KR100771197B1 - Waterproofing sheet, waterproofing process and waterproofing structure of the same - Google Patents

Waterproofing sheet, waterproofing process and waterproofing structure of the same Download PDF

Info

Publication number
KR100771197B1
KR100771197B1 KR1020060037619A KR20060037619A KR100771197B1 KR 100771197 B1 KR100771197 B1 KR 100771197B1 KR 1020060037619 A KR1020060037619 A KR 1020060037619A KR 20060037619 A KR20060037619 A KR 20060037619A KR 100771197 B1 KR100771197 B1 KR 100771197B1
Authority
KR
South Korea
Prior art keywords
layer
waterproof
waterproofing
asphalt
sheet
Prior art date
Application number
KR1020060037619A
Other languages
Korean (ko)
Inventor
정인규
Original Assignee
주식회사 대화 정밀화학
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 대화 정밀화학 filed Critical 주식회사 대화 정밀화학
Priority to KR1020060037619A priority Critical patent/KR100771197B1/en
Application granted granted Critical
Publication of KR100771197B1 publication Critical patent/KR100771197B1/en

Abstract

A waterproofing sheet, a waterproofing method, and a waterproofing structure are provided to allow construction on a wet surface by coating a water-soluble epoxy resin mortar. In a waterproofing method, a water proofing sheet(10) includes a reinforcing fabric layer(2), an asphalt layer(4), and a bonding layer(6). The asphalt layer is formed by coating asphalt at least on one side of the reinforcing fabric layer and is submerged in the reinforcing fabric layer. The bonding layer is formed by attaching silica to the asphalt layer. The asphalt includes asphalt, styrenebutadiene rubber, acrylic, and impurities. The waterproofing layer forms a congealed waterproofing layer by mixing inorganic cement and a polymer distributor.

Description

방수 시트, 방수 공법 및 방수 구조 {waterproofing sheet, waterproofing process and waterproofing structure of the same}Waterproofing sheet, waterproofing process and waterproofing structure of the same}

도1은 본 발명의 일 실시예에 따른 방수 시트의 단면도이다.1 is a cross-sectional view of a waterproof sheet according to an embodiment of the present invention.

도2는 본 발명의 제1 실시예에 따른 방수 공법의 공정 및 방수 구조의 단면도이다.2 is a cross-sectional view of the process and waterproof structure of the waterproof method according to the first embodiment of the present invention.

도3은 방수 시트 이음부의 단면도이다.3 is a cross-sectional view of the waterproof sheet joint portion.

도4는 본 발명의 제2 실시예에 따른 방수 공법의 공정 및 방수 구조의 단면도이다.4 is a cross-sectional view of a process and waterproof structure of the waterproof method according to the second embodiment of the present invention.

<도면의 주요 부분에 대한 부호의 설명><Explanation of symbols for main parts of the drawings>

2 : 보강포층 4 : 아스팔트층2: reinforcing cloth layer 4: asphalt layer

6 : 접착층 8 : 바탕면6: adhesive layer 8: base surface

10 : 방수 시트 10a, 10b : 제1, 제2 방수 시트10: waterproof sheet 10a, 10b: first, second waterproof sheet

11 : 프라이머층 12 : 도막 방수층11: primer layer 12: coating film waterproofing layer

12a, 12b : 제1, 제2 도막 방수층 13 : 시트 방수층12a, 12b: 1st, 2nd coating film waterproofing layer 13: sheet waterproofing layer

21 : 방수/방식층 21a : 방수층21: waterproof / anticorrosive layer 21a: waterproof layer

21b : 방식층21b: anticorrosive layer

본 발명은 방수 시트, 방수 공법 및 방수 구조에 관한 것으로서, 보다 상세하게는 시트 방수의 장점과 도막 방수의 장점을 가지게 하는 방수 시트, 이를 사용하는 방수 공법 및 이 공법으로 형성되는 방수 구조에 관한 것이다.The present invention relates to a waterproof sheet, a waterproof method and a waterproof structure, and more particularly, to a waterproof sheet having advantages of waterproofing a sheet and waterproofing a coating film, a waterproof method using the same, and a waterproof structure formed by the method. .

일반적으로 건축물의 옥상이나 지하 주차장 상판 및 교량 상판 등에는 각 구조물의 부식 및 파손을 방지하기 위하여, 방수 공법이 적용되고 있다. 이 방수 공법은 크게 분류되는 시트(sheet) 방수 공법과 도막 방수 공법을 포함한다.In general, in order to prevent corrosion and damage of each structure, the waterproofing method is applied to the roof of the building, the roof of the underground parking lot, and the bridge deck. This waterproofing method includes sheet waterproofing and coating film waterproofing.

시트 방수 공법은 시트를 사용하며, 이 시트는 도막 방수에 비하여, 방수 성능, 구조물의 거동 대응성, 크랙(crack) 추종성 및 외부 충격에 대하여 우수한 대응력을 가진다.The sheet waterproofing method uses a sheet, which has superior resistance to waterproofing, structure behavior response, crack tracking and external impact, compared to waterproofing of the coating film.

또한, 도막 방수 공법은 현장에서 도막을 형성하여 시트 방수에 비하여, 이음매가 없는 구조를 가진다.In addition, the coating film waterproofing method forms a coating film in the field and has a seamless structure as compared with sheet waterproofing.

그러나, 시트 방수 공법은 누수로 인한 하자 발생시 원인 장소를 찾기 어려우므로 피방수 구조물 전체에 대한 방수 공사를 다시 하여야 하는 단점을 가진다.However, the sheet waterproofing method has a disadvantage in that it is difficult to find the place of the cause when a defect occurs due to leakage, so that the waterproof construction of the entire waterproof structure is performed again.

또한, 도막 방수 공법은 사용되는 방수재의 절대량을 증가시키지 않는 한 피방수 구조물 전체에 걸쳐 일정 두께 이상의 방수 도막을 형성하기 어려운 단점을 가진다.In addition, the coating film waterproofing method has a disadvantage in that it is difficult to form a waterproof coating film of a predetermined thickness or more over the whole waterproof structure unless the absolute amount of the waterproofing material used is increased.

특히, 두 방수 공법을 큰 하중이 작용하는 교량의 상판 방수에 적용하는 경우, 두 방수 공법에 의하여 형성된 방수 구조는 방수 시트 및 방수 도막의 내구성 부족으로 인하여, 방수 구조가 쉽게 파괴되는 단점을 가진다.In particular, when the two waterproofing methods are applied to the waterproofing of the upper plate of the bridge under a large load, the waterproofing structure formed by the two waterproofing methods has a disadvantage in that the waterproofing structure is easily destroyed due to the lack of durability of the waterproofing sheet and the waterproofing coating film.

본 발명은 상기한 바와 같은 단점들을 해결하기 위하여 창안된 것으로, 그 목적은 시트 방수의 장점과 도막 방수의 장점을 겸비하는 방수 시트, 방수 공법 및 방수 구조를 제공하는 데 있다.The present invention was devised to solve the above disadvantages, and an object thereof is to provide a waterproof sheet, a waterproofing method, and a waterproof structure that combine the advantages of sheet waterproofing and coating film waterproofing.

본 발명의 일 실시예에 따른 방수 시트는, 보강포층, 상기 보강포층에 함침되면서 상기 보강포층의 적어도 한쪽에 아스팔트를 도포하여 형성되는 아스팔트층, 및 상기 아스팔트층에 규사를 산포 부착하여 형성되는 접착층을 포함할 수 있다.Waterproof sheet according to an embodiment of the present invention, an asphalt layer formed by applying asphalt to at least one of the reinforcing fabric layer, while being impregnated in the reinforcement cloth layer, the reinforcement cloth layer, and an adhesive layer formed by scattering silica sand on the asphalt layer. It may include.

상기 보강포층은 부직포로 형성될 수 있다.The reinforcement cloth layer may be formed of a nonwoven fabric.

상기 부직포는 유리 섬유 및 아크릴 섬유 중 하나를 포함할 수 있다.The nonwoven fabric may comprise one of glass fibers and acrylic fibers.

상기 부직포는 폴리프로필렌(PP), 폴리에틸렌(PE), 및 고밀도 폴리 에틸렌(HDPE) 중 하나로 형성될 수 있다.The nonwoven fabric may be formed of one of polypropylene (PP), polyethylene (PE), and high density polyethylene (HDPE).

상기 방수 시트의 두께는 1-2mm일 수 있다.The waterproof sheet may have a thickness of 1-2 mm.

상기 아스팔트층은, 중량%로 아스팔트 42-52%, 스티렌부타디엔고무(SBR) 33-36%, 아크릴 수지 8-11%, 탄산염(CaCO3) 3-6% 및 기타 불순물 1-5%를 포함할 수 있다.The asphalt layer, by weight percent contains 42-52% asphalt, 33-36% styrene butadiene rubber (SBR), 8-11% acrylic resin, 3-6% carbonate (CaCO 3 ) and other impurities 1-5% can do.

또한, 본 발명의 일 실시에에 따른 방수 공법은, 피방수 구조물의 바탕면에 프라이머를 도포하여 프라이머층을 형성하는 제1 단계, 상기 프라이머층에 도막 방 수재를 도포하여 도막 방수층을 형성하는 제2 단계, 및 상기 도막방수층에 방수 시트를 부착하여 시트 방수층을 형성하는 제3 단계를 포함할 수 있다.In addition, the waterproof method according to an embodiment of the present invention, the first step of forming a primer layer by applying a primer on the base surface of the water-resistant structure, the agent to form a coating film waterproof layer by applying a coating film waterproofing material to the primer layer And a third step of attaching the waterproof sheet to the waterproofing layer to form a sheet waterproof layer.

상기 제3 단계는, 복수의 방수 시트를 필요로 하는 경우, 1매의 제1 방수 시트를 부착하는 제31 단계, 상기 제1 방수 시트의 이어질 부분에 기설정된 폭을 가지고 일측에 도막 방수재를 도포하는 제32 단계, 상기 제1 도막 방수재에 겹쳐서 제2 방수 시트를 부착하는 제33 단계, 및 상기 제2 방수 시트의 끝과 상기 도막 방수재의 끝을 상기 제1 방수 시트에 아스팔트로 실링하는 제34 단계를 포함할 수 있다.In the third step, when a plurality of waterproof sheets are required, the thirty-first step of attaching one sheet of the first waterproof sheet, the coating film waterproofing material is applied to one side of the first waterproof sheet having a predetermined width to be connected to the first waterproof sheet. The thirty-third step, the thirty-third step of attaching the second waterproof sheet to the first waterproofing sheet overlapping the first waterproofing film; and the thirty-fourth sealing of the end of the second waterproofing sheet and the tip of the coating waterproofing material with the first waterproof sheet It may include a step.

상기 프라이머는 아스팔트와 바탕 조정용 분체로 이루어질 수 있다.The primer may be composed of asphalt and ground adjustment powder.

상기 도막 방수재는 2액형으로 이루어질 수 있다.The coating film waterproofing material may be formed in a two-component type.

상기 도막 방수재는, 수용성 고무화 아스팔트의 주제, 및 이소시아네이트가 첨가된 경화제를 포함할 수 있다.The coating film waterproofing material may include a main material of water-soluble rubberized asphalt and a curing agent added with isocyanate.

또한, 본 발명의 일 실시예에 따른 방수 공법은, 피방수 구조물의 바탕면에 수용성 에폭시 수지 몰탈을 도포하여 방수층/방식층을 형성하는 제10 단계, 및 상기 방수/방식층에 방수 시트를 부착하여 시트 방수층을 형성하는 제20 단계를 포함할 수 있다.In addition, the waterproof method according to an embodiment of the present invention, the tenth step of forming a waterproof layer / anticorrosive layer by applying a water-soluble epoxy resin mortar on the base surface of the water-resistant structure, and attaching the waterproof sheet to the waterproof / anticorrosive layer By the 20th step to form a sheet waterproof layer.

상기 방수/방식층 중 방수층은, 무기질 시멘트와 폴리머 분산제를 혼합한 형태의 수화 응고형 방수층을 형성할 수 있다.The waterproof layer of the waterproof / corrosive layer may form a hydrated solidified waterproof layer of a form in which inorganic cement and a polymer dispersant are mixed.

상기 폴리머 분산제는, 에틸렌아세트산비닐 에멀션계, 아크릴 에멀션계, 합성고무 라텍스 및 고무아스팔트계일 수 있다.The polymer dispersant may be an ethylene vinyl acetate emulsion system, an acrylic emulsion system, a synthetic rubber latex, or a rubber asphalt system.

상기 방수/방식층 중 방식층은, 상기 방수층 위에 에폭시 수지로 형성될 수 있다.The anticorrosive layer of the waterproof / corrosive layer may be formed of an epoxy resin on the waterproof layer.

또한, 본 발명의 일 실시예에 따른 방수 구조는, 적어도 상기 방수 시트의 1가지를 사용하고, 적어도 상기 방수 공법의 1가지를 적용하여 방수 구조를 형성한다.In addition, the waterproof structure according to an embodiment of the present invention, at least one of the waterproof sheet, and at least one of the waterproof method is applied to form a waterproof structure.

이하, 첨부한 도면을 참조하여 본 발명의 실시예에 대하여 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다. 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 동일 또는 유사한 구성요소에 대해서는 동일한 참조부호를 붙였다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those skilled in the art may easily implement the present invention. As those skilled in the art would realize, the described embodiments may be modified in various different ways, all without departing from the spirit or scope of the present invention. In the drawings, parts irrelevant to the description are omitted in order to clearly describe the present invention, and like reference numerals designate like elements throughout the specification.

도1은 본 발명의 일 실시예에 따른 방수 시트의 단면도이다.1 is a cross-sectional view of a waterproof sheet according to an embodiment of the present invention.

이 도면을 참조하면, 방수 시트(10)는 보강포층(2)과 아스팔트층(4) 및 접착층(6)을 포함하여 형성된다.Referring to this figure, the waterproof sheet 10 is formed including the reinforcing cloth layer 2, the asphalt layer 4 and the adhesive layer (6).

보강포층(2)은 방수 시트(10)의 내구성 및 내마모성을 증대시키는 것으로, 부직포로 형성된다.The reinforcement cloth layer 2 increases the durability and wear resistance of the waterproof sheet 10, and is formed of a nonwoven fabric.

부직포는 유리 섬유나 아크릴 섬유를 포함하며, 폴리프로필렌(PP), 폴리에틸렌(PE), 또는 고밀도 폴리 에틸렌(HDPE)으로 형성된다.Nonwovens include glass fibers or acrylic fibers and are formed of polypropylene (PP), polyethylene (PE), or high density polyethylene (HDPE).

아스팔트층(4)은 중량%로 아스팔트 42-52%, 스티렌부타디엔고무(SBR) 33- 36%, 아크릴 수지 8-11%, 탄산염(CaCO3) 3-6% 및 기타 불순물 1-5%를 포함하여 형성된다.Asphalt layer (4) by weight% 42-52% asphalt, 33-36% styrene butadiene rubber (SBR), 8-11% acrylic resin, 3-6% carbonate (CaCO 3 ) and other impurities 1-5% It is formed to include.

이 아스팔트층(4)은 보강포층(2)의 1면에 형성될 수도 있으나, 2면에 형성될 수 있다.The asphalt layer 4 may be formed on one surface of the reinforcement cloth layer 2, but may be formed on two surfaces.

접착층(6)은 아스팔트층(4)에 규사를 산포하여 부착하여 형성된다. 따라서 접착층(6)은 방수 시트(10) 상에 타설되는 보호 콘크리트 및 아스콘(14)(도2 참조)과의 접착력을 향상시킨다.The adhesive layer 6 is formed by scattering and attaching silica sand to the asphalt layer 4. Thus, the adhesive layer 6 improves the adhesion between the protective concrete and the asphalt concrete 14 (see Fig. 2) that is cast on the waterproof sheet 10.

접착층(6)은 보강포층(2)의 2면에 형성된 아스팔트층들(4) 모두에 형성되어, 방수 시트(10)의 상면과 하면에서 접착력을 향상시킬 수 있다.The adhesive layer 6 may be formed on both of the asphalt layers 4 formed on the two surfaces of the reinforcing cloth layer 2 to improve the adhesive strength on the upper and lower surfaces of the waterproof sheet 10.

규사를 아스팔트층(4)의 양면에 부착하여 접착층(6)을 형성함으로써, 방수 시트(10)의 접착 면적을 넓히는 효과가 있다. 따라서 방수 시트(10)와 보호 콘크리트 또는 방수 시트(10)와 도로 면을 형성하는 아스팔트와의 접착력을 향상시켜, 방수 시트(10)의 양측에 형성되는 경계면에서 발생될 수 있는 방수 시트(10)의 분리에 따른 하자를 방지한다.By attaching the silica sand to both surfaces of the asphalt layer 4 to form the adhesive layer 6, there is an effect of widening the adhesive area of the waterproof sheet 10. Therefore, by improving the adhesion between the waterproof sheet 10 and the protective concrete or waterproof sheet 10 and the asphalt forming the road surface, the waterproof sheet 10 that can be generated at the interface formed on both sides of the waterproof sheet 10 Prevent the defects caused by separation of

규사로 형성되는 접착층(6)은 방수 시트(10)의 내수성, 내열성, 내화학성, 내후성, 내구성, 및 내약품성을 향상시킨다. 규사의 내열성으로 인하여 방수 시트(10)를 시공한 후, 150-180도씨를 가지는 아스콘을 시공하여도 접착층(6)은 열에 영향을 받지 않고 접착력을 가지게 된다.The adhesive layer 6 formed of silica sand improves the water resistance, heat resistance, chemical resistance, weather resistance, durability, and chemical resistance of the waterproof sheet 10. Due to the heat resistance of the silica sand, after the waterproof sheet 10 is constructed, the adhesive layer 6 may have adhesive strength without being affected by heat even when constructing an ascon having 150 to 180 degrees.

즉, 접착층(6)은 방수 시트(10) 시공 후, 별도의 건조 기간을 가지지 않고, 콘크리트 타설 공정 또는 아스콘 포장 공사를 가능하게 하여, 공사 기간을 단축시킬 수 있게 한다.That is, the adhesive layer 6 does not have a separate drying period after construction of the waterproof sheet 10, and enables the concrete pouring process or the asphalt concrete construction, thereby shortening the construction period.

방수 시트(10)는 1-2mm의 두께로 형성되어, 얇은 두께에 의하여 시공성을 향상시킨다. 방수 시트(10) 두께가 1mm 미만인 경우 방수 시트(10)의 내구성이 지나키게 약화될 수 있고, 두께가 2mm 초과인 경우 방수 시트(10)의 부피를 지나치게 크게 하여 운반 및 취급을 불편하게 한다. 이 방수 시트(10)는 보강포층(2)을 형성하는 부직포의 내구성에 따라 그 두께를 다르게 형성할 수 있다.Waterproof sheet 10 is formed to a thickness of 1-2mm, improve the workability by a thin thickness. If the thickness of the waterproof sheet 10 is less than 1 mm, the durability of the waterproof sheet 10 may be excessively weakened. If the thickness of the waterproof sheet 10 is greater than 2 mm, the volume of the waterproof sheet 10 may be excessively large to make transportation and handling uncomfortable. The waterproof sheet 10 may have a different thickness depending on the durability of the nonwoven fabric forming the reinforcing fabric layer 2.

이 방수 시트(10)는 길이 방향 및 너비 방향으로 각각 116, 51 N/㎝의 인장 강도와, 34, 105%의 신장률을 가지며, 32, 69%의 인열 성능를 가진다. 이와 같은 방수 시트(10)는 방수 구조를 견고하게 형성하고, 방수 시트(10) 시공 후 아크콘 포장 공사를 가능하게 하여 공사 기간을 단축시킨다.This waterproof sheet 10 has tensile strengths of 116 and 51 N / cm, lengths of 34 and 105%, and tearing performances of 32 and 69%, respectively, in the longitudinal direction and the width direction. Such a waterproof sheet 10 is formed of a waterproof structure, and after the construction of the waterproof sheet 10 to enable the arccon pavement construction to shorten the construction period.

도2는 본 발명의 제1 실시예에 따른 방수 공법의 공정 및 방수 구조의 단면도이다.2 is a cross-sectional view of the process and waterproof structure of the waterproof method according to the first embodiment of the present invention.

이 도면을 참조하면, 이 방수 공법은 피방수 구조물의 바탕면(8)에 프라이머를 도포하여 프라이머층(11)을 형성하는 제1 단계(a), 상기 프라이머층(11)에 도막 방수재를 도포하여 도막 방수층(12)을 형성하는 제2 단계(b), 및 상기 도막 방수층(12)에 방수 시트(10)를 부착하여 시트 방수층(13)을 형성하는 제3 단계(c)를 포함한다.Referring to this figure, this waterproof method is the first step (a) of forming a primer layer 11 by applying a primer on the base surface 8 of the water-resistant structure, coating film waterproofing material on the primer layer 11 A second step (b) of forming the coating waterproof layer 12, and a third step (c) of attaching the waterproof sheet 10 to the coating waterproof layer 12 to form the sheet waterproof layer 13.

바탕면(8)은 옥상, 지하 주차장 상판 또는 교량 상판과 같이 방수 구조를 필요로 하는 부분들이다.Base surface 8 is a portion that requires a waterproof structure, such as a rooftop, underground parking deck or bridge deck.

제1 단계(a)는 프라이머를 바탕면(8)에 도포하여 프라이머층(11)을 형성한다. 이때 사용되는 프라이머는 일례로서 아스팔트와 바탕 조정용 분체로 이루어진다. 바탕 조정용 분체는 중량%로 스티렌부타디엔고무(SBR) 고형분 15%, 아크릴 수지 고형분 15%를 포함한다.In the first step (a), a primer layer 11 is formed by applying a primer to the base surface 8. The primer used at this time consists of asphalt and ground adjustment powder as an example. The ground-adjusting powder contains 15% of styrene-butadiene rubber (SBR) solids and 15% of acrylic resin solids by weight.

제2 단계(b)는 프라이머층(11) 위에 도막 방수재를 도포하여, 도막 방수층(12)을 형성한다. 이 도막 방수층(12)은 방수 구조에서 도막 방수의 장점, 즉 이음매가 없는 방수막을 형성한다.In the second step (b), the coating film waterproofing material is coated on the primer layer 11 to form the coating film waterproofing layer 12. This coating waterproof layer 12 forms an advantage of the coating waterproof in the waterproof structure, that is, a seamless waterproof membrane.

이 도막 방수재는 2액형으로 이루어진다. 일례로서, 도막 방수재는 주제와 경화제로 이루어진다. 주제는 수용성 고무화 아스팔트로 이루어지고, 경화제는 이소시아네이트를 첨가하여 이루어진다.This coating film waterproofing material consists of two components. As an example, the coating waterproof material consists of a main body and a hardener. The main material consists of water-soluble rubberized asphalt, and the hardener is made by adding isocyanate.

이 도막 방수재는 중량%로 85±2%의 고형분으로 이루어지고, 1200mpa.s의 점도를 가지며, 1.0±0.02 비중을 가지고, 10.2 PH를 가진다. 따라서 이 도막 방수재는 78.5N/㎠의 인장강도와 2102의 신장률, 및 64.2N/㎝의 인열 강도를 가진다.This coating film waterproofing material is 85 ± 2% solids by weight, has a viscosity of 1200 mpa · s, has a specific gravity of 1.0 ± 0.02, and has a 10.2 PH. Therefore, the coating film waterproofing material has a tensile strength of 78.5 N / cm 2, an elongation of 2102, and a tear strength of 64.2 N / cm.

도막 방수재가 경화제를 구비하므로 이 도막 방수재로 도막 방수층(12)을 형성하고, 건조 전, 도막 방수층(12) 위에 방수 시트(10)를 시공하더라도 경화제에 의하여 도막 방수재의 건조를 가능하게 한다.Since the coating film waterproofing material includes a hardening agent, the coating film waterproofing layer 12 is formed with the coating film waterproofing material, and even if the waterproof sheet 10 is applied on the coating film waterproofing layer 12 before drying, the coating film waterproofing material can be dried by the curing agent.

도막 방수층(12)은 도막 방수의 장점과 시트 방수의 장점을 가지도록 도막 방수층(12)과 시트 방수층(13)을 하나의 방수 구조에 형성할 수 있게 한다.The coating film waterproofing layer 12 allows the coating film waterproofing layer 12 and the sheet waterproofing layer 13 to be formed in one waterproof structure to have the advantages of the waterproofing of the coating film and the advantages of sheet waterproofing.

제3 단계(c)는 도막 방수층(12)에 방수 시트(10)를 부착 시공하여, 시트 방수층(13)을 형성한다. 이 방수 시트에는 도1을 참조하여 설명한 상기와 같이 구성 되는 방수 시트(10)가 적용될 수 있다.In the third step (c), the waterproof sheet 10 is attached to the coating waterproof layer 12 to form the sheet waterproof layer 13. The waterproof sheet 10 configured as described above with reference to FIG. 1 may be applied to the waterproof sheet.

이 방수 시트(10)에 의한 시트 방수층(13)은 방수 구조에 시트 방수의 장점, 즉 방수 성능, 거동 대응성, 크랙 추종성 및 외부 충격에 대한 강한 대응력을 가지게 한다.The sheet waterproof layer 13 by this waterproof sheet 10 has the advantages of waterproofing the sheet, that is, waterproof performance, behavioral correspondence, crack followability, and a strong response to external impact.

또한, 방수 시트(10)에 의한 방수 구조는 복수의 방수 시트들(10)을 사용하게 된다. 편의상, 방수 시트(10)는 2매 즉, 제1 방수 시트(10a)와 제2 방수 시트(10b)로 이루어지고, 도막 방수층(12)은 프라이머층(11)에 형성되는 제1 도막 방수층(12a)과, 제1 방수 시트(10a)에 끝 위에 형성되는 제2 도막 방수층(12b)으로 이루어지는 것을 예로 들어 설명한다.In addition, the waterproof structure by the waterproof sheet 10 is to use a plurality of waterproof sheets (10). For convenience, the waterproof sheet 10 is composed of two sheets, that is, the first waterproof sheet 10a and the second waterproof sheet 10b, and the coating film waterproof layer 12 is formed of the first coating film waterproof layer formed on the primer layer 11 ( 12a) and the 2nd coating film waterproofing layer 12b formed on the tip in the 1st waterproofing sheet 10a, it demonstrates as an example.

따라서 제3 단계(c)는 도3에 도시된 바와 같은 단계들을 더 포함할 수 있다. 즉 제3 단계(c)는 1매의 제1 방수 시트(10a)를 부착하는 제31 단계(c1), 제1 방수 시트(10a)의 이어질 부분에 기설정된 폭을 가지고 일측에 도막 방수재를 도포하여 제2 도막 방수층(12a)을 형성하는 제32 단계(c2), 제1 방수 시트(10a)에 겹쳐서 제2 방수 시트(10b)를 부착하는 제33 단계(c3), 및 제2 방수 시트(10b)의 끝과 제2 도막 방수층(12b)의 끝을 실링하도록 아스팔트를 도포하여 아스팔트층(4)을 형성하는 제34 단계(c4)를 포함한다.Therefore, the third step (c) may further include the steps as shown in FIG. That is, the third step (c) is to apply the coating film waterproofing material to one side with a predetermined width at the portion to be connected to the first step (c1) and the first waterproof sheet 10a to attach the first waterproof sheet 10a to one sheet. (C2) to form the second waterproofing layer 12a, the 33rd step (c3) of attaching the second waterproof sheet 10b to the first waterproof sheet 10a, and the second waterproof sheet ( And a thirty-fourth step (c4) of forming the asphalt layer 4 by applying asphalt to seal the end of 10b) and the end of the second coating layer 12b.

이와 같이 제1 방수 시트(10a)와 제2 방수 시트(10b)의 이음부에 제2 도막 방수층(12b)을 형성하고, 아스팔트층(4)을 제2 방수 시트(10b)의 끝과 제2 도막 방수층(12b)의 끝을 제1 방수 시트(10b)에 연결하여 실링 구조를 형성함으로써, 이음부에서의 방수 구조가 긴밀하게 형성된다.Thus, the 2nd coating film waterproofing layer 12b is formed in the joint part of the 1st waterproofing sheet 10a and the 2nd waterproofing sheet 10b, and the asphalt layer 4 is made into the tip and the 2nd of the 2nd waterproofing sheet 10b. By connecting the end of the coating film waterproofing layer 12b to the first waterproofing sheet 10b to form a sealing structure, the waterproofing structure at the joint is closely formed.

도4는 본 발명의 제2 실시예에 따른 방수 공법의 공정 및 방수 구조의 단면도이다.4 is a cross-sectional view of a process and waterproof structure of the waterproof method according to the second embodiment of the present invention.

제2 실시예의 방수 공법 및 방수 구조는 프라이머층(11)과 도막 방수층(12)을 구비하는 제1 실시예와 비교되는 방수/방식층(21)을 구비하고 있다.The waterproofing method and the waterproofing structure of the second embodiment include the waterproof / corrosive layer 21 compared with the first embodiment having the primer layer 11 and the coating film waterproofing layer 12.

제2 실시예의 방수 공법은, 피방수 구조물의 바탕면(8)에 수용성 에폭시 수지 몰탈을 도포하여 방수/방식층(21)을 형성하는 제10 단계(a)와, 이 방수/방식층(21)에 방수 시트(10)를 부착하여 시트 방수층(13)을 형성하는 제20 단계(b)를 포함한다.In the waterproofing method of the second embodiment, a tenth step (a) of forming a waterproof / anticorrosive layer 21 by applying a water-soluble epoxy resin mortar to the base surface 8 of the waterproof structure, and the waterproof / anticorrosive layer 21 (B) attaching the waterproof sheet 10 to the sheet) to form the sheet waterproof layer 13.

방수/방식층(21)은 바탕면(8)에 수용성 에폭시 수지 몰탈을 도포함에 따라 방수층(21a)과 방식층(21b)을 동시에 형성한다. The waterproof / corrosive layer 21 forms a waterproof layer 21a and an anticorrosive layer 21b at the same time by applying a water-soluble epoxy resin mortar on the base surface 8.

방수층(21a)은 무기질 시멘트와 폴리머 분산제를 혼합한 형태의 수화 응고형 방수층으로 형성된다.The waterproof layer 21a is formed of a hydrated solidification type waterproof layer in which inorganic cement and a polymer dispersant are mixed.

이 폴리머 분산제는 에틸렌아세트산비닐 에멀션계, 아크릴 에멀션계, 합성고무 라텍스 또는 고무아스팔트계로 이루어진다.This polymer dispersant consists of an ethylene vinyl acetate emulsion system, an acrylic emulsion system, a synthetic rubber latex or a rubber asphalt system.

방식층(21b)은 방수층(21a) 위에 에폭시 수지로 형성된다.The anticorrosive layer 21b is formed of an epoxy resin on the waterproof layer 21a.

수용성 에폭시 수지 몰탈은 에폭시 수지에 무기질 시멘트 및 폴리머 분사제로 혼합된 몰탈 상태로 형성되어 롤러나 에어리스(airless) 도장기를 이용하여 균일하게 도포함으로써 방수층(21a)과 방식층(21b)을 형성하게 된다.The water-soluble epoxy resin mortar is formed in a mortar state mixed with an inorganic cement and a polymer propellant in an epoxy resin and uniformly applied using a roller or an airless sprayer to form the waterproof layer 21a and the anticorrosive layer 21b.

수용성 에폭시 수지로 이루어지는 방수/방식층(21)은, 강한 접착력과 표면장력을 가짐으로 인하여, 콘크리트로 이루어지는 피방수 구조물의 바탕면(8)과 일체 를 이루며, 콘크리트의 중성화를 방지할 수 있다.Since the waterproof / corrosive layer 21 made of a water-soluble epoxy resin has a strong adhesive force and surface tension, the waterproof / corrosive layer 21 is integral with the base surface 8 of the waterproof structure made of concrete, and can prevent the neutralization of the concrete.

시트 방수층은(13)은 수용성 에폭시 수지 몰탈을 도포하여 형성된 방수/방식층(21) 위에, 방수 시트(10)를 부착 시공함으로서 형성된다. 이 방수시트(10)는 제1 실시예에서와 같이 보호 콘트리트(14)로 덮여진다.The sheet waterproof layer 13 is formed by attaching the waterproof sheet 10 on the waterproof / anticorrosive layer 21 formed by applying a water-soluble epoxy resin mortar. This waterproof sheet 10 is covered with a protective concrete 14 as in the first embodiment.

제2 실시예는 교량 상판의 방수 구조에 효과적으로 적용된다. 방수 시트(10)의 보강포층(2) 및 접착층(6)은 교량 상판에 포장되는 아스콘을 통하여 전달되는 차량의 고속 주행과 급제동시의 마찰계수에 의한 방수층과 아스콘층을 분리하려는 작용력에 효과적인 내구성을 발휘한다.The second embodiment is effectively applied to the waterproof structure of the bridge deck. The reinforcement cloth layer 2 and the adhesive layer 6 of the waterproof sheet 10 are effective for separating the waterproof layer and the asphalt concrete layer by the friction coefficient during high-speed driving and braking of the vehicle delivered through the asphalt concrete packaged on the bridge deck. Exert.

이상을 통해 본 발명의 바람직한 실시예에 대하여 설명하였지만, 본 발명은 이에 한정되는 것이 아니고 특허청구범위와 발명의 상세한 설명 및 첨부한 도면의 범위 안에서 여러 가지로 변형하여 실시하는 것이 가능하고 이 또한 본 발명의 범위에 속하는 것은 당연하다.Although the preferred embodiments of the present invention have been described above, the present invention is not limited thereto, and various modifications and changes can be made within the scope of the claims and the detailed description of the invention and the accompanying drawings. Naturally, it belongs to the scope of the invention.

이상 설명한 바와 같이 본 발명에 따르면, 보강포에 아스팔트층을 구비하고, 이에 규사를 산포 부착하여 형성되는 방수 시트를 사용함으로써, 구조물의 방수에서 보강포에 의하여 이음부가 없으면서, 방수 성능, 거동 대응성, 크랙 추종성 및 외부 충격에 대한 강한 대응력을 가지며, 보강포에 아스팔트 및 규사를 구비하여 보호 콘크리트 또는 아스팔트와의 부착력을 강하게 하는 효과가 있다. 또한, 피방수 구조물의 바탕면에 수용성 에폭시 수지 몰탈을 도포하여 방수/방식층을 형성하는 경우, 습윤 바탕면에도 시공 가능한 효과가 있다.As described above, according to the present invention, by using the waterproof sheet provided with an asphalt layer on the reinforcement cloth and scattering silica sand thereon, the waterproofing performance and the behavior correspondence of the structure without the seam by the reinforcement cloth In addition, it has a strong response to crack followability and external impact, and has an effect of strengthening the adhesion to the protective concrete or asphalt by having asphalt and silica sand in the reinforcement cloth. In addition, when the water-soluble epoxy resin mortar is applied to the base surface of the waterproof structure to form a waterproof / anticorrosive layer, there is an effect that can be applied to the wet base surface.

Claims (16)

삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 피방수 구조물의 바탕면에 수용성 에폭시 수지 몰탈을 도포하여 방수/방식층을 형성하는 제10 단계, 및A tenth step of forming a waterproof / anticorrosive layer by applying a water-soluble epoxy resin mortar on the base surface of the waterproof structure, and 상기 방수/방식층에 방수 시트를 부착하여 시트 방수층을 형성하는 제20 단계를 포함하며,And attaching a waterproof sheet to the waterproof / anticorrosive layer to form a sheet waterproof layer, 상기 방수 시트는,The waterproof sheet, 보강포층,Reinforcement layer, 상기 보강포층에 함침되면서 상기 보강포층의 적어도 한쪽에 아스팔트를 도포하여 형성되는 아스팔트층, 및An asphalt layer formed by applying asphalt to at least one side of the reinforcement cloth layer while being impregnated into the reinforcement cloth layer, and 상기 아스팔트층에 규사를 산포 부착하여 형성되는 접착층을 포함하며,And an adhesive layer formed by scattering and attaching silica sand to the asphalt layer. 상기 아스팔트층은,The asphalt layer, 중량%로 아스팔트 42-52%, 스티렌부타디엔고무(SBR) 33-36%, 아크릴 수지 8-11%, 탄산염(CaCO3) 3-6% 및 기타 불순물 1-5%를 포함하고,% By weight 42-52% asphalt, 33-36% styrene butadiene rubber (SBR), 8-11% acrylic resin, 3-6% carbonate (CaCO 3 ) and 1-5% other impurities, 상기 방수/방식층에서 방수층은,The waterproof layer in the waterproof / anticorrosive layer, 무기질 시멘트와 폴리머 분산제를 혼합한 형태의 수화 응고형 방수층을 형성하는 방수 공법.Waterproofing method to form a hydrated solidifying waterproofing layer in which inorganic cement and polymer dispersant are mixed. 제13 항에 있어서,The method of claim 13, 상기 폴리머 분산제는,The polymer dispersant, 에틸렌아세트산비닐 에멀션계, 아크릴 에멀션계, 합성고무 라텍스 및 고무아스팔트계인 방수 공법.Waterproofing method of ethylene vinyl acetate emulsion system, acrylic emulsion system, synthetic rubber latex and rubber asphalt. 피방수 구조물의 바탕면에 수용성 에폭시 수지 몰탈을 도포하여 방수/방식층을 형성하는 제10 단계, 및A tenth step of forming a waterproof / anticorrosive layer by applying a water-soluble epoxy resin mortar on the base surface of the waterproof structure, and 상기 방수/방식층에 방수 시트를 부착하여 시트 방수층을 형성하는 제20 단계를 포함하며,And attaching a waterproof sheet to the waterproof / anticorrosive layer to form a sheet waterproof layer, 상기 방수 시트는,The waterproof sheet, 보강포층,Reinforcement layer, 상기 보강포층에 함침되면서 상기 보강포층의 적어도 한쪽에 아스팔트를 도포하여 형성되는 아스팔트층, 및An asphalt layer formed by applying asphalt to at least one side of the reinforcement cloth layer while being impregnated into the reinforcement cloth layer, and 상기 아스팔트층에 규사를 산포 부착하여 형성되는 접착층을 포함하며,And an adhesive layer formed by scattering and attaching silica sand to the asphalt layer. 상기 아스팔트층은,The asphalt layer, 중량%로 아스팔트 42-52%, 스티렌부타디엔고무(SBR) 33-36%, 아크릴 수지 8-11%, 탄산염(CaCO3) 3-6% 및 기타 불순물 1-5%를 포함하고,% By weight 42-52% asphalt, 33-36% styrene butadiene rubber (SBR), 8-11% acrylic resin, 3-6% carbonate (CaCO 3 ) and 1-5% other impurities, 상기 방수/방식층 중에서 방식층은,Of the waterproof / anticorrosive layer is an anticorrosive layer, 상기 방수층 위에 에폭시 수지로 형성되는 방수 공법.The waterproof method is formed of an epoxy resin on the waterproof layer. 제13 항 내지 제15 항 중 어느 한 항에 의하여 형성되는 방수 구조.Waterproof structure formed by any one of claims 13 to 15.
KR1020060037619A 2006-04-26 2006-04-26 Waterproofing sheet, waterproofing process and waterproofing structure of the same KR100771197B1 (en)