KR100500773B1 - Within conclusion of interior for a building and manufacturing method of within conclusion - Google Patents
Within conclusion of interior for a building and manufacturing method of within conclusion Download PDFInfo
- Publication number
- KR100500773B1 KR100500773B1 KR10-2002-0035720A KR20020035720A KR100500773B1 KR 100500773 B1 KR100500773 B1 KR 100500773B1 KR 20020035720 A KR20020035720 A KR 20020035720A KR 100500773 B1 KR100500773 B1 KR 100500773B1
- Authority
- KR
- South Korea
- Prior art keywords
- interior
- weight
- finishing material
- layer
- mortar
- Prior art date
Abstract
본 발명은 건축물 실내 인테리어용 내장마감재에 관한 것으로, 그 목적은 마감재로서의 실내 인테리어 효과와 더불어 탈취기능과 원적외선 방출기능으로 실내를 아름답게 함과 동시에 실내공기를 정화하여 청결한 주거환경을 조성하도록 하는 것이다.The present invention relates to an interior finishing material for building interiors, the purpose of which is to clean the indoor air at the same time as a deodorizing function and far-infrared emission function as well as the interior interior effect as a finishing material to create a clean living environment.
본 발명에 따른 건축물 실내 인테리어용 내장마감재에 의하면, 일측면에 부석과 사금파리, 혼화제등의 보조재료로 이루어져 벽면과 접착용 몰탈이 채워지도록 몰탈채움홈이 형성된 접착층과, 상기 접착층의 타측면에 동일규격으로 형성되되, 황토, 참숯, 게르마늄분말과 맥반석, 천연옥, 자수정등의 광물질이 혼합된 혼합재료로 이루어져 색상, 문양과 탈취, 원적외선 방출기능을 갖는 문양층과, 상기 문양층의 표면에 코팅되어 표면강도를 증대함과 동시에 오염을 방지하도록 하는 유약코팅층을 포함하는 것이다.According to the interior finishing material for the interior of the building according to the present invention, an adhesive layer formed of auxiliary materials such as pumice, gold dust, admixture, etc. on one side and a mortar filling groove is formed to fill the wall surface and the bonding mortar, and the same on the other side of the adhesive layer. It is formed to a standard, and consists of a mixture of mineral materials such as ocher, charcoal, germanium powder and elvan, natural jade, and amethyst, and is coated on the surface of the pattern layer having a color, pattern and deodorization, and far-infrared emission function. It is to include a glaze coating layer to prevent surface contamination while increasing the surface strength.
이에 따라, 본 발명의 내장마감재에 의해 실내 미관은 아름답게 하고 혼합재료 특유의 탈취기능과 원적외선 방출기능으로 실내공기를 정화하여 쾌적한 주거환경을 조성한 이점이 있다.Accordingly, the interior finishing material of the present invention has the advantage that the interior aesthetics are beautiful and the indoor air is purified by the deodorizing function and the far-infrared ray emitting function peculiar to the mixed material to create a comfortable living environment.
Description
본 발명은 건축물 내부에 마련되어 미려한 외관을 표출하는 인테리어용 내장마감재에 관한 것으로, 더욱 더 상세하게는 폐자재와 혼화제를 적절히 혼합하여 이루어진 일측면에 벽면과 접착이 용이하도록 몰탈채움홈이 형성된 접착층과, 이 접착층의 타측면에 동일규격으로 형성되되, 황토, 참숯, 게르마늄분말과 맥반석, 천연옥, 자수정등의 광물질이 혼합된 혼합재료로 이루어져 색상, 문양과 탈취, 원적외선 방출기능을 갖는 문양층과, 상기 문양층의 표면에 코팅되어 표면강도를 증대함과 동시에 오염을 방지하도록 하는 코팅층으로 이루어진 건축물 실내 인테리어용 내장마감재와 그 마감재의 제조방법에 관한 것이다.The present invention relates to an interior finishing material for interiors provided inside a building to express a beautiful appearance, and more particularly, an adhesive layer having a mortar-filled groove formed on one side to be easily adhered to a wall formed by properly mixing waste materials and admixtures. The pattern is formed on the other side of the adhesive layer with the same standard, and consists of a mixture of mineral materials such as ocher, charcoal, germanium powder, ganban stone, natural jade and amethyst, and a pattern layer having a function of color, pattern and deodorization, and far infrared ray emission. The present invention relates to a method for manufacturing interior finishing materials and interior finishing materials for the interior of a building comprising a coating layer which is coated on the surface of the pattern layer to increase surface strength and prevent contamination.
일반적으로 건축물, 특히, 화장실 벽체에 배치되는 타일이나 바닥면에 배치하는 테라조와 세면대 및 변기등은 시멘트나 점토 및 횟가루등으로만 만들어지기 때문에 그 표면에 표현된 무늬등에 의한 장식효과 이외의 다른 효과를 기대할 수 없으므로, 통상의 방향제나 기타 여러 가지 수단을 동원하고 있는 실정이었다.Buildings, especially terrazzos, washbasins and toilets, which are placed on tiles or floors on bathroom walls, are made only of cement, clay, and ash, so other effects than the decorative effect of patterns on the surface Because it can not be expected, it was mobilizing the usual air freshener and various other means.
또한, 이와같은 방향제로 악취를 제거하기에는 한계가 있어 염산이 함유된 세정제(일명 "락스")를 이용하여 화장실 바닥과 벽면을 청소하는 과정에서 그 독성에 의해 호흡장애등의 안전사고가 유발되는 문제가 있었다.In addition, there is a limit to remove the odor with such a fragrance, the problem that causes safety accidents such as breathing disorder due to its toxicity in the process of cleaning the floor and walls of the toilet using a detergent containing hydrochloric acid (aka "lax") there was.
또한, 하절기에는 청소가 용이하지 못한 욕조나 세면대의 하부구석에 서식하는 세균에 의해 비위생적인 환경에 노출되는 문제가 있었다.In addition, in summer, there was a problem of being exposed to an unsanitary environment by bacteria inhabiting the lower corner of a bath or wash basin, which is not easy to clean.
또한, 화장실의 세면대 및 욕조는 상술한 점토 및 횟가루 이외에 합성수지재인 F.R.P로 제조가 이루어지므로 표면에 물때 또는 이물질에 의해 오염되면 잘 닦이지 않아 미관상 보기 흉한 문제가 있었다.In addition, the wash basin and bath of the toilet is made of synthetic resin material F.R.P in addition to the above-mentioned clay and ash powder, so if the surface is contaminated by dirt or foreign matter, there was a problem of unsightly appearance.
본 발명은 이러한 문제점을 해결하기 위한 것으로, 본 발명의 목적은 내장마감재의 실내 인테리어효과 이외에 별도의 세정과 탈취제를 구비하지 않아도 항균, 탈취기능과 원적외선 방출기능을 복합적으로 수행할 수 있는 인테리어용 실내마감재를 공급하는데 있다.The present invention is to solve this problem, an object of the present invention is to interior the interior of the interior that can perform a combination of antibacterial, deodorizing function and far-infrared radiation without having to separate cleaning and deodorant in addition to the interior interior effect of the interior finish material To supply the finishing materials.
또한, 본 발명의 다른 목적은 물때 또는 이물질에 잘 오염되지 않고, 오염되어도 용이하게 청소할 수 있도록 하여 실내를 미려하고 청결한 상태를 유지할 수 있도록 하는데 있다. In addition, another object of the present invention is not to be contaminated with scale or foreign matter, so that it can be easily cleaned even if contaminated to maintain a beautiful and clean state of the room.
이러한 목적을 달성하기 위한 본 발명은;The present invention for achieving this object is;
실내 인테리어용 내장마감재에 관한 것으로,Regarding the interior finishing materials for the interior,
상기 내장마감재는 일측면에 벽면과 접착용 몰탈이 채워지도록 길이방향으로 적어도 1열이상의 몰탈채움홈이 형성된 접착층과;The interior finishing material and the adhesive layer is formed with at least one row of mortar filling groove in the longitudinal direction to fill the wall surface and the bonding mortar on one side;
상기 접착층의 타측면에 동일규격으로 형성되며 외부로 색상과 문양의 표출이 가능한 문양층과;A pattern layer formed on the other side of the adhesive layer with the same standard and capable of expressing colors and patterns to the outside;
상기 접착층과 문양층의 표면에 코팅된 유약코팅층을 포함하는 것을 특징으로 한다.It characterized in that it comprises a glaze coating layer coated on the surface of the adhesive layer and the pattern layer.
또한, 상기 코팅층은 유약을 도포하여 된 것을 특징으로 한다.In addition, the coating layer is characterized in that by applying a glaze.
또한, 상기 문양층은 30중량/%의 황토와, 12.5중량/%의 참숯과, 22.5중량/%의 게르마늄으로 이루어진 분말과, 15중량/%의 맥반석과, 10중량/%의 천연옥과, 10중량/%의 자수정으로 이루어진 골재가 혼합된 혼합재료인 것을 특징으로 한다.In addition, the pattern layer is made of 30% by weight of ocher, 12.5% by weight of charcoal, 22.5% by weight of germanium, 2% by weight of germanium, 15% by weight of ganban stone, 10% by weight of natural jade, 10 It is characterized in that the aggregate made of amethyst by weight /% is a mixed material mixed.
또한, 상기 접착층은 60 중량/%의 부석과, 20중량/%의 사금파리와, 20중량/%의 혼화제로 이루어진 것을 특징으로 한다.In addition, the adhesive layer is characterized in that consisting of 60% by weight of pumice, 20% by weight of gold dust and 20% by weight of admixture.
또한, 본 발명은 건축용 내장마감재의 제조방법에 관한 것으로,In addition, the present invention relates to a method of manufacturing a building interior finishing material,
상기 내장마감재 제조방법은 소정 형상의 형틀에 문양층이 형성되도록 혼합재료를 도포하는 1차 몰탈과, 상기 1차몰탈이 완료된 문양층 상부에 접착층이 형성될 보조재료를 투입하는 2차 몰탈로 이루어진 몰탈단계와; The interior finishing material manufacturing method is composed of a primary mortar for applying a mixed material to form a pattern layer in a mold of a predetermined shape, and a secondary mortar for inputting an auxiliary material to form an adhesive layer on top of the pattern layer is completed. Mortar step;
상기 2차 몰탈에서 투입된 혼합재료의 밀도를 높이기 위해 상기 형틀을 진동시키는 압축단계와; A compression step of vibrating the mold to increase the density of the mixed material injected from the secondary mortar;
상기 압축단계에서의 진동에 의해 압축이 완료된 접착층과 문양층에 히터로 가열하여 양생시키는 양생단계와; A curing step of curing by heating with a heater to the adhesive layer and the glyph layer, the compression is completed by the vibration in the compression step;
상기 소정의 시간이 경과 후 양생이 완료된 마감재을 형틀에서 분리하는 탈형단계와; A demolding step of separating the finishing material from which the curing is completed after the predetermined time elapses from the mold;
상기 문양층 표면에 코팅제인 유약을 적어도 1번 이상 도포하는 코팅단계와; A coating step of applying at least one glaze, which is a coating agent, on the surface of the pattern layer;
상기 코팅단계에서 도포된 유약을 경화하는 열처리단계를 포함하는 것을 특징으로 한다.It characterized in that it comprises a heat treatment step of curing the glaze applied in the coating step.
이하, 본 발명에 따른 하나의 바람직한 실시예를 첨부도면을 참조하여 상세히 설명한다. 첨부도면을 간략히 설명하면, 도 1은 본 발명에 따른 건축물 내장마감재를 보인 단면도이고, 도 2와 도 3은 본 발명에 따른 건축물 내장마감재의 제조방법을 보인 공정블럭도와 공정별 작업진행도이고, 도 4는 본 발명에 따른 건축물 내장마감재의 외관을 보인 사시도이고, 도 5는 본발명에 따른 건축물 내, 외벽 장식용마감재의 시공을 설명하기 위해 순차적으로 도시한 단면도이다.Hereinafter, one preferred embodiment according to the present invention will be described in detail with reference to the accompanying drawings. Briefly the accompanying drawings, Figure 1 is a cross-sectional view showing a building interior finishing material according to the present invention, Figures 2 and 3 is a process block diagram showing the manufacturing method of the building interior finishing material according to the present invention and the operation progress diagram for each process, Figure 4 is a perspective view showing the appearance of the building interior finishing material according to the present invention, Figure 5 is a cross-sectional view sequentially illustrating the construction of the building interior, exterior wall decorative finishing material according to the present invention.
도 1을 참조하면, 본 발명에 따른 건축물 내장마감재(100)(이하, "마감재"이라 칭한다.)는 사각판형의 일측면에 몰탈채움홈(111)이 길이방향으로 적어도 1열 이상 형성되어 벽면과 접착이 용이하도록 하는 접착층(110)과, 접착층(110)의 타측면에 일체로 형성되어 시공이 완료되면 외부로 노출되는 문양층(120)과, 이 문양층(120) 표면에 유약으로 코팅된 코팅층(130)을 포함한다.Referring to Figure 1, the building interior finishing material 100 (hereinafter referred to as "finishing material") according to the present invention is formed on at least one row of the mortar filling groove 111 in the longitudinal direction on one side of the rectangular plate wall surface And the adhesive layer 110 to facilitate the adhesion, the glyph layer 120 is integrally formed on the other side of the adhesive layer 110 and exposed to the outside when the construction is completed, and coated on the surface of the glyph layer 120 with glaze It includes a coating layer 130.
접착층(110)은 다양한 종류의 폐자재를 적정한 비율로 혼합하여 이루어지는 보조재료로, 마감재(100) 전체구성의 대다수 비율을 차지하여 저가에 제조가 가능하도록 하는 것으로, 그 구성은 60 중량/%의 부석과, 20중량/%의 사금파리와, 20중량/%의 혼화제로 이루어진다.The adhesive layer 110 is an auxiliary material formed by mixing various kinds of waste materials at an appropriate ratio. The adhesive layer 110 occupies a majority ratio of the entire composition of the finishing material 100 to enable manufacturing at a low cost. It consists of pumice stone, 20 weight% of gold dust, and 20 weight% of admixture.
부석과 사금파리는 분말로 이루어지는데, 우선, 접착층(110)의 재료중 가장 높은 비율을 차지하는 부석(浮石)은 통상적으로 속돌 또는 경석(輕石)이라고 하는 것으로, 마그마가 대기 중으로 방출될 때 압력이 갑자기 감소한 결과로 마그마 중의 휘발성 성분이 빠져 나가서 수많은 기공(氣孔)이 형성된 것으로, 외관상 비중이 작아서 물에 뜰 만큼 가벼우므로 본 발명에서의 마감재(100) 중량을 전체적으로 경량화할 수 있다. Pumice and gold dust are made of powder. First, pumice, which occupies the highest proportion among the materials of the adhesive layer 110, is commonly referred to as pumice or pumice. As a result of the sudden decrease of the volatile components in the magma to form a large number of pores (氣孔), the apparent specific gravity is small enough to float in water so that the weight of the finishing material 100 in the present invention can be reduced as a whole.
또한, 사금파리는 깨어진 도자기를 분말화한 것으로, 부석에 의해 경량화된 접착층(110)의 강도를 향상시키는 것이다.In addition, the gold dust flies are powdered ceramics, which is to improve the strength of the adhesive layer 110, which is lightened by pumice stone.
마지막으로 혼화제는 상기한 부석과 사금파리분말이 경화하기 전 또는 경화 후의 성질을 개선하기 위해 첨가되는 것으로, 가장 많이 사용되는 것은 분산제나 AE(Air Entraining Agent)로 분말화된 부석과 사금파리의 경화를 촉진하고 상기 부석과 사금파리 내부에 공기층을 형성하는 공기연행작용을 하는 특징이 있다.Finally, the admixture is added to improve the properties of the above-mentioned pumice and sapphire powder before or after curing. The most commonly used agent promotes cure of pumice and sapphire powdered with a dispersant or AE (Air Entraining Agent). And it is characterized in that the air entrainment to form an air layer inside the pumice and placer.
이와 같은 특징을 가진 재료들에 적정비율의 물을 혼합하여 후술하는 제조방법에서의 형틀(10)에 주입하면 본 발명에 따른 접착층(110)이 형성되는 것이다.The adhesive layer 110 according to the present invention is formed by injecting water having a proper ratio into the materials having such characteristics and injecting the mold 10 in the manufacturing method described below.
한편, 상기한 물의 혼합비율은 통상의 슬럼프값, 즉, 아직 굳지 않은 콘크리트 또는 시멘트의 반죽질기(consistency)를 시험을 통하여 지나치게 되거나 질지 않게한 정도면 된다.On the other hand, the mixing ratio of the water may be such that the normal slump value, that is, the degree of consistency of concrete or cement that has not yet been hardened through the test.
한편, 접착층(110)의 타측에 일체로 형성되는 문양층(120)은 35중량/%의 황토와, 12.5중량/%의 참숯과, 22.5중량/%의 게르마늄으로 이루어진 분말과, 각각 10중량/%씩 함유된 맥반석, 천연옥, 자수정등의 골재로 이루어진 혼합재료이다.On the other hand, the pattern layer 120 is formed integrally on the other side of the adhesive layer 110 is composed of 35% by weight of ocher, 12.5% by weight of charcoal, 22.5% by weight of germanium, and 10% by weight / It is a mixed material composed of aggregates such as ganban stone, natural jade and amethyst contained in%.
상기한 황토와 참숯과 게르마늄으로 된 분말과 맥반석과 천연옥, 자수정은 항균, 탈취기능과 함께 원적외선 발산기능등 다양한 광물질이 조합된 형태로서 후술하는 코팅층(130)의 유약에 형성된 기공에 의해 외부로 발산되며 항균, 탈취기능을 하는 것이다. The ocher, charcoal, germanium powder, ganban stone and natural jade, amethyst is emitted in the form of a combination of various minerals such as anti-bacterial, deodorizing function and far-infrared light emitting function by pores formed in the glaze of the coating layer 130 to be described later And antibacterial, deodorizing function.
이상과 같은 혼합재료(121)에 소정색상의 안료와 물을 혼합, 반죽하면 본 발명에 따른 마감재(100)의 문양층(120)이 형성되는 것이다.When mixing and kneading the pigment and water of a predetermined color to the mixed material 121 as described above is to form the pattern layer 120 of the finishing material 100 according to the present invention.
상기한 바와 같은 문양층(120) 표면에 코팅제를 도포하여 코팅층(130)을 형성하는데, 이때 도포되는 코팅제는 통상의 유약(釉藥)으로 문양층(120) 표면에 광택을 주무로서 제품을 아름답게 하는 것 이외에도 강도를 더하고 표면을 반질반질하게 하여 더러워지는 것을 예방하도록 하고, 설령 더러워지더라도 특유의 매끄러운 표면에 의해 더러워져도 용이하게 청소할 수 있다.Applying a coating on the surface of the pattern layer 120 as described above to form a coating layer 130, wherein the coating is applied to the surface of the pattern layer 120 with a conventional glaze to make the product beautiful In addition to adding strength, the surface is made semi-finished, so that it is prevented from becoming dirty, and even if it is dirty, it can be easily cleaned even if it is soiled by a unique smooth surface.
일반적으로 투명한 것이 대부분이지만 유백유, 색유, 결정유, 무염유, 균열유등이 있다.In general, most of them are transparent, but there are milk milk, color oil, crystalline oil, unsalted oil and cracked oil.
이상과 같은 구성으로 이루어진 마감재(100)의 제조방법에 대해 설명한다.The manufacturing method of the finishing material 100 which consists of the above structures is demonstrated.
도 2와 도 3을 참조하면, 마감재(100)의 제조방법은 공정별로 몰탈단계(MS)와, 압축단계(PS)와, 양생단계(FS)와, 탈형단계(ES)와 코팅단계(CS), 건조단계(DS)를 포함한다.2 and 3, the manufacturing method of the finishing material 100 is a mortar step (MS), compression step (PS), curing step (FS), demolding step (ES) and coating step (CS) for each process ), Drying step (DS).
첫번째 공정인 몰탈단계(MS)는 상술한 바와 같은 접착층(110)과 문양층(120)을 형성하기 위해 형틀(10) 내부에 상술한 바와 같은 혼합재료가 도포되는 1차 몰탈(M1)과 보조재료가 투입되는 2차 몰탈(M2)이 시행되는 것으로, 형틀(10)을 기준으로 한 제조공정상 문양층(120)이 형성될 혼합재료를 도포하는 1차 몰탈(M1)이 먼저 시행된다.(도시한 형틀(10)은 일실시예로서 바닥면에 요철이 형성된 것을 도시하였으나, 평면으로 형성할 수도 있다.)The first process mortar step (MS) and the secondary mortar (M1) and the auxiliary material is applied to the mixed material as described above in the mold 10 to form the adhesive layer 110 and the pattern layer 120 as described above The secondary mortar (M2) is injected into the material, the primary mortar (M1) for applying the mixed material to form the pattern layer 120 is first performed in the manufacturing process based on the mold (10). Although the illustrated mold 10 shows that the unevenness is formed on the bottom surface as an embodiment, it may be formed in a plane.)
우선, 1차 몰탈(M1)은 형틀(10)의 저면에 상술한 황토와, 참숯, 게르마늄으로 이루어진 분말과, 맥반석, 천연옥, 자수정등의 골재로 이루어진 혼합재료를 단면두께 3 ~ 5mm정도가 되도록 도포하여 1차로 문양층(120)을 형성한다.First, the primary mortar (M1) is made of the above-mentioned ocher, powder made of charcoal, germanium, and aggregate material composed of aggregates such as ganban stone, natural jade, amethyst, and the like so as to have a cross-sectional thickness of about 3 to 5 mm. It is applied to form a pattern layer 120 first.
이와 같이, 1차 몰탈(M1) 작업이 완료된 상태에서 부석, 사금파리, 혼화제로 이루어진 보조재료를 투입하는 2차 몰탈(M2) 작업이 이어지는데, 2차 몰탈(M2)작업을 하기 전에 형틀(10) 상부에 길이방향으로 몰탈안착홈(111)이 형성되도록 다수의 치구(11)를 설치하고, 형틀(10) 내부에서 1차로 코팅된 문양층(120) 상부에 부석과 사금파리, 혼화제와 물이 적정비율로 혼합된 보조재료를 형틀(10)의 내부에 소복하게 투입하여 2차 몰탈(M2)작업이 끝나면 몰탈단계(MS)의 작업이 완료되고, 다음 공정인 압축단계(PS)로 이어진다.In this way, the secondary mortar (M2) operation to inject the auxiliary material consisting of pumice, placer flies, admixtures in the state that the primary mortar (M1) operation is completed, the mold 10 before the second mortar (M2) operation Installing a plurality of jig 11 to form a mortar mounting groove 111 in the longitudinal direction on the top, and the pumice and placer, the admixture and water is titrated on the pattern layer 120 coated first inside the mold 10 After the secondary mortar (M2) operation is completed by injecting auxiliary materials mixed at a ratio into the mold 10, the work of the mortar stage MS is completed, and the compression process PS is performed.
압축공정(PS)은 형틀(10) 전체를 도시하지 않은 진동기(Vibrator)에서 발생되는 진동에 의해 제 1코팅층(130)이 형성되도록 2차로 투입된 폐자재를 견실하게 다져 조직의 밀도를 높이도록 하는 것이고, 이 과정에서 상기한 몰탈단계(MS)에서 순차적으로 투입된 1, 2차 몰탈(M1)(M2)은 점상(粘狀)의 상태이므로, 진동기의 진동에 의해 자연적으로 압축되며 상호 접촉면이 일부혼합되며 견실하게 접착되는 것이다.Compression process (PS) is to solidify the waste material injected into the second coating so that the first coating layer 130 is formed by the vibration generated in the vibrator (not shown) the entire mold 10 to increase the density of the tissue In this process, since the first and second mortars (M1) and (M2) sequentially introduced in the above-described mortar stage (MS) is in the form of a point (粘 狀), it is naturally compressed by the vibration of the vibrator and the mutual contact surface is partially It is mixed and firmly bonded.
또한, 압축공정(PS)은 지속적으로 발생하는 진동에 의해 형틀(10)의 상부로 소복하게 쌓였던 혼합재료(112) 내부에 기포발생으로 인한 공극(Void)이 형성되는 것을 방지하여 마감재(100)의 성형이 완료되면 강도를 향상시키는 역할을 한다.In addition, the compression process (PS) to prevent the formation of voids (Void) due to the bubbles generated in the mixed material 112 accumulated in the upper portion of the mold 10 by the continuously generated vibration finishing material 100 When the molding of the finished serves to improve the strength.
압축공정(PS)이 완료된 형틀(10)은 다은 공정인 양생공정(FS)을 위해 양생실(미도시)로 이동한다.The mold 10 in which the compression process PS is completed is moved to a curing chamber (not shown) for the curing process FS, which is another process.
이동이 완료된 형틀(10)은 양생실 내부에 배치된 히터(미도시)에 의해 소정시간을 가열하여 양생하면 적정한 비율의 물과 혼합된 접착층(110)과 문양층(120)은 건조, 경화되며 양생공정(FS)이 완료된다.When the mold 10 is moved, the curing layer 110 and the glyph layer 120 mixed with water in an appropriate ratio are dried and cured by heating a predetermined time by a heater (not shown) disposed in the curing chamber. Curing process (FS) is completed.
양생이 완료되면 탈형단계(ES)를 통해 형틀(10) 내부에서 성형이 완료된 마감재(100)을 빼내고, 1차로 형성된 문양층(120)의 조직사이로 침투하여 강도를 보강하도록 문양층(120)의 표면에 유약을 도포하여 코팅층(130)을 형성하는 코팅단계(CS)가 이어지는데, 여기서 코팅층(130)은 코팅제를 1번만 도포하여도 무방하지만, 2번 이상을 도포할 경우 마감재(100)의 수명을 연장할 수 있는데, 유약은 스프레이 또는 붓으로 도포하여 코팅할 수 있다.After curing is completed, the mold 100 is removed from the mold 10 through the demolding step (ES), and penetrates between the tissues of the first pattern glyph layer 120 to reinforce the strength of the glyph layer 120. The coating step (CS) is followed by applying a glaze to the surface to form a coating layer 130, where the coating layer 130 may be applied only once, but if applied more than two times the life of the finish 100 The glaze can be coated by spraying or brushing.
또한, 코팅단계(CS)에서 코팅이 완료된 마감재(100)는 도시하지 않은 열처리로로 이동하여 히터에 의해 적정한 소성온도로 가열하여 건조, 경화가 완료되는 열처리단계(DS)를 끝으로 전체적인 제조공정이 완료되어 도 4에 도시한 바와 같은 마감재(100)의 제조가 완료되는 것이다.In addition, the coating finish (100) in the coating step (CS) is moved to a heat treatment furnace (not shown) and heated to an appropriate firing temperature by a heater to finish the heat treatment step (DS) to complete the drying, curing the entire manufacturing process This is completed and the manufacture of the finishing material 100 as shown in FIG. 4 is completed.
도 5를 참조하면, 이와 같이 제조된 마감재(100)의 시공에 대해 설명하기 위해 순차적으로 도시한 단면도로서, 1차적으로 벽면(WF)에 붙임몰탈(SM)을 미장한 후, 본 발명에 따른 마감재(100)의 일면에 형성된 몰탈삽입홈(111)에 붙임몰탈(SM)을 충분히 채워넣는다.Referring to Figure 5, in order to explain the construction of the finished material 100 prepared as described above in sequential cross-sectional view, after first plastering the mortar (SM) attached to the wall (WF), according to the present invention Fill the mortar (SM) with the mortar insertion groove 111 formed on one surface of the finish 100 sufficiently.
벽면(WF)과 마감재(100)에 미장된 붙임몰탈(SB)을 상호 면접착시키면 견실한 접착이 이루어진다.When the surface bonding of the bonding mortar (SB) plastered on the wall surface (WF) and the finishing material 100 is a strong adhesion is made.
이때, 몰탈삽입홈(111)과 벽면(WL)에 미장된 붙임몰탈(SM)이 접착되며 마감재(100)이 고정되는 것이고, 역사다리꼴로 형성된 몰탈삽입홈(111)이 지지턱의 역할을 하여 마감재(100)가 분리되는 것이 방지된다. At this time, the mortar insertion groove 111 and the plaster mortar (SM) plastered on the wall (WL) is bonded and the finishing material 100 is fixed, the mortar insertion groove 111 formed in the inverted trapezoid serves as a supporting jaw. The finishing material 100 is prevented from being separated.
또한, 도시하지는 않았으나, 상호 이웃하는 마감재(100)들의 4방측면에는 사춤몰탈로 충만시키면되고, 위와 같은 방법으로 다른 마감재(100)를 퍼즐식으로 붙여 접착시키면 시공이 완료된다.In addition, although not shown, the four sides of the neighboring finishing materials 100 to be filled with filling mortar, and the other finishing materials 100 in the same manner as the above by attaching a jigsaw puzzle, the construction is completed.
이때, 본 발명에 따른 마감재에는 다양한 형상의 문양을 형성하여 실내 인테리어 효과를 극대화할 수 있다.At this time, the finishing material according to the present invention can maximize the interior effect by forming a pattern of various shapes.
본 발명에 따른 마감재(100)는 몰탈삽입홈(111)이 형성된 일면의 붙임몰탈(SM)과 4방 측면의 테두리에 충만되는 사춤몰탈에 의해 견실하게 고정되는 것이다.Finishing material 100 according to the present invention is to be firmly fixed by the filling mortar (SM) of one side formed mortar insertion groove 111 and the filling mortar filled in the four sides of the edge.
이와 같이, 본 발명에 따른 마감재(100)는 사금파리와 부석이 혼합된 접착층(110)에 의해 전체적인 중량을 경량화하여 현장에서 시공이 용이하도록 하였고, 벽면과 역사다리꼴로 형성된 몰탈안착홈(111)이 지지턱의 역할을 하여 벽면(WF)과 견실하게 장착된 상태를 유지함과 동시에 저가에 생산이 가능하도록 하였고, 문양층(120)에 함유된 황토, 게르마늄, 참숯, 맥반석, 천연옥, 자수정등에 의해 항균, 탈취기능을 함과 동시에 원적외선을 방출하므로 실내의 공기를 정화하였다.As described above, the finishing material 100 according to the present invention is easy to be installed in the field by reducing the overall weight by the adhesive layer 110 mixed with placer flies and pumice, and the mortar mounting groove 111 formed in the wall and history trapezoidal It acts as a support jaw and maintains the wall (WF) and mounted state at the same time to enable production at low cost, and antibacterial by ocher, germanium, charcoal, elvan, natural stone, amethyst, etc. contained in the pattern layer 120 As it deodorizes and emits far infrared rays, it purifies the indoor air.
또한, 상술한 일실시예는 타일식의 판형으로 된 마감재(100)에 대해서만 설명하였으나, 그것은 당 업계의 제조기술로서 얼마든지 용이하게 바위형상, 동물형상으로 변형하여 실시가 가능한 것은 물론이다.In addition, the above-described embodiment has been described only with respect to the tile-like plate-like finish 100, but it is a matter of course that can be easily transformed into a rock shape, animal shape as the manufacturing technology in the art.
본 발명은 상술한 특정 바람직한 실시예에 한정되지 아니하며, 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 고안이 속하는 기술분야에서 통상의 지식을 가진자라면 누구든지 용이하게 변형실시가 가능한 것은 물론이고, 그와 같은 변경은 청구항 기재의 범위내에 있게 된다.The present invention is not limited to the above-described specific preferred embodiments, and can be easily modified by anyone having ordinary skill in the art without departing from the gist of the present invention claimed in the claims. Of course, such changes are intended to fall within the scope of the claims.
이상에서 상세히 설명한 바와 같이, 본 발명에 따른 건축물 인테리어용 내장마감재와 그 내장마감재의 제조방법에 의하면, 내장마감재의 실내 인테리어효과 이외에 별도의 세정과 탈취제를 구비하지 않아도 항균, 탈취기능과 원적외선 방출기능을 복합적으로 수행할 수 있는 인테리어용 실내마감재를 공급한 효과가 있다.As described in detail above, according to the present invention, the interior finishing material for building interior and the manufacturing method of the interior finishing material, antibacterial, deodorizing function and far-infrared ray emitting function without additional cleaning and deodorant in addition to the interior interior effect of the interior finishing material It has the effect of supplying interior finishing material for interior that can be combined to perform.
또한, 물때 또는 이물질에 잘 오염되지 않고, 오염되어도 코팅층에 의해 용이하게 청소할 수 있도록 하여 실내를 미려하고 청결한 상태를 유지할 수 있도록 한 효과가있다.In addition, it is not contaminated with scales or foreign matters, and even if contaminated, it is possible to easily clean by the coating layer to maintain the beautiful and clean state of the room.
또한, 문양층에 함유된 황토, 게르마늄, 참숯, 맥반석, 천연옥, 자수정등의 광물질에 의해 항균, 탈취기능을 함과 동시에 원적외선을 방출하므로 실내의 공기를 정화한 효과가 있다. In addition, it has the effect of purifying the indoor air because it emits far-infrared radiation while antibacterial and deodorizing function by the minerals such as ocher, germanium, charcoal, elvan, natural jade, amethyst contained in the pattern layer.
도 1은 본 발명에 따른 건축물 내장마감재를 보인 단면도이고,1 is a cross-sectional view showing a building interior finishing material according to the present invention,
도 2와 도 3은 본 발명에 따른 건축물 내장마감재의 제조방법을 보인 공정블럭도와 공정별 작업진행도이고, 2 and 3 is a process block diagram showing the manufacturing method of the building interior finishing material according to the present invention and the operation progress diagram for each process,
도 4는 본 발명에 따른 건축물 내장마감재의 외관을 보인 사시도이고,Figure 4 is a perspective view showing the appearance of the building interior finishing material according to the present invention,
도 5는 본발명에 따른 건축물 내, 외벽 장식용마감재의 시공을 설명하기 위해 순차적으로 도시한 단면도이다.Figure 5 is a cross-sectional view sequentially shown to explain the construction of the decorative finishing material for the inner wall of the building according to the present invention.
*도면의 주요부분에 대한 부호의 설명** Description of the symbols for the main parts of the drawings *
100;내장마감재 110;접착층100; interior finishing material 110; adhesive layer
111;몰탈채움홈 120;문양층111; mortar filling groove 120; glyph layer
130;코팅층130; coating layer
Claims (5)