KR100359696B1 - The marble placed a reinforcement iron core, and the manufacturing method of it - Google Patents
The marble placed a reinforcement iron core, and the manufacturing method of it Download PDFInfo
- Publication number
- KR100359696B1 KR100359696B1 KR1020000034213A KR20000034213A KR100359696B1 KR 100359696 B1 KR100359696 B1 KR 100359696B1 KR 1020000034213 A KR1020000034213 A KR 1020000034213A KR 20000034213 A KR20000034213 A KR 20000034213A KR 100359696 B1 KR100359696 B1 KR 100359696B1
- Authority
- KR
- South Korea
- Prior art keywords
- marble
- iron core
- buried groove
- groove
- corner
- Prior art date
Abstract
본 발명은 대리석에 관한 것으로 더욱 상세하게는, 판상으로 절단되어 실내외의 장식용으로 널리 사용되는 대리석을 무거운 하중과 충격에도 쉽게 파손되지 않도록 가공 처리한 보강철심이 매설된 대리석 및 그 제조방법에 관한 것이다.The present invention relates to marble, and more particularly, to a marble embedded in a reinforcing iron core which is cut into a plate shape and widely processed for indoor and outdoor decoration so as not to be damaged by heavy loads and impacts. .
이를 위하여 본 발명은, 대리석을 소정 크기와 두께로 절단하여 일정한 형태의 대리석판(10)을 가공하는 대리석판 가공단계와(21), 상기 대리석판(10)의 하부면에 대각선방향과 가장자리방향으로 바닥면매설홈(11)을 소정 깊이로 형성하고, 상기 바닥면매설홈(11)의 모서리부에 화살표형상의 모서리매설홈(11a)을 소정 깊이로 형성하는 매설홈 형성단계(22)와, 상기 바닥면매설홈(11)과 모서리매설홈(11a)에 일치하게 결합되는 보강철심(13)을 제작하는 보강철심 제작단계(23)와, 상기 바닥면매설홈(11)과 모서리매설홈(11a)에 석재용 에폭시수지(12)를 충진하는 석재용 에폭시수지 충진단계(24)와, 상기 석재용 에폭시수지(12)가 충진된 바닥면매설홈(11)과 모서리매설홈(11a)에 보강철심(13)을 매설하는 보강철심 매설단계(25)와, 상기 바닥면매설홈(11)과 모서리매설홈(11a)에 충진된 석재용 에폭시수지(12)에 보강철심(13)을 매설홈(11)에 매설시켜 견고하게 경화되도록 하는 석재용 에폭시수지 경화단계(26)로 이루어진 것을 특징으로 하는 보강철심이 매설된 대리석 제조방법과, 상기의 방법으로 제조된 보강철심이 매설된 대리석을 특징으로 한다.To this end, the present invention, the marble plate processing step 21 for processing a marble plate 10 of a predetermined shape by cutting the marble into a predetermined size and thickness, and the diagonal direction and the edge direction on the lower surface of the marble plate 10 A buried groove forming step 22 of forming a bottom buried groove 11 to a predetermined depth, and forming an arrow-shaped corner buried groove 11a to a predetermined depth at a corner of the bottom buried groove 11; Reinforcing iron core manufacturing step 23 for producing a reinforcing iron core (13) coupled to match the bottom buried groove 11 and the edge buried groove (11a), and the bottom buried groove 11 and the corner buried groove Stone epoxy resin 12 filling step (11a) for filling the epoxy resin for stone step (24), and the bottom surface filling groove 11 and the corner buried groove (11a) filled with the stone epoxy resin (12) Reinforcing iron core embedding step (25) for embedding the reinforcing iron core (13), and the bottom buried groove 11 and the corner buried groove (11a) Embedded in the epoxy resin for stone (12) filled in the reinforcing iron core (13) embedded in the reinforcing groove (11) to bury the reinforcing iron core, characterized in that it consists of a stone epoxy curing step (26) to harden It is characterized in that the marble manufacturing method, and the marble embedded in the reinforcing iron core manufactured by the above method.
Description
본 발명은 대리석에 관한 것으로 더욱 상세하게는, 판상으로 절단되어 실내외의 장식용으로 널리 사용되는 대리석을 무거운 하중과 충격에도 쉽게 파손되지 않도록 가공 처리한 보강철심이 매설된 대리석 및 그 제조방법에 관한 것이다.The present invention relates to marble, and more particularly, to a marble embedded in a reinforcing iron core which is cut into a plate shape and widely processed for indoor and outdoor decoration so as not to be damaged by heavy loads and impacts. .
대리석은 색채나 모양이 여러 가지이고 결이 고우며, 연마(硏磨)하면 아름다운 광택이 나는 성질이 있고, 경도(硬度)가 낮아 가공해서 이용하기가 쉬운 이점이 있어 실내외의 벽면이나 바닥 장식재로 널리 사용되고 있다.Marble has a variety of colors and shapes, has a good texture, and when polished, it has a beautiful luster, and its low hardness makes it easy to process and use. It is widely used.
그러나, 대리석은 경도가 낮아 가공하기가 쉬운 이점이 있는 반면에, 경도가 낮음으로 인하여 무거운 하중이나 충격을 견디지 못하고 쉽게 파손되는 경우가 빈번하므로 대리석을 가공하더라도 파손의 위험 때문에 한정된 크기의 규격보다 면적을 제작하지 못하는 문제점이 있었다.However, while marble has the advantage of being easy to be processed due to its low hardness, it is frequently broken due to the low hardness, which cannot withstand heavy loads or impacts. There was a problem that can not be produced.
따라서, 면적이 넓은 장소에 대리석을 설치할 경우에는 많은 수의 규격화된 대리석을 연접해서 시공을 하게되므로 대리석과 대리석 사이에 틈새가 형성되어 심미감을 저하시키는 요인이 되며, 대리석의 무늬가 연속적으로 이어지지 않고 각각의 대리석에서 무늬의 끊어지게 되는 문제점이 있었다.Therefore, when marble is installed in a large area, a large number of standardized marbles are connected to each other so that a gap is formed between marbles and marbles, thereby degrading the aesthetics, and the marble pattern does not continue continuously. There was a problem of broken patterns in each marble.
또한, 무거운 하중과 충격에 충분히 견디도록 하기 위해서는 대리석을 두껍게 제작하여야 하는데, 이렇게 대리석의 두께가 두꺼워지면 대리석의 무게가 무거워 운반에 위험이 있으며, 시공이 용이하지 않아 작업에 소요되는 시간이 많이 소요되며, 무거운 하중과 충격에 견디기 위하여 필요이상으로 두꺼운 대리석을 사용하게 되므로 재료의 낭비를 초래하는 문제점이 있었다.In addition, in order to withstand heavy loads and impacts sufficiently, the marble should be made thick, but if the thickness of the marble becomes thick, the marble is heavy, which is dangerous to transport, and it is not easy to construct, which takes much time for work. In order to withstand heavy loads and impacts, thick marble is used more than necessary, resulting in waste of materials.
본 발명은 상기와 같은 문제점을 해결하기 위하여 제공된 것으로, 본 발명이 이루고자 하는 기술적 과제는, 대리석판의 하부면에 보강철심을 견고하게 매설시켜 대리석판의 강도를 향상시킴으로써 파손의 위험을 줄이며, 그에 따라, 대리석판을 두께는 얇고 면적은 넓게 가공할 수 있어 대리석의 무게를 줄여 대리석판의 운반에 따른 위험과 시공에 소요되는 작업시간을 단축할 수 있으며, 대리석판의 면적을 종래의 대리석과 비교하여 상대적으로 넓게 형성하여 대리석과 대리석이 연접하는 부위의 틈새를 줄이고 대리석의 무늬를 연속적으로 넓고 길게 나타내어서 심미감을 향상시킬 수 있도록 하는 것이다.The present invention is provided to solve the above problems, the technical problem to be achieved by the present invention, by reinforcing the reinforcement core firmly on the lower surface of the marble plate to improve the strength of the marble plate to reduce the risk of breakage, Therefore, the marble plate can be processed to be thin and large in area, thereby reducing the weight of the marble, thereby reducing the risk of transporting the marble plate and reducing the work time required for construction. By forming relatively wide, the gap between the marble and the marble is reduced, and the pattern of the marble is continuously wide and long to improve the aesthetics.
이를 위하여 본 발명은, 대리석을 소정 크기와 두께로 절단하여 일정한 형태의 대리석판을 가공하는 대리석판 가공단계와, 상기 대리석판의 하부면에 대각선방향과 가장자리방향으로 바닥면매설홈을 소정 깊이로 형성하고, 상기 바닥면매설홈의 모서리부에 화살표형상의 모서리매설홈을 소정 깊이로 형성하는 매설홈 형성단계와, 상기 바닥면매설홈과 모서리매설홈에 일치하게 결합되는 보강철심을 제작하는 보강철심 제작단계와, 상기 바닥면매설홈과 모서리매설홈에 석재용 에폭시수지를 충진하는 석재용 에폭시수지 충진단계와, 상기 석재용 에폭시수지가 충진된 바닥면매설홈과 모서리매설홈에 보강철심을 매설하는 보강철심 매설단계와, 상기 바닥면매설홈과 모서리매설홈에 충진된 석재용 에폭시수지에 보강철심을 매설홈에 매설시켜 견고하게 경화되도록 하는 석재용 에폭시수지 경화단계로 이루어진 것을 특징으로 하는 보강철심이 매설된 대리석 제조방법과, 상기의 방법으로 제조된 보강철심이 매설된 대리석을 특징으로 한다.To this end, the present invention, the marble plate processing step of processing a marble plate of a certain shape by cutting the marble to a predetermined size and thickness, and the bottom buried groove in the diagonal direction and the edge direction on the lower surface of the marble plate to a predetermined depth And a buried groove forming step of forming an arrow-shaped corner buried groove to a predetermined depth at an edge portion of the bottom buried groove, and reinforcing steel core fabricated to match the bottom buried groove and the corner buried groove. Iron core manufacturing step, the step of filling the epoxy resin for stone filling the epoxy resin for stone in the bottom buried groove and the corner buried groove, and the reinforcing iron core in the bottom buried groove and the corner buried groove filled with the epoxy resin for stone The reinforcing iron core is embedded and the reinforcing iron core is embedded in the epoxy resin for stone filled in the bottom buried groove and the corner buried groove. To the Marble method for producing the reinforcing core is embedded, characterized in that consisting of stone epoxy resin curing step for curing and such that, characterized by a core made of marble with a reinforcement buried in the method.
도 1은 본 발명에 따른 보강철심이 매설된 대리석의 제조방법을 나타낸 순서도.1 is a flow chart showing a method of manufacturing a marble embedded reinforcing iron core according to the present invention.
도 2는 본 발명에 따른 보강철심이 매설된 대리석의 구성을 보인 저면 분해사시도.Figure 2 is an exploded perspective view showing the bottom of the reinforcement core embedded marble according to the present invention.
도 3은 본 발명에 따른 보강철심이 매설된 대리석의 구성을 보인 단면도.3 is a cross-sectional view showing the configuration of a marble embedded reinforcing iron core according to the present invention.
<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>
10 : 대리석판 11 : 바닥면매설홈10: marble plate 11: floor buried groove
11a : 모서리매설홈 12 : 석재용 에폭시수지11a: corner buried groove 12: stone epoxy resin
13 : 보강철심 13a : 모서리보강살13: reinforcement core 13a: edge reinforcement
21 : 대리석판 가공단계 22 : 매설홈 형성단계21: marble plate processing step 22: buried groove forming step
23 : 보강철심 제작단계 24 : 석재용 에폭시수지 충진단계23: reinforcement core manufacturing step 24: stone epoxy resin filling step
25 : 보강철심 매설단계 26 : 석재용 에폭시수지 경화단계25: Reinforcement core buried step 26: Stone epoxy curing step
이하 본 발명의 구성 및 작용을 첨부한 도면을 참조하여 상세히 설명하면 다음과 같다.Hereinafter, the configuration and operation of the present invention will be described in detail with reference to the accompanying drawings.
도 1은 본 발명에 따른 보강철심이 매설된 대리석의 제조방법을 나타낸 순서도이고, 도 2는 본 발명에 따른 보강철심이 매설된 대리석의 구성을 보인 저면 분해사시도이며, 도 3은 본 발명에 따른 보강철심이 매설된 대리석의 구성을 보인 단면도이다.1 is a flow chart showing a method of manufacturing a marble buried reinforcement core according to the present invention, Figure 2 is a bottom exploded perspective view showing the configuration of a marble buried reinforcement core according to the present invention, Figure 3 according to the present invention This is a cross-sectional view showing the composition of marble embedded with reinforcing iron core
도 1 내지 도 3에 도시된 바와 같이 본 발명에 따른 보강철심이 매설된 대리석의 제조방법은 다음과 같다.As shown in Figure 1 to Figure 3 is a method of manufacturing a marble embedded reinforcing iron core according to the present invention.
원석인 대리석을 소정 크기와 두께로 절단하여 일정한 형태의 대리석판(10)을 규격에 맞게 가공하는 대리석판 가공단계(21)를 거친 후, 상기 대리석판(10)의 하부면에 대각선방향과 가장자리방향으로 바닥면매설홈(11)을 소정 깊이로 형성하고, 상기 바닥면매설홈(11)의 모서리부에 화살표형상의 모서리매설홈(11a)을 소정 깊이로 형성하는 매설홈 형성단계(22)를 거친다.After the marble is cut into a predetermined size and thickness, the marble plate 10 is processed into a predetermined size according to the standard. A buried groove forming step 22 of forming a bottom buried groove 11 in a predetermined depth and forming an arrow-shaped corner buried groove 11a at a predetermined depth in a corner of the bottom buried groove 11. Go through.
또한, 상기 대리석판(10)의 하부면에 형성된 바닥면매설홈(11)과 모서리매설홈(11a)에 일치하도록 결합되는 보강철심(13)과 모서리보강살(13a)을 별도로 제작하는 보강철심 제작단계(23)를 마련한다.In addition, the reinforcing iron core 13 and the reinforcing iron core 13a are separately manufactured to be combined to match the bottom buried groove 11 and the corner buried groove 11a formed on the lower surface of the marble plate 10. Prepare a manufacturing step (23).
그리고, 상기 바닥면매설홈(11)과 모서리매설홈(11a)에는 석재용 에폭시수지(12)를 골고루 충진하는 석재용 에폭시수지 충진단계(24)를 마련하고, 상기 에폭시수지(12)가 충진되어 경화되기 전에 바닥면매설홈(11)과모서리매설홈(11a)에는 각각 보강철심(13)과 모서리보강살(13a)을 일치되도록 매설하는 보강철심 매설단계(25)를 거쳐서 석재용 에폭시수지(12)를 경화시키는 석재용 에폭시수지 경화단계(26)로 이루어진다.In addition, the bottom buried groove 11 and the corner buried groove 11a is provided with a stone epoxy resin filling step 24 for evenly filling the stone epoxy resin 12, the epoxy resin 12 is filled Epoxy resin for stone through reinforcement core laying step (25) to bury the reinforcing iron core (13) and the edge reinforcement (13a) in the bottom buried groove (11) and the corner buried groove (11a) before hardening It consists of the epoxy resin curing step 26 for the stone to cure (12).
그리고, 상기와 같은 방법으로 제조되는 본 발명에 따른 보강철심이 매설된 대리석의 구성은 다음과 같다.And, the configuration of the marble embedded in the reinforcing iron core according to the present invention manufactured by the above method is as follows.
원석인 대리석을 소정 크기와 두께로 절단하여 일정한 형태의 대리석판(10)을 규격에 맞게 가공한 후, 상기 대리석판(10)의 하부면에 대각선방향과 가장자리방향으로 소정 깊이의 바닥면매설홈(11)을 형성하고, 상기 바닥면매설홈(11)의 모서리부에는 화살표형상의 모서리매설홈(11a)을 바닥면매설홈(11)과 동일한 깊이로 형성한다.After cutting the marble, which is a gemstone, to a predetermined size and thickness, processing a marble plate 10 having a predetermined shape according to a standard, and having a bottom surface groove of a predetermined depth in a diagonal direction and an edge direction on the lower surface of the marble plate 10. (11) is formed, and the corner portion of the bottom buried groove 11 is formed with an arrow-shaped corner buried groove (11a) to the same depth as the bottom buried groove (11).
그리고, 상기 대리석판(10)의 하부면에 형성된 바닥면매설홈(11)과 모서리매설홈(11a)에 일치하도록 결합되는 보강철심(13)과, 상기 보강철심(13)의 모서리부에 돌출 형성되는 모서리보강살(13a)을 별도로 제작하여 마련해 둔다.And, the reinforcing iron core 13 is coupled to match the bottom buried groove 11 and the corner buried groove (11a) formed on the lower surface of the marble plate 10, and protrudes in the corner portion of the reinforcing iron core (13) The corner reinforcement (13a) to be formed is prepared and prepared separately.
상기에서 바닥면매설홈(11)과 모서리매설홈(11a)은 제작하는 대리석의 크기와 형상에 따라 다양하게 변화를 줄 수 있으며, 그에 따라 보강철심(13)과 모서리보강살(13a)의 형태도 다양하게 변하게 된다.In the above, the bottom buried groove 11 and the corner buried groove (11a) can vary depending on the size and shape of the marble to be produced, according to the shape of the reinforcement core 13 and the edge reinforcement (13a) Will also vary.
또한, 상기에서 보강철심(13)과 모서리보강살(13a)은 일체로 제작하여도 무방하며, 다수 개의 조각편으로 제작하여 바닥면매설홈(11)과 모서리매설홈(11a)에 끼워 맞추어도 됨을 밝혀둔다.In addition, the reinforcing iron core 13 and the corner reinforcement 13a may be manufactured integrally, and may be made into a plurality of pieces to fit the bottom buried groove 11 and the corner buried groove 11a. Reveal.
상기 바닥면매설홈(11)과 모서리매설홈(11a)에는 석재용 에폭시수지(12)를골고루 충진하고, 석재용 에폭시수지(12)가 충진된 바닥면매설홈(11)과 모서리매설홈(11a)에 일치되도록 보강철심(13)과 모서리보강살(13a)을 매설시켜서 구성이 이루어지며, 상기 보강철심(13)과 모서리보강살(13a)이 대리석판(10)의 하부면에 매설되면 석재용 에폭시수지(12)를 경화시켜 대리석판(10)과 보강철심(13)이 일체로 견고하게 결합되도록 한다.The bottom buried grooves 11 and the corner buried grooves 11a are evenly filled with the epoxy resin 12 for the stone, and the bottom buried grooves 11 and the corner buried grooves filled with the epoxy resin 12 for the stone ( 11a) is made by embedding the reinforcement core 13 and the corner reinforcement (13a) to match, the reinforcement core 13 and the corner reinforcement (13a) is embedded in the lower surface of the marble plate 10 The stone epoxy resin 12 is cured so that the marble plate 10 and the reinforcing iron core 13 are integrally and firmly coupled.
상기에서 대리석판(10)과 보강철심(13)을 일체화시키는 석재용 에폭시수지(12)는 금속표면과 석재표면 양쪽 모두에 친화력을 가지고 강한 접착력을 지닌 접착제로서, 이러한 용도의 접착제는 다양한 종류가 있으며 본 발명에 사용되는 접착제도 석재용 에폭시수지에만 한정되지 않음을 밝혀 둔다.In the above, the epoxy resin for stone 12 integrating the marble plate 10 and the reinforcing iron core 13 has an affinity for both the metal surface and the stone surface and has a strong adhesive force. And it is to be noted that the adhesive used in the present invention is not limited only to the epoxy resin for stone.
이하 본 발명에 따른 보강철심이 매설된 대리석의 작용을 설명하면 다음과 같다.Hereinafter, the operation of the marble embedded in the reinforcing iron core according to the present invention will be described.
본 발명은 대리석판(10)의 하부면에 강도가 뛰어난 철심으로 제작된 보강철심(13)과 모서리보강살(13)을 매설하여 석재용 에폭시수지(12)로 일체화시킨 것으로, 대리석판(10)의 약한 강도를 보강철심(13)과 모서리보강살(13a)이 보강하여 주므로 대리석판(10)이 무거운 하중과 충격에도 충분히 견딜 수 있게 된다.The present invention is to embed the reinforcing iron core 13 and the corner reinforcement (13) made of the iron core with excellent strength on the lower surface of the marble plate 10 to be integrated with the epoxy resin for stone (12), marble plate (10) Since the reinforcing iron core 13 and the edge reinforcement 13a strengthen the weak strength of), the marble plate 10 can sufficiently withstand heavy loads and impacts.
상기와 같이 철심으로 강도가 보강된 대리석판(10)은 종래 대리석판보다 면적은 넓고 두께는 얇게 제작하여도 무거운 하중과 충격에도 쉽게 파손되지 않고 충분히 견딜 수 있으므로, 건물의 내외벽이나 바닥에 시공을 할 경우 무게가 가벼워 운반과 작업을 신속하고 용이하게 할 수 있으며, 운반과 시공에서 발생하는 파손을 줄일 수 있다.As described above, the marble plate 10 reinforced with iron core has a wider area and a thinner thickness than the conventional marble plate, and thus can be sufficiently damaged without heavy loads and impacts, so that the marble plate 10 is constructed on the inner and outer walls or floors of a building. In this case, the weight is light, which makes transportation and work quick and easy, and reduces the damage caused by transportation and construction.
또한, 본 발명은 면적을 넓게 제작할 수 있으므로 대리석과 대리석이 연접하여 생기는 틈새를 줄여 심미감을 향상시킬 수 있으며, 적은 수의 대리석으로 넓은 장소를 장식할 수 있어 작업시간을 단축시킬 수 있으며 작업을 더욱 용이하게 할 수 있다.In addition, the present invention can be manufactured in a wide area, thereby reducing the gap between marble and marble to improve the aesthetics, and to decorate a large place with a small number of marbles, which can shorten the working time and further work. It can be done easily.
이상에서 살펴본 바와 같이 본 발명은, 대리석판의 하부면에 철심을 견고하게 매설시켜 대리석판의 강도를 향상시킴으로써 운반이나 시공시에 발생하는 파손을 줄이고, 그에 따라 대리석판의 두께는 얇고 면적은 넓게 가공할 수 있어 대리석의 무게를 줄여 대리석판의 운반에 따른 위험과 시공에 소요되는 작업시간을 단축할 수 있으며, 대리석판의 면적을 종래의 대리석과 비교하여 상대적으로 넓게 형성하여 대리석과 대리석이 연접하는 부위의 틈새를 줄이고 대리석의 무늬를 연속적으로 넓고 길게 나타내어서 심미감을 향상시킬 수 있도록 하는 효과가 있다.As described above, the present invention, by embedding the iron core firmly on the lower surface of the marble plate to improve the strength of the marble plate to reduce the damage caused during transportation or construction, accordingly the thickness of the marble plate is thin and the area is wide It can be processed to reduce the weight of the marble, reducing the risk of transporting the marble plate and the time required for construction.The area of the marble plate is relatively wider than that of the conventional marble, so that marble and marble are connected. There is an effect that can improve the aesthetics by reducing the gap of the part to be shown and the pattern of the marble in a wide and long continuous.
Claims (2)