KR100880047B1 - Processed porous gemstones and preparation methods thereof, and drain pipes having a mixture of these porous gemstones attached therein - Google Patents

Abstract

The present invention relates to a processed porous gemstone and a manufacturing method thereof, and a drain pipe that performs a multifunctional role by attaching an environmentally friendly functional material based on the porous gemstone as a main material therein.

The present invention for this purpose, so as to be attached to or coupled to the inside of the pipes or pipe parts used as the drain pipe,

75 to 85% by weight of selected porous gemstones of 5 to 40mm size and 14.5 to 22% by weight of film waterproofing agent, which were calcined at 300 to 1000 ° C, were rotated for 20 to 30 minutes, and then some tagging remained. When the step of adding 0.5 to 3% by weight of anionic powder or tourmaline powder;

Adding a curing accelerator in an amount corresponding to 0.3 to 3% by weight of the mixture while rotating the crotch in which the mixture is added at a constant speed and repeating the process for 2 to 5 times for 30 minutes to 1 hour;

65 to 75% by weight of the processed porous ore, 15 to 20% by weight of charcoal and 10 to 15% by weight of the resin binder prepared in the same range as the size of the porous ore by stirring in a stirrer to obtain an environmentally friendly functional material;

It is achieved by including the step of attaching and attaching the inside of the pipes or the pipe parts thereof before the obtained eco-friendly functional material is solidified.

Porous gemstones, functional materials, drain pipes, piping, piping parts

Description

Processed porous gemstones and preparation methods thereof, and drainage pipes having a mixture of these porous gemstones attached therein {.}

Figure 1a is a cross-sectional view showing the piping and the sewer pipe of the bathroom to which the present invention is applied.

Figure 1b is a cross-sectional view showing the piping parts and sewer pipe of the kitchen to which the present invention is applied.

Figure 1c is a cross-sectional view showing an excellent pipe of the balcony to which the present invention is applied.

2 is a view showing an embodiment of a sewage pipe that serves as a multifunctional filter through the eco-friendly functional material according to the present invention.

3 is another embodiment of the present invention.

* Description of symbols on the main parts of the drawings *

10: piping 20: sewage pipe

30: excellent view 40: balcony

The present invention relates to a processed porous gemstone and a manufacturing method thereof, and a drain pipe that performs a multifunctional role by attaching an environmentally friendly functional material based on the porous gemstone as a main material therein.

In general, the drainage pipe refers to a drainage system connected to sewage and rainwater pipes to discharge wastewater and rainwater discharged indoors and outdoors, and in a narrower range, it refers to sewage / water drainage pipes that are piped to the balcony of a kitchen, a bathroom, or an apartment. .

In particular, household sewage used in kitchens or bathrooms such as homes are discharged through sewage pipes buried underground, and the sewage pipes consist of a constant gradient, so that the sewage is naturally discharged and discharged.

In addition, balconies are usually provided in aggregates such as apartments or townhouses, and rainwater pipes penetrating the upper and lower floors of the aggregates are installed in the balconies, and the rainwater drained from the rooftops is discharged through underground sewer pipes. Let's go.

However, the sewage discharged from the kitchen or bathroom has a bad smell backflow through the sewage pipe, and especially in the bathroom of the assembly building, the noise of the discharge is severe. Therefore, the pipe parts such as traps or elbows are variously modified in the piping of the kitchen or bathroom. The above problem is solved.

In addition, rainwater pipes on the veranda of the apartment are also causing noise by falling rainwater, which causes the rainwater to splash into the balcony.

The present invention has been made to solve such a problem, the object of the present invention is buried underground by attaching or combining a lightweight porous ore that emits anion and gemstone ultraviolet rays inside the pipes used as drainage pipes and their parts. It is to provide a drain pipe that performs a multifunctional role through an eco-friendly functional material that can block the odor flowing back from the sewer pipe, remove the noise of the discharge and at the same time purify the discharged sewage and rainwater quality.

Other objects and effects of the present invention will become apparent from the following detailed description, and the detailed description and examples showing the preferred embodiments of the present invention do not limit the scope of the present invention.

The present invention for achieving the above object, in the pipes used as a drain pipe or a method for producing a porous gemstone attached or coupled to the inside of the pipe part,

75 to 85% by weight of selected porous gemstones of 5 to 40mm size and 14.5 to 22% by weight of film waterproofing agent, which were calcined at 300 to 1000 ° C, were rotated for 20 to 30 minutes, and then anion was left when the tagging remained. 0.5 to 3% by weight of any one of the powder or tourmaline powder is mixed and put into the crotch and rotated to harden to 100% by weight of the mixture consisting of any one selected from the porous gemstone, coating waterproofing agent, anion powder or tourmaline powder The accelerator is added in an amount corresponding to 0.3 to 3% by weight of the mixture, characterized in that it is obtained by repeating the process for 2 to 5 times to rotate it for 30 minutes to 1 hour.

In the pipes used as a drain pipe or a method for producing a porous raw stone mixture attached or bonded to the inside of the pipe portion,
75 to 85% by weight of selected porous gemstones of 5 to 40mm size and 14.5 to 22% by weight of film waterproofing agent, which were calcined at 300 to 1000 ° C, were rotated for 20 to 30 minutes, and then anion was left when the tagging remained. 0.5 to 3% by weight of any one selected from powder or tourmaline powder is mixed, it is put into the crotch and rotated, 100% by weight of the mixture of any one selected from the porous gemstone, coating waterproofing agent and anionic powder or tourmaline powder Based on the amount of the curing accelerator in the amount of 0.3 to 3% by weight and the porous gemstone prepared by repeating the process 2 to 5 times for 30 minutes to 1 hour repeated 65 to 75% by weight, and the size of the porous gemstone 15 to 20% by weight of charcoal and 10 to 15% by weight of the resin binder provided in the same range is characterized in that the stirring in the stirrer.

As a drain pipe formed by inserting and attaching a porous raw stone mixture therein,
The porous gemstone mixture,
75 ~ 85% by weight of selected porous gemstones of 5 ~ 40mm size and 14.5 ~ 22% by weight of film waterproofing agent fired under the condition of 300 ~ 1000 ℃, rotated for 20 ~ 30 minutes and then rotated for 20 ~ 30 minutes. Or 0.5 to 3% by weight of any one selected from tourmaline powder to mix, put into the crotch and rotated to harden to 100% by weight of the mixture of any one selected from the porous gemstone, coating waterproofing agent and anionic powder or tourmaline powder Including the promoter in an amount corresponding to 0.3 to 3% by weight and having a porous gemstone 65-75% by weight repeated two to five times the process of rotating for 30 minutes to 1 hour, 65-75% of the porous gemstone 15 to 20% by weight of charcoal and 10 to 15% by weight of the resin binder provided in the same range as the size of the% is made by stirring in a stirrer,
It is characterized in that the porous raw stone mixture made as described above is formed by being introduced into and attached to the pipes or the pipe parts thereof before solidification.

delete

In addition, any one of a straight pipe, an elbow pipe, a tee pipe, and a trap is applied to the pipe part.

delete

Hereinafter, one preferred embodiment according to the present invention will be described in detail with reference to the accompanying drawings. First, like reference numerals designate functionally identical or similar parts throughout the drawings.

Figure 1a is an installation cross-sectional view showing the piping parts and sewage pipe of the bathroom to which the present invention is applied, Figure 1b is an installation cross-sectional view showing the piping parts and sewage pipe of the kitchen to which the present invention is applied, Figure 1c is applied to the present invention This is a sectional view showing an excellent pipe of a balcony.

As shown in Figures 1a to 1b, the pipe part 10 to which the present invention is applied has an interior in order to prevent the backflow of the drainage noise or odor when the domestic sewage falls vertically, such as a trap and an elbow pipe. It can be seen that it forms a curved surface.

These pipe parts 10 are connected to the drainage sewer pipe 20, and in particular, the sewage may fall from the place reaching the curved surface of the maximum diameter of the trap or elbow pipe and hit each other to generate drainage noise. have.

Figure 1c is a storm pipe installed on the balcony, extending vertically to allow the rain flow flowing down from the roof or upper floor to flow downward. In particular, the rain pipe 30 is formed with rainwater inlet groove 32 which is opened to the upper surface of the balcony 40 of each floor, where the noise due to the fall of rainwater is generated.

Again, Figure 2 is a view showing an embodiment of the sewage pipe that serves as a multifunctional filter through the eco-friendly functional material according to the present invention.

1A to 2, the present invention is to be attached to or coupled to the pipes used as the drain pipe 20 or the pipe part 10 inside thereof,

75 to 85% by weight of selected porous gemstones of 5 to 40mm size and 14.5 to 22% by weight of film waterproofing agent, which were calcined at 300 to 1000 ° C, were rotated for 20 to 30 minutes, and then some tagging remained. When the step of adding 0.5 to 3% by weight of anionic powder or tourmaline powder;

Adding a curing accelerator in an amount corresponding to 0.3 to 3% by weight of the mixture while rotating the crotch in which the mixture is added at a constant speed and repeating the process for 2 to 5 times for 30 minutes to 1 hour;

65 to 75% by weight of the processed porous gemstone, 15 to 20% by weight of charcoal and 10 to 15% by weight of a resin binder in a stirrer to obtain an environmentally friendly functional material;

It is characterized in that it comprises the step of attaching, attached to the inside of the pipe or the pipe parts before the obtained eco-friendly functional material is solidified.

First, the environmentally friendly functional material 50 applied to the present invention is composed of processed porous gemstones 52 and charcoal 54 and a resin binder 56 combining them.

Eco-friendly functional material 50 is to solve the problem of the conventional sewage as described above, and can have a physical effect while having a variety of environmentally friendly functional effects using natural materials.

For this purpose, the porous gemstone 52 is processed to a size of 5 to 40 mm, selected one of selected vermiculite, pumice, feldspar, pearlite, or using two or more of these mixed ores, and vermiculite, pumice, feldspar, Briefly look at Jinjuam.

First, vermiculite is an inorganic material formed by volcanic rock system with gas depletion in magma state, which is porous and has good absorption ability. .

Pumice is a result of the sudden decrease in pressure when the magma is released into the atmosphere, resulting in the release of volatile components in the magma resulting in numerous pores.These pumice stones are light enough to float in water due to their low specific gravity. In addition, it is used as aggregate of heat shield wall concrete.

It is mainly used for horticulture as an inorganic material. It has many pores and is a lightweight body, and has good water retention, drainage, and breathability.

Pearlite is suitable as the main material of the present invention to be used for industrial, construction and agriculture as a light aggregate raw material after expanding at high temperature.

Therefore, porous ore selected from vermiculite, pumice stone, calcite and pearlite is used alone or in combination of two or more.

When the porous gemstone provided as above is heated and calcined at a temperature of 300 to 1000 ° C. in the heating furnace, the porous gemstone expands vertically in the direction of splitting with water vapor during heating, and the pores of the porous gemstone are 6 It becomes ~ 20 times larger and emits negative ions or raw ultraviolet rays through the enlarged pores.

The porous gemstones that have been sintered and thus formed are formed as sterile soils of low acidity (ph5.4 ~ 6) by high temperature treatment, and are hard, very light, chemically nontoxic, stable, as well as optimum insulating properties and ion exchange capacity. This has a nice feature.

It is well known that the charcoal 54 is excellent in the effect of radiating negative ions and far infrared rays, and furthermore, it can be seen that the deodorizing function is also excellent.

The charcoal 54 having a function as described above is processed to 5 to 40 mm, the size of which the porous gemstone 52 is provided and mixed with the porous gemstone 52.

In particular, the mixing ratio of the porous gemstone 52 and the charcoal 54 is mixed with 65 to 75% by weight of the porous gemstone 52 processed by the following processing method at a ratio of 15 to 20% by weight of the charcoal 54. The reason for setting the ratio of the porous gemstone 52 as above is to endure the impact of sewage or rain drop, and the porous gemstone 52 is lightweight and thus affects the load of the pipe part 10 to be attached or coupled. This is because it does not affect.

On the other hand, the porous gemstone 52 should be made in a more robust state due to the characteristics of the drop impact and semi-permanent use as described above.

To this end, by processing the calcined porous gemstone 52 as described above with a film waterproofing agent, anionic powder, tourmaline powder, a curing accelerator, the desired porous gemstone 52 can be obtained.

The process of processing porous gemstones is carried out by putting 75 ~ 85% by weight of selected porous gemstones and 14.5 ~ 22% by weight of the film waterproofing agent into the crotch and rotating for 20-30 minutes, and then when there is some tagging, anion powder or tourmaline powder Add 0.5 to 3% by weight.

Then, while slowly rotating the crotch at a constant speed is added to the curing accelerator in an amount corresponding to 0.3 to 3% by weight of the mixture and repeated for 2 minutes to 5 minutes to rotate for 30 minutes to 1 hour.

During the processing process, the porous gemstone is dried and cured in a granular state to maximize the space (pores) between the grains and at the same time maintains a lightweight state, and the surface of the porous gemstone is waterproof coated by a coating film over several times.

Here, the anion powder is a natural mineral that emits negative ions and serves to release a large amount of negative ions beneficial to the human body.

Tourmaline is a borosilicate with hexagonal columnar crystals. It is a natural mineral belonging to the hexagonal system. The crystal itself generates electricity and is discharged momentarily upon contact with moisture. The separated hydrogen ions (H ⁺ ) are combined with the electrons that are attracted to the negative electrode and are neutralized. The hydrogen ions (H ₂ ) are evaporated to become alkali ionized, and the hydroxide ions (OH ⁻ ) are separated from the surrounding water molecules. coupled to a hydroxyl anion (H ₃ O ₂ ^-) generated there is a surface-active substance, called, the hydroxyl anion is about alkalized water to optimal and pH7.4, generated far-infrared is natanaeseo a high value by staggering Promotes blood circulation, blood purification and thrombolysis to human body with strong thermal effect and high penetration It is effective, and it is well known that while stimulating the autonomic nervous system while improving the immune function in the human body to suppress the excitability of the sympathetic nerve and serves to reduce the acidified human body.

Subsequently, the porous raw stone 52 and the charcoal 54 mixed through the resin binder 56 are combined and then solidified to form an eco-friendly functional material 50.

In particular, the resin binder 56 is only one example, but is solidified together with the piping part 10 in the piping part 10. The porous gemstone 52 and the charcoal 54 are integrated to integrate the pipe part 10. It serves to attach or bond with.

As described above, the optimum mixing ratio of the resin binder 56 to be attached to or coupled to the pipe part 10 by forming the functional material 50 is 65 to 75% by weight of the processed porous gemstone 52 and charcoal 54. It is preferable to mix 10-15 weight% of resin binders 56 with -20 weight%.

In particular, the resin binder 56 is conventionally all admixtures including natural rubber and synthetic rubber that can be added to the cement mortar, for example, styrene butadiene rubber (SBR), nitrile butadiene rubber (NBR), epoxy, acrylic, The resin of any one selected from the urethane system may be used, and an emulsion may be usually added to such a resin binder.

As shown, the environmentally-friendly functional material 50 as described above is a solid multifunctional filter through the environmentally friendly functional material according to the present invention by inputting, attaching or combining the inside of the pipes or the pipe parts 10 before solidification. Complete the drain pipe.

In addition, as shown in detail, the functional material 50 is attached to or coupled to the pipe part 10 in a streamlined shape to attenuate the flow rate of falling sewage and absorbs the drop shock to cancel the noise. Able to know.

On the other hand, Figure 3 shows a state in which the eco-friendly functional material 50 is attached or combined inside the rain pipe 30 of the balcony 40 as another embodiment of the present invention.

That is, rainwater that is accumulated on the rooftop or balcony 40 falls along the rainwater pipe 30, and the rainwater that falls is collided with the eco-friendly functional material 50, and the flow rate thereof decreases. As it flows down along the rain pipe 30, the fall noise is drastically reduced.

Next will be described in detail the operation process and the effects of the environmentally friendly functional material 50 formed in the pipe part 10 or the sewage pipe 20.

As described above, the present invention may be attached to or coupled to the inside of the pipe part 10 and the sewer pipe 20 shown in FIGS. 1A to 1C, and it will be described in particular with reference to FIG. 2.

The drainage of living sewage falls and passes through the pipe part 10. Passed household sewage is preferably dropped into the upper portion of the eco-friendly functional material 50 formed in a streamlined form, and the dropped household sewage is penetrated into the porous groove 52a of the porous gemstone 52 forming the eco-friendly functional material 50. The drop load is canceled, which causes the drop noise, that is, the drain noise, to be drastically reduced.

The sewage that continues to fall is reduced in frying and proceeds to the sewer pipe 20 by natural flow.

At this time, the living sewage penetrated into the porous groove (52a) is purified by the anion and far infrared rays emitted from the porous ore (52) and charcoal (54), and then proceeds to the sewer pipe (20).

On the other hand, although not shown in the sewage pipe 20, anyone can see that the living sewage flowing by attaching or combining the eco-friendly functional material 50 is purified as it passes through the eco-friendly functional material 50.

In addition, the environmentally friendly functional material 50 according to the present invention performs the radiation and deodorization of the anion to the far infrared as described above at the same time to offset the odor flowing back through the sewage pipe (20).

In addition, the necessity of cleaning occurs when used for a long time as a property that can be used semi-permanently, but the eco-friendly functional material 50 according to the present invention is poured into the porous groove 52a of the porous gemstone 50 by pouring only clean hot water. Just remove the dirt.

That is, as will be clear from the electric description, the present invention provides an eco-friendly functional material 50 capable of performing various functions and a drain pipe to which the eco-friendly functional material 50 is attached or combined, which is environmentally friendly and can improve water quality. It can be used semi-permanently.

This invention can be implemented in other various forms, without deviating from the mind or main characteristic. For this reason, the above-described embodiments are merely examples in all respects and should not be interpreted limitedly. The scope of the present invention is shown by the scope of the claims, and is not limited by the specification text. Again, all variations and modifications belonging to the equivalent scope of the claims are within the scope of the present invention.

On the other hand, the drain pipe referred to in this specification is used in the widest sense, such as a pipe in which five or rainwater is discharged to the outdoors, and is not limited only to the aforementioned pipe part.

As described in detail above, according to the drain pipe that performs a multifunctional role through the eco-friendly functional material according to the present invention, by attaching or combining a lightweight porous gemstone that emits negative ions and gemstones to various pipes and its parts, It blocks the odor flowing back from the sewer pipe buried in, reduces the noise generated by the drop impact, and at the same time has the effect of purifying the discharged sewage and rainwater quality.

Claims (7)

In the pipes used as a drain pipe or a method for producing a porous gemstone attached or coupled to the inside of the pipe part, 75 to 85% by weight of selected porous gemstones of 5 to 40mm size and 14.5 to 22% by weight of film waterproofing agent, which were calcined at 300 to 1000 ° C, were rotated for 20 to 30 minutes, and then anion was left when the tagging remained. 0.5-3% by weight of any one selected from powder or tourmaline powder is mixed and rotated in the crotch. Method of producing a porous gemstone obtained by repeating the process of adding the promoter in an amount corresponding to 0.3 to 3% by weight of the mixture and rotating it for 30 minutes to 1 hour. delete In the pipes used as a drain pipe or a method for producing a porous raw stone mixture attached or bonded to the inside of the pipe portion, 75 to 85% by weight of selected porous gemstones of 5 to 40mm size and 14.5 to 22% by weight of film waterproofing agent, which were calcined at 300 to 1000 ° C, were rotated for 20 to 30 minutes, and then anion was left when the tagging remained. 0.5 to 3% by weight of any one selected from powder or tourmaline powder is mixed, it is put into the crotch and rotated, 100% by weight of the mixture of any one selected from the porous gemstone, coating waterproofing agent and anionic powder or tourmaline powder Based on the amount of the curing accelerator in the amount of 0.3 to 3% by weight and the porous gemstone prepared by repeating the process 2 to 5 times for 30 minutes to 1 hour repeated 65 to 75% by weight, and the size of the porous gemstone 15 to 20% by weight of the charcoal and 10 to 15% by weight of the resin binder provided in the same range is stirred in a stirrer. delete As a drain pipe formed by inserting and attaching a porous raw stone mixture therein, The porous gemstone mixture, 75 ~ 85% by weight of selected porous gemstones of 5 ~ 40mm size and 14.5 ~ 22% by weight of film waterproofing agent fired under the condition of 300 ~ 1000 ℃, rotated for 20 ~ 30 minutes and then rotated for 20 ~ 30 minutes. Or 0.5 to 3% by weight of any one selected from tourmaline powder to mix, put into the crotch and rotated to harden to 100% by weight of the mixture of any one selected from the porous gemstone, coating waterproofing agent and anionic powder or tourmaline powder Including the promoter in an amount corresponding to 0.3 to 3% by weight and having a porous gemstone 65-75% by weight repeated two to five times the process of rotating for 30 minutes to 1 hour, 65-75% of the porous gemstone 15 to 20% by weight of charcoal and 10 to 15% by weight of the resin binder provided in the same range as the size of the% is made by stirring in a stirrer, A drain pipe, characterized in that the porous raw stone mixture made as described above is formed by being introduced into and attached to the pipes or the pipe parts thereof before solidification. The method of claim 5, The pipe part is a drain pipe, characterized in that any one of a straight pipe, elbow pipe, tee pipe, trap is applied. delete