CN106978081A - A kind of sintered quartz sand sand textured coating - Google Patents
A kind of sintered quartz sand sand textured coating Download PDFInfo
- Publication number
- CN106978081A CN106978081A CN201710197376.XA CN201710197376A CN106978081A CN 106978081 A CN106978081 A CN 106978081A CN 201710197376 A CN201710197376 A CN 201710197376A CN 106978081 A CN106978081 A CN 106978081A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- sand
- quartz sand
- sintered quartz
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention proposes coating and aqueous overcoating material in a kind of sintered quartz sand sand textured coating, including aqueous primer, the bonding non-woven cloth coating set gradually from the inside to the outside, sintered quartz sand.The paint coatings are attractive in appearance, elegant, and color and luster is soft, and particle is uniform, it is adaptable to villa and high-grade civil buildings.The composite coating antiseptic property is excellent, weatherability is up to 20 years, self-cleaning function is strong and beautifying and decorating function is distinct, the unique construction technology for after non-woven fabrics drape over one's shoulders and scraping by using pasting, improve the adhesive force of coating and basal plane, reduce weight of coated paint, reduce coating application cost, non-woven fabrics and building adhesive water layer can play excellent waterproof action simultaneously, reduce exterior wall water drenching leak source.
Description
Technical field
The present invention relates to a kind of sintered quartz sand sand textured coating.
Background technology
At present, with the steady-state growth of China's economic development, urban construction is maked rapid progress, and moulding is unique, outward appearance is eye-catching
Building is seen everywhere, and the alien invasion of new building also increasingly enriches in terms of selection and color.In recent years, as people give birth to
Running water is flat to be stepped up, and everybody requires more and more higher to urban residential environment, and we also recognize that glass curtain wall is present gradually
Light pollution, security can not be ignored, and lightning-arrest property, the durability of metal curtain wall are also worrying, the load of lithotome, protection against the tide
It can not be ignored, glazed tile is easy to fall off dangerous.And exterior coating body weight most light, color is most bright-coloured, security is best, progressively
Obtain the welcome of people.Covered with paint, lacquer, colour wash, etc. on elevation of building the advantage of exterior coating except color it is beautiful it is abundant in addition to, also building load is small, valency
The relatively low energy-conserving product of energy consumption in the characteristics of lattice are low, easy construction, duration are shorter and easily update, or production.
In building coating in use, the drawbacks of various coating have respective different.Common put down is applied because using a large amount of mill bases, when
Between easily fade long, the easy leak when crackle occurs in metope；Texture coating color is single, and decorative effect is general；True mineral varnish is used
Spraying application, Construction of High-rise is difficult, and spraying sand leakage amount is big, pollutes environment；Art coatings are difficult to large area because of technique limitation
Construction.
The content of the invention
The present invention proposes a kind of sintered quartz sand sand textured coating, including primer, middle coating and coating materials, and formation is answered
Closing coating both has a superior weatherability, excellent workability, and with surmounting the third dimension of common buildings coating, stereovision,
Make outside vertical surface of building more attractive.
The technical proposal of the invention is realized in this way：
A kind of sintered quartz sand sand textured coating, including aqueous primer, the bonding non-woven fabrics set gradually from the inside to the outside
Coating and aqueous overcoating material in coating, sintered quartz sand.
Preferably, the aqueous primer includes following component composition by weight：Alkali resistant sealing emulsion 40-60
Part, 40-60 parts of water, 0.8~1.2 part of pH adjusting agent, 0.8~1.2 part of coalescents, 0.5~0.8 part of bactericide, defoamer 0.8
~1.2 parts.
Preferably, the cohesive non-woven cloth coating is that front is plane cl oth with groove, the back side to there is non-woven fabrics fiber
The non-woven fabrics of silk, both are bonded by binding material.
Preferably, the binding material includes component A and B component, the use of proportioning is 1:1；The component A composition is by weight
It is calculated as：8~14 parts of water, 1-2 parts of HPMC celluloses, 40~60 parts of adhesive for building, 0.5~0.8 part of biocide mildewcide, 40~
70 15~25 parts of mesh quartz sands, 80~120 15~25 parts of mesh quartz sands, 0.5~0.8 part of defoamer；The B component is 42.5 marks
Number cement.
Preferably, coating includes following component by weight in the sintered quartz sand：Resin-bonded base-material 24~
32 parts, 75~81 parts of sintered quartz sand, 0.5~1 part of mica sheet.
Preferably, the resin-bonded base-material includes following component by weight：4~8 parts of water, resin aqueous emulsion
13~15 parts, 1.8~2.2 parts of cellulose, 0.8~1.2 part of pH adjusting agent, 0.8~1.2 part of coalescents, bactericide 0.5~
0.8 part, 0.8~1.2 part of defoamer.
Preferably, the resin aqueous emulsion is in aqueous silicone acrylic emulsion, aqueous pure acrylic latex, waterborne styrene-acrylic emulsion
One of which.
Preferably, the sintered quartz sand uses high-temperature calcination after 30~40 mesh round shaped grain quartz sands, hybrid pigment, after cooling
It is broken to be filtrated to get.
Preferably, the aqueous overcoating material includes following component by weight：20-60 parts of water, water-based fluorocarbon resin
40-80 parts, 0.8~1.2 part of pH adjusting agent, 0.8~1.2 part of coalescents, 0.5~0.8 part of bactericide, defoamer 0.8~1.2
Part, 0.5~0.8 part of leveling auxiliary agent.
Preferably, the water-based fluorocarbon resin is water-based fluorocarbon resin or water-based fluorocarbon resin and the aqueous modified poly of silicon third
One of which in the mixture of thing.
Compared with prior art, beneficial effects of the present invention are：
(1) present invention is a kind of high-weatherability, and waterproof is graceful, high-rise easy working green building decoration material, with commonly building
Build coating to compare, combine the advantage of flexible texture coating and stone-like coating, provided on the basis of with excellent decoration functions
High-weatherability, easily water proofing property and the performance such as construction, with reference to excellent coating materials, improves the stain resistance of paint film.
(2) present invention solves the drawbacks of high-rise outer wall coating is sprayed by way of blade coating, while avoiding texture painting
The unicity of material, color is more rich；By the control to floating coat particle diameter, make coating granule sense stronger, with reference to flash of light mica sheet
The noble quality of this coating can be more embodied, it is elegant.
(3) present invention solves the same particle diameter coating application difficulty of traditional coating, it is difficult to the problem of scraping is draped over one's shoulders, by using outer
Wall moisture-proof adhesive and unique non-woven fabrics bonding process, make construction more smooth, coating particles are more evenly distributed, while improving outer
The performance of wall waterproof anticracking.
Embodiment
Technical scheme is clearly and completely described below in conjunction with the embodiment of the present invention, it is clear that retouched
The embodiment stated is only a part of embodiment of the invention, rather than whole embodiments.Based on the embodiment in the present invention, sheet
The every other embodiment that field those of ordinary skill is obtained under the premise of creative work is not made, belongs to the present invention
The scope of protection.
Embodiment 1
A kind of sintered quartz sand sand wall-like building external paint, the coating includes the aqueous basecoat set gradually from the inside to the outside
Coating and aqueous overcoating material in material, bonding non-woven cloth coating, sintered quartz sand.
The aqueous priming paint raw material composition and its weight part ratio are：50 parts of alkali resistant sealing emulsion, 46.9 parts of water and pH are adjusted
0.8 part of agent, 1 part of coalescents, 0.5 part of bactericide, 0.8 part of defoamer.PH adjusting agent is AMP-95 (2- amino-2-methyls -1-
Propyl alcohol), coalescents are alcohol ester 12, and bactericide is chlormethylisothiazo,ine ketone, and defoamer is polysiloxane emulsion.
The cohesive non-woven cloth coating raw material composition and its weight part ratio are：Component A component ratio is：8 parts of water, HPMC is fine
1 part of dimension element, 50 parts of adhesive for building, 0.5 part of biocide mildewcide, 40~70 20 parts of mesh quartz sands, 80~120 mesh quartz sands 20
Part, 0.5 part of defoamer.Adhesive for building is styrene-acrylic emulsion NaPoly CB 421, and bactericide is chlormethylisothiazo,ine ketone,
Defoamer is polysiloxane emulsion；B component is 42.5 grade cements.
Coating raw material composition and its weight part ratio are in the sintered quartz sand：75 parts of sintered quartz sand, 1 part of mica sheet,
In resin-bonded 24 parts of base-material, resin-bonded base-material：6.6 parts of water, 12 parts of resin aqueous emulsion, 2 parts of cellulose, PH conditioning agents
0.8 part, 0.8 part of coalescents, 0.8 part of bactericide, 1 part of defoamer.Resin aqueous emulsion is aqueous silicone acrylic emulsion, aqueous pure third
One kind in olefin(e) acid emulsion, waterborne styrene-acrylic emulsion, cellulose is that hydroxyethyl cellulose HEC30000, PH conditioning agent are AMP-95
(2-amino-2-methyl-1-propanol), coalescents are alcohol ester 12, and bactericide is chlormethylisothiazo,ine ketone, and defoamer is ore deposit
Thing oils, quartz sand is 30-40# high temperature sintering colorful quartz sands.
The raw material of the coating materials is constituted and its weight part ratio is：40 parts of water, 56.2 parts of water-based fluorocarbon resin, PH conditioning agents
1 part, 1 part of coalescents, 0.5 part of bactericide, 0.8 part of defoamer, 0.5 part of leveling auxiliary agent.Water-based fluorocarbon resin is water-based fluorocarbon
One kind in resin, water-based fluorocarbon resin and the polymer-modified mixture of aqueous silicon third, PH conditioning agents are AMP-95 (2- ammonia
Base -2- methyl isophthalic acids-propyl alcohol), coalescents are alcohol ester 12, and bactericide is chlormethylisothiazo,ine ketone, and defoamer is mineral oil
Class, leveling auxiliary agent is nonionic polyurethane polymer or hydrophobically-modified alkali swelling type polyacrylic acid.
The preparation method of aqueous primer comprises the following steps：Water is added into the reactor of homogenizer, in stirring
Water, pH adjusting agent, coalescents, bactericide, defoamer and alkali resistant sealing emulsion are sequentially added under into whirlpool state, is uniformly dispersed
30 ± 10min is kept in the case where stirring into whirlpool state afterwards, is filtered and packaged.
Paste the preparation of the component A of non-woven cloth coating：(1) hot water of requirement is taken, vessel in heating is put into 85 DEG C
More than, HPMC celluloses are gradually added into the case where slowly stirring, originally HPMC celluloses float on the surface, but are gradually disperseed, shape
Into uniform slurry, solution is cooled down under agitation；(2) water is added into sand textured coating special reactor, under stirring
The auxiliary agents such as defoamer, biocide mildewcide are sequentially added, the cellulose dissolved with water is added；(3) building is added into reactor
With adhesive, quartz sand is being added, low speed is at the uniform velocity stirred 1 hour.Preparation finishes component A, and B component according to 1:1 ratio is mixed
Close, stirred with electric blender and non-woven cloth coating is pasted needed for being made.
The preparation method of coating comprises the following steps successively in sintered quartz sand：(1) add into homogenizer reactor
Enter water, pH adjusting agent is added in the case where stirring into whirlpool state, bactericide, defoamer, high-speed stirred uniformly adds cellulose afterwards
HEC30000, high-speed stirred to cellulose uniform dissolution；(2) reduction rotating speed is to 300 ± 50rpm, add coalescents and
Resin aqueous emulsion, is at the uniform velocity stirred standby after 30-50min；(3) the resin sizing material that completes is prepared, to be added to sand textured coating special
With in reactor, sintered quartz sand and mica sheet needed for input, low speed at the uniform velocity stir i.e. obtained required sintered quartz after 1h
Sand sand textured coating intermediate coat.
The preparation method of aqueous overcoating material comprises the following steps successively：(1) water is added into reactor, whirlpool is being stirred into
PH adjusting agent, bactericide, the auxiliary agent such as defoamer and leveling auxiliary agent are sequentially added under state；(2) after being uniformly dispersed, reduction rotating speed is extremely
300 ± 50rpm, adds coalescents and water-based fluorocarbon resin emulsion, 30-40min, bag filter is kept under at the uniform velocity stirring
Dress, obtains aqueous overcoating material.
It is interior to outer to set gradually aqueous primer, bond coating and aqueous overcoating material in non-woven cloth coating, sintered quartz sand
And coagulation forming produces the sand textured coating of the present invention.
Embodiment 2：
Step be the same as Example 1, unlike：
Aqueous priming paint raw material is constituted and its weight part ratio is：40 parts of alkali resistant sealing emulsion, 56.9 parts of water and PH conditioning agents 0.8
Part, 1 part of coalescents, 0.5 part of bactericide, 0.8 part of defoamer.
Bond non-woven cloth coating raw material composition and its weight part ratio is：Component A component ratio is：8 parts of water, HPMC celluloses
1 part, 40 parts of adhesive for building, 0.5 part of biocide mildewcide, 40~70 25 parts of mesh quartz sands, 80~120 25 parts of mesh quartz sands,
0.5 part of defoamer；B component is 42.5 grade cements.Wherein component A, B component by weight 1:1 assembles.
Coating raw material composition and its weight part ratio are in sintered quartz sand：75 parts of sintered quartz sand, 1 part of mica sheet, resin
24 parts of base-material of bonding, resin-bonded 5.6 parts of base-material reclaimed water, 13 parts of resin aqueous emulsion, 2 parts of cellulose, 0.8 part of PH conditioning agents,
0.8 part of coalescents, 0.8 part of bactericide, 1 part of defoamer,
The raw material of aqueous overcoating material is constituted and its weight part ratio is：20 parts of water, 76 parts of water-based fluorocarbon resin, PH conditioning agents 1
Part, 1.2 parts of coalescents, 0.5 part of bactericide, 0.8 part of defoamer, 0.5 part of leveling auxiliary agent.
Embodiment 3：
Step be the same as Example 1, unlike：
Aqueous priming paint raw material is constituted and its weight part ratio is：Alkali resistant sealing emulsion 56.9%, water 40% and PH conditioning agents
0.8%, coalescents 1%, bactericide 0.5%, defoamer 0.8%.
Bond non-woven cloth coating raw material composition and its weight part ratio is：.A composition component ratio is：Water 8%, HPMC fibers
Element 1%, adhesive for building 60%, biocide mildewcide 0.5%, 40~70 mesh quartz sands 15%, 80~120 mesh quartz sands
15%, defoamer 0.5%；B component is 42.5 grade cements.Wherein component A, B component by weight 1:1 assembles.
Raw materials for varnish composition and its weight part ratio are in the middle of sintered quartz sand sand textured coating：Sintered quartz sand 73%, mica
The resin-bonded base-material 26% of piece 1%, resin-bonded base-material reclaimed water 6.6%, resin aqueous emulsion 15%, cellulose 2%, PH regulations
Agent 0.8%, coalescents 0.8%, bactericide 0.8%, defoamer 1%
The raw material of coating materials is constituted and its weight part ratio is：Water 50%, water-based fluorocarbon resin 45.9%, PH conditioning agents
0.8%, coalescents 1.2%, bactericide 0.5%, defoamer 0.8%, leveling auxiliary agent 0.8%.
After being stirred in a kind of sintered quartz sand sand wall-like building external paint, container made from above three embodiment
Without caking, in uniform state, paint film appearance is normal；Drying time (GB/T 1728-1979) is 3h；Move and inspire initial stage crack resistance without
Crackle；Water resistance (GB/T 1733-1993) 96h is without exception；Alkali resistance (GB/T 9265, the immersion of saturated calcium hydroxide solution)
96h is without exception；After 5 cyclic tests of stain resistance (GB/T 9780)≤2 grades；Artificial ageing resistance (GB/T 1865-1997)
500h is non-foaming, do not ftracture, fall off；Excellent impact resistance；Resistance to coating temperature denaturation (JG/T 25) is without exception；Adhesion strength mark
Under quasi- state >=0.7, after immersion >=0.5.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
God is with principle, and any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (10)
1. a kind of sintered quartz sand sand textured coating, it is characterised in that including the aqueous primer, viscous set gradually from the inside to the outside
Tie coating and aqueous overcoating material in non-woven cloth coating, sintered quartz sand.
2. a kind of sintered quartz sand sand textured coating as claimed in claim 1, it is characterised in that the aqueous primer includes
Following component composition by weight：40-60 parts of alkali resistant sealing emulsion, 40-60 parts of water, 0.8~1.2 part of pH adjusting agent, into
0.8~1.2 part of film auxiliary agent, 0.5~0.8 part of bactericide, 0.8~1.2 part of defoamer.
3. a kind of sintered quartz sand sand textured coating as claimed in claim 1, it is characterised in that the cohesive non-woven cloth coating
It is that plane cl oth with groove, the back side are the non-woven fabrics that has non-woven fabrics fiber silk for front, both are bonded by binding material.
4. a kind of sintered quartz sand sand textured coating as claimed in claim 3, it is characterised in that the binding material includes A groups
Divide and B component, the use of proportioning is 1:1；The component A composition is calculated as by weight：8~14 parts of water, 1-2 parts of HPMC celluloses,
40~60 parts of adhesive for building, 0.5~0.8 part of biocide mildewcide, 40~70 15~25 parts of mesh quartz sands, 80~120 mesh stones
15~25 parts of sand, 0.5~0.8 part of defoamer；The B component is 42.5 grade cements.
5. a kind of sintered quartz sand sand textured coating as claimed in claim 1, it is characterised in that applied in the sintered quartz sand
Material includes following component by weight：Resin-bonded 24~32 parts of base-material, 75~81 parts of sintered quartz sand, mica sheet 0.5
~1 part.
6. a kind of sintered quartz sand sand textured coating as claimed in claim 5, it is characterised in that the resin-bonded base-material bag
Containing following component by weight：4~8 parts of water, 13~15 parts of resin aqueous emulsion, 1.8~2.2 parts of cellulose, pH regulations
0.8~1.2 part of agent, 0.8~1.2 part of coalescents, 0.5~0.8 part of bactericide, 0.8~1.2 part of defoamer.
7. a kind of sintered quartz sand sand textured coating as claimed in claim 6, it is characterised in that the resin aqueous emulsion is
One of which in aqueous silicone acrylic emulsion, aqueous pure acrylic latex, waterborne styrene-acrylic emulsion.
8. a kind of sintered quartz sand sand textured coating as claimed in claim 5, it is characterised in that the sintered quartz sand is used
Crush and be filtrated to get after high-temperature calcination, cooling after 30~40 mesh round shaped grain quartz sands, hybrid pigment.
9. a kind of sintered quartz sand sand textured coating as claimed in claim 1, it is characterised in that the aqueous overcoating material is included
Following component by weight：20-60 parts of water, 40-80 parts of water-based fluorocarbon resin, 0.8~1.2 part of pH adjusting agent, film forming is helped
0.8~1.2 part of agent, 0.5~0.8 part of bactericide, 0.8~1.2 part of defoamer, 0.5~0.8 part of leveling auxiliary agent.
10. a kind of sintered quartz sand sand textured coating as claimed in claim 9, it is characterised in that the water-based fluorocarbon resin
For water-based fluorocarbon resin or water-based fluorocarbon resin and the one of which in the polymer-modified mixture of aqueous silicon third.