KR100421713B1 - Multi-fluid embrocation for build ing construction - Google Patents
Multi-fluid embrocation for build ing construction Download PDFInfo
- Publication number
- KR100421713B1 KR100421713B1 KR10-2001-0012291A KR20010012291A KR100421713B1 KR 100421713 B1 KR100421713 B1 KR 100421713B1 KR 20010012291 A KR20010012291 A KR 20010012291A KR 100421713 B1 KR100421713 B1 KR 100421713B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- water
- present
- added
- powder
- Prior art date
Abstract
본 발명은 원적외선이 다량 방출되는 일라이트(illite)에 다량의 음이온이 방출되는 전기석과, 역시 원적외선이 다량 방출되는 항균사, 그리고 전자파 차단 및 흡수효과가 탁월한 전도성 고분자 물질 및 페라이트 등을 분말형태로 혼합하여 스프레이나 붓 등으로 건축물의 바닥, 벽, 천정 등에 코팅하므로서 피로회복기능과 심신의 안정화기능, 그리고 공기의 정화기능과 항균, 방충기능, 전자파차단 및 흡수기능, 온열기능 등을 할 수 있게 하여 인체의 건강을 크게 증진한 건축물 마감시공용 다기능 액상 도포제에 관한 것으로서,The present invention is in the form of powder tourmaline that emits a large amount of negative ions in the illite, which emits a large amount of far infrared rays, antimicrobial yarn that also emits a large amount of far infrared rays, and conductive polymers and ferrites with excellent electromagnetic shielding and absorption effects. By mixing and coating the floor, wall, and ceiling of the building with spray or brush, etc., it can be used for fatigue recovery, stabilization of mind and body, air purification, antibacterial, insect repellent, electromagnetic wave blocking and absorption, and thermal function. The present invention relates to a multifunctional liquid coating agent for building finishing, which greatly improves the health of the human body.
특히, 본 발명은 미세분말 처리된 일라이트 30 중량%∼40 중량%, 항균사(抗菌砂) 분말 10 중량%∼30 중량%, 전기석(토루말린) 분말 5 중량%∼10 중량%, 물 20 중량%∼30 중량%에 상기 분말들의 상호 결합력을 유지시키는 수용성수지 및 경화방지용 천연용제를 나머지 잔부로 하여 소정 농도의 액상을 유지할 수 있도록 한 특징이 있다.In particular, the present invention is 30% to 40% by weight of fine powder treated illite, 10% to 30% by weight of antibacterial sand powder, 5% to 10% by weight of tourmaline powder, water 20 The water-soluble resin and the anti-hardening natural solvent for maintaining the mutual bonding strength of the powders in the weight% to 30% by weight as the remainder is characterized in that to maintain a liquid phase of a predetermined concentration.
본 발명은 또, 상기 수용성수지는 10 중량%∼20 중량%를 첨가하는 한편, 상기 수용성수지로는 실리콘 변성에폭시수지, 실리콘 변성아크릴수지, 실리콘 변성수지중 어느 하나를 사용하는 것을 특징으로 한 것이다.In addition, the water-soluble resin is added to 10% by weight to 20% by weight, while the water-soluble resin is characterized in that any one of silicone modified epoxy resin, silicone modified acrylic resin, silicone modified resin is used. .
또한, 본 발명은 천연용제는 5 중량%∼10 중량%를 첨가하는 한편, 상기 천연용제로는 감귤류, 테레핀유, 유카립투스테레핀유 및 발산테레핀유중 어느 하나를 사용하는 것을 특징으로 한 것이며, 본 발명은 또 소정량의 착색제와 점도 증강제,그리고 PH 조정제를 소정량 투입한 것을 특징으로 한 것이다.In addition, the present invention is characterized in that the natural solvent is added to 5% to 10% by weight, while the natural solvent is any one of citrus fruits, terepin oil, eukarip tustereperin oil and divergent terpine oil. The present invention is also characterized in that a predetermined amount of a coloring agent, a viscosity enhancer, and a pH adjuster are added.
또한, 본 발명은 전도성 고분자 물질 5 중량%∼10 중량%를 첨가한 것을 특징으로 한 것이다.In addition, the present invention is characterized in that 5 to 10% by weight of the conductive polymer material is added.
Description
본 발명은 건축물 마감시공용 다기능 액상 도포제에 관한 것으로서, 더욱 상세하게는 원적외선 및 음이온이 다량 방출되는 일라이트(illite)와 전기석, 그리고 항균사와 전자파차단 및 흡수효과가 있는 전도성 고분자물질과 페라이트물질을 주성분으로 한 분말을 혼합하여 스프레이나 붓 등으로 건축물의 바닥, 벽, 천정 등에 코팅하므로서 인체의 건강을 크게 증진할 수 있도록 한 건축물 마감시공용 다기능 액상 도포제에 관한 것이다.The present invention relates to a multifunctional liquid coating agent for building finishing, and more specifically, to illite and tourmaline, in which a large amount of far-infrared rays and anions are emitted, and antimicrobial yarn, electromagnetic shielding, and conductive polymer material and ferrite material having an absorption effect. The present invention relates to a multi-functional liquid coating agent for building finishing, which can greatly improve the health of the human body by mixing a powder composed of a main component and coating the floor, the wall, and the ceiling with a spray or a brush.
근래에 들어서, 아파트와 같은 건축물의 바닥, 벽, 천정 등에 원적외선이 방사되는 물질을 성형하여 시공하거나 또는 원적외선이 방사되는 물질을 액상으로 제조하여 코팅하므로서 인체의 건강을 증진하는 것이 추세이며, 특히 시공이 매우 간편한 스프레이식 코팅방식은 본인이 이미 특허출원(대한민국 특허출원번호 2000-40977호)바 있다.In recent years, it is a trend to promote the health of the human body by forming and coating materials that emit far infrared rays on floors, walls, and ceilings of buildings such as apartments, or by manufacturing and coating materials that emit far infrared rays in liquid form. This very simple spray coating method has already been patented (Korean Patent Application No. 2000-40977).
즉, 상기 특허출원은 일라이트를 극미세로 분쇄한 중량비 60%와, 상기 일라이트분말과 교반되어 액상을 유지토록 하는 용제를 잔부로 하여 구성되며, 이때 용제는 무기용제, 유기용제, 천연용제 중 어느 하나를 소정량 포함하고, 상기 용제에 전착성을 갖는 실리콘 변성에폭시수지, 실리콘 변성아크릴수지, 실리콘 변성수지중 어느 하나를 소정량 포함하는 한편, 상기 일라이트분말에 약 10%의 숯분말을 첨가하여 된 것으로서, 이는 원적외선을 다량으로 방출하여 신진대사촉진 및 세포활성화기능을 촉진하는 한편, 기존의 건물이나 신축건물에 액상의 도포제를 스프레이 방식으로 도포하므로서 시공 시간, 시공 비용을 줄임은 물론 그 작업을 용이하게 할 수 있었다.That is, the patent application is composed of 60% by weight of the finely pulverized illite and the remainder of the solvent to maintain the liquid state by stirring with the illite powder, wherein the solvent is an inorganic solvent, an organic solvent, a natural solvent A predetermined amount is included, and any one of silicon-modified epoxy resins, silicone-modified acrylic resins, and silicone-modified resins having electrodeposition property to the solvent is contained, and about 10% of the charcoal powder is contained in the illite powder. As it is added, it releases a large amount of far-infrared rays to promote metabolism promotion and cell activation functions, while reducing the construction time and construction cost by spraying a liquid coating agent onto existing buildings or new buildings. It was easy to work.
그러나, 종래에는 일라이트만을 주성분으로 사용하고 있기 때문에 다량의 원적외선으로 인한 신진대사촉진 및 세포활성화효과는 있으나 다른 기능 예컨대, 피로회복기능과 심신의 안정화기능, 그리고 공기의 정화기능과 항균, 방충기능 등을 요구하는 거주자들의 욕구를 충족시켜 주지 못하는 문제점이 있었다.However, conventionally, since only illite is used as a main ingredient, it has metabolic acceleration and cell activation effect due to a large amount of far infrared rays, but other functions such as fatigue recovery function, stabilization of mind and body, air purification function, antibacterial and insect repellent function. There was a problem that could not satisfy the needs of the residents who demand the back.
따라서, 본 발명은 상기와 같은 문제점을 토대로 연구 개발한 것으로서 원적외선이 다량 방출되는 일라이트(illite)에 다량의 음이온이 방출되는 전기석과, 역시 원적외선이 다량 방출되는 항균사, 그리고 전자파에 대한 자체 저항성을 갖는 전도성 고분자 물질과 페라이트 등을 분말형태로 혼합하여 스프레이나 붓 등으로 건축물의 바닥, 벽, 천정 등에 코팅하므로서 피로회복기능과 심신의 안정화기능,그리고 공기의 정화기능과 항균, 방충기능, 전자파차단 및 흡수기능, 온열기능 등을 할 수 있게 하여 인체의 건강을 크게 증진한 건축물 마감시공용 다기능 액상 도포제를 제공함에 그 목적이 있다.Therefore, the present invention has been researched and developed based on the above problems, tourmaline that emits a large amount of negative ions in the illite that emits a large amount of far infrared rays, antibacterial yarn that also emits a large amount of far infrared rays, and its own resistance to electromagnetic waves. Conductive polymer material and ferrite are mixed in the form of powder and coated on the floor, wall, and ceiling of the building with spray or brush to recover fatigue, stabilize mind and body, purify air, antibacterial, insect repellent, electromagnetic wave The purpose of the present invention is to provide a multifunctional liquid coating agent for building finishing that greatly improves the health of the human body by enabling the blocking and absorbing function and the heating function.
상기와 같은 목적을 달성하기 위한 본 발명은 미세분말 처리된 일라이트 30 중량%∼40 중량%, 항균사(抗菌砂) 분말 10 중량%∼30 중량%, 전기석(토루말린) 분말 5 중량%∼10 중량%, 물 20 중량%∼30 중량%에 상기 분말들의 상호 결합력을 유지시키는 수용성수지 및 경화방지용 천연용제를 나머지 잔부로 하여 소정농도의 액상을 유지할 수 있도록 한 특징이 있다.The present invention for achieving the above object is 30% to 40% by weight of fine powder treated illite, 10% to 30% by weight of antibacterial sand powder, 5% by weight of tourmaline (torumaline) powder 10% by weight, 20% by weight to 30% by weight of water is a water-soluble resin that maintains the mutual bonding strength of the powders and a natural solvent for preventing hardening as the remainder is characterized in that to maintain a liquid of a predetermined concentration.
또한, 본 발명은 전도성 고분자 물질과 페라이트물질 5 중량%∼10 중량%를 첨가한 것을 특징으로 한다.In addition, the present invention is characterized in that the conductive polymer material and the ferrite material 5% by weight to 10% by weight is added.
본 발명은 또, 상기 수용성수지는 10 중량%∼20 중량%를 첨가하는 한편, 상기 수용성수지로는 실리콘 변성에폭시수지, 실리콘 변성아크릴수지, 실리콘 변성수지중 어느 하나를 사용하는 것을 특징으로 한다.The present invention further comprises 10 wt% to 20 wt% of the water soluble resin, and the water soluble resin is characterized by using any one of a silicone modified epoxy resin, a silicone modified acrylic resin and a silicone modified resin.
또한, 본 발명은 천연용제는 5 중량%∼10 중량%를 첨가하는 한편, 상기 천연용제로는 감귤류, 테레핀유, 유카립투스테레핀유 및 발산테레핀유중 어느 하나를 사용하는 것을 특징으로 한다.In addition, the present invention is added to the natural solvent 5% by weight to 10% by weight, while the natural solvent is characterized in that any one of citrus fruits, terepin oil, eukarip Tustereperin oil and divergent terpene oil.
본 발명은 또, 소정량의 착색제와 점도 증강제, 그리고 PH 조정제를 소정량 투입한 것을 특징으로 한다.The present invention is also characterized in that a predetermined amount of a coloring agent, a viscosity enhancer, and a PH regulator are added.
이하, 본 발명의 바람직한 일실시예를 상세히 설명하면 다음과 같다.Hereinafter, a preferred embodiment of the present invention will be described in detail.
먼저, 본 발명을 실시하기 위해서는 일라이트와 항균사, 그리고 전기석 및 전도성 고분자 물질 및 페라이트를 미세분말로 형성하는 것이 우선되어야 하는데, 상기 일라이트는 80에서 400메쉬 사이로 분쇄하게 된다.First, in order to implement the present invention, it is necessary to first form an illite, an antibacterial yarn, a tourmaline, a conductive polymer material and a ferrite as fine powder, and the illite is pulverized between 80 and 400 mesh.
참고로, 상기 항균사는 대한민국 특허출원 제1999-36750호, 36751호, 36752호에 이미 개시됨은 물론이고 현재 시중에서 널리 사용되고 있는 것으로서, 상기 항균사의 제조과정을 보면 용해로에 일반적인 모래와 첨가제(유동제,기능제)를 투입하여 1400℃로 용해한 다음, 이를 급속냉각한 후 소정의 시간동안 건조하여 소정의 메쉬로 체질을 하므로서 완성되는데, 이렇게 구입된 항균사를 일라이트와 같이 80에서 400메쉬 사이로 분쇄하게 된다. 이때, 상기 항균사는 원적외선의 방사율이 높고, 항균, 항곰팡이 기능은 물론 열효율이 기존 모래의 두배가 넘으며, 현재 각종 건축물은 물론 찜질용, 화훼용, 잔자파차단용 등으로 널리 적용되고 있으며, 상기 항균사와 유사하게 사용되고 있는 재료들과의 효과를 시험하여 본 결과 하기와 같은 결과를 얻었다.For reference, the antimicrobial yarn is already disclosed in Korean Patent Application Nos. 1999-36750, 36751, and 36752, and is currently widely used in the market. After dissolving at 1400 ℃ by adding a functional agent, and then rapidly cooled and dried for a predetermined time to sieving to a predetermined mesh, the antibacterial yarn thus obtained is pulverized between 80 to 400 mesh like the illite Done. At this time, the antimicrobial yarn has high emissivity of far-infrared rays, antibacterial and antifungal functions, and thermal efficiency is more than twice that of the existing sand, and is currently widely applied to various buildings as well as for poultice, flowers, and remnant wave blocking. As a result of testing the effect with the materials used similarly to the antimicrobial yarn, the following results were obtained.
한편, 전기석은 희토류광석을 주원료로 한 것으로, 이 전기석은 현재 시중에서 오피 파우더(OP POWDER)라는 이름으로 널리 사용되고 있는 것인바, 이의 제조과정은 활성 희토류광석에 원적외선 재료를 혼합하여 1차 파쇄한 다음, 파쇄된 혼합물을 여과 및 건조공정을 거쳐 다시 파쇄한 후 이 혼합물을 두번에 걸쳐 소성공정을 하고, 소성된 혼합물을 다시 파쇄함과 동시에 여과하므로서 80에서 400메쉬 사이의 분말을 제공받을 수 있다. 이때, 상기와 같이 제조된 전기석은 다량의 음이온이 방출되는데, 상기 음이온의 효과로는 심신을 편하게 만들어 혈행을 원활하게 하고, 어깨결림, 요통, 심경 등을 부드럽게 하거나 피로회복을 촉진시킨다.On the other hand, the tourmaline is made of rare earth ore as the main raw material, and this tourmaline is widely used in the market under the name of OP POWDER, and its manufacturing process is performed by primary crushing by mixing far-infrared material with active rare earth ore. Next, the crushed mixture may be crushed again through filtration and drying, and then the mixture is calcined twice, and the crushed mixture is crushed and filtered at the same time, thereby providing a powder between 80 and 400 mesh. . At this time, the tourmaline manufactured as described above is released a large amount of negative ions, the effect of the negative ions to relax the mind and body to smooth blood circulation, stiff shoulders, back pain, deep heart, or to facilitate fatigue recovery.
상술한 음이온의 효과에 대해서 좀 더 부연하자면, 의학적으로 음이온을 흡수하게 되면 혈액에 용해되어 생체조직을 구성하는 세포의 활성을 증가시키고, 세포막을 경계로 해서 나트륨, 칼륨 등의 전해질과 노폐물의 수송, 교환의 신진대사가 촉진되며, 이에 따라서 인체의 자연치유력이 크게 향상되고, 더욱 더 자율신경의 움직임이 활발해진다고 보고되고 있다.More specifically, the effect of the anion described above is that medically absorbing an anion increases the activity of cells soluble in blood and constituting biological tissues, and transports electrolytes and waste products such as sodium and potassium across the cell membrane. It is reported that the metabolism of exchange is promoted, and thus the natural healing power of the human body is greatly improved, and the movement of autonomic nerves becomes more active.
전자파 차단 및 흡수효과 있는 전도성 고분자는 전도성물질과 전자파흡수체물질이 조합된 것으로서 전도성물질인 카본블랙, Cu, Ni중 어느 하나와, 전자파흡수체물질인 Mn-Zn, Ni-Zn, Cu-Zn, Cu-Zn-Mg-, Mn-Mg-Al, Mg-Zn-, YIG계 ferrite중 어느 하나를 혼합한 것이며, 이 또한 시중에 널리 이용되고 있는 물질이다. 여기에서, 상기 전도성 고분자와 페라이트를 투입하는 것은 각종 가전제품에서 나오는 전기장과 자기장에 장기간 노출됐을 경우 호르몬·면역체계가 깨져 백혈병·림프암·뇌암·기형아 등을 일으킨다고 알려져 있기 때문이며, 전기장은 전압이 높을수록, 자기장은 전류가 높을수록 많이 생기고, 전기장은 전기가 통하는 구리 등 금속, 또식물이나 생체에 의해 상당부분 흡수·차단되지만 자기장은 자석의 힘처럼 거의 모든 물질을 통과하므로 일반인들이 이에 대처하기가 매우 어렵다. 따라서, 상술한 전도성 고분자를 첨가하여 각종 전자파를 차단, 또는 흡수토록 하므로서 건강한 생활을 영위할 수 있으며, 이에 대한 실험 데이터는 하기와 같다.The conductive polymer with electromagnetic wave blocking and absorption effect is a combination of a conductive material and an electromagnetic wave absorber material, and any one of conductive materials carbon black, Cu, and Ni, and Mn-Zn, Ni-Zn, Cu-Zn, Cu, which are electromagnetic wave absorber materials. It is a mixture of any one of -Zn-Mg-, Mn-Mg-Al, Mg-Zn-, and YIG-based ferrite, which is also widely used in the market. In this case, the conductive polymer and the ferrite are introduced because the hormones and the immune system are broken after prolonged exposure to electric and magnetic fields from various home appliances, causing leukemia, lymph cancer, brain cancer, malformations, etc. The higher the magnetic field, the more the electric current is generated, and the electric field is absorbed and blocked by metals such as copper, electricity, plants, and living bodies, but magnetic fields pass through almost all materials like the force of magnets. Very difficult to do Therefore, by adding the above-mentioned conductive polymer to block or absorb various electromagnetic waves, it is possible to lead a healthy life. Experimental data on this are as follows.
상술한 바와 같이 일라이트와 항균사, 그리고 전기석을 80에서 400메쉬 사이가 되도록 미세분말로 형성한 후 물 20 중량%∼30 중량%에 분자끼리의 상호 결합력을 유지시키는 수용성수지 10 중량%∼10 중량%를 혼합하게 되는데, 이때 수용성수지는 수용성 에멀젼수지와 수용성 우레탄수지를 4:1의 비율로 혼합한 것으로 수용성 에멀젼수지는 50% 고형분의 퓨어 아크릴 코폴리머(pure acrylic copolymer)가, 그리고 수용성 우레탄수지는 우레탄 메타크릴레이트 고분자 물질이 사용됨이 바람직하다.As described above, the illite, the antimicrobial yarn, and the tourmaline are formed into fine powder to be between 80 and 400 mesh, and then, 20 wt% to 30 wt% of water is 10 wt% to 10 wt% to maintain the mutual bonding force between the molecules. In this case, the water-soluble resin is mixed with the water-soluble emulsion resin and the water-soluble urethane resin at a ratio of 4: 1. The water-soluble emulsion resin is a 50% solids pure acrylic copolymer and a water-soluble urethane. It is preferable that a urethane methacrylate polymer material is used for resin.
물과 수용성수지가 혼합된 상태에서 일라이트 30 중량%∼40 중량%, 전기석(토루말린) 분말 5 중량%∼10 중량%, 항균사(抗菌砂) 분말 10 중량%∼30 중량%를 순차적으로 투입한 다음, 전도성 고분자 물질과 페라이트 물질 5 중량%∼10 중량%를 첨가한다.30% by weight to 40% by weight of illite, 5% to 10% by weight of tourmaline powder, and 10% to 30% by weight of antibacterial sand powder in a state of mixing water and water-soluble resin After the addition, 5 wt% to 10 wt% of the conductive polymer material and the ferrite material are added.
그런 다음, 상기 혼합물에 경화방지용 천연용제를 5 중량%∼10 중량%를 첨가하게 되는데, 경화방지용 천연용제로는 오렌지나무의 추출물인 감귤유, 소나무의 추출물인 테레핀유, 유카립투스테레핀유 및 발산테레핀유가 사용된다.Then, 5% by weight to 10% by weight of the anti-curing natural solvent is added to the mixture, and the anti-curing natural solvent is citrus oil, the extract of orange trees, terepine oil, the extract of pine, yucrip tousterpene oil and Divergent terpene oil is used.
그리고, 상기 혼합물에 다양한 색상이 표출되도록 소정의 착색제 0.65 중량%를 첨가하고, 그 다음에 0.3 중량%의 점도 증강제를 투입하여 수분산을 시키는 한편, 0.05 중량% 정도의 PH조정제를 투입하여 PH를 적당하게 조정하는데, 이때 PH조정제로는 AMT-95가 사용됨이 바람직하다.한편 일라이트 30∼40중량%를 투입하는 것은 일라이트 성분이 다량의 원적외선 방출물질로써 인체에 유익한 원적외선을 방출하는 물질이기 때문에 30%이하일때에는 원적외선 방출량이 미미하여 원적외선 방출효과가 없고 40%이상일때에는 과다한 원적외선 방출로 인한 인체에 해가 될 수 있기 때문이다.그리고, 향균사 분말은 건축물 마감시공시 곰팡이, 박테리아등의 서식을 방지하는 균 살균물질로써 10∼30%중량을 첨가하나 10%이하 첨가시는 향균효과가 떨어지는 문제점이 있고 30%이상일때에는 그 이하와 별다른 차이점이 없어 30%로 제한하였다.전기석(토루말린)분말은 다량의 음이온이 방출되어 쾌적한 실내환경을 만들어 주는 역할을 하는 물질로써 5%이하일때에는 음이온의 방출이 미미하고 10%를 넘으면 차이점이 없어 10%로 한정하였다.물은 도포제 시공시 액상물질의 농도유지를 위해 첨가되는 것으로써 20%이하일때에는 점도가 낮아 도포제 분사가 원활히 이루어지지 않고 30%이상일때에는 너무 묽어 시공시 분사에 문제가 있다.Then, 0.65% by weight of a predetermined colorant is added to the mixture to express various colors, and then 0.3% by weight of a viscosity enhancer is added to disperse the water, while a pH adjuster of about 0.05% by weight is added to the PH. In this case, AMT-95 is preferably used as the pH adjusting agent. Meanwhile, adding 30-40 wt% of illite is a substance that emits far-infrared rays, which are beneficial to the human body as a large amount of far-infrared emitters. Therefore, when 30% or less, far infrared ray emission is insignificant, there is no effect of far infrared ray emission, and when it is 40% or above, it may harm the human body due to excessive far infrared ray emission. As an antiseptic bactericide, 10 ~ 30% weight is added, but when it is less than 10%, the antibacterial effect is reduced and 30% In case of phase, there is no difference between them and it is limited to 30%. Tourmaline powder is a substance that plays a role in creating a pleasant indoor environment by releasing a large amount of anions. If it is more than%, there is no difference, so it is limited to 10%. Water is added to maintain the concentration of liquid substance during the application of the coating material, and when the viscosity is 20% or less, the viscosity is low so that the coating agent is not sprayed smoothly. There is a problem with spraying.
상기와 같이 각 조성물을 모두 순차적으로 투입한 다음 믹싱하여 건축물 마감시공용 다기능 액상 도포제를 완료하므로서 이 다기능 액상 도포제를 스프레이방식으로 벽이나 바닥, 또는 도배 대용으로 분사 도포한다.As described above, all the compositions are sequentially added and then mixed to complete the multifunctional liquid coating agent for the building finishing, and the multifunctional liquid coating agent is spray-coated to a wall or floor or a substitute for the spraying method.
즉, 다기능 액상 도포제를 건축물의 벽이나 바닥면에 도포층이 형성되게 스프레이방식으로 도포하는 것으로 그 시공이 매우 간편하다 할 것이다.In other words, the application of the multi-functional liquid coating agent in a spray method so that the coating layer is formed on the wall or floor of the building will be very simple in its construction.
<실시예><Example>
먼저, 물 25중량%에 수용성수지 15중량%를 혼합하되, 상기 수용성수지의 수용성 에멀젼수지와 수용성 우레탄수지를 4:1의 비율로 혼합, 믹싱한 것으로 수용성 에멀젼수지는 50% 고형분의 퓨어 아크릴 코폴리머(pure acrylic copolymer)가, 그리고 수용성 우레탄수지는 우레탄 메타크릴레이트 고분자 물질이 사용됨이 바람직하다.First, 15% by weight of water-soluble resin is mixed with 25% by weight of water, but the water-soluble emulsion resin and water-soluble urethane resin of the water-soluble resin are mixed and mixed in a ratio of 4: 1. The water-soluble emulsion resin is 50% solid acrylic pure acrylic nose. The polymer (pure acrylic copolymer), and the water-soluble urethane resin is preferably a urethane methacrylate polymer material.
그런 다음, 물과 수용성수지가 혼합된 상태에서 약 300메쉬의 분말 일라이트30중량%, 약 300메쉬의 전기석(토루말린) 분말 5중량%, 약 300메쉬의 항균사(抗菌砂) 분말 15중량%를 순차적으로 투입하고, 전도성 고분자 물질과 페라이트 5 중량%를 첨가한다.Then, 30% by weight of powdered illite of about 300 mesh, 5% by weight of tourmaline powder of about 300 mesh, and 15% of antimicrobial powder of about 300 mesh with water and water-soluble resin mixed % Is added sequentially and 5% by weight of conductive polymer material and ferrite are added.
그런 다음, 상기 혼합물에 경화방지용 천연용제를 4 중량%를 첨가하게 되는데, 경화방지용 천연용제로는 오렌지나무의 추출물인 감귤유, 소나무의 추출물인 테레핀유, 유카립투스테레핀유 및 발산테레핀유가 사용된다.Then, 4% by weight of the anti-hardening natural solvent is added to the mixture, and the anti-hardening natural solvent is citrus oil, which is an extract of orange trees, terepin oil, an extract of pine tree, eukariptusterpene oil, and divergent terpene oil. Used.
그리고, 상기 혼합물에 다양한 색상이 표출되도록 소정의 착색제 0.65 중량%를 첨가하고, 그 다음에 0.3 중량%의 점도 증강제를 투입하여 수분산을 시키는 한편, 0.05 중량% 정도의 PH조정제를 투입하여 PH를 적당하게 조정하는데, 이때 PH조정제로는 AMT-95가 사용됨이 바람직하다.Then, 0.65% by weight of a predetermined colorant is added to the mixture to express various colors, and then 0.3% by weight of a viscosity enhancer is added to disperse the water, while a pH adjuster of about 0.05% by weight is added to the PH. In this case, AMT-95 is preferably used.
상기와 같이 각 조성물을 모두 순차적으로 투입한 다음 믹싱하여 건축물 마감시공용 다기능 액상 도포제를 완료하였다.As described above, all the compositions were sequentially added and then mixed to complete the multifunctional liquid coating agent for building finishing.
참고로, 상기 실시예에 의해 제조된 다기능 액상 도포제를 한국건자재 시험연구소에서 시험한 시험성적서를 도시한 것이다.For reference, it shows the test report of the multi-functional liquid coating agent prepared by the above embodiment tested in the Korea Building Materials Testing Institute.
1. 다기능 액상 도포제의 원적외선 방사율1. Far-infrared emissivity of multifunctional liquid coating agent
* 본 시험은 FT-IR spectrometer를 이용한 BLACK BODY대비 측정결과임.* This test is a measurement result of BLACK BODY using FT-IR spectrometer.
2. 다기능 액상 도포제의 음이온 방사율2. Anion Emissivity of Multifunctional Liquid Coating Agent
* 시험방법은 KICM-FIR-1042이고, 시험편은 내경=44㎜, 높이=297㎜의 원기둥이며, 전하입자 측정장치를 이용하여 실내온도 26도, 습도 65%, 대기중 음이온 수 66/cc 조건에서 시험한 것임.* The test method is KICM-FIR-1042, the test piece is a cylinder with inner diameter = 44 mm and height = 297 mm, using a charged particle measuring device, room temperature 26 degrees, humidity 65%, the number of anions in the air 66 / cc Tested by
3. 다기능 액상 도포제의 탈취시험3. Deodorization test of multifunctional liquid coating agent
* 시험방법은 KICM-FIR-1042이고, 시험편은 50×36×7(㎜)이며, 시험가스명은 암모니아이고, 가스농도측정은 가스검지관.* The test method is KICM-FIR-1042, the test piece is 50 × 36 × 7 (mm), the test gas name is ammonia, and the gas concentration measurement is a gas detector tube.
따라서, 본 발명은 원적외선이 다량 방출되는 일라이트(illite)에 다량의 음이온이 방출되는 전기석과, 역시 원적외선이 다량 방출되는 항균사와 전도성 고분자 물질, 페라이트 등을 분말형태로 혼합하여 스프레이나 붓 등으로 건축물의 바닥, 벽, 천정 등에 코팅하므로서 피로회복기능과 심신의 안정화기능, 그리고 공기의 정화기능과 항균, 방충기능, 전자파차단 및 흡수기능, 온열기능 등을 할 수 있게 하여 인체의 건강을 크게 증진할 수 있도록 한 매우 유용한 효과가 있다.Therefore, in the present invention, a tourmaline in which a large amount of anions are released in an illite in which a large amount of far infrared rays are emitted, and an antimicrobial yarn in which a large amount of far infrared rays are emitted, a conductive polymer material, ferrite, etc. are mixed in a powder form to spray or brush. By coating on the floor, wall, and ceiling of the building, fatigue recovery function, stabilization of mind and body, air purification, antibacterial, insect repellent, electromagnetic wave blocking and absorption function, and thermal function are greatly improved. There is one very useful effect that can be done.
Claims (5)