KR100740011B1 - Heat transfer joining pattern color glass plate and manufacturing method thereof - Google Patents

Heat transfer joining pattern color glass plate and manufacturing method thereof Download PDF

Info

Publication number
KR100740011B1
KR100740011B1 KR1020060025970A KR20060025970A KR100740011B1 KR 100740011 B1 KR100740011 B1 KR 100740011B1 KR 1020060025970 A KR1020060025970 A KR 1020060025970A KR 20060025970 A KR20060025970 A KR 20060025970A KR 100740011 B1 KR100740011 B1 KR 100740011B1
Authority
KR
South Korea
Prior art keywords
thermal transfer
layer
glass plate
sheet
double
Prior art date
Application number
KR1020060025970A
Other languages
Korean (ko)
Inventor
최한탁
Original Assignee
최한탁
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 최한탁 filed Critical 최한탁
Priority to KR1020060025970A priority Critical patent/KR100740011B1/en
Application granted granted Critical
Publication of KR100740011B1 publication Critical patent/KR100740011B1/en

Abstract

Provided is a heat transfer joining pattern color glass plate to express a variety of patterns between transparent glass plates on opposite sides at high productivity and to produce environment-friendly, semipermanent interior and exterior materials for construction. The heat transfer joining pattern color glass plate(18) comprises a heat transfer layer(11) for expressing a variety of patterns between glass plates(10), at least one of the glass plates(10) being transparent, in which the heat transfer layer(11) consists of an inner release layer(5) for facilitating separation of a transport sheet, a thermally cured paint layer(6) for preventing the heat transfer layer(11) from getting too soft, a pattern color printed layer(8) having a variety of patterned colors being printed thereon, a transparent adhesive layer(9) used for hot pressing, and a double-side adhesive layer(15) for helping the inner release layer(5) thermally join with the inner face of the transparent glass plate(10).

Description

열전사 접합 무늬칼라 유리판제 및 이것의 제조방법{Heat Transfer Joining Pattern Color Glass Plate and Manufacturing Method Thereof}Heat Transfer Joining Pattern Color Glass Plate and Manufacturing Method Thereof}

도 1은 본 발명의 바람직한 일 실시예에 따른 열전사 접합 무늬칼라 유리판제를 나타내는 사시도이고,1 is a perspective view showing a thermal transfer bonding patterned color glass plate according to an embodiment of the present invention,

도 2은 본 발명의 다른 바람직한 일 실시예에 따라 은폐력층이 포함된 열전사 접합 무늬칼라 유리판제를 나타내는 사시도이고,Figure 2 is a perspective view showing a thermal transfer bonding patterned color glass plate containing a hiding power layer according to another preferred embodiment of the present invention,

도 3은 본 발명의 또 다른 바람직한 일 실시예에 따라 무늬칼라인쇄층이 포함된 열전사층과 포함되지 않은 열전사층이 적층된 구조의 열전사 접합 무늬칼라 유리판제를 나타내는 사시도이고,3 is a perspective view illustrating a thermal transfer bonding patterned color glass plate having a structure in which a thermal transfer layer including a patterned chain chain layer and a thermal transfer layer not included are stacked according to another preferred embodiment of the present invention;

도 4는 본 발명의 또 다른 바람직한 일 실시예에 따라 양면접착층을 통하여 2개의 무늬칼라유리판제가 열접합된 열전사 접합 무늬칼라 유리판제를 나타내는 사시도이고,4 is a perspective view showing a thermal transfer bonding patterned color glass sheet in which two patterned color glass sheets are thermally bonded through a double-sided adhesive layer according to another preferred embodiment of the present invention;

도 5는 본 발명의 또 다른 바람직한 일 실시예에 따른 열전사 접합 무늬칼라 유리판제의 제조방법을 나타내는 흐름도이고,5 is a flowchart illustrating a method of manufacturing a thermal transfer bonding patterned glass sheet according to another preferred embodiment of the present invention.

도 6은 본 발명에 따른 열전사 접합 무늬칼라 유리판제의 제조를 위해 투명유리내면용다이렉트접착열전사지가 열접합된 무늬칼라유리판제를 나타내는 단면도 이고,6 is a cross-sectional view showing a patterned color glass sheet heat-bonded direct adhesive thermal transfer paper for the inner surface of the transparent glass for the production of thermal transfer bonded patterned glass sheet according to the present invention,

도 7은 본 발명에 따른 열전사 접합 무늬칼라 유리판제의 제조를 위해 투명유리내면용다이렉트접착열전사지를 제조하는 단계를 나타내는 공정도이고,7 is a process chart showing the steps of preparing a direct adhesive thermal transfer paper for the inner surface of the transparent glass for the production of thermal transfer bonding patterned color glass plate according to the present invention,

도 8은 본 발명에 따른 열전사 접합 무늬칼라 유리판제의 제조를 위해 사용되는 양면접착층이 포함된 양면접착열전사지를 나타내는 단면도이고,8 is a cross-sectional view showing a double-sided adhesive thermal transfer paper containing a double-sided adhesive layer used for the production of thermal transfer bonded patterned glass sheet according to the present invention,

도 9는 본 발명에 따른 열전사 접합 무늬칼라 유리판제의 제조를 위해 사용되는 양면접착층이 포함된 양면접착열전사지를 제조하는 단계를 나타내는 공정도이고,9 is a process chart showing a step of manufacturing a double-sided adhesive thermal transfer paper containing a double-sided adhesive layer used for the production of thermal transfer bonded patterned glass sheet according to the present invention,

도 10은 본 발명의 또 다른 바람직한 일 실시예에 따라 무늬칼라인쇄층이 포함된 열전사층과 포함되지 않은 열전사층이 적층된 구조의 열전사 접합 무늬칼라 유리판제의 제조방법을 나타내는 흐름도이고,FIG. 10 is a flowchart illustrating a method of manufacturing a thermal transfer bonded patterned glass sheet having a structure in which a thermal transfer layer including a patterned chain chain layer and a thermal transfer layer not included are stacked according to another preferred embodiment of the present invention.

도 11은 본 발명의 또 다른 바람직한 일 실시예에 따라 양면접착층을 통하여 2개의 무늬칼라유리판제가 열접합된 열전사 접합 무늬칼라 유리판제의 제조방법을 나타내는 흐름도이다.FIG. 11 is a flowchart illustrating a method of manufacturing a thermal transfer bonded patterned glass sheet in which two patterned color glass sheets are thermally bonded through a double-sided adhesive layer according to another preferred embodiment of the present invention.

** 도면의 주요부분에 대한 기호의 간단한 설명 **** Brief description of symbols for the main parts of the drawing **

1: 투명유리내면용다이렉트접착열전사지 2: 시트1: direct adhesive thermal transfer paper for transparent glass inner sheet 2: sheet

3: 배면슬립층 4: 운송시트3: back slip layer 4: transport sheet

5: 내면박리층 6: 열경화도료층5: inner peeling layer 6: thermosetting paint layer

7: 은폐력층 8: 무늬칼라인쇄층7: hiding layer 8: pattern line layer

9: 투명접착층 10: 투명유리판제9: transparent adhesive layer 10: transparent glass plate

11: 열전사층 12: 투명유리판제의 내면11: heat transfer layer 12: inner surface of transparent glass plate

13: 무늬칼라유리판제 14: 내면슬립층13: Pattern color glass board 14: Inner slip layer

15: 양면접착층 16: 접합열전사층15: double-sided adhesive layer 16: bonded thermal transfer layer

17: 양면접착열전사지 18: 열전사 접합 무늬칼라 유리판제 17: Double-sided adhesive thermal transfer paper 18: Thermal transfer bonding pattern color glass plate

본 발명은 열전사 접합 무늬칼라 유리판제 및 이것의 제조방법에 관한 것으로, 특히 투명유리내면용다이렉트접착열전사지와 양면접착열전사지를 이용하여 평면 열전사기에서 제조된 열전사 접합 무늬칼라 유리판제 및 이것의 제조방법에 관한 것이다. 더욱 상세하게는 적어도 한쪽이 투명한 대향하는 투명유리판제 사이에 다양한 무늬를 나타내기 위한 열전사층을 포함하는 열전사 접합 무늬칼라 유리판제에 있어서, 상기 열전사층의 내면박리층이 투명유리판제의 내면에 열접합이 될 수 있도록 하는 양면접착층을 더 포함하여 이루어지는 것을 특징으로 한다. The present invention relates to a thermal transfer bonded patterned glass plate and a method for manufacturing the same, in particular, a thermal transfer bonded patterned glass plate manufactured in a planar thermal transfer machine using a direct adhesive thermal transfer paper and a double-sided adhesive thermal transfer paper for transparent glass inner surface and The manufacturing method of this is related. More specifically, at least one of the thermal transfer bonding patterned color glass plate comprising a thermal transfer layer for showing a variety of patterns between the transparent glass plate facing each other, the inner surface peeling layer of the thermal transfer layer on the inner surface of the transparent glass plate Characterized in that it further comprises a double-sided adhesive layer to be a thermal bonding.

일반적으로, 서로 대향하는 2장의 투명 유리판제를 가진 접합 칼라 유리를 제조하는 방법은 액상의 접착성 수지를 이용하는 접합 방법과 진공 접합기를 이용 하는 접합 방법이 있다. 그 중에서 자동차 앞 유리와 같이 무늬를 나타낼 필요가 없는 경우에, 상기의 진공접합기를 이용하는 수지 접합 방법은 라미네이팅 필름의 한 종류로써 PVB 접합 필름 등의 시트지 한장을 대향하는 유리판제 사이에 넣고 진공으로 고열을 가하면 상기 PVB 접합 필름의 접착력에 의해 투명한 유리판제를 접합시키는 방법이다. 그리고, 무늬를 나타내기 위하여 상기 진공 접합기를 이용하는 무늬칼라 접합 방법은 EVA 접합 필름과 천 소재를 대향하는 유리판제 각각에 한장씩 부착시킨후 접합시키고, 상기 접합된 유리판제 사이를 진공접합기를 이용하여 진공상태로 만듬과 동시에 고열을 가함으로써 접합시키는 방법이다.Generally, the method of manufacturing the laminated color glass which has two transparent glass plates facing each other includes the joining method using a liquid adhesive resin, and the joining method using a vacuum bonding machine. In the case where it is not necessary to show a pattern like the windshield of the car, the resin bonding method using the above-mentioned vacuum bonding machine is a kind of laminating film, and puts a sheet of sheet paper, such as a PVB bonding film, between glass plates facing each other and is heated by vacuum. It is a method of bonding a transparent glass plate by the adhesive force of the said PVB bonding film when it adds. And, in order to show the pattern, the pattern color bonding method using the vacuum bonding machine is attached to each of the glass plate made of EVA bonding film and cloth material facing each other and then bonded, and vacuumed between the bonded glass plate using a vacuum bonder It is a method of joining by making a state and applying high heat at the same time.

그러나, 상기한 수지를 이용하는 접합 방법과 진공 접합기를 이용하는 접합 방법은 PVB 접합 필름 등의 시트지나 EVA 접합 필름 등의 천 소재를 각각으로 한장씩 부착시키는 수작업으로 인하여 주름 및 기포현이 발생하기도 하며, 이로 인한 접합력 부족으로 인해, 제조공정 상의 심각한 문제점이 발생하였고, 이것은 진공 접합기를 이용하여 유리판제 사이를 진공으로 제조하는 경우 미약한 접합력 문제는 완전히 해결될 수 없는 결점을 가지고 있다.However, in the bonding method using the above resin and the bonding method using the vacuum bonding machine, wrinkles and bubbles may occur due to the manual work of attaching sheet material such as PVB bonding film or cloth material such as EVA bonding film one by one, respectively. Due to the lack of bonding strength, serious problems have arisen in the manufacturing process, which has a drawback that the weak bonding strength problem cannot be completely solved when vacuuming between glass plates using a vacuum bonding machine.

근래에, 투명 유리판제에 칼라무늬를 표현하는 방법은 투명 유리판제를 접합시키기 위한 별도의 접합성 수지를 사용하는 것이다. 이것은 열전사지를 다이렉트로 열전사하는 것은 아니고, 전사용 프라이머 도장층을 투명 유리판제의 표면에 형성하는 것이다. 상기 전사용 프라이머 도장층이라는 것은 대향하는 유리판제를 접합시키 기 위한 접합성 수지를 말하는 것으로, 실크스크린 인쇄방법이나 선팅방법 또는 인새된 시트지를 점착제로 부착하는 방법에 의해 프린트되어 지는 것이며, 그 중에서 가장 일반적인 방법은 인쇄된 시트지를 접합성 수지 등의 점착제로 부착하는 방법이다.In recent years, the method of expressing a color pattern on a transparent glass sheet is to use a separate bonding resin for bonding the transparent glass sheet. This does not directly heat transfer the thermal transfer paper, but forms the primer coating layer for transfer on the surface of the transparent glass plate. The primer coating layer for transfer refers to a bonding resin for bonding opposing glass plates, and is printed by a silkscreen printing method, a spinning method, or a method of attaching a sheet of paper with a pressure-sensitive adhesive. The general method is a method of attaching printed sheet paper with an adhesive such as a adhesive resin.

그러나, 상기와 같이 투명 유리판제에 프라이머 코팅 수지 또는 접착제를 별도로 이용하는 방법은 프라이머 코팅 수지 또는 접착제를 롤 코팅이나 스프레이 코팅 방법으로 도포한 후에 장시간 고열로 건조시키는 과정을 거쳐야 하기 때문에, 기포가 발생하기 쉽고 다른 이물질이 포함되는 심각한 문제점을 가지고 있다. 이것은 제품의 불량으로 연결되어 막대한 비용 손실을 가져올 수도 있다. 또한, 다양한 무늬칼라를 유리판제에 칼라프린트 하는 경우, 프라이머 코팅 수지 또는 접착제의 접착이 불완전하거나 장시간 고열에 의한 변조가 발생하면 유리판제 자체를 폐기처분해야만 하는 문제점을 가지고 있다. However, since a method of separately using a primer coating resin or an adhesive on the transparent glass sheet as described above requires a process of drying the primer coating resin or adhesive by a roll coating or a spray coating method at a high temperature for a long time, bubbles are generated. There is a serious problem that it is easy to include other foreign matter. This can lead to product defects and result in huge cost loss. In addition, in the case of color printing various pattern colors on the glass plate, when the adhesion of the primer coating resin or the adhesive is incomplete or a modulation occurs due to high temperature for a long time, the glass plate itself has to be disposed of.

따라서, 위와 같은 방법은 프라이머 코팅 수지 또는 접착제를 도포하고 건조시키는 별도의 과정을 필요로 하는 것이기 때문에, 유리판제의 표면에 순간적으로 다이렉트 열전사되기에는 부적합한 것이고, 이러한 종래의 열전사지나 라미네이팅지를 유리판제의 표면에 직접 열전사하여 프린트할 수도 없는 것이다. 상기와 같은 제조 방법이나 그렇게 제조된 무늬칼라 유리판제에 열전사 방법을 그대로 적용하기에는 근본적으로 불가능한 것이다. Therefore, since the above method requires a separate process of applying and drying the primer coating resin or adhesive, it is not suitable for instant thermal transfer on the surface of the glass plate, and such a conventional thermal transfer paper or laminating paper is a glass plate. It is not possible to print directly on the surface of the agent by thermal transfer. It is fundamentally impossible to apply the thermal transfer method as it is to the manufacturing method as described above or the patterned color glass sheet thus produced.

이에 본 발명은 상기와 같은 문제점을 해결하기 위하여 안출된 것으로, 적어도 한쪽이 투명한 대향하는 투명유리판제 사이에 다양한 무늬를 나타내기 위한 열전사층을 포함하는 열전사 접합 무늬칼라 유리판제에 있어서, 상기 열전사층의 내면박리층이 투명유리판제의 내면에 열접합이 될 수 있도록 하는 양면접착층을 더 포함하여 이루어지는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제를 제공하기 위한 것이다. Accordingly, the present invention has been made to solve the above problems, at least one of the thermal transfer bonding patterned color glass plate comprising a thermal transfer layer for showing a variety of patterns between the transparent glass plate facing the transparent, the thermoelectric The inner surface peeling layer of the four layers to provide a thermal transfer bonding patterned color glass sheet further comprises a double-sided adhesive layer to be thermally bonded to the inner surface of the transparent glass plate.

이러한 본 발명에 의하여, 투명한 유리판제의 내면 사이에 별도의 필름이나 프라이머 코팅 수지 또는 접착제를 사용하지 않기 때문에 기포나 이물질이 발생하지 않으며, 다양한 무늬를 평면 열전사기에서 열전사 방법으로 접합 무늬 칼라유리판제를 제조하고자 하는 것이 본 발명의 목적이다. 또한, 종래에는 무늬칼라층을 부착시키는 것과는 별도로 프라이머 코팅 수지 또는 접착제를 도포하는 추가의 과정이 필요했지만, 본 발명을 통하여 상기한 추가 과정이 필요 없이 유리판제를 세척하고 건조시킨 상태에서 바로 유리판제의 내면에 무늬칼라층과 함께 접착층을 순간적으로 열전사시킴으로써 다양한 무늬를 간단하고 손쉽게 프린트하고자 하는 것이다. According to the present invention, since no separate film or primer coating resin or adhesive is used between the inner surfaces of the transparent glass plate, no bubbles or foreign substances are generated, and various patterns are bonded patterned color glass plates by a thermal transfer method in a planar thermal transfer machine. It is an object of the present invention to prepare an agent. In addition, in the past, an additional process of applying a primer coating resin or an adhesive is required separately from attaching a patterned color layer, but the glass plate is directly washed in a state in which the glass plate is washed and dried without the need for the above additional process. By thermally transferring the adhesive layer together with the pattern color layer on the inner surface of the various patterns to be printed simply and easily.

즉, 본 발명은 대향하는 투명한 유리판제 사이에서 다양한 무늬를 나타낼 수 있는 열전사 접합 무늬칼라 유리판제 및 이의 제조방법에 관한 것으로, 특히 투명유리내 면용다이렉트접착열전사지와 양면접착열전사지를 이용하여 평면 열전사기에서 제조되는 열전사 접합 무늬칼라 유리판제 및 이것의 제조방법에 관한 것으로써, 평면 열 전사기에서 열전사 접합의 생산공정을 보다 간략히 할 수 있고 강력한 접착력으로 응력이 강화된 반 영구적인 기능을 가지는 열전사 접합 무늬칼라 유리판제를 생산하기 위한 것이다. 다시 말해서, 본 발명에 따라 평면 열 전사기에서 다양한 무늬칼라를 빠르게 전사 프린트하는 것과 아울러 유리판제의 접합 공정을 개선시킴으로써, 제품의 생산성과 제조의 작업성을 향상시킬 수 있고, 투명 유리판제에 보다 향상된 기능을 제공할 수 있으며, 생산공정 단축에 따른 제조설비 절감과 함께 환경친화적인 불연 건축 내, 외장제를 반영구적으로 생산하는 것이 본 발명의 목적이다. That is, the present invention relates to a thermal transfer bonded color glass plate and a method for manufacturing the same, which can exhibit various patterns between opposing transparent glass plates, and in particular, using a direct adhesive thermal transfer paper and a double-sided adhesive thermal transfer paper for transparent glass. The present invention relates to a thermal transfer bonded patterned glass sheet manufactured by a planar thermal transfer machine and a method of manufacturing the same, which further simplifies the production process of thermal transfer bonding in a planar thermal transfer machine and provides a semi-permanent stress reinforced by strong adhesive force. It is for producing the thermal transfer bonding patterned glass sheet having a function. In other words, according to the present invention, it is possible to improve the productivity of the product and the workability of the production by improving the glass plate bonding process as well as the rapid transfer printing of various patterned colors in the planar heat transfer machine. It is an object of the present invention to semi-permanently produce environmentally friendly non-flammable building and exterior materials in addition to the reduction of manufacturing facilities due to the shortening of the production process, which can provide improved functions.

상기한 목적을 달성하기 위한 본 발명은 적어도 한쪽이 투명한 대향하는 투명유리판제 사이에 다양한 무늬를 나타내기 위한 열전사층을 포함하는 열전사 접합 무늬칼라 유리판제에 있어서, 상기 열전사층은 운송시트의 탈거를 용이하게 할 수 있도록 하는 내면박리층과, 열전사층이 흐무러지는 현상을 방지하기 위한 열경화도료층과, 다양한 무늬칼라가 인쇄된 무늬칼라인쇄층과, 상기 투명유리판제의 내면에 열접착으로 열전사가 될 수 있도록 하는 투명접착층을 포함하고, 상기 내면박리층이 투명유리판제의 내면에 열접합이 될 수 있도록 하는 양면접착층을 더 포함하여 이루어지는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제이다.The present invention for achieving the above object is at least one of the thermal transfer bonding patterned color glass plate comprising a thermal transfer layer for showing a variety of patterns between the transparent glass plate facing each other, wherein the thermal transfer layer is removed from the transport sheet Inner peeling layer for facilitating the film, a thermosetting paint layer for preventing the heat transfer layer from blurring, a patterned calorie chain layer printed with various pattern colors, and heat-bonded to the inner surface of the transparent glass plate The thermal transfer bonding patterned color glass sheet comprises a transparent adhesive layer to enable thermal transfer, and the inner surface peeling layer further comprises a double-sided adhesive layer to be thermally bonded to the inner surface of the transparent glass plate.

이러한 본 발명에 있어서, 상기 열전사층은 평면 열 전사기에 의해 투명접착층을 통하여 투명유리판제의 내면에 열전사된 것이고, 그 이후에 상기 양면접착층이 상기 내면박리층 위에 열전사된 것임을 특징으로 하는 것이 바람직하다. 그리고, 상기 양면접착층이 열전사되는 것은, 먼저 열전사층이 열전사되고 난 다음에 상기 열전사층의 내면박리층에 형성되었던 운송시트가 박리되고 나서 열전사되는 것을 특징으로 하는 것이 더욱 바람직하다. 그리고, 상기 양면접착층은 양면접착층과 내면슬립층 및 운송시트로 이루어진 양면접착열전사지에 의해 열전사된 것임을 특징으로 하는 열전사 접합 무늬칼라 유리판제일 수 있다.In the present invention, the thermal transfer layer is thermally transferred to the inner surface of the transparent glass plate through a transparent adhesive layer by a planar heat transfer machine, after which the double-sided adhesive layer is thermally transferred on the inner surface peeling layer. desirable. Further, the double-sided adhesive layer is thermally transferred, more preferably characterized in that the thermal transfer layer is first thermally transferred and then the transport sheet formed on the inner surface peeling layer of the thermal transfer layer is peeled off and then thermally transferred. In addition, the double-sided adhesive layer may be a thermal transfer bonding patterned color glass plate, characterized in that the thermal transfer by a double-sided adhesive thermal transfer paper consisting of a double-sided adhesive layer, the inner surface slip layer and the transport sheet.

또한, 여기서 상기 열전사층은 반사와 투명을 방지하여 무늬칼라를 선명하게 하기 위한 배경색을 가지는 은폐력층을 더 포함하는 것이 가능하고, 상기 양면접착층은 불투명한 것일 수 있다. 나아가, 본 발명에 따른 열전사 접합 무늬칼라 유리판제는 운송시트의 탈거를 용이하게 할 수 있도록 하는 내면박리층과, 열전사층이 흐무러지는 현상을 방지하기 위한 열경화도료층과, 상기 투명유리판제의 내면에 열접착으로 열전사가 될 수 있도록 하는 투명접착층으로 이루어진 열전사층, 즉 무늬칼라인쇄층이 없는 열전사층을 더 포함하는 특징으로 할 수 있다. In addition, the thermal transfer layer may further include a concealment layer having a background color for sharpening the pattern color by preventing reflection and transparency, and the double-sided adhesive layer may be opaque. Further, the thermal transfer bonding patterned glass sheet according to the present invention is an inner surface peeling layer for facilitating the removal of the transport sheet, a thermosetting paint layer for preventing the thermal transfer layer from blurring, and the transparent glass sheet It may be characterized in that it further comprises a thermal transfer layer made of a transparent adhesive layer, that is, without a patterned chain chain layer to be thermally transferred to the inner surface of the thermal bonding.

그리고, 본 발명의 다른 실시형태는 상기 열전사층이 투명유리판제의 내면에 열전사된 무늬칼라유리판제 2개가 내면박리층을 통하여 서로 마주보는 상태로 열접합 된 것을 특징으로 할 수 있다. 즉, 적어도 한 쪽이 투명한 대향하는 투명유리판제 사이에 다양한 무늬를 나타내기 위한 열전사층을 포함하는 열전사 접합 무늬칼라 유리판제에 있어서, 상기 열전사층은 운송시트의 탈거를 용이하게 할 수 있도록 하는 내면박리층과, 열전사층이 흐무러지는 현상을 방지하기 위한 열경화도료층과, 반사와 투명을 방지하여 무늬칼라를 선명하게 하기 위한 배경색을 가지는 은폐력층과, 다양한 무늬칼라가 인쇄된 무늬칼라인쇄층과, 상기 투명유리판제의 내면에 열접착으로 열전사가될 수 있도록 하는 투명접착층을 포함하고, 이러한 열전사층이 상기 투명유리판제의 내면에 열전사된 무늬칼라유리판제 2개가 내면박리층을 통하여 서로 마주보는 상태로 평면 열전사기에서 열전사 접합이 될 수 있도록 하는 양면접착층을 더 포함하여 이루어지는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제이다.In addition, another embodiment of the present invention may be characterized in that the thermal transfer layer is thermally bonded in a state in which two of the patterned color glass plates thermally transferred to the inner surface of the transparent glass plate face each other through the inner surface peeling layer. That is, in the thermal transfer bonding patterned color glass plate including at least one of the heat transfer layer for showing various patterns between the transparent glass plate facing the transparent, the heat transfer layer is to facilitate the removal of the transport sheet Inner peeling layer, a thermosetting paint layer to prevent the thermal transfer layer from blurring, a concealment layer having a background color for sharpening a pattern color by preventing reflection and transparency, and a patterned calorie printed with various pattern colors A layer and a transparent adhesive layer to be thermally transferred to the inner surface of the transparent glass plate by thermal bonding, wherein two heat transfer layers are patterned color glass plates thermally transferred to the inner surface of the transparent glass plate through the inner surface peeling layer. It further comprises a double-sided adhesive layer to be a thermal transfer bonding in a planar thermal transfer machine facing each other Thermal bonding pattern is the color of the glass plate gong.

상기한 본 발명에 따른 열전사 접합 무늬칼라 유리판제에 있어서, 상기 양면접착층과 상기 열전사층의 내면박리층, 열경화도료층, 은폐력층, 무늬칼라인쇄층 및 투명접착층은 순차적으로 적층되어 이루어지는 것이 바람직하다.In the thermal transfer bonded patterned glass plate according to the present invention, the inner surface peeling layer, the thermosetting paint layer, the concealing force layer, the patterned chain layer and the transparent adhesive layer of the double-sided adhesive layer and the thermal transfer layer are sequentially laminated. desirable.

본 발명의 다른 목적을 달성하기 다른 실시형태는 이러한 열전사 접합 무늬칼라 유리판제를 제조하는 방법에 관한 것이다. 즉, 적어도 한쪽이 투명한 대향하는 투명유리판제 사이에 다양한 무늬를 나타내기 위한 열전사층을 포함하는 열전사 접합 무늬칼라 유리판제의 제조방법에 있어서, 상기 열전사층과 운송시트로 이루어진 투 명유리내면용다이렉트접착열전사지를 투명유리판제의 내면에 1차 열전사시키는 단계; 상기 운송시트를 1차 박리하는 단계; 상기 운송시트가 박리된 열전사층에 양면접착층과 내면슬립층 및 운송시트로 이루어진 양면접착열전사지를 2차 열전사시키는 단계; 상기 내면슬립층 및 운송시트를 2차 박리하는 단계; 및 상기 내면슬립층 및 운송시트가 박리된 양면접착층에 투명유리판제를 부착시키고 평면 열전사기에서 열전사 방법으로 접합시키는 단계;를 포함하는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제의 제조방법이다.Another embodiment of the present invention relates to a method for producing such a thermal transfer bonded patterned glass sheet. That is, in the manufacturing method of the thermal transfer bonding patterned color glass plate comprising a thermal transfer layer for displaying various patterns between the transparent glass plate facing at least one transparent, for the transparent glass inner surface made of the thermal transfer layer and the transport sheet Primary thermal transfer of the direct adhesive thermal transfer paper to the inner surface of the transparent glass plate; First peeling the transport sheet; Secondarily thermally transferring a double-sided adhesive thermal transfer paper including a double-sided adhesive layer, an inner slip layer, and a transfer sheet to the thermal transfer layer from which the transfer sheet is peeled off; Secondary peeling the inner slip layer and the transport sheet; And attaching the transparent glass plate to the double-sided adhesive layer on which the inner slip layer and the transport sheet are peeled off, and bonding the transparent glass plate by a thermal transfer method in a planar thermal transfer machine. .

이러한 본 발명에 있어서, 상기 열전사층은 운송시트의 탈거를 용이하게 할 수 있도록 하는 내면박리층과, 열전사층이 흐무러지는 현상을 방지하기 위한 열경화도료층과, 다양한 무늬칼라가 인쇄된 무늬칼라인쇄층과, 상기 투명유리판제의 내면에 열접착될 수 있도록 하는 투명접착층을 포함하여 이루어지는 것이 바람직하고, 상기 운송시트는 시트와 상기 시트의 배면에 열전사지의 브록킹 방지를 위하여 형성된 배면슬립층으로 이루어진 것이 더욱 바람직하다. In the present invention, the thermal transfer layer is an inner peeling layer to facilitate the removal of the transport sheet, a thermosetting paint layer to prevent the thermal transfer layer from blurring, and a pattern color printed with various pattern colors Preferably it comprises a printing layer and a transparent adhesive layer to be thermally bonded to the inner surface of the transparent glass plate, the transport sheet is a back slip layer formed to prevent the blocking of the thermal transfer paper on the back of the sheet and the sheet More preferably, it is made of.

본 발명의 또 다른 실시형태는 무늬칼라인쇄층이 포함된 열전사층과 포함되지 않은 열전사층이 적층된 구조의 열전사 접합 무늬칼라 유리판제를 제조하는 방법에 관한 것이다. 즉, 적어도 한쪽이 투명한 대향하는 투명유리판제 사이에 다양한 무늬를 나타내기 위한 열전사층을 포함하는 열전사 접합 무늬칼라 유리판제의 제조방법에 있어서, 상기 열전사층과 운송시트로 이루어진 투명유리내면용다이렉트접착열전사 지를 투명유리판제의 내면에 1차 열전사시키는 단계; 상기 운송시트를 1차 박리하는 단계; 상기 운송시트가 박리된 열전사층에 무늬칼라인쇄층이 없는 열전사층과 운송시트로 이루어진 투명유리내면용다이렉트접착열전사지를 2차 열전사시키는 단계; 상기 운송시트를 2차 박리하는 단계; 상기 운송시트가 박리된 열전사층에 양면접착층과 내면슬립층 및 운송시트로 이루어진 양면접착열전사지를 3차 열전사시키는 단계; 상기 내면슬립층 및 운송시트를 3차 박리하는 단계; 상기 운송시트가 박리된 양면접착층에 투명유리판제를 부착시키고 평면 열전사기에서 열전사 방법으로 접합시키는 단계;를 포함하는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제의 제조방법이다.Another embodiment of the present invention relates to a method for producing a thermal transfer bonded patterned glass sheet having a structure in which a thermal transfer layer including a patterned chain chain layer and a thermal transfer layer not included are laminated. That is, in the method of manufacturing a thermal-transfer bonded patterned color glass plate comprising a thermal transfer layer for displaying various patterns between at least one transparent opposing transparent glass plate, the transparent glass inner direct comprising the thermal transfer layer and the transport sheet Primary thermal transfer of the adhesive thermal transfer paper onto the inner surface of the transparent glass sheet; First peeling the transport sheet; Performing a second thermal transfer of a transparent glass inner direct adhesive thermal transfer paper including a thermal transfer layer and a transportation sheet on the thermal transfer layer from which the transportation sheet is peeled off; Second peeling the transport sheet; Tertiary thermal transfer of a double-sided adhesive thermal transfer paper including a double-sided adhesive layer, an inner slip layer, and a transfer sheet to the thermal transfer layer from which the transfer sheet is peeled off; Tertiary peeling the inner slip layer and the transport sheet; And attaching the transparent glass plate to the double-sided adhesive layer on which the transport sheet is peeled off and bonding the transparent glass plate by a thermal transfer method in a planar thermal transfer machine.

본 발명의 또 다른 실시형태는 상기 열전사층이 형성된 무늬칼라유리판제 2개가 내면박리층을 통하여 서로 마주보는 상태로 열접착된 것을 특징으로 하는 유리판제의 제조방법이다. 즉, 적어도 한쪽이 투명한 대향하는 투명유리판제 사이에 다양한 무늬를 나타내기 위한 열전사층을 포함하는 열전사 접합 무늬칼라 유리판제의 제조방법에 있어서, 상기 열전사층과 운송시트로 이루어진 투명유리내면용다이렉트접착열전사지를 투명유리판제의 내면에 1차 열전사시켜서 무늬칼라유리판제를 제조하는 단계; 상기 무늬칼라유리판제의 운송시트를 1차 박리하는 단계; 상기 운송시트가 박리된 무늬칼라유리판제의 열전사층에 양면접착층과 내면슬립층 및 운송시트로 이루어진 양면접착열전사지를 2차 열전사시키는 단계; 상기 내면슬립층 및 운송시트를 2차 박리하는 단계; 상기 내면슬립층 및 운송시트가 박리된 양면접착층에 상기 운송시트가 박리된 또 다른 무늬칼라유리판제를 부착시키고 평면 열전사기에서 열전사 방법으로 접합시키는 단계;를 포함하는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제의 제조방법이다.Another embodiment of the present invention is a method for producing a glass plate, characterized in that two of the patterned color glass plate on which the thermal transfer layer is formed are thermally bonded in a state of facing each other through an inner surface peeling layer. That is, in the method of manufacturing a thermal-transfer bonded patterned color glass plate comprising a thermal transfer layer for displaying various patterns between at least one transparent opposing transparent glass plate, the transparent glass inner direct comprising the thermal transfer layer and the transport sheet Preparing a patterned color glass sheet by first performing thermal transfer on the inner surface of the transparent glass sheet; Primary peeling the transport sheet of the patterned color glass sheet; Performing a second thermal transfer of a double-sided adhesive thermal transfer paper including a double-sided adhesive layer, an inner slip layer, and a transfer sheet on a heat-transfer layer made of a patterned color glass plate from which the transport sheet is peeled off; Secondary peeling the inner slip layer and the transport sheet; Attaching another patterned color glass sheet from which the transport sheet is peeled to the double-sided adhesive layer from which the inner slip layer and the transport sheet are peeled off, and bonding them by a thermal transfer method in a plane thermal transfer machine; It is a manufacturing method of a patterned color glass plate.

나아가, 상술한 바와 같은 본 발명에 따른 열전사 접합 무늬칼라 유리판제의 제조방법에 있어서, 상기 평면 열전사기에서 열전사 방법으로 접합시키는 것은, 상기 투명유리판제 또는 무늬칼라유리판제가 부착된 열전사 접합 무늬칼라 유리판제를 100℃ 내지 130℃의 온도 범위 내로 예열하는 단계; 및 상기 예열된 열전사 접합 무늬칼라 유리판제를 평면 열 전사기에서 180℃ 내지 220℃의 온도 범위로 예열된 탄성고무롤러를 이용하여 순간적으로 압착회전시키는 단계;를 거치는 것일 수 있다. Further, in the method for manufacturing a thermal transfer bonded patterned glass sheet according to the present invention as described above, bonding by the thermal transfer method in the planar thermal transfer machine is the thermal transfer bonding with the transparent glass sheet or the patterned color glass sheet. Preheating the patterned color glass sheet within a temperature range of 100 ° C to 130 ° C; And pressing and rotating the preheated thermal transfer bonded color glass plate instantaneously using an elastic rubber roller preheated to a temperature range of 180 ° C. to 220 ° C. in a planar heat transfer machine.

이하에서는 본 발명의 바람직한 하나의 실시형태를 첨부된 도면을 참조하여 상세하게 설명하기로 한다. 본 발명은 하기의 실시예에 의하여 보다 더 잘 이해 될 수 있으며, 하기의 실시예는 본 발명의 예시 목적을 위한 것이며, 첨부된 특허청구범위에 의하여 한정되는 보호범위를 제한하고자 하는 것은 아니다.Hereinafter, one preferred embodiment of the present invention will be described in detail with reference to the accompanying drawings. The invention may be better understood by the following examples, which are intended for purposes of illustration of the invention and are not intended to limit the scope of protection defined by the appended claims.

도 1은 본 발명의 바람직한 일 실시예에 따른 열전사 접합 무늬칼라 유리판제(18)를 나타내는 사시도이다. 여기에 도시된 바와 같이, 본 발명에 따른 열전사 접합 무늬칼라 유리판제는 적어도 한쪽이 투명한 대향하는 투명유리판제(10) 사이에 다 양한 무늬를 나타내기 위한 열전사층(11)을 포함하는 열전사 접합 칼라무늬 유리판제(18)에 있어서, 상기 열전사층(11)은 운송시트의 탈거를 용이하게 할 수 있도록 하는 내면박리층(5)과, 열전사층이 흐무러지는 현상을 방지하기 위한 열경화도료층(6)과, 다양한 무늬칼라가 인쇄된 무늬칼라인쇄층(8)과, 상기 투명유리판제(10)의 내면에 열접착으로 열전사가 될 수 있도록 하는 투명접착층(9)을 포함하고, 상기 내면박리층(5)이 투명유리판제(10)의 내면에 열접합이 될 수 있도록 하는 양면접착층(15)을 더 포함하여 이루어지는 것을 특징으로 한다. 1 is a perspective view showing a thermal transfer bonding color glass plate 18 according to a preferred embodiment of the present invention. As shown here, the thermal transfer bonding patterned color glass plate according to the present invention includes a thermal transfer layer 11 including at least one of a thermal transfer layer 11 for displaying various patterns between transparent glass plates 10 facing each other. In the laminated color patterned glass plate 18, the thermal transfer layer 11 is an inner peeling layer 5 to facilitate the removal of the transport sheet, and a thermosetting paint for preventing the thermal transfer layer from becoming cloudy. A layer 6, a pattern line chain layer 8 on which various pattern colors are printed, and a transparent adhesive layer 9 to be thermally transferred to the inner surface of the transparent glass plate 10 by thermal bonding. The inner surface peeling layer 5 is characterized in that it further comprises a double-sided adhesive layer 15 to be thermally bonded to the inner surface of the transparent glass plate (10).

본 발명은 서로 대향하는 투명 유리판제 사이에 다양한 무늬 형성할 수 있는 인쇄층 또는 장식층을 형성하기 위한 것이다. 이를 위한, 본 발명의 특징은 유리판제의 배면 또는 내면에 종래와 같이 롤 코팅이나 스프레이 코팅방법에 의해 별도의 프라이머 코팅 수지나 접착제를 도포하지 않으면서, 유리판제의 내면에 직접 다이렉트로 열전사를 수행함으로써 보다 강화된 응력으로 선명한 무늬칼라를 얻을 수 있는 열전사 접합 무늬칼라 유리판제(18)이다. The present invention is to form a printing layer or a decorative layer capable of forming various patterns between transparent glass plates facing each other. To this end, a feature of the present invention is to directly heat transfer directly to the inner surface of the glass plate without applying a separate primer coating resin or adhesive to the back or inner surface of the glass plate by a roll coating or spray coating method as in the prior art. It is a thermal transfer bonding patterned color glass plate 18 which can obtain a clear patterned color with a stronger stress by performing.

이를 위하여, 본 발명에 따른 열전사 접합 무늬칼라 유리판제(18)는 적어도 한쪽이 투명한 대향하는 투명유리판제(10) 사이에 다양한 무늬를 나타내기 위한 열전사층(11)을 포함하는 열전사 접합 무늬칼라 유리판제(18)로써, 상기 열전사층(11)은 내면박리층(5), 열경화도료층(6), 무늬칼라인쇄층(8) 및 상기 투명유리판제(10)의 내면에 열접착으로 열전사가 될 수 있도록 하는 투명접착층(9)을 포함하고, 상기 내 면박리층(5)이 투명유리판제(10)의 내면에 열접합이 될 수 있도록 하는 양면접착층(15)을 더 포함하여 이루어지는 것을 특징으로 한다. 즉, 상기 열전사층(11)은 평면 열 전사기에 의해 투명접착층(9)을 통하여 투명유리판제(10)의 내면(12)에 열전사됨으로써 무늬칼라유리판제(13)가 되는 것이고, 그 이후에 상기 양면접착층(15)이 상기 내면박리층(5) 위에 열전사되는 것이다. To this end, the thermal transfer bonding patterned color glass plate 18 according to the present invention includes a thermal transfer bonding pattern including a thermal transfer layer 11 for displaying various patterns between transparent glass plates 10 at least one of which is transparent. As the color glass plate 18, the thermal transfer layer 11 is heat-bonded to the inner surface of the inner peeling layer 5, the thermosetting paint layer 6, the patterned calorie chain layer 8 and the transparent glass plate 10 It further comprises a transparent adhesive layer (9) for thermal transfer, the inner surface peeling layer (5) further comprises a double-sided adhesive layer (15) to be thermally bonded to the inner surface of the transparent glass plate (10) Characterized in that made. That is, the thermal transfer layer 11 is thermally transferred to the inner surface 12 of the transparent glass plate 10 through the transparent adhesive layer 9 by a planar heat transfer machine, thereby becoming a patterned color glass plate 13. The double-sided adhesive layer 15 is thermally transferred on the inner surface peeling layer 5.

본 발명에 있어서, 상기 양면접착층(15)은 내면박리층(5)으로 하여금 열전사층(11)이 투명유리판제(10)의 내면(12)에 열접합이 되도록 할 수 있는 것이다. 이러한 상기 양면접착층(15)이 열전사되는 것은, 먼저 열전사층(11)이 열전사되고 난 다음에 상기 열전사층(11)의 내면박리층(5)에 이미 형성되었있던 운송시트(4, 도시하지 않음)가 박리된 후, 상기한 내면박리층(5) 위에 열전사되는 것이 바람직하다. 즉, 본 발명에 따른 열전사층(11)은 투명접착층(9)을 통하여 투명 유리판제(10)의 한쪽 내면(12)에 열전사된 것이고, 상기 열전사층(11)이 열전사된 후에 이러한 열전사층(11)의 운반을 위해 기 형성되었던 운송시트(4)가 박리되고 난 후, 양면접착층(15)을 포함하는 별도의 양면접착열전사지(17)를 이용하여 양면접착층(15)을 상기 열전사층(11)의 내면박리층(5) 위에 열전사시킴으로써 형성된 것이다. 여기서, 상기 양면접착층(15)은 후술하는 바와 같이 양면접착층(15)과 내면슬립층(14) 및 운송시트(4)로 이루어진 양면접착열전사지(17)에 의해 열전사된 것임이 바람직하다.In the present invention, the double-sided adhesive layer 15 allows the inner surface peeling layer 5 to be thermally bonded to the inner surface 12 of the transparent glass plate 10. The double-sided adhesive layer 15 is thermally transferred to the transport sheet 4, which is already formed on the inner surface peeling layer 5 of the thermal transfer layer 11 after the thermal transfer layer 11 is thermally transferred. After peeling off), it is preferable to be thermally transferred on the inner surface peeling layer 5 described above. That is, the thermal transfer layer 11 according to the present invention is thermally transferred to one inner surface 12 of the transparent glass plate 10 through the transparent adhesive layer 9, and the thermal transfer layer 11 is thermally transferred after the thermal transfer layer 11 is thermally transferred. After the transport sheet 4 previously formed for transporting the sand layer 11 is peeled off, the double-sided adhesive layer 15 is thermocoupled using a separate double-sided adhesive thermal transfer paper 17 including the double-sided adhesive layer 15. It is formed by thermal transfer on the inner surface peeling layer (5) of the sand layer (11). Here, it is preferable that the double-sided adhesive layer 15 is thermally transferred by the double-sided adhesive thermal transfer paper 17 including the double-sided adhesive layer 15, the inner surface slip layer 14, and the transport sheet 4, as described below.

이러한 열전사 접합 무늬칼라 유리판제(18)에 의하는 경우, 종래에는 무늬칼라층을 부착시키는 것과는 별도로 프라이머 코팅 수지 또는 접착제를 도포하는 추가의 과정이 필요했지만, 본 발명은 상기한 추가 과정이 필요 없이 유리판제를 세척하고 건조시킨 상태에서 바로 유리판제의 내면에 무늬칼라층과 함께 접착층을 순간적으로 열전사시킴으로써 다양한 무늬를 간단하고 손쉽게 프린트할 수 있는 것이다. In the case of the thermal transfer bonded patterned glass plate 18, an additional process of applying a primer coating resin or an adhesive is required separately from attaching the patterned color layer, but the present invention requires the additional process described above. In the state of washing and drying the glass plate without the instantaneous thermal transfer of the adhesive layer together with the pattern color layer on the inner surface of the glass plate it is possible to simply and easily print a variety of patterns.

본 발명의 다른 실시형태는 도 2에 나타난 바와 같이 상기한 열전사층(11)이 반사와 투명을 방지하여 무늬칼라를 선명하게 하기 위한 배경색을 가지는 은폐력층(7)을 더 포함하는 것을 특징으로 하는 것이다. 도 2은 본 발명의 다른 바람직한 일 실시예에 따라 은폐력층이 포함된 열전사 접합 무늬칼라 유리판제를 나타내는 사시도이고, 여기서,은폐력층(7)은 상기한 의 칼라무늬를 더욱 선명하게 나타내기 위한 것으로, 반사와 투명을 방지할 수도 있다. Another embodiment of the present invention is characterized in that the thermal transfer layer 11 further includes a hiding force layer 7 having a background color for sharpening the pattern color by preventing reflection and transparency as shown in FIG. 2. will be. 2 is a perspective view showing a thermal transfer bonding patterned color glass plate containing a concealment force layer according to another preferred embodiment of the present invention, wherein the concealment force layer 7 is for more clearly showing the color pattern of the In this way, reflection and transparency can be prevented.

이것은 무늬칼라인쇄층(8)의 배경색을 형성함으로써 상기 무늬칼라인쇄층(8)에 의해 나타나는 다양한 무늬를 더욱 효과적으로 나타내기 위한 것으로, 포함되는 안료에 따라 필요에 맞게 다양한 색으로 구현될 수 있으며, 이러한 점에서 알루미늄을 주성분으로 하여 은색으로 밖에 구현이 안되는 종래의 은색증착층과는 구별되는 것이다. This is to more effectively represent the various patterns represented by the pattern line chain layer 8 by forming the background color of the pattern line chain layer 8, it can be implemented in a variety of colors as needed, depending on the pigment included, In this respect, aluminum is distinguished from the conventional silver deposition layer which is implemented only in silver as a main component.

본 발명에 따른 열전사 접합 무늬칼라 유리판제(18)의 열전사층(11)이 은폐력층(7)을 포함하지 않는 상술한 실시예에 의하는 경우는 다른 층이 투명할때 무늬칼라인 쇄층(8)의 다양한 무늬가 투명유리판제(10)의 양쪽으로 모두 비추어질 수 있다. 이를 위해 상기 양면접착층(15)은 투명한 것이 바람직하다. 이와는 반대로, 열전사층(11)이 은폐력층(7)을 포함하는 경우에는 다른 층이 투명하더라도 무늬칼라인쇄층(8)의 다양한 무늬가 은폐력층(7)이 있는 투명유리판제(10) 쪽으로는 비추어지지 않을 것이다. 이 경우, 상기 양면접착층(15)은 불투명한 것일 수 있다. In the case of the above-described embodiment in which the thermal transfer layer 11 of the thermal transfer bonding patterned color glass plate 18 according to the present invention does not include the concealing force layer 7, the patterned column chain layer is formed when the other layer is transparent ( Various patterns of 8) may be illuminated on both sides of the transparent glass plate 10. To this end, the double-sided adhesive layer 15 is preferably transparent. On the contrary, in the case where the thermal transfer layer 11 includes the hiding power layer 7, the various patterns of the patterned chain chain layer 8 are toward the transparent glass plate 10 having the hiding power layer 7 even though the other layers are transparent. It will not be illuminated. In this case, the double-sided adhesive layer 15 may be opaque.

그리고, 본 발명의 또 다른 실시형태는 도 3에 나타난 바와 같이, 운송시트의 탈거를 용이하게 할 수 있도록 하는 내면박리층(5)과, 열전사층이 흐무러지는 현상을 방지하기 위한 열경화도료층(6)과, 상기 투명유리판제(10)의 내면에 열접착으로 열전사가 될 수 있도록 하는 투명접착층(9)으로 이루어진 열전사층(11)을 더 포함하는 것을 특징으로 할 수 있다. 즉, 본 발명에 따른 열전사 접합 무늬칼라 유리판제(18)는 무늬칼라인쇄층(8)이 포함되지 않은 열전사층(11)을 더 포함할 수 있는데, 이 경우 무늬칼라인쇄층(8)이 포함된 열전사층(11)과 무늬칼라인쇄층(8)이 포함되지 않은 열전사층(11)은 적층된 구조를 가지는 것이 바람직하다. In addition, another embodiment of the present invention, as shown in Figure 3, the inner surface peeling layer (5) to facilitate the removal of the transport sheet, and the thermosetting coating layer for preventing the phenomenon of the thermal transfer layer cloudy (6) and a heat transfer layer 11 made of a transparent adhesive layer 9 to be thermally transferred by thermal bonding on the inner surface of the transparent glass plate 10. That is, the thermal transfer bonded patterned glass plate 18 according to the present invention may further include a thermal transfer layer 11 that does not include the patterned column chain layer 8, in which case the patterned column chain layer 8 is formed. It is preferable that the thermal transfer layer 11 and the thermal transfer layer 11 not including the pattern calorie chain layer 8 are laminated.

도 3은 본 발명의 또 다른 바람직한 일 실시예에 따라 무늬칼라인쇄층(8)이 포함된 열전사층(11)과 무늬칼라인쇄층(8)이 포함되지 않은 열전사층(11)이 적층된 구조의 열전사 접합 무늬칼라 유리판제(18)를 나타내는 사시도이고, 여기서 무늬칼라인쇄층(8)이 포함되지 않은 열전사층(11)은 내면박리층(5)과, 열경화도료층(6)과, 투명접착층(9)으로 이루어지는 것이 가능하고, 여기에 은폐력층(7)이 더 포함되어 이루 어지는 구조를 가질 수 있다. 3 is a structure in which a thermal transfer layer 11 including a patterned chain layer 8 and a thermal transfer layer 11 not including a patterned column chain layer 8 are stacked according to another preferred embodiment of the present invention. Is a perspective view showing a thermal transfer bonding patterned color glass plate 18, wherein the thermal transfer layer 11, which does not include the patterned column chain layer 8, includes an inner surface peeling layer 5, a thermosetting paint layer 6, It may be made of a transparent adhesive layer (9), it may have a structure consisting of a hiding force layer (7) further included.

이렇게, 무늬칼라인쇄층(8)이 포함되거나 포함되지 않은 열전사층(11) 2개가 적층되어 이루어진 구조의 접합열전사층(16)은 무늬칼라인쇄층(8)과 은폐력층(7)에 의해 표시되는 무늬칼라 및 배경을 다양하게 선택할 수 있게 한다. In this way, the bonded heat transfer layer 16 having a structure in which two thermal transfer layers 11 including or without the patterned column chain layer 8 is stacked is indicated by the patterned column chain layer 8 and the concealment force layer 7. Various patterns and backgrounds can be selected.

또한, 본 발명의 또 다른 실시형태는 도 4에 나타난 바와 같이, 상기 열전사층(11)이 투명유리판제(10)의 내면(12)에 열전사된 무늬칼라유리판제(13) 2개가 양면접착층(15)을 사이에 두고 내면박리층(5)을 통하여 서로 마주보는 상태로 열접합 된 것을 특징으로 할 수 있다. 도 4는 본 발명의 또 다른 바람직한 일 실시예에 따라 양면접착층(15)을 통하여 무늬칼라유리판제(13) 2개의 열전사층(11)이 서로 열접합 된 열전사 접합 무늬칼라 유리판제(18)를 나타내는 사시도이다. In another embodiment of the present invention, as shown in FIG. 4, the two-color adhesive layer 13 of the patterned color glass plate 13 in which the thermal transfer layer 11 is thermally transferred to the inner surface 12 of the transparent glass plate 10 is formed. It may be characterized in that the thermal bonding in a state facing each other through the inner surface peeling layer (5) with the intervening (15). 4 is a thermal transfer bonding patterned color glass plate 18 in which two thermal transfer layers 11 of the patterned color glass plate 13 are thermally bonded to each other through a double-sided adhesive layer 15 according to another preferred embodiment of the present invention. It is a perspective view showing.

본 발명에 있어서, 상기 무늬칼라유리판제(13)라 함은 도 6에 나타난 바와 같이, 투명유리내면용다이렉트접착열전사지(1)의 열전사층(11)이 투명접착층(9)을 통하여 투명유리판제(10)의 내면(12)에 열접착으로 열전사된 것으로 말하고, 특별한 한정이 없으면 상기 운송시트(4)가 박리된 상태로 열전사층(11) 만이 투명유리판제(10)에 열접합된 유리판제를 의미하는 것이며, 여기에는 특별히 운송시트(4)가 포함될 수도 있다. In the present invention, the patterned color glass plate 13 is, as shown in Figure 6, the heat transfer layer 11 of the direct adhesive thermal transfer paper 1 for the inner surface of the transparent glass transparent glass plate through the transparent adhesive layer (9) The thermal transfer layer 11 is thermally bonded to the inner surface 12 of the tenth, and unless otherwise specified, only the thermal transfer layer 11 is thermally bonded to the transparent glass plate 10 while the transport sheet 4 is peeled off. It means a glass plate, which may in particular include a transport sheet (4).

이러한 본 발명은 도 4에 나타난 바와 같이, 적어도 한 쪽이 투명한 대향하는 투명유리판제(10) 사이에 다양한 무늬를 나타내기 위한 열전사층(11)을 포함하는 열전사 접합 무늬칼라 유리판제(18)에 있어서, 상기 열전사층(11)은 운송시트의 탈거를 용이하게 할 수 있도록 하는 내면박리층(5)과, 열전사층이 흐무러지는 현상을 방지하기 위한 열경화도료층(6)과, 반사와 투명을 방지하여 무늬칼라를 선명하게 하기 위한 배경색을 가지는 은폐력층(7)과, 다양한 무늬칼라가 인쇄된 무늬칼라인쇄층(8)과, 상기 투명유리판제(10)의 내면에 열접착으로 열전사가될 수 있도록 하는 투명접착층(9)을 포함하고, 이러한 열전사층(11)이 상기 투명유리판제(10)의 내면에 열전사된 무늬칼라유리판제(13) 2개가 내면박리층(5)을 통하여 서로 마주보는 상태로 평면 열전사기에서 열전사 접합이 될 수 있도록 하는 양면접착층(15)을 더 포함하여 이루어지는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18)일 수 있다.This invention, as shown in Figure 4, at least one of the thermal transfer bonding patterned color glass plate 18 including a thermal transfer layer 11 for showing a variety of patterns between the transparent glass plate 10 facing each other transparent In the thermal transfer layer 11, the inner surface peeling layer (5) to facilitate the removal of the transport sheet, the thermosetting paint layer (6) to prevent the thermal transfer layer from blurring, and the reflection and Concealment layer (7) having a background color for clearing the pattern color by preventing transparency, the pattern line layer (8) on which various pattern colors are printed, and thermoelectric on the inner surface of the transparent glass plate (10) by thermal adhesion It includes a transparent adhesive layer (9) to be twisted, two heat transfer layer 11 is a patterned color glass plate 13 is heat-transferred to the inner surface of the transparent glass plate 10 is the inner peeling layer (5) In a plane thermal transfer machine facing each other through Thermal transfer, characterized in that further comprising a double-sided adhesive layer (15) for the transfer to be bonded may be a bond pattern color glass sheet of claim 18.

또한, 상술한 본 발명에 있어서, 상기 양면접착층(15)과 상기 열전사층(11)의 내면박리층(5), 열경화도료층(6), 은폐력층(7), 무늬칼라인쇄층(8) 및 투명접착층(9)은 순차적으로 적층되어 이루어진 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18)이거나 이것의 제조방법일 수 있다.In addition, in the present invention described above, the inner surface peeling layer (5), the thermosetting paint layer (6), the concealing force layer (7) of the double-sided adhesive layer 15 and the thermal transfer layer 11, the pattern calender chain layer (8) ) And the transparent adhesive layer 9 may be a thermal transfer bonding patterned color glass plate 18, or a manufacturing method thereof, which is formed by sequentially stacking.

이러한 본 발명 역시 유리판제의 배면 또는 내면에 종래와 같이 롤 코팅이나 스프레이 코팅방법에 의해 별도의 프라이머 코팅 수지나 접착제를 도포하지 않으면서, 유리판제의 내면(12)에 직접 다이렉트로 열전사가 수행됨으로써 보다 강화된 응력으로 선명한 칼라무늬를 얻을 수 있는 열전사 접합 무늬칼라 유리판제(18)이다. 즉, 상기 열전사층(11)은 평면 열 전사기에 의해 투명접착층(9)을 통하여 투명유리판제(10)의 한쪽 내면(12)에 열전사되어 무늬칼라유리판제(13)가 형성되는 것이고, 그 다음에 양면접착층(15)이 상기 무늬칼라유리판제(13)의 최상층인 내면박리층(5) 위에 열전사되는 것이며, 그리고 나서 상기 열전사층(11)이 기 형성된 다른 한쪽의 투명유리판제(10), 즉 상기 열전사층(11)이 기 형성된 무늬칼라유리판제(13)를 상기한 양면접착층(15)에 부착시킨 뒤 접합 열전사시킴으로써 제조되는 것이다. The present invention is also carried out by direct thermal transfer directly to the inner surface 12 of the glass plate without applying a separate primer coating resin or adhesive to the back or inner surface of the glass plate by a roll coating or spray coating method as conventionally The thermal transfer bonding patterned color glass plate 18 which can obtain a clear color pattern by a strengthened stress. That is, the thermal transfer layer 11 is thermally transferred to one inner surface 12 of the transparent glass plate 10 through the transparent adhesive layer 9 by a planar heat transfer machine to form a patterned color glass plate 13. Next, the double-sided adhesive layer 15 is thermally transferred onto the inner surface peeling layer 5, which is the uppermost layer of the patterned color glass plate 13, and then the other transparent glass sheet 10 on which the thermal transfer layer 11 is already formed. ), Ie, the thermal transfer layer 11 is prepared by attaching a patterned color glass plate 13 previously formed to the double-sided adhesive layer 15 and bonding thermal transfer.

본 발명에 있어서, 상기 양면접착층(15)은 2개의 무늬칼라유리판제(13)의 열전사층(11)이 서로 마주보는 상태로, 특히 열전사층(11)의 투명접착층(9)은 투명유리판제(10)의 내면(12)을 향하도록하고 열전사층(11)의 내면박리층(5)이 양면접착층(15)을 중심으로 서로 마주보는 상태로 열접합이 될 수 있도록 하기 위한 것이고, 이를 통하여 무늬칼라유리판제(13)의 열전사층(11)이 서로 대향하는 투명유리판제(10)의 내면(12)에 열전사되도록 할 수 있는 것이다. 이러한 상기 양면접착층(15)이 열전사층(11) 위에 열전사되는 것은, 먼저 열전사층(11)이 열전사되고 난 다음에 상기 열전사층(11)의 내면박리층(5)에 이미 형성되었있던 운송시트(4, 도시하지 않음)가 박리된 후, 상기한 열전사층(11)의 내면박리층(5) 위에 열전사되는 것이 바람직하다. In the present invention, the double-sided adhesive layer 15 is in a state in which the thermal transfer layers 11 of the two patterned color glass plates 13 face each other, in particular, the transparent adhesive layer 9 of the thermal transfer layer 11 is made of a transparent glass plate. To face the inner surface 12 of the (10) and to allow the inner surface peeling layer (5) of the thermal transfer layer 11 to be thermally bonded in a state facing each other around the double-sided adhesive layer (15), through The thermal transfer layer 11 of the patterned color glass plate 13 can be thermally transferred to the inner surface 12 of the transparent glass plate 10 facing each other. The double-sided adhesive layer 15 is thermally transferred on the thermal transfer layer 11, which has been already formed on the inner surface peeling layer 5 of the thermal transfer layer 11 after the thermal transfer layer 11 is thermally transferred. After the transport sheet 4 (not shown) is peeled off, it is preferable that the thermal transfer is performed on the inner surface peeling layer 5 of the thermal transfer layer 11 described above.

이렇게 투명 유리판제(10)의 안쪽 내면(12)에 열전사지를 직접 평면 열 전사기에서 다이렉트로 열전사시킴으로써 투명한 유리의 외부에서 안쪽 내면에 있는 다양한 장식무늬를 감상할 수 있고, 열전사층(11)이 투명 유리판제(10)의 내면(12)에 위치함으로써, 더욱 선명한 장식 무늬 효과를 가질 수 있는 것이다. 나아가, 상술한 다른 실시예와 비교하여, 본 실시예에 따른 열전사 접합 무늬칼라 유리판제(18)는 양면접착층(15)을 중심으로 열전사층(11)이 대향하도록 배치됨으로써, 양쪽 열전사층(11)의 무늬칼라인쇄층(8)이 단 하나의 투명접착층(9)만을 사이에 두고 투명유리판제(10)의 외면에 비춰지는 것이다. 이에 따라, 본 발명의 무늬칼라인쇄층(8)은 대향하는 투명유리판제(10)의 양쪽 모두에 보다 더 선명한 칼라 무늬를 나타낼 수 있는 것이다. Thus, by thermally transferring the thermal transfer paper directly to the inner inner surface 12 of the transparent glass plate 10 in a planar heat transfer machine, it is possible to appreciate a variety of decorative patterns on the inner inner surface from the outside of the transparent glass, the thermal transfer layer 11 ) Is located on the inner surface 12 of the transparent glass plate 10, it is possible to have a more vivid decorative pattern effect. Furthermore, compared with the other embodiments described above, the thermal transfer bonding patterned color glass plate 18 according to the present embodiment is arranged so that the thermal transfer layer 11 is opposed to the double-sided adhesive layer 15 so that both thermal transfer layers ( The pattern calorie chain layer 8 of 11) is projected on the outer surface of the transparent glass plate 10 with only one transparent adhesive layer 9 therebetween. Thereby, the pattern line chain layer 8 of this invention can show a more vivid color pattern on both of the opposing transparent glass plates 10.

본 발명의 다른 실시형태는 도 5에 나타난 바와 같은 흐름을 따라 이러한 열전사 접합 무늬칼라 유리판제(18)를 제조하는 방법에 관한 것이다. 도 5는 본 발명의 또 다른 바람직한 일 실시예에 따른 열전사 접합 무늬칼라 유리판제(18)의 제조방법을 나타내는 흐름도이다.Another embodiment of the present invention relates to a method for producing such a thermal transfer bonded patterned glass sheet 18 along a flow as shown in FIG. 5. 5 is a flowchart showing a method of manufacturing a thermal transfer bonding patterned color glass plate 18 according to another preferred embodiment of the present invention.

즉, 적어도 한쪽이 투명한 대향하는 투명유리판제(10) 사이에 다양한 무늬를 나타내기 위한 열전사층(11)을 포함하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법에 있어서, 상기 열전사층(11)과 운송시트(4)로 이루어진 투명유리내면용다이렉트접착열전사지(1)를 투명유리판제(10)의 내면에 1차 열전사시키는 단계(S40); 상 기 운송시트(4)를 1차 박리하는 단계(S41); 상기 운송시트(4)가 박리된 열전사층(11)에 양면접착층(15)과 내면슬립층(14) 및 운송시트(4)로 이루어진 양면접착열전사지(17)를 2차 열전사시키는 단계(S50); 상기 내면슬립층(14) 및 운송시트(4)를 2차 박리하는 단계(S51); 및 상기 내면슬립층(14) 및 운송시트(4)가 박리된 양면접착층(15)에 투명유리판제(10)를 부착시키고(S60) 평면 열전사기에서 열전사 방법으로 접합시키는 단계;를 포함하는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법이다.That is, in the manufacturing method of the thermal transfer bonding patterned color glass plate 18 comprising a thermal transfer layer 11 for displaying various patterns between the transparent glass plate 10 facing at least one transparent, the thermal transfer layer ( 11) primary direct thermal transfer of the transparent glass inner surface direct adhesive thermal transfer paper (1) consisting of a transport sheet (4) to the inner surface of the transparent glass plate (10) (S40); First peeling the transport sheet (4) (S41); Performing second thermal transfer of the double-sided adhesive thermal transfer paper 17 including the double-sided adhesive layer 15, the inner slip layer 14, and the transfer sheet 4 to the thermal transfer layer 11 from which the transport sheet 4 is peeled off ( S50); Secondary peeling the inner slip layer 14 and the transport sheet 4 (S51); And attaching the transparent glass plate 10 to the double-sided adhesive layer 15 on which the inner slip layer 14 and the transport sheet 4 are peeled off (S60) and joining by a thermal transfer method in a plane thermal transfer machine. It is a manufacturing method of the thermal transfer bonding patterned glass plate 18 characterized by the above-mentioned.

이것은 도 1과 도 2에 나타난 열전사 접합 무늬칼라 유리판제(18)를 제조하기 위한 것으로, 이러한 열전사 접합 무늬칼라 유리판제(18)의 제조를 위해서는 상기한 바와 같이 열전사층(11)과 운송시트(4)로 이루어진 투명유리내면용다이렉트접착열전사지(1)가 1차로 열전사된 후(S40) 상기 운송시트(4)가 1차로 박리되는 과정(S41)을 거치고, 여기에 양면접착층(15)과 내면슬립층(14) 및 운송시트(4)로 이루어진 양면접착열전사지(17)가 2차로 열전사된 후(S50) 상기 내면슬립층(14) 및 운송시트(4)가 2차로 박리되는 과정(S51)을 거치는 것이 특징이다. This is for manufacturing the thermal transfer bonded patterned glass plate 18 shown in Figs. 1 and 2, and for the manufacture of such thermal transfer bonded patterned glass plate 18, transport with the thermal transfer layer 11 as described above. After the transparent glass inner surface direct adhesive thermal transfer paper 1 composed of the sheet 4 is primarily thermally transferred (S40), the transport sheet 4 is first peeled off (S41), and a double-sided adhesive layer ( 15) and the double-sided adhesive thermal transfer paper 17 composed of the inner slip layer 14 and the transport sheet 4 are second thermally transferred (S50), and the inner slip layer 14 and the transport sheet 4 are secondary. It is characterized in that the process (S51) to be peeled off.

도 6은 본 발명에 따른 열전사 접합 무늬칼라 유리판제(18)의 제조를 위해 투명유리내면용다이렉트접착열전사지(1)가 열접합된 무늬칼라유리판제(13)를 나타내는 단면도이고, 여기에 나타난 바와 같이 상기 투명유리내면용다이렉트접착열전사지(1)는 열전사층(11)과 운송시트(4)로 이루어진 것이 바람직하다. 6 is a cross-sectional view showing a patterned color glass sheet 13 heat-bonded to the transparent glass inner direct adhesive thermal transfer paper 1 for the production of the thermal transfer bonded patterned glass sheet 18 according to the present invention, As shown, the transparent glass direct adhesive thermal transfer paper 1 is preferably made of a thermal transfer layer 11 and a transport sheet 4.

그 중에서도 상기 열전사층(11)은 운송시트의 탈거를 용이하게 할 수 있도록 하는 내면박리층(5)과, 열전사층이 흐무러지는 현상을 방지하기 위한 열경화도료층(6)과, 다양한 무늬칼라가 인쇄된 무늬칼라인쇄층(8)과, 상기 투명유리판제(10)의 내면(12)에 열접착으로 열전사가 될 수 있도록 하는 투명접착층(9)을 포함하여 이루어진 것일 수 있고, 여기에는 도 2에 나타난 열전사 접합 무늬칼라 유리판제(18)를 제조하기 위한 방법으로써 반사와 투명을 방지하기 위한 배경색을 가지는 은폐력층(7)이 더 포함되어질 수도 있다. 또한, 상기 투명유리내면용다이렉트접착열전사지(1)의 운송시트(4)는 시트(2)와 상기 시트(2)의 배면에 열전사지의 브록킹 방지를 위하여 형성된 배면슬립층(3)으로 이루어진 것이 바람직하다. Among them, the thermal transfer layer 11 has an inner peeling layer 5 to facilitate the removal of the transport sheet, a thermosetting paint layer 6 for preventing the thermal transfer layer from blurring, and various pattern colors. It may be made to include a printed pattern printed chain layer (8), and a transparent adhesive layer (9) to be thermally transferred to the inner surface 12 of the transparent glass plate 10 by thermal bonding, which is shown in FIG. As a method for manufacturing the thermal transfer bonded patterned glass plate 18 shown in Fig. 2, a hiding layer 7 having a background color for preventing reflection and transparency may be further included. In addition, the transport sheet 4 of the direct adhesive thermal transfer paper 1 for the inner surface of the transparent glass is a back slip layer 3 formed to prevent the thermal transfer paper from blocking on the sheet 2 and the back of the sheet 2. It is preferable that it is made.

구체적으로, 도 7은 본 발명에 따른 열전사 접합 무늬칼라 유리판제(18)의 제조를 위해 투명유리내면용다이렉트접착열전사지(1)를 제조하는 단계를 나타내는 공정도이고, 여기에 도시된 바와 같이, 상기 투명유리내면용다이렉트접착열전사지(1)의 열전사층(11)에 부착되어 열전사층(11)을 보호할 수 있는 운송시트(4)는 상기한 투명유리내면용다이렉트접착열전사지(1)가 두루마리 형태로 곤치된 상태에서 고온 다습한 환경으로 인하여 투명접찹층(9)이 운송시트(4)의 배면에 접착되어 브록킹 불량 제품이 발생되는 것을 미연에 방지하기 위한 것으로, 상기 운송시트(4)의 시트(2) 배면에 실록산폴리머, 가교제, 첨가제, 촉매제 및 솔벤트를 혼합한 혼합물을 200선 또는 250선 그라비아 베다동판으로 롤 코팅하면서 100℃ 내지 120℃ 의 챔버 에서 35~50초 정도로 열경화시켜서 형성된 배면슬립층(3)을 포함하는 것이 특징이다(S110). Specifically, Figure 7 is a process diagram showing the step of producing a direct adhesive thermal transfer paper 1 for the inner surface of the transparent glass for the manufacture of the thermal transfer bonding patterned color glass plate 18 according to the present invention, as shown here The transport sheet 4 which is attached to the thermal transfer layer 11 of the transparent glass inner direct thermal transfer paper 1 to protect the thermal transfer layer 11 is the direct adhesive thermal transfer paper 1 for the transparent glass inner surface. In order to prevent the occurrence of poor blocking product by bonding the transparent adhesive layer 9 to the back of the transport sheet 4 due to the high temperature and high humidity in a state in which it is stuck in a roll form, the transport sheet About 35-50 seconds in the chamber of 100 degreeC-120 degreeC, roll-coating the mixture which mixed the siloxane polymer, a crosslinking agent, an additive, a catalyst, and the solvent with the 200- or 250-line gravure copper plate on the back of the sheet | seat of (4). Thermal Is characterized in that by including a back-slip layer 3 is formed (S110).

그리고, 상기 열전사층(11)의 내면박리층(5)은 운송시트(4)의 탈거를 용이하게 할 수 있도록 하기 위한 것으로, 아크릴계 수지, 폴리에틸렌확스, 계면활성제, 셀룰로이드, 클로로에이티브라마 및 실록산 폴리머로 이루어진 군에서 선택된 하나 이상의 수지를 포함하고, 가교제, 촉매제 및 솔벤트를 더 포함하여 이루어지는 혼합물을 상기 운송시트(4)(특히 배면슬립층(3))의 내면에 200선 또는 250선 그라비아 베다동판으로 롤 코팅방법에 의해 도포하면서 90℃ 내지 120℃ 의 챔버에서 35~50초 정도로 건조 및 열경화시켜서 형성된 것이다(S120). In addition, the inner surface peeling layer 5 of the thermal transfer layer 11 is to facilitate the removal of the transport sheet 4, acrylic resin, polyethylene zoom, surfactants, celluloid, chloroactive lama and siloxane A 200- or 250-line gravure cutting is carried out on the inner surface of the transport sheet 4 (particularly the back slip layer 3), comprising a mixture comprising at least one resin selected from the group consisting of polymers and further comprising a crosslinking agent, a catalyst and a solvent. It is formed by drying and heat curing in a chamber of 90 ℃ to 120 ℃ 35 ~ 50 seconds while applying by a roll coating method to a copper plate (S120).

또한, 상기 열전사층(11)의 열경화도료층(6)은 열전사 과정에서 100℃ 내지 130℃ 챔버의 예열 온도와 평면 열전사지에서 180℃ 내지 220℃ 로 가열된 탄성고무롤러로 순간적으로 압착회전시킬때 열전사층(11)이 흐무르는 현상을 방지하기 위한 것으로, 건축 내 외장제로 시공될 때 경화용 실리콘 접착제, 자외선 UV 접착제 또는 유사형 접착제 등에 의해 녹지 않으면서 내광, 내습, 내마모, 내여르 내약품성을 가지면서, 폴리에스테르, 염화비닐졸, 실리콘, 아크릴, 우레탄 및 멜라민으로 이루어진 군에서 선택된 하나 이상의 수지를 포함하고, 가교제, 촉매제 및 솔벤트를 더 포함하여 이루어진 혼합물을 상기 내면박리층에 200선 또는 250선 그라비아 베다동판으로 롤 코팅방법에 의해 도포하면서 100℃ 내지 120℃ 의 챔버에서 35~50초 정도로 건조 및 열경화시켜서 형성된 것이다(S130). In addition, the thermosetting paint layer 6 of the thermal transfer layer 11 is instantaneously crimped with an elastic rubber roller heated to a temperature of 180 ° C. to 220 ° C. in a planar thermal transfer paper and a preheating temperature of a 100 ° C. to 130 ° C. chamber during the thermal transfer process. It is to prevent the heat transfer layer 11 from spinning when rotating, and when it is applied as an exterior coating material in a building, it is not melted by a curing silicone adhesive, an ultraviolet UV adhesive or a similar adhesive, and is resistant to light, moisture, abrasion, The inner peeling layer comprises a mixture comprising at least one resin selected from the group consisting of polyester, vinyl chloride sol, silicone, acrylic, urethane and melamine, and further comprising a crosslinking agent, a catalyst and a solvent. Drying and thermosetting in a chamber of 100 ° C. to 120 ° C. for about 35 to 50 seconds while applying by a roll coating method to a 200 wire or 250 wire gravure copper plate. It is generated (S130).

다음으로, 본 발명에 따른 열전사층(11)에 선택적으로 포함될 수 있는 은폐력층(7)은 무늬칼라인쇄층의 무늬칼라를 더욱 선명하게 나타내기 위한 것으로, 폴리염화비닐수지, 우레탄수지, 코폴리머수지, 아크릴계수지, 초산비닐계, 피그먼트왁스, 폴리에스트, 아마이드레진 및 무기안료로 이루어진 군에서 선택된 하나 이상의 수지를 포함하고 분산제 및 솔벤트를 더 포함하여 이루어진 그라비아 잉크로 100선 또는 150선 다수의 그라비아 베다동판에 의해 10~15 마이크론 두께로 베다 인쇄하면서 60℃ 내지 90℃ 로 건조시켜 상기 열경화도료층(6) 위에 형성되는 것이다(S140). Next, the concealment force layer 7 which may be selectively included in the thermal transfer layer 11 according to the present invention is to more clearly represent the pattern color of the patterned chain chain layer, polyvinyl chloride resin, urethane resin, copolymer Gravure ink comprising at least one resin selected from the group consisting of resins, acrylic resins, vinyl acetates, pigment waxes, polyesters, amide resins and inorganic pigments, and further comprising a dispersant and a solvent. It is formed on the thermosetting paint layer 6 by drying at 60 ℃ to 90 ℃ while printing by gravure chopped copper plate 10 ~ 15 microns thick cut (S140).

계속해서, 상기 열전사층(11)의 무늬칼라인쇄층(8)은 투명 유리판제(10)의 내면(12)에 다양한 무늬칼라를 인쇄하기 위한 것으로, 비닐아세테이트, 아크릴, 피그먼트왁스, 폴리에스테르, 아마이드레진, 우레탄레진, 비닐레진 및 안료나 염료로 이루어진 군에서 선택된 하나 이상의 수지를 포함하고, 분산제 및 솔벤트를 더 포함하여 이루어진 그라비아 인쇄용 잉크로 장식성 무늬를 디자인하여 전자 조각한 그라비아 동판을 그라비아 인쇄기에서 다수의 칼라로 핀트하여 합성된 것이며, 상기 열경화도료층(6) 또는 은폐력층(7) 위에 형성된 것이다(S150). Subsequently, the pattern line chain layer 8 of the thermal transfer layer 11 is for printing various pattern colors on the inner surface 12 of the transparent glass plate 10, and vinyl acetate, acrylic, pigment wax, polyester , Gravure printing machine which comprises a gravure printing ink comprising amide resin, urethane resin, vinyl resin and at least one resin selected from the group consisting of pigments and dyes, and further comprising a dispersant and a solvent. It is synthesized by pinching in a plurality of colors in, and formed on the thermosetting paint layer 6 or the concealing force layer (7) (S150).

나아가, 상기 열전사층(11)의 투명접착층(9)은 상기 투명 유리판제의 내면에 열접착될 수 있도록 하기 위한 것으로, 폴리에스트, 로진, 비닐레진, 나일론, 이소프렌 스타일렌, 아크릴, 셀룰로이드, 폴리아미드, 아마이드레진, 우레탄레진, 베닐아세테이트, 피그먼트왁스, EVA 중에서 하나 이상이 선택되어 이루어진 핫멜트계 수지를 60℃ 내지 80℃ 로 가열하면서 녹인 후, 분산제, 실리카, 솔벤트와 혼합하여 그라비아 롤 코팅기에 의해 10~30 마이크론 두께로 상기 무늬칼라인쇄층(8) 위에 형성되는 것이다(S160). Furthermore, the transparent adhesive layer 9 of the thermal transfer layer 11 is to be thermally bonded to the inner surface of the transparent glass plate, polyester, rosin, vinyl resin, nylon, isoprene styrene, acrylic, celluloid, polyamide , Hot-melt-based resin made of at least one selected from amaride resin, urethane resin, benzyl acetate, pigment wax, EVA and heated to 60 ℃ to 80 ℃ melt, and then mixed with a dispersant, silica, solvent by a gravure roll coating machine 10 to 30 microns thick to be formed on the pattern line chain layer (8) (S160).

이후에는 이것을 100℃ 내지 120℃ 의 챔버에서 35~50초 정도로 건조 및 숙성시킴으로써 본 발명에 따른 투명유리내면용다이렉트접착열전사지(1)가 완성되는 것이다(S170). Thereafter, by direct drying and aging in a chamber at 100 ° C. to 120 ° C. for about 35 to 50 seconds, the direct adhesive thermal transfer paper 1 for the inner surface of the transparent glass according to the present invention is completed (S170).

이러한 투명유리내면용다이렉트접착열전사지(1)는 투명 유리판제(10)의 내면(12)에 다양한 무늬와 칼라를 가진 무늬칼라인쇄층(8)을 열전사시키기 위한 것으로, 본 발명에서는 열전사층(11)과 운송시트(4)로 이루어진 투명유리내면용다이렉트접착열전사지(1)가 투명 유리판제(10)의 내면(12)에 부착되고, 상기 운송시트(4)의 배면슬립층(3)에 고열(160℃ 내지 200℃)로 가열된 탄성고무롤러를 순간적으로 압착회전시킴으로써 투명유리내면용다이렉트접착열전사지(1)가 투명 유리판제의 내면에 1차적으로 열전사되도록 한다(S40). 그리고, 상기 투명유리내면용다이렉트접착열전사지(1)를 이루는 운송시트(4)를 박리시켜서 열전사층(11)의 내면박리층(5)이 드러나도록 하는 것이다(S41). 이것은 또한 운송시트(4)를 박리시켜서 열전사층(11)의 내면박리층(5)이 드러나도록 함으로써, 열전사층(11)이 투명 유리판제 (10)의 내면(12)에 열전사된 형태의 무늬칼라유리판제(13)가 형성되는 방법이기도 하다.The direct adhesive thermal transfer paper 1 for the inner surface of the transparent glass is to thermally transfer the patterned calorie chain layer 8 having various patterns and colors to the inner surface 12 of the transparent glass plate 10. In the present invention, the thermal transfer layer The direct adhesive thermal transfer paper 1 for the inner surface of the transparent glass, consisting of the 11 and the transport sheet 4, is attached to the inner surface 12 of the transparent glass plate 10, and the back slip layer 3 of the transport sheet 4 is attached. By instantaneous compression rotation of the elastic rubber roller heated to a high temperature (160 ℃ to 200 ℃) to the inner surface of the transparent glass direct adhesive thermal transfer paper (1) is primarily thermal transfer to the inner surface of the transparent glass plate (S40) . Then, the inner surface peeling layer 5 of the thermal transfer layer 11 is exposed by peeling off the transport sheet 4 constituting the transparent glass direct adhesive thermal transfer paper 1 (S41). This also allows the transport sheet 4 to be peeled off so that the inner peeling layer 5 of the thermal transfer layer 11 is exposed so that the thermal transfer layer 11 is thermally transferred to the inner surface 12 of the transparent glass plate 10. It is also the method by which the patterned color glass plate 13 is formed.

다음으로, 도 8은 본 발명에 따른 열전사 접합 무늬칼라 유리판제(18)의 제조를 위해 사용되는 양면접착층(15)이 포함된 양면접착열전사지(17)를 나타내는 단면도이고, 여기에 나타난 바와 같이 상기 양면접착열전사지(17)는 양면접착층(15)과 내면슬립층(14) 및 운송시트(4)로 이루어진 것이 바람직하다. Next, FIG. 8 is a cross-sectional view showing the double-sided adhesive thermal transfer paper 17 including the double-sided adhesive layer 15 used for the manufacture of the thermal transfer bonded patterned glass plate 18 according to the present invention. As described above, the double-sided adhesive thermal transfer paper 17 is preferably made of a double-sided adhesive layer 15, an inner slip layer 14, and a transport sheet 4.

그 중에서도 본 발명은 상기 양면접착열전사지(17)의 양면접착층(15)만이 열전사되어 남아 있는 것을 특징으로 한다. 즉, 내면슬립층(14)과 운송시트(4)는 열전사단계에서 함께 부착되지만, 양면접착층(15)이 열전사층(11)의 내면박리층(5)에 열전사된 후에는 상기 양면접착층(15)과 분리되어 박리되는 것이다. 상기 내면슬립층(14)은 이와 같이 양면접착층(15)과 분리되기 위하여, 배면슬립층(3)과 동일한 물성으로 형성될 수 있다. Among them, the present invention is characterized in that only the double-sided adhesive layer 15 of the double-sided adhesive thermal transfer paper 17 remains thermally transferred. That is, the inner slip layer 14 and the transport sheet 4 are attached together in the thermal transfer step, but after the double-sided adhesive layer 15 is thermally transferred to the inner peeling layer 5 of the thermal transfer layer 11, the double-sided adhesive layer It is separated from (15) and peeled off. The inner slip layer 14 may be formed with the same physical properties as the rear slip layer 3 so as to be separated from the double-sided adhesive layer 15.

구체적으로, 도 9는 본 발명에 따른 열전사 접합 무늬칼라 유리판제의 제조를 위해 사용되는 양면접착층이 포함된 양면접착열전사지를 제조하는 단계를 나타내는 공정도이다. 상기한 운송시트(4)는 상술한 바와 같이, 배면슬립층(3)과 시트(2)로 이루어질 수 있고, 상기 배면슬립층(3)과 운송시트(4)의 구체적인 성분 및 제조방법은 상술한 바와 같을 수 있다. 즉, 여기에 도시된 바와 같이, 상기 양면접착열전 사지(17)는 시트(2)(S200)에 배면슬립층(3)이 형성되고(S210), 상기 배면슬립층(3)과 동일한 방법으로 시트(2) 내면에 내면슬립층(14)이 형성되는 것이다(S220). Specifically, Figure 9 is a process chart showing the step of producing a double-sided adhesive thermal transfer paper containing a double-sided adhesive layer used for the production of thermal transfer bonding patterned color glass plate according to the present invention. As described above, the transport sheet 4 may be formed of the back slip layer 3 and the sheet 2, and specific components and manufacturing methods of the back slip layer 3 and the transport sheet 4 are described above. May be as described. That is, as shown here, the double-sided adhesive thermal transfer limb 17 is formed with the back slip layer 3 on the sheet 2 (S200) (S210), in the same manner as the back slip layer 3 The inner surface slip layer 14 is formed on the inner surface of the sheet 2 (S220).

이러한 내면슬립층(14)은 배면슬립층(3)과 동일한 물성으로 제조되지만, 상술한 투명유리내면용다이렉트접착열전사지(1)의 내면박리층(5)과는 정반대의 기능을 한다. 즉, 상기 내면박리층(5)은 자신에서 탈거되지 않고 운송시트(4)의 시트(2)면과 탈거되도록 하는 것이지만, 상기 내면슬립층(14)은 운송시트(4)와 함께 자신도 탈거되는 것이다. 이러한 내면슬립층(14)은 양면 접합을 용이하게하는 양면접착층(15)만을 접합열전사층(16)으로 구성되게 함으로써, 대향하는 투명유리판제(10) 사이에서 칼라무늬를 평면 열전사기에 의해 열전사 방법으로 접합될 수 있게 하는 것이다.The inner slip layer 14 is manufactured with the same physical properties as the rear slip layer 3, but functions opposite to the inner peeling layer 5 of the above-mentioned direct adhesive thermal transfer paper 1 for transparent glass inner surface. That is, the inner peeling layer 5 is to be removed from the sheet 2 surface of the transport sheet 4 without being detached from itself, but the inner slip layer 14 is also removed with the transport sheet 4 itself. Will be. The inner slip layer 14 is formed by the bonding heat transfer layer 16 of only the double-sided adhesive layer 15 to facilitate the double-sided bonding, so that the color pattern between the opposing transparent glass plate 10 by the thermoelectric thermal transfer machine It is to be joined in four ways.

이렇게 운송시트(4)의 내면슬립층(14)에 코팅된 것으로써, 상기 내면슬립층(14)과 박리되는 것을 특징으로 하는 양면접착층(15)은 폴리에스트, 로진, 비닐레진, 나일론, 이소프렌스타일렌, 아크릴, 셀룰로이드, 폴리아미드, 아마이드레진, 우레탄레진, 비닐아세테이트, 피그먼트왁스, EVA 중에서 하아 이상이 선택되어 이루어진 핫멜트계 수지를 60℃ 내지 80℃ 로 가열하면서 녹인 후, 분산제, 실리카, 솔벤트와 혼합하여 그라비아 롤 코팅기에서 10~30 마이크론 두께로 상기 내면슬립층(14) 위에 코팅하면서 형성되는 것이다(S230). Thus coated on the inner slip layer 14 of the transport sheet 4, the double-sided adhesive layer 15, characterized in that peeled off with the inner slip layer 14 is polyester, rosin, vinyl resin, nylon, isoprene After dissolving hot-melt-based resin in which at least one of styrene, acrylic, celluloid, polyamide, amaride resin, urethane resin, vinyl acetate, pigment wax, and EVA is heated to 60 ° C. to 80 ° C., the dispersant, silica, solvent Mixed with and is formed while coating on the inner slip layer 14 to a thickness of 10 to 30 microns in a gravure roll coater (S230).

이후에는 이것을 100℃ 내지 120℃ 의 챔버에서 35~50초 정도로 건조 및 숙성시킴으로써 본 발명에 따른 양면접착열전사지(17)가 완성되는 것이다(S240). After this, the double-sided adhesive thermal transfer paper 17 according to the present invention is completed by drying and aging in a chamber of 100 ° C. to 120 ° C. for about 35 to 50 seconds (S240).

본 발명은 이렇게 제조된 양면접착열전사지(17)를 상기 운송시트(4)가 박리된 열전사층(11)에 2차로 열전사시키는 단계(S50)를 거친다. 즉, 상기 열전사층의 내면박리층(5)에 평면 열 전사기에서 열전사 접합을 간편하면서 용이하게 할 수 있도록 하는 양면접착열전사지(17)를 부착하면서 고열(160℃ 내지 200℃)로 가열된 탄성고무롤러를 상기 양면접착열전사지(17)의 배면슬립층(3)에 순간적으로 압착회전시킴으로써 상기 양면접착열전사지(17)를 열전사층(11)에 2차적으로로 열전사시키는 것이다(S50). 그리고, 상기 양면접착열전사지(17)를 이루는 상기 내면슬립층(14) 및 운송시트(4)를 박리시켜서 본 발명에 따른 양면접착층(15)이 드러나도록 하는 것이다(S51). The present invention undergoes the second step thermal transfer of the double-sided adhesive thermal transfer paper 17 thus manufactured to the thermal transfer layer 11 from which the transport sheet 4 is peeled off (S50). That is, the heat transfer layer is heated to a high temperature (160 ° C. to 200 ° C.) while attaching the double-sided adhesive thermal transfer paper 17 to the inner surface peeling layer 5 of the thermal transfer layer to facilitate and facilitate thermal transfer bonding in a planar heat transfer machine. The double-sided adhesive thermal transfer paper 17 is thermally transferred to the thermal transfer layer 11 by pressing and rotating the elastic rubber roller to the back slip layer 3 of the double-sided adhesive thermal transfer paper 17 in an instant. S50). Then, the inner slip layer 14 and the transport sheet 4 forming the double-sided adhesive thermal transfer paper 17 are peeled off to expose the double-sided adhesive layer 15 according to the present invention (S51).

그 이후에는 상기 내면슬립층(14) 및 운송시트(4)가 박리된 양면접착층(15)에 투명유리판제(10)를 부착시키는 단계(S60);를 거치고, 100℃ 내지 130℃ 챔버에서 예열시킨 뒤, 평면 열 전사기에서 180℃ 내지 220℃로 가열된 탄성 고무롤러로 순간적으로 압착회전시킴으로써 본 발명에 따른 열전사 접합 무늬칼라 유리판제(18)가 완성되는 것이다. Thereafter, attaching the transparent glass plate 10 to the double-sided adhesive layer 15 on which the inner slip layer 14 and the transport sheet 4 are peeled off (S60); and preheated in a chamber at 100 ° C to 130 ° C. After the heat transfer, the thermal transfer bonding patterned glass sheet 18 according to the present invention is completed by pressing and rotating the elastic rubber roller heated to 180 ° C. to 220 ° C. in a plane heat transfer machine.

본 발명의 또 다른 실시형태는 도 10에 도시된 바와 같이, 무늬칼라인쇄층 (8)이 포함된 열전사층(11)과 포함되지 않은 열전사층(11)이 적층된 구조의 열전사 접합 무늬칼라 유리판제(18)를 제조하는 방법에 관한 것이다. 이것은 도 3에 나타난 바와 같은 열전사 접합 무늬칼라 유리판제(18)를 제조하기 위한 것으로, 도 10은 본 발명의 또 다른 바람직한 일 실시예에 따라 무늬칼라인쇄층이 포함된 열전사층과 포함되지 않은 열전사층이 적층된 구조의 열전사 접합 무늬칼라 유리판제의 제조방법을 나타내는 흐름도이다.According to another embodiment of the present invention, as shown in FIG. 10, a thermal transfer bonding patterned color having a structure in which the thermal transfer layer 11 including the pattern line chain layer 8 and the thermal transfer layer 11 not included are stacked. It relates to a method for producing the glass plate (18). This is to produce a thermal transfer bonded patterned glass plate 18 as shown in Figure 3, Figure 10 is not included with the thermal transfer layer containing a patterned calendered chain layer according to another preferred embodiment of the present invention It is a flowchart which shows the manufacturing method of the thermal transfer bonding patterned color glass plate of the structure by which the thermal transfer layer was laminated | stacked.

즉, 도 10에 나타난 바와 같이, 적어도 한쪽이 투명한 대향하는 투명유리판제(10) 사이에 다양한 무늬를 나타내기 위한 열전사층(11)을 포함하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법에 있어서, 상기 열전사층(11)과 운송시트(4)로 이루어진 투명유리내면용다이렉트접착열전사지(1)를 투명유리판제(10)의 내면에 1차 열전사시키는 단계(S40); 상기 운송시트(4)를 1차 박리하는 단계(S41); 상기 운송시트(4)가 박리된 열전사층(11)에 무늬칼라인쇄층(8)이 없는 열전사층(11)과 운송시트(4)로 이루어진 투명유리내면용다이렉트접착열전사지(1)를 2차 열전사시키는 단계(S42); 상기 운송시트(4)를 2차 박리하는 단계(S43); 상기 운송시트(4)가 박리된 열전사층(11)에 양면접착층(15)과 내면슬립층(14) 및 운송시트(4)로 이루어진 양면접착열전사지(17)를 3차 열전사시키는 단계(S50); 상기 내면슬립층(14) 및 운송시트(4)를 3차 박리하는 단계(S51); 상기 운송시트(4)가 박리된 양면접착층(15)에 투명유리판제(10)를 부착시키고(S60) 평면 열전사기에서 열전사 방법으로 접합시키는 단계;를 포함하는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18)의 제조 방법이다.That is, as shown in Figure 10, at least one of the method for producing a thermal transfer bonding patterned color glass plate 18 including a thermal transfer layer 11 for showing a variety of patterns between the transparent glass plate 10 facing each other transparent In the first step of the thermal transfer layer 11 and the transport sheet (4) for direct transparent thermal transfer paper (1) for the inner surface of the transparent glass plate 10, the first thermal transfer (S40); First peeling the transport sheet (4) (S41); The direct adhesive thermal transfer paper 1 for the transparent glass inner surface which consists of the heat transfer layer 11 and the transport sheet 4 which do not have the patterned chain layer 8 in the heat transfer layer 11 in which the said transport sheet 4 was peeled off was carried out. Differential thermal transfer (S42); Secondary peeling the transport sheet (4) (S43); Tertiary thermal transfer of the double-sided adhesive thermal transfer paper 17 including the double-sided adhesive layer 15, the inner slip layer 14, and the transfer sheet 4 to the thermal transfer layer 11 from which the transfer sheet 4 is peeled off ( S50); Tertiary peeling the inner slip layer 14 and the transport sheet 4 (S51); Attaching the transparent glass plate 10 to the double-sided adhesive layer 15 on which the transport sheet 4 has been peeled off (S60) and joining by a thermal transfer method in a planar thermal transfer machine; and a thermal transfer bonding pattern It is a manufacturing method of the color glass plate 18.

이러한 제조방법은 상술한 바와 같이 운송시트(4)를 1차 박리하는 단계 이후에, 상기 운송시트(4)가 박리된 열전사층(11)에 무늬칼라인쇄층(8)이 없는 열전사층(11)과 운송시트(4)로 이루어진 투명유리내면용다이렉트접착열전사지(1)를 2차 열전사시키는 단계(S42); 상기 운송시트(4)를 2차 박리하는 단계(S43);를 더 포함하는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법이다.This manufacturing method is a heat transfer layer 11 without the patterned chain chain layer 8 in the heat transfer layer 11 from which the transport sheet 4 is peeled off after the first peeling of the transport sheet 4 as described above. Secondary thermal transfer of the transparent adhesive inner heat-transfer paper (1) consisting of a sheet and a transport sheet (4) (S42); The second step of peeling the transport sheet (4) (S43); The method of manufacturing a thermal transfer bonding patterned color glass plate 18 further comprises.

상기한 두번째 투명유리내면용다이렉트접착열전사지(1), 즉 무늬칼라인쇄층(8)이 없는 투명유리내면용다이렉트접착열전사지(1)를 2차 열전사시키고(S42), 운송시트(4)를 2차 박리하는 과정(S43)은 상술한 1차 열전사과정(S40) 및 1차 박리과정(S41)과 동일하다. 이러한 방법에 따르면, 상기 열전사층(11)은 평면 열 전사기에 의해 투명접착층(9)을 통하여 투명유리판제(10)의 한쪽 내면(12)에 열전사되고, 그 다음에 상기 무늬칼라인쇄층(8)이 없는 투명유리내면용다이렉트접착열전사지(1)의 열전사층(11)이 1차 열전사단계(S40)에서 형성된 열전사층(11)의 내면박리층(5) 위에 2차 열전사되는 것이며, 그리고 나서 상기 열전사층(11)의 내면박리층(5)에 상기 양면접착층(15)에 다시 열전사시킨 뒤, 다른 한쪽의 투명유리판제(10)를 부착하여 평면 열전사기에서 열전사방법으로 접합시킴으로써 제조되는 것이다. The second transparent glass direct adhesive thermal transfer paper 1 for the inner surface of the transparent glass, that is, the direct adhesive thermal transfer paper 1 for the inner surface of the transparent glass without the patterned calorie chain layer 8, is subjected to secondary thermal transfer (S42), and the transport sheet (4). ) Secondary peeling process (S43) is the same as the above-described primary thermal transfer process (S40) and primary peeling process (S41). According to this method, the thermal transfer layer 11 is thermally transferred to one inner surface 12 of the transparent glass plate 10 through the transparent adhesive layer 9 by a planar thermal transfer machine, and then the patterned calorie chain layer ( 8) the thermal transfer layer 11 of the transparent direct thermal adhesive paper 1 for the inner surface of the transparent glass is not secondary heat-transferred on the inner peeling layer 5 of the thermal transfer layer 11 formed in the first thermal transfer step S40. Then, heat transfer the inner surface peeling layer 5 of the thermal transfer layer 11 to the double-sided adhesive layer 15 again, and then attach the other transparent glass plate 10 to the thermal transfer method in a planar thermal transfer machine. It is manufactured by joining.

본 발명의 또 다른 실시형태는 상기 열전사층(11)이 형성된 무늬칼라유리판 제(13) 2개가 양면접착층(15)을 중심으로 내면박리층(5)을 통하여 서로 마주보는 상태로 열접착된 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법이다. 이것은 도 4에 나타난 바와 같은 열전사 접합 무늬칼라 유리판제(18)를 제조하기 위한 것으로, 도 11은 본 발명의 또 다른 바람직한 일 실시예에 따라 양면접착층을 통하여 2개의 무늬칼라유리판제가 열접합된 열전사 접합 무늬칼라 유리판제의 제조방법을 나타내는 흐름도이다.According to another embodiment of the present invention, two patterned color glass plates 13 having the thermal transfer layer 11 formed thereon are thermally bonded in a state of facing each other through the inner surface peeling layer 5 around the double-sided adhesive layer 15. It is a manufacturing method of the thermal transfer bonding patterned color glass plate 18 characterized by the above-mentioned. This is to produce a thermal transfer bonded patterned glass plate 18 as shown in Figure 4, Figure 11 is a heat-bonded two patterned color glass plate through the double-sided adhesive layer according to another preferred embodiment of the present invention It is a flowchart which shows the manufacturing method of the thermal transfer bonding patterned color glass plate.

즉, 도 11에 나타난 바와 같이, 적어도 한쪽이 투명한 대향하는 투명유리판제(10) 사이에 다양한 무늬를 나타내기 위한 열전사층(11)을 포함하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법에 있어서, 상기 열전사층(11)과 운송시트(4)로 이루어진 투명유리내면용다이렉트접착열전사지(1)를 투명유리판제(10)의 내면에 1차 열전사시켜서 무늬칼라유리판제(13)를 제조하는 단계(S40); 상기 무늬칼라유리판제(13)의 운송시트(4)를 1차 박리하는 단계(S41); 상기 운송시트(4)가 박리된 무늬칼라유리판제(13)의 열전사층(11)에 양면접착층(15)과 내면슬립층(14) 및 운송시트(4)로 이루어진 양면접착열전사지(17)를 2차 열전사시키는 단계(S50); 상기 내면슬립층(14) 및 운송시트(4)를 2차 박리하는 단계(S51); 상기 내면슬립층(14) 및 운송시트(4)가 박리된 양면접착층(15)에 상기 운송시트(4)가 박리된 또 다른 무늬칼라유리판제(13)를 부착시키고(S61) 평면 열전사기에서 열전사 방법으로 접합시키는 단계;를 포함하는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법이다.That is, as shown in Figure 11, at least one of the method for producing a thermal transfer bonding patterned color glass plate 18 including a thermal transfer layer 11 for showing various patterns between the transparent glass plate 10 facing each other transparent In the first embodiment, the direct adhesive thermal transfer paper 1 for the inner surface of the transparent glass made of the thermal transfer layer 11 and the transport sheet 4 is thermally transferred to the inner surface of the transparent glass plate 10 so as to have a patterned color glass plate 13. Manufacturing step (S40); First peeling the transport sheet 4 of the patterned color glass sheet 13 (S41); The double-sided adhesive thermal transfer paper 17 comprising a double-sided adhesive layer 15, an inner slip layer 14, and a transfer sheet 4 on the thermal transfer layer 11 of the patterned color glass plate 13 on which the transfer sheet 4 is peeled off. Secondary thermal transfer (S50); Secondary peeling the inner slip layer 14 and the transport sheet 4 (S51); On the double-sided adhesive layer 15 on which the inner slip layer 14 and the transport sheet 4 were peeled off, another patterned color glass sheet 13 on which the transport sheet 4 was peeled off was attached (S61). The method of manufacturing a thermal transfer bonding patterned color glass plate 18 comprising a; step of bonding by a thermal transfer method.

이러한 제조방법은 상술한 바와 같이 내면슬립층(14) 및 운송시트(4)를 2차 박리하는 단계(S51); 이후에, 상기 내면슬립층(14) 및 운송시트(4)가 박리된 양면접착층(15)에 상기 운송시트(4)가 박리된 또 다른 무늬칼라유리판제(13)를 부착시키는 단계(S61);를 더 포함하는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법이다.This manufacturing method includes the step of secondary peeling the inner slip layer 14 and the transport sheet 4 as described above (S51); Thereafter, attaching another patterned color glass sheet 13 on which the transport sheet 4 is peeled to the double-sided adhesive layer 15 on which the inner slip layer 14 and the transport sheet 4 are peeled off (S61). It is a manufacturing method of the thermal transfer bonding patterned color glass plate 18 characterized by including further.

이러한 본 발명은 유리판제의 배면 또는 내면에 종래와 같이 롤 코팅이나 스프레이 코팅방법에 의해 별도의 프라이머 코팅 수지나 접착제를 도포하지 않으면서, 열전사층(11)을 대향하는 유리판제의 내면(12)에 직접 다이렉트로 열전사 수행하기 위한 것이다. 여기서, 상기 운송시트(4)가 박리된 또 다른 무늬칼라유리판제(13)는 상술한 1차 열전사단계(S41) 및 운송시트 박리단계(S42)를 거침으로써 형성된 것으로써, 구체적으로는 열전사층(11)과 운송시트(4)로 이루어진 투명유리내면용다이렉트접착열전사지(1)를 투명유리판제(10)에 열전사시킨 후 상기 운송시트(4)를 박리한 것으로, 열전사층(11)이 열전사된 투명유리판제(10)를 말한다. In the present invention, the inner surface 12 of the glass plate facing the thermal transfer layer 11 without applying a separate primer coating resin or adhesive to the back or inner surface of the glass plate by a roll coating or spray coating method as in the related art. It is intended to perform direct thermal transfer directly to. Here, another patterned color glass sheet 13 from which the transport sheet 4 is peeled off is formed by undergoing the above-described first thermal transfer step S41 and the transport sheet peeling step S42, specifically, thermoelectric. The transparent glass inner direct adhesive thermal transfer paper 1 composed of the sand layer 11 and the transport sheet 4 is thermally transferred to the transparent glass plate 10, and then the transport sheet 4 is peeled off. Refers to the transparent glass plate 10 is thermal transfer.

즉, 본 발명은 상기 열전사층(11)이 평면 열 전사기에 의해 투명접착층(9)을 통하여 투명유리판제(10)의 한쪽 내면(12)에 열전사되고, 그 다음에 상기 양면접착층(15)이 상기 내면박리층(5) 위에 열전사되는 것이며, 그리고 나서 상기 열전사층(11)이 기 형성된 다른 한쪽의 투명유리판제(10) 즉, 운송시트(4)가 박리된 또 다 른 무늬칼라유리판제(13)를 상기한 양면접착층(15)에 부착시킨 뒤 접합 열전사시킴으로써 제조되는 것이다. That is, in the present invention, the thermal transfer layer 11 is thermally transferred to one inner surface 12 of the transparent glass plate 10 through the transparent adhesive layer 9 by a planar heat transfer machine, and then the double-sided adhesive layer 15. Another patterned color glass sheet, which is thermally transferred on the inner surface peeling layer 5, and then the other transparent glass sheet 10, on which the thermal transfer layer 11 is formed, that is, the transport sheet 4 is peeled off. It is produced by attaching the agent (13) to the double-sided adhesive layer (15) described above, followed by bonding thermal transfer.

이렇게 대향하는 투명 유리판제(10)의 안쪽 내면(12)에 2개의 열전사층(11)을 직접 평면 열 전사기에서 다이렉트로 열전사시킴으로써 본 발명의 무늬칼라인쇄층(8)은 대향하는 투명유리판제(10)의 양쪽 모두에 보다 더 선명한 칼라 무늬를 나타낼 수 있고, 열전사층(11)이 투명 유리판제(10)의 내면(12)에 위치함으로써, 더욱 선명한 장식 무늬 효과를 가질 수 있는 것이다. The patterned column chain layer 8 of the present invention is directly opposed to the transparent glass plate by direct thermal transfer of two thermal transfer layers 11 directly to the inner inner surface 12 of the opposing transparent glass plate 10 in a planar thermal transfer machine. More vivid color patterns can be exhibited on both sides of the agent (10), and the heat transfer layer 11 is located on the inner surface 12 of the transparent glass plate 10, whereby a vivid decorative pattern effect can be obtained.

나아가, 상술한 바와 같은 본 발명에 따른 열전사 접합 무늬칼라 유리판제(18)의 제조방법에 있어서, 상기 평면 열전사기에서 열전사 방법으로 접합시키는 것은, 상기 투명유리판제(10) 또는 무늬칼라유리판제(13)가 부착된 열전사 접합 무늬칼라 유리판제(18)를 100℃ 내지 130℃의 온도 범위 내로 예열하는 단계(S70); 및 상기 예열된 열전사 접합 무늬칼라 유리판제(18)를 평면 열 전사기에서 180℃ 내지 220℃의 온도 범위로 예열된 탄성고무롤러를 이용하여 순간적으로 압착회전시키는 단계(S80);를 거치는 것을 특징으로 할 수 있다. Furthermore, in the manufacturing method of the thermal transfer bonding patterned color glass plate 18 according to the present invention as described above, bonding by the thermal transfer method in the planar thermal transfer machine is the transparent glass plate 10 or the patterned color glass plate. Preheating the thermal transfer bonding color glass plate 18 having the agent 13 attached thereto within a temperature range of 100 ° C. to 130 ° C. (S70); And step (S80) of the preheated thermal transfer bonding patterned glass plate 18 using an elastic rubber roller preheated to a temperature range of 180 ° C to 220 ° C in a planar heat transfer machine (S80). It can be characterized.

한편, 상기에서는 본 발명을 특정의 바람직한 실시예에 관련하여 도시하고 설명하였지만, 이하의 특허청구범위에 의해 마련되는 본 발명의 기술적 특징이나 분야를 이탈하지 않는 한도 내에서 본 발명이 다양하게 개조 및 변화될 수 있다는 것은 당업계에서 통상의 지식을 가진에게 명백한 것이다. On the other hand, while the present invention has been shown and described with respect to certain preferred embodiments, the invention is variously modified and modified without departing from the technical features or fields of the invention provided by the claims below It will be apparent to those skilled in the art that such changes can be made.

상술한 바와 같이, 본 발명에 의하는 경우 적어도 한쪽이 투명한 대향하는 투명유리판제 사이에 다양한 무늬를 나타내기 위한 열전사층을 포함하는 열전사 접합 무늬칼라 유리판제에 있어서, 상기 열전사층은 운송시트의 탈거를 용이하게 할 수 있도록 하는 내면박리층과, 열전사층이 흐무러지는 현상을 방지하기 위한 열경화도료층과, 다양한 무늬칼라가 인쇄된 무늬칼라인쇄층과, 상기 투명유리판제의 내면에 열접착으로 열전사가 될 수 있도록 하는 투명접착층을 포함하고, 상기 내면박리층이 투명유리판제의 내면에 열접합이 될 수 있도록 하는 양면접착층을 더 포함하여 이루어지는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제를 제공할 수 있다. As described above, according to the present invention, at least one of the thermal transfer bonding patterned color glass plate comprising a thermal transfer layer for showing a variety of patterns between the transparent glass plate facing each other, wherein the thermal transfer layer of the transport sheet An inner peeling layer to facilitate removal, a thermosetting paint layer to prevent the thermal transfer layer from blurring, a patterned calorie chain layer printed with various patterned colors, and a thermal adhesive to the inner surface of the transparent glass plate. Thermal transfer bonding patterned color glass sheet comprising a transparent adhesive layer to be thermal transfer to the surface, wherein the inner peeling layer further comprises a double-sided adhesive layer to be thermally bonded to the inner surface of the transparent glass plate Can provide.

이러한 본 발명에 의하면, 투명한 유리판제의 내면 사이에 별도의 필름이나 프라이머 코팅 수지 또는 접착제를 사용하지 않기 때문에 기포나 이물질이 발생하지 않으며, 다양한 무늬를 열전사 방법으로 프린트할 수 있는 효과가 있다. 또한, 종래에는 무늬칼라층을 부착시키는 것과는 별도로 프라이머 코팅 수지 또는 접착제를 도포하는 추가의 과정이 필요했지만, 본 발명은 상기한 추가 과정이 필요 없이 유리판제를 세척하고 건조시킨 상태에서 바로 유리판제의 내면에 무늬칼라층과 함께 접착층을 순간적으로 열전사시킴으로써 다양한 무늬를 간단하고 손쉽게 프린트할 수 있는 것이다. According to the present invention, since no separate film or primer coating resin or adhesive is used between the inner surfaces of the transparent glass plate, no bubbles or foreign substances are generated, and various patterns can be printed by a thermal transfer method. In addition, in the related art, an additional process of applying a primer coating resin or an adhesive is required separately from attaching a patterned color layer. However, the present invention is a glass plate immediately after being cleaned and dried without the need for the above additional process. By thermally transferring the adhesive layer together with the patterned color layer on the inner surface, various patterns can be printed simply and easily.

즉, 본 발명은 대향하는 투명한 유리판제 사이에서 다양한 무늬를 나타낼 수 있는 열전사 접합 무늬칼라 유리판제 및 이의 제조방법에 관한 것으로, 특히 특히 투명유리내면용다이렉트접착열전사지와 양면접착열전사지를 이용하여 평면 열전사기에서 제조된 열전사 접합 무늬칼라 유리판제 및 이것의 제조방법에 관한 것으로써, 평면 열 전사기에서 열전사 접합의 생산공정을 보다 간략히 할 수 있고 강력한 접착력으로 응력이 강화된 반 영구적인 기능을 가지는 열전사 접합 무늬칼라 유리판제를 생산할 수 있는 것이다. 다시 말해서, 본 발명에 따르면 평면 열 전사기에서 다양한 무늬칼라를 빠르게 전사 프린트하는 것과 아울러 무늬칼라 유리판제의 접합 공정을 개선시킴으로써, 제품의 생산성과 제조의 작업성을 향상시킬 수 있고, 투명 유리판제에 보다 향상된 기능을 제공할 수 있으며, 생산공정 단축에 따른 제조설비 절감과 함께 환경친화적인 불연 건축 내, 외장제를 반영구적으로 생산할 수 있는 효과가 있다. That is, the present invention relates to a thermal transfer laminated color glass plate and a method of manufacturing the same, which can exhibit various patterns between opposing transparent glass plates, and in particular, using a direct adhesive thermal transfer paper and a double-sided adhesive thermal transfer paper for transparent glass. The present invention relates to a thermal transfer bonded patterned glass sheet manufactured in a planar thermal transfer machine and a method for manufacturing the same, which further simplifies the production process of thermal transfer bonding in a planar thermal transfer machine and provides a semi-permanent stress reinforced by strong adhesive force. It is possible to produce a thermal transfer bonded color glass sheet having a phosphorus function. In other words, according to the present invention, it is possible to improve the productivity and workability of the product by improving the bonding process of the patterned color glass plate, as well as the rapid transfer printing of various patterned colors in the planar heat transfer machine. It can provide more advanced function, and it is possible to semi-permanently produce environmentally friendly non-flammable interior and exterior materials with the reduction of manufacturing facilities due to the shortening of production process.

Claims (15)

적어도 한쪽이 투명한 대향하는 투명유리판제(10) 사이에 다양한 무늬를 나타내기 위한 열전사층(11)을 포함하는 열전사 접합 무늬칼라 유리판제(18)에 있어서,In the thermal transfer bonding patterned color glass plate (18) comprising a thermal transfer layer (11) for displaying various patterns between opposing transparent glass plate (10) at least one of which is transparent, 상기 열전사층(11)은 운송시트의 탈거를 용이하게 할 수 있도록 하는 내면박리층(5)과, 열전사층이 흐무러지는 현상을 방지하기 위한 열경화도료층(6)과, 다양한 무늬칼라가 인쇄된 무늬칼라인쇄층(8)과, 상기 투명유리판제(10)의 내면에 열접착으로 열전사가 될 수 있도록 하는 투명접착층(9)을 포함하고, The thermal transfer layer 11 has an inner peeling layer 5 to facilitate the removal of the transport sheet, a thermosetting paint layer 6 for preventing the thermal transfer layer from blurring, and various pattern colors. And a transparent adhesive layer 9 to be thermally transferred by thermal adhesion to the inner surface of the transparent glass plate 10 and the transparent glass plate 10, 상기 내면박리층(5)이 평면 열전사기에서 투명유리판제(10)의 내면에 열접합이 될 수 있도록 하는 양면접착층(15)을 더 포함하여 이루어지는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18).Thermal transfer bonding patterned color glass plate, characterized in that the inner surface peeling layer 5 further comprises a double-sided adhesive layer 15 to be thermally bonded to the inner surface of the transparent glass plate 10 in a planar thermal transfer machine ( 18). 제1항에 있어서, 상기 열전사층(11)은 평면 열 전사기에 의해 투명접착층(9)을 통하여 투명유리판제(10)의 내면(12)에 열전사된 것이고, 그 이후에 상기 양면접착층(15)이 상기 내면박리층(5) 위에 열전사된 것임을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18).2. The thermal transfer layer (11) according to claim 1, wherein the thermal transfer layer (11) is thermally transferred to the inner surface (12) of the transparent glass plate (10) through the transparent adhesive layer (9) by a planar heat transfer device, and then the double-sided adhesive layer (15). 18) is a thermal transfer bonding patterned color glass plate, characterized in that the thermal transfer on the inner surface peeling layer (5). 제2항에 있어서, 상기 양면접착층(15)이 열전사되는 것은, 먼저 열전사층(11)이 열전사되고 난 다음에 상기 열전사층(11)의 내면박리층(5)에 형성되었던 운송시트(4)가 박리되고 나서 열전사되는 것임을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18).The transfer sheet of claim 2, wherein the double-sided adhesive layer 15 is thermally transferred, which is formed on the inner peeling layer 5 of the thermal transfer layer 11 after the thermal transfer layer 11 is thermally transferred. The thermal transfer bonding patterned color glass plate (18) characterized by the above-mentioned. 제1항에 있어서, 상기 양면접착층(15)은 양면접착층(15)과 내면슬립층(14) 및 운송시트(4)로 이루어진 양면접착열전사지(17)에 의해 열전사된 것임을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18).The thermoelectric transfer method of claim 1, wherein the double-sided adhesive layer 15 is thermally transferred by a double-sided adhesive thermal transfer paper 17 including a double-sided adhesive layer 15, an inner slip layer 14, and a transport sheet 4. Yarn bonding patterned color glass plate (18). 제1항에 있어서, 상기 열전사층(11)은 반사와 투명을 방지하여 무늬칼라를 선명하게 하기 위한 배경색을 가지는 은폐력층(7)을 더 포함하는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18).The method of claim 1, wherein the thermal transfer layer 11 further comprises a hiding layer (7) having a background color for sharpening the pattern color by preventing reflection and transparency of the thermal transfer bonding patterned color glass plate ( 18). 제5항에 있어서, 상기 양면접착층(15)은 불투명한 것임을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18).The heat transfer bonding patterned color glass plate (18) according to claim 5, wherein the double-sided adhesive layer (15) is opaque. 제1항에 있어서, 운송시트의 탈거를 용이하게 할 수 있도록 하는 내면박리층(5)과, 열전사층이 흐무러지는 현상을 방지하기 위한 열경화도료층(6)과, 상기 투명유리판제(10)의 내면에 열접착으로 열전사가 될 수 있도록 하는 투명접착층(9)으로 이루어진 열전사층(11)을 더 포함하는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18).The inner surface peeling layer (5) to facilitate the removal of the transport sheet, the thermosetting paint layer (6) to prevent the thermal transfer layer from blurring, and the transparent glass sheet (10). Thermal transfer bonding patterned color glass plate (18), characterized in that it further comprises a thermal transfer layer (11) made of a transparent adhesive layer (9) to be thermally transferred by thermal bonding on the inner surface. 적어도 한 쪽이 투명한 대향하는 투명유리판제(10) 사이에 다양한 무늬를 나타내기 위한 열전사층(11)을 포함하는 열전사 접합 무늬칼라 유리판제(18)에 있어서,In the thermal transfer bonding patterned color glass plate (18) comprising at least one of the thermal transfer layer (11) for showing various patterns between the transparent glass plate (10) facing each other, 상기 열전사층(11)은 운송시트의 탈거를 용이하게 할 수 있도록 하는 내면박리층(5)과, 열전사층이 흐무러지는 현상을 방지하기 위한 열경화도료층(6)과, 반사와 투명을 방지하여 무늬칼라를 선명하게 하기 위한 배경색을 가지는 은폐력층(7)과, 다양한 무늬칼라가 인쇄된 무늬칼라인쇄층(8)과, 상기 투명유리판제(10)의 내면에 열접착으로 열전사가될 수 있도록 하는 투명접착층(9)을 포함하고, The thermal transfer layer 11 has an inner peeling layer 5 to facilitate the removal of the transport sheet, a thermosetting paint layer 6 for preventing the thermal transfer layer from blurring, and reflection and transparency Concealment layer 7 having a background color for sharpening the pattern color, a patterned collar layer 8 having various pattern colors printed thereon, and thermal transfer to the inner surface of the transparent glass plate 10 by thermal bonding. Including a transparent adhesive layer (9), 이러한 열전사층(11)이 상기 투명유리판제(10)의 내면에 열전사된 무늬칼라유리판제(13) 2개가 내면박리층(5)을 통하여 서로 마주보는 상태로 평면 열전사기에서 열전사 접합이 될 수 있도록 하는 양면접착층(15)을 더 포함하여 이루어지는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18).The thermal transfer layer 11 is thermally bonded in a planar thermal transfer machine in a state in which two color-coated glass plates 13 thermally transferred to the inner surface of the transparent glass plate 10 face each other through the inner surface peeling layer 5. Thermal transfer bonding patterned color glass plate 18, characterized in that it further comprises a double-sided adhesive layer 15 to be made. 제8항에 있어서, 상기 양면접착층(15)과 상기 열전사층(11)의 내면박리층(5), 열경화도료층(6), 은폐력층(7), 무늬칼라인쇄층(8) 및 투명접착층(9)은 순차적으로 적층되어 이루어진 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18).The inner surface peeling layer (5) of the double-sided adhesive layer (15) and the thermal transfer layer (11), the thermosetting paint layer (6), the concealing force layer (7), the patterned calender chain layer (8) and the transparent The thermal transfer bonding patterned color glass plate 18, characterized in that the adhesive layer 9 is sequentially laminated. 적어도 한쪽이 투명한 대향하는 투명유리판제(10) 사이에 다양한 무늬를 나타내기 위한 열전사층(11)을 포함하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법에 있어서,In the manufacturing method of the thermal transfer bonding patterned color glass plate 18 which includes the thermal transfer layer 11 for showing various patterns between the transparent glass plate 10 which opposes at least one side, 상기 열전사층(11)과 운송시트(4)로 이루어진 투명유리내면용다이렉트접착열전사지(1)를 투명유리판제(10)의 내면에 1차 열전사시키는 단계;Primary thermal transfer of the direct adhesive thermal transfer paper (1) for the inner surface of the transparent glass made of the thermal transfer layer (11) and the transport sheet (4) to the inner surface of the transparent glass plate (10); 상기 운송시트(4)를 1차 박리하는 단계;First peeling the transport sheet (4); 상기 운송시트(4)가 박리된 열전사층(11)에 양면접착층(15)과 내면슬립층(14) 및 운송시트(4)로 이루어진 양면접착열전사지(17)를 2차 열전사시키는 단계;Performing a second thermal transfer of the double-sided adhesive thermal transfer paper (17) consisting of the double-sided adhesive layer (15), the inner slip layer (14) and the transfer sheet (4) to the thermal transfer layer (11) from which the transport sheet (4) has been peeled off; 상기 내면슬립층(14) 및 운송시트(4)를 2차 박리하는 단계; 및Secondary peeling the inner slip layer 14 and the transport sheet 4; And 상기 내면슬립층(14) 및 운송시트(4)가 박리된 양면접착층(15)에 투명유리판제(10)를 부착시키고 평면 열전사기에서 열전사 방법으로 접합시키는 단계;를 포함하는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법.And attaching the transparent glass plate 10 to the double-sided adhesive layer 15 on which the inner slip layer 14 and the transport sheet 4 are peeled off, and bonding the transparent glass plate 10 by a thermal transfer method in a planar thermal transfer machine. The manufacturing method of the thermal transfer bonding patterned glass plate (18). 제10항에 있어서, 상기 열전사층(11)은 운송시트의 탈거를 용이하게 할 수 있도록 하는 내면박리층(5)과, 열전사층이 흐무러지는 현상을 방지하기 위한 열경화도료층(6)과, 다양한 무늬칼라가 인쇄된 무늬칼라인쇄층(8)과, 상기 투명유리판제(10)의 내면에 열접착될 수 있도록 하는 투명접착층(9)을 포함하여 이루어진 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법.The thermal transfer layer (11) according to claim 10, wherein the thermal transfer layer (11) includes an inner peeling layer (5) for facilitating removal of the transport sheet, and a thermosetting paint layer (6) for preventing the thermal transfer layer from becoming cloudy. , A thermal transfer bonding patterned color comprising a patterned collar layer (8) printed with various pattern colors and a transparent adhesive layer (9) to be thermally bonded to the inner surface of the transparent glass plate (10) The manufacturing method of the glass plate 18. 제10항에 있어서, 상기 운송시트(4)는 시트(2)와 상기 시트(2)의 배면에 열전사지의 브록킹 방지를 위하여 형성된 배면슬립층(3)으로 이루어진 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법.The thermal transfer bonding according to claim 10, wherein the transport sheet (4) comprises a sheet (2) and a back slip layer (3) formed on the back surface of the sheet (2) to prevent blocking of thermal transfer paper. The manufacturing method of the patterned color glass plate (18). 적어도 한쪽이 투명한 대향하는 투명유리판제(10) 사이에 다양한 무늬를 나타내기 위한 열전사층(11)을 포함하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법에 있어서,In the manufacturing method of the thermal transfer bonding patterned color glass plate 18 which includes the thermal transfer layer 11 for showing various patterns between the transparent glass plate 10 which opposes at least one side, 상기 열전사층(11)과 운송시트(4)로 이루어진 투명유리내면용다이렉트접착열전사지(1)를 투명유리판제(10)의 내면에 1차 열전사시키는 단계;Primary thermal transfer of the direct adhesive thermal transfer paper (1) for the inner surface of the transparent glass made of the thermal transfer layer (11) and the transport sheet (4) to the inner surface of the transparent glass plate (10); 상기 운송시트(4)를 1차 박리하는 단계;First peeling the transport sheet (4); 상기 운송시트(4)가 박리된 열전사층(11)에 무늬칼라인쇄층(8)이 없는 열전 사층(11)과 운송시트(4)로 이루어진 투명유리내면용다이렉트접착열전사지(1)를 2차 열전사시키는 단계;The direct adhesive thermal transfer paper 1 for the transparent glass inner surface which consists of the heat transfer layer 11 and the transport sheet 4 which do not have the patterned chain layer 8 in the heat transfer layer 11 in which the said transport sheet 4 was peeled off was carried out. Secondary thermal transfer; 상기 운송시트(4)를 2차 박리하는 단계; Secondary peeling the transport sheet (4); 상기 운송시트(4)가 박리된 열전사층(11)에 양면접착층(15)과 내면슬립층(14) 및 운송시트(4)로 이루어진 양면접착열전사지(17)를 3차 열전사시키는 단계;Tertiary thermal transfer of a double-sided adhesive thermal transfer paper (17) consisting of a double-sided adhesive layer (15), an inner slip layer (14) and a transfer sheet (4) to the thermal transfer layer (11) from which the transport sheet (4) has been peeled off; 상기 내면슬립층(14) 및 운송시트(4)를 3차 박리하는 단계; Tertiary peeling the inner slip layer 14 and the transport sheet 4; 상기 운송시트(4)가 박리된 양면접착층(15)에 투명유리판제(10)를 부착시키고 평면 열전사기에서 열전사 방법으로 접합시키는 단계;를 포함하는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법.Attaching the transparent glass plate 10 to the double-sided adhesive layer 15 on which the transport sheet 4 has been peeled off, and bonding the transparent glass plate 10 to each other by a thermal transfer method in a planar thermal transfer machine. (18) The manufacturing method. 적어도 한쪽이 투명한 대향하는 투명유리판제(10) 사이에 다양한 무늬를 나타내기 위한 열전사층(11)을 포함하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법에 있어서,In the manufacturing method of the thermal transfer bonding patterned color glass plate 18 which includes the thermal transfer layer 11 for showing various patterns between the transparent glass plate 10 which opposes at least one side, 상기 열전사층(11)과 운송시트(4)로 이루어진 투명유리내면용다이렉트접착열전사지(1)를 투명유리판제(10)의 내면에 1차 열전사시켜서 무늬칼라유리판제(13)를 제조하는 단계;The transparent glass inner direct adhesive thermal transfer paper 1 composed of the thermal transfer layer 11 and the transport sheet 4 is primarily thermally transferred to the inner surface of the transparent glass plate 10 to produce a patterned color glass plate 13. step; 상기 무늬칼라유리판제(13)의 운송시트(4)를 1차 박리하는 단계;Primary peeling the transport sheet (4) of the patterned color glass sheet (13); 상기 운송시트(4)가 박리된 무늬칼라유리판제(13)의 열전사층(11)에 양면접착층(15)과 내면슬립층(14) 및 운송시트(4)로 이루어진 양면접착열전사지(17)를 2 차 열전사시키는 단계;The double-sided adhesive thermal transfer paper 17 comprising a double-sided adhesive layer 15, an inner slip layer 14, and a transfer sheet 4 on the thermal transfer layer 11 of the patterned color glass plate 13 on which the transfer sheet 4 is peeled off. Secondary thermal transfer; 상기 내면슬립층(14) 및 운송시트(4)를 2차 박리하는 단계; Secondary peeling the inner slip layer 14 and the transport sheet 4; 상기 내면슬립층(14) 및 운송시트(4)가 박리된 양면접착층(15)에 상기 운송시트(4)가 박리된 또 다른 무늬칼라유리판제(13)를 부착시키고 평면 열전사기에서 열전사 방법으로 접합시키는 단계;를 포함하는 것을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법.Attaching another patterned color glass plate 13 on which the transport sheet 4 was peeled to the double-sided adhesive layer 15 on which the inner slip layer 14 and the transport sheet 4 were peeled off, and thermal transfer method in a planar thermal transfer machine. The method of manufacturing a thermal transfer bonding patterned color glass plate (18) comprising a. 제10항 내지 제14항 중 어느 한 항에 있어서, 상기 평면 열전사기에서 열전사 방법으로 접합시키는 것은,The method according to any one of claims 10 to 14, wherein joining by the thermal transfer method in the planar thermal transfer machine, 상기 투명유리판제(10) 또는 무늬칼라유리판제(13)가 부착된 열전사 접합 무늬칼라 유리판제(18)를 100℃ 내지 130℃의 온도 범위 내로 예열하는 단계; 및Preheating the thermal transfer bonded patterned glass plate 18 having the transparent glass plate 10 or the patterned color glass plate 13 attached thereto within a temperature range of 100 ° C. to 130 ° C .; And 상기 예열된 열전사 접합 무늬칼라 유리판제(18)를 평면 열 전사기에서 180℃ 내지 220℃의 온도 범위로 예열된 탄성고무롤러를 이용하여 순간적으로 압착회전시키는 단계;를 거치는 것임을 특징으로 하는 열전사 접합 무늬칼라 유리판제(18)의 제조방법.Thermally bonding the preheated thermal transfer bonded patterned glass plate 18 using an elastic rubber roller preheated to a temperature range of 180 ° C. to 220 ° C. in a planar heat transfer machine. The manufacturing method of the yarn bonded pattern color glass plate (18).
KR1020060025970A 2006-03-22 2006-03-22 Heat transfer joining pattern color glass plate and manufacturing method thereof KR100740011B1 (en)