KR100732435B1 - Coat material for construction - Google Patents
Coat material for construction Download PDFInfo
- Publication number
- KR100732435B1 KR100732435B1 KR1020070008184A KR20070008184A KR100732435B1 KR 100732435 B1 KR100732435 B1 KR 100732435B1 KR 1020070008184 A KR1020070008184 A KR 1020070008184A KR 20070008184 A KR20070008184 A KR 20070008184A KR 100732435 B1 KR100732435 B1 KR 100732435B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- concentrated
- coating material
- oil
- charcoal
- Prior art date
Abstract
Description
본 발명은 건축마감재용 바름재에 관한 것으로서, 보다 상세하게는 천연물질로만 구성되는 접착수단으로서의 바름재 조성물 및 이를 이용한 것으로서 유해물질의 정화작용 등의 기능이 구비되는 건축마감재용 바름재에 관한 것이다. The present invention relates to a coating material for building finishing materials, and more particularly, to a coating material composition as an adhesive means composed only of natural materials and to a building finishing material having a function of purifying harmful substances by using the same. .
생태환경의 악화에 따른 경계의식과 함께 주거환경에 관한 문제도 큰 사회적 이슈가 된지 오래다. 도시의 고밀도화에 따른 대기오염, 신축건물에서 방출되는 각종의 유해물질에 의한 폐해를 최소화하기 위한 노력이 진행되어 왔다. 특히 근래에 들어 웰빙(well-being)붐, 아토피 질환의 심각성 등으로 인해 그러한 노력에 박차가 가해지고 있는 실정이다. Along with the alertness of the deteriorating ecological environment, the issue of residential environment has long been a big social issue. Efforts have been made to minimize the damage caused by air pollution and various harmful substances emitted from new buildings due to the high density of cities. In recent years, such efforts are being accelerated due to the well-being boom and the seriousness of atopic diseases.
예를 들면 주거생활의 근거인 아파트가 신축되는 경우에 있어, 일명 "새집증후군"이 입주자의 건강을 크게 위협하는 문제로 된다. "새집증후군"은 보통 건물신축에 필요적으로 사용되는 시멘트 몰탈, 방음·단열재, 각종의 페인트, 접착제 등의 화학제품으로부터 야기된다. 이러한 문제를 방지하기 위한 안이 다양하게 제안된바 있는데, 대표적으로는 액상의 물질을 건축용 마감재의 표면에 도포하는 방식, 활성탄과 같이 실내에 유치시켜 놓는 방식, 실내공기를 강제순환시켜가며 정화하는 방식 등이 있다. For example, when a new apartment is built on the basis of residential life, so-called "new house syndrome" is a problem that greatly threatens the health of the tenants. The "Sick House Syndrome" is caused by chemical products such as cement mortar, sound insulation and insulation, various paints and adhesives, which are usually used for building construction. Various proposals have been made to prevent such problems, typically, by applying a liquid material to the surface of the building finishing material, by placing it in the room such as activated carbon, and by purifying the indoor air by forced circulation. Etc.
그중 첫째 방식으로서 국내 특허등록 10-0625688호, 10-0651265에는 도료조성물, 코팅제가 각각 개시된바 있다. 그 내용을 보면 모두 숯이 첨가제로 이용되고 있다. 숯의 기능, 효과는 이미 사회적으로 많은 실험을 거쳐 인정된바 있으므로 그에 따른 효과를 의도한 것이다. 그러나 숯을 사용함에 있어서의 가장 큰 문제점은 도료 또는 코팅제의 벽면 접착성이 약하다는데 있다. 비록 나름대로의 방식으로 숯과 도료의 결합력을 높이고는 있지만, 도료의 접착기능을 수행하는 바인더 자체는 클로로프렌, 폴리초산비닐, 폴리아크릴산에스테르 등의 화학제품이 그대로 이용되고 있다. 즉, 숯 또는 기타 환경에 유익한 다른 물질이 도료첨가제로 사용되고 있기는 하지만 바인더는 그대로 사용되고 있기 때문에 언급된 "새집증후군"의 문제가 완전히 제거되었다고 단정할 수는 없다. Among them, as a first method, Korean Patent Registration Nos. 10-0625688 and 10-0651265 disclose paint compositions and coating agents, respectively. In all, charcoal is used as an additive. The function and effect of charcoal have already been recognized through a number of social experiments, so the effect is intended. However, the biggest problem in using charcoal is that the wall adhesion of the paint or coating is weak. Although the bonding strength between the charcoal and the paint is increased in its own way, the binder itself, which performs the adhesion function of the paint, is used as chemical products such as chloroprene, polyvinyl acetate, and polyacrylic acid ester. In other words, although charcoal or other environmentally beneficial materials are used as paint additives, the binder is used as it is, and thus, it cannot be concluded that the problem of "new house syndrome" mentioned is completely eliminated.
위와 같은 문제에 대한 본 발명의 목적은, 자연친화적인 천연물질만의 배합에 의한 피막형성용 바름재 조성물을 제공하는 것에 있다. 또한 신축건물로부터 발산되는 각종의 유해물질을 차단하거나 또는 실내의 공기를 자체적으로 정화할 수 있는 기능을 가지는 건축마감재용 바름재를 제공하며, 더 나아가 인체에 유용한 소재를 부가적으로 첨가함으로써 기능성을 더욱 향상시킬 수 있는 건축마감재용 바름재를 제공하는 것에 본 발명의 다른 목적이 있다. An object of the present invention for the above problems is to provide a coating material composition for forming a film by blending only natural-friendly natural materials. In addition, it provides a coating material for building finishing materials that has the function of blocking various harmful substances emitted from new buildings or purifying the air in the room itself, and furthermore, by adding additional useful materials to the human body, Another object of the present invention is to provide a coating material for building finishing materials that can be further improved.
위와 같은 문제는 목적물에 도포시 피막을 형성하고 접착성능을 발휘하기 위한 수단으로서, 농축된 파파야유(papaya oil)와 농축된 야자수 수액의 혼합액을 포함하는 것을 특징으로 하는 건축마감재용 바름재에 의해 달성된다. 여기서, 상기 파파야유(papaya oil)와 야자수 수액의 배합비는 1.5 ~ 3.0 : 1의 중량비이며, 상기 혼합액은 바름재 전체 중량에 대하여 50~90중량%가 되게끔 첨가되는 것을 특징으로 한다. The above problem is a means for forming a film and applying the adhesive performance when applied to the target object, by the building material finish coating material, characterized in that it comprises a mixture of concentrated papaya oil and concentrated palm sap Is achieved. Here, the blending ratio of papaya oil (palaya oil) and palm sap is a weight ratio of 1.5 to 3.0: 1, the mixture is characterized in that it is added to 50 to 90% by weight relative to the total weight of the coating material.
본 발명의 다른 목적은, 분상(粉狀)의 숯 25~45중량%, 농축된 파아야유(papaya oil) 30~50중량%, 농축된 야자수 수액 10~30중량%가 교반에 의해 혼합 형성된 건축마감재용 바름재에 의해 달성된다. Another object of the present invention, 25 to 45% by weight of powdered charcoal, 30 to 50% by weight of concentrated papaya oil, 10 to 30% by weight of concentrated palm sap mixed by stirring Achieved by building finishes.
본 발명의 또 다른 목적은, 농축된 파아야유(papaya oil) 30~50중량%, 농축된 야자수 수액 10~30중량%, 및 옥, 황토, 제오라이트(zeolite) 또는 게르마늄과 같은 기능성 소재중 하나 이상이 전체 중량에 대하여 20~40중량%가 되도록 첨가된 건축마감재용 바름재에 의해 달성된다. Another object of the present invention is one of 30 to 50% by weight of concentrated papaya oil, 10 to 30% by weight of concentrated palm sap, and one of functional materials such as jade, ocher, zeolite or germanium. The above is achieved by the coating material for building finishing materials added so as to be 20 to 40% by weight based on the total weight.
이하, 본 발명의 실시예를 더욱 상세하게 설명한다. 본 발명은 천연재료에 의한 바름재의 조성물을 제시하고 있다. 이는 기존 도료 등에서 바인더(binder) 및/또는 증점제의 기능을 하는 것으로서, 목적물에 도포시 피막을 형성하며 접착기능을 발휘하도록 하는 것이다. 그 구성은 농축된 파파야유(papaya oil)와 농축된 야 자수 수액이 중량비가 1.5 ~ 3.0 : 1, 바람직하게는 2 : 1 이 되도록 첨가되어 있는 것을 특징으로 한다. 이 파아야유와 야자수 수액의 배합물이 조성물 전체 중량에 대하여 50~90중량%를 차지하도록 함이 바람직하다. 바름재 조성물은 색상을 내기 위한 안료를 포함할 수 있으며, 사용 용도에 따라 다양한 천연성분이 선택적으로 포함될 수 있다. Hereinafter, embodiments of the present invention will be described in more detail. The present invention proposes a composition of a coating material made of natural materials. This is to function as a binder (binder) and / or thickener in the existing paint, such as to form a film when applied to the target material to exhibit an adhesive function. The constitution is characterized in that the concentrated papaya oil and the concentrated palm sap are added in a weight ratio of 1.5 to 3.0: 1, preferably 2: 1. It is preferable that the blend of the palm oil and palm sap accounts for 50 to 90% by weight based on the total weight of the composition. The coating material composition may include a pigment for producing a color, and various natural ingredients may be optionally included depending on the use purpose.
파파야(papaya)는 카리카과(科 Caricaceae)에 속하는 카리카 파파이아(Carica papaya)의 즙이 많은 열매로서, 그의 나무는 열대 전역과 아열대의 따뜻한 지역에서 재배되고 있다. 파파야는 식사용으로 흔히 쓰이며, 샐러드·파이·쥬스·당과 등을 만드는 데도 쓰이는 것이다. Papaya is the succulent fruit of Carica papaya belonging to the genus Caricaceae, whose trees are cultivated throughout the tropics and subtropical warm regions. Papaya is commonly used for meals, and is used to make salads, pies, juices, sweets, and so on.
본 발명에서 사용되는 파파야유(papaya oil)는 파파야열매를 파쇄하여 오일을 채취한후 필터로써 불순물을 분리 제거한 후, 200~300℃의 온도로 24~48시간 가열 및 농축시킨 후, 숙성이 잘 이루어지는 온도인 3~7℃의 온도에서 5~10일간 숙성시킴으로써 준비된다. 이렇게 농축된 파파야유는 젤(gel)과 같은 성상을 갖게 된다. 고온에서 숙성시킬 경우 변질될 수 있고, 저온에서 숙성시킬 경우 숙성이 잘 이루어지지 않을 수 있다. 파파야유의 농축 및 숙성과정은 후술되는 실시예에서도 동일하게 적용된다.Papaya oil used in the present invention, after crushing the papaya fruit to collect the oil to remove the impurities by a filter, and then heated and concentrated for 24 to 48 hours at a temperature of 200 ~ 300 ℃, well aged It prepares by aging for 5 to 10 days at the temperature of 3-7 degreeC which is the temperature which becomes. This concentrated papaya oil has a gel-like property. When aged at high temperature may be deteriorated, when aged at low temperature may not be well aged. The process of concentrating and ripening papaya oil is equally applicable to the examples described below.
야자수 수액은 야자수를 파쇄한 후, 압축하여 수액을 추출한후, 필터로 이물질을 분리 제거하고, 200~300℃의 온도에서 약 24~48시간 동안 가열 및 농축시킴으로써 준비된다. 이의 기능은 바름재의 접착성능과 접착강도를 보조 또는 향상시키기 위함이다. Palm sap is prepared by crushing palm trees, compressing and extracting sap, separating and removing foreign matter with a filter, and heating and concentrating at a temperature of 200 to 300 ° C. for about 24 to 48 hours. Its function is to assist or improve the adhesion performance and adhesion strength of the coating material.
이하, 위의 조성물을 이용한 건축마감재용 바름재의 제조예를 설명한다. 우선은 기능성 제품으로 널리 사용되고 있는 숯이 첨가된 경우를 설명한다.Hereinafter, the manufacturing example of the coating material for building finish using the above composition. First, the case where the char is widely used as a functional product is added.
숯으로는 참숯이 사용되는데, 파쇄기에 의해 30~70nm의 입경으로 1차 분쇄된 후 진동분쇄기에 의해 300~700 매쉬(mash)의 입도로 분말화된 것이 사용된다. 숯의 기능, 효과는 종래 여러 실험에 의해 입증된 것으로서 그에 대한 상세한 설명은 생략한다. Charcoal is used as charcoal, which is first pulverized to a particle size of 30 to 70 nm by a crusher, and then powdered to a particle size of 300 to 700 mash by a vibration crusher. The function and effect of charcoal have been proved by various experiments in the past, and a detailed description thereof will be omitted.
숯이 함유량이 적으면 그에 따른 효과가 미흡할 것이고 과다하게 되면 바름재의 표면 접착력 등에 문제가 생기게 된다. 숯의 함유량은 바람직하게는 혼합물 총중량에 대하여 35중량%가 최적이다. If the content of charcoal is low, the effect thereof will be insufficient. If excessive, the problem of surface adhesion of the coating material will occur. The content of charcoal is preferably 35% by weight with respect to the total weight of the mixture.
파파야유(papaya oil)는 파파야열매를 파쇄하여 오일을 채취한후 200~300℃의 온도로 처리하여 농축시킨 후, 3~7℃의 온도에서 5~10일간 숙성시킴으로써 준비된다. 파파야유의 최적 함유량은 혼합물 총중량에 대하여 41중량%이다.Papaya oil is prepared by crushing papaya fruit, collecting oil, treating it at a temperature of 200 to 300 ° C, concentrating, and then aging at a temperature of 3 to 7 ° C for 5 to 10 days. The optimum content of papaya oil is 41% by weight based on the total weight of the mixture.
야자수 수액은 야자수를 파쇄한 후, 압축하여 농축액을 추출하여 5~10일간 수분을 분리제거하고 200~300℃의 온도로 열처리에 의해 준비된다. 야자수 수액의 최적 함유량은 혼합물 총중량에 대하여 18중량%이다. Palm sap is crushed palm tree, compressed to extract the concentrated solution to remove the water for 5-10 days and is prepared by heat treatment at a temperature of 200 ~ 300 ℃. The optimum content of palm sap is 18% by weight relative to the total weight of the mixture.
위에 언급된 각 성분의 배합비는 발명자의 수많은 실험을 통해 얻어진 것이다.The compounding ratio of each of the above-mentioned components is obtained through numerous experiments of the inventors.
본 발명의 바름재에 관련된 다른 실시예를 설명한다. 위 혼합물에 석재의 물리적 성질을 부여하기 위한 보조재가 혼합물의 전체 중량에 대하여 1~10중량%가 되 도록 더 혼합될 수 있다. 보조재로는 게르마늄, 옥(玉)이 대표적으로 선택될 수 있다. Another embodiment related to the coating material of the present invention will be described. Auxiliary materials for imparting the physical properties of the stone to the mixture may be further mixed to be from 1 to 10% by weight relative to the total weight of the mixture. As an auxiliary material, germanium and jade may be representatively selected.
게르마늄은 회백색 광택을 가진 반금속 원소로서, 기능적으로는 사회 일반에 알려진 게르마늄의 효능(예를 들면, 체질의 산성화 방지, 세포기관의 노화방지, 면역력 활성화 등)을 부여하기 위함이다. 게르마늄은 400~600 매쉬, 바람직하게는 500매쉬의 입도로 분쇄된 상태로 혼합된다. 이는 숯과 더불어 인체 또는 환경 정화에 기여하기 위한 것으로서, 분상의 옥(玉) 등 다른 물질로 대체되거나 또는 병용될 수 있다. Germanium is a semi-metallic element with an off-white gloss, and is functionally intended to confer the effects of germanium known to society in general (for example, preventing acidification of the constitution, anti-aging of organelles, activation of immunity, etc.). Germanium is mixed in a pulverized state at a particle size of 400 to 600 mesh, preferably 500 mesh. This is for contributing to the human body or environmental purification along with charcoal, and may be replaced or combined with other materials such as powdery jade.
한편, 본 발명의 바름재에서 숯이 게르마늄 또는 옥으로 대체될 수 있음은 물론이며, 황토, 제오라리트(zeolite) 등의 기능성 소재가 부가될 수도 있다. Meanwhile, the charcoal may be replaced with germanium or jade in the coating material of the present invention, and a functional material such as ocher or zeolite may be added.
위의 혼합물은 분상(粉狀)의 숯 및/또는 게르마늄 등의 첨가물이 파파야유와 야자수 수액의 혼합액에 고르게 분산되도록 교반기에 의해 약 1700rpm 의 회전속도로 교반된다. The above mixture is stirred at a rotational speed of about 1700 rpm by a stirrer so that additives such as powdered char and / or germanium are evenly dispersed in the mixture of papaya oil and palm sap.
본 발명에 따른 바름재는 페인트와 같이 컴프레서로 작동되는 스프레이건에 의해 분무되는 방식으로 목적물에 도포되거나, 붓 또는 롤러에 의해 도포될 수도 있다. 형성되는 피막의 두께는 0.1 ~ 1mm 의 범위에서 사용환경에 따라 선택될 수 있다. 본 발명의 바름재는 주거공간의 실내 마감재로 바닥, 벽, 천정 등에 도포되거나 가구 등에도 적용될 수 있다. 바름재의 물리적 성능시험 결과를 대표적인 사항만 열거하기로 한다. The coating material according to the invention may be applied to the object in a manner sprayed by a spray gun operated by a compressor such as paint, or may be applied by a brush or roller. The thickness of the formed film can be selected according to the use environment in the range of 0.1 ~ 1mm. The coating material of the present invention may be applied to a floor, a wall, a ceiling, or the like as an interior finishing material of a living space, or may be applied to furniture. The physical performance test results of the baring materials will be listed only.
위와 같이 본 발명에 의한 바름재는 건축물 내장재용으로서 기능상의 문제가 전혀 없는 것으로 나타났다. 본 발명의 바름재는 시멘트 몰탈, 금속, 목재 등 각종의 피접착물 모두에 강한 접착력을 보였다.As described above, the coating material according to the present invention has been found to have no functional problem for building interior materials. The coating material of the present invention showed strong adhesion to all kinds of adherends such as cement mortar, metal, wood, and the like.
건물 내벽에 도포되는 경우 그 상면에 벽지가 도배될 수 있는데, 이 경우에도 벽지를 통해 실내공기의 정화작용을 할 수 있음이 나타났다. 숯을 대신하여 또는 숯의 함량을 낮추고 소정의 천연안료를 배합하는 경우라면, 본 발명의 바름재는 미감을 발휘할 수 있게 되기 때문에 건축용마감재에 상도 코팅용으로도 사용될 수 있을 것이다. 또한, 파파야 또는 야자수의 천연향에 의한 아로마테라피의 효과도 득할 수 있을 것이다. When applied to the inner wall of the building can be wallpapered on the upper surface, even in this case it was shown that the indoor air can be purified through the wallpaper. If instead of charcoal or lower the content of charcoal and formulated with a predetermined natural pigment, the coating material of the present invention will be able to be used as a top coat in a building finishing material because it can exhibit aesthetics. In addition, the effect of aromatherapy by the natural aroma of papaya or palm tree will also be able to be obtained.
기타, 당업자는 위에 개시된 기술내용을 바탕으로 하여 본 발명의 기술사상의 범위 내에서 다양한 변형실시를 할 수 있을 것이다. 그 가운데, 첨가물의 선택 및 각 성분의 배합비는 충분히 응용이 가능한 사항일 것이다. In addition, those skilled in the art will be able to make various modifications within the scope of the technical idea of the present invention based on the technical contents disclosed above. Among them, the choice of additives and the mixing ratio of each component will be a matter that can be sufficiently applied.
위와 같은 구성에 의하면, 천연물질에 의한 접착수단으로서의 바름재 조성물이 제공된다. 또한, 신축건물의 벽면, 내장재 등 마감재로부터 나오는 유해물질을 차단하거나 또는 실내공기를 정화할 수 있으며, 나아가 인체에 유익한 작용을 하는 기능성 바름재가 제공된다. 본 발명에 의하면 도료 등의 원료로서 화학제품이 전혀사용되지 아니하여 종래의 "새집증후군" 문제를 완전히 해결할 수 있는 기능성 바름재가 제공된다. According to the above configuration, there is provided a coating material composition as an adhesive means by a natural material. In addition, it is possible to block harmful substances from finishing materials such as walls, interior materials of new buildings or to clean indoor air, and furthermore, a functional coating material is provided that has a beneficial effect on the human body. According to the present invention, there is provided a functional coating material that can completely solve the problem of conventional "birdhouse syndrome" because no chemical product is used as a raw material such as paint.
Claims (5)