KR100819822B1 - Water proof construction method for tunnel using union water proof sheet - Google Patents

Water proof construction method for tunnel using union water proof sheet Download PDF

Info

Publication number
KR100819822B1
KR100819822B1 KR1020060101406A KR20060101406A KR100819822B1 KR 100819822 B1 KR100819822 B1 KR 100819822B1 KR 1020060101406 A KR1020060101406 A KR 1020060101406A KR 20060101406 A KR20060101406 A KR 20060101406A KR 100819822 B1 KR100819822 B1 KR 100819822B1
Authority
KR
South Korea
Prior art keywords
waterproof sheet
tunnel
construction surface
nonwoven fabric
composite waterproof
Prior art date
Application number
KR1020060101406A
Other languages
Korean (ko)
Inventor
김상용
Original Assignee
연일화섬공업(주)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 연일화섬공업(주) filed Critical 연일화섬공업(주)
Priority to KR1020060101406A priority Critical patent/KR100819822B1/en
Application granted granted Critical
Publication of KR100819822B1 publication Critical patent/KR100819822B1/en

Abstract

A waterproof construction method for a tunnel using composite waterproof sheets is provided to restrict cavity and crack of the tunnel after concrete lining construction by integrating waterproof sheets and reinforced nonwoven fabric with the shotcrete constructed surface in the tunnel. A waterproof nonwoven fabric(16) welded by point welding parts is formed at the other surface of a waterproof sheet(12) in which one side is formed with a reinforced nonwoven fabric(14) to prepare for composite waterproof sheets(10). The composite waterproof sheets are bonded on a shotcrete constructed surface(T) to face the composite waterproof sheets toward the shotcrete constructed surface. A waterproof coating film(20) is formed on the reinforced nonwoven fabric. The concrete linings are constructed below the composite waterproof sheets. Ends of the concrete linings are connected by extended connectors(220).

Description

복합 방수시트를 이용한 터널의 방수공법 {WATER PROOF CONSTRUCTION METHOD FOR TUNNEL USING UNION WATER PROOF SHEET}WATER PROOF CONSTRUCTION METHOD FOR TUNNEL USING UNION WATER PROOF SHEET}

도 1은 본 발명의 실시예에 따른 터널 방수공사용 복합 방수시트를 도시한 투영사시도.1 is a perspective perspective view showing a composite waterproof sheet for tunnel waterproofing construction according to an embodiment of the present invention.

도 2는 본 발명의 실시예에 따른 터널 방수공법을 설명하기 위한 터널 방수 구조물의 개략적인 단면도.Figure 2 is a schematic cross-sectional view of the tunnel waterproof structure for explaining the tunnel waterproofing method according to an embodiment of the present invention.

도 3은 도 2의 I-I를 따라 취해진 단면도.3 is a cross-sectional view taken along the line II of FIG. 2;

도 4는 본 발명의 실시예에 따른 터널 방수공법을 설명하기 위한 터널 방수 구조물의 부부 절단 사시도.Figure 4 is a perspective view of the couple cut of the tunnel waterproof structure for explaining the tunnel waterproofing method according to an embodiment of the present invention.

도 5는 본 발명의 다른 실시예에 따른 터널 방수공사용 복합 방수시트를 도시한 사시도.5 is a perspective view showing a composite waterproof sheet for tunnel waterproofing construction according to another embodiment of the present invention.

<도면의 주요부분에 대한 부호설명><Code Description of Main Parts of Drawing>

10: 복합 방수시트 12: 방수시트10: composite waterproof sheet 12: waterproof sheet

13: 점 융착부 14: 보강 부직포13: point welding part 14: reinforcing nonwoven fabric

16: 배수용 부직포 20: 방수도막16: drainage nonwoven fabric 20: waterproof coating

T: 숏크리트층 100: 방수층T: Shotcrete layer 100: Waterproofing layer

200: 콘크리트 라이닝 210, 220: 신축이음재200: concrete lining 210, 220: expansion joint material

230: 유리 섬유망230: glass fiber net

본 발명은 터널공사 분야에 관한 것으로서, 더욱 상세하게는, 복합 방수시트를 이용한 방수공사에서 방수시트로 인하여 발생될 수 있는 콘크리트 라이닝의 공극 및 균열방지를 위한 터널의 방수공법에 관한 것이다.The present invention relates to the field of tunnel construction, and more particularly, to a waterproof method of the tunnel for preventing voids and cracks in the concrete lining that can be generated by the waterproof sheet in the waterproof construction using the composite waterproof sheet.

일반적으로, 터널은 수송, 채광, 또는, 각종 설비(예컨대, 전력설비)의 지하 설치에 이용되는 것으로, 예를 들면, 철도 터널, 지하도 터널, 도로 터널, 채광 터널, 송수 또는 하수용 터널, 전력설비용 터널 등이 있다. 이러한 터널공사에 있어서, 터널 내 물(특히, 지하수)의 유입은 어떠한 형태의 터널 공사에서도 일어나는 것으로, 이러한 물 유입에 대처하기 위한 방수공사의 중요성은 예전부터 인식되어 왔다. 그리고, 터널공사에 따른 많은 하자 중에는 방수공사의 부실시공에 의한 하자가 상당히 많은 부분을 차지하는 것으로 알려져 있다.In general, tunnels are used for transportation, mining, or underground installation of various equipment (for example, electric power facilities), for example, railway tunnels, underpass tunnels, road tunnels, mining tunnels, water or sewage tunnels, and electric power. Tunnels for equipment; In such tunnel construction, the inflow of water (particularly groundwater) in the tunnel occurs in any form of tunnel construction, and the importance of waterproof construction to cope with the inflow of water has been recognized for a long time. In addition, among many defects caused by the tunnel construction, it is known that the defects caused by the subconstruction of the waterproof construction occupy a considerable part.

종래 터널 방수공법의 일예로, 숏크리트(shotcrete)가 타설된 굴착 터널에 콘크리트 라이닝을 시공함에 있어서, 먼저 타정못과 란델을 이용하여 배수 유도용 부직포를 터널 내면에 고정하고, 불투명의 ECB(Ethylene Copolymer Bitumen) 방수시트를 배수 유도용 부직포 상의 란델에 열 융착시키는 공법이 알려져 있다. 이때, 배수유도용 부직포와 위에 고정된 란델은 고온의 열풍(600℃)을 이용하여 란델 표면을 녹인 후 불 투명 ECB 방수시트를 열 융착 접합하는 과정으로 이루어진다. 이 때에 보이지도 않는 위치에서 오직 손의 감각으로 고온의 열풍으로 접합해야 되므로 란델의 아래에 접합하는 배수용 부직포의 탄화현상이 초래된다. 또한, 란델의 고정 위치가 방수시트의 폭 (2.0m)안으로 40∼60㎝ 정도의 손이 들어가는 위치에 임의로 선정하여 숏크리트 바닥면의 굴곡과는 상관없이 고정된다.As an example of the conventional tunnel waterproofing method, when constructing a concrete lining in an excavation tunnel in which shotcrete is poured, the nonwoven fabric for drainage induction is fixed to the inner surface of the tunnel using a tableting nail and a randel, and an opaque ethylene copolymer Bitumen) A technique for thermally bonding a waterproof sheet to a landel on a nonwoven for drainage induction is known. At this time, the induction non-woven fabric and the fixed Randell is made of a process of heat-sealing the opaque ECB waterproof sheet after melting the surface of the Randell using a high temperature hot air (600 ℃). At this time, invisible position should be bonded by hot hot air only by the sense of hand, which causes carbonization of the drainage nonwoven fabric bonded to the bottom of the landel. In addition, the fixed position of Landel is arbitrarily selected at a position of about 40 to 60 cm into the width (2.0 m) of the waterproof sheet and fixed regardless of the curvature of the shotcrete bottom.

그러나, 전술한 종래의 터널 방수공법은 터널 내의 여굴 또는 굴곡 부분에 의해 방수시트 등의 밀착시공이 어렵다는 문제점을 안고 있다. 특히, 이러한 밀착시공의 어려움은 다음 공정인 콘크리트 라이닝 시공 시에 하중에 의하여, 방수시트가 터널 천정 부근에서 란델의 표면으로부터 처지거나, 더 나아가서는, 그 처짐에 의해 방수시트가 찢겨지는 현상을 야기한다. 이러한 현상은, 터널 천정의 방수시트에 발생하는 과다한 집중하중에 의해 야기되는 것으로, 터널 천정 부근에 과다한 공극현상을 발생시키고, 이에 따라, 콘크리트 라이닝의 균열 및 누수를 일으킨다. 특히, 콘크리트 라이닝 후 발생된 공극은, 진동 또는 기온변화에 따른 수축/팽창의 반복에 따라 콘크리트 라이닝의 균열 및 탈락을 더욱 심화시키는 원인이 된다.However, the above-described conventional tunnel waterproofing method has a problem that it is difficult to close the waterproof sheet or the like due to the excavation or bent portion in the tunnel. In particular, this difficulty in close contact causes the waterproof sheet to sag from the surface of Randell near the ceiling of the tunnel, or, moreover, to tear the waterproof sheet by the load during the concrete lining construction, which is the next process. do. This phenomenon is caused by an excessive concentrated load occurring in the waterproof sheet of the tunnel ceiling, which causes excessive voids in the vicinity of the tunnel ceiling, thereby causing cracking and leakage of the concrete lining. In particular, the voids generated after the concrete lining is a cause to further deepen the crack and fall of the concrete lining in accordance with the repetition of the shrinkage / expansion caused by vibration or temperature change.

또한, 위 종래의 터널 방수공법은, 방수시트와 부직포 간의 열 융착 접합을 위한 열풍기의 과다한 열로 인해 부직포의 탄화 현상이 일어나고, 부직포 부착 공정과 방수시트의 열 융착 공정이 분리되어 진행됨에 따른 많은 시간적, 경제적인 손실을 야기하며, 방수시트가 불투명하여 방수시트와 란델 사이의 접착 여부를 육안으로 확인하기 어렵다는 등의 문제점을 안고 있다.In addition, in the conventional tunnel waterproofing method, carbonization of the nonwoven fabric occurs due to excessive heat of the heat blower for thermal fusion bonding between the waterproof sheet and the nonwoven fabric, and a lot of time is achieved by separating the nonwoven fabric attaching process and the thermal fusion bonding process of the waterproof sheet. It causes economic losses, and the waterproof sheet is opaque, so it is difficult to visually check whether the waterproof sheet is adhered to the Landel.

본 발명의 목적은, 굴곡 및/또는 여굴이 있는 터널 내 숏크리트 시공면에 대하여 방수시트, 배수용 부직포, 보강 부직포로 일체화된 복합 방수시트를 이용해 방수구조물을 형성하여, 그 다음 공정인 콘크리트 라이닝 시공 후에 공곡 및/또는 균열 억제가 용이한 터널 방수공법을 제공하는 것이다.An object of the present invention is to form a waterproof structure by using a composite waterproof sheet integrated with a waterproof sheet, a drainage nonwoven fabric, and a reinforcement nonwoven fabric for a shotcrete construction surface in a tunnel having a bend and / or a mine, and then a concrete lining construction process. It is then to provide a tunnel waterproofing method that is easy to suppress the hole and / or cracks.

본 발명의 다른 목적은, 굴곡 및/또는 여굴이 있는 터널 내 숏크리트 시공면에 대하여 방수시트와 보강 부직포로 일체화된 복합 방수시트를 이용해 방수구조물을 형성하여, 그 다음 공정인 콘크리트 라이닝 시공 후에 공곡 및/또는 균열 억제가 용이한 터널 방수공법을 제공하는 것이다.It is another object of the present invention to form a waterproof structure using a composite waterproof sheet integrated with a waterproof sheet and a reinforcing nonwoven fabric for a shotcrete construction surface in a tunnel having a bend and / or a mine, and then, after the concrete lining construction, / Or to provide a tunnel waterproofing method that is easy to suppress cracks.

본 발명의 일 측면에 따라 굴착터널 내 숏크리트 시공면에 시행되는 터널 방수공법이 제공된다. 이 터널 방수공법은, (a) 보강 부직포가 일측면에 형성된 방수시트의 타측면에 다수의 점 융착부에 의해 열 융착된 배수용 부직포를 형성하여 복합 방수시트를 준비하는 단계와; (b)　상기 배수용 부직포가 숏크리트 시공면을 향하도록 상기 복합 방수시트를 상기 숏크리트 시공면에 부착하는 단계와; (c) 상기 숏크리트 시공면에 부착된 상기 복합 방수시트의 상기 보강 부직포 상에 아스팔트를 주성분으로 하는 방수도막을 형성하는 단계와; (d) 상기 방수도막이 형성된 상기 복합 방수시트 아래로 복수의 콘크리트 라이닝을 시공하는 단계를; 포함한다.According to an aspect of the present invention there is provided a tunnel waterproofing method that is carried out on the shotcrete construction surface in the excavation tunnel. The tunnel waterproofing method includes the steps of: (a) preparing a composite waterproof sheet by forming a nonwoven fabric for drainage heat-sealed by a plurality of spot welding parts on the other side of the waterproof sheet on which the reinforced nonwoven fabric is formed on one side; (b) attaching the composite waterproof sheet to the shotcrete construction surface such that the drainage nonwoven fabric faces the shotcrete construction surface; (c) forming a waterproof coating film mainly composed of asphalt on the reinforcing nonwoven fabric of the composite waterproof sheet attached to the shotcrete construction surface; (d) constructing a plurality of concrete linings under the composite waterproof sheet having the waterproof coating film formed thereon; Include.

본 발명의 다른 측면에 따른 터널 방수 공법은, (a) 보강 부직포 및 그 보강 부직포의 일측면에 접합되어 형성된 방수시트로 이루어진 복합 방수시트를 준비하는 단계와; (b) 상기 방수시트가 숏크리트 시공면을 향하도록 상기 복합 방수시트 를 상기 숏크리트 시공면에 부착하는 단계와; (c) 상기 숏크리트 시공면에 부착된 상기 복합 방수시트의 상기 보강 부직포 상에 아스팔트를 주성분으로 하는 방수도막을 형성하는 단계와; (d) 상기 방수도막이 형성된 상기 복합 방수시트 아래로 복수의 콘크리트 라이닝을 시공하는 단계를; 포함한다. Tunnel waterproofing method according to another aspect of the present invention, (a) preparing a composite waterproof sheet consisting of a reinforcing nonwoven fabric and a waterproof sheet formed by bonding to one side of the reinforcing nonwoven fabric; (b) attaching the composite waterproof sheet to the shotcrete construction surface such that the waterproof sheet faces the shotcrete construction surface; (c) forming a waterproof coating film mainly composed of asphalt on the reinforcing nonwoven fabric of the composite waterproof sheet attached to the shotcrete construction surface; (d) constructing a plurality of concrete linings under the composite waterproof sheet having the waterproof coating film formed thereon; Include.

바람직하게는, 상기 (b) 단계는 타정못을 상기 복합 방수시트에 타정하여 이루어지되, 상기 타정못의 타정 위치는 숏크리트 시공면 표면의 가장 낮은 골 부분으로 결정된다. 또한, 상기 타정못에 끼워진 패킹재가 상기 타정못 주위에 생긴 틈새를 패킹하는 것이 바람직하다. 바람직하게는, 상기 방수도막은 아스팔트를 주성분으로 하여 경화제와 접착제가 혼합되어 이루어진다.Preferably, the step (b) is made by tableting the tablet nail to the composite waterproof sheet, the tableting position of the tableting nail is determined as the lowest bone portion of the shotcrete surface. In addition, it is preferable that the packing material fitted to the tableting nail packs the gap formed around the tableting nail. Preferably, the waterproof coating is made by mixing a curing agent and an adhesive based on asphalt.

바람직하게는, 상기 (d) 단계는 서로 이웃하는 콘크리트 라이닝의 단부를 신축이음재로 이음하는 것을 포함하며, 상기 콘크리트 라이닝의 터널형 표면에 균열 억제용 유리 섬유망을 터널 형태로 제공하여 마무리하는 것이 바람직하다.Preferably, the step (d) includes joining the ends of the concrete linings adjacent to each other with expansion joint material, and finishing by providing a glass fiber net for preventing cracks in the tunnel form on the tunnel-like surface of the concrete lining desirable.

본 발명의 또 다른 측면에 따라, 굴착터널 내 숏크리트 시공면에 부착되는 복합 방수시트가 제공된다. 상기 복합 방수시트는, 수지로 형성된 방수시트와; 방수도막과의 접합강도 향상을 위해, 상기 방수시트의 일측면에 형성되는 보강 부직포와; 다수의 점 융착부에 의해 상기 방수시트의 타측면에 열 융착되는 배수용 부직포를; 포함한다. 이때, 상기 배수용 부직포의 없이 보강 부직포와 방수시트가 서로 접합되어 형성된 복합 방수시트의 이용도 가능하다.According to another aspect of the invention, there is provided a composite waterproof sheet attached to the shotcrete construction surface in the excavation tunnel. The composite waterproof sheet, the waterproof sheet formed of a resin; A reinforcing nonwoven fabric formed on one side of the waterproof sheet to improve bonding strength with the waterproof coating film; A non-woven fabric for drainage, which is thermally fused to the other side of the waterproof sheet by a plurality of spot welding parts; Include. At this time, it is also possible to use a composite waterproof sheet formed by bonding the reinforcement nonwoven fabric and the waterproof sheet without the drainage nonwoven fabric.

본 발명의 다른 목적 및 이점은 이하 실시예의 설명으로부터 보다 명확하게 이해되어질 것이다. Other objects and advantages of the invention will be more clearly understood from the following description of the examples.

<실시예 : 터널 방수시공><Example: Tunnel waterproof construction>

도 1은 본 발명의 실시예에 따라 터널 방수공법에 이용되는 복합 방수시트를 도시한 투영사시도이고, 도 2는 본 발명의 실시예에 의해 시공된 터널 내 방수구조물을 도시한 개략적인 단면도이고, 도 3은 도 2의 I-I를 따라 취해진 단면도이며, 도 4는 터널의 주요부분을 보이기 위해 도시된 부분 절단사시도이다.1 is a perspective view showing a composite waterproof sheet used in the tunnel waterproofing method according to an embodiment of the present invention, Figure 2 is a schematic cross-sectional view showing a waterproof structure in the tunnel constructed by the embodiment of the present invention, 3 is a cross-sectional view taken along II of FIG. 2, and FIG. 4 is a partial cutaway perspective view to show the main part of the tunnel.

도 1을 참조하면, 본 발명의 실시예에 따라, 굴착터널 내 숏크리트 시공면에 부착되는 복합 방수시트가 제공된다. 상기 복합 방수시트(10)는, 수지로 형성된 방수시트(12)와, 방수도막과의 접합강도 향상을 위해, 상기 방수시트(10)의 일측면에 형성되는 보강 부직포(14)와. 다수의 점 융착부(13)에 의해 상기 방수시트(12)의 타측면에 열 융착되는 배수용 부직포(16)를 포함한다. 본 발명의 실시예에 따른 터널 방수시공 방법은 위와 같은 복합 방수시트(10)을 이용해 시공된다.Referring to Figure 1, according to an embodiment of the present invention, there is provided a composite waterproof sheet attached to the shotcrete construction surface in the excavation tunnel. The composite waterproof sheet 10, and the waterproof sheet 12 formed of a resin, reinforcing non-woven fabric (14) is formed on one side of the waterproof sheet 10 to improve the bonding strength of the waterproof coating film. It includes a non-woven fabric 16 for drainage heat-sealed to the other side of the waterproof sheet 12 by a plurality of spot fusion portion (13). Tunnel waterproof construction method according to an embodiment of the present invention is constructed using the composite waterproof sheet 10 as described above.

도 2 내지 도 4에 도시된 바와 같이, 본 실시예의 방수구조물은 터널 내 숏크리트층(T)으로부터 방수층(100)과 콘크리트 라이닝(200) 등을 연속적으로 형성함으로써 얻어진다. As shown in Figures 2 to 4, the waterproof structure of the present embodiment is obtained by continuously forming the waterproof layer 100, concrete lining 200 and the like from the shotcrete layer T in the tunnel.

도 3 및 도 4에 잘 도시된 바와 같이, 상기 방수층(100)의 형성은 숏크리트층(T)의 시공면을 정리한 후 그 숏크리트 시공면에 대하여 복합 방수시트(10)를 부착하고, 그 부착된 복합 방수시트(10)에 방수도막(20)을 형성하는 순서로 이루어진다. 또한, 상기 방수층(100)이 형성되면 그 아래에 콘크리트 라이닝(200)이 시공 형성된다.3 and 4, the waterproof layer 100 is formed by arranging the construction surface of the shotcrete layer T, and then attaching the composite waterproof sheet 10 to the shotcrete construction surface, and attaching the composite surface. The composite waterproof sheet 10 is formed in the order of forming a waterproof coating film (20). In addition, when the waterproof layer 100 is formed, a concrete lining 200 is formed thereunder.

상기 복합 방수시트(10)는 자체의 배수용 부직포(16)가 숏크리트층(T)을 향 하도록 숏크리트 시공면에 부착된다. 이때, 복합 방수시트(10)의 부착에는 타정못(32)과, 그 타정못(32)에 끼워진 채 타정못(32)의 타정 중 생긴 복합 방수시트(10) 상의 틈새 또는 째짐을 패킹하는 패킹재(34)를 포함하는 패스너 장치(30)가 이용된다. 또한, 상기 패스너 장치(30)는 타정못(32)과 상기 패킹재(34) 외에 패킹재(34)를 가압하는 와셔(36) 등을 더 포함할 수 있다. The composite waterproof sheet 10 is attached to the shotcrete construction surface so that its drainage nonwoven fabric 16 faces the shotcrete layer (T). At this time, the packing for packing a gap or crushing on the tableting nail 32 and the composite waterproof sheet 10 formed during tableting of the tableting nail 32 while being attached to the tableting nail 32 to attach the composite waterproof sheet 10. Fastener device 30 comprising ash 34 is used. In addition, the fastener device 30 may further include a washer 36 for pressing the packing material 34 in addition to the tableting nail 32 and the packing material 34.

그리고, 상기 타정못(32)의 타정 위치는 숏크리트 시공면 상의 함몰 부분, 즉, 골 부분(V)으로 정해지며, 이에 의해, 복합 방수시트(10)의 숏크리트 시공면에 대한 밀착시공이 가능해진다. 그리고, 상기 복합 방수시트(10)는 열 융착된 배수용 부직포(16)를 갖되 그 열 융착을 위해 종, 횡 양방향으로의 방수시트(12)의 신장률 저하가 거의 없는 점 융착부(13)를 이용한다는 점에서 숏크리트 시공면에 대하여 밀착 시공이 가능하여 콘크리트 라이닝 시공 후에 공극 발생을 최소화 할 수 있다. 더 나아가, 복합 방수시트(10) 타측면의 보강 부직포(14) 가 방수시트(12)의 신장율에 영향을 거의 미치지 않는 정도의 자체 두께 및 열 융착 두께를 갖는다는 점에서 위의 부착 시공 시 밀착시공이 저해되는 등의 문제점을 거의 발생시키지 않는다.In addition, the tableting position of the tableting nail 32 is determined to be a recessed portion on the shotcrete construction surface, that is, the bone portion (V), thereby making it possible to adhere closely to the shotcrete construction surface of the composite waterproof sheet 10. . In addition, the composite waterproof sheet 10 has a heat-sealed nonwoven fabric 16 for drainage, but the thermal bonding of the point fusion unit 13 with little decrease in elongation of the waterproof sheet 12 in both longitudinal and transverse directions for thermal fusion. It can be used in close contact with the shotcrete construction in that it can minimize the generation of voids after the construction of concrete lining. Furthermore, the reinforcing nonwoven fabric 14 on the other side of the composite waterproof sheet 10 has its own thickness and thermal fusion thickness that hardly affects the elongation rate of the waterproof sheet 12, and thus is closely adhered to the above installation. It hardly causes problems such as impeding construction.

복합 방수시트(10)가 숏크리트 시공면에 부착된 후, 상기 보강 부직포(14) 상에는 아스팔트재가 스프레이되어 일정 두께의 방수도막(20)이 형성된다. 이때, 상기 아스팔트재는 방수 신뢰성이 탁월한 일반 아스팔트 재료에 경화를 촉진시키는 경화재와 보강 부직포와의 접착성 향상을 위한 접착제가 혼합된 것을 사용한다. 그리고, 상기 보강 부직포(14)는 상기 방수도막(20)에 대한 접합 강도 향상을 위한 것이며, 그것의 두께가 접합 강도에 큰 영향을 미치지 않으므로, 복합 방수시트(10)의 신장율 개선을 위해 가능한 한 얇게 형성되는 것이 바람직하다.After the composite waterproof sheet 10 is attached to the shotcrete construction surface, asphalt material is sprayed on the reinforcing nonwoven fabric 14 to form a waterproof coating 20 having a predetermined thickness. In this case, the asphalt material is a mixture of an adhesive for improving the adhesion between the hardening material and the reinforcing nonwoven fabric to promote the hardening to the general asphalt material excellent in waterproof reliability. In addition, the reinforcing nonwoven fabric 14 is for improving the bonding strength with respect to the waterproofing film 20, and since its thickness does not significantly affect the bonding strength, it is possible to improve the elongation of the composite waterproof sheet 10 as much as possible. It is preferable to form thin.

위와 같이, 타정못(32)에 의해 생긴 복합 방수시트(10)의 틈새 또는 째짐이 타정못(32) 상의 패킹재(34)에 의해 1차로 패킹되고, 그 위의 방수도막(20)이 타정못(32) 등을 포함한 패스너 장치(30)를 완전히 덮으므로, 복합 방수시트(14)에서 의도치 않은 누수 등의 위험성을 원천적으로 차단할 수 있다. 그리고, 상기 방수도막(20)은 이하 설명되는 콘크리트 라이닝 시공시에 발생하는 공극을 최소화시켜 콘크리트 라이닝의 균열 발생과 뒷 채움 콘크리트를 크게 줄여주는 역할을 한다. As above, the gap or slit of the composite waterproof sheet 10 produced by the tableting nail 32 is primarily packed by the packing material 34 on the tableting nail 32, and the waterproofing film 20 thereon is tableted. Since the fastener device 30 including the nails 32 and the like is completely covered, the composite waterproof sheet 14 can fundamentally block the risk of accidental leakage or the like. In addition, the waterproof coating 20 serves to greatly reduce the occurrence of cracks and backfill concrete of the concrete lining by minimizing voids generated during the construction of the concrete lining described below.

위의 모든 방수층(100) 형성 공정이 완료되면, 그 아래로 복수의 콘크리트 라이닝(200)이 터널형으로 시공되는 공정이 수행된다. 복수의 콘크리트 라이닝(200)은, 터널 길이방향으로 복수개로 배열되고, 터널 천정을 중심으로 좌, 우 한 벌로 대칭 배열된다.When all of the above waterproofing layer 100 forming process is completed, a process of constructing a plurality of concrete lining 200 in a tunnel form below it is performed. The plurality of concrete linings 200 are arranged in plural in the longitudinal direction of the tunnel and symmetrically arranged in a left and right suit around the tunnel ceiling.

특히 상기 콘크리트 라이닝(200)들 각각은 이웃하는 콘크리트 라이닝(200)과 신축이음재(210, 220)에 의해 신축 이음 되어, 콘크리트 라이닝(200)의 수축/팽창에 대하여 균열이 억제되는 구성을 갖는다. 보다 구체적으로, 상기 신축이음재(210, 220)는, 터널 천정에서 서로 대칭하면서 이웃하는 콘크리트 라이닝(200)들의 상단부를 이음하는 제 1 신축이음재(210; 도 2에 도시됨)와, 터널 측면에서 길이방향으로 이웃하는 콘크리트 라이닝(20)의 측단부를 이음하는 제 2 신축이음재(220; 도 5에 도시됨)를 포함한다. 따라서, 제 1 및 제 2 신축이음재(210, 220)에 의해, 콘크리트 라이닝(200)의 균열을 종방향 및 횡방향으로 억제될 수 있다.In particular, each of the concrete lining 200 is stretched by the neighboring concrete lining 200 and the expansion joint (210, 220) has a configuration that the crack is suppressed against the shrinkage / expansion of the concrete lining (200). More specifically, the expansion joints (210, 220), the first expansion joint 210 (shown in Figure 2) and the tunnel side symmetrical to each other in the tunnel ceiling to join the upper end of the adjacent concrete linings 200, And a second expansion joint material 220 (shown in FIG. 5) for joining the side ends of the concrete lining 20 adjacent in the longitudinal direction. Therefore, the cracks in the concrete lining 200 can be suppressed in the longitudinal and transverse directions by the first and second expansion joint members 210 and 220.

추가로, 본 발명의 실시예에 따른 방수공법은 콘크리트 라이닝(200)의 시공 후 생길 수 있는 표면 균열을 억제하기 위한 또 하나의 구성으로 일정 강도를 갖는 유리 섬유망(230)을 터널 형태로 상기 콘크리트 라이닝(200)의 표면에 함침하여 형성하는 구성을 추가로 포함한다. 이 유리 섬유망(230)은 일정한 강도를 갖추며 점착테이프에 의해 소정 형틀에 부착 시공된 상태로 상기 콘크리트 라이닝(200) 표면에 제공되며, 이 유리 섬유망(230)에 의해 콘크리트 라이닝(200)의 표면 균열이 더욱 억제될 수 있고 표면 강도가 향상된다.In addition, the waterproof method according to an embodiment of the present invention is a tunnel to the glass fiber net 230 having a certain strength as another configuration for suppressing the surface cracks that may occur after the construction of the concrete lining 200 It further comprises a configuration formed by impregnating the surface of the concrete lining (200). The glass fiber net 230 has a certain strength and is provided on the surface of the concrete lining 200 in a state of being attached to a predetermined mold by adhesive tape, and the glass fiber net 230 of the concrete lining 200 Surface cracking can be further suppressed and surface strength is improved.

본 발명의 다른 실시예에 따라, 도 5에 도시된 것과 같은 복합 방수시트(10)가 이용될 수도 있다. 도 5를 참조하면, 상기 복합 방수시트(10)는 앞선 실시예의 복합 방수시트와 달리 배수용 부직포가 생략된 방수시트(12)와 이에 접합된 보강 부직포(14)로 이루어진다.According to another embodiment of the present invention, a composite waterproof sheet 10 as shown in FIG. 5 may be used. Referring to FIG. 5, the composite waterproof sheet 10 includes a waterproof sheet 12 and a reinforcing nonwoven fabric 14 bonded thereto, in which the nonwoven fabric for drainage is omitted, unlike the composite waterproof sheet of the previous embodiment.

본 실시예에 따른 복합 방수시트(10)를 굴착 터널 내 방수시공에 이용함에 있어서, 배수용 부직포의 생략에 따라, 방수시트(12)가 숏크리트층(T)를 향한 채로 그 숏크리트 시공면에 부착된다. 그리고, 상기 보강 부직포(14) 상에는 아스팔트재가 스프레이되어 일정 두께의 방수도막이 형성되며, 이는 앞선 실시예와 같다. 그리고, 위 배수용 부직포의 생략을 제외한 나머지 사항은 앞선 실시예의 설명과 같으므로 중복을 피하기 위해 그 설명은 생략한다.In using the composite waterproof sheet 10 according to the present embodiment for waterproofing in an excavation tunnel, according to the omission of the drainage nonwoven fabric, the waterproof sheet 12 is attached to the shotcrete construction surface with the waterproof sheet 12 facing the shotcrete layer T. do. In addition, the asphalt material is sprayed on the reinforcing nonwoven fabric 14 to form a waterproof coating film having a predetermined thickness, which is the same as the previous embodiment. In addition, since the remaining matters except for omitting the drainage nonwoven fabric are the same as those of the foregoing embodiment, the description thereof is omitted to avoid duplication.

본 발명의 실시예들에 따르면, 굴곡 및/또는 여굴이 많은 터널 내 숏크리트 시공면에 대하여 복합 방수시트의 밀착시공이 가능하고 또한 복합 방수시트에 일체 화된 보강 부직포에 의해 예컨대, 아스팔트재로 이루어진 방수 도막을 용이하게 형성할 수 있어, 콘크리트 라이닝 시공 후 야기되는 공극 및 균열 발생 등과 같은 여러 문제점을 손쉽게 억제할 수 있는 효과를 갖는다. 또한, 본 발명의 실시예들에 따르면, 콘크리트 라이닝 시공에 채용되는 신축이음재 및/또는 유리 섬유망 설치 구조에 따라, 더욱 더 콘크리트 라이닝 시공 후의 공극 및/또는 균열발생을 억제하여 줄 수 있다. According to the embodiments of the present invention, the composite waterproof sheet can be closely adhered to the shotcrete construction surface in the tunnel with a lot of flexion and / or excavation, and the waterproofing made of, for example, asphalt material by the reinforcing nonwoven fabric integrated in the composite waterproof sheet. Since the coating film can be easily formed, various problems such as voids and cracks caused after the construction of the concrete lining can be easily suppressed. In addition, according to the embodiments of the present invention, according to the expansion joint material and / or glass fiber network installation structure employed in the concrete lining construction, it is possible to further suppress the generation of voids and / or cracks after the concrete lining construction.

Claims (7)

굴착터널 내 숏크리트 시공면에 시행되는 터널 방수공법에 있어서,In the tunnel waterproofing method applied to the shotcrete construction surface in the excavation tunnel, (a) 보강 부직포가 일측면에 형성된 방수시트의 타측면에 다수의 점 융착부에 의해 열 융착된 배수용 부직포를 형성하여 복합 방수시트를 준비하는 단계와;(A) preparing a composite waterproof sheet by forming a non-woven fabric for drainage heat-sealed by a plurality of point welds on the other side of the waterproof sheet formed on one side of the reinforced non-woven fabric; (b) 상기 배수용 부직포가 숏크리트 시공면을 향하도록 상기 복합 방수시트를 상기 숏크리트 시공면에 부착하는 단계와;(b) attaching the composite waterproof sheet to the shotcrete construction surface such that the drainage nonwoven fabric faces the shotcrete construction surface; (c) 상기 숏크리트 시공면에 부착된 상기 복합 방수시트의 상기 보강 부직포 상에 아스팔트를 주성분으로 하는 방수도막을 형성하는 단계와;(c) forming a waterproof coating film mainly composed of asphalt on the reinforcing nonwoven fabric of the composite waterproof sheet attached to the shotcrete construction surface; (d) 상기 방수도막이 형성된 상기 복합 방수시트 아래로 복수의 콘크리트 라이닝을 시공하는 단계를 포함하되,(d) constructing a plurality of concrete linings under the composite waterproof sheet having the waterproof coating formed thereon; 상기 (d) 단계는 서로 이웃하는 콘크리트 라이닝의 단부를 신축이음재로 이음하는 것을 포함하는 것을 특징으로 하는 터널 방수공법. The step (d) is a tunnel waterproofing method, characterized in that it comprises the joint of the end of the adjacent concrete lining with expansion joint material. 굴착터널 내 숏크리트 시공면에 시행되는 터널 방수공법에 있어서,In the tunnel waterproofing method applied to the shotcrete construction surface in the excavation tunnel, (a) 보강 부직포 및 그 보강 부직포의 일측면에 접합되어 형성된 방수시트로 이루어진 복합 방수시트를 준비하는 단계와;(a) preparing a composite waterproof sheet consisting of a reinforced nonwoven fabric and a waterproof sheet bonded to one side of the reinforced nonwoven fabric; (b) 상기 방수시트가 숏크리트 시공면을 향하도록 상기 복합 방수시트를 상기 숏크리트 시공면에 부착하는 단계와;(b) attaching the composite waterproof sheet to the shotcrete construction surface such that the waterproof sheet faces the shotcrete construction surface; (c) 상기 숏크리트 시공면에 부착된 상기 복합 방수시트의 상기 보강 부직포 상에 아스팔트를 주성분으로 하는 방수도막을 형성하는 단계와;(c) forming a waterproof coating film mainly composed of asphalt on the reinforcing nonwoven fabric of the composite waterproof sheet attached to the shotcrete construction surface; (d) 상기 방수도막이 형성된 상기 복합 방수시트 아래로 복수의 콘크리트 라이닝을 시공하는 단계를; 포함하되,(d) constructing a plurality of concrete linings under the composite waterproof sheet having the waterproof coating film formed thereon; Including, 상기 (d) 단계는 서로 이웃하는 콘크리트 라이닝의 단부를 신축이음재로 이음하는 것을 포함하는 것을 특징으로 하는 터널 방수공법. The step (d) is a tunnel waterproofing method, characterized in that it comprises the joint of the end of the adjacent concrete lining with expansion joint material. 청구항 1 또는 청구항 2에 있어서, 상기 (b) 단계는 타정못을 상기 복합 방수시트에 타정하여 이루어지되, 상기 타정못의 타정 위치는 상기 숏크리트의 시공면의 골부분에 대응되도록 결정되는 것을 특징으로 하는 터널 방수공법.The method according to claim 1 or 2, wherein the step (b) is made by tableting nails to the composite waterproof sheet, the tableting position of the tableting nail is characterized in that it is determined to correspond to the bone portion of the construction surface of the shotcrete Tunnel waterproofing. 청구항 3에 있어서, 상기 타정못에 끼워진 패킹재가 상기 타정못 주위에 생긴 틈새를 패킹하는 것을 특징으로 하는 터널 방수공법.The tunnel waterproofing method according to claim 3, wherein the packing material inserted into the tableting nail packs a gap formed around the tableting nail. 청구항 1에 있어서, 상기 방수도막은 아스팔트를 주성분으로 하여 경화제와 접착제가 혼합되어 이루어진 것을 특징으로 하는 터널 방수공법. The method of claim 1, wherein the waterproof coating is a tunnel waterproofing method, characterized in that the hardener and the adhesive is mixed with asphalt as a main component. 굴착터널 내 숏크리트 시공면에 시행되는 터널 방수공법에 있어서,In the tunnel waterproofing method applied to the shotcrete construction surface in the excavation tunnel, (a) 보강 부직포가 일측면에 형성된 방수시트의 타측면에 다수의 점 융착부에 의해 열 융착된 배수용 부직포를 형성하여 복합 방수시트를 준비하는 단계와;(A) preparing a composite waterproof sheet by forming a non-woven fabric for drainage heat-sealed by a plurality of point welds on the other side of the waterproof sheet formed on one side of the reinforced non-woven fabric; (b) 상기 배수용 부직포가 숏크리트 시공면을 향하도록 상기 복합 방수시트를 상기 숏크리트 시공면에 부착하는 단계와;(b) attaching the composite waterproof sheet to the shotcrete construction surface such that the drainage nonwoven fabric faces the shotcrete construction surface; (c) 상기 숏크리트 시공면에 부착된 상기 복합 방수시트의 상기 보강 부직포 상에 아스팔트를 주성분으로 하는 방수도막을 형성하는 단계와;(c) forming a waterproof coating film mainly composed of asphalt on the reinforcing nonwoven fabric of the composite waterproof sheet attached to the shotcrete construction surface; (d) 상기 방수도막이 형성된 상기 복합 방수시트 아래로 복수의 콘크리트 라이닝을 시공하는 단계를 포함하되,(d) constructing a plurality of concrete linings under the composite waterproof sheet having the waterproof coating formed thereon; 상기 콘크리트 라이닝의 터널형 표면에 균열 억제용 유리 섬유망을 터널 형태로 제공하여 마무리하는 것을 특징으로 하는 터널 방수공법. Tunnel waterproofing method characterized in that to finish by providing a glass fiber net for crack suppression in the tunnel form on the tunnel-like surface of the concrete lining. 굴착터널 내 숏크리트 시공면에 시행되는 터널 방수공법에 있어서,In the tunnel waterproofing method applied to the shotcrete construction surface in the excavation tunnel, (a) 보강 부직포 및 그 보강 부직포의 일측면에 접합되어 형성된 방수시트로 이루어진 복합 방수시트를 준비하는 단계와;(a) preparing a composite waterproof sheet consisting of a reinforced nonwoven fabric and a waterproof sheet bonded to one side of the reinforced nonwoven fabric; (b) 상기 방수시트가 숏크리트 시공면을 향하도록 상기 복합 방수시트를 상기 숏크리트 시공면에 부착하는 단계와;(b) attaching the composite waterproof sheet to the shotcrete construction surface such that the waterproof sheet faces the shotcrete construction surface; (c) 상기 숏크리트 시공면에 부착된 상기 복합 방수시트의 상기 보강 부직포 상에 아스팔트를 주성분으로 하는 방수도막을 형성하는 단계와;(c) forming a waterproof coating film mainly composed of asphalt on the reinforcing nonwoven fabric of the composite waterproof sheet attached to the shotcrete construction surface; (d) 상기 방수도막이 형성된 상기 복합 방수시트 아래로 복수의 콘크리트 라이닝을 시공하는 단계를; 포함하되,(d) constructing a plurality of concrete linings under the composite waterproof sheet having the waterproof coating film formed thereon; Including, 상기 콘크리트 라이닝의 터널형 표면에 균열 억제용 유리 섬유망을 터널 형태로 제공하여 마무리하는 것을 특징으로 하는 터널 방수공법.Tunnel waterproofing method characterized in that to finish by providing a glass fiber net for crack suppression in the tunnel form on the tunnel-like surface of the concrete lining.
KR1020060101406A 2006-10-18 2006-10-18 Water proof construction method for tunnel using union water proof sheet KR100819822B1 (en)