 바와 같이 본 발명은 크게 네 단계의 공정으로 제조되는바, 소재성형공정(S1)과 하도공정(S2), 중도공정(S3) 및 상도공정(S4)을 통해 옻칠 낚싯대의 제작을 완료한다.Figure 1 shows the manufacturing process of the lacquer rod of the present invention, Figure 2 shows a cross-sectional view of the present invention, as shown in the present invention is largely manufactured by a four-step process, material forming step (S1) and bottom The manufacturing of the lacquer fishing rod is completed through the process (S2), the intermediate process (S3), and the top coat process (S4).
우선, 제 1공정은 소재를 성형하는 소재성형공정(S1)으로서, 금형에 맞도록 설계된 규격으로 재단된 원단을 낚싯대 본체 제조용 금형에 권취하고, 권취된 원단 표면에 성형용 고온 테이프를 조밀한 간격으로 감은 후 이를 120℃의 성형로에서 2 내지 3시간 가열 성형시킨다.First, the first step is a material forming step (S1) for molding a material, the fabric cut to a specification designed to fit the mold is wound in a fishing rod body manufacturing mold, and the high temperature tape for molding is tightly spaced on the wound fabric surface. After winding up, it was heat-molded in a forming furnace at 120 ° C. for 2 to 3 hours.
이와 같이 원단(11)이 가열 성형되면 원단(11)에 함유된 열가소성수지는 팽창되어져 원단과 함께 성형되고 잔여량의 수지액은 성형용 고온 테이프의 틈 사이로 유출되어지면서 성형이 이루어진다.As such, when the
상기와 같이 성형이 완료되면 낚싯대 본체를 금형과 분리시킨 후 낚싯대 표면의 고온 테이프를 풀어내고 절단 및 표면가공, 연마공정 등의 작업을 통하여 소재성형을 완료하며, 상기 소재성형공정(S1)에서 사용되는 원단은 유리섬유 또는 카본섬유 등으로 구성된다.When the molding is completed as described above, the rod body is separated from the mold, and the high temperature tape on the surface of the rod is released, and the material is completed by cutting, surface processing, polishing, etc., and used in the material forming process (S1). The fabric is made of glass fiber or carbon fiber.
그 후 행해지는 제 2공정은, 상기 소재성형공정(S1)에서 가공된 낚싯대의 표 면에 생옻을 칠한 후 건조하여 하도층(12)을 형성시키는 하도공정(S2) 단계이다.After that, the second step is a step of applying the raw lacquer to the surface of the fishing rod processed in the material forming step (S1), followed by drying to form the undercoat layer (12).
상기 하도공정(S2)은, 생옻을 30℃ 내지 55℃온도로 가열함과 동시에 교반기로 교반을 시켜 수분이 제거된 옻 원액을 낚싯대의 표면에 칠함으로서 낚싯대 표면에 분포하는 미세한 구멍을 메워줌과 동시에 낚싯대 표면과 옻과의 접착력이 증대되어 추후 행해지는 중도공정(S3)과 상도공정(S4)이 용이하게 칠해지도록 하는 구성을 갖는다.The undercoat step (S2) is to fill the fine holes distributed on the surface of the fishing rod by heating the raw lacquer to 30 ℃ to 55 ℃ temperature and at the same time by stirring with a stirrer to paint the surface of the fishing rod lacquer solution is removed At the same time, the adhesive force between the surface of the rod and the lacquer is increased so that the intermediate process (S3) and the top coat process (S4) to be performed later can be easily painted.
상기 옻칠 작업이 완료되면 건조룸으로 옮겨 건조시키는 작업을 하게 되는데 이때, 건조룸의 온도는 18℃ 내지 27℃의 온도로 하고 습도는 60 내지 70%의 습도가 유지되도록 하여 12시간 동안 건조시키고 건조가 완료된 후에는 표면을 연마함으로써 하도공정(S2)을 완료한다.When the lacquer work is completed to move to a drying room to dry the work, at this time, the temperature of the drying room to 18 ℃ to 27 ℃ temperature and humidity to maintain the humidity of 60 to 70% for 12 hours to dry and dry After the completion is completed, the undercoat step (S2) is completed by polishing the surface.
그런 다음, 제 3공정은 상기 하도공정(S2)을 통해 형성된 하도층(12)의 상면에 중도층(13)이 형성되도록 정제된 옻을 칠하는 중도공정(S3) 단계이다.Then, the third process is a middle step (S3) of applying refined lacquer to form the
중도공정(S3)에서 사용하는 옻은 상기 하도공정(S2)에서 사용하였던 생옻을 그대로 사용하는 것이 아니라 은은한 광택과 색상이 나타날 수 있도록 정제된 옻을 사용한다. The lacquer used in the intermediate process (S3) is not using the raw lacquer used in the undercoat process (S2) as it is, but uses refined lacquer so that a soft luster and color may appear.
..
상기 중도공정(S3)을 더욱 상세히 살펴보면, 먼저 생옻 원액과 유광제 및 안료를 혼합하여 30℃ 내지 55℃의 온도로 가열함과 동시에 교반기로 교반을 시킨다.Looking at the intermediate process (S3) in more detail, first, the raw lacquer stock solution, a gloss agent and a pigment are mixed and heated to a temperature of 30 ℃ to 55 ℃ and stirred with a stirrer.
이때 상기 생옻 원액과 유광제 및 안료의 혼합비율은, 생옻 원액은 60 내지 70 중량%이며, 유광제는 동백기름과 들기름 중 어느 하나로 구성되어 20 내지 30중량%이며, 안료는 10%로 구성되는바, 안료로 사용되는 물질로는 낚싯대 표면에 형성되는 색상에 따라 치자와 홍화 및 산화철 등을 선택하여 사용되는 구성을 갖는다.At this time, the mixing ratio of the raw lacquer undiluted solution and the glossing agent and pigment, the raw lacquer undiluted solution is 60 to 70% by weight, the gloss agent is composed of any one of camellia oil and perilla oil 20 to 30% by weight, the pigment is composed of 10% As a material used as a pigment, it has a configuration used by selecting the gardenia and safflower, iron oxide, etc. according to the color formed on the surface of the rod.
위와 같이 정제 옻의 제작이 완료되면, 상기 하도층(12)의 상부로 중도층(13)이 형성되도록 혼합액을 칠한 다음 건조룸에 12시간 동안 건조시키며, 이때 건조룸의 온도 및 습도조건은 상기 하도공정(S2)의 건조조건과 동일하다.When the preparation of the purified lacquer as described above is completed, the mixture is coated to form the
상기와 같이 건조가 완료된 후에는 표면을 연마한 다음, 상기와 같은 옻칠, 건조, 연마를 3 내지 5회 반복함으로써 중도공정(S3)을 완료한다.After the drying is completed as described above, the surface is polished, and then the lacquer, drying and polishing are repeated 3 to 5 times to complete the intermediate process (S3).
그 후 마지막 공정인 제4공정은, 상기 중도공정(S3)을 통해 형성된 중도층(13)의 상면에 정제 옻을 칠하여 상도층(14)을 형성시키는 상도공정(S4)을 완료한다.Thereafter, the fourth step, which is the last step, completes the top coat step S4 of forming the
상기 상도공정(S4)에서는 미려한 광택을 형성시키기 위함으로, 이때 사용되는 혼합물은 상기의 중도공정(S3)에서와 마찬가지로 생옻 원액과 유광제 및 안료로 이루어진 혼합물을 제조하여 사용하지만 그 혼합비율이 상이하다.In order to form a beautiful gloss in the top coat step (S4), the mixture used is prepared by using a mixture of raw lacquer stock, a gloss agent and a pigment as in the above-mentioned intermediate step (S3), but the mixing ratio is different. Do.
이때 사용되는 혼합물의 혼합비율은, 생옻 원액은 40 내지 50 중량%이며, 유광제는 40 내지 50중량%이며, 안료는 10%로 구성되는바, 유광제로 사용되는 동백기름과 들기름 중 하나의 비율을 상기 중도공정(S3)의 약 2배의 비율로 높여서 혼합물을 제조함으로써 상도층(14)에 광택이 형성되도록 구성된다.In this case, the mixing ratio of the mixture used is 40 to 50% by weight of the raw lacquer, 40 to 50% by weight of the gloss agent, and 10% of the pigment, and the ratio of one of camellia oil and perilla oil used as the gloss agent. It is configured so that the gloss is formed on the
상기와 같이 구성된 혼합물을 가열과 동시에 교반기에 의해 교반시킨 후, 이를 중도층(13)의 상부에 칠하고, 칠 작업이 완료되면 건조룸에 12시간 정도 건조시키며, 이때 사용되는 건조룸의 온도 및 습도조건은 상기 하도 및 중도공정(S2, S3)의 건조조건과 동일하다.After stirring the mixture configured as described above with a stirrer at the same time with heating, it is applied to the upper portion of the
건조가 끝난 후에는 별도의 연마작업을 하지 않아 표면에 광택이 살아있도록 함으로써 상도층(14)의 생성을 완료한다.After the drying is completed, the polishing layer is not polished, so that the surface of the
상기와 같이 구성된 본 발명을 통해 얻어지는 낚싯대의 제작과정을 살펴보면, 끝단이 서로 다른 직경을 갖는 일정한 길이의 금속 막대 형태로 다수 개 제작한 이후, 상기 제1공정에서부터 제4공정까지의 과정을 반복하여 제작함으로써 낚싯대 본체(10)를 완성하고, 이를 직경이 작은 것에서부터 큰 것으로 순차적으로 다단 결합함으로써 하나의 낚싯대를 완성한다.Looking at the manufacturing process of the fishing rod obtained through the present invention configured as described above, after producing a plurality of ends of a metal rod of a predetermined length having a different diameter, by repeating the process from the first step to the fourth step The fishing rod
도 1은 본 발명 옻칠 낚싯대의 제조방법의 제조공정을 도시한 공정도1 is a process chart showing the manufacturing process of the manufacturing method of the present invention lacquer fishing rod
도 2는 본 발명의 단면도 2 is a cross-sectional view of the present invention
[도면의 주요부분에 대한 부호의 설명][Explanation of symbols on the main parts of the drawings]
10 : 낚싯대 본체 11 : 원단10: rod body 11: fabric
12 : 하도층 13 : 중도층12: lower layer 13: middle layer
14 : 상도층14: top layer
Claims (3)