KR100448172B1 - Double pile knitted fabric for cleansing and manufacturing process of that's - Google Patents

Double pile knitted fabric for cleansing and manufacturing process of that's Download PDF

Info

Publication number
KR100448172B1
KR100448172B1 KR10-2002-0009258A KR20020009258A KR100448172B1 KR 100448172 B1 KR100448172 B1 KR 100448172B1 KR 20020009258 A KR20020009258 A KR 20020009258A KR 100448172 B1 KR100448172 B1 KR 100448172B1
Authority
KR
South Korea
Prior art keywords
yarn
pile
knitted fabric
polyester
double
Prior art date
Application number
KR10-2002-0009258A
Other languages
Korean (ko)
Other versions
KR20030070212A (en
Inventor
노귀영
Original Assignee
노귀영
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 노귀영 filed Critical 노귀영
Priority to KR10-2002-0009258A priority Critical patent/KR100448172B1/en
Publication of KR20030070212A publication Critical patent/KR20030070212A/en
Application granted granted Critical
Publication of KR100448172B1 publication Critical patent/KR100448172B1/en

Abstract

본 발명은 세척용 파일 편포에 있어서 그 지조직에는 폴리에스터와 폴리프로필렌의 혼방사를 사용하고, 표면 파일사로는 굵은 폴리에스터 분사(分絲 : 굵은 모노필라멘트 여러가닥을 꼬임이 없이 모아놓은 실)를, 이면 파일사로는 나일론과 폴리에스터의 복합사로 0.1∼05D의 초극세사를 사용하여 통상의 방법으로 양면 파일 편포를 편직하고, 이를 염색한 후 텐터링(tentering) 및 열처리하여 지조직과 파일사들이 잘 융착되게 하고, 다시 표면 파일사를 용융 아크릴수지로 코팅함으로 분사가 서로 결합하여 더욱 딱딱해지므로 하나의 세척포로써 딱딱한 오물이나 미세한 먼지까지도 쉽게 제거할 수 있는 세척용 양면 파일 편포를 얻을 수 있으며, 지조직용 혼방사 또는 편포 전체에 항균 가공을 함으로써 더욱 위생적인 세척용 양면 파일 편포를 얻을 수 있는 것이다.The present invention uses a blended yarn of polyester and polypropylene in the fabric of the pile pile for washing, and the surface pile yarn is a coarse polyester spray (the yarn which gathered several strands of thick monofilament without twisting). As a back pile yarn, a composite yarn of nylon and polyester is used, and a double-side pile knitted fabric is knitted using a conventional microfiber of 0.1-05D, and then dyed and then tented and heat treated to make the tissue and pile yarn well. By fusion and coating the surface pile yarn with molten acrylic resin, the sprays become more rigid by combining with each other, so that you can get a double-sided pile fabric for washing that can easily remove even hard dirt or fine dust as a single cleaning cloth. More hygienic cleaning double-sided pile knitted fabric can be obtained by antibacterial processing of whole yarn or knitted fabric for paper tissue. Will.

Description

세척용 양면 파일 편포 및 그 제조 방법 { Double pile knitted fabric for cleansing and manufacturing process of that's }Double pile knitted fabric for cleaning and manufacturing method thereof {Double pile knitted fabric for cleansing and manufacturing process of that's}

본 발명은 세척용 양면 파일 편포 및 그 제조 방법에 관한 것으로 보다 상세하게는 지조직으로는 일반적인 폴리에스터(이하 PE로 표기함)와 융점이 낮은 폴리올레핀계 섬유인 폴리프로필렌(이하 PP로 표기함)의 혼방사를 사용하고, 표면 파일사로는 PE로 된 굵은 분사(分絲)를, 이면 파일사로는 나일론과 PE의 복합사(이하 NP복합사라 칭함)인 초극세사를 사용하여 편직하여 열처리와 표면 코팅처리 함으로써 하나의 편포로 딱딱한 오물을 제거하는 수세미 효과와 부드럽게 닦아내는 행주의 역할 및 미세한 먼지까지도 쉽게 제거할 수 있는 세척용 파일 편포 및 그 제조방법에 관한 것이다.The present invention relates to a double-sided pile knitted fabric for washing and a method of manufacturing the same. More specifically, the paper is polypropylene (hereinafter referred to as PP) which is a general polyester (hereinafter referred to as PE) and a polyolefin-based fiber having a low melting point. Heat treated and surface-coated by using a blend of yarns and knitting using a thick spray of PE as the surface pile yarn, and a microfiber of nylon and PE as the back pile yarn (hereinafter referred to as NP composite yarn). The present invention relates to a scrubbing brush for removing hard dirt from a single fabric, a role of a gentle wiping cloth, and a washing file fabric for easily removing even fine dust and a method of manufacturing the same.

일반적으로 세척용 편포는 일반적인 PE섬유를 지조직으로 하고, 파일사로는 NP복합사만을 사용하여 세척용 편포를 제조하여 왔으나, 이는 부드럽기 때문에 행주로는 가능하였으나 수세미로써는 효과가 없어 별도의 수세미를 준비해야하는 불편과 습윤상태에서 세균이 발생하여 비위생적이라는 단점이 있었으며, 건조된 상태에서 유리 등을 닦을 때에는 정전기가 발생하여 먼지 등이 그대로 유리 표면에 부착되는 단점도 있었다.In general, the cleaning knitted fabric has a general PE fiber as a paper tissue, and the pile yarn has been manufactured using only NP composite yarn, but this is possible because it is soft, but it is not effective as a scrubber. There was a disadvantage in that the discomfort and wet conditions caused the bacteria to be unsanitary, and when cleaning the glass in a dry state, there was a disadvantage that the static electricity is generated as it is attached to the glass surface as it is.

한편, 상기한 단점을 보안하고자 본 출원인이 선등록한 실용신안 등록 출원 제2000-0029285호와 같이 지조직에 키토산등으로 항균 가공된 흡습성이 양호한 면사를 사용함으로써 정전기의 발생을 억제하고 세균의 발생을 저지함으로 위생적이며 보다 깨끗하게 먼지를 제거할 수는 있었으나 수세미 작용을 하지 못하기 때문에 딱딱한 불순물을 제거하는 데에는 적합하지 않아 별도의 수세미를 준비하여야 하였다.On the other hand, by using a good hygroscopic cotton yarn antimicrobially processed with chitosan, such as utility model registration application No. 2000-0029285 previously registered by the present applicant in order to secure the above-mentioned disadvantages to suppress the generation of static electricity and to suppress the generation of bacteria Although it was possible to remove the dust more sanitarily and cleanly by blocking it, it was not suitable for removing hard impurities because it could not work with a loofah, so a separate loofah had to be prepared.

본 발명자는 상기한 각종 기술에서 발생하는 문제점을 해결하여 쉽게 세척하고 유리나 가구 및 그릇 등을 닦을 때에도 힘들이지 않고 잘 닦여지는 것은 물론 위생적이며, 딱딱한 불순물까지도 하나의 세척포로 제거할 수 있는 세척포를 개발하기 위하여 오랜 기간 연구한 결과 세척포의 지조직에 PE사와 PP사를 혼방한 혼방사를 사용하고, 표면 파일사로는 PE로 된 굵은 분사(分絲 : 굵은 모노필라멘트 여러 가닥을 꼬임이 없이 모아놓은 실)를, 이면 파일사로는 초극세사인 NP복합사를사용하여 편직한 후 열처리와 표면 코팅처리를 함으로써 세척효과가 우수할 뿐만 아니라 위생적이며, 미세한 먼지에서부터 딱딱한 불순물까지도 하나의 세척포로 쉽게 제거할 수 있는 세척용 양면 파일 편포를 제조할 수 있었다.The present invention solves the problems caused by the above-described various techniques to easily wash and wipe the glass, furniture and bowls, etc., not only hard to be wiped well, but also hygienic, hard impurities can be removed with a single cleaning cloth As a result of research for a long time to develop, a blended yarn mixed with PE yarn and PP yarn is used for the paper tissue of the cleaning cloth, and the surface pile yarn is a bundle of thick sprays of thick monofilament without twisting. Yarn) is used as a back pile yarn using NP composite yarn, which is a microfiber yarn, and then heat treated and surface coated to provide excellent cleaning effect and hygienic and easy removal of fine dust and hard impurities with a single cleaning cloth. Washable double-sided pile knitted fabrics could be prepared.

도1은 본 발명의 일예를 보인 조직 및 사용된 실의 종류를 보인 것이다.Figure 1 shows the tissue showing an example of the present invention and the type of yarn used.

<도면의 주요 부분에 대한 부의 호의 설명><Description of negative arcs for main parts of the drawing

1 : 지조직용 혼방사 (PE와 PP의 혼방)1: blended yarn for paper tissue (blend of PE and PP)

2 : 표면 파일사 (PE분사(分絲))2: surface pile yarn (PE injection)

3 : 이면 파일사 (NP복합 초극세사)3: back side pile yarn (NP composite microfiber yarn)

본 발명에 따른 세척용 양면 편포는 그 지조직에 일반적인 PE와 융점이 낮은 폴리올레핀계 섬유인 PP섬유를 혼방한 혼방사(1)를 사용하며, 표면 파일사(2)로는 PE로 된 굵은 분사를 사용하고, 이면 파일사(3)로는 초극세사인 NP 복합사를 사용하여 통상의 방법으로 양면 파일 편포(P)를 편직한 후 이를 열처리 및 표면 코팅처리를 함으로써 제조되는 것으로 제조 공정별로 실시예를 겸하여 보다 구체적으로 설명하면 다음과 같다.The double-sided knitted fabric for washing according to the present invention uses a mixed yarn (1) mixed with a general PE and a PP fiber, which is a polyolefin-based fiber having a low melting point, and used a thick spray of PE as the surface pile yarn (2). In addition, as the back pile yarn (3) is manufactured by knitting double-sided pile knitted fabric (P) by a conventional method using an ultra-fine NP composite yarn and then heat-treating and surface coating treatment, it is also combined with an embodiment for each manufacturing process Specifically, it is as follows.

1) 편직공정1) Knitting Process

먼저 지조직용으로 일반적인 폴리에스터(PE)와 폴리프로필렌(PP)의 비율이 30∼80중량％ : 70∼20중량％가 되도록 혼방한 혼방사(1)를 준비하고, 표면 파일사(2)로는 200∼300D/2∼12F의 폴리에스터로 된 굵은 분사를, 이면 파일사(3)로는 나일론과 폴리에스터의 복합사로 된 0.1∼0.5D의 초극세사를 준비하여 통상적인 환편기에서 통상적인 방법으로 양면 파일 편포(P)를 편직한다.First, a blended blended yarn 1 is prepared so that the ratio of general polyester (PE) and polypropylene (PP) is 30 to 80% by weight: 70 to 20% by weight for the paper tissue. 200-300D / 2-12F polyester coarse injection, and back pile yarn 3, 0.1-0.5D ultra-fine yarn made of a composite yarn of nylon and polyester is prepared. Knit the fabric P.

상기 지조직용의 혼방사(1)에서 PE의 비율이 30중량％ 미만이면, 즉 PP의 비율이 70중량％를 초과하면 최종 제품이 너무 딱딱하여져서 포백으로써의 부드러움이 저하되고, 반대로 PE의 비율이 80중량％를 초과하면 즉 PP의 비율이 20중량％ 미만이면 최종 제품에서 지조직과 파일사(1)(2)를 완전히 결합시키지 못하므로 파일이 밀리거나 조직이 흩어질 우려가 있다.If the ratio of PE in the blended yarn 1 for the paper tissue is less than 30% by weight, that is, if the proportion of PP is more than 70% by weight, the final product becomes too hard and the softness of the cloth is lowered. If it exceeds 80% by weight, that is, if the proportion of PP is less than 20% by weight, the final product may not be able to completely bond the tissue and pile yarns (1) (2), so that the pile may be pushed or the tissue may be scattered.

또한, 표면 파일사(2)는 그 굵기가 200D 미만이면 파일이 부드러워 수세미 역할을 하기가 어려우며, 300D보다 굵으면 파일이 너무 강하여 표면이 부드러운 가구 등이 긁혀져 손상될 염려가 있으며, 이면 파일사(3)인 NP복합사의 굵기가 0.1데니어 미만이어도 효과에는 큰 차이가 없으나 초극세사를 제조하기 어려운 단점이 있으며, 0.5데니어보다 굵으면 유리면과 같이 평면에 부착된 미세한 먼지 등을 제거하기가 어려운 결점이 있다.In addition, if the thickness of the surface pile yarn (2) is less than 200D, the pile is soft, it is difficult to play a loofah, If thicker than 300D, the pile is too strong, there is a risk that the surface of the soft furniture, etc. may be scratched and damaged. (3) Even if the thickness of NP composite yarn is less than 0.1 denier, there is no big difference in effect, but it is difficult to manufacture microfiber. If thicker than 0.5 denier, it is difficult to remove fine dust attached to the plane such as glass surface. have.

한편, 상기한 지조직용 혼방사를 항균 가공하여 사용하면 편포를 습윤 상태로 장시간 보존하여도 세균의 발생을 억제하여 위생적인 세척포를 얻을 수 있다. 이때 전 편포를 항균가공처리를 하여도 되지만 가공이 어렵고 그 비용이 막대하여 경제적이지 못하기 때문에 적은 비용과 약제로 가공이 용이한 지조직용 혼방사(1)만을 항균가공처리함으로써 경제적이며, 항균효과도 우수하며, 지조직에 사용하기 때문에 약제가 탈리되는 일이 적어 항균성을 오랫동안 지속할 수 있는 효과도 있는 것이다.On the other hand, if the blended yarn for the paper tissue is used as an antibacterial treatment, even if the knitted fabric is stored in a wet state for a long time, it is possible to suppress the generation of bacteria and obtain a sanitary washing cloth. At this time, the whole knitted fabric may be treated with antibacterial treatment, but it is economical because it is difficult to process and its cost is not economical because only the mixed yarn (1) for the paper tissue, which is easy to process with low cost and chemicals, is antibacterial. It is also excellent, because it is used for lichen tissue is less detachment of the drug is effective to last for a long time antibacterial.

2) 염색공정2) dyeing process

편직공정에서 얻어진 편포(P)를 120∼140℃에서 통상의 방법으로 침염한다. 120℃ 미만에서는 합성섬유의 염색성이 좋지않으며, 140℃를 초과하면 지조직용 혼방사(1)에 함유된 PP섬유에 손상을 입어 편포가 구겨질 염려가 있으므로 주의해야 한다.The knitted fabric P obtained in the knitting process is impregnated by a conventional method at 120 to 140 ° C. If it is less than 120 ℃, the dyeability of the synthetic fiber is not good, and if it exceeds 140 ℃ should be careful because the damage to the PP fibers contained in the mixed yarn (1) for the tissue tissue may be wrinkled.

3) 텐터링 및 가열 공정3) tentering and heating process

염색된 편포(P)는 습윤에 의해 조직이 약간 흐트러지고 폭과 길이가 약간씩 줄어들기 때문에 이를 텐터(tenter)에 걸어 본래의 폭을 회복시키는 것이다.Dyeing knitted fabric (P) is a tissue that is slightly distracted by the wetting and the width and length is slightly reduced by hanging on a tenter (tenter) to restore the original width.

텐터링(tentering) 공정에서 로울을 통하여 편포에 160∼200℃로 열을 가하면 편포가 고정된 상태에서 지조직에 함유된 PP섬유만 용융하여 양면 파일사(2)(3)와 지조직의 PE섬유를 확실하게 융착시키므로 표리 조직의 안정화를 기할 수 있으며, 편포 전체에 적당한 정도의 딱딱함도 부여함으로 세척포로 사용하기에 적합한 제품이 되는 것이다.In the tentering process, when heat is applied to the knitted fabric at a temperature of 160 to 200 ° C. through a roll, only the PP fibers contained in the paper tissue are melted in the state where the knitted fabric is fixed and double-sided pile yarn (2) (3) and PE of the paper tissue Since the fibers are firmly fused, stabilization of the front and back tissues can be achieved, and a suitable degree of rigidity is given to the entire knitted fabric, thereby making the product suitable for use as a cleaning cloth.

이때 가열 온도가 160℃미만이면 PP섬유가 잘 용융하지 않으며, 200℃를 초과하면 PE나 다른 섬유에 손상을 입혀 편포의 강도가 저하되어 세척포의 수명을 단축시키는 단점이 발생할 수 있다.At this time, if the heating temperature is less than 160 ℃ PP fiber does not melt well, if it exceeds 200 ℃ may damage the PE or other fibers to reduce the strength of the knitted fabric may shorten the life of the cleaning cloth.

4) 표면 코팅공정4) Surface coating process

텐터링 및 가열공정을 거친 편포(P)는 아직 딱딱한 오물을 제거하기에는 표면 파일사(2)가 너무 부럽기 때문에 표면 파일사(2)를 딱딱하게 하기 위하여 표면 파일에 용융 아크릴수지를 스프레이 방식으로 코팅하여준다.The fabric P, which has undergone the tenting and heating process, is coated with molten acrylic resin on the surface pile in order to harden the surface pile yarn because the surface pile yarn 2 is too enviable to remove hard dirt. Do it.

이때 꼬임이 없는 분사(分絲)의 필라멘트들이 강하게 결합될 뿐만 아니라 더욱 딱딱해지므로 어떠한 오물이라도 제거할 수 있는 수세미 역할을 하며, 이면 파일사(3)는 그대로 부드러운 효과를 유지함으로 딱딱한 오물이나 미세한 먼지까지 쉽게 제거할 수 있는 양면 세척포를 얻게 되는 것이다.At this time, the filaments of the kink without twisting are not only strongly bonded but also become harder, and thus serve as a scrubber that can remove any dirt, and the back pile 3 keeps a soft effect as it is, so that it is hard dirt or fine. You get a double-sided cleaning cloth that can easily remove dust.

이상과 같은 본 발명은 하나의 세척포로 딱딱한 오물을 제거할 수 있는 수세미와 부드럽고 미세한 먼지까지 제거할 수 있는 먼지 닦기를 겸할 수 있는 제품을 간단한 공정으로 제조함으로써 하나의 세척포로 언제든지 오염된 장판, 유리, 식기, 가구 등을 깨끗하게 닦아낼 수 있을 뿐만 아니라 세균의 발생도 방지할 수 있는 항균처리가 되어 있으므로 위생적인 세척포를 제공하게 되는 것이다.As described above, the present invention provides a simple process to prepare a product that can also function as a scrubbing brush to remove hard dirt and a dust wiping to remove soft and fine dust in a single process, so that any plate, glass contaminated with one washing cloth at any time. As well as cleaning dishes, furniture, etc., as well as antibacterial treatment to prevent the occurrence of bacteria will provide a hygienic cleaning cloth.

Claims (3)

세척용 파일 편포의 제조 방법에 있어서, 지조직용으로 일반적인 폴리에스터와 폴리프로필렌의 비율이 30∼80중량％ : 70∼20중량％가 되도록 혼방사를 준비하고, 표면 파일사로는 200 ∼ 300D/2∼12F의 굵은 폴리에스터 분사를, 이면 파일사로는 나일론과 폴리에스터의 복합사로 된 0.1∼ 0.5D의 초극세사를 준비하여 통상적인 방법으로 양면 파일 편포를 편직하는 편직공정과;In the manufacturing method of the washing pile knitted fabric, a blended yarn is prepared so that the ratio of general polyester and polypropylene for a paper tissue becomes 30 to 80 weight%: 70 to 20 weight%, and it is 200-300D / 2 as surface pile yarn A knitting process of knitting a double-sided pile knitted fabric in a conventional manner by preparing a coarse polyester spray of -12F, and preparing a 0.1-0.5D ultra-fine yarn made of a composite yarn of nylon and polyester as the back pile yarn; 편직공정에서 얻어진 편포를 120∼140℃에서 침염하는 염색공정과;A dyeing step of dyeing the knitted fabric obtained in the knitting step at 120 to 140 ° C; 염색된 편포를 텐터링(tentering)하면서 160∼200℃로 가열하여 폴리프로필렌을 융착시키는 텐터링 및 가열공정과;A tentering and heating step of fusing polypropylene by heating the dyed knitted fabric to 160 to 200 ° C while tentering; 가열공정을 거친 편포의 표면 파일에 용융 아크릴 수지를 스프레이 방식으로 코팅하여주는 표면 코팅공정을 갖추는 것을 특징으로 하는 세척용 양면 파일 편포의 제조방법.A method of manufacturing a double-sided pile knitted fabric for cleaning, characterized in that it comprises a surface coating process for coating the surface pile of the knitted fabric subjected to the heating process by spray coating. 세척용 파일 편포에 있어서, 지조직은 일반적인 폴리에스터와 폴리프로필렌의 비율이 30∼80중량％ : 70∼20중량％인 혼방사이고, 표면 파일사는 200 ∼ 300D/2∼12F의 굵은 폴리에스터 분사를, 이면에는 나일론과 폴리에스터의 복합사로 된 0.1∼05D의 초극세사로 되며, 이를 텐터링 공정에서 가열하여 폴리프로필렌 섬유를 융착시킨 다음 표면 파일에 용융 아크릴 수지를 코팅하여서 되는 것을 특징으로 하는 세척용 양면 파일 편포.In the washing pile knitted fabric, the paper texture is a blended yarn having a ratio of general polyester and polypropylene of 30 to 80% by weight: 70 to 20% by weight, and the surface pile yarn is coated with a thick polyester spray of 200 to 300D / 2 to 12F. On the back, it is made of ultrafine yarn of 0.1-05D made of a composite yarn of nylon and polyester, and it is heated in the tenterizing process to fuse the polypropylene fibers, and then coat a molten acrylic resin on the surface pile. File knitted. 청구항 2에 있어서, 지조직용 혼방사에 항균가공처리를 하는 것을 특징으로 하는 세척용 양면 파일 편포.The double-sided pile knitted fabric for washing according to claim 2, wherein the mixed yarn for paper tissue is subjected to an antibacterial processing.
KR10-2002-0009258A 2002-02-21 2002-02-21 Double pile knitted fabric for cleansing and manufacturing process of that's KR100448172B1 (en)