CN107628793A - A kind of dry powder artistic effect aggregate and its application - Google Patents
A kind of dry powder artistic effect aggregate and its application Download PDFInfo
- Publication number
- CN107628793A CN107628793A CN201711018168.5A CN201711018168A CN107628793A CN 107628793 A CN107628793 A CN 107628793A CN 201711018168 A CN201711018168 A CN 201711018168A CN 107628793 A CN107628793 A CN 107628793A
- Authority
- CN
- China
- Prior art keywords
- mesh
- dry powder
- metope
- sand
- aggregate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of dry powder artistic effect aggregate and its application.The dry powder artistic effect aggregate can justify sand, 40 80 mesh coloured silk sand, 80 120 mesh coloured silk sand etc. by 42.5 grades of white cements, 200 400 mesh calcite in powder, HPMC water-loss reducers, EVA latex powders, starch ether, 80 120 mesh texture and form.The dry powder art aggregate of the present invention, which can be criticized, to be coated on inside and outside metope, top layer is polished off after drying, again by applying Thief zone transparent confinement priming paint and except aldehyde glaze paint clear dope, it can make the coating to be formed that both there is rock art texture, again have good waterproof, anti-scratch, it is antifouling, except aldehyde and other effects, application prospect it is extensive.
Description
Technical field
The present invention relates to a kind of art of architecture ornament materials, and in particular to a kind of dry powder artistic effect aggregate and its application,
Belong to allotment and the construction application field of art of architecture ornament materials.
Background technology
Improved constantly with the living standard of people, also day is increasingly for the concern that interior decoration of the people for building is given
By force.Traditional interior decoration is mainly using interiro wall latex paint as indoor wall, the primary decoration material of ceiling.It is however, existing
Interiro wall latex paint generally existing decorative effect it is limited, color is more dull, and water proofing property is general, and soil resistance is bad, and scrub resistance has
Limit, and the deficiencies of certain pollution in work progress be present.Therefore, people gradually favor more environmentally friendly dry powder building materials in recent years
Ornament materials, but to still have decorative effect undesirable for existing dry powder building materials and ornaments material, and the defects of function is single.
The content of the invention
It is a primary object of the present invention to provide a kind of dry powder artistic effect aggregate and its application, so as to overcome prior art
In deficiency.
To realize aforementioned invention purpose, the technical solution adopted by the present invention includes：
Present invention firstly provides a kind of dry powder artistic effect aggregate, and it includes the following component calculated in parts by weight：
42.5 grades of white cements 150 ~ 250
200 ~ 400 mesh calcite in powder 200 ~ 300
HPMC water-loss reducers 4 ~ 7
EVA latex powders 4 ~ 10
Starch ether 0.2 ~ 0.8
80-120 mesh texture justifies sand 100 ~ 250
40-80 mesh coloured silks sand 100 ~ 300
80-120 mesh coloured silks sand 50 ~ 200.
Further, the dry powder artistic effect aggregate can also be made up of the following component calculated in parts by weight：
2.5 grades of white cements 150 ~ 250
200 ~ 400 mesh calcite in powder 190 ~ 260
HPMC water-loss reducers 4 ~ 7
EVA latex powders 2 ~ 8
Starch ether 0.2 ~ 0.8
80-120 mesh texture justifies sand 100 ~ 250
40-80 mesh coloured silks sand 100 ~ 300
80-120 mesh coloured silks sand 50 ~ 200
Natural sliver 10 ~ 40.
Present invention also offers a kind of slurry, and it includes the dry powder artistic effect aggregate and for uniform with the aggregate
It is mixed to form the water of the slurry.
Present invention also offers the decorative material layer formed by the dry powder artistic effect aggregate or the slurry.
Present invention also offers the purposes of the dry powder artistic effect aggregate, for example, the invention provides in one kind building
Wall construction method, it comprises the following steps：
（1）Base treatment is carried out to metope to be onstructed；
（2）Full coat transparent confinement priming paint at least one time on metope；
（3）At least twice of granted full water proof putty on metope；
（4）Metope is polished flat with 240-320 mesh rubbers；
（5）Full coat transparent confinement priming paint at least one time on metope；
（6）The slurry that is uniformly mixed to form by the dry powder artistic effect aggregate and water of granted full at least one time on metope；
（7）Through step（6）After the coating of formation is dried, then granted full is equal by the dry powder artistic effect aggregate and water on metope
The even slurry being mixed to form at least one time；
（8）Will be through step with 80-120 mesh rubber（7）The top layer of the coating of formation polishes off；
（9）Roller coating Thief zone type seal coat at least one time on metope；
（10）Roller coating removes aldehyde glaze paint clear dope at least twice on metope.
Compared with prior art, the present invention is by choosing the groups such as with particular dimensions the color sand of high-quality white cement, natural sliver
Into dry powder art aggregate, by the way that its batch is coated on inside and outside metope, and top layer is polished off after the drying, then it is hypertonic by applying
Saturating transparent confinement priming paint and except aldehyde glaze paint clear dope, can make the decorative material layer to be formed both have rock art texture, again
With good waterproof, anti-scratch, it is antifouling, except aldehyde effect and other effects, application prospect is extensive.
Embodiment
Make more detailed illustrate to technical scheme below in conjunction with some embodiments.Following each embodiment
The each component of middle use can use type known to industry, and can be obtained by the approach such as purchased in market.
Embodiment 1：A kind of dry powder artistic effect aggregate, it is made up of the following component calculated in parts by weight：
42.5 grades of white cements 250
400 mesh calcite in powder 250
HPMC water-loss reducers 4.5
EVA latex powders 4
Starch ether 0.5
80-120 mesh texture justifies sand 250
40-80 mesh coloured silks sand 100
80-120 mesh coloured silks sand 200.
Embodiment 2：A kind of dry powder artistic effect aggregate, it is made up of the following component calculated in parts by weight：
42.5 grades of white cements 200
400 mesh calcite in powder 200
HPMC water-loss reducers 4
EVA latex powders 10
Starch ether 0.3
80-120 mesh texture justifies sand 100
40-80 mesh coloured silks sand 300
80-120 mesh coloured silks sand 50.
Embodiment 3：A kind of dry powder artistic effect aggregate, it is made up of the following component calculated in parts by weight：
42.5 grades of white cements 225
325 mesh calcite in powder 300
HPMC water-loss reducers 5
EVA latex powders 8
Starch ether 0.6
80-120 mesh texture justifies sand 150
40-80 mesh coloured silks sand 1200
80-120 mesh coloured silks sand 100.
Embodiment 4：A kind of dry powder artistic effect aggregate, it is made up of the following component calculated in parts by weight：
42.5 grades of white cements 200
325 mesh calcite in powder 300
HPMC water-loss reducers 5
EVA latex powders 5
Starch ether 0.4
80-120 mesh texture justifies sand 150
40-80 mesh coloured silks sand 1200
80-120 mesh coloured silks sand 100
Natural sliver trumpet 20
Natural sliver medium size 20.
Embodiment 5：A kind of dry powder artistic effect aggregate, it is made up of the following component calculated in parts by weight：
42.5 grades of white cements 225
325 mesh calcite in powder 300
HPMC water-loss reducers 4.5
EVA latex powders 5
Starch ether 0.4
80-120 mesh texture justifies sand 150
40-80 mesh coloured silks sand 1200
80-120 mesh coloured silks sand 100
Natural sliver trumpet 30
Natural sliver medium size 10.
Dry powder artistic effect aggregate processing method may each comprise in foregoing embodiments：Imitated according to dry powder art
The composition configuration raw material of fruit aggregate, afterwards uniformly mixing（Such as mixed by modes such as stirrings）, form the dry powder art effect
Fruit aggregate.
The method that inner wall of building construction is carried out using foregoing embodiments dry powder artistic effect aggregate is as follows：
Base treatment is carried out to metope；
Base treatment；
Full coat transparent confinement priming paint one time；
Two times water proof putties of granted full；
240-320 mesh rubbers polish flat；
Time transparent confinement priming paint of full coat；
Time slurry being uniformly mixed to form by the dry powder artistic effect aggregate and water of granted full；
Time slurry being uniformly mixed to form by the dry powder artistic effect aggregate and water of granted full again after dry；
80-120 mesh rubber polishes off on surface for one layer；
Time Thief zone type seal coat of roller coating；
Roller coating removes aldehyde glaze paint clear dope two times.
By the dry powder artistic effect aggregate of foregoing embodiments, and foregoing construction method is utilized, can be formed has
The coating of imitative stone decorative effect, the coating have waterproof, it is ventilative, antifouling, except aldehyde and other effects, metope can be made attractive in appearance and prevented for a long time
Water and antifouling.
It should be appreciated that the technical concepts and features of above-described embodiment only to illustrate the invention, its object is to allow be familiar with this
The personage of item technology can understand present disclosure and implement according to this, and it is not intended to limit the scope of the present invention.It is all
The equivalent change or modification made according to spirit of the invention, it should all be included within the scope of the present invention.
Claims (5)
1. a kind of dry powder artistic effect aggregate, it is characterised in that including the following component calculated in parts by weight：
42.5 grades of white cements 150 ~ 250
200 ~ 400 mesh calcite in powder 200 ~ 300
HPMC water-loss reducers 4 ~ 7
EVA latex powders 4 ~ 10
Starch ether 0.2 ~ 0.8
80-120 mesh texture justifies sand 100 ~ 250
40-80 mesh coloured silks sand 100 ~ 300
80-120 mesh coloured silks sand 50 ~ 200.
2. a kind of dry powder artistic effect aggregate, it is characterised in that be made up of the following component calculated in parts by weight：
42.5 grades of white cements 150 ~ 250
200 ~ 400 mesh calcite in powder 190 ~ 260
HPMC water-loss reducers 4 ~ 7
EVA latex powders 2 ~ 8
Starch ether 0.2 ~ 0.8
80-120 mesh texture justifies sand 100 ~ 250
40-80 mesh coloured silks sand 100 ~ 300
80-120 mesh coloured silks sand 50 ~ 200
Natural sliver 10 ~ 40.
3. slurry, it is characterised in that comprising dry powder artistic effect aggregate any one of claim 1-2 and for it is described
Aggregate is uniformly mixed to form the water of the slurry.
4. the dress that dry powder artistic effect aggregate or the slurry described in claim 4 as any one of claim 1-2 are formed
The decoration materials bed of material.
5. a kind of inner wall of building construction method, it is characterised in that comprise the following steps：
（1）Base treatment is carried out to metope to be onstructed；
（2）Full coat transparent confinement priming paint at least one time on metope；
（3）At least twice of granted full water proof putty on metope；
（4）Metope is polished flat with 240-320 mesh rubbers；
（5）Full coat transparent confinement priming paint at least one time on metope；
（6）The slurry that granted full is uniformly mixed to form by the dry powder artistic effect aggregate of claim 1 or 2 and water on metope is extremely
It is few one time；
（7）Through step（6）After the coating of formation is dried, then granted full is equal by the dry powder artistic effect aggregate and water on metope
The even slurry being mixed to form at least one time；
（8）Will be through step with 80-120 mesh rubber（7）The top layer of the coating of formation polishes off；
（9）Roller coating Thief zone type seal coat at least one time on metope；
（10）Roller coating removes aldehyde glaze paint clear dope at least twice on metope.