KR100904248B1 - Ocher perlite and manufactruing method thereof - Google Patents
Ocher perlite and manufactruing method thereof Download PDFInfo
- Publication number
- KR100904248B1 KR100904248B1 KR1020070123395A KR20070123395A KR100904248B1 KR 100904248 B1 KR100904248 B1 KR 100904248B1 KR 1020070123395 A KR1020070123395 A KR 1020070123395A KR 20070123395 A KR20070123395 A KR 20070123395A KR 100904248 B1 KR100904248 B1 KR 100904248B1
- Authority
- KR
- South Korea
- Prior art keywords
- perlite
- weight
- ocher
- parts
- mixed
- Prior art date
Abstract
본 발명은 상토에 섞었을 때 식물의 성장을 돕는 동시에 상토의 색깔과 조화를 이루는 황토 퍼라이트 및 그 제조방법에 관한 것이다. 상기와 같은 문제를 해결하기 위한 수단으로, 제올라이트 20 ~ 40중량부, 황토 5 ~ 15중량부, 세리사이트 20 ~ 40중량부, 토르마린 20 ~ 40중량부, 게르마늄 파우더 0.01 ~ 0.05중량부 및 티탄 파우더 0.01 ~ 0.05중량부를 혼합하여 분쇄한 혼합분쇄물과, 혼합분쇄물에 퍼라이트와 물을 첨가하여 형성된 것이 특징이다. 본 발명인 황토 퍼라이트는 상토와 유사한 색상을 가지고 있어 상토와 섞어 사용할 때 자연스럽게 어우러져 미관상 좋다. 또한 음이온과 원적외선이 방출되어 공기정화 및 탈취 효과가 있다. 또한 통기성과 배수성이 좋아 식물이 잘 자랄 수 있도록 도와주고, 배수구가 없는 화분이나 화단의 상토에 혼합하여 사용할 수 있다. 또한 발포유리 같이 날카로운 부분이 없어, 식물의 뿌리를 보호할 수 있고 운반시 포장이 찢어지거나 사람이 다치는 일도 미연에 방지할 수 있다. 또한 무게가 가벼워 상토와 혼합하여 사용할 때 중량을 감소시킬 수 있고, 생산이 용이하고 생산 비용이 저렴하여 경제적이다. The present invention relates to an ocher perlite and a method for producing the same, which are compatible with the color of the clay while helping to grow the plant when mixed with the clay. As a means for solving the above problems, 20 to 40 parts by weight of zeolite, 5 to 15 parts by weight of ocher, 20 to 40 parts by weight of sericite, 20 to 40 parts by weight of tourmaline, 0.01 to 0.05 parts by weight of germanium powder and titanium powder It is characterized by being formed by adding a mixture of crushed by grinding 0.01 ~ 0.05 parts by weight and perlite and water to the mixed powder. The ocher perlite of the present invention has a color similar to topsoil, so when it is mixed with the topsoil, it naturally looks good. In addition, the negative ions and far-infrared rays are emitted, thereby purifying and deodorizing the air. In addition, it has good breathability and drainage to help the plant grow well, and can be used by mixing in the soil of pots or flower beds without drains. In addition, there are no sharp parts like foam glass, which protects the roots of plants and prevents the packaging from being torn or injured. In addition, it is light in weight, and can be reduced in weight when used in combination with the topsoil.
황토, 퍼라이트, 펄라이트 Ocher, perlite, perlite
Description
본 발명은 황토 퍼라이트 및 그 제조방법에 관한 것으로, 보다 상세하게는 상토에 섞었을 때 식물의 성장을 돕는 동시에 상토의 색깔과 조화를 이루는 황토 퍼라이트 및 그 제조방법에 관한 것이다.The present invention relates to an ocher perlite and a method for manufacturing the same, and more particularly, to an ocher perlite and a method for producing the same, which are compatible with the color of the soil while helping to grow a plant when mixed with the soil.
일반적으로 관상용 화분이나 옥상, 가정의 간이 화단 등에는 흙이나 원예용 상토가 사용된다. 특히 최근에는 상토채취에 대한 노동력 절감과 상토 소독이 되어 있고, 비료가 함유되어 있는 인공상토를 많이 사용한다.Generally, soil or horticultural soil is used for ornamental flower pots, rooftops, and simple flower beds in homes. In particular, in recent years, the labor force reduction and topsoil disinfection for topsoil collection, and artificial soils containing fertilizer are frequently used.
그러나 인공상토는 가격이 비쌀 뿐만 아니라 인공상토만을 이용하여 식물을 식재하면 식물이 건강하게 잘 자랄 수 없다. 이러한 문제 때문에 통기성을 위해 인공상토에 발포유리를 섞어서 사용해왔었다.However, artificial clay is not only expensive, but planting plants using artificial clay alone does not allow plants to grow well. Because of this problem, a mixture of foam glass has been used in artificial clay for breathability.
발포유리는 세라믹 덩어리를 잘게 파쇄하여 형성된다. 파쇄된 발포유리는 입자가 균일하지 않고, 표면이 날카로운 유리날이나 뾰족한 송곳형상을 갖게 된다. 이러한 표면을 부드럽고 무디게 하는 과정을 거치지만 일부 발포유리의 표면이 날카로워 유통중 손을 다치거나 봉투가 찢어지거나 식물 뿌리에 손상을 주는 경우가 발생하게 된다. 또한 발포유리의 소재가 고가이기 때문에 비경제적이다.Foamed glass is formed by finely crushing a ceramic mass. The crushed foam glass has a non-uniform particle and has a sharp glass blade or sharp awl shape. Although the surface is softened and blunted, the surface of some foam glass is sharp, which may injure hands, tear bags, or damage plant roots during distribution. In addition, because the material of the foam glass is expensive, it is uneconomical.
또한 발포유리를 대신하여 퍼라이트를 사용하기도 한다.Perlite is also used instead of foam glass.
퍼라이트는 진주암(화산석)을 약 1200℃의 고온에서 압력을 가하면서 본래의 부피에 비해 4~12배까지 팽창시킨 것이다. 이는 마치 팝콘을 만드는 원리와 같다. 퍼라이트는 팽창될 때, 눈처럼 하얀 각각의 알갱이들이 아주 많은 작은 기포들로 채워지고 PH가 중성인 상태로 소독된다. Perlite is a swelling of pearlite (volcanic rock) 4-12 times its original volume under pressure at a high temperature of about 1200 ° C. This is like the principle of making popcorn. When the ferrite is inflated, each grain of snow white is filled with so many small bubbles and disinfected with a neutral pH.
퍼라이트 알갱이 표면은 작은 공극들로 뒤덮여 있기 때문에 아주 큰 표면적을 갖게 된다. 이러한 표면은 수분과 비료를 유지시켜주고, 최적의 통기성과 배수성을 제공하는 공기의 통로가 형성된다. 또한 소독이 되어 있어 무균상태로 잡초종자나 해충이 없고, 가볍고 부드러우며 가격이 저렴한 장점이 있다. The surface of the ferrite grain is covered with small voids and therefore has a very large surface area. These surfaces provide air passages that retain moisture and fertilizers and provide optimal breathability and drainage. In addition, it is sterilized, so there are no weed seeds or pests, and it is light, soft and inexpensive.
그러나 퍼라이트는 하얀색을 띄고 있어 상토에 섞었을 경우 미관상 좋지 않다. 특히 상토를 육안으로 볼 수 있는 투명한 유리화분의 상토에 섞으면 이물질처럼 보일 수 있어 식재된 식물의 미관을 저해한다.However, the ferrite is white, which is not good when mixed with soil. In particular, when mixed with the topsoil of the vitrified vitrified flower pot visible to the naked eye, it may look like a foreign matter, which hinders the aesthetics of planted plants.
또한 하얀색 퍼라이트를 대신하여 황갈색으로 코팅한 퍼라이트를 사용하기도 한다. 그러나 코팅시 접착제를 사용하기 때문에 퍼라이트의 표면 공극들이 막히게 되어 통기성과 배수성이 떨어진다. 또한 퍼라이트의 속은 하얗고 겉은 황갈색을 띠고 있어 퍼라이트의 코팅이 벗겨질 경우 중간중간 하얀색이 드러나게 되어 지저분해 보일 수 있다.In addition, instead of white perlite, yellowish-brown coated perlite is used. However, because of the use of adhesives in the coating, the pores of the surface of the ferrite are clogged, resulting in poor breathability and drainage. In addition, the inside of the ferrite is white and the outside is yellowish brown, so when the coating of the ferrite is peeled off, the intermediate white color can be revealed and it may look messy.
본 발명은 상기와 같은 문제를 해결하고자 하는 것으로, 본 발명의 목적은 상토 색상과 유사한 색상의 퍼라이트를 제작하여 상토에 섞었을 경우 육안으로 확인되지 않아 자연스럽게 보이도록 하는 황토 퍼라이트 및 그 제조방법을 제공하는 것이다.The present invention is to solve the above problems, an object of the present invention is to provide a loess perlite and a method of manufacturing the same so as to produce a perlite of the color similar to the topsoil so that it is not visible to the naked eye to look natural. It is.
또한 본 발명의 또 다른 목적은 상토와 섞어서 사용할 때 미관상 자연스러울 뿐만 아니라 퍼라이트의 표면에 형성된 공극이 그대로 유지되기 때문에 본래의 통기성과 배수성이 유지되도록 하는 황토 퍼라이트 및 그 제조방법을 제공하는 것이다.It is another object of the present invention to provide an ocher perlite and a method of manufacturing the same, which maintains the original breathability and drainage because the pores formed on the surface of the perlite are not only aesthetically natural when used in combination with the clay.
또한 본 발명의 또 다른 목적은 통기성과 항균성이 좋아 구멍 없는 화분에 혼합하여 사용 가능하도록 하는 황토 퍼라이트 및 그 제조방법을 제공하는 것이다.In addition, another object of the present invention is to provide an ocher perlite and a method for manufacturing the same, which can be mixed and used in a potless plant having good breathability and antibacterial properties.
상기와 같은 문제를 해결하고자 하는 수단으로,As a means to solve the above problems,
제올라이트 20 ~ 40중량부, 황토 5 ~ 15중량부, 세리사이트 20 ~ 40중량부, 토르마린 20 ~ 40중량부, 게르마늄 파우더 0.01 ~ 0.05중량부 및 티탄 파우더 0.01 ~ 0.05중량부를 혼합하여 분쇄한 혼합분쇄물과, 혼합분쇄물에 퍼라이트와 물을 첨가하여 형성된 것이 특징이다.20 to 40 parts by weight of zeolite, 5 to 15 parts by weight of ocher, 20 to 40 parts by weight of sericite, 20 to 40 parts by weight of tourmaline, 0.01 to 0.05 parts by weight of germanium powder and 0.01 to 0.05 parts by weight of titanium powder It is characterized by being formed by adding perlite and water to the water and the mixed crushed material.
또한 혼합분쇄물은 0.5 ~ 1.5 ㎛의 크기로 분쇄된 것이 특징이다.In addition, the mixed powder is characterized in that the crushed to the size of 0.5 ~ 1.5 ㎛.
또한 황토 퍼라이트는 5 ~ 25부피비로 상토와 혼합되는 것이 특징이다.In addition, ocher perlite is characterized in that it is mixed with the top soil in a 5 to 25 volume ratio.
또한 퍼라이트는 입자의 크기가 0.5 ~ 1.5 ㎝인 것이 특징이다.In addition, the perlite is characterized by a particle size of 0.5 ~ 1.5 cm.
또한 제올라이트 20 ~ 40중량부, 황토 5 ~ 15중량부, 세리사이트 20 ~ 40중량부, 토르마린 20 ~ 40중량부, 게르마늄 파우더 0.01 ~ 0.05중량부 및 티탄 파우더 0.01 ~ 0.05중량부를 혼합하여 분쇄하는 단계와; 혼합분쇄물과 퍼라이트에 물을 첨가하면서 중탕으로 가열하는 단계와; 물을 증발시키면서 가압하여 가열하는 단계; 및 냉각과 건조를 통해 황토 퍼라이트를 완성하는 단계;로 이루어지는 것이 특징이다.In addition, 20 to 40 parts by weight of zeolite, 5 to 15 parts by weight of ocher, 20 to 40 parts by weight of sericite, 20 to 40 parts by weight of tourmaline, 0.01 to 0.05 parts by weight of germanium powder and 0.01 to 0.05 parts by weight of titanium powder, followed by grinding Wow; Heating with a hot bath while adding water to the mixed powder and the perlite; Heating by pressurizing while evaporating water; And completing the ocher perlite through cooling and drying.
또한 황토 퍼라이트 제조방법에 있어서, 혼합분쇄물과 퍼라이트와 물은 1 : 1 : 5중량비로 혼합되는 것이 특징이다.In addition, in the ocher perlite manufacturing method, the mixed ground product, the perlite and the water are mixed in a 1: 1: 5 weight ratio.
또한 황토 퍼라이트 제조방법에 있어서, 혼합분쇄물은 0.5 ~ 1.5 ㎛의 크기로 분쇄된 것이 특징이다.In addition, in the ocher perlite manufacturing method, the mixed powder is characterized in that the crushed to the size of 0.5 ~ 1.5 ㎛.
또한 황토 퍼라이트 제조방법에 있어서, 중탕가열 단계는 46 ~ 48시간 동안 가열하는 것이 특징이다.In addition, in the ocher perlite manufacturing method, the hot water heating step is characterized in that the heating for 46 to 48 hours.
또한 황토 퍼라이트 제조방법에 있어서, 가압가열 단계는 1 ~ 2시간 동안 가열하는 것이 특징이다.In addition, in the ocher perlite manufacturing method, the pressure heating step is characterized by heating for 1 to 2 hours.
또한 황토 퍼라이트 제조방법에 있어서, 가압가열 단계는 800 ~ 1000 ℃의 온도가 되도록 가열하는 것이 특징이다.In the ocher perlite manufacturing method, the pressure heating step is characterized in that the heating to a temperature of 800 ~ 1000 ℃.
또한 황토 퍼라이트 제조방법에 있어서, 냉각과 건조단계는 자연상태에서 이루어지는 것이 특징이다.In the ocher perlite manufacturing method, the cooling and drying step is characterized in that the natural state.
아울러 황토 퍼라이트 제조방법에 있어서, 퍼라이트는 입자의 크기가 0.5 ~ 1.5 ㎝인 것이 특징이다.In addition, in the ocher perlite manufacturing method, the perlite is characterized in that the particle size of 0.5 ~ 1.5 cm.
본 발명인 황토 퍼라이트는 상토와 유사한 색상을 가지고 있어 상토와 섞어 사용할 때 자연스럽게 잘 어우러져 미관상 좋다. The ocher perlite of the present invention has a color similar to that of topsoil, so when it is mixed with the topsoil, it naturally blends well and looks good.
또한 음이온과 원적외선이 방출되어 공기정화 및 탈취 효과가 있다.In addition, the negative ions and far-infrared rays are emitted, thereby purifying and deodorizing the air.
또한 통기성과 배수성이 좋아 식물이 잘 자랄 수 있도록 도와주고, 배수구가 없는 화분이나 화단의 상토에 혼합하여 사용할 수 있다.In addition, it has good breathability and drainage to help the plant grow well, and can be used by mixing in the soil of pots or flower beds without drains.
또한 발포유리 같이 날카로운 부분이 없어, 식물의 뿌리를 보호할 수 있고 운반시 포장이 찢어지거나 사람이 다치는 일도 미연에 방지할 수 있다.In addition, there are no sharp parts like foam glass, which protects the roots of plants and prevents the packaging from being torn or injured.
또한 무게가 가벼워 상토와 혼합하여 사용할 때 중량을 감소시킬 수 있고, 생산이 용이하고 생산 비용이 저렴하여 경제적이다. In addition, it is light in weight, and can be reduced in weight when used in combination with the topsoil.
이하, 본 발명의 바람직한 실시예를 첨부한 도면들을 참조하여 상세히 설명한다. 우선 각 도면의 구성요소들에 참조부호를 부가함에 있어서, 동일한 구성요소들에 대해서는 비록 다른 도면상에 표시되더라도 가능한 한 동일한 부호를 사용한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. First, in adding reference numerals to components of each drawing, the same reference numerals are used for the same components as much as possible even if they are shown in different drawings.
또한 하기에서 본 발명을 설명함에 있어, 관련된 공지기능 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략한다.In addition, in the following description of the present invention, if it is determined that a detailed description of a related known function or configuration may unnecessarily obscure the subject matter of the present invention, the detailed description thereof will be omitted.
도 1은 본 발명인 황토 퍼라이트 평면도이다. 도 1에 도시된 바와 같이, 본 발명인 황토 퍼라이트(100)는 제올라이트 20 ~ 40중량부, 황토 5 ~ 15중량부, 세리사이트 20 ~ 40중량부, 토르마린 20 ~ 40중량부, 게르마늄 파우더 0.01 ~ 0.05중량부 및 티탄 파우더 0.01 ~ 0.05중량부를 혼합하여 분쇄한 혼합분쇄물과, 혼합분쇄물에 퍼라이트와 물을 첨가하여 형성된다.1 is a top view of an ocher perlite of the present invention. As shown in Figure 1, the present
혼합분쇄물은 0.5 ~ 1.5 ㎛의 크기로 분쇄된 것이다. 혼합물을 분쇄하여 혼합물에 의해 퍼라이트가 황토색으로 쉽게 변하도록 한다.The mixed powder is pulverized to a size of 0.5 ~ 1.5 ㎛. The mixture is pulverized so that the perlite is easily turned ocher by the mixture.
퍼라이트의 입자 크기는 0.5 ~ 1.5 ㎝정도이다.The particle size of the perlite is about 0.5 to 1.5 cm.
혼합분쇄물과 퍼라이트와 물은 1 : 1 : 5중량비로 혼합한다. 상기 중량비보다 혼합분쇄물을 더 넣으면 진흙형태로 황토색의 퍼라이트가 형성되어 상토와 섞어 사용하기 어렵다. 또한 퍼라이트를 상기 중량비보다 더 넣으면 퍼라이트에 혼합물이 잘 침투되지 않아 황토 퍼라이트(100)가 형성되기 힘들어진다. Mixed ground product, perlite and water are mixed in a 1: 1: 5 weight ratio. When the mixed powder is added more than the weight ratio, yellow clay perlite is formed in the form of mud, and it is difficult to use it with mixed soil. In addition, if the perlite is added more than the weight ratio, the mixture does not penetrate well into the perlite, and thus it becomes difficult to form the
이하 본 발명의 제조방법을 설명하면 다음과 같다.Hereinafter, the manufacturing method of the present invention will be described.
도 2는 본 발명인 황토 퍼라이트의 제조 방법을 나타낸 제조 공정도이다. 도 2에 도시된 바와 같이, 황토 퍼라이트(100)의 제조방법은 제올라이트 20 ~ 40중량부, 황토 5 ~ 15중량부, 세리사이트 20 ~ 40중량부, 토르마린 20 ~ 40중량부, 게르마늄 파우더 0.01 ~ 0.05중량부 및 티탄 파우더 0.01 ~ 0.05중량부를 혼합하여 분쇄하는 단계(S10)와; 혼합분쇄물과 퍼라이트에 물을 첨가하면서 중탕으로 가열하는 단계(S20)와; 물을 증발시키면서 가압하여 가열하는 단계(S30); 및 냉각과 건조를 통해 황토 퍼라이트를 완성하는 단계(S40);로 이루어진다.Figure 2 is a manufacturing process diagram showing a method for producing ocher perlite of the present invention. As shown in Figure 2, the manufacturing method of the
먼저 제올라이트 20 ~ 40중량부, 황토 5 ~ 15중량부, 세리사이트 20 ~ 40중 량부, 토르마린 20 ~ 40중량부, 게르마늄 파우더 0.01 ~ 0.05중량부 및 티탄 파우더 0.01 ~ 0.05중량부를 혼합하여 혼합물을 형성한다. First, 20 to 40 parts by weight of zeolite, 5 to 15 parts by weight of ocher, 20 to 40 parts by weight of sericite, 20 to 40 parts by weight of tourmaline, 0.01 to 0.05 parts by weight of germanium powder and 0.01 to 0.05 parts by weight of titanium powder to form a mixture. do.
제올라이트는 퍼라이트에 대한 황토의 흡수율을 높여주는 역할을 한다. Zeolites play a role of increasing the absorption rate of ocher to perlite.
황토는 세균을 흡수 제거하고 원적외선을 발산시켜 생체리듬을 활성화시켜 준다. 또한 황토는 천연 염색의 재료로 이용되어 황토 이불이나 황토 옷과 같이 일상생활 용품의 염색에 자주 사용되었다. 본 발명에서는 퍼라이트를 황토색으로 제조하여 미관상 자연스럽게 상토와 섞일 수 있도록 한다.Ocher absorbs and removes bacteria and emits far infrared rays, activating biorhythms. Also, ocher was used as a natural dyeing material and was often used for dyeing everyday items such as ocher quilts and ocher cloth. In the present invention, the perlite is produced in ocher color so that it can be naturally mixed with normal soil.
세리사이트(견운모)는 항균력을 갖고, 원적외선을 발생시킨다. 원적외선은 세균을 없애고, 모세혈관을 확장시켜 혈액순환과 세포조직 생성에 도움을 주는 것으로 알려져 있다.Serisite has antimicrobial activity and generates far infrared rays. Far infrared rays are known to remove bacteria and expand capillaries to help blood circulation and tissue formation.
토르마린(일명 전기석)은 보석의 일종으로 음이온과 원적외선을 발생시킨다. 음이온은 포름알데히드와 같은 유해물질을 정화하고, 담배 연기나 불쾌한 냄새를 제거하며 살균작용을 통해 곰팡이의 발생 및 공기의 오염을 방지하는 기능을 하는 것으로 알려져 있다. Tourmaline (aka tourmaline) is a type of gem that generates negative ions and far infrared rays. Negative ions are known to function to purify harmful substances such as formaldehyde, remove tobacco smoke or unpleasant odors, and to prevent the occurrence of mold and air pollution through sterilization.
게르마늄 파우더와 티탄 파우더는 항균성을 갖고 다량의 원적외선과 음이온을 방출시키며 광촉매 작용을 통하여 공기를 정화시키는 탈취 효과가 있다.Germanium powder and titanium powder have antibacterial effect, release a large amount of far infrared rays and anions, and have a deodorizing effect to purify the air through photocatalytic action.
혼합물은 0.5 ~ 1.5 ㎛의 크기가 되도록 분쇄하여 준비한다. The mixture is prepared by grinding to a size of 0.5 ~ 1.5 ㎛.
분쇄된 혼합물에 0.5 ~ 1.5 ㎝ 크기의 퍼라이트를 1 : 1중량비가 되도록 혼합한다. 0.5-1.5 cm of size of perlite is mixed in a 1: 1 weight ratio to the ground mixture.
퍼라이트는 상토에 혼합하여 사용하는 인공토양의 한 종류이다. 퍼라이트는 작은 공극들로 뒤덮여 있기 때문에 아주 큰 표면적을 갖게 된다. 이러한 표면은 수분과 비료를 유지시켜주고, 최적의 통기성과 배수성을 제공하는 공기의 통로가 형성된다.Perlite is a kind of artificial soil mixed with topsoil. Perlite is covered with small voids and therefore has a very large surface area. These surfaces provide air passages that retain moisture and fertilizers and provide optimal breathability and drainage.
혼합분쇄물과 퍼라이트와 물의 중량비가 1 : 1 : 5가 되도록 혼합하여 중탕으로 가열한다. 가열 시 가압되지 않도록 뚜껑을 덮지 않은 상태에서 가열하고, 물이 줄어들면 물을 보충하면서 46 ~ 48시간동안 가열한다. Mix the mixed powder, the weight ratio of perlite and water so that it is 1: 1: 5, and heat it with a bath. Heat the lid without lid to prevent it from being pressurized, and heat it for 46 to 48 hours with water replenishing if water is reduced.
마지막으로 1 ~ 2시간 동안 뚜껑을 덮어 가압하면서 가열한다. 이때 물을 보충하지 않으면서 가열하여 물을 증발시킨다. 퍼라이트는 1200 ℃에서 발포되어 생성되기 때문에 1200 ℃가 넘지 않는 800 ~ 1000 ℃의 온도가 유지되도록 가압하면서 가열하는 것이 바람직하다. Finally, cover with lid and heat under pressure for 1-2 hours. At this time, the water is evaporated by heating without adding water. Since the perlite is produced by foaming at 1200 ° C, it is preferable to heat it while pressurizing such that the temperature of 800 to 1000 ° C not exceeding 1200 ° C is maintained.
수분이 촉촉하게 남아 있는 상태가 되면 자연 냉각과 건조를 통하여 황토 퍼라이트(100)가 완성된다. When the moisture remains moist, the
상기와 같은 과정을 거치면서 퍼라이트에 구성된 다수의 공극을 통해서 혼합분쇄물에 포함된 황토가 퍼라이트의 속과 겉을 모두 황토색으로 변화시킨다. 즉, 퍼라이트는 이온결합으로 이루어져 있어 혼합분쇄물의 황토물이 내부까지 쉽게 침투된다. 또한 퍼라이트의 공극은 그대로 유지되면서 겉과 속이 모두 황토색으로 변하게 된다.Through the above process, the yellow soil contained in the mixed pulverized through the plurality of pores configured in the perlite changes both the inside and the outside of the perlite to ocher color. That is, the perlite is composed of ionic bonds so that the loess of the mixed powder is easily penetrated to the inside. In addition, the pores of the ferrite remain intact while the outer and inner sides turn yellow.
즉, 퍼라이트의 통기성과 보습력은 유지되면서 자연스럽게 상토에 혼합되어지기 때문에 미관상 보기 좋은 황토 퍼라이트(100)가 형성된다. 또한 통기성과 배수성이 좋아 식물이 잘 자랄 수 있도록 도와준다.That is, because the permeability and moisturizing power of the perlite is naturally mixed with the top soil, aesthetic appearance is
상토와 황토 퍼라이트(100)는 95 ~ 75 : 5 ~ 25 부피비로 혼합하여 사용한다. 황토 퍼라이트(100)를 너무 많이 혼합하면 화분 내의 양분이 부족하게 되어 식물의 성장을 저해시킬 수 있다. 또한 너무 적게 혼합하면 통기성이 저하되어 식물이 잘 자랄 수 없게 된다.Top soil and ocher perlite (100) is used by mixing in a volume ratio of 95 to 75: 5 to 25. If the
또한 세리사이트, 토르마린, 게르마늄 파우더 및 티탄 파우더가 황토 퍼라이트에 함유되어 음이온과 원적외선을 방사시켜 인체에 좋은 영향을 주게된다. 또한 항균효과와 탈취효과로 인하여 공기를 정화 시켜줌으로써 쾌적한 실내 공기 조성에 도움을 준다.In addition, sericite, tourmaline, germanium powder and titanium powder are contained in ocher perlite, which emits negative ions and far infrared rays, which affects the human body. In addition, by purifying the air due to the antibacterial and deodorant effect helps to create a comfortable indoor air.
특히 배수구가 없는 화분에 사용하는 상토(일명 항균성 인공토양, 특허등록 제0761496호)는 고령토 24중량부에 대해 붕사 1중량부, 붕산 1중량부 및 소다 1중량부를 배합하여 유리 전이온도까지 가열하고, 자연 냉각시켜 유리결정질 입자로 분쇄하여 형성된다. 본 발명인 황토 퍼라이트(100)는 항균성 인공토양에 혼합하여 배수구가 없는 화분에 사용할 수 있다. In particular, the soil used for pots without drainage (aka antimicrobial artificial soil, Patent Registration No. 0761496) is heated to the glass transition temperature by mixing 1 part by weight of borax, 1 part by weight of boric acid and 1 part by weight of soda with respect to 24 parts by weight of kaolin. It is naturally cooled and pulverized into glass crystalline particles. The
(제 1실시예)(First embodiment)
제올라이트 30중량부, 황토 9중량부, 세리사이트 30중량부, 토르마린 30중량부, 게르마늄 파우더 0.02중량부 및 티탄 파우더 0.03중량부를 혼합하여 1 ㎛의 크기로 분쇄한다.30 parts by weight of zeolite, 9 parts by weight of ocher, 30 parts by weight of sericite, 30 parts by weight of tourmaline, 0.02 parts by weight of germanium powder and 0.03 parts by weight of titanium powder are mixed and ground to a size of 1 μm.
분쇄된 혼합물과 입자 크기가 0.7 ㎝인 퍼라이트와 물을 1 : 1 : 5중량비로 혼합하여 47시간 동안 중탕으로 가열한다. 가열시 가압이 되지 않도록 뚜껑을 덮지 않고 가열한다. 또한 물이 줄어들면 물을 첨가하면서 가열한다.The milled mixture, perlite having a particle size of 0.7 cm, and water were mixed in a 1: 1: 5 weight ratio and heated in a bath for 47 hours. Heat without lid to prevent pressurization during heating. In addition, when water is reduced, it is heated while adding water.
47시간 동안 가열한 후 1시간 동안 물을 첨가하지 않고 뚜껑을 덮은 채로 가압하면서 가열하여 물을 증발시킨다. 이때 퍼라이트의 발포온도인 1200 ℃보다 낮은 900 ℃ 사이의 온도를 유지하는 것이 바람직하다.After heating for 47 hours, the water is evaporated by heating with pressurized lid without adding water for 1 hour. At this time, it is preferable to maintain the temperature between 900 ℃ lower than 1200 ℃ the foaming temperature of the ferrite.
수분이 촉촉하게 남아 있는 상태가 되면 자연 냉각과 건조를 통하여 황토 퍼라이트(100)가 완성된다. When the moisture remains moist, the
황토 퍼라이트(100)는 자연스럽게 상토와 혼합되어 미관상 좋다.
이때 상토와 황토 퍼라이트(100)는 85 : 15 부피비로 혼합하여 사용하는 것이 바람직하다. 황토 퍼라이트(100)를 너무 많이 혼합하면 화분 내의 양분이 부족하게 되어 식물의 성장을 저해시킬 수 있다. 또한 너무 적게 혼합하면 통기성이 저하되어 식물이 잘 자랄 수 없게 된다.At this time, the top soil and ocher perlite (100) is preferably used in a mixture of 85: 15 by volume. If the
(제 2실시예)(Second embodiment)
제올라이트 20중량부, 황토 5중량부, 세리사이트 20중량부, 토르마린 20중량부, 게르마늄 파우더 0.01중량부 및 티탄 파우더 0.01중량부를 혼합하여 0.5 ㎛의 크기로 분쇄한다.20 parts by weight of zeolite, 5 parts by weight of ocher, 20 parts by weight of sericite, 20 parts by weight of tourmaline, 0.01 parts by weight of germanium powder and 0.01 parts by weight of titanium powder are mixed and ground to a size of 0.5 μm.
분쇄된 혼합물과 입자 크기가 0.7 ㎝인 퍼라이트와 물을 1 : 1 : 5중량비로 혼합하여 46시간 동안 중탕으로 가열한다. 가열시 가압이 되지 않도록 뚜껑을 덮지 않고 가열한다. 또한 물이 줄어들면 물을 첨가하면서 가열한다.The milled mixture, perlite having a particle size of 0.7 cm and water were mixed in a 1: 1: 5 weight ratio and heated in a bath for 46 hours. Heat without lid to prevent pressurization during heating. In addition, when water is reduced, it is heated while adding water.
46시간 동안 가열한 후 2시간 동안 물을 첨가하지 않고 뚜껑을 덮은 채로 가압하면서 가열하여 물을 증발시킨다. 이때 퍼라이트의 발포온도인 1200 ℃보다 낮은 800 ℃ 사이의 온도를 유지하는 것이 바람직하다.After heating for 46 hours, the water is evaporated by heating with pressurized lid without adding water for 2 hours. At this time, it is preferable to maintain the temperature between 800 ℃ lower than 1200 ℃ the foaming temperature of the ferrite.
수분이 촉촉하게 남아 있는 상태가 되면 자연 냉각과 건조를 통하여 황토 퍼라이트(100)가 완성된다. When the moisture remains moist, the
이때 상토와 황토 퍼라이트(100)는 80 : 20 부피비로 혼합하여 사용한다. At this time, the top soil and ocher perlite (100) is used by mixing in a volume ratio of 80:20.
(제 3실시예)(Third Embodiment)
제올라이트 40중량부, 황토 13중량부, 세리사이트 40중량부, 토르마린 40중량부, 게르마늄 파우더 0.03중량부 및 티탄 파우더 0.03중량부를 혼합하여 1.3 ㎛의 크기로 분쇄한다.40 parts by weight of zeolite, 13 parts by weight of ocher, 40 parts by weight of sericite, 40 parts by weight of tourmaline, 0.03 parts by weight of germanium powder and 0.03 parts by weight of titanium powder are mixed and ground to a size of 1.3 μm.
분쇄된 혼합물과 입자 크기가 1.0 ㎝인 퍼라이트와 물을 1 : 1 : 5중량비로 혼합하여 48시간 동안 중탕으로 가열한다. 가열시 가압이 되지 않도록 뚜껑을 덮지 않고 가열한다. 또한 물이 줄어들면 물을 첨가하면서 가열한다.The pulverized mixture was mixed with a 1.0 cm perlite and water in a 1: 1: 5 weight ratio and heated in a bath for 48 hours. Heat without lid to prevent pressurization during heating. In addition, when water is reduced, it is heated while adding water.
48시간 동안 가열한 후 1시간 동안 물을 첨가하지 않고 뚜껑을 덮은 채로 가압하면서 가열하여 물을 증발시킨다. 이때 퍼라이트의 발포온도인 1200 ℃보다 낮은 1000 ℃ 사이의 온도를 유지하는 것이 바람직하다.After heating for 48 hours, the water is evaporated by heating with pressurized lid for 1 hour without adding water. At this time, it is preferable to maintain the temperature between 1000 ℃ lower than 1200 ℃ the foaming temperature of the ferrite.
수분이 촉촉하게 남아 있는 상태가 되면 자연 냉각과 건조를 통하여 황토 퍼라이트(100)가 완성된다. When the moisture remains moist, the
이때 상토와 황토 퍼라이트(100)는 90 : 10 부피비로 혼합하여 사용한다. At this time, the top soil and ocher perlite (100) is used by mixing in a 90:10 volume ratio.
이하에서는 상기와 같은 실시예들을 통해 제조된 황토 퍼라이트(100) 샘플의 시험 결과에 대해 설명하도록 한다. 시험은 한국건자재시험연구원(KICM)에 의뢰하여 이루어졌다.Hereinafter will be described with respect to the test results of the
* 샘플 : 본 발명인 황토 퍼라이트 샘플을 나타냄.* Sample: Represents an ocher perlite sample of the present invention.
[표1]에 나타난 바와 같이, 황토 퍼라이트(100)가 없는 상태에서보다 황토 퍼라이트(100)가 있는 상태일 때 음이온이 13배 이상 방출되는 것을 알 수 있다.As shown in [Table 1], it can be seen that the anion is released more than 13 times when the
* 본 시험결과는 FT-IR Spectrometer를 이용한 Black Body대비 측정 결과이다.* This test result is compared with Black Body using FT-IR Spectrometer.
[표2]에 나타난 바와 같이, 황토 퍼라이트(100)로부터 많은 양의 원적외선이 방출된다는 것을 확인할 수 있다.As shown in [Table 2], it can be seen that a large amount of far infrared rays are emitted from the
[표3]에 나타난 바와 같이, 황토 퍼라이트(100)가 포함되지 않은 경우는 탈취가 거의 이루어지지 않았지만, 황토 퍼라이트(100) 샘플의 경우에는 120분이 경과한 후 탈취율이 약 90 %에 달하여 대부분의 악취가 탈취된 것을 확인할 수 있다.As shown in [Table 3], when the
도 1은 본 발명인 황토 퍼라이트 평면도.1 is a top view of the ocher perlite of the present invention.
도 2는 본 발명인 황토 퍼라이트의 제조 방법을 나타낸 제조 공정도.Figure 2 is a manufacturing process diagram showing a method for producing ocher perlite of the present invention.
* 도면의 주요부분에 대한 부호의 설명 * Explanation of symbols on the main parts of the drawings
100 : 황토 퍼라이트100: ocher perlite
Claims (12)