KR100982609B1 - Manufacturing Method of Artificial Marble Having Various Pattern And The Artificial Marble Thereby - Google Patents

Manufacturing Method of Artificial Marble Having Various Pattern And The Artificial Marble Thereby Download PDF

Info

Publication number
KR100982609B1
KR100982609B1 KR1020080077477A KR20080077477A KR100982609B1 KR 100982609 B1 KR100982609 B1 KR 100982609B1 KR 1020080077477 A KR1020080077477 A KR 1020080077477A KR 20080077477 A KR20080077477 A KR 20080077477A KR 100982609 B1 KR100982609 B1 KR 100982609B1
Authority
KR
South Korea
Prior art keywords
weight
artificial marble
parts
colorful pattern
colorful
Prior art date
Application number
KR1020080077477A
Other languages
Korean (ko)
Other versions
KR20100018807A (en
Inventor
김병열
Original Assignee
김병열
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김병열 filed Critical 김병열
Priority to KR1020080077477A priority Critical patent/KR100982609B1/en
Publication of KR20100018807A publication Critical patent/KR20100018807A/en
Application granted granted Critical
Publication of KR100982609B1 publication Critical patent/KR100982609B1/en

Abstract

본 발명은 다채무늬를 가진 인조대리석 제조방법 및 상기 방법에 의해 제조된 인조대리석에 관한 것으로서, 액상의 불포화폴리에스테르 수지 100 중량부에 펄분말 0.5 ~ 1.0 중량부, 아연분말 0.5 ~ 1.0 중량부 및 분산제 0.5 ~ 1 중량부를 넣고 혼합하여 수지혼합물을 제조하고, 제조된 수지 혼합물에 귀갑 문양의 해머톤을 형성하는 첨가제로서 오르가노 폴리실록산 용액(organo poly siloxane solution)을 0.5 ~ 5.0 중량부를 넣고 혼합한 후, 경화제 0.5 ~ 5.0 중량부를 넣고 혼합하여 도료조성물을 제조하는 단계(120); 상기 경화제가 혼합된 도료조성물을 판재(30)의 일면에 고르게 도포하여 다채무늬층(20)을 형성하는 단계(130); 도포된 다채무늬층(20)을 건조시킨 후 연마하고 광택 처리하는 마무리 단계를 포함한다. 이에 따라 다채무늬를 형성하기 위한 도료의 조성 과정이 간단하여 비숙련자라도 쉽게 혼합가능하고 도포 과정이 용이하도록 하는 등의 효과가 제공된다.The present invention relates to a method of manufacturing artificial marble having a colorful pattern and artificial marble prepared by the above method, 0.5 to 1.0 parts by weight of pearl powder, 0.5 to 1.0 parts by weight of zinc powder, 0.5 to 1 part by weight of dispersant was mixed to prepare a resin mixture, and 0.5 to 5.0 parts by weight of organo poly siloxane solution (organo poly siloxane solution) was added as an additive to form a hammer-pattern hammerton in the resin mixture. Preparing a paint composition by mixing 0.5 to 5.0 parts by weight of a curing agent; Forming a colorful pattern layer 20 by uniformly applying the paint composition mixed with the curing agent to one surface of the plate member 30; And drying the coated colorful pattern layer 20, followed by polishing and polishing. Accordingly, the composition of the paint for forming a colorful pattern is simple, so that even an unskilled person can easily mix and provide an easy application process.

인조대리석, 다채무늬, 호마이카, 귀갑 문양, 도료 Artificial marble, colorful pattern, Homica, patten pattern, paint

Description

다채무늬를 가진 인조대리석 제조방법 및 상기 방법에 의해 제조된 인조대리석{Manufacturing Method of Artificial Marble Having Various Pattern And The Artificial Marble Thereby}Manufacturing method of artificial marble having various patterns and the artificial marble thereby

본 발명은 일반적으로 다채무늬를 가진 인조대리석 제조에 관한 것으로서, 더 상세하게는, 다채무늬를 형성하기 위한 도료의 조성 과정이 간단하여 비숙련자라도 쉽게 혼합가능하고 도포 과정이 용이하도록 하는 새로운 다채무늬를 가진 인조대리석 제조방법 및 상기 방법에 의해 제조된 인조대리석에 관한 것이다.The present invention generally relates to the manufacture of artificial marble having a colorful pattern, and more particularly, a new colorful pattern which is easy to mix and facilitates the application process even by a non-skilled person by simplifying the composition of the paint for forming the colorful pattern. It relates to an artificial marble manufacturing method having a and artificial marble prepared by the above method.

일반적으로, 석회암과 돌로마이트가 접촉변성작용이나 광역변성작용을 받아 재결정되어 형성되는 천연대리석은, 연마하면 특유의 다색무늬와 광택이 나타나 건축물의 고급스러운 내장 및 외장재로 사용되고 있다. 그러나 천연대리석으로 된 건축재는 부피와 중량이 크고 가격이 고가라는 단점이 있었다. 그리하여 가격은 천연대리석보다 저렴하면서, 천연대리석과 같은 느낌을 줄 수 있는 인조대리석을 제조하는 데 많은 노력이 기울여져 오고 있으며, 더 나아가 천연대리석과 같은 다양한 외관과 고급스러운 질감을 갖는, 즉 다채무늬를 가지는 인조대리석에 대한 요구가 있었다.In general, natural marble, which is formed by recrystallization of limestone and dolomite by contact or wide-area metamorphism, has a unique multicolored pattern and luster when polished and is used as a luxurious interior and exterior material of buildings. However, the building materials made of natural marble had the disadvantages of being bulky, heavy, and expensive. Thus, while the price is cheaper than natural marble, much effort has been devoted to manufacturing artificial marble which can give a feeling like natural marble. Furthermore, it has a variety of appearances and luxurious textures such as natural marble, that is, colorful patterns. There was a need for artificial marble with

이러한 요구에 부응하기 위하여 종래 다양한 제안들이 있었다. 예컨대 대한민국 특허 등록번호 10-0605090 (등록일자: 2006년07월19일) "인조대리석 및 그 제조방법"의 등록공보에는, 불포화폴리에스테르 수지(일명, '호마이카 수지')에 펄과 왁스를 소량 혼합하여 사용함으로써 천연대리석과 유사한 다양한 무늬를 가지는 인조대리석과 그 제조방법이 개시되어 있다. 이에 따르면, i) 판넬의 상면의 가장자리를 블록킹 처리하여 원하는 도막 두께의 공간을 형성하는 단계; ii) 상기 공간에, 불포화폴리에스테르 수지 100 중량부에 펄 0.1 ~ 2.5 중량부 및 왁스 0.01 ~ 0.2 중량부를 처리하는 단계로서, 왁스를 점적 적용하거나 수지 혼합물에 첨가한 후, 액상의 도포액을 상기 i) 단계에서 만든 공간에 채우는 처리 단계; 및 iii) 경화시킨 후 가장자리의 블록킹을 제거하는 단계로 이루어진다. 이는 수지와 전혀 섞이지 않는 왁스를 이용하여 다채무늬를 성형할 수 있다는 장점이 제공된다.In order to meet this demand, various conventional proposals have been made. For example, Korean Patent Registration No. 10-0605090 (Registration Date: July 19, 2006) In the publication of "Artificial marble and its manufacturing method", a small amount of pearl and wax in an unsaturated polyester resin (aka 'Homaika resin') By using a mixture, artificial marble having various patterns similar to natural marble and a method of manufacturing the same are disclosed. According to this, i) blocking the edge of the upper surface of the panel to form a space having a desired coating thickness; ii) treating 0.1-2.5 parts by weight of pearl and 0.01-0.2 parts by weight of wax to 100 parts by weight of an unsaturated polyester resin in the space, and then applying dropwise wax or adding to the resin mixture, a processing step of filling the space created in step i); And iii) removing the blocking of the edges after curing. This provides the advantage that a colorful pattern can be formed using a wax that is not mixed with the resin at all.

그러나 상기 왁스를 사용한 방식에서는, 액상의 수지 혼합물에 왁스를 점적 적용 또는 혼합한 액상의 도료의 점성이 너무 낮기 때문에, 일반적인 도료 도포 방식을 사용할 수 없고, 먼저 판넬의 가장자리를 블록킹하여 공간을 만든 후, 이 공간에 도료를 채워서 건조시킨 후 블록킹을 제거하여야만 한다. 이는 묽은 액상의 도료 도포 과정이 복잡하고, 왁스의 점적 적용이나 혼합도 숙련자에 의하여 이루어져야 한다는 제한이 있었다. 더 나아가 판넬의 가장자리가 복잡한 경우 블록킹의 형성과정이 너무 까다로울 수도 있다.However, in the method using the wax, since the viscosity of the liquid paint in which the wax is applied or mixed into the liquid resin mixture is too low, the general paint application method cannot be used, and first, the edge of the panel is blocked to make a space. In this case, the space must be filled with paint and dried before the blocking is removed. This has a limitation that the process of applying a thin liquid paint is complicated, and the application or mixing of wax should be made by a skilled person. Furthermore, if the panel edges are complex, the formation of blocking may be too tricky.

따라서 다채무늬를 형성하기 위한 도료의 조성 과정이 간단하여 비숙련자라도 쉽게 혼합가능하며, 예컨대 롤러를 사용하는 일반적인 도료 도포 방식으로 도료 를 도포할 수 있어 도포 과정이 용이하도록 하면서도, 다양한 질감과 외관을 가지는 다채무늬를 구비한 인조대리석을 제조할 수 있는 새로운 기술에 대한 요구는 여전히 존재한다.Therefore, the composition of the paint to form a colorful pattern is simple and can be easily mixed even by unskilled people. For example, the paint can be applied by a general paint application method using a roller, so that the application process is easy, and various textures and appearances are provided. There is still a need for new technologies that can produce artificial marble with eggplants.

본 발명은 종래 다채무늬를 가진 인조대리석 제조 기술을 개선하고 다양한 추가 장점을 제공하기 위하여 발명된 것으로서, 다양한 질감과 외관을 가지는 다채무늬를 구비한 인조대리석에 있어서, 다채무늬를 형성하기 위한 도료의 조성 과정이 간단하여 비숙련자라도 쉽게 혼합가능하며, 예컨대 롤러를 사용하는 일반적인 도료 도포 방식으로 도료를 도포할 수 있어 도포 과정이 용이하도록 한 다채무늬를 가진 인조대리석 제조방법 및 상기 방법에 의해 제조된 인조대리석을 제공하는 것을 그 목적으로 한다.The present invention has been invented to improve a conventional artificial marble manufacturing technology with a colorful pattern and to provide a variety of additional advantages, in the artificial marble having a colorful pattern having a variety of textures and appearance, the coating of a paint for forming a colorful pattern The composition process is simple and can be easily mixed even by unskilled people. For example, the method of manufacturing artificial marble having a multi-colored pattern made by the method and the method can be applied by a general paint application method using a roller. The purpose is to provide artificial marble.

상기 목적은 본 발명에 따라 제공되는 다채무늬를 가진 인조대리석 제조방법 및 상기 방법에 의해 제조된 인조대리석에 의하여 달성된다.The object is achieved by a method of manufacturing artificial marble having a colorful pattern provided in accordance with the present invention and the artificial marble produced by the method.

본 발명의 일 양상에 따른 다채무늬를 가진 인조대리석 제조방법은, 액상의 불포화폴리에스테르 수지 100 중량부에 펄분말 0.5 ~ 1.0 중량부, 아연분말 0.5 ~ 1.0 중량부 및 분산제 0.5 ~ 1 중량부를 넣고 혼합하여 수지혼합물을 제조하고, 제조된 수지 혼합물에 귀갑 문양의 해머톤을 형성하는 첨가제로서 오르가노 폴리실록산 용액(organo poly siloxane solution)을 0.5 ~ 5.0 중량부를 넣고 혼합한 후, 경화제 0.5 ~ 5.0 중량부를 넣고 혼합하여 도료조성물을 제조하는 단계; 상기 경화제가 혼합된 도료조성물을 판재의 일면에 고르게 도포하여 다채무늬층을 형성하는 단계(130); 도포된 다채무늬층(20)을 건조시킨 후 연마하고 광택 처리하는 마무리 단계를 포함할 수 있다.Artificial marble having a colorful pattern according to an aspect of the present invention, 100 parts by weight of a liquid unsaturated polyester resin 0.5 to 1.0 parts by weight of pearl powder, 0.5 to 1.0 parts by weight of zinc powder and 0.5 to 1 parts by weight of dispersant To prepare a resin mixture by mixing, 0.5 to 5.0 parts by weight of an organo poly siloxane solution (0.5 to 5.0 parts by weight) of an organo poly siloxane solution as an additive to form a hammerhead pattern hammerton in the prepared resin mixture, and then mixed, 0.5 to 5.0 parts by weight of a curing agent Putting and mixing to prepare a paint composition; Forming a colorful pattern layer by uniformly applying the paint composition mixed with the curing agent to one surface of the plate; After drying the coated colorful pattern layer 20 may include a finishing step of polishing and polishing.

바람직한 실시예에 있어서, 상기 도료조성물 제조 단계에서 컬러 안료 0.001 ~ 0.05 중량부를 더 첨가하여 혼합한다.In a preferred embodiment, 0.001 to 0.05 parts by weight of color pigments are further added and mixed in the paint composition manufacturing step.

바람직한 실시예에 있어서, 상기 마무리 단계 중 광택 처리 과정은 건조되고 연마된 상기 다채무늬층(20)에 불포화폴리에스테르 수지를 도포한 후 건조시키고 연마한 후 약품처리 또는 기계에 의한 광택 처리를 하는 것이거나, 또는 건조되고 연마된 상기 다채무늬층(20)에 우레탄계 도료 또는 래커계 도료를 도포한 후 건조시키는 것이다.In a preferred embodiment, the polishing process of the finishing step is to apply the unsaturated polyester resin to the dried and polished multi-pattern layer 20, and then to dry and polish the chemical treatment or mechanical polishing Alternatively, the urethane-based paint or lacquer-based paint is applied to the dried and polished colorful pattern layer 20 and then dried.

본 발명의 또 다른 양상에 따라, 상기의 방법들 중 어느 한 방법에 따라, 판재의 적어도 한면에 형성된, 다채무늬층을 구비하는 것을 특징으로 하는 인조대리석이 제공된다.According to another aspect of the present invention, there is provided an artificial marble, characterized in that it comprises a multi-patterned layer, formed on at least one side of the sheet, according to any of the above methods.

상술한 바와 같은 목적과 구성을 가지는 본 발명에 따른 다채무늬를 가진 인조대리석 제조방법 및 상기 방법에 의해 제조된 인조대리석은, 다양한 질감과 외관을 가지는 다채무늬를 구비한 인조대리석에 있어서, 다채무늬를 형성하기 위한 도료의 조성 과정이 간단하여 비숙련자라도 쉽게 혼합가능하며, 예컨대 롤러를 사용하는 일반적인 도료 도포 방식으로 도료를 도포할 수 있어 도포 과정이 용이하도록 하는 등의 효과를 제공한다.Artificial marble having a colorful pattern according to the present invention having the object and configuration as described above and the artificial marble prepared by the method, in the artificial marble having a colorful pattern having a variety of textures and appearance, The composition of the paint to form a simple to be easy to mix even non-skilled person, for example, it is possible to apply the paint in a general paint application method using a roller to provide an effect such as to facilitate the application process.

이하, 첨부된 도면을 참조하여 본 발명을 구체적인 예를 들어 설명하면 다음과 같다.Hereinafter, with reference to the accompanying drawings illustrating the present invention with a specific example as follows.

도 1은 본 발명의 일 실시예에 따른 다채무늬를 가진 인조대리석 제조방법의 과정을 설명하기 위한 흐름도이고, 도 2는 본 발명의 일 실시예에 따른 다채무늬를 가진 인조대리석 제조방법에 의한 인조대리석의 구성을 보여주는 개략적인 단면도이며, 도 3 내지 도 10은 본 발명의 실시예들에 따른 다채무늬를 가진 인조대리석 제조방법에 의해 만들어진 다양한 다채무늬의 예를 예시하는 도면들이다.1 is a flowchart illustrating a process of a method of manufacturing artificial marble with a colorful pattern according to an embodiment of the present invention, Figure 2 is an artificial marble by a method of manufacturing artificial marble with a colorful pattern according to an embodiment of the present invention 3 through 10 are views illustrating examples of various colorful patterns made by a method of manufacturing artificial marble having colorful patterns according to embodiments of the present invention.

도 1 및 도 2에 도시된 바와 같이, 본 발명의 일 양상에 따라 다채무늬를 가진 인조대리석 제조방법(100)과, 이 방법에 따라 제조된 다채무늬층(20)을 판재(30)의 적어도 일면에 형성한 인조대리석이 제공된다.As shown in Figures 1 and 2, according to an aspect of the present invention, the artificial marble manufacturing method 100 having a colorful pattern, and the colorful pattern layer 20 produced according to the method at least of the plate 30 Artificial marble formed on one side is provided.

도 1을 참조하면, 본 발명에 따른 제조방법에 있어서, 먼저 재료를 준비한다(110). 재료는 판재(30) 및 다채무늬층(20)을 형성할 도료조성물 재료이다. 판재(30)는 석재 또는 목재로 된 판으로서, 예컨대 식탁, 장롱, 탁자, 서랍장 등의 가구 상판, 외장용 재, 주방 상판, 벽체나 화장실, 세면 상판 실내인테리어 등에 사용하는 것일 수 있다.Referring to Figure 1, in the manufacturing method according to the present invention, first prepare a material (110). The material is a paint composition material for forming the plate 30 and the colorful pattern layer 20. The plate 30 is a stone or wood plate, for example, may be used for furniture, such as dining table, cabinet, table, chest of drawers, exterior material, kitchen top, wall or toilet, washroom interior.

다채무늬층(20)을 위한 도료조성물의 재료는, 일명 '호마이카 수지'라고 알려진 액상의 불포화폴리에스테르 수지(예컨대, 주식회사 애경으로부터 구입가능한 애경 포리코트 PC-N 제품)에, 소량의 첨가제인 액상의 해머톤 형성 첨가제(예컨대 ShinEstu 사로부터 구입가능한 KP-310, 310B 제품), 분산제, 아연, 펄, 경화제, 및 컬러 안료를 포함할 수 있다.The material of the coating composition for the colorful pattern layer 20 is a liquid which is a small amount of an additive in a liquid unsaturated polyester resin (for example, Aekyung Polycoat PC-N product available from Aekyung Co., Ltd.) known as 'homica resin'. Hammertone forming additives (such as KP-310, 310B available from ShinEstu), dispersants, zinc, pearls, curing agents, and color pigments.

일명 '호마이카 수지'라고 알려진 액상의 불포화폴리에스테르 수지(예컨대, 주식회사 애경으로부터 구입가능한 애경 포리코트 PC-N 제품)는, 건축자재 분야에서 널리 사용되며, 경화시 일정 두께의 도막을 형성할 수 있는, 통상의 2액형 또는 3액형 불포화폴리에스테르 수지가 사용될 수 있다. 또한 경도, 치수안정성, 수축률 및/또는 광택과 같은 물성의 개량을 위해 변형된 불포화폴리에스테르 수지도 사용가능하다.Liquid unsaturated polyester resins (eg, Aekyung Polycoat PC-N products available from Aekyung Co., Ltd.), also known as 'Homaika Resin', are widely used in the field of construction materials and can form coatings having a certain thickness upon curing. Ordinary two-component or three-component unsaturated polyester resins may be used. Unsaturated polyester resins may also be used to improve physical properties such as hardness, dimensional stability, shrinkage and / or gloss.

액상의 해머톤 형성 첨가제(예컨대 ShinEstu 사로부터 구입가능한 KP-310, 310B 제품)는 귀갑 문양을 나타내는 일종의 안료이며, 화학명은 오르가노 폴리실록산 용액(organo polysiloxane solution)이다. 일반적으로 ShinEstu 사로부터 구입가능한 KP-310제품은 일반적인 문양을 나타내기 위해 사용하고, KP-310B 제품은 선명한 형태의 문양을 나타내기 위해 사용된다.Liquid hammertone-forming additives (eg KP-310, 310B available from ShinEstu) are a type of pigment that exhibits the pattery pattern, and the chemical name is organo polysiloxane solution. In general, KP-310 products, available from ShinEstu, are used to represent general patterns, and KP-310B products are used to display vivid patterns.

분산제는 안료 표면에 흡착하여 정전기적인 반발력이나 입체 장애 효과로 안료와 안료 사이의 간격을 일정하게 유지시켜 안료들이 재응집되는 것을 막아준다. The dispersant is adsorbed on the surface of the pigment to maintain a constant gap between the pigment by the electrostatic repulsive force or steric hindrance effect to prevent the pigment from reaggregating.

아연은 발포제 역할을 하며 수지의 안정성을 위하여 혼합한다. Zinc acts as a blowing agent and mixes for stability of the resin.

펄은 통상 가구용 도료에 미려한 색상을 창출하기 위해 첨가되는 안료의 일종으로, 창출되는 색상에 따라서 진주펄, 황금펄, 동펄, 은펄 등이 있으며 통상 분말형태로 사용된다. 본 발명에서는 1종 이상의 펄이 사용되는데, 사용되는 펄의 종류와 안료 혼합비에 따라 다양한 색상의 대리석 표면이 창출될 수 있다.Pearl is a kind of pigment that is usually added to create a beautiful color in furniture paints, there are pearl pearls, golden pearls, copper pearls, silver pearls, etc., depending on the color to be produced is usually used in powder form. In the present invention, one or more types of pearls are used, and marble surfaces of various colors may be created depending on the type of pearls used and the pigment mixing ratio.

경화제는 도료조성물의 경화를 촉진하며, 컬러 안료는 다양한 컬러를 구현하기 위하여 첨가될 수 있다.Curing agents promote curing of the paint composition, and color pigments may be added to realize various colors.

본 발명에 따른 다채무늬 도료 제조 단계(120)는, 우선 액상의 불포화폴리에스테르 수지 100 중량부에 펄분말 0.5 ~ 1.0 중량부, 아연분말 0.5 ~ 1.0 중량부 및 분산제 0.5 ~ 1 중량부를 넣고 예컨대 손으로 막대기를 저어 혼합하여 수지혼합물을 제조한다. 이후 제조된 수지 혼합물에 귀갑 문양의 해머톤을 형성하는 첨가제로서 오르가노 폴리실록산 용액(organo poly siloxane solution)을 0.5 ~ 5.0 중량부를 넣고 혼합한다. 잘 혼합한 다음 여기에 경화제 0.5 ~ 5.0 중량부를 넣고 혼합함으로써, 다채무늬 도료조성물을 제조한다.In the manufacturing process of the colorful pattern paint 120 according to the present invention, first, 0.5 to 1.0 parts by weight of pearl powder, 0.5 to 1.0 parts by weight of zinc powder, and 0.5 to 1 parts by weight of a dispersant are added to 100 parts by weight of an unsaturated polyester resin in a liquid. Stir the rods and mix to prepare a resin mixture. Thereafter, 0.5 to 5.0 parts by weight of an organo polysiloxane solution is added and mixed as an additive to form a hammer-pattern hammerton in the prepared resin mixture. After mixing well, 0.5 to 5.0 parts by weight of a curing agent is added thereto and mixed to prepare a colorful pattern paint composition.

이 다채무늬 도료조성물에는 다양한 컬러를 구현하기 위하여 컬러 안료 0.001 ~ 0.05 중량부를 더 첨가하여 혼합할 수 있다.The colorful pattern paint composition may be mixed by adding 0.001 to 0.05 parts by weight of color pigments to implement various colors.

오르가노 폴리실록산 용액이 0.5 중량부 미만이면 귀갑 문양이 거의 구별이 안되며, 5.0 중량부 초과하면 귀갑 문양이 너무 뚜렷하여 고급스러운 문양/색상의 대리석이 형성되기 어렵다. 분산제, 아연, 또는 펄이 0.5 중량부 미만이거나 1.0 중량부 초과하면 고급스러운 문양/색상의 대리석이 형성되기 어렵다. 또한 본 발명에 따른 인조대리석에는 필요에 따라서, 일반적으로 도료에 사용되는 적색, 황색등 기타 컬러 안료가 추가로 포함될 수 있다. 원하는 대리석의 색상농도에 따라 안료의 첨가량이 달라질 수 있으나, 일반안료는 불포화폴리에스테르 수지 100 중량부에 대해, 0.001 ~ 0.05 중량부로 포함되는 것이 바람직하다. 일반안료가 0.001 중량부 이하면 안료의 효과를 발휘하기 어렵고 0.05 중량부 초과하면 너무 진한색의 대리 석 문양/색상이 형성될 수 있다.If the organopolysiloxane solution is less than 0.5 parts by weight, the palatal pattern is almost indistinguishable. If it is more than 5.0 parts by weight, the palatal pattern is so distinct that it is difficult to form a luxurious pattern / colored marble. If the dispersant, zinc, or pearl is less than 0.5 parts by weight or more than 1.0 part by weight, it is difficult to form a luxurious pattern / colored marble. In addition, the artificial marble according to the present invention may further include other color pigments such as red, yellow, and the like, which are generally used in paints as needed. The amount of the pigment may vary depending on the color of the desired marble, but the general pigment is preferably included in an amount of 0.001 to 0.05 parts by weight based on 100 parts by weight of the unsaturated polyester resin. When the pigment is 0.001 parts by weight or less, it is difficult to exert the effect of the pigment, and when it exceeds 0.05 parts by weight, too dark marble pattern / color may be formed.

이후 도료조성물을 판재(30)의 일면에 예컨대 롤러를 사용하여 고르게 도포하여 다채무늬층(20)을 형성시킨다(130).Thereafter, the paint composition is evenly applied to one surface of the plate 30 using a roller, for example, to form the colorful pattern layer 20 (130).

도포된 다채무늬층(20)을 건조시킨 후 연마하고 광택 처리하는 마무리 단계를 진행시킨다. 마무리 단계는 고광택 제품을 제조할 수 있는 마무리A 과정(141 ~ 146)과 공정을 단순화시킨 마무리B 과정(151 ~ 154) 중 어느 한 단계를 거치게 할 수 있다.After the coated colorful pattern layer 20 is dried, a finishing step of polishing and polishing is performed. The finishing step may be any one of the finishing A process (141 to 146) and the finishing B process (151 to 154) which can simplify the process to produce a high gloss product.

마무리A 과정(141 ~ 146)에 따르면, 판재에 도포된 다채무늬층(20)이 예컨대 상온에서 방치하여 건조(141)되도록 하고, 예컨대 사포와 같은 연마 기구를 사용하여 연마(142)한 다음에, 건조되고 연마된 상기 다채무늬층(20)에 불포화폴리에스테르 수지 즉 호마이카 수지를 도포한다(143). 이후 호마이카 수지가 건조(144)되면 다시 예컨대 사포로 연마(145)한 후 약품처리 또는 기계에 의한 광택 처리(146)를 할 수 있다. 이러한 마무리A 과정은 고광택 제품을 제조할 수 있다는 장점을 제공하지만, 마무리 공정이 복잡하고 공정 비용이 증가한다는 단점을 가진다.According to the finishing A process (141 to 146), the colorful pattern layer 20 applied to the sheet is allowed to dry (141), for example, left at room temperature, and then polished (142) using a polishing apparatus such as sandpaper, for example. In addition, an unsaturated polyester resin, ie, a Homica resin, is applied to the dried and polished colorful pattern layer 20 (143). After the Homica resin is dried 144, for example, sandpaper 145 may be polished again with sandpaper, and then chemical treatment or mechanical polishing 146 may be performed. This finishing A process provides the advantage of being able to manufacture high gloss products, but has the disadvantage of a complicated finishing process and an increase in processing costs.

다른 식으로 공정을 단순화시켜 저렴하게 제조할 수 있는 마무리B 과정(151 ~ 154)을 거칠 수도 있다. 이 과정에 따르면, 판재에 도포된 다채무늬층(20)이 예컨대 상온에서 방치하여 건조(151)되도록 하고, 예컨대 사포와 같은 연마 기구를 사용하여 연마(152)한 다음에, 건조되고 연마된 다채무늬층(20)에 우레탄계 도료 또는 래커계 도료를 도포(154)한 후 건조(154)시킨다. 광택은 사용된 우레탄계 도료 또는 래커계 도료를 무광, 반광, 또는 유광 도료 중 어느 하나를 사용함으 로써, 최종 제품도 무광, 반광, 또는 유광의 광택을 나타낼 수 있다. 따라서 이러한 과정에 따르면, 마무리 공정이 저렴하게 이루어질 수 있고, 다양한 정도의 광택을 가지도록 조절할 수 있다는 장점이 제공될 수 있다.Alternatively, it may be subjected to the finishing B process (151 to 154) which can be manufactured at a low cost by simplifying the process. According to this process, the colorful pattern layer 20 applied to the sheet is allowed to dry (151), for example, at room temperature, and then polished (152) using, for example, a polishing tool such as sandpaper, and then dried and polished colorful The urethane-based paint or lacquer-based paint is applied to the patterned layer 20 and then dried (154). Gloss may be a matte, semi-gloss, or gloss by using the urethane-based paint or lacquer-based paint either matte, semi-gloss, or gloss paint. Therefore, according to this process, the finishing process can be made inexpensively, it can be provided with the advantage that it can be adjusted to have various degrees of gloss.

본 발명은 또한 도 2에 도시된 바와 같이 위 방법에 따라 판재(30)의 적어도 한면에 형성된, 다채무늬층(20)(도 3 내지 도 10 참조)을 구비하는 것을 특징으로 하는 인조대리석을 제공한다.The present invention also provides an artificial marble, characterized in that it comprises a colorful pattern layer 20 (see FIGS. 3 to 10) formed on at least one side of the plate 30 according to the above method as shown in FIG. 2. do.

이상에서는 본 발명을 구체적인 실시예를 통하여 설명하였으나, 당업자라면 본 명세서에서 설명된 여러 가지 특징을 참조하고 조합하여 다양한 변형이 가능하다. 따라서 본 발명의 범위가 설명된 실시예에만 국한되는 것이 아니라, 첨부된 청구범위에 의하여 해석되어야 함을 지적해둔다.Although the present invention has been described through specific embodiments, various modifications are possible to those skilled in the art by referring to and combining various features described herein. Therefore, it should be pointed out that the scope of the present invention should not be limited to the described embodiments, but should be interpreted by the appended claims.

이상에서 설명한 바와 같이 본 발명에 의하면 천연대리석과 같은 다양한 외관과 고급스러운 질감을 갖는 인조대리석을 얻을 수 있다. 또한 본 발명에 의한 인조대리석은 천연대리석에 비하여 경량이면서 가공성이 뛰어나서, 차세대 대리석으로 건축 내외장재 및 가구 상판 자재로 사용될 수 있다. 구체적으로는 값비싼 천연대리석의 대체물로서, 식탁, 장롱, 탁자, 서랍장 등의 가구 상판, 외장용 재, 주방 상판, 벽체나 화장실, 세면 상판 실내인테리어 등에 사용가능한 인조대리석 관련 분야에서 널리 이용할 수 있다. As described above, according to the present invention, artificial marble having various appearances and luxurious textures, such as natural marble, can be obtained. In addition, the artificial marble according to the present invention is light and excellent in processability compared to natural marble, it can be used as interior and exterior building materials and furniture top plate as the next generation marble. Specifically, as a substitute for expensive natural marble, it can be widely used in artificial marble-related fields that can be used for furniture tops such as dining tables, chests, tables, and chests of drawers, exterior materials, kitchen tops, walls, toilets, and vanity tops.

도 1은 본 발명의 일 실시예에 따른 다채무늬를 가진 인조대리석 제조방법의 과정을 설명하기 위한 흐름도.1 is a flow chart for explaining the process of manufacturing artificial marble with a colorful pattern according to an embodiment of the present invention.

도 2는 본 발명의 일 실시예에 따른 다채무늬를 가진 인조대리석 제조방법에 의한 인조대리석의 구성을 보여주는 개략적인 단면도.Figure 2 is a schematic cross-sectional view showing the configuration of artificial marble by a method of manufacturing artificial marble with a colorful pattern according to an embodiment of the present invention.

도 3 내지 도 10은 본 발명의 실시예들에 따른 다채무늬를 가진 인조대리석 제조방법에 의해 만들어진 다양한 다채무늬의 예를 예시하는 도면들.3 to 10 are views illustrating examples of various colorful patterns made by the method of manufacturing artificial marble with colorful patterns according to embodiments of the present invention.

<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>

20 : 다채무늬층 30 : 판재20: colorful pattern layer 30: plate

Claims (4)

다채무늬를 가진 인조대리석 제조방법에 있어서,In the manufacturing method of artificial marble having a colorful pattern, 액상의 불포화폴리에스테르 수지 100 중량부에 펄분말 0.5 ~ 1.0 중량부, 아연분말 0.5 ~ 1.0 중량부 및 분산제 0.5 ~ 1 중량부를 넣고 혼합하여 수지혼합물을 제조하고, 제조된 수지 혼합물에 귀갑 문양의 해머톤을 형성하는 첨가제로서 오르가노 폴리실록산 용액(organo poly siloxane solution)을 0.5 ~ 5.0 중량부를 넣고 혼합한 후, 경화제 0.5 ~ 5.0 중량부를 넣고 혼합하여 도료조성물을 제조하는 단계(120);100 parts by weight of the unsaturated polyester resin in the liquid powder 0.5 to 1.0 parts by weight of the powder, 0.5 to 1.0 parts by weight of zinc powder and 0.5 to 1 parts by weight of dispersant was mixed to prepare a resin mixture, and the hammer mixture pattern of hammer Preparing an coating composition by adding 0.5 to 5.0 parts by weight of an organo poly siloxane solution as an additive forming a ton, and then mixing 0.5 to 5.0 parts by weight of a curing agent; 상기 경화제가 혼합된 도료조성물을 판재(30)의 일면에 고르게 도포하여 다채무늬층(20)을 형성하는 단계(130);Forming a colorful pattern layer 20 by uniformly applying the paint composition mixed with the curing agent to one surface of the plate member 30; 도포된 다채무늬층(20)을 건조시킨 후 연마하고 광택 처리하는 마무리 단계를After drying the coated colorful pattern layer 20 is polished and polished finishing step 포함하는 것을 특징으로 하는, 다채무늬를 가진 인조대리석 제조방법.Characterized in that, comprising: artificial marble manufacturing method with a colorful pattern. 청구항 1에 있어서, 상기 도료조성물 제조 단계에서 컬러 안료 0.001 ~ 0.05 중량부를 더 첨가하여 혼합하는 것을 특징으로 하며, 다채무늬를 가진 인조대리석 제조방법.The method of claim 1, wherein the coating composition is prepared by adding 0.001 to 0.05 parts by weight of color pigments, and mixing the artificial marble. 청구항 1에 있어서, 상기 마무리 단계 중 광택 처리 과정은 건조되고 연마된 상기 다채무늬층(20)에 불포화폴리에스테르 수지를 도포한 후 건조시키고 연마한 후 약품처리 또는 기계에 의한 광택 처리를 하는 것이거나, 또는 건조되고 연마된 상기 다채무늬층(20)에 우레탄계 도료 또는 래커계 도료를 도포한 후 건조시키는 것을 특징으로 하며, 다채무늬를 가진 인조대리석 제조방법.The method of claim 1, wherein the polishing process of the finishing step is to apply an unsaturated polyester resin to the dried and polished multi-pattern layer 20, and then to dry and polish the chemical treatment or polishing by a machine Or or applying a urethane-based paint or a lacquer-based paint to the dried and polished colorful pattern layer 20, and drying the dried, polished artificial marble having a colorful pattern. 청구항 1 내지 청구항 3 중 어느 한 항에 따른 방법에 따라, 판재(30)의 적어도 한면에 형성된, 다채무늬층(20)을 구비하는 것을 특징으로 하는 인조대리석.The artificial marble according to any one of claims 1 to 3, comprising a colorful pattern layer (20) formed on at least one surface of the sheet material (30).
KR1020080077477A 2008-08-07 2008-08-07 Manufacturing Method of Artificial Marble Having Various Pattern And The Artificial Marble Thereby KR100982609B1 (en)