KR100527282B1 - Multi-functional flooring that mixed properly the elastic poly-urethane and the epoxy having abrasion resistance and its construction method - Google Patents

Multi-functional flooring that mixed properly the elastic poly-urethane and the epoxy having abrasion resistance and its construction method Download PDF

Info

Publication number
KR100527282B1
KR100527282B1 KR10-2002-0064138A KR20020064138A KR100527282B1 KR 100527282 B1 KR100527282 B1 KR 100527282B1 KR 20020064138 A KR20020064138 A KR 20020064138A KR 100527282 B1 KR100527282 B1 KR 100527282B1
Authority
KR
South Korea
Prior art keywords
layer
flooring
urethane
epoxy resin
polyurethane
Prior art date
Application number
KR10-2002-0064138A
Other languages
Korean (ko)
Other versions
KR20040034080A (en
Inventor
유중근
Original Assignee
중앙방수기업주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 중앙방수기업주식회사 filed Critical 중앙방수기업주식회사
Priority to KR10-2002-0064138A priority Critical patent/KR100527282B1/en
Publication of KR20040034080A publication Critical patent/KR20040034080A/en
Application granted granted Critical
Publication of KR100527282B1 publication Critical patent/KR100527282B1/en

Abstract

본 발명은 탄성이 있는 폴리우레탄과 내마모성의 에폭시를 복합 적층한 다기능성 바닥마감재 및 그 시공방법에 관한 것으로, 그 목적은 누수발생, 패임, 들뜸, 균열, 박리, 마모층과 같은 바닥재의 기능저하 등이 발생하지 않도록 층간 구성물을 복합화시켜 바닥재 기능상향 및 사용상 내구성능을 연장시키고 보수비용을 절감시킴으로서 품질개선을 한층 높인 바닥마감재 및 그 시공방법을 제공하는데 있다. The present invention relates to a multi-functional floor finishing material and a method for constructing a composite laminated elastic polyurethane and wear-resistant epoxy, the object of which is the leakage of the flooring material, such as leakage, pitting, lifting, cracking, peeling, wear layer It is to provide a floor finishing material and its construction method to further improve the quality by increasing the improvement of flooring function and durability in use by reducing the cost of maintenance by compounding the interlayer composition to prevent such occurrence.

본 발명의 구성은 기초를 이루는 콘크리트 슬라브층(1)과 그 위에 형성되는 바닥재에 있어서, 상기 콘크리트 슬라브층(1) 위에 형성되는 접착성 및 침투성을 가진 유성 우레탄 프라이머층(9)과, 그 위에 도포된 탄성력 및 신축력을 가진 우레탄 바닥재층(10)과, 상기 층 위에 형성되는 내마모성, 접착성, 강도강화 기능을 가진 에폭시 레진 몰탈 바닥재층(11)과, 그 위에 도포되는 톱 코트층(12)의 순서로 적층된 구조를 특징으로 하는 탄성이 있는 폴리우레탄과 내마모성의 에폭시를 복합 적층한 다기능성 바닥마감재 및 그 시공방법을 기술적 요지로 한다.The construction of the present invention is the base concrete slab layer (1) and the flooring formed thereon, the adhesive and permeable oil-based urethane primer layer (9) formed on the concrete slab layer (1), and thereon Urethane flooring layer 10 having elasticity and elasticity applied, epoxy resin mortar flooring layer 11 having abrasion resistance, adhesiveness and strength enhancing function formed on the layer, and top coat layer 12 applied thereon Technical features of a multi-functional floor finishing material comprising a laminated composite of elastic polyurethane and abrasion resistant epoxy characterized by a laminated structure in the order of and a construction method thereof.

Description

탄성이 있는 폴리우레탄과 내마모성의 에폭시를 복합 적층한 다기능성 바닥마감재 및 그 시공방법{Multi-functional flooring that mixed properly the elastic poly-urethane and the epoxy having abrasion resistance and its construction method} Multi-functional flooring that mixed properly the elastic poly-urethane and the epoxy having abrasion resistance and its construction method}

본 발명은 건축물의 옥상이나 옥외주차장 및 건물지하층 내부주차장 바닥등에 시공되는 탄성이 있는 폴리우레탄과 내마모성의 에폭시를 복합 적층한 다기능성 바닥마감재 및 그 시공방법에 관한 것으로, 특히 바닥재의 각 층구조를 이루는 재료를 폴리우레탄과 에폭시로 복합사용 함으로서 서로의 장점을 극대화시킴으로서 기존 공법에서 문제시되는 제반의 약점을 보완함과 동시에 주차장 바닥재의 수명연장 및 방수 효과에도 뛰어난 성능이 발휘되는 다기능성 바닥재 및 그 시공방법에 관한 것이다.The present invention relates to a multi-functional floor finishing material laminated composite of elastic polyurethane and abrasion-resistant epoxy to be installed on the roof of the building or the floor of the outdoor parking lot and the basement floor of the building underground, and in particular, each layer structure of the flooring Multi-functional flooring material and its construction, which are excellent in extension of lifespan and waterproofing effect of parking lot flooring, while complementing the weak points of existing methods by maximizing each other's advantages by using polyurethane and epoxy composite materials. It is about a method.

종래의 주차장바닥 마감재 구조는 도 1과 도 2에서 도시되는 바와 같이 구성되어 있다. The conventional parking lot floor finisher structure is constructed as shown in Figs.

도 1의 경우는 콘크리트 슬라브층(1)의 상면에 접착용 우레탄 프라이머층(2)을 도포하고 그 위에 탄성력이 있는 1차 폴리우레탄 바닥재층(3)을 도포한 다음 약 24시간 이상 경화시킨 후 2차 폴리우레탄 바닥재층(4)을 재차 도포하여 총 두께 약 2.5~3.Omm 정도가 되도록 한다. 그 다음 우레탄 톱코트재(5)를 마감 도포하는 바닥구조로 이루어져 있다.In the case of Figure 1 after applying the adhesive urethane primer layer (2) to the upper surface of the concrete slab layer (1) and then the elastic primary polyurethane flooring layer (3) is applied thereon and then cured for about 24 hours or more The second polyurethane floor covering layer 4 is applied again so that the total thickness is about 2.5 to 3.0 mm. Next, the urethane topcoat material 5 is made of a bottom structure to finish coating.

도 2의 경우는 콘크리트 슬라브층(1)의 상면에 접착용 에폭시 프라이머층(6)을 도포하고 그 위에 내마모성이 있는 1차 에폭시수지 바닥재층(7)을 도포한 다음 약 24~48시간 이상 경화시킨 후 2차 에폭시 바닥재층(8)을 재차 도포하여 총 두께가 약 2.0~3.Omm 정도가 되도록 하여 바닥재를 마감하는 바닥구조로 이루어져 있다.In the case of FIG. 2, the epoxy epoxy layer 6 for adhesion is coated on the upper surface of the concrete slab layer 1, and the first epoxy resin flooring layer 7 having abrasion resistance is applied thereon, and then cured for about 24 to 48 hours. After the secondary epoxy flooring layer 8 is applied again, the total thickness is about 2.0 to 3.0mm and consists of a floor structure to finish the flooring.

상기와 같이 구성되는 종래의 방수구조는 사용용도가 주로 옥외 주차장이나 지하 주차장 바닥마감재로 사용되고 있기 때문에 대형 건축물의 경우 필연적으로 구조체의 신축, 팽창에 의한 콘크리트 슬라브층의 균열 압력에 직면하고 있으며 특히 차량이동, 주차 등에 따른 동적부가하중의 영향으로 바닥마감재의 피로성이 증대됨으로써 바닥 마감재가 쉽게 마모되거나 패임, 들뜸, 균열 등을 피할 수 없어 바닥 마감재로써 장기적인 내구성이 크게 떨어지고 있다.As the conventional waterproof structure configured as described above is mainly used as an outdoor parking lot or an underground parking lot floor finishing material, a large building inevitably faces cracking pressure of the concrete slab layer due to the expansion and expansion of the structure. As the fatigue of floor finishing materials increases due to the dynamic loads caused by movement and parking, the floor finishing materials can not be easily worn, or the dents, lifting, cracks, etc. cannot be avoided, and the long-term durability of the floor finishing materials is greatly reduced.

구체적으로 설명하면 도 1의 경우 폴리우레탄 바닥마감재 공법은 사용재료가 탄성력이 풍부한 성질을 지니고 있으며 대표적 재료성질을 살펴보면 신축율이 450~600% 정도의 신축성을 가지고 있으며 강도를 나타내는 경도지수가 55~75 정도이다.Specifically, in the case of Figure 1 polyurethane floor finishing method has a property that the material used is rich in elasticity, and looking at the typical material properties has a stretch ratio of about 450 ~ 600% elasticity and hardness index of 55 ~ 75 or so.

이러한 재료의 기본성질을 살펴볼 때 도 1의 시공법은 차량이동이나 급제동에 대한 움직임이나 건축물의 신축, 팽창에 의한 거동 안정성에는 이점이 있으나, 그 반면에 바닥마감재 기능으로 가장 중요한 내마모성, 강도 면에서는 약해 차량이동시 급제동이나 바퀴돌림현상 등에 의해 바닥마감재의 표층이 쉽게 마모되거나 패임현상, 들뜸, 박리현상이 일어나기 때문에 사용 중 누수우려성이 높으며 아울러 수명이 단축되는 약점이 있다.When considering the basic properties of these materials, the construction method of Figure 1 has the advantage of the stability of the movement by moving or braking the vehicle, or the expansion and expansion of the building, while weak in terms of wear resistance and strength, which is the most important floor function function When the vehicle moves, the surface of the floor finishing material is easily worn out due to sudden braking or wheel turning, or the dent, lifting and peeling occur.

도 2의 경우는 강도 및 내마모성이 강한 에폭시 바닥마감재 공법의 대표적인 기본성질을 살펴보면 압축강도는 약 4OO~5OOkg/㎠ 정도이나 탄성력, 즉 신축성은 O에 가까운 정도로써 차량이동이나 주차시 내마모성은 우수하나 그 반면에 건축물의 균열추종성은 거의 없으며 차량 급제동시 피로파괴 현상에 약점이 있다.In the case of FIG. 2, the representative basic properties of the epoxy floor finishing method with strong strength and abrasion resistance are that the compressive strength is about 4OO-50,000 kg / ㎠, but the elasticity, that is, the elasticity is close to O, which is excellent in abrasion resistance when moving or parking a vehicle. On the other hand, there is little crack tracking of the building, and there is a weak point in fatigue breakdown during braking.

따라서 종래 도 1과 도 2의 시공방법은 사용환경상이나 사용목적에 요구성능을 모두 만족하지 못하고 상반된 약점을 지니고 있어 각각 단일공법으로 시공할 시 누수문제를 야기시킴과 동시에 바닥재의 기능이 쉽게 상실되는 문제점으로 사용시 건물의 가치하락이나 재산상 손실 및 미관까지 손상되는 문제점이 있었다.Therefore, the conventional construction method of FIGS. 1 and 2 does not satisfy all of the required performance in terms of use environment or purpose, and has opposite weaknesses, which causes leakage problems when the construction is performed in a single construction method. As a problem, there was a problem of deterioration of the value of buildings or damage to property and aesthetics.

상기와 같은 문제점을 해결하기 위한 본 발명의 목적은 누수발생, 패임, 들뜸, 균열, 박리, 마모층과 같은 바닥재의 기능저하 등이 발생하지 않도록 층간 구성물을 복합화시켜 바닥재 기능상향 및 사용상 내구성능을 연장시키고 보수비용을 절감시킴으로서 품질개선을 한층 높인 바닥마감재 및 그 시공방법을 제공하는데 있다.An object of the present invention for solving the above problems is to improve the flooring functionalities and durability in use by compounding the interlayer components to prevent the occurrence of leakage, depression, lifting, cracking, peeling, deterioration of the flooring material, such as wear layer. It is to provide a floor finishing material and its construction method which have improved quality by further extending and reducing maintenance cost.

상기와 같은 본 발명의 목적은 첫째 탄성력 즉 신축성이 있는 우수한 우레탄 도막층을 바닥재 하부면에 도포하여 구조체 슬라브의 거동시 발생하는 응력을 완화시켜 바닥재의 파단, 균열을 방지하여 주며, 둘째, 탄성층위에 내마모성, 접착성, 강도가 뛰어난 에폭시 레진몰탈 마감층을 복층화시킴으로서 차량이동시 패임, 박리, 균열을 방지함과 동시에 일정의 두께 약 3.O ~ 5.Omm를 얻을 수 있도록 하며, 셋째, 차량이동이나 사람, 물건 운반시 미끄럼을 방지하기 위해 에폭시와 규사(크기 약 5~6호)를 혼합 도포하여 논슬립성이 있도록 한 다음, 넷째, 바닥재의 미려한 색상을 연출시키기 위해 지정색의 톱코트재를 도포하여 마감하는 다기능성 복합 바닥마감재 구조로 바닥재의 성력화에 의한 장기내구수명 효과가 있고 논슬립성 기능을 부여하는 복합바닥재 구조 및 그 시공방법을 제공함으로써 달성된다. The object of the present invention as described above is to first apply an excellent urethane coating layer having elasticity, that is, elasticity on the bottom surface of the flooring material to relieve stress generated during the behavior of the structural slab to prevent fracture and cracking of the flooring material, and second, the elastic layer Epoxy resin mortar finish layer with excellent wear resistance, adhesiveness and strength on the top layer prevents pitting, peeling and cracking while moving the vehicle, and at the same time obtains a thickness of about 3.O to 5.Omm. Third, moving the vehicle Epoxy and silica sand (sizes 5 ~ 6) are mixed and applied to prevent slippage when transporting people, objects, and objects.Non fourth, a top color material of designated color is applied to produce a beautiful color of the flooring material. Multi-functional composite floor finish structure that is applied and finished, which has long-term durability life effect by strengthening floor materials and gives non-slip function By providing a reconstruction and its construction method.

상기한 바와 같은 목적을 달성하고 종래의 결점을 제거하기 위한 과제를 수행하는 본 발명의 실시예인 구성과 그 작용을 첨부도면에 연계시켜 상세히 설명하면 다음과 같다.When described in detail with reference to the accompanying drawings, the configuration and the operation of the embodiment of the present invention to achieve the object as described above and to perform the task for eliminating the conventional drawbacks.

도 3은 본 발명에 의한 다기능성 복합바닥구조를 나타내는 단면도를 도시하고 있는데, 하부로부터 설명하면 기초를 이루는 콘크리트 슬라브층(1)과, 그 위에 형성되는 접착성 및 침투성을 가진 유성 우레탄 프라이머층(9)과, 그 위에 도포된 탄성력 및 신축력을 가진 우레탄 바닥재층(10)과, 상기 층 위에 형성되는 내마모성, 접착성, 강도강화 기능을 가진 에폭시 레진 몰탈 바닥재층(11)과, 그 위에 도포되는 톱 코트층(12)의 순서로 적층된 구성을 가진다. Figure 3 shows a cross-sectional view showing a multifunctional composite floor structure according to the present invention, which will be described from the bottom of the concrete slab layer (1) to form a base, and an oil-based urethane primer layer having an adhesive and permeability formed thereon ( 9), the urethane flooring layer 10 having elasticity and elasticity applied thereon, the epoxy resin mortar flooring layer 11 having abrasion resistance, adhesiveness and strength enhancing function formed on the layer, and applied thereon It has the structure laminated | stacked in the order of the top coat layer 12. FIG.

상기 우레탄 바닥재층(10)은 주제인 우레탄과 경화제를 2:1로 혼합하여 사용한다. The urethane flooring layer 10 is used by mixing the main urethane and the curing agent 2: 1.

상기 우레탄 바닥재층(10)의 형성 두께는 1.O~1.5mm로 형성한다.The formation thickness of the urethane flooring layer 10 is formed to 1.O ~ 1.5mm.

상기 바닥재층에 사용되는 주제인 폴리우레탄 바닥재의 품질은 신축율이 약 450~500% 정도로 하며 경도는 약 65~75 정도의 성능을 지닌 재료를 사용한다.The quality of the polyurethane flooring material used in the flooring layer is about 450 ~ 500% of the stretch rate and the hardness of about 65 to 75 using a material having a performance of about.

상기 내마모성, 접착성, 강도강화 기능을 가진 에폭시 레진 몰탈 바닥재층(11)은 에폭시 수지와 규사(칼라규사 포함)는 1:4.5 ~ 5.O 비율로 혼합한다.The epoxy resin mortar flooring layer 11 having the abrasion resistance, adhesiveness, and strength enhancing function is mixed with epoxy resin and silica sand (including color silica) in a ratio of 1: 4.5 to 5.O.

상기 에폭시 레진 몰탈 바닥재층(11)의 두께는 3.O ~ 4.Omm 정도로 한다.The thickness of the epoxy resin mortar flooring layer 11 is about 3.O ~ 4.Omm.

상기 톱코트층(12)은 지정색을 롤러나 스프레이 등으로 살포한다.The top coat layer 12 sprays a designated color with a roller, a spray, or the like.

상기와 같은 본 발명 층구조의 시공방법 및 실시예를 자세히 설명하면 다음과 같다. Referring to the construction method and embodiment of the present invention layer structure in detail as follows.

본 발명은 콘크리트 슬라브층(1)의 상면에 접착성 및 침투성이 우수한 유성 우레탄 프라이머층(9)을 도포하고 그 위에 유용성 폴리우레탄 바닥재층(10)의 주제와 경화제를 2:1 비율로 혼합한 다음 고무헤라나 주걱 등으로 두께가 약 1.O~1.5mm가 형성되도록 도포한다.The present invention is coated with an oil-based urethane primer layer (9) having excellent adhesion and permeability on the upper surface of the concrete slab layer (1) and mixing the main agent and the curing agent of the oil-soluble polyurethane flooring layer (10) in a 2: 1 ratio. Next, apply a rubber spatula or spatula to form a thickness of about 1.O ~ 1.5mm.

이때 폴리우레탄 바닥재의 품질은 신축율이 약 450~500% 정도로 하며 경도는 약 65~75 정도의 성능을 지닌 재료를 사용한다. Polyurethane flooring material is about 450 ~ 500% elongation and hardness is about 65 ~ 75 .

폴리우레탄 바닥재층(10)을 시공한 위에 내마모성, 접착성, 강도 기능을 발현하여 에폭시층을 형성하는데 이때 시공방법은 에폭시 수지와 규사(칼라규사 포함)를 1:4.5 ~ 5.O 비율로 하여 전동 믹서기로 충분히 혼합한 다음 표준두께가 3.O ~ 4.Omm 정도 확보되도록 쇠흙손이나 전용장비를 이용하여 내마모성의 에폭시 레진 몰탈 바닥재층(11)을 형성한다.On top of the polyurethane flooring layer 10, an epoxy layer is formed by expressing abrasion resistance, adhesiveness, and strength functions. The construction method is epoxy resin and silica sand (including color silica) in a ratio of 1: 4.5 to 5.O. After mixing sufficiently with an electric blender, a wear-resistant epoxy resin mortar flooring layer 11 is formed by using a trowel or a dedicated device so that a standard thickness of 3.O to 4.Omm is secured.

그 다음 에폭시 레진 몰탈 바닥재층(11)이 경화되면 지정색의 톱코트층(12)을 롤러나 스프레이 등으로 살포하여 논슬립성, 내마모성, 강도, 신축성의 다기능성 복합 바닥재의 전공정이 완료된다.Then, when the epoxy resin mortar flooring layer 11 is cured, the top coat layer 12 of the designated color is sprayed with a roller or a spray to complete the entire process of the non-slip, abrasion resistance, strength and elasticity of the multifunctional composite flooring.

본 발명은 상술한 특정의 바람직한 실시예에 한정되지 아니하며, 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 누구든지 다양한 변형실시가 가능한 것은 물론이고, 그와 같은 변경은 청구범위 기재의 범위 내에 있게 된다. The present invention is not limited to the above-described specific preferred embodiments, and various modifications can be made by any person having ordinary skill in the art without departing from the gist of the present invention claimed in the claims. Of course, such changes will fall within the scope of the claims.

상기와 같이 본 발명은 각층의 재료를 복합사용 함으로서 서로의 장점을 극대화시킴으로서 기존 공법에서 문제시되는 제반의 약점을 보완함과 동시에 주차장 바닥재의 수명연장 및 방수 효과에도 뛰어난 성능이 발휘되는 다기능성 바닥재 및 그 시공방법으로, 건축물의 옥상이나 옥외주차장 및 건물지하층 내부주차장 바닥재가 논슬립성, 내마모성, 강도, 신축성의 다기능성을 가지게 되어 그 산업상 이용이 기대되는 유용한 발명인 것이다.As described above, the present invention maximizes the advantages of each other by using the materials of each layer, and complements the weak points of the existing methods, and at the same time, the multifunctional flooring material exhibits excellent performance in extending the life and waterproofing effect of the parking lot flooring. As a method of construction, the roof of the building or the floor of the outdoor parking lot and the basement floor of the building basement floor has a non-slip resistance, wear resistance, strength, and elasticity, which is a useful invention that is expected to be used industrially.

도 1은 종래의 바닥구조인 폴리우레탄 바닥재를 나타내는 단면도이고,1 is a cross-sectional view showing a polyurethane flooring which is a conventional floor structure,

도 2는 종래의 바닥구조인 에폭시 바닥재를 나타내는 단면도이며,Figure 2 is a cross-sectional view showing an epoxy flooring which is a conventional floor structure,

도 3은 본 발명에 의한 다기능성 복합바닥구조를 나타내는 단면도이다.3 is a cross-sectional view showing a multifunctional composite floor structure according to the present invention.

<도면의 주요부분에 대한 부호의 설명><Description of Symbols for Main Parts of Drawings>

(1) : 콘크리트 슬라브층 (2, 9) : 우레탄 프라이머층(1): concrete slab layer (2, 9): urethane primer layer

(3) : 1차 폴리우레탄 바닥재층 (4) : 2차 폴리우레탄 바닥재층(3): primary polyurethane flooring layer (4): secondary polyurethane flooring layer

(5) : 우레탄 톱 코트층 (6) : 에폭시 프라이머층(5): urethane top coat layer (6): epoxy primer layer

(7) : 1차 에폭시 바닥재층 (8) : 2차 에폭시 바닥재층(7): primary epoxy flooring layer (8): secondary epoxy flooring layer

(10) : 우레탄 바닥재층 (11) : 에폭시 레진 몰탈 바닥재층 10: urethane flooring layer 11 epoxy resin mortar flooring layer

(12) : 톱 코트층(12): top coat layer

Claims (7)

삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 기초를 이루는 콘크리트 슬라브층(1)과 그 위에 형성되는 유성 우레탄 프라이머층(9), 바닥재층과 마지막의 탑코트층(12)으로 다층 구성되는 바닥재에 있어서,  In the flooring material which consists of a multilayered concrete slab layer (1), an oil-based urethane primer layer (9) formed on it, a flooring layer, and the last topcoat layer (12), 상기 유성 우레탄 프라이머층(9) 위에 도포되는 바닥재층은 탄성력 및 신축력을 가진 유성 우레탄 바닥재층(10)과, 그 위에 형성되는 내마모성, 접착성, 강도강화 기능을 가진 에폭시 레진 몰탈 바닥재층(11)로 적층하여 구성하되; The flooring layer applied on the oily urethane primer layer 9 includes an oily urethane flooring layer 10 having elasticity and elasticity, and an epoxy resin mortar flooring layer 11 having abrasion resistance, adhesiveness, and strength enhancing function formed thereon. Laminated to be configured; 상기 우레탄 바닥재층(10)은 주제인 우레탄과 경화제를 2:1로 혼합하고, 형성 두께는 1.O~1.5mm로 형성하고, 주제인 폴리우레탄은 신축율이 450~500%이고, 경도는 65~75인 것을 사용하고, The urethane flooring layer 10 is mixed with a main urethane and a curing agent 2: 1, the forming thickness is formed from 1.O ~ 1.5mm, the main polyurethane is a stretch rate of 450 ~ 500%, the hardness is I use 65-75 thing, 상기 내마모성, 접착성, 강도강화 기능을 가진 에폭시 레진 몰탈 바닥재층(11)은 에폭시 수지와 규사(칼라규사 포함)를 1:4.5 ~ 5.O 비율로 혼합하고, 그 형성 두께는 3.O ~ 4.Omm로 형성하여 적층 구성한 것을 특징으로 하는 탄성이 있는 폴리우레탄과 내마모성의 에폭시를 복합 적층한 다기능성 바닥마감재.The epoxy resin mortar flooring layer 11 having the abrasion resistance, adhesiveness, and strength enhancing function mixes epoxy resin and silica sand (including color silica sand) in a ratio of 1: 4.5 to 5.O, and the thickness thereof is 3.O to 4. Multi-functional floor finishing material which is laminated with elastic polyurethane and abrasion-resistant epoxy, characterized in that formed by laminating by forming in Omm. 기초를 이루는 콘크리트 슬라브층(1)과 그 위에 형성되는 유성 우레탄 프라이머층(9), 바닥재층과 마지막의 탑코트층(12)으로 다층 구성되는 바닥재를 시공하는 방법에 있어서, In the method of constructing the flooring material which consists of a multilayered concrete slab layer 1, an oil-based urethane primer layer 9 formed on it, a flooring layer, and the last topcoat layer 12, 콘크리트 슬라브층(1)의 상면에 유성 우레탄 프라이머층(9)을 도포하고 그 위에 주제인 폴리우레탄과 경화제를 2:1 비율로 혼합한 다음 고무헤라나 주걱으로 1.O~1.5mm의 두께로 유용성 폴리우레탄 바닥재층(10)을 형성하는 단계와,Apply the oil-based urethane primer layer 9 on the upper surface of the concrete slab layer 1, mix the main polyurethane and the hardener in a 2: 1 ratio on the upper surface of the concrete slab layer, and then use a rubber spatula or spatula to make the thickness of 1.O ~ 1.5mm. Forming an oil-soluble polyurethane flooring layer (10), 상기 폴리우레탄 바닥재층(10)을 시공한 위에 내마모성, 접착성, 강도강화 기능을 부여하도록 에폭시 수지와 규사를 1:4.5 ~ 5.O 비율로 혼합한 다음 두께 3.O ~ 4.Omm가 되도록 쇠흙손이나 전용장비를 이용하여 내마모성의 에폭시 레진 몰탈 바닥재층(11)을 형성하는 단계와;Epoxy resin and silica are mixed at a ratio of 1: 4.5-5.O to give abrasion resistance, adhesiveness, and strength enhancing function on the polyurethane flooring layer 10, and then the thickness is 3.O-4.Omm. Forming a wear-resistant epoxy resin mortar flooring layer (11) using a trowel or a dedicated equipment; 상기 에폭시 레진 몰탈 바닥재층(11)이 경화되면 롤러나 스프레이로 지정색의 톱코트층(12)을 살포하는 단계로 이루어진 것을 특징으로 하는 탄성이 있는 폴리우레탄과 내마모성의 에폭시를 복합 적층한 다기능성 바닥마감재의 시공방법.When the epoxy resin mortar flooring layer 11 is cured, a multi-layered composite of elastic polyurethane and abrasion resistant epoxy is formed by spraying a top coat layer 12 of a designated color with a roller or spray. Construction method of floor finishing materials.
KR10-2002-0064138A 2002-10-21 2002-10-21 Multi-functional flooring that mixed properly the elastic poly-urethane and the epoxy having abrasion resistance and its construction method KR100527282B1 (en)