KR100303203B1 - Transfer solution for coating and coating method using the same - Google Patents

Transfer solution for coating and coating method using the same Download PDF

Info

Publication number
KR100303203B1
KR100303203B1 KR1019970080807A KR19970080807A KR100303203B1 KR 100303203 B1 KR100303203 B1 KR 100303203B1 KR 1019970080807 A KR1019970080807 A KR 1019970080807A KR 19970080807 A KR19970080807 A KR 19970080807A KR 100303203 B1 KR100303203 B1 KR 100303203B1
Authority
KR
South Korea
Prior art keywords
coating
coated
transfer solution
wood grain
water
Prior art date
Application number
KR1019970080807A
Other languages
Korean (ko)
Other versions
KR19980079570A (en
Inventor
유락기
Original Assignee
유락기
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 유락기 filed Critical 유락기
Priority to KR1019970080807A priority Critical patent/KR100303203B1/en
Publication of KR19980079570A publication Critical patent/KR19980079570A/en
Application granted granted Critical
Publication of KR100303203B1 publication Critical patent/KR100303203B1/en

Abstract

PURPOSE: Provided are a transfer solution for coating which enables wood grain to be coated on an object to be coated without requiring a medium, and a coating method which can coat the object having complex curves and edges with wood grain, using the transfer solution. CONSTITUTION: The transfer solution is prepared by mixing 60-80 wt.% of a coating for lacquering, 20-10 wt.% of gasoline, 10-5 wt.% of coal oil, and 10-5 wt.% of trephine oil to obtain a mixture and aging the mixture at the temperature of 18-23deg.C and the humidity of 25-35% for approximately 48 hours. The coating method comprises the steps of (i) preparing a container with water, (ii) forming a layer of transfer solution on the water surface and designing a coating for lacquering contained in the transfer solution so as to have a wood grain, (iii) immersing an object to be coated in the water through the layer of transfer solution to transfer the wood grain to surface of the object, (iv) removing the layer of transfer solution, and (v) removing the object from the water and drying the object.

Description

도장용 전사용액 및 그를 이용한 도장방법(Transcriptive Solution for Paint and Method for Painting the same)Transcriptive Solution for Paint and Method for Painting the same

본 발명은 도장대상물체에 도장되어질 도장물질에 관한 것으로, 특히 다양한 형상의 도장대상물체의 표면을 우드그레인의 형태로 도장하기에 적합한 전사용액에 관한 것이다. 또한, 본 발명은 상기의 전사용액을 이용하여 다양한 형상의 도장대상물체의 표면에 우드 그레인을 도장하는 도장방법에 관한 것이다.The present invention relates to a coating material to be coated on an object to be coated, and more particularly to a transfer solution suitable for coating the surface of the object to be coated in various shapes in the form of wood grain. The present invention also relates to a coating method for coating wood grain on the surface of the object to be coated in various shapes using the transfer solution.

통상적으로 침대와 같은 가구류, 차량용 핸들, 창틀 사시 등 산업제품들은 구매자들의 구매욕구를 일으키게끔 그 외관이 미려하게 도장되고 있다. 이러한 산업제품들의 외관에 도장되는 형태(즉, 무닉)에는 특정한 모양의 셀 패턴이 상하, 좌우 또는 상하좌우로 일정한 규칙에 따라 반복되는 형태(이하 "규칙성 무닉"라 함)와, 특정한 모양 및 규칙 없이 패턴이 자유롭게 변하면서 상하좌우로 진행되는 형태(이하, "불규칙성 무닉"라 함)가 주로 사용되게 된다. 이들 무닉들중 불규칙성 무닉는 구매자 또는 사용자가 자연미를 느낄 수 있게 하여 산업제품들과 친숙하게 할 수 있다는 점에서 자주 채택되고 있다. 이 불규칙성 무닉에서도 자유롭게 변하는 나이테와 같다 하여 "우드 그레인"이라 불리는 나무의 절단면 모양(이하, "우드 그레인"이라 함)은 산업제품이 나무와 같이 느껴지게 함과 아울러 고품질의 것으로 보이게 한다는 점에서 가장 많이 이용되고 있다.Typically, industrial products such as furniture, such as a bed, a steering wheel for a vehicle, and a window frame are beautifully painted to cause buyers' desire to purchase. In the form of coating on the exterior of these industrial products (ie, Miconic), the cell pattern of a specific shape is repeated in accordance with a certain rule in the vertical, vertical, horizontal, left and right (hereinafter referred to as "regular munic"), and the specific shape and The pattern that changes freely without rules and moves up, down, left and right (hereinafter referred to as "irregular munic") is mainly used. Irregular munics among these munics are frequently adopted in that they can be familiar with industrial products by allowing buyers or users to feel natural beauty. The shape of the cutout of a tree, called "wood grain" (hereinafter referred to as "wood grain"), which is like a ring that changes freely in this irregularity munic, is the best in that it makes an industrial product look like a tree and also look high quality. It is used a lot.

이 우드 그레인을 도장대상물체에 도장하는데에는 통상 우드 그레인이 인쇄되어진 필름이 이용되게 된다. 이를 상세히 하면, 우드 그레인이 인쇄되어진 필름을 도장대상물체의 표면에 부착·처리한 후 그 필름을 제거함으로써 도장대상물체의 표면에 우드 그레인이 전사되게 된다.In order to apply this wood grain to the object to be painted, a film usually printed with wood grain is used. In detail, the wood grain is transferred onto the surface of the object to be coated by attaching and treating the film on which the wood grain is printed to the surface of the object to be coated and then removing the film.

이와 같이 필름을 이용한 우드 그레인 도장방법은 어느 정도의 굴곡이나 에지부가 있는 도장대상물체의 표면에 우드 그레인을 도장할 수는 있으나 환형의 형상을 가지는 차량용 핸들 또는 구의 형상을 가지는 공과 같이 복잡한 굴곡이나 에지부들을 가지는 도장대상물체에는 적용되기 곤란하다. 이와 더불어, 우드 그레인이 인쇄되어진 필름에서는 투명한 수지필름과 같은 매개물에 우드 그레인이 전사가능하게 인쇄 되여야 하므로 필요한 수지가 낭비되고, 나아가 우드 그레인의 도장비용이 증가되게 된다. 그러므로, 수지필름과 같은 매개물을 소모하지 않으면서 우드 그레인을 도장대상물질에 도장할 수 있는 도장용 전사용액이 요구되고, 아울러 복잡한 굴곡이나 에지부들을 가지는 도장대상물체에도 우드 그레인을 도장할 수 있는 도장방법이 요구된다.As such, the wood grain coating method using a film can coat wood grain on the surface of the object to be coated with a certain degree of bending or edges, but complex bends or edges, such as a ball having the shape of a steering wheel or a sphere having an annular shape, may be used. It is difficult to apply to the object to be coated having the parts. In addition, in the film on which the wood grain is printed, the wood grain must be printed on a medium such as a transparent resin film so as to be able to be transferred so that the required resin is wasted and the coating cost of the wood grain is increased. Therefore, a transfer solution for coating wood grain onto the object to be coated without consuming a medium such as a resin film is required, and wood grain can also be coated on an object to be coated having complex bends or edges. Coating method is required.

따라서, 본 발명의 목적은 매개물을 요구하지 않으면서 도장대상물체에 우드 그레인이 도장되게 하는 도장용 전사용액을 제공함에 있다.Accordingly, it is an object of the present invention to provide a transfer solution for coating which allows wood grain to be coated on an object to be coated without requiring a medium.

본 발명의 다른 목적은 복잡한 굴곡 및 에지부들이 있는 도장대상물체에 우드 그레인이 도장되게 하는 도장용 전사용액을 제공함에 있다.Another object of the present invention is to provide a transfer solution for coating which allows wood grain to be coated on an object to be coated having complicated bends and edges.

본 발명의 또 다른 목적은 복잡한 굴곡 및 에지부들이 있는 도장대상물체에 우드 그레인을 도장 할 수 있는 도장용 전사용액을 이용한 도장방법을 제공함에 있다.Still another object of the present invention is to provide a coating method using a transfer solution for coating which can coat wood grain on an object to be coated having complex bends and edges.

본 발명에 따른 도장용 전사용액에는 도장대상물체에 우드 그레인이 도장되기에 적합하게끔 60 내지 80 중량% 의 옻칠용 도료, 20 내지 10 중량%의 휘발유, 10 내지 5 중량% 의 석유 및 10 내지 5 중량% 의 트레핀유가 혼합되게 된다.The transfer solution for coating according to the present invention includes 60 to 80% by weight of lacquer paint, 20 to 10% by weight of gasoline, 10 to 5% by weight of petroleum, and 10 to 5 to be suitable for coating wood grain on the object to be coated. By weight trepin oil will be mixed.

이렇게 조성되어진 본 발명에 따른 도장용 전사용액은 액체상태에서 복잡한 굴곡 및 에지부들이 있는 도장대상물체의 표면에 우드 그레인이 도장되게 한다.The transfer solution for coating according to the present invention thus constructed allows wood grain to be coated on the surface of the object to be coated with complicated bends and edges in the liquid state.

이에 따라, 본 발명에 따른 도장용 전사용액은 우드 그레인의 도장에 매개물을 제거할 수 있게 된다.Accordingly, the transfer solution for coating according to the present invention can remove the medium in the coating of the wood grain.

본 발명에 따른 도장용 전사용액을 이용한 도장방법은 물이 담긴 용기를 마련하는 단계와, 물의 표면에 옻칠용 도료가 우드 그레인의 도안을 이루게끔 혼합되어진 도장용 전사용액층을 형성하는 단계와, 도장용 전사용액층을 통과하여 물에 도장대상물체를 입수시킴으로서 우드 그레인이 도장대상물체의 표면에 전사되게 하는 단계와, 도장용 전사용액층을 제거하는 단계와, 도장대상물체를 물로부터 꺼내어 건조시키는 단계를 포함한다.The coating method using the coating transfer solution for coating according to the present invention comprises the steps of providing a container containing water, and forming a transfer solution layer for painting mixed with a lacquer paint to form a pattern of wood grain on the surface of the water, The wood grain is transferred to the surface of the paint object by passing the paint transfer liquid layer through the paint transfer layer, the removal of the paint transfer liquid layer, and taking the paint object out of the water to dry. It comprises the step of.

상기 목적 외에 본 발명의 다른 목적 및 특징들은 첨부도면을 참조한 실시예에 대한 설명을 통하여 명백하게 드러나게 될 것이다.Other objects and features of the present invention in addition to the above objects will become apparent from the description of the embodiments with reference to the accompanying drawings.

이하, 본 발명에 따른 도장용 전사용액과 그 제조방법 그리고 도장용 전사용액을 이용한 도장방법의 실시예들을 상세히 설명하기로 한다.Hereinafter, embodiments of the coating transfer solution, a manufacturing method thereof, and a coating method using the coating transfer solution according to the present invention will be described in detail.

먼저, 우드 그레인을 도장대상물체에 도장하는데 사용될 도장용 전사용액의 제조방법을 살펴보기로 한다. 도장용 전사용액은 60 내지 80 중량% 의 옻칠용 도료, 10 내지 20 중량% 의 휘발유, 5 내지 10 중량%의 석유 및 5 내지 10 중량% 의 트레핀유를 희석(또는 혼합)하고 그 희석되어진 용액을 18 내지 23 ℃의 온도와 25 내지 35 %의 습도에서 대략 48 시간 정도 숙성함에 의해 제조되게 된다. 이렇게 제조되는 도장용 전사용액은 그 조성비율 별 도장상태, 건조속도 및 작업능률 등으로 평가되었다.First, a method of preparing a transfer solution for painting to be used for painting wood grain onto an object to be coated will be described. The transfer solution for painting is diluted (or mixed) with 60 to 80% by weight of lacquer paint, 10 to 20% by weight of gasoline, 5 to 10% by weight of petroleum and 5 to 10% by weight of trepin oil, and the diluted solution. It is prepared by aging about 48 hours at a temperature of 18 to 23 ℃ and a humidity of 25 to 35%. The coating solution thus prepared was evaluated in terms of coating state, drying speed and work efficiency by composition ratio.

[실시예]EXAMPLE

표1 은 상기 방법에 의해 산출되는 본 발명의 제1 내지 제3 실시예의 도장용 전사용액들의 조성비를 나타낸다. 표1 에서의 조성비는 도장용 전사용액의 무게를 100 중량% 로 하여 산출된 것이다. 이들 제1 내지 제3 실시예의 도장용 전사용액들은 표1 에서와 같이 옻칠용 도료의 함량이 증가하면 그 증가량만큼 휘발유, 석유 및 트레핀유의 함량이 감소되는 형태의 조성비를 가진다.Table 1 shows the composition ratios of the coating transfer solutions for the first to third embodiments of the present invention calculated by the above method. The composition ratio in Table 1 was calculated by making the weight of the transfer solution for coating 100 wt%. As shown in Table 1, the coating transfer solutions of the first to third embodiments have a composition ratio in which the content of gasoline, petroleum, and trepin oil is decreased by the increase amount of the lacquer coating.

[표 1]TABLE 1

Figure kpo00001
Figure kpo00001

상기 옻칠용 도료의 함량이 증가함에 따라, 제1 내지 제3 실시예의 도장용 전사용액에 의한 우드 그레인의 도장상태, 그 전사용액의 건조속도, 작업능률 등의 특성은 표2 와 같이 된다.As the content of the lacquer paint increases, the characteristics of the coating state of the wood grain by the transfer solution for coating of the first to third embodiments, the drying speed of the transfer solution, the working efficiency, and the like are shown in Table 2.

[표2][Table 2]

Figure kpo00002
Figure kpo00002

표2 에서와 같이 도장용 전사용액에서 옻칠용 도료의 함량이 증가 될 수록 우드 그레인의 색도가 진하게 되는 반면 건조속도가 느려지게 된다. 이를 상세히 하면, 제1 실시예의 도장용 전사용액은 무닉의 형태는 좋으나 건조가 40 내지 50초 정도로 너무 빨라 도장대상물체에 전사되어지는 면이 묽게 보여짐으로써 형태가 잘 나타나지 않게 된다. 이로 인하여, 제1 실시예의 도장용 전사용액은 원하는 우드 그레인 무닉를 얻을 수 없다. 그리고 제3 실시예의 도장용 전사용액은 건조속도가 80 내지 10초 정도로 느리고 이와 더불어 옻칠용 도료가 많이 포함되어 있어 도장대상물체에 전사될 때 옻칠용 도료가 무닉에 따라 도두러지게 된다. 이로 인하여, 제3 실시예의 도장용 전사용액은 도장된 표면이 울퉁불통하게 된다. 이 결과, 제3 실시예의 도장용 전사용액은 별도의 표면 평탄화 공정을 요구하게 되어 작업능률이 떨어지게 된다. 반면, 제2 실시예의 도장용 전사용액은 65 내지 80초 정도로 건조속도가 가장 적당하고 도장대상물체에 도장된 무닉 표면이 표탄하게 유지됨과 아울러 우드 그레인 무닉 및 색도도 적당하게 나타나게 된다. 이러한 관점에서, 제2 실시예의 도장용 전사용액은 별도의 작업을 요구하지 않으면서도 원하는 무닉를 얻을 수 있기 때문에 가장 양호하게 된다. 이러한 조성비 별 특성에 따라, 우드 그레인의 도장하는데 사용되는 도장용 전사용액은 옻칠용 도료, 휘발유, 석유 및 트레핀유가 7:2:1:1 의 비율로 조성되는 것이 바람직하게 된다.As shown in Table 2, as the content of lacquer paint increases in the coating transfer solution, the color of wood grain becomes darker, but the drying speed becomes slower. In detail, the transfer solution for coating of the first embodiment is good in the form of a nick, but the drying is too fast for about 40 to 50 seconds, so that the surface to be transferred to the object to be painted is thin, so that the shape does not appear well. For this reason, the coating transfer solution of the first embodiment cannot obtain the desired wood grain munic. In addition, the transfer solution for coating of the third embodiment has a drying speed of about 80 to 10 seconds, and also includes a lot of lacquer paint, so that the lacquer paint is knocked off when the transfer object is painted. For this reason, the coated transfer solution of the third embodiment is unevenly painted. As a result, the coating transfer solution of the third embodiment requires a separate surface planarization process, thereby reducing work efficiency. On the other hand, the transfer solution for the coating of the second embodiment is the most suitable drying speed of about 65 to 80 seconds, the munic surface painted on the object to be painted is kept dignified, and the wood grain munic and chromaticity are also appropriately shown. In view of this, the coating transfer solution of the second embodiment is the best because the desired munic can be obtained without requiring a separate work. According to such composition ratio, the coating solution used for coating the wood grain is preferably lacquer coating, gasoline, petroleum and trepin oil in a ratio of 7: 2: 1: 1.

락카, 우레탄 및 잉크와 같은 일반적인 도료는 수면 상에서 무닉 자체가 획일적이고 도막이 두껍게 형성되므로 도장대상물체에 도장된 후 마감칠을 매우 곤란하게 합니다. 이로 인하여, 일반적인 도료는 도장 시 시간이 많이 소요되고 공정이 복잡하게 됩니다. 나아가, 일반적인 도료는 무닉 자체가 자연스럽지 못하게 됩니다.Common paints such as lacquers, urethanes and inks have a uniform and thick film on the surface of the water, making it very difficult to finish after painting on the object to be coated. Because of this, common paints are time-consuming and complicated to paint. Furthermore, ordinary paints will not be natural to Munk.

다음으로, 상기의 도장용 전사용액을 이용하여 우드 그레인을 도장대상물체의 표면에 도장하는 본 발명의 실시예에 따른 도장방법을 설명하기로 한다.Next, a coating method according to an embodiment of the present invention for coating the wood grain on the surface of the object to be coated using the above-mentioned transfer solution for painting will be described.

도장용 전사용액을 이용한 도장방법의 첫 번째 단계로는 도장대상물체는 표면이 매끈하게끔 가공되게 된다. 매끈하게 된 도장대상물체의 표면에는 기본 색이 칠해지게 된다. 이렇게 도장대상물체의 표면에 칠하여진 기본 색은 우드 그레인의 명암을 결정하게 된다.In the first step of the coating method using the transfer solution for painting, the object to be coated is processed to have a smooth surface. The surface of the object to be smoothed is painted with a basic color. The basic color painted on the surface of the object to be coated determines the contrast of the wood grain.

이어서, 물이 담겨진 용기에 도장용 전사용액이 담기게 된다. 이 때, 물의 표면에는 일정한 두께의 도장용 전사용액층이 형성되게 된다. 이 도장용 전사용액은 옻칠용 도료, 휘발유, 석유 및 트레핀유가 특정한 비율로 희석(또는 혼합)된 후 대략 48 시간 정도 숙성됨에 의해 제조된 것이다. 물의 표면에 형성되어진 도장용 전사용액층은 사포가루 및 먼지와 같은 이물질과 기포 등이 제거되게끔 처리된다.Subsequently, the transfer solution for painting is contained in a container containing water. At this time, the transfer solution layer for coating having a predetermined thickness is formed on the surface of the water. This coating transfer solution is prepared by dipping (or mixing) lacquer paint, gasoline, petroleum and trepin oil in a specific ratio and then aging for about 48 hours. The transfer solution layer for coating formed on the surface of the water is treated to remove foreign substances such as sandpaper and dust and bubbles.

아울러, 도장용 전사용액층은 표면에 옻칠용 도료 성분에 의해 그레인 무닉가 형성되도록 처리되게 된다. 도장용 전사용액층의 표면에 형성되는 그레인 무닉은 도장용 전사용액층이 희석봉 등과 같은 막대에 의해 자유롭게 휘저어짐으로써 형성되게 된다. 이 때, 물은 18 내지 23 ℃의 온도를 유지하여야 하며 실내습도도 25 내지 35%를 유지하여야 한다. 이렇게 형성되어진 그레인 무닉은 도장대상물체가 도장용 전사용액층을 경유하여 물쪽으로 입수될 때에 도장대상물체의 표면에 전사되게 된다. 도장대상물체는 유압식 치구가 매달린 채로 물쪽으로 입수된다. 물에 입수된 도장대상물체는 도장용 전사용액이 물의 표면으로부터 제거된 후 물로부터 건져내어져 일정한 기간(예를 들면 대략 48 시간) 동안 건조된다. 이와 같이, 도장대상 물체가 도장용 전사용액층을 경유하여 물에 입수되었다 꺼내어진 후 건조됨으로 도장대상물체의 표면에는 우드 그레인이 도장(또는 형성 또는 새겨진)되게 된다.In addition, the transfer solution layer for coating is treated so that grain munic is formed by the lacquer coating component on the surface. The grain munic formed on the surface of the painting transfer solution layer is formed by freely stirring the coating transfer solution layer by a rod such as a dilution rod. At this time, the water should maintain a temperature of 18 to 23 ℃ and room humidity should be maintained at 25 to 35%. The grain munic thus formed is transferred to the surface of the object to be coated when the object to be coated is obtained toward the water via the transfer solution layer for painting. The object to be painted is obtained into the water with the hydraulic jig hanging. The coating object obtained in the water is removed from the surface of the water after the coating transfer solution is removed from the water and dried for a predetermined period (for example, approximately 48 hours). In this way, the object to be coated is obtained through water through the transfer solution layer for coating, and after being taken out and dried, wood grain is coated (or formed or engraved) on the surface of the object to be coated.

이렇게 우드 그레인이 새겨진 도장대상물체의 표면에는 오일 스테인과 우레탄의 혼합되어진 혼합도장용액이 도장되게 된다. 이 도장용액은 도장대상물체의 표면에 새겨진 우드 그레인이 선명하게 나타나게 한다. 오일 스테인과 우레탄의 혼합도장용액이 도장되어진 도장대상물체의 표면에 우레탄과 같은 마감도장용액이 추가로 도장되게 된다. 이 마감도장용액은 우드 그레인이 새겨진 도장대상물체의 표면에 광택이 나타나게 한다.The surface of the object to be coated with wood grain is coated with a mixed coating solution of oil stain and urethane. This coating solution makes the wood grain inscribed on the surface of the object to be painted clear. A finish coating solution such as urethane is additionally coated on the surface of the object to be coated on which the mixed solution of oil stain and urethane is coated. This finishing solution causes the surface of the object to be carved with wood grain to appear glossy.

위와 같은 수순으로 진행되는 도장용 전사용액을 이용한 도장방법은 도장대상물체의 재질 및 형상과 무관하게 이용될 수 있다. 즉, 도장용 전사용액을 이용한 도장방법은 목재, 금속 및 수지류를 불문하고 여타의 재질에도 우드 그레인을 도장할 수 있으며 아울러 링 및 구와 같이 복잡한 굴곡 및 에지부들이 있는 도장대상물체의 표면에도 우드 그레인을 도장 할 수 있다.The coating method using the transfer solution for coating that proceeds as described above may be used regardless of the material and shape of the object to be coated. In other words, the coating method using the transfer solution for coating can apply wood grain to other materials regardless of wood, metal and resin, and also to the surface of the object to be coated with complex bends and edges such as rings and spheres. You can paint grain.

상술한 바와 같이, 본 발명에 따른 도장용 전사용액은 필름과 같은 매개물없이도 도장대상물체의 표면에 우드 그레인을 형성시킬 수 있다. 이에 따라, 본 발명에 따른 도장용 전사용액은 링과 구와 같이 복잡한 굴곡 및 에지부들이 있는 도장대상물체의 표면에 우드 그레인을 형성시킬 수 있게 된다.As described above, the transfer solution for coating according to the present invention can form wood grain on the surface of the object to be coated even without a medium such as a film. Accordingly, the coating transfer solution according to the present invention can form wood grain on the surface of the object to be coated with complex bends and edges such as rings and spheres.

또한, 본 발명에 따른 도장용 전사용액을 이용한 도장방법에서는 물의 상부에 도장용 전사용액층을 도장대상물체가 통과하게 함으로써 우드 그레인이 도장대상물체의 표면에 전사되게 한다. 이에 따라, 북잡한 굴곡 및 에지부들이 있는 도장대상물체의 표면에는 우드 그레인이 손쉽게 도장되게 된다.In addition, in the coating method using the transfer liquid for coating according to the present invention, the wood grain is transferred to the surface of the object to be coated by allowing the object to be coated to pass through the transfer liquid layer for coating on top of the water. As a result, wood grain is easily painted on the surface of the object to be coated, which has crowded bends and edges.

이상 설명한 내용을 통해 당업자라면 본 발명의 기술사상을 일탈하지 아니하는 범위에서 다양한 변경 및 수정이 가능함을 알 수 있을 것이다. 따라서, 본 발명의 기술적 범위는 명세서의 상세한 설명에 기재된 내용으로 한정되는 것이 아니라 특허 청구의 범위에 의해 정하여 져야만 할 것이다.Those skilled in the art will appreciate that various changes and modifications can be made without departing from the technical spirit of the present invention. Therefore, the technical scope of the present invention should not be limited to the contents described in the detailed description of the specification but should be defined by the claims.

Claims (9)

60 내지 80 중량%의 옻칠용 도료, 20 내지 10 중량%의 휘발유, 10 내지 5중량%의 석유, 및 10 내지 5 중량%의 트렌핀유가 혼합되어진 후, 18 내지 23 ℃의 온도 및 25 내지 35 % 의 습도에서 대략 48 시간 정도 숙성되는 것을 특징으로 하는 도장용 전사용액.60 to 80% by weight of lacquer paint, 20 to 10% by weight of gasoline, 10 to 5% by weight of petroleum, and 10 to 5% by weight of trenpin oil, after mixing the temperature of 18 to 23 ℃ and 25 to 35 A transfer solution for coating, which is aged for about 48 hours at a humidity of%. 옻칠용 도료, 휘발유, 석유 및 트레핀유가 70 중량%, 15 중량%, 7.5 중량% 및 7.5 중량% 의 조성비로 혼합되어진 후, 18 내지 23℃의 온도 및 25 내지 35%의 습도에서 대략 48시간 정도 숙성됨에 의해 제조되어 도장대상물체에 우드 그레인의 형태로 도장 것을 특징으로 하는 도장용 전사용액.Approximately 48 hours at a temperature of 18-23 ° C. and a humidity of 25-35% after mixing lacquer paint, gasoline, petroleum and trepin oil in a composition ratio of 70%, 15%, 7.5% and 7.5% by weight. A transfer solution for coating, which is prepared by being matured to a degree and painted in the form of wood grain on an object to be painted. 제 2 항에 있어서, 상기 우드 그레인은 상기 옻칠용 도료, 휘발유, 석유 및 트레핀유가 혼합된 상태에서 희석봉에 의해 휘저어짐에 의해 다양한 형태로 도안되는 것을 특징으로 하는 도장용 전사용액.The transfer solution of claim 2, wherein the wood grain is designed in various forms by stirring by a dilution rod in a state in which the lacquer paint, gasoline, petroleum, and trepin oil are mixed. (A) 물이 담긴 용기를 마련하는 단계와, (B) 상기 물의 표면에 도장용 전사용액층을 형성하고 그 도장용 전사용액을 희석봉에 의해 휘저어줌으로써 상기 전사용액에 포함된 옻칠용 도료가 우드 그레인의 도안을 이루게 하는 단계와, (C) 상기 도장용 전사용액층을 통과하여 상기 물에 도장대상물체를 입수시킴으로써 상기 우드 그레인이 상기 도장대상물체의 표면에 전사되게 하는 단계와, (D) 상기 도장용 전사용액층을 제거하는 단계와, (E) 상기 도장대상물체를 물에서 꺼내어 건조시키는 단계를 포함하는 것을 특징으로 하는 도장용 전사용액을 이용한 도장방법.(A) preparing a container containing water, and (B) forming a coating solution layer on the surface of the water and agitating the coating transfer solution with a dilution rod to the lacquer paint contained in the transfer solution (C) allowing the wood grain to be transferred to the surface of the object to be coated by obtaining a object to be coated with water through the coating layer for transferring the paint; The coating method using a transfer solution for coating, characterized in that it comprises the step of removing the coating solution layer for the coating, and (E) removing the coating object from water and drying. 제 4 항에 있어서, 상기 물은 18 내지 23 ℃를 유지하는 것을 특징으로 하는 도장용 전사용액을 이용한 도장방법.The method of claim 4, wherein the water is maintained at 18 to 23 ° C. 제 4 항에 있어서, 상기 (C)단계에서 상기 도장대상물체는 유압식 치구에 매달린 채로 물에 입수되는 것을 특징으로 도장용 전사용액을 이용한 도장방법.The method according to claim 4, wherein in the step (C), the object to be coated is obtained in water while being suspended from a hydraulic jig. 제 4 항 내지 제 6 항 중 어느 한 항에 있어서, 상기 도장대상물체가 환형 및 구의 형상 중 어느 한 형상으로 된 것을 특징으로 하는 도장용 전사용액을 이용한 도장방법.The coating method according to any one of claims 4 to 6, wherein the object to be coated has any one of annular and spherical shapes. 제 4 항 내지 제 6 항 중 어느 한 항에 있어서, 상기 도장대상물체가 차량용 핸들인 것을 특징으로 하는 도장용 전사용액을 이용한 도장방법.7. The coating method according to any one of claims 4 to 6, wherein the object to be coated is a steering wheel for a vehicle. 제 4 항 내지 제 6 항 중 어느 한 항에 있어서, 상기 도장대상물체가 목재, 금속 및 수지 중 어느 한 재질로 된 것을 특징으로 하는 도장용 전사용액을 이용한 도장방법.The coating method according to any one of claims 4 to 6, wherein the object to be coated is made of any one material from wood, metal, and resin.
KR1019970080807A 1997-12-31 1997-12-31 Transfer solution for coating and coating method using the same KR100303203B1 (en)